WO1997036939A1 - A novel composition, its preparation and use - Google Patents
A novel composition, its preparation and use Download PDFInfo
- Publication number
- WO1997036939A1 WO1997036939A1 PCT/FI1997/000192 FI9700192W WO9736939A1 WO 1997036939 A1 WO1997036939 A1 WO 1997036939A1 FI 9700192 W FI9700192 W FI 9700192W WO 9736939 A1 WO9736939 A1 WO 9736939A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- composition
- carboxylic acid
- process according
- coor
- alkyl
- Prior art date
Abstract
Description
Claims