WO1999040043A1 - Partially densified carbon preform - Google Patents
Partially densified carbon preform Download PDFInfo
- Publication number
- WO1999040043A1 WO1999040043A1 PCT/US1999/000850 US9900850W WO9940043A1 WO 1999040043 A1 WO1999040043 A1 WO 1999040043A1 US 9900850 W US9900850 W US 9900850W WO 9940043 A1 WO9940043 A1 WO 9940043A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- preform
- densified
- precursor liquid
- decomposition product
- precursor
- Prior art date
Abstract
Description
Claims