WO1999000235A1 - Composites lies par moulage et leur procede de fabrication - Google Patents

Composites lies par moulage et leur procede de fabrication Download PDF

Info

Publication number
WO1999000235A1
WO1999000235A1 PCT/US1998/012118 US9812118W WO9900235A1 WO 1999000235 A1 WO1999000235 A1 WO 1999000235A1 US 9812118 W US9812118 W US 9812118W WO 9900235 A1 WO9900235 A1 WO 9900235A1
Authority
WO
WIPO (PCT)
Prior art keywords
metal
stone
particles
resin matrix
resin
Prior art date
Application number
PCT/US1998/012118
Other languages
English (en)
Inventor
Roger Questel
Brent Merriam
David Pelletier
Original Assignee
Questech Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Questech Corporation filed Critical Questech Corporation
Priority to AU78360/98A priority Critical patent/AU7836098A/en
Publication of WO1999000235A1 publication Critical patent/WO1999000235A1/fr

Abstract

L'invention concerne un composite décoratif et/ou architectural fabriqué à partir d'une matrice de résine (22) liée à un substrat (24). La matrice comprend essentiellement une résine liquide durcissable, des particules de métal ou de roche, et un catalyseur. Le composite a l'apparence du métal ou de la roche et peut être utilisé comme un panneau contreplaqué, un panneau de particules ou un autre panneau de construction. L'invention concerne également un procédé pour la fabrication de ce type de composite.
PCT/US1998/012118 1997-06-26 1998-06-10 Composites lies par moulage et leur procede de fabrication WO1999000235A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
AU78360/98A AU7836098A (en) 1997-06-26 1998-06-10 In mold bonded composites and a method for manufacturing the composites

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US88287497A 1997-06-26 1997-06-26
US08/882,874 1997-06-26

Publications (1)

Publication Number Publication Date
WO1999000235A1 true WO1999000235A1 (fr) 1999-01-07

Family

ID=25381519

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US1998/012118 WO1999000235A1 (fr) 1997-06-26 1998-06-10 Composites lies par moulage et leur procede de fabrication

Country Status (2)

Country Link
AU (1) AU7836098A (fr)
WO (1) WO1999000235A1 (fr)

Cited By (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1319525A2 (fr) * 2001-12-12 2003-06-18 Totalstone, S.A. Reproductions murals
US6650706B2 (en) 2000-01-14 2003-11-18 Koninklijke Philips Electronics N.V. Frequential-based data modifying method and device
EP1364812A1 (fr) * 2002-05-20 2003-11-26 Demak S.r.l. Fabrication d'un article décorative comprenant un substrat laminaire avec un revêtement à base de résine
ES2222067A1 (es) * 2001-09-10 2005-01-16 Dada 2000, S.L. Mejoras introducidas en la patente de invencion num. p-200102034/1, por: baldosa para construccion.
ES2244318A1 (es) * 2004-03-10 2005-12-01 Jose Antonio Asumendi Garcia Uso de una resina para la obtencion de paneles de construccion.
EP1667840A1 (fr) * 2003-08-28 2006-06-14 Surfaces Techniboard Inc. Lamine de type pierre
WO2007141359A1 (fr) * 2006-06-07 2007-12-13 Pablo Peris Dominguez Procédé de fabrication de pièces décoratives ou fonctionnelles pour le revêtement de surfaces et pièce ainsi obtenue
ES2535549A1 (es) * 2015-02-17 2015-05-12 David Roberto SOMLO MORENO Material polimérico ornamental, y método para su obtención
NL2017681B1 (en) * 2016-10-27 2018-05-18 Texture Painting Bvba Decorative panel
WO2020163540A1 (fr) * 2019-02-08 2020-08-13 ByDesign, LLC Procédés, systèmes et dispositifs de revêtement décoratif
CN114230263A (zh) * 2022-02-23 2022-03-25 北京慕湖外加剂有限公司 一种纤维水泥板及其制备方法

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB1159801A (en) * 1965-06-02 1969-07-30 Colin Bruce Thrush Improved Decorative Ware.
US3615963A (en) * 1968-01-19 1971-10-26 Cebem Ab Panels from settled particles liquid binder and absorbent layer

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB1159801A (en) * 1965-06-02 1969-07-30 Colin Bruce Thrush Improved Decorative Ware.
US3615963A (en) * 1968-01-19 1971-10-26 Cebem Ab Panels from settled particles liquid binder and absorbent layer

