WO2000022627A1 - Application de metaux nobles sur les surfaces internes de reacteurs a eau bouillante en conditions de marche, en presence de zinc dans l'eau de reacteur - Google Patents

Application de metaux nobles sur les surfaces internes de reacteurs a eau bouillante en conditions de marche, en presence de zinc dans l'eau de reacteur Download PDF

Info

Publication number
WO2000022627A1
WO2000022627A1 PCT/US1999/023643 US9923643W WO0022627A1 WO 2000022627 A1 WO2000022627 A1 WO 2000022627A1 US 9923643 W US9923643 W US 9923643W WO 0022627 A1 WO0022627 A1 WO 0022627A1
Authority
WO
WIPO (PCT)
Prior art keywords
water
noble metal
reactor
zinc
platinum
Prior art date
Application number
PCT/US1999/023643
Other languages
English (en)
Inventor
Samson Hettiarachchi
David Phillip Siegwarth
Robert Lee Ii Cowan
Robert James Law
Original Assignee
General Electric Company
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by General Electric Company filed Critical General Electric Company
Priority to HU0102586A priority Critical patent/HUP0102586A3/hu
Priority to EP99970499A priority patent/EP1075695A1/fr
Priority to CA002333072A priority patent/CA2333072A1/fr
Publication of WO2000022627A1 publication Critical patent/WO2000022627A1/fr

Abstract

Cette invention concerne un procédé qui permet de réduire la corrosion de pièces en alliage dans un réacteur nucléaire refroidi par eau ou autres organes connexes. Ce procédé consiste à injecter dans l'eau du réacteur, en présence de zinc, un composé libérant des cations de métal noble, ou bien une espèce cationique renfermant un métal noble dans l'eau du réacteur dans les conditions thermiques régnant pendant la marche.
PCT/US1999/023643 1998-10-13 1999-10-12 Application de metaux nobles sur les surfaces internes de reacteurs a eau bouillante en conditions de marche, en presence de zinc dans l'eau de reacteur WO2000022627A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
HU0102586A HUP0102586A3 (en) 1998-10-13 1999-10-12 Application of noble metals to internal surfaces of operating boiling water reactors in the presence of zinc in reactor water
EP99970499A EP1075695A1 (fr) 1998-10-13 1999-10-12 Application de metaux nobles sur les surfaces internes de reacteurs a eau bouillante en conditions de marche, en presence de zinc dans l'eau de reacteur
CA002333072A CA2333072A1 (fr) 1998-10-13 1999-10-12 Application de metaux nobles sur les surfaces internes de reacteurs a eau bouillante en conditions de marche, en presence de zinc dans l'eau de reacteur

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
US10398398P 1998-10-13 1998-10-13
US60/103,983 1998-10-13
US22789399A 1999-01-11 1999-01-11
US09/227,893 1999-01-11

Publications (1)

Publication Number Publication Date
WO2000022627A1 true WO2000022627A1 (fr) 2000-04-20

Family

ID=26801066

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US1999/023643 WO2000022627A1 (fr) 1998-10-13 1999-10-12 Application de metaux nobles sur les surfaces internes de reacteurs a eau bouillante en conditions de marche, en presence de zinc dans l'eau de reacteur

Country Status (7)

Country Link
EP (1) EP1075695A1 (fr)
AR (1) AR020800A1 (fr)
CA (1) CA2333072A1 (fr)
CZ (1) CZ20004662A3 (fr)
HU (1) HUP0102586A3 (fr)
TW (1) TW429379B (fr)
WO (1) WO2000022627A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9280688B2 (en) 2005-02-28 2016-03-08 Areva Inc. Apparatus and method for limiting and analyzing stress corrosion cracking in pressurized water reactors
WO2018027030A3 (fr) * 2016-08-04 2018-04-05 Dominion Engineering, Inc. Suppression du dépôt de radionucléides sur des composants de centrale nucléaire

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3175461B1 (fr) * 2014-07-30 2024-05-15 Westinghouse Electric Company Llc Procédé chimique pour passivation de matériau de système primaire pendant l'essai fonctionnel à chaud de centrales nucléaires

