WO1998029492A1 - Flame resistant nylon elastomers - Google Patents
Flame resistant nylon elastomers Download PDFInfo
- Publication number
- WO1998029492A1 WO1998029492A1 PCT/US1998/001122 US9801122W WO9829492A1 WO 1998029492 A1 WO1998029492 A1 WO 1998029492A1 US 9801122 W US9801122 W US 9801122W WO 9829492 A1 WO9829492 A1 WO 9829492A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- composition
- flame
- nylon elastomer
- nylon
- retardant
- Prior art date
Abstract
Description
Claims