WO2000008655A1 - Cable electrique pour courant continu avec systeme isolant comprenant une composition en polyethylene extrude et son procede de fabrication - Google Patents

Cable electrique pour courant continu avec systeme isolant comprenant une composition en polyethylene extrude et son procede de fabrication Download PDF

Info

Publication number
WO2000008655A1
WO2000008655A1 PCT/SE1999/001335 SE9901335W WO0008655A1 WO 2000008655 A1 WO2000008655 A1 WO 2000008655A1 SE 9901335 W SE9901335 W SE 9901335W WO 0008655 A1 WO0008655 A1 WO 0008655A1
Authority
WO
WIPO (PCT)
Prior art keywords
composition
cable
compound
insulation
formula
Prior art date
Application number
PCT/SE1999/001335
Other languages
English (en)
Inventor
Bill Gustafsson
Jan-Ove BOSTRÖM
Ulf Nilsson
Perry Nylander
Peter Carstensen
Andreas Farkas
Anders Gustafsson
Kenneth Johannesson
Original Assignee
Abb Ab
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Abb Ab filed Critical Abb Ab
Priority to AU55415/99A priority Critical patent/AU760355B2/en
Priority to CA002339541A priority patent/CA2339541A1/fr
Priority to KR1020017001528A priority patent/KR20010072260A/ko
Priority to JP2000564209A priority patent/JP2002522875A/ja
Priority to MXPA01001363A priority patent/MXPA01001363A/es
Priority to EP99941942A priority patent/EP1103052A1/fr
Publication of WO2000008655A1 publication Critical patent/WO2000008655A1/fr
Priority to NO20010592A priority patent/NO20010592L/no

Abstract

La présente invention concerne un câble électrique pour courant continu avec système isolant comprenant une composition en polyéthylène, t le procédé de fabrication y relatif. Le système isolant comprend une gaine isolante à base de polyéthylène réticulé obtenue par extrusion. En plus du composé à base de polyéthylène, la gaine obtenue par extrusion renferme un additif sous forme d'ester d'acide gras de glycérol représenté par la formule générale (I): R1O(C3H5(OR2)O)nR3. Selon cette formule, n est supérieur ou égal à n≥1, R?1, R2 et R3¿, qui sont identiques ou différents, désignent l'hydrogène ou le résidu d'acide carboxylique avec 8-24 atomes de carbone, à condition qu'il y ait au moins deux groupes OH libres et au moins un résidu d'acide carboxylique avec 8-24 atomes de carbone dans la molécule. La composition à base de polyéthylène utilisée pour la fabrication de ce câble est extrudée et soumise à une température suffisante pendant un laps de temps suffisant pour déclencher une réaction de réticulation.
PCT/SE1999/001335 1998-08-06 1999-08-04 Cable electrique pour courant continu avec systeme isolant comprenant une composition en polyethylene extrude et son procede de fabrication WO2000008655A1 (fr)

Priority Applications (7)

Application Number Priority Date Filing Date Title
AU55415/99A AU760355B2 (en) 1998-08-06 1999-08-04 An electric dc-cable with an insulation system comprising an extruded polyethylene composition and a method for manufacturing such cable
CA002339541A CA2339541A1 (fr) 1998-08-06 1999-08-04 Cable electrique pour courant continu avec systeme isolant comprenant une composition en polyethylene extrude et son procede de fabrication
KR1020017001528A KR20010072260A (ko) 1998-08-06 1999-08-04 압출된 폴리에틸렌 조성물을 포함하는 절연 시스템을구비한 직류 케이블과 그러한 케이블의 제조방법
JP2000564209A JP2002522875A (ja) 1998-08-06 1999-08-04 押し出し加工によるポリエチレン混合物からなる絶縁被覆を有する直流電力ケーブルとその製造方法
MXPA01001363A MXPA01001363A (es) 1998-08-06 1999-08-04 Un cable electrico de corriente directa (dc) con un sistema de aislamiento que comprende una composicion de polietileno extruido y un metodo para la fabricacion de tal cable.
EP99941942A EP1103052A1 (fr) 1998-08-06 1999-08-04 Cable electrique pour courant continu avec systeme isolant comprenant une composition en polyethylene extrude et son procede de fabrication
NO20010592A NO20010592L (no) 1998-08-06 2001-02-05 Elektrisk likestromskabel med isolasjonssystem omfattende ekstrudert polyetylenmateriale, og fremgangsmate for fremstilling av kabelen

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
SE9802681-8 1998-08-06
SE9802681A SE512745C2 (sv) 1998-08-06 1998-08-06 Elektrisk DC-kabel med isoleringssystem omfattande en strängsprutad polyetenkomposition och en metod för framställning av sådan kabel

