JPH09150488A - Laminated film - Google Patents

Laminated film

Info

Publication number
JPH09150488A
JPH09150488A JP31043595A JP31043595A JPH09150488A JP H09150488 A JPH09150488 A JP H09150488A JP 31043595 A JP31043595 A JP 31043595A JP 31043595 A JP31043595 A JP 31043595A JP H09150488 A JPH09150488 A JP H09150488A
Authority
JP
Grant status
Application
Patent type
Prior art keywords
propylene
film
monomer unit
unit based
random copolymer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP31043595A
Other languages
Japanese (ja)
Inventor
Koji Hirata
Takeshi Nakagawa
Yuzo Sugita
毅 中川
浩二 平田
裕三 杉田
Original Assignee
Tokuyama Corp
株式会社トクヤマ
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date

Abstract

PROBLEM TO BE SOLVED: To provide a heat seal film excellent in peelability, heat sealability, slip properties and opening properties. SOLUTION: An intermediate layer (A) composed of a propylene type block copolymer with wt. average mol.wt. (Mw)/number average mol.wt. (Mn) of 1-4 consisting of 1-70wt.% of a propylene random copolymer component (a) containing 90mol% or more of a propylene homopolymer component or a monomer unit based on propylene, and 30-99wt.% of a propylene/ethylene random copolymer component containing 10-40mol% of a monomer unit based on ethylene and 90-60mol% of a monomer unit based on propylene is laminated to at least one surface of a base material film, and further an outer surface layer (B) composed of a propylene type random copolymer containing 88-99mol% of polyethylene with density of 0.91-0.95 and/or a monomer unit based on propylene is laminated on the intermediate layer.

Description

【発明の詳細な説明】 DETAILED DESCRIPTION OF THE INVENTION

【0001】 [0001]

【発明の属する技術分野】本発明は、積層フィルム、詳しくはヒートシールフィルムとして好適な積層フィルムに関する。 The present invention relates to a laminated film, more particularly preferred multilayer film as a heat seal film.

【0002】 [0002]

【従来の技術】物品をフィルムで包装して密封する際、 BACKGROUND OF THE INVENTION when sealed in packaging an article in a film,
フィルムの包装片同士をヒートシールすることが行われている。 Packaging piece together the film be heat-sealing has been carried out. その際、フィルムとして、ポリプロピレン、ポリエチレンのようなポリオレフィン系の熱可塑性樹脂からなるヒートシール層を基材フィルムの表面に積層したものを使用することが知られている。 At that time, as a film, a polypropylene, it is known to use a material obtained by laminating a heat sealing layer comprising a polyolefin-based thermoplastic resin such as polyethylene to the surface of the base film.

【0003】 [0003]

【発明が解決しようとする課題】ところで、こうしたヒートシールによる包装では、かかるヒートシールされた包装片同士の結合部が、包装体の開封時に手で容易に開封できる程度の適度な強度を有することが要求される。 [SUMMARY OF THE INVENTION Incidentally, in the packaging by such heat sealing bond of the package pieces between which is such heat sealing, to have an appropriate strength that can easily be opened by hand when opening of the package There is required.

【0004】また、この包装体の開封時に該結合部が良好な可剥性を有することが要求される。 Further, the coupling portion upon opening of the package is required to have a good strippability. 即ち、前記ポリオレフィン系の熱可塑性樹脂からなるヒートシール層を有する積層フィルムでは、通常、この結合部を引き剥そうとすると、糸引きや毛羽立ちが生じ易いのと同時に、 That is, in the laminated film having a heat sealing layer comprising a thermoplastic resin in the polyolefin, usually, when you Hagaso pull the coupling portion, as easily stringing and scuffing occur simultaneously,
溶着する包装片同士の界面やヒートシール層の内部でスムーズな剥離が生じず、結合部は元の包装片同士に再び分離することなく、該結合部の途中で包装片のいずれか一方の厚み方向に基材フィルム層が引き裂かれてしまう。 Not smooth peeling occurs inside the interface and the heat seal layer of the packaging strip between the welding coupling section without again separated into each other original packaging strip, one of the thickness of the packaging strip in the middle of the coupling portion base film layer resulting in torn direction. こうした現象は、開封時の物品に対する外観不良につながり、その物品の商品価値を低下させる。 This phenomenon leads to a poor appearance to an article at the time of opening, reducing the commercial value of the article. また、この引き裂かれ部分が起点となって、開封の途中で、フィルムが大きく破断し、内容物が落下する等の危険性もあった。 Also, the torn portion becomes a starting point, in the middle of the opening, the film is broken large content had also danger of falling.

【0005】こうしたことから、上記欠点を解消し、可剥性、ヒートシール性、開封性に優れたヒートシールフィルムを開発することが望まれていた。 [0005] For these reasons, to solve the above drawbacks, peelable, heat-sealable, it has been desired to develop a heat-sealing film excellent in openability.

【0006】以上の背景にあって本発明者らは、上記課題を解決するために特定の組成のブロック共重合体、即ち、a)プロピレン単独重合体成分、またはプロピレンに基づく単量体単位を90モル%より多く含むプロピレン系ランダム共重合体成分1〜70重量%、 b)エチレンに基づく単量体単位を10〜40モル%、 [0006] or more In the background the present inventors have found that a block copolymer of a specific composition in order to solve the above problems, i.e., a) a propylene homopolymer component or monomer unit based on propylene, 90 mol% more include propylene random copolymer component 1-70 weight%, b) a monomer unit based on ethylene 10-40 mol%,
プロピレンに基づく単量体単位を90〜60モル%含むプロピレン−エチレンランダム共重合体成分30〜99 Propylene containing a monomer unit based on propylene 90-60 mol% - ethylene random copolymer component 30-99
重量%よりなり、重量平均分子量(Mw)/数平均分子量(Mn)が1〜4であるプロピレン系ブロック共重合体よりなる樹脂層が、少なくとも一方のフィルム表面に積層されてなる積層ヒートシールフィルムを提案した(特願平7−52983号)。 Consists wt%, the weight-average molecular weight (Mw) / number average molecular weight (Mn) consisting of propylene block copolymer is a 1-4 resin layer is laminated heat seal film obtained by laminating on at least one surface of the film It was proposed (Japanese Patent Application No. 7-52983).

