WO2000033411A1 - Pressurized metal-air battery cells - Google Patents
Pressurized metal-air battery cells Download PDFInfo
- Publication number
- WO2000033411A1 WO2000033411A1 PCT/US1999/028120 US9928120W WO0033411A1 WO 2000033411 A1 WO2000033411 A1 WO 2000033411A1 US 9928120 W US9928120 W US 9928120W WO 0033411 A1 WO0033411 A1 WO 0033411A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- cell
- pressure
- metal
- air
- battery cell
- Prior art date
Abstract
Description
Claims