Publications (1)

Publication Number Publication Date
WO2000008655A1 true WO2000008655A1 (fr) 2000-02-17

Family

ID=20412208

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/SE1999/001335 WO2000008655A1 (fr) 1998-08-06 1999-08-04 Cable electrique pour courant continu avec systeme isolant comprenant une composition en polyethylene extrude et son procede de fabrication

Country Status (11)

Country Link
EP (1) EP1103052A1 (fr)
JP (1) JP2002522875A (fr)
KR (1) KR20010072260A (fr)
CN (1) CN1322362A (fr)
AR (1) AR019993A1 (fr)
AU (1) AU760355B2 (fr)
CA (1) CA2339541A1 (fr)
MX (1) MXPA01001363A (fr)
NO (1) NO20010592L (fr)
SE (1) SE512745C2 (fr)
WO (1) WO2000008655A1 (fr)

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6903263B2 (en) 2000-12-27 2005-06-07 Pirelli, S.P.A. Electrical cable, particularly for high voltage direct current transmission or distribution, and insulating composition
US8257782B2 (en) 2000-08-02 2012-09-04 Prysmian Cavi E Sistemi Energia S.R.L. Electrical cable for high voltage direct current transmission, and insulating composition
US9058918B2 (en) 2008-06-05 2015-06-16 Union Carbide Chemicals & Plastics Technology Llc Method for producing water tree-resistant, TRXLPE-type cable sheath
WO2015090644A1 (fr) * 2013-12-19 2015-06-25 Abb Technology Ltd Procédé pour fournir un câble électrique haute tension isolé
WO2016131478A1 (fr) * 2015-02-18 2016-08-25 Abb Technology Ltd Câble d'alimentation électrique et procédé de production de câble d'alimentation électrique
WO2018090940A1 (fr) * 2016-11-16 2018-05-24 Dow Global Technologies Llc Composition présentant un bon équilibre entre facteur de dissipation et acceptation d'additif

Families Citing this family (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20020188867A1 (en) * 2001-06-08 2002-12-12 Bushey Robert D. System and method for appliance adaptation and evolution
WO2005015577A1 (fr) * 2003-07-25 2005-02-17 Pirelli & C. S.P.A. Procede continu de fabrication de cables electriques
US8217105B2 (en) * 2006-10-16 2012-07-10 Basf Se Stabilized medium and high voltage insulation composition
CN102231295A (zh) * 2011-04-20 2011-11-02 大连沈特电缆有限公司 铜包铝芯聚乙烯绝缘直流高压电缆
EP3142206B1 (fr) * 2015-09-11 2018-05-23 ABB Schweiz AG Isolateur haute tension/tension continue destine a isoler un conducteur alimente en tension continue et procede de fabrication correspondant
US10703496B2 (en) 2017-04-21 2020-07-07 General Electric Company Propulsion system for an aircraft
CN109180969B (zh) * 2018-07-06 2020-11-10 三峡大学 外电场下盐交联聚乙烯分子结构及分析外电场下盐交联聚乙烯分子结构构建的方法
CN115651105B (zh) * 2022-10-25 2023-08-18 哈尔滨理工大学 一种接枝改性型交联聚乙烯抗水树绝缘料及其制备方法和应用

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB2079521A (en) * 1980-06-30 1982-01-20 Pirelli Cavi Spa Overhead electrical cable
GB2120449A (en) * 1982-05-11 1983-11-30 Standard Telephones Cables Ltd Power cables

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB2079521A (en) * 1980-06-30 1982-01-20 Pirelli Cavi Spa Overhead electrical cable
GB2120449A (en) * 1982-05-11 1983-11-30 Standard Telephones Cables Ltd Power cables

Cited By (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US8257782B2 (en) 2000-08-02 2012-09-04 Prysmian Cavi E Sistemi Energia S.R.L. Electrical cable for high voltage direct current transmission, and insulating composition
US6903263B2 (en) 2000-12-27 2005-06-07 Pirelli, S.P.A. Electrical cable, particularly for high voltage direct current transmission or distribution, and insulating composition
US9058918B2 (en) 2008-06-05 2015-06-16 Union Carbide Chemicals & Plastics Technology Llc Method for producing water tree-resistant, TRXLPE-type cable sheath
WO2015090644A1 (fr) * 2013-12-19 2015-06-25 Abb Technology Ltd Procédé pour fournir un câble électrique haute tension isolé
WO2016131478A1 (fr) * 2015-02-18 2016-08-25 Abb Technology Ltd Câble d'alimentation électrique et procédé de production de câble d'alimentation électrique
WO2018090940A1 (fr) * 2016-11-16 2018-05-24 Dow Global Technologies Llc Composition présentant un bon équilibre entre facteur de dissipation et acceptation d'additif
US20190270870A1 (en) * 2016-11-16 2019-09-05 Dow Global Technologies Llc Composition with Balance of Dissipation Factor and Additive Acceptance
US10793707B2 (en) 2016-11-16 2020-10-06 Dow Global Technologies Llc Composition with balance of dissipation factor and additive acceptance