【0007】この積層ヒートシールフィルムは、可剥性、ヒートシール性に優れる他、ヒートシール後熱融着された結合部を引き剥す際に、両フィルムがその界面や表面層部分で良好に剥離する、極めて優れた包装フィルムである。 [0007] The laminated heat-sealing film, in addition to excellent peelable, heat-sealable, when peeled off the coupling portion that is thermally fused after heat sealing, good peeling both films at the interface and the surface layer portion to, is a very excellent packaging film.

【0008】ところが、自動包装等の機械走行性を勘案すると、フィルムの滑り性に多少の改良の余地があった。 [0008] However, when taking into account the machine running properties such as automatic packaging, there is room for some improvement in the sliding property of the film. この問題を解決するために、プロピレン系ブロック共重合体中にアンチブロッキング剤や滑剤等を比較的多量に添加すると、滑り性は向上するものの、例えば、基材層のフィルムが透明性の良好なものである場合において積層ヒートシールフィルムの透明性が低下する等の弊害が生じてくる。 To solve this problem, when a relatively large amount of added antiblocking agent or lubricant or the like during the propylene block copolymer, although the slip properties improved, for example, good film of the substrate layer is transparent transparency of the laminated heat seal film comes cause adverse effects such as a decrease in the case is intended.

【0009】以上の背景にあって本発明は、良好な滑り性を有し、可剥性、ヒートシール性、に優れた積層フィルムを提供することを目的とする。 [0009] In the above background the present invention has a good sliding property, and to provide peelable, heat-sealable, excellent laminated films.

【0010】 [0010]

【課題を解決するための手段】本発明者らは、上記の課題を解決すべく鋭意研究を重ねてきた。 Means for Solving the Problems The present inventors have conducted extensive studies to solve the above problems. その結果、特定の組成のブロック共重合体からなる中間層とポリエチレン、及び/または特定の組成のプロピレン系ランダム共重合体からなる外表面層とを使用することで上記課題が解決できることを見い出し、本発明を完成するに至った。 As a result, we found that can solve the above problem by using an outer surface layer consisting of the intermediate layer and polyethylene, and / or propylene-based random copolymer of a specific composition of a block copolymer of specific composition, this has led to the completion of the present invention.

【0011】即ち、本発明は、基材フィルムの少なくとも一方の表面に、 A)a)プロピレン単独重合体成分、またはプロピレンに基づく単量体単位を90モル%より多く含むプロピレン系ランダム共重合体成分1〜70重量%、 b)エチレンに基づく単量体単位を10〜40モル%、 [0011] Namely, the present invention is at least one surface of the base film, A) a) a propylene homopolymer component or a propylene random copolymer the monomer unit based on propylene containing more than 90 mol%, components 1 to 70 wt%, b) a monomer unit based on ethylene 10-40 mol%,
プロピレンに基づく単量体単位を90〜60モル%含むプロピレン−エチレンランダム共重合体成分30〜99 Propylene containing a monomer unit based on propylene 90-60 mol% - ethylene random copolymer component 30-99
重量%よりなり、重量平均分子量(Mw)/数平均分子量(Mn)が1〜4であるプロピレン系ブロック共重合体よりなる中間層が積層されてなり、さらに、該中間層の表面に、 B)密度が0.91〜0.95であるポリエチレン、及び/またはプロピレンに基づく単量体単位を88〜99 Consists wt%, the in weight average molecular weight (Mw) / number average molecular weight (Mn) consisting of propylene block copolymer is from 1 to 4 the intermediate layer are stacked and further, the surface of the intermediate layer, B ) polyethylene density of 0.91 to 0.95, and / or a monomer unit based on propylene 88-99
モル%含むプロピレン系ランダム共重合体からなる外表面層が積層されてなる積層フィルムである。 The outer surface layer comprising a propylene random copolymer containing mol% is a laminated film obtained by laminating.

【0012】本発明で中間層に使用するプロピレン系ブロック共重合体は、a)プロピレン単独重合体成分、またはプロピレンに基づく単量体単位を90モル%より多く含むプロピレン系ランダム共重合体成分と、b)エチレンに基づく単量体単位を10〜40モル%、プロピレンに基づく単量体単位を90〜60モル%含むプロピレン−エチレンランダム共重合体成分とを含んでいる。 [0012] The propylene block copolymer used in the intermediate layer in the present invention, a) a propylene homopolymer component or a propylene random copolymer component a monomer unit based on propylene containing more than 90 mol%, , b) 10 to 40 mole% of monomer units derived from ethylene, propylene containing a monomer unit based on propylene 90-60 mol% - and an ethylene random copolymer component. ここで、上記a)プロピレン単独重合体成分、またはプロピレン系ランダム共重合体成分とb)プロピレン−エチレンランダム共重合体成分の成分割合は、前者が1〜7 Here, the a) a propylene homopolymer component or a propylene random copolymer component and b) propylene, - component ratio of ethylene random copolymer component, the former is 1-7
0重量%好適には3〜60重量%、後者が30〜99重量%好適には40〜97重量%である。 0 wt% preferably 3-60 wt%, the latter preferably from 30 to 99% by weight is 40 to 97 wt%. このa)プロピレン単独重合体成分、またはプロピレン系ランダム共重合体成分が1重量%よりも少ないと、得られるヒートシールフィルムの機械的強度が低下し、また、70重量% When the a) a propylene homopolymer component or a propylene random copolymer component, is less than 1 wt%, the mechanical strength of the resulting heat-sealing film is lowered, also 70 wt%
を越えると、得られるヒートシールフィルムの可剥性、 By weight, peelable obtained heat-sealing film,
ヒートシール性、透明性が低下するために好ましくない。 Heat sealability, transparency is not preferable to decrease.

