WO1995010555A1 - Moisture-activated adhesive compositions - Google Patents
Moisture-activated adhesive compositionsInfo
- Publication number
- WO1995010555A1 WO1995010555A1 PCT/EP1994/003371 EP9403371W WO9510555A1 WO 1995010555 A1 WO1995010555 A1 WO 1995010555A1 EP 9403371 W EP9403371 W EP 9403371W WO 9510555 A1 WO9510555 A1 WO 9510555A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- moisture
- adhesive composition
- activated adhesive
- tertiary amine
- polyisocyanate
- Prior art date
Abstract
Description
Claims