Also Published As

Publication number Publication date
SE512745C2 (sv) 2000-05-08
NO20010592L (no) 2001-02-22
KR20010072260A (ko) 2001-07-31
AR019993A1 (es) 2002-03-27
AU5541599A (en) 2000-02-28
SE9802681L (sv) 2000-02-07
AU760355B2 (en) 2003-05-15
NO20010592D0 (no) 2001-02-05
SE9802681D0 (sv) 1998-08-06
EP1103052A1 (fr) 2001-05-30
CA2339541A1 (fr) 2000-02-17
CN1322362A (zh) 2001-11-14
MXPA01001363A (es) 2002-04-24
JP2002522875A (ja) 2002-07-23

Similar Documents

Publication Publication Date Title
AU760355B2 (en) An electric dc-cable with an insulation system comprising an extruded polyethylene composition and a method for manufacturing such cable
US7767741B2 (en) Semiconductive polymer compositions
US20120227997A1 (en) Medium-or high-voltage electric cable
EP1057191B1 (fr) Cable electrique de courant continu
EP1046177B1 (fr) Cable electrique pour courant continu dote d'un systeme d'isolation
KR20100095201A (ko) 유연성과 가교 특성이 뛰어난 전선용 절연 재료 및 이를 갖춘 전선
US20020039654A1 (en) Electric DC-cable with an insulation system
EA018317B1 (ru) Кабель низкого, среднего или высокого напряжения, включающий сшиваемую полиолефиновую композицию, содержащую дикарбоксилат дигидрокарбилолова в качестве катализатора силанольной конденсации
EP3013896A1 (fr) Compositions polymères stabilisées en tension
WO1999040589A1 (fr) Procede de production d'un cable
KR20200078402A (ko) 용이하게 박리가능한 반도전층을 포함하는 케이블
JP7380804B1 (ja) 樹脂組成物、ペレット、電力ケーブル、および電力ケーブルの製造方法
KR100291668B1 (ko) 고압 케이블용 반도전 재료
MXPA00007989A (en) An electric direct current cable
KR20230103829A (ko) 케이블용 절연 조성물 및 이로부터 형성된 절연층을 포함하는 케이블

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 99811805.2

Country of ref document: CN

AK Designated states

Kind code of ref document: A1

Designated state(s): AE AL AM AT AT AU AZ BA BB BG BR BY CA CH CN CR CU CZ CZ DE DE DK DK EE EE ES FI FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MD MG MK MN MW MX NO NZ PL PT RO RU SD SE SG SI SK SK SL TJ TM TR TT UA UG US UZ VN YU ZA ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH GM KE LS MW SD SL SZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
WWE Wipo information: entry into national phase

Ref document number: 55415/99

Country of ref document: AU

ENP Entry into the national phase

Ref document number: 2339541

Country of ref document: CA

Ref document number: 2339541

Country of ref document: CA

Kind code of ref document: A

WWE Wipo information: entry into national phase

Ref document number: 2001/00973

Country of ref document: ZA

Ref document number: 200100973

Country of ref document: ZA

Ref document number: 1020017001528

Country of ref document: KR

WWE Wipo information: entry into national phase

Ref document number: PA/a/2001/001363

Country of ref document: MX

Ref document number: IN/PCT/2001/00104/DE

Country of ref document: IN

WWE Wipo information: entry into national phase

Ref document number: 1999941942

Country of ref document: EP

WWE Wipo information: entry into national phase

Ref document number: 09744938

Country of ref document: US

WWP Wipo information: published in national office

Ref document number: 1999941942

Country of ref document: EP

REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

WWP Wipo information: published in national office

Ref document number: 1020017001528

Country of ref document: KR

WWG Wipo information: grant in national office

Ref document number: 55415/99

Country of ref document: AU

WWW Wipo information: withdrawn in national office

Ref document number: 1020017001528

Country of ref document: KR

WWW Wipo information: withdrawn in national office

Ref document number: 1999941942

Country of ref document: EP