【0013】a)のプロピレン系ランダム共重合体成分における、プロピレンに基づく単量体単位以外の単量体単位としては、プロピレンと共重合可能な他の公知の単量体に基づく単位が制限なく採用できる。 [0013] in the propylene random copolymer component of a), as a monomer unit other than the monomer unit based on propylene, propylene can be copolymerized with other known units based on monomer without limitation It can be adopted. 好適には、エチレンおよび炭素数が4〜12のα−オレフィンに基づく単量体単位が挙げられ、これらは1種または2種以上を組み合わせて採用しても良い。 Preferably, ethylene and carbon atoms include monomer unit based on 4-12 α- olefins, these may be employed alone or in combination of two or more kinds. 特に、エチレンおよび炭素数4〜8のα−オレフィンに基づく単量体単位が好ましい。 In particular, monomer units derived from ethylene and carbon number 4 to 8 α- olefin is preferred. このプロピレンに基づく単量体単位以外の単量体単位の含有割合は、10モル%未満であることが必要である。 Content of the monomer unit other than the monomer unit based on the propylene is required to be less than 10 mol%. 該含有割合が10モル%以上であり、プロピレンに基づく単量体単位の含有割合が90モル%以下の場合、得られるフィルムの粘着性が強くなり、取扱いが困難になる。 And in the proportion of 10 mol% or more, when the content of the monomer unit based on propylene of 90 mol% or less, the stronger the adhesiveness of the obtained film, the handling becomes difficult. また、かかるプロピレンに基づく単量体単位以外の単量体単位の含有割合は、好ましくは2モル%以上であるのが良好である。 Further, the content of monomer units other than the monomer unit based on such propylene are preferably good that is 2 mol% or more.

【0014】b)のプロピレン−エチレンランダム共重合体成分において、エチレンに基づく単量体単位及びプロピレンに基づく単量体単位のそれぞれの含有割合は、 [0014] propylene b) - in the ethylene random copolymer component, each content of the monomer unit based on the monomer units and propylene-based ethylene,
エチレンに基づく単量体単位10〜40モル%、好ましくは15〜35モル%であり、プロピレンに基づく単量体単位90〜60モル%、好ましくは85〜65モル% Monomer unit 10 to 40 mol% based on ethylene is preferably 15 to 35 mol%, a monomer based on propylene unit 90 to 60 mol%, preferably 85 to 65 mol%
である。 It is. エチレンに基づく単量体単位の含有割合が10 Content of the monomer unit based on ethylene is 10
モル%未満であり、プロピレンに基づく単量体単位の含有割合が90モル%を越える場合、得られるヒートシールフィルムの可剥性が充分でなくなり好ましくない。 Less than mol%, if the content of the monomer unit based on propylene exceeds 90 mol%, peelable obtained heat-sealing film is unfavorably insufficient. 一方、エチレンに基づく単量体単位の含有割合が40モル%を越え、プロピレンに基づく単量体単位の含有割合が60モル%未満である場合、得られるヒートシールフィルムの粘着性が強くなり、取扱いが困難になるため好ましくない。 On the other hand, the content of the monomer unit based on ethylene exceeds 40 mol%, When the content of the monomer unit based on propylene is less than 60 mol%, the stronger the adhesiveness of the resulting heat-sealing film, It is not preferable because the handling is difficult.

【0015】なお、このプロピレン−エチレンランダム共重合体成分には、本発明に関するプロピレン系ブロック共重合体の物性を阻害しない限り、他のα−オレフィンが少量、例えば5モル%以下の範囲で共重合されて含まれていてもよい。 [0015] Incidentally, the propylene - The ethylene random copolymer component, so long as it does not inhibit the physical properties of the propylene block copolymer regarding the present invention, a small amount of other α- olefins, co in the range of 5 mol% or less e.g. may be included are polymerized. 他のα−オレフィンとしては、特に制限されないが、炭素数が4〜12のα−オレフィンの1種または2種以上が挙げられ、炭素数4〜8のα−オレフィンが好ましい。 Other α- olefin is not particularly limited, carbon atoms include one or more of the 4 to 12 α- olefin, preferably of α- olefin having 4 to 8 carbon atoms.

【0016】また、本発明のプロピレン系ブロック共重合体は、上記a)プロピレン単独重合体成分、またはプロピレン系ランダム共重合体成分及びb)プロピレン− Further, the propylene block copolymer of the present invention, the above a) a propylene homopolymer component or a propylene random copolymer component and b) propylene, -
エチレンランダム共重合体成分の他に、好ましくは10 Other ethylene random copolymer component, preferably 10
重量%以下の範囲で、他のα−オレフィンの重合体成分が含有されていても良い。 Weight% or less, the polymer component of other α- olefins may be contained. このα−オレフィンとしては、前記したものが制限なく使用される。 As the α- olefins, those mentioned above can be used without limitation. 好適には、ポリブテン成分が良好である。 Preferably, the polybutene component is good.

【0017】本発明で使用するプロピレン系ブロック共重合体は、通常、a)プロピレン単独重合体成分、またはプロピレン系ランダム共重合体成分及びb)プロピレン−エチレンランダム共重合体成分が一分子鎖中に配列したいわゆるブロック共重合体の分子鎖と、a)プロピレン単独重合体成分、またはプロピレン系ランダム共重合体成分及びb)プロピレン−エチレンランダム共重合体成分のそれぞれ単独よりなる分子鎖とが機械的な混合では達成できない程度にミクロに混合しているものと考えられる。 Propylene block copolymer used in the [0017] present invention is generally, a) a propylene homopolymer component or a propylene random copolymer component and b) propylene, - ethylene random copolymer component in a molecule chain and the molecular chains of the so-called block copolymers which are arranged in, a) a propylene homopolymer component or a propylene random copolymer component and b) propylene, - a molecular chain, each consisting of a single ethylene random copolymer component machine It is believed that by mixing the micro to the extent that can not be achieved with mixing.

【0018】本発明において、上記のプロピレン系ブロック共重合体は、分子量分布が特定の値に狭くなっていることが必要である。 [0018] In the present invention, the propylene block copolymer described above, the molecular weight distribution is required to have narrowed to a specific value. 具体的には、ゲルパーミエーションクロマトグラフィー(以下「GPC」と略す)で測定した重量平均分子量(Mw)/数平均分子量(Mn)が1〜4、好適には1.2〜3.5、さらに好適には1. Specifically, gel permeation chromatography (hereinafter abbreviated as "GPC") The weight average molecular weight measured by (Mw) / number average molecular weight (Mn) of 1 to 4, preferably 1.2 to 3.5, even more preferably 1.
5〜3の範囲にある。 It is in the range of 5 to 3. この範囲において、得られるヒートシールフィルムは、可剥性に優れたものとなり、また、フィルムのべたつき等がない性状の好ましいものとなる。 In this range, the resulting heat seal film becomes excellent in strippability, also becomes preferable properties is not such as stickiness of the film.

