WO1997000528A1 - Fabrication of capacitors - Google Patents
Fabrication of capacitors Download PDFInfo
- Publication number
- WO1997000528A1 WO1997000528A1 PCT/AU1996/000364 AU9600364W WO9700528A1 WO 1997000528 A1 WO1997000528 A1 WO 1997000528A1 AU 9600364 W AU9600364 W AU 9600364W WO 9700528 A1 WO9700528 A1 WO 9700528A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- metal
- capacitor
- layers
- web
- deposition
- Prior art date
Abstract
Description
Claims