WO1997045457A1 - Procede de preparation de matieres polymeres reticulees poreuses de faible densite - Google Patents

Procede de preparation de matieres polymeres reticulees poreuses de faible densite Download PDF

Info

Publication number
WO1997045457A1
WO1997045457A1 PCT/US1997/009008 US9709008W WO9745457A1 WO 1997045457 A1 WO1997045457 A1 WO 1997045457A1 US 9709008 W US9709008 W US 9709008W WO 9745457 A1 WO9745457 A1 WO 9745457A1
Authority
WO
WIPO (PCT)
Prior art keywords
acid ester
water
glycerol
fatty acid
emulsion
Prior art date
Application number
PCT/US1997/009008
Other languages
English (en)
Inventor
Sharon Marie Beshouri
Original Assignee
Shell Oil Company
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shell Oil Company filed Critical Shell Oil Company
Priority to AU30790/97A priority Critical patent/AU3079097A/en
Publication of WO1997045457A1 publication Critical patent/WO1997045457A1/fr

Abstract

Emulsions stables eau-dans-huile à phase interne élevée, contenant des monomères vinyliques polymérisables, des monomères de réticulation, et des initiateurs, qui sont utiles pour préparer des mousses polymères réticulées poreuses de faible densité grâce à l'utilisation d'un système de tensioactif contenant (a) un ou plusieurs esters d'acide gras de sorbitanne ou esters d'acide gras de saccharide et (b) un ester monoacide gras de glycérol. Des émulsions eau-dans-huile présentant un rapport eau-dans-huile plus élevé peuvent être préparées avec la même composition en utilisant le tensioactif ester de monoacide gras de glycérol.
PCT/US1997/009008 1996-05-30 1997-05-27 Procede de preparation de matieres polymeres reticulees poreuses de faible densite WO1997045457A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
AU30790/97A AU3079097A (en) 1996-05-30 1997-05-27 Process to prepare low density porous cross-linked polymeric materials

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US1855596P 1996-05-30 1996-05-30
US60/018,555 1996-05-30

Publications (1)

Publication Number Publication Date
WO1997045457A1 true WO1997045457A1 (fr) 1997-12-04

Family

ID=21788546

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US1997/009008 WO1997045457A1 (fr) 1996-05-30 1997-05-27 Procede de preparation de matieres polymeres reticulees poreuses de faible densite

Country Status (2)

Country Link
AU (1) AU3079097A (fr)
WO (1) WO1997045457A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2002034798A2 (fr) * 2000-10-24 2002-05-02 Nippon Shokubai Co., Ltd. Procede de production d'un materiau polymere poreux reticule
SG134967A1 (en) * 2000-09-28 2007-09-28 Uni Charm Corp Absorbent article and barrier agent for absorbent article

Citations (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5334621A (en) * 1993-11-04 1994-08-02 Shell Oil Company Process to prepare low density porous crosslinked polymeric materials

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5334621A (en) * 1993-11-04 1994-08-02 Shell Oil Company Process to prepare low density porous crosslinked polymeric materials
US5362762A (en) * 1993-11-04 1994-11-08 Shell Oil Company Process to prepare low density porous crosslinked polymeric materials

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
SG134967A1 (en) * 2000-09-28 2007-09-28 Uni Charm Corp Absorbent article and barrier agent for absorbent article
WO2002034798A2 (fr) * 2000-10-24 2002-05-02 Nippon Shokubai Co., Ltd. Procede de production d'un materiau polymere poreux reticule
WO2002034798A3 (fr) * 2000-10-24 2002-09-19 Nippon Catalytic Chem Ind Procede de production d'un materiau polymere poreux reticule
US6730711B2 (en) * 2000-10-24 2004-05-04 Nippon Shokubai Co., Ltd. Method for production of porous cross-linked polymer material

Also Published As

Publication number Publication date
AU3079097A (en) 1998-01-05

Similar Documents

Publication Publication Date Title
US5334621A (en) Process to prepare low density porous crosslinked polymeric materials
US5340842A (en) Low density porous crosslinked polymeric materials
US5210104A (en) Process for preparing low density porous crosslinked polymeric materials
US5200433A (en) Process for preparing low density porous crosslinked polymeric materials
US5252619A (en) Process for preparing low density porous crosslinked polymeric materials
US5189070A (en) Process for preparing low density porous crosslinked polymeric materials
WO1995004105A1 (fr) Procede de preparation de materiaux polymeres reticules, poreux, de faible densite
EP0861287B1 (fr) Procede de preparation de compositions de mousse diphasique
US5912276A (en) Process to prepare low density porous cross-linked polymeric materials
EP0902805B1 (fr) Procede de preparation de matieres polymeres reticulees poreuses de faible densite
WO1997045457A1 (fr) Procede de preparation de matieres polymeres reticulees poreuses de faible densite

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AL AU BA BB BG BR CA CN CU CZ EE GE HU IL IS JP KP KR LC LK LR LT LV MK MN MX NO NZ PL RO SG SI SK TR TT UA US UZ VN AM AZ BY KG KZ MD RU TJ TM

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): GH KE LS MW SD SZ UG AT BE CH DE DK ES FI FR GB GR IE IT LU MC NL PT SE BF BJ CF CG CI CM GA GN ML MR NE SN TD TG

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
121 Ep: the epo has been informed by wipo that ep was designated in this application
NENP Non-entry into the national phase

Ref country code: JP

Ref document number: 97542876

Format of ref document f/p: F

122 Ep: pct application non-entry in european phase
NENP Non-entry into the national phase

Ref country code: CA