【0019】さらに、このプロピレン系ブロック共重合体は、通常、重量平均分子量(Mw)が10万以上、より一般的には15万以上のものを用いるのが一般的である。 Furthermore, the propylene block copolymer is usually a weight-average molecular weight (Mw) of 100,000 or more, more typically it is common to use one of the more than 150,000. メルトフローレート(以下MFRと略す)は、製膜性を勘案すると、0.1〜20g/10分、好ましくは0.5〜15g/10分が好適である。 (Hereinafter abbreviated as MFR) The melt flow rate, when considering the film forming property, 0.1 to 20 g / 10 min, preferably suitably 0.5 to 15 g / 10 min. また、示差走査熱分析(DSC)における主ピークは、ヒートシール開始温度やフィルム成形時のロールへの貼り付き性を勘案すると120〜160℃、好ましくは125〜155℃ The main peak in the differential scanning calorimetry (DSC), upon consideration of the sticking of the heat seal initiation temperature and the film forming time of the roll 120 to 160 ° C., preferably 125-155 ° C.
の範囲にあることが良好である。 It is good in the range of.

【0020】本発明において、こうしたプロピレン系ブロック共重合体は、上記性状を有するものであれば、公知の如何なる方法によって重合したものを用いても良い。 [0020] In the present invention, such propylene block copolymer, as long as it has the above properties may be used as the polymerized by any known methods. また、重合したプロピレン系ブロック共重合体を有機過酸化物で分解させて得たものであっても良い。 Moreover, polymerized propylene block copolymer may be one obtained by decomposing an organic peroxide.

【0021】なお、このプロピレン系ブロック共重合体は、さらに必要に応じて帯電防止剤、防曇剤、アンチブロッキング剤、酸化防止剤、光安定剤、結晶核剤、滑剤等の公知の添加材を配合させて用いても良い。 [0021] Incidentally, the propylene block copolymer, further antistatic agent, if necessary, anti-fogging agents, anti-blocking agents, antioxidants, light stabilizers, nucleating agent, known additives such as a lubricant it may be used by blending. また、本発明に関する物性を阻害しない程度、他の樹脂を混合することができる。 The degree that does not inhibit the physical properties related to the present invention, it is possible to mix another resin. 混合する樹脂としては特に制限されないが、例えばプロピレン、エチレン、ブテン等のオレフィンの単独重合体または共重合体、或いはこれらの2種以上の混合物が好適である。 As the mixed resin is not particularly limited, for example, propylene, ethylene, homopolymers or copolymers of olefins butene, or a mixture of two or more thereof are suitable. 添加量は特に制限されないが、50重量%以下、さらには40重量%以下が好ましい。 The addition amount is not particularly limited, 50 wt% or less, more preferably 40 wt% or less.

【0022】次に、本発明の積層ヒートシールフィルムにおいて、以上のプロピレン系ブロック共重合体よりなる中間層が、少なくとも一方の表面に積層される基材フィルムは、如何なるものであっても良いが、成形性を勘案すると、DSCにおける主ピークが120〜250 Next, in the laminated heat-sealing film of the present invention, an intermediate layer made from the above propylene block copolymer, the base film which is laminated on at least one surface may but be any one , in consideration of moldability, the main peak in the DSC 120 to 250
℃、さらに好適には130〜170℃の樹脂フィルムからなるのが好ましい。 ° C., more preferably preferably made of a resin film 130 to 170 ° C.. 一般にはポリオレフィンからなる樹脂フィルムであるのが好適であり、具体的には、エチレン、プロピレン、ブテン、メチルペンテン等のオレフィンの単独重合体、または共重合体が挙げられ、これらの中で透明性を勘案すればポリプロピレンからなるフィルムが特に好適である。 Typically a preferred that a resin film comprising a polyolefin, specifically, ethylene, propylene, butene, homopolymers of olefins such as methylpentene, or copolymers and the like, transparency among these of polypropylene considering the film is particularly preferred. これらの基材フィルムとして使用されうる樹脂は、単独で使用してもよく、2種以上を混合して使用してもよい。 Resins that can be used as these base film may be used alone or may be used by mixing two or more kinds.

【0023】基材フィルムに用いるポリプロピレンとしては、プロピレンの単独重合体、プロピレンの90モル%以上とプロピレン以外のα−オレフィン、例えば、エチレン、1−ブテン、1−ペンテン、1−ヘキセン、1 Examples of the polypropylene used in the base film, a propylene homopolymer, propylene 90 mol% or more and other than propylene α- olefins, such as ethylene, 1-butene, 1-pentene, 1-hexene, 1
−ヘプテン、4−メチル−1−ペンテン等の1種以上の10モル%以下とのランダム共重合体、またはブロック共重合体を一般に使用することができる。 - heptene, can be used a random copolymer of less than 10 mol% of one or more 4-methyl-1-pentene, or block copolymers generally. MFRは、製膜性を勘案すれば0.5〜15g/10分の範囲であることが好適である。 MFR, it is preferable in the range of 0.5 to 15 g / 10 min Considering the film forming properties.

【0024】こうした基材フィルムに使用する樹脂には、必要に応じて帯電防止剤、防曇剤、アンチブロッキング剤、酸化防止剤、光安定剤、結晶核剤、滑剤等の公知の添加剤を配合させても良い。 [0024] The resin used in such a substrate film, an antistatic agent, if necessary, anti-fogging agents, anti-blocking agents, antioxidants, light stabilizers, nucleating agent, a known additive such as a lubricant it may be blended.

【0025】本発明では、以上の積層フィルムにおいて、前記したプロピレン系ブロック共重合体よりなる中間層の表面に、さらに密度が0.91〜0.95であるポリエチレン、及び/またはプロピレンに基づく単量体単位を88〜99モル%含むプロピレン系ランダム共重合体からなる外表面層が積層されている。 [0025] In the present invention, in the above laminated film, the surface of the intermediate layer made of the propylene block copolymer described above, further the polyethylene density is from 0.91 to 0.95, and / or propylene-based single the outer surface layer is laminated consisting of propylene random copolymer containing mer units 88 to 99 mol%. それにより本発明の積層フィルムは、フィルムの滑り性についても良好なものとなる。 Laminate film whereby the present invention also becomes excellent for slipperiness of the film.

