WO2000039046A1 - Silicon containing grinding aides for slag - Google Patents
Silicon containing grinding aides for slag Download PDFInfo
- Publication number
- WO2000039046A1 WO2000039046A1 PCT/US1999/031012 US9931012W WO0039046A1 WO 2000039046 A1 WO2000039046 A1 WO 2000039046A1 US 9931012 W US9931012 W US 9931012W WO 0039046 A1 WO0039046 A1 WO 0039046A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- slag
- silicon containing
- composition
- grinding aid
- clinker
- Prior art date
Abstract
Description
Claims