WO2000043202A1 - Coextruded sheets used in heat sealed thermoformed articles - Google Patents
Coextruded sheets used in heat sealed thermoformed articles Download PDFInfo
- Publication number
- WO2000043202A1 WO2000043202A1 PCT/US1999/027964 US9927964W WO0043202A1 WO 2000043202 A1 WO2000043202 A1 WO 2000043202A1 US 9927964 W US9927964 W US 9927964W WO 0043202 A1 WO0043202 A1 WO 0043202A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polymer
- sheet
- monovinylidene aromatic
- coextruded
- weight percent
- Prior art date
Abstract
Description
Claims