【0026】ここで、ポリエチレンとしては、フィルムの滑り性、ヒートシール性、透明性等を勘案すると、密度が0.91〜0.95であることが必要であり、さらには0.915〜0.940であることがより好ましい。 [0026] As the polyethylene, slipperiness of the film, heat sealability, In consideration of transparency and the like, it is necessary that the density is from 0.91 to 0.95, still more 0.915 to 0 and more preferably from .940. また製膜性等を勘案すると、190℃におけるメルトフローレート(MFR)が、0.1〜20g/10分であることが好ましく、さらには0.5〜15g/10 Also when considering the film forming property and the like, melt flow rate (MFR) of at 190 ° C., is preferably 0.1 to 20 g / 10 min, more 0.5 to 15 g / 10
分であることがより好ましい。 It is more preferably a minute.

【0027】こうしたポリエチレンを具体的に例示すると、エチレンの単独重合体、エチレン−α−オレフィン共重合体、或はこれらの混合物等を用いることができる。 [0027] With specific examples of such polyethylene, ethylene homopolymer, ethylene -α- olefin copolymer, or it may be a mixture thereof or the like. 特に延伸加工性の面から、エチレン−α−オレフィン共重合体である直鎖状低密度ポリエチレンが好ましい。 Particularly from the viewpoint of stretchability, linear low density polyethylene is an ethylene -α- olefin copolymer.

【0028】ここで、ポリエチレンの密度が0.91未満の場合、フィルムの滑り性が十分でなくなる。 [0028] Here, if the density of the polyethylene is less than 0.91, the slipping property of the film becomes insufficient. 一方、 on the other hand,
この密度が0.95を越える場合、フィルムの低温でのヒートシール性や透明性が低下し好ましくない。 If the density exceeds 0.95, the heat sealability and transparency undesirably lowers at low temperatures of the film.

【0029】一方、プロピレンに基づく単量体単位を8 [0029] On the other hand, the monomer unit based on propylene 8
8〜99モル%含むプロピレン系ランダム共重合体における、プロピレンに基づく単量体単位以外の単量体単位としては、プロピレンと共重合可能な他の公知の単量体に基づく単位が制限なく採用できる。 In the propylene-based random copolymer containing 8-99 mol%, as the monomer unit other than the monomer unit based on propylene, employing propylene can be copolymerized with other known units based on monomer without limitation it can. 好適には、エチレンおよび炭素数が4〜12のα−オレフィンに基づく単量体単位が挙げられ、これらは1種または2種以上を組み合わせて採用しても良い。 Preferably, ethylene and carbon atoms include monomer unit based on 4-12 α- olefins, these may be employed alone or in combination of two or more kinds. かかるプロピレン系ランダム共重合体としては、具体的には、プロピレン−エチレン共重合体、プロピレン−エチレン−ブテン三元共重合体、プロピレン−α−オレフィン共重合体、或はこれらの混合物等を用いることができる。 Such propylene random copolymer, specifically, propylene - ethylene copolymer, a propylene - ethylene - butene terpolymers, propylene -α- olefin copolymer, or a mixture thereof, etc. be able to.

【0030】ここで、プロピレン系ランダム共重合体中のプロピレンに基づく単量体単位の含有割合は、88〜 The content of this case, the monomer unit based on propylene of the propylene-based random copolymer is 88 to
99モル%、好適には90〜98モル%であることが必要である。 99 mol%, preferably it is necessary that 90 to 98 mol%. このプロピレンに基づく単量体単位の含有割合が88モル%未満の場合、フィルムの滑り性が十分でなくなる。 When the content of the monomer unit based on the propylene is less than 88 mol%, slipperiness of the film is not sufficient. 一方、プロピレンに基づく単量体単位の含有割合が99モル%を越える場合、フィルムのヒートシール性が低下し好ましくない。 On the other hand, if the content of the monomer unit based on propylene exceeds 99 mol%, undesirably reduces the heat sealability of the film. また製膜性等を勘案すると、このプロピレン系ランダム共重合体は、230℃におけるメルトフローレート(MFR)が、0.1〜20 Also when considering the film forming property and the like, the propylene random copolymer, the melt flow rate (MFR) of at 230 ° C., 0.1 to 20
g/10分であることが好ましく、さらには0.5〜1 Is preferably g / 10 min, more 0.5-1
5g/10分であることがより好ましい。 And more preferably 5 g / 10 min.

【0031】なお、これらの樹脂からなる外表面層には、本発明の物性を阻害しない程度、該樹脂の他に他の樹脂が混合されても良い。 [0031] Note that the outer surface layer formed of the above resin, so as not to inhibit the physical properties of the present invention, other resins in addition to the resin may be mixed. こうした他の樹脂の混合量としては、20重量%以下であることが好ましく、さらには15重量%以下であることがより好ましい。 The mixing amount of such other resins, preferably 20 wt% or less, more and more preferably 15 wt% or less. さらに必要に応じて帯電防止剤、防曇剤、アンチブロッキング剤、酸化防止剤、光安定剤、結晶核剤、滑剤等の公知の添加剤を配合させて用いても良い。 Further antistatic agent, if necessary, anti-fogging agents, anti-blocking agents, antioxidants, light stabilizers, nucleating agent, may be used by blending a known additive such as a lubricant.

【0032】本発明において、以上の構成にある積層フィルムの厚みは特に制限されるものではないが、通常は、10〜250μm、好適には15〜120μmであるのが好ましい。 [0032] In the present invention, it is not particularly limited, the thickness of the laminated film in the above construction, generally, 10 to 250 .mu.m, preferably preferably a 15~120Myuemu. このうち前記中間層の厚みは、一般には0.1〜15μmの範囲から適宜選択され、0.5〜 The thickness of these said intermediate layer is generally selected appropriately from the range of 0.1-15, 0.5 to
10μmであることが好ましい。 It is preferable that the 10μm. また、外表面層の厚みは、滑り性、製膜性等を勘案すると、0.1〜10μm The thickness of the outer surface layer, slipping property, when considering the film forming property and the like, 0.1 to 10 [mu] m
であることが好ましく、さらには0.5〜5μmであることがより好ましい。 It is preferably, and more preferably still is 0.5 to 5 [mu] m.

