WO1992000932A1 - Corps en ceramique composites a teneur accrue en metal - Google Patents

Corps en ceramique composites a teneur accrue en metal Download PDF

Info

Publication number
WO1992000932A1
WO1992000932A1 PCT/US1991/004949 US9104949W WO9200932A1 WO 1992000932 A1 WO1992000932 A1 WO 1992000932A1 US 9104949 W US9104949 W US 9104949W WO 9200932 A1 WO9200932 A1 WO 9200932A1
Authority
WO
WIPO (PCT)
Prior art keywords
metal
parent metal
boron
molten
self
Prior art date
Application number
PCT/US1991/004949
Other languages
English (en)
Inventor
Philip Joseph Roach
Original Assignee
Lanxide Technology Company, Lp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Lanxide Technology Company, Lp filed Critical Lanxide Technology Company, Lp
Priority to US07/960,408 priority Critical patent/US5500182A/en
Publication of WO1992000932A1 publication Critical patent/WO1992000932A1/fr

Abstract

Nouveau procédé de formation d'un corps autoporteur. Spécifiquement, le corps autoporteur formé a un pourcentage volumique supérieur en constituant métallique par rapport à un corps formé selon des techniques similaires. On forme premièrement un corps autoporteur poreux par infiltration réactive d'un métal de base fondu dans un lit ou une masse contenant une matière donneuse de bore et une matière donneuse de carbone (par exemple, du carbure de bore) et/ou une matière donneuse de bore ainsi qu'une matière azotée (par exemple, du nitrure de bore) et, facultativement, une ou plusieurs matières de remplissage inