WO1999060026A1 - Cellulosic solutions and their uses - Google Patents
Cellulosic solutions and their uses Download PDFInfo
- Publication number
- WO1999060026A1 WO1999060026A1 PCT/GB1999/001566 GB9901566W WO9960026A1 WO 1999060026 A1 WO1999060026 A1 WO 1999060026A1 GB 9901566 W GB9901566 W GB 9901566W WO 9960026 A1 WO9960026 A1 WO 9960026A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- cellulose
- solution
- solvent
- oxide
- solutions
- Prior art date
Abstract
Description
Claims