Cited By (16)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6650706B2 (en) 2000-01-14 2003-11-18 Koninklijke Philips Electronics N.V. Frequential-based data modifying method and device
ES2222067A1 (es) * 2001-09-10 2005-01-16 Dada 2000, S.L. Mejoras introducidas en la patente de invencion num. p-200102034/1, por: baldosa para construccion.
EP1319525A3 (fr) * 2001-12-12 2003-09-17 Totalstone, S.A. Reproductions murals
ES2211262A1 (es) * 2001-12-12 2004-07-01 Totalstone, S.A. Procedimiento para la obtencion de reproducciones murales y arquitectonicas, y producto resultante.
EP1319525A2 (fr) * 2001-12-12 2003-06-18 Totalstone, S.A. Reproductions murals
EP1364812A1 (fr) * 2002-05-20 2003-11-26 Demak S.r.l. Fabrication d'un article décorative comprenant un substrat laminaire avec un revêtement à base de résine
EP1667840A4 (fr) * 2003-08-28 2010-10-13 Surfaces Techniboard Inc Lamine de type pierre
EP1667840A1 (fr) * 2003-08-28 2006-06-14 Surfaces Techniboard Inc. Lamine de type pierre
ES2244318A1 (es) * 2004-03-10 2005-12-01 Jose Antonio Asumendi Garcia Uso de una resina para la obtencion de paneles de construccion.
WO2007141359A1 (fr) * 2006-06-07 2007-12-13 Pablo Peris Dominguez Procédé de fabrication de pièces décoratives ou fonctionnelles pour le revêtement de surfaces et pièce ainsi obtenue
ES2293830A1 (es) * 2006-06-07 2008-03-16 Pablo Peris Dominguez Procedimiento para la fabricacion de piezas decorativas o funcionales para el recubrimiento de superficies y la pieza asi obtenida.
ES2535549A1 (es) * 2015-02-17 2015-05-12 David Roberto SOMLO MORENO Material polimérico ornamental, y método para su obtención
NL2017681B1 (en) * 2016-10-27 2018-05-18 Texture Painting Bvba Decorative panel
WO2020163540A1 (fr) * 2019-02-08 2020-08-13 ByDesign, LLC Procédés, systèmes et dispositifs de revêtement décoratif
CN114230263A (zh) * 2022-02-23 2022-03-25 北京慕湖外加剂有限公司 一种纤维水泥板及其制备方法
CN114230263B (zh) * 2022-02-23 2022-06-21 揭阳市好夫曼建材有限公司 一种纤维水泥板及其制备方法

Also Published As

Publication number Publication date
AU7836098A (en) 1999-01-19

Similar Documents

Publication Publication Date Title
US5177124A (en) Plastic molded pieces having the appearance of a solid metallic piece
US5364672A (en) Artificial stones
US5885503A (en) Mold process for producing a finished solid surface countertop
US4956030A (en) Method of fabricating simulated stone surfaces and improved simulated stone products
US4952462A (en) Decorative panels and methods of making the same
EP0356148A2 (fr) Imitation de surfaces de pierre
US5628949A (en) Mold process for producing a finished solid surface countertop
US6403004B1 (en) Process for making a multi-layered solid surface article
US5789032A (en) Moldless coated board
KR100246937B1 (ko) 폴리에스테르 백킹 아크릴계 복합체 성형구조물 및 그 제조방법
US5342565A (en) Method for manufacturing simulated granite
WO2004058491A1 (fr) Materiau composite et processus de moulage d'une table de toilette ou d'un revetement de comptoir
WO1999000235A1 (fr) Composites lies par moulage et leur procede de fabrication
US20040194421A1 (en) Process for carrying out panels, tiles and the like using agglomerates of different minerals
WO2002040237A1 (fr) Procedes et materiaux destines a la fabrication d'un article a surface solide
WO1999018150A1 (fr) Composites fins lies dans le moule et procede de fabrication
JPH05507032A (ja) ポリエステル裏当てされたアクリル複合成形構造
Bera et al. Recent developments in synthetic marble processing
KR100295340B1 (ko) 열경화성수지및무기충전물로만든조립식욕실용벽파넬및그제조방법
US20040161546A1 (en) Method Of Making A Stone Veneer
US3419454A (en) Method of making and reinforcing decorative polyester resin products
US20020041937A1 (en) Stone veneer
RU2326008C1 (ru) Способ нанесения декоративного покрытия и декоративное изделие (варианты)
EP4303256A1 (fr) Matériau composite avec couche de revêtement
CA2000535C (fr) Methode de fabrication de surfaces de simili-pierre et produit de simili-pierre ameliore

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AL AM AT AU AZ BA BB BG BR BY CA CH CN CU CZ DE DK EE ES FI GB GE GH GM GW HU ID IL IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MD MG MK MN MW MX NO NZ PL PT RO RU SD SE SG SI SK SL TJ TM TR TT UA UG UZ VN YU ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH GM KE LS MW SD SZ UG ZW AM AZ BY KG KZ MD RU TJ TM AT BE CH CY DE DK ES FI FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN ML MR NE SN TD TG

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
121 Ep: the epo has been informed by wipo that ep was designated in this application
NENP Non-entry into the national phase

Ref country code: JP

Ref document number: 1999505565

Format of ref document f/p: F

REG Reference to national code

Ref country code: DE

Ref legal event code: 8642

122 Ep: pct application non-entry in european phase
NENP Non-entry into the national phase

Ref country code: CA