WO1999029920A1 - Multilayered pvd coated cutting tool - Google Patents
Multilayered pvd coated cutting tool Download PDFInfo
- Publication number
- WO1999029920A1 WO1999029920A1 PCT/SE1998/002268 SE9802268W WO9929920A1 WO 1999029920 A1 WO1999029920 A1 WO 1999029920A1 SE 9802268 W SE9802268 W SE 9802268W WO 9929920 A1 WO9929920 A1 WO 9929920A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- mlx
- cutting tool
- coating
- tool according
- metal
- Prior art date
Abstract
Description
Claims