WO2000011092A1 - Selective deposition modeling material - Google Patents
Selective deposition modeling material Download PDFInfo
- Publication number
- WO2000011092A1 WO2000011092A1 PCT/EP1999/005788 EP9905788W WO0011092A1 WO 2000011092 A1 WO2000011092 A1 WO 2000011092A1 EP 9905788 W EP9905788 W EP 9905788W WO 0011092 A1 WO0011092 A1 WO 0011092A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- weight
- modeling material
- modeling
- plasticizing
- base material
- Prior art date
Abstract
Description
Claims