WO1998037143A1 - Corona discharge treated films having excellent coefficients of friction - Google Patents
Corona discharge treated films having excellent coefficients of friction Download PDFInfo
- Publication number
- WO1998037143A1 WO1998037143A1 PCT/US1998/003602 US9803602W WO9837143A1 WO 1998037143 A1 WO1998037143 A1 WO 1998037143A1 US 9803602 W US9803602 W US 9803602W WO 9837143 A1 WO9837143 A1 WO 9837143A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- film
- mpe
- ethylene
- friction
- layer
- Prior art date
Abstract
Description
Claims