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0671485A1 (fr) * 1994-03-10 1995-09-13 General Electric Company Méthode pour réduire le potential de corrosion d'articles
US5600691A (en) * 1993-10-29 1997-02-04 General Electric Company Noble metal doping or coating of crack interior for stress corrosion cracking protection of metals
EP0790621A1 (fr) * 1996-02-15 1997-08-20 Abb Atom Ab Méthode pour empêcher la déposition des produits corrosifs radioactifs dans une centrale nucléaire

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5600691A (en) * 1993-10-29 1997-02-04 General Electric Company Noble metal doping or coating of crack interior for stress corrosion cracking protection of metals
EP0671485A1 (fr) * 1994-03-10 1995-09-13 General Electric Company Méthode pour réduire le potential de corrosion d'articles
EP0790621A1 (fr) * 1996-02-15 1997-08-20 Abb Atom Ab Méthode pour empêcher la déposition des produits corrosifs radioactifs dans une centrale nucléaire

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US9280688B2 (en) 2005-02-28 2016-03-08 Areva Inc. Apparatus and method for limiting and analyzing stress corrosion cracking in pressurized water reactors
WO2018027030A3 (fr) * 2016-08-04 2018-04-05 Dominion Engineering, Inc. Suppression du dépôt de radionucléides sur des composants de centrale nucléaire
US11469006B2 (en) 2016-08-04 2022-10-11 Dominion Engineering, Inc. Suppression of radionuclide deposition on nuclear power plant components

Also Published As

Publication number Publication date
HUP0102586A2 (hu) 2002-01-28
AR020800A1 (es) 2002-05-29
CA2333072A1 (fr) 2000-04-20
EP1075695A1 (fr) 2001-02-14
CZ20004662A3 (cs) 2002-11-13
TW429379B (en) 2001-04-11
HUP0102586A3 (en) 2002-02-28

Similar Documents

Publication Publication Date Title
EP0833962B1 (fr) Dopage ou enduction in situ de surfaces d'acier inoxydable
US5608766A (en) Co-deposition of palladium during oxide film growth in high-temperature water to mitigate stress corrosion cracking
US5805653A (en) Noble metal doping or coating of crack interior for stress corrosion cracking protection of metals
US5774516A (en) Modification of oxide film electrical conductivity to maintain low corrosion potential in high-temperature water
US6793883B2 (en) Application of catalytic nanoparticles to high temperature water systems to reduce stress corrosion cracking
US5448605A (en) Palladium acetylacetonate solution and related method of manufacture
US5600692A (en) Method for improving tenacity and loading of palladium on palladium-doped metal surfaces
US6697449B2 (en) Temperature-based method for controlling the amount of metal applied to metal oxide surfaces to reduce corrosion and stress corrosion cracking
US20020101953A1 (en) Application of noble metals to internal surfaces of operating boiling water reactors in the presence of zinc in reactor water
EP0651397B1 (fr) Dopage ou revêtement sur place de surfaces en acier inox avec palladium
US20020118787A1 (en) Noble metal catalysis for mitigation of corrosion, erosion and stress corrosion cracking in pressurized water reactor and related high temperature water environments
EP1036218B1 (fr) Technique fondee sur la temperature permettant de regler la dose de metal appliquee sur des surfaces d'oxyde metallique pour reduire la corrosion et les fissurations par corrosion sous contrainte
EP1075695A1 (fr) Application de metaux nobles sur les surfaces internes de reacteurs a eau bouillante en conditions de marche, en presence de zinc dans l'eau de reacteur
MXPA00005257A (en) Temperature based method for controlling the amount of metal applied to metal oxide surfaces to reduce corrosion and stress corrosion cracking

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): BG BR CA CN CZ HU JP KR MX RO ZA

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE

121 Ep: the epo has been informed by wipo that ep was designated in this application
ENP Entry into the national phase

Ref document number: 2333072

Country of ref document: CA

WWE Wipo information: entry into national phase

Ref document number: 1999970499

Country of ref document: EP

WWE Wipo information: entry into national phase

Ref document number: 2000/07228

Country of ref document: ZA

Ref document number: 200007228

Country of ref document: ZA

WWE Wipo information: entry into national phase

Ref document number: PV2000-4662

Country of ref document: CZ

WWP Wipo information: published in national office

Ref document number: 1999970499

Country of ref document: EP

WWP Wipo information: published in national office

Ref document number: PV2000-4662

Country of ref document: CZ