【0033】本発明において、積層フィルムを成形する方法は、特に制限されるものではなく如何なる方法によっても良い。 [0033] In the present invention, a method of molding the laminated film may be by any method is not particularly limited. 一般には、前記中間層の樹脂成分と外表面層の樹脂成分と基材フィルムの樹脂成分とを、本発明の積層フィルムの層構成になるように共押出して、温度制御チルロール上で急冷し無延伸で製膜するか、さらにその後一軸または二軸に延伸するか、または一層または複層の樹脂を溶融押出して一軸延伸し、その上に他層の樹脂を溶融押出して上記一軸延伸の方向とほぼ直角方向に延伸する方法等が採用される。 In general, the a resin component of the resin component and the substrate film of the resin component of the intermediate layer and the outer surface layer, co-extruded so that the layer structure of the multilayer film of the present invention, quenched on a temperature controlled chill roll no or film by stretching Thereafter either uniaxially or biaxially stretched, or the resin of one layer or multiple layers by melt-extruded and uniaxially stretching, the direction of the upper to the uniaxial stretching is melt extruded resin other layer a method in which stretching in a direction substantially perpendicular is employed. 縦一軸延伸の一例として、一般には最前部の低速度で回転するロールと最後部の高速度で回転するロール間にフィルムを通し、両ロールの回転数比によって延伸される。 As an example of a longitudinal uniaxial stretching, generally through the film between the rolls rotating at high speed roll and the last portion which rotates at a low speed of the foremost, it is drawn by the rotational speed ratio of the rolls. 一方横一軸延伸の一例として、好ましくはテンター方式で行うと良い。 On the other hand as an example of a transverse uniaxial stretching, but it is preferable carried out by a tenter method. また、以上に示した方法で縦横逐次二軸延伸、同時二軸延伸等も可能である。 Also, more than a method in vertical and horizontal sequential biaxial stretching indicated, it is also possible simultaneous biaxial stretching or the like. 延伸倍率は、面積倍率で5〜60 Stretch ratio is 5 to 60 in area ratio
倍、さらには30〜50倍が好適である。 Times, furthermore is suitably 30 to 50 times.

【0034】以上はフラット状の場合であるが、これ以外にもチューブ状原反をインフレ方式により縦一軸、横一軸、同時二軸延伸等を行うことも可能である。 The above is the case of a flat-shaped, longitudinal uniaxial by inflation method a tubular raw sheet other than this, a transverse uniaxial, it is also possible to carry out the simultaneous biaxial stretching or the like. この場合、原反を例えば80〜150℃に加熱し、チューブ状フィルム内に加圧空気を送り込み、無延伸で製膜したり、または縦もしくは横方向に一軸延伸、または縦横方向に同時二軸延伸すればよい。 In this case, heating the raw example, 80 to 150 ° C., fed pressurized air into the tubular film, or a film in unstretched, or vertical or horizontal direction in uniaxial stretching or simultaneous biaxial in the vertical and horizontal directions, It can be stretched.

【0035】なお、本発明で使用する前記プロピレン系ブロック共重合体は、任意の割合でポリプロピレンと相溶可能であり、またポリエチレンとの相溶性も良好である。 [0035] Incidentally, the propylene block copolymer used in the present invention may be compatible with polypropylene in any proportion, also the compatibility with the polyethylene is good. 従って、本発明の積層フィルムにおいて、上記成形時の中間層や外表面層部分の不適合品は、基材フィルムの素材や外表面層に混合する他の樹脂の素材として再生還元できる。 Therefore, in the laminated film of the present invention, non-conforming products of the intermediate layer and the outer surface layer portion in a the molding can play reduction as another resin material to be mixed into the material and the outer surface layer of the base film. また、他のポリプロピレン系あるいはポリエチレン系成形体の用途に再生利用することもできる。 It can also be recycled for use in other polypropylene or polyethylene-based moldings.
さらに、基材フィルムの素材樹脂がポリプロピレンやポリエチレンである場合、積層フィルムの不適合品は、溶融混練することで基材フィルム、中間層、外表面層を均一に混合でき、同様に再生利用し易い。 Furthermore, if the material resin of the base material film is a polypropylene or polyethylene, non-conforming items of the laminated film, the substrate film by melt-kneading, the intermediate layer, the outer surface layer be uniformly mixed, similarly recycled easily .

【0036】 [0036]

【発明の効果】本発明の積層フィルムは、ヒートシールして密封信頼性の優れた構造を形成するだけでなく、ヒートシールした際の可剥性、易開封性にも優れている。 The laminated film of the present invention exhibits not only to form a good structure of the sealing reliability by heat sealing, peelable when heat sealed, is excellent in easy-open performance.
特に、融着された結合部を引き剥す際に、両フィルムがその界面や表面層部分で剥離せず、いずれか一方の基材フィルム層が引き裂かれて分離することが抑制される。 In particular, when peeled off the fused binding unit, both the film that does not peel at the interface or surface layer portion, one of the base film layer that is separated torn is suppressed.
また、滑り性も良好で、自動包装時等において機械走行性に優れ、安定して物品の包装を行うことができる。 Also, sliding property is good, and excellent mechanical running properties during automatic packaging and the like, can be stably perform packaging of the article. 従って、本発明の積層フィルムによれば、極めて有用なヒートシールフィルムを提供できる。 Therefore, with the multilayer film of the present invention can provide a very useful heat-sealing film. そうして、この積層フィルムにおいて、前記プロピレン系ブロック共重合体からなる中間層及び外表面層は、透明性も良好であり、 Then, in the laminated film, the intermediate layer and the outer surface layer made of the propylene block copolymer, also transparency is good,
そのため基材フィルムの素材樹脂として透明性の良好なものを使用した場合、透明性にも優れたものが得られる。 When using that for having good transparency as a material resin of the base film, it is excellent in transparency can be obtained.

【0037】 [0037]

【実施例】以下、本発明を実施例及び比較例を掲げて説明するが、本発明はこれらの実施例に限定されるものではない。 EXAMPLES As follows is a description by set a the present invention examples and comparative examples, the present invention is not limited to these examples.

【0038】実施例及び比較例において中間層として使用したプロピレン系ブロック共重合体は、表1に示すものである。 The propylene block copolymer used as the intermediate layer in Examples and Comparative Examples are as shown in Table 1.

