WO2000024813A1 - Method of preparing rigid polyurethane foam - Google Patents
Method of preparing rigid polyurethane foam Download PDFInfo
- Publication number
- WO2000024813A1 WO2000024813A1 PCT/EP1999/007691 EP9907691W WO0024813A1 WO 2000024813 A1 WO2000024813 A1 WO 2000024813A1 EP 9907691 W EP9907691 W EP 9907691W WO 0024813 A1 WO0024813 A1 WO 0024813A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polyol
- cyclopentane
- polyurethane foam
- rigid polyurethane
- weight
- Prior art date
Abstract
Description
Claims