WO1998024826A1 - Adhesives - Google Patents
Adhesives Download PDFInfo
- Publication number
- WO1998024826A1 WO1998024826A1 PCT/GB1997/003340 GB9703340W WO9824826A1 WO 1998024826 A1 WO1998024826 A1 WO 1998024826A1 GB 9703340 W GB9703340 W GB 9703340W WO 9824826 A1 WO9824826 A1 WO 9824826A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- cross
- linked polyurethane
- linked
- diamine
- isocyanate
- Prior art date
Abstract
Description
Claims