WO2000024561A1 - Multilayer rolls having a thin fluoropolymer top coat and method of manufacture - Google Patents
Multilayer rolls having a thin fluoropolymer top coat and method of manufacture Download PDFInfo
- Publication number
- WO2000024561A1 WO2000024561A1 PCT/US1998/022752 US9822752W WO0024561A1 WO 2000024561 A1 WO2000024561 A1 WO 2000024561A1 US 9822752 W US9822752 W US 9822752W WO 0024561 A1 WO0024561 A1 WO 0024561A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- mold
- core
- top coat
- sleeve
- roll
- Prior art date
Abstract
Description
Claims