【0039】 [0039]

【表1】 [Table 1]

【0040】また、以下の実施例及び比較例において用いた測定方法は次の方法により実施した。 Further, the measuring methods used in the following Examples and Comparative Examples were carried out by the following method.

【0041】(1)数平均分子量(Mn)、重量平均分子量(Mw) GPC(ゲルパーミエーションクロマトグラフィー)法により測定した。 [0041] (1) The number average molecular weight (Mn), as measured by the weight-average molecular weight (Mw) GPC (gel permeation chromatography). ウォーターズ社製GPC−150CによりO−ジクロルベンゼンを溶媒とし、135℃で行った。 The O- dichlorobenzene as a solvent by Waters Co. GPC-150C, was carried out at 135 ° C.. 用いたカラムは、東ソー製TSK gel GMH Column was used, manufactured by Tosoh TSK gel GMH
6−HT、ゲルサイズ10〜15μmである。 6-HT, is a gel size 10~15μm. 較正曲線は標準試料として重量平均分子量が950、2900、 The calibration curve is weight average molecular weight as a standard sample 950,2900,
1万、5万、49.8万、270万、675万のポリスチレンを用いて作成した。 10,000, 50,000, 498,000, 2.7 million, was made using the 6.75 million of polystyrene.

【0042】(2)プロピレン−エチレンランダム共重合体成分におけるエチレンに基づく単量体単位及びプロピレンに基づく単量体単位のそれぞれ割合の測定13 C−NMRスペクトルのチャートを用いて算出した。 [0042] (2) propylene - was calculated using the respective proportions measured 13 C-NMR chart of the spectrum of the monomer unit based on monomer units and propylene derived from ethylene in the ethylene random copolymer component.
即ち、プロピレン−エチレンランダム共重合体成分におけるエチレンに基づく単量体単位及びプロピレンに基づく単量体単位のそれぞれの割合は、まず、ポリマー(P That is, the propylene - respective proportions of ethylene random copolymer monomer unit based on monomer units and propylene derived from ethylene in the component, first, the polymer (P
olymer)第29巻(1988年)1848頁に記載された方法により、ピークの帰属を決定し、次にマクロモレキュールズ(Macromolecules)第10巻(1977年)773頁に記載された方法により、エチレンに基づく単量体単位及びプロピレンに基づく単量体単位のそれぞれの割合を算出した。 Olymer) by the method described in Vol. 29 (1988) pp. 1848 to determine the attribution of peaks, then Macromolecules (Macromolecules) Vol. 10 (1977) by the method described in 773 pages, It was calculated respective proportions of the monomer unit based on monomer units and propylene-based ethylene.

【0043】次いで,プロピレンに基づいて単量体単位中のメチル炭素に起因するピークと、ポリブテン成分中のメチル炭素に起因するピークとの積分強度比からポリブテン成分の重量と割合を算出した。 [0043] Then, a peak due to the methyl carbon in the monomer units based on propylene, and calculate the weight and percentage of polybutene component from the integrated intensity ratio of the peak due to the methyl carbons of the polybutene component.

【0044】(3)メルトフローレート(MFR) JIS K7210に準じて測定した。 [0044] (3) was measured in accordance with the melt flow rate (MFR) JIS K7210.

【0045】(4)DSCによる主ピークの測定 約5〜6mgの試料を評量後、アルミパンに封入し、示差熱量計にて20ml/minの窒素気流中で室温から235℃または270℃まで昇温し、これらの温度で1 [0045] (4) After Hyoryou sample measurement about 5~6mg main peak by DSC, was sealed in an aluminum pan, to 235 ° C. or 270 ° C. from room temperature in a nitrogen stream of 20 ml / min with a differential calorimeter heated, 1 at these temperatures
0分間保持し、次いで10℃/minで室温まで冷却する。 And held for 10 minutes, then cooled to room temperature at 10 ° C. / min. この後、昇温速度10℃/minで得られる融解曲線により、主ピークの温度を測定した。 Thereafter, the melting curve obtained at a heating rate 10 ° C. / min, to measure the temperature of the main peak.

【0046】(5)透明性 JIS−K6714に準じ、フィルムのヘイズ値を測定した。 [0046] (5) according to the transparency of JIS-K6714, the haze was measured value of the film.

【0047】(6)ヒートシール性(ヒートシール開始温度) 積層フィルムのヒートシール面同士を、5×200mm [0047] (6) Heat sealability (heat sealing initiation temperature) heat-sealing faces of the laminated film, 5 × 200 mm
のヒートシールバーを用い、各設定温度(80℃から1 Using a heat seal bar, 1 from each set temperature (80 ° C.
55℃まで5℃毎に測定)においてヒートシール圧力1 Heat in the measurement) for each 5 ° C. to 55 ° C. sealing pressure 1
kg/cm2、ヒートシール時間1.0秒の条件でシールした試料から、15mm幅のサンプルを切り取り、引張試験機を用いて引張速度100mm/分で測定した。 kg / cm @ 2, the sealed sample under the conditions of heat sealing time of 1.0 seconds, cut a sample of 15mm width was measured at a speed 100 mm / min tensile using a tensile tester.
結果は5サンプルの平均値とした。 Results were the average of five samples. 以上の方法で求めたヒートシール曲線から、ヒートシール強度が300g/ From the heat seal curve obtained by the above method, the heat seal strength is 300g /
15mmの温度をヒートシール開始温度とした。 The temperature of the 15mm was the heat seal initiation temperature.

【0048】(7)可剥性 ヒートシール開始温度および、さらに5℃および10℃ [0048] (7) peelable heat seal initiation temperature and, further 5 ℃ and 10 ℃
高い温度にてヒートシールしたサンプルにおいて、10 In the samples that were heat-sealed at a high temperature, 10
サンプルずつ測定した合計30サンプルのうち、結合部が両フィルムの界面や表面層部分で剥離せず、いずれか一方のフィルムの基層が引き裂かれて分離しているものの数により判定した。 Of a total of 30 samples measured by the sample, binding portion does not peel at the interface or surface layer portions of both film was determined by the number of those either base layer of one film are separated torn. 判定基準は以下のとうりである。 Criteria are the following Tori.

