WO1996022239A1 - Bande transporteuse ayant des caracteristiques antimicrobiennes et procede de fabrication - Google Patents

Bande transporteuse ayant des caracteristiques antimicrobiennes et procede de fabrication Download PDF

Info

Publication number
WO1996022239A1
WO1996022239A1 PCT/US1996/000417 US9600417W WO9622239A1 WO 1996022239 A1 WO1996022239 A1 WO 1996022239A1 US 9600417 W US9600417 W US 9600417W WO 9622239 A1 WO9622239 A1 WO 9622239A1
Authority
WO
WIPO (PCT)
Prior art keywords
antimicrobial agent
belting
yarns
polymeric material
staple fibers
Prior art date
Application number
PCT/US1996/000417
Other languages
English (en)
Inventor
William D. Hanrahan
Florian S. Zabron
Mary Ellen Marlette
Miles S. Rothman
Original Assignee
Habasit Globe, Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Habasit Globe, Inc. filed Critical Habasit Globe, Inc.
Priority to AU47542/96A priority Critical patent/AU4754296A/en
Publication of WO1996022239A1 publication Critical patent/WO1996022239A1/fr

Abstract

Cette invention se rapporte à une bande transporteuse (10, 20) à laquelle est associé un agent antimicrobien à large spectre, de façon à empêcher la croissance bactérienne et à promouvoir l'asepsie sur cette bande. L'agent antimicrobien peut comprendre un constituant du mélange polymère à partir duquel sont fabriqués les fils synthétiques (12, 14, 24, 26) de la toile de la bande, ou l'agent antimicrobien peut être déposé comme revêtement sur les fils de la toile de la bande, par filage desdits fils à travers un bain comprenant ledit agent antimicrobien, ou à l'aide d'une technique de revêtement par vaporisation ou similaire. Dans une variante, la toile de la bande peut être fabriquée avant que l'agent antimicrobien lui soit associé. Des nappes non tissées de fibres discontinues peuvent également être tissées sur la toile de la bande et celle-ci peut être recouverte d'un mélange élastomère contenant ledit agent antimicrobien. La bande faisant l'objet de cette invention est particulièrement utile pour le transport d'aliments, notamment dans l'industrie de la transformation des aliments et dans la manutention d'aliments.
PCT/US1996/000417 1995-01-18 1996-01-17 Bande transporteuse ayant des caracteristiques antimicrobiennes et procede de fabrication WO1996022239A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
AU47542/96A AU4754296A (en) 1995-01-18 1996-01-17 Belting having antimicrobial characteristics and method of manufacture

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US37434495A 1995-01-18 1995-01-18
US08/374,344 1995-01-18

Publications (1)

Publication Number Publication Date
WO1996022239A1 true WO1996022239A1 (fr) 1996-07-25

Family

ID=23476386

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US1996/000417 WO1996022239A1 (fr) 1995-01-18 1996-01-17 Bande transporteuse ayant des caracteristiques antimicrobiennes et procede de fabrication

Country Status (2)

Country Link
AU (1) AU4754296A (fr)
WO (1) WO1996022239A1 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2000013992A1 (fr) * 1998-09-03 2000-03-16 Healthshield Technologies L.L.C. Courroie presentant un effet antimicrobien
WO2003086910A1 (fr) * 2002-04-12 2003-10-23 Habasit Ag Transporteur a courroie permettant de manipuler des articles de boulangerie/patisserie et procede de fabrication associe
US7438178B2 (en) 2006-11-16 2008-10-21 Habasit Ag Composite conveying belt
EP2108261A1 (fr) * 2008-04-11 2009-10-14 Busch Fashion GmbH Textiles pour être utilisés en boulangerie

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4267776A (en) * 1979-06-29 1981-05-19 Motorola, Inc. Muzzle velocity compensating apparatus and method for a remote set fuze
US4897202A (en) * 1988-01-25 1990-01-30 Pure-Chem Products, Inc. Process and apparatus for recovery and recycling conveyor lubricants
US5495935A (en) * 1994-08-12 1996-03-05 Globe International Inc. Conveyor belting and method of manufacture

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4267776A (en) * 1979-06-29 1981-05-19 Motorola, Inc. Muzzle velocity compensating apparatus and method for a remote set fuze
US4897202A (en) * 1988-01-25 1990-01-30 Pure-Chem Products, Inc. Process and apparatus for recovery and recycling conveyor lubricants
US5495935A (en) * 1994-08-12 1996-03-05 Globe International Inc. Conveyor belting and method of manufacture

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2000013992A1 (fr) * 1998-09-03 2000-03-16 Healthshield Technologies L.L.C. Courroie presentant un effet antimicrobien
WO2003086910A1 (fr) * 2002-04-12 2003-10-23 Habasit Ag Transporteur a courroie permettant de manipuler des articles de boulangerie/patisserie et procede de fabrication associe
US7438178B2 (en) 2006-11-16 2008-10-21 Habasit Ag Composite conveying belt
EP2108261A1 (fr) * 2008-04-11 2009-10-14 Busch Fashion GmbH Textiles pour être utilisés en boulangerie

Also Published As

Publication number Publication date
AU4754296A (en) 1996-08-07

Similar Documents

Publication Publication Date Title
US5906269A (en) Conveyor belting and method of manufacture
US5495935A (en) Conveyor belting and method of manufacture
US3998986A (en) Conveyor belt of rubber reinforced with stitch-bonded web fabric
US6994209B2 (en) Conveyor belt with a polymer surface coating containing an antimicrobial additive
SU1369661A3 (ru) Галантерейное изделие дл защиты от порезов
EP0136727B2 (fr) Fil en polyamide aromatique imprégné de particules lubrifiantes, procédé pour sa fabrication et matériau de garniture ou corde contenant ce fil
CN101291743A (zh) 抗微生物的阳离子聚合电解质涂层
WO2000032247A2 (fr) Tissu antimicrobien et greffe medicale constituee de ce tissu
CA2206193A1 (fr) Materiau de protection et methode
CN102754946A (zh) 轻薄型柔性聚合物涂覆的手套和制备方法
EP1402105A2 (fr) Fil traite et ses procedes de fabrication
NO135947B (fr)
WO1996022239A1 (fr) Bande transporteuse ayant des caracteristiques antimicrobiennes et procede de fabrication
US4679859A (en) Method of making mops and mats impregnated with antimicrobial compounds
US1213118A (en) Protective and non-penetrative covering and the like.
EP1124743B1 (fr) Courroie presentant un effet antimicrobien
US20030194928A1 (en) Conveyor belting for handling bakery goods
WO2010080956A1 (fr) Carreau de tapis ayant des propriétés antimicrobiennes et son procédé de fabrication
US4444305A (en) Conveyor belting for handling bakery goods
CA2257143A1 (fr) Bande transporteuse pour denrees alimentaires
CA1294771C (fr) Particules spheriques en fibres, utilisees en particulier comme remplissage de coussins, d'edredon
WO1995026650A1 (fr) Article vestimentaire presentant une aptitude a la prehension et une resistance au glissement superieures
KR102008489B1 (ko) 유해 화학물질제거용 보호복 섬유 소재 및 이의 제조방법
FI86894C (fi) Bandmaterial foer transportband
NL1009742C1 (nl) Antimicrobieel middel bevattende transportband.

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AU CA MX NZ

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): AT BE CH DE DK ES FR GB GR IE IT LU MC NL PT SE

121 Ep: the epo has been informed by wipo that ep was designated in this application
DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
122 Ep: pct application non-entry in european phase