【0049】 [0049]

【表2】 [Table 2]

【0050】(8)滑り性 フィルム製膜後、40℃で2日間養生後にASTM−D [0050] (8) after sliding film casting, ASTM-D after 2 days aging at 40 ° C.
−1894の動摩擦係数測定法に準拠して測定した。 It was measured according to the dynamic friction coefficient measurement method of -1894.

【0051】実施例1 表2に示す基層、中間層及び外表面層の樹脂を、3層T The base layer shown in Example 1 in Table 2, the resin of the intermediate layer and the outer surface layer, three-layer T
ダイ押出し機を用いて、260℃で加熱溶融下共押出しし、テンター法2軸延伸機により、縦4.5倍、横9倍に延伸した積層フィルムを得た。 From a die extruder, heat-melted under coextrusion at 260 ° C., by a tenter method biaxially stretching machine, vertical 4.5 times to obtain a laminated film stretched in the transverse 9 times. 得られたフィルムの厚み、ヘイズ、ヒートシール性、可剥性、滑り性を測定し、結果を表3に示した。 The thickness of the resulting film, haze, heat-sealable, peelable, measured slipperiness, and the results are shown in Table 3.

【0052】実施例2 表2に示す基層、中間層及び外表面層の樹脂を、3層T [0052] The base layer shown in Example 2 in Table 2, the resin of the intermediate layer and the outer surface layer, three-layer T
ダイ押出し機を用いて、260℃で加熱溶融下共押出しし、チルロール上で冷却固化し、無延伸2層フィルムを得た。 From a die extruder, and lower co-extruded heat-melting at 260 ° C., and cooled and solidified on a chill roll to obtain an unstretched two-layered film. 得られたフィルムの厚み、ヘイズ、ヒートシール性、可剥性、滑り性を測定し、結果を表3に示した。 The thickness of the resulting film, haze, heat-sealable, peelable, measured slipperiness, and the results are shown in Table 3.

【0053】実施例3 表2に示す基層の樹脂を、Tダイ押出し機を用いて、2 [0053] The resin of the base layer shown in Example 3 in Table 2, using a T-die extruder, 2
80℃で加熱溶融下シート状に押出し、チルロール上で冷却固化した後、加熱ロール延伸機により4.5倍に延伸し、1軸延伸シートを得た。 Extruding the heated and melted under sheet at 80 ° C., was cooled and solidified on a chill roll, by the heating roll stretching machine and stretched 4.5 times to obtain a uniaxially stretched sheet. 次いで、表2に示す中間層及び表面層の樹脂を、2層Tダイ押出し機を用いて2 Then, the resin of the intermediate layer and the surface layer shown in Table 2, using a 2-layer T-die extruder 2
80℃で加熱溶融下、シート状に押出し、前記1軸延伸シートとロール上で貼り合わせて3層シートを得、ひき続き横延伸機で、9倍に延伸した。 Under heat-melting at 80 ° C., extruded into a sheet to obtain the uniaxially stretched sheet and bonded to 3-layer sheet on a roll, with continuing transverse stretching machine, and stretched to 9 times. 得られたフィルムの厚み、ヘイズ、ヒートシール性、可剥性、滑り性を測定し、結果を表3に示した。 The thickness of the resulting film, haze, heat-sealable, peelable, measured slipperiness, and the results are shown in Table 3.

【0054】実施例4〜8 実施例3において、基層、中間層及び外表面層の樹脂として表2に示したものを用いたこと以外は、実施例3と同様にしてフィルムを得た。 [0054] In Examples 4 to 8 Example 3, the base layer, except that as a resin for an intermediate layer and an outer surface layer with that shown in Table 2, to obtain a film in the same manner as in Example 3. 得られたフィルムの厚み、 The thickness of the resulting film,
ヘイズ、ヒートシール性、可剥性、滑り性を測定し、結果を表3に示した。 Haze, heat-sealing property, measured peelable, slipperiness, the results are shown in Table 3.

【0055】比較例1〜6 実施例3において、基層、中間層及び外表面層の樹脂として表2に示したものを用いたこと以外は、実施例3と同様にしてフィルムを得た。 [0055] In Comparative Examples 1-6 Example 3, the base layer, except that as a resin for an intermediate layer and an outer surface layer with that shown in Table 2, to obtain a film in the same manner as in Example 3. 得られたフィルムの厚み、 The thickness of the resulting film,
ヘイズ、ヒートシール性、可剥性、滑り性を測定し、結果を表3に示した。 Haze, heat-sealing property, measured peelable, slipperiness, the results are shown in Table 3.

【0056】 [0056]

【表3】 [Table 3]

【0057】 [0057]

【表4】 [Table 4]

Claims (1)

    【特許請求の範囲】 [The claims]
  1. 【請求項1】基材フィルムの少なくとも一方の表面に、 A)a)プロピレン単独重合体成分、またはプロピレンに基づく単量体単位を90モル%より多く含むプロピレン系ランダム共重合体成分1〜70重量%、 b)エチレンに基づく単量体単位を10〜40モル%、 To claim 1 wherein at least one surface of the base film, A) a) a propylene homopolymer component or a propylene random copolymer component 1-70 of the monomer unit containing more than 90 mol% based on propylene, wt%, b) a monomer unit based on ethylene 10-40 mol%,
    プロピレンに基づく単量体単位を90〜60モル%含むプロピレン−エチレンランダム共重合体成分30〜99 Propylene containing a monomer unit based on propylene 90-60 mol% - ethylene random copolymer component 30-99
    重量%よりなり、重量平均分子量(Mw)/数平均分子量(Mn)が1〜4であるプロピレン系ブロック共重合体よりなる中間層が積層されてなり、さらに、該中間層の表面に、 B)密度が0.91〜0.95であるポリエチレン、及び/またはプロピレンに基づく単量体単位を88〜99 Consists wt%, the in weight average molecular weight (Mw) / number average molecular weight (Mn) consisting of propylene block copolymer is from 1 to 4 the intermediate layer are stacked and further, the surface of the intermediate layer, B ) polyethylene density of 0.91 to 0.95, and / or a monomer unit based on propylene 88-99
    モル%含むプロピレン系ランダム共重合体からなる外表面層が積層されてなる積層フィルム。 Laminate film outer surface layer is laminated consisting of propylene random copolymer containing mol%.
JP31043595A 1995-11-29 1995-11-29 Laminated film Pending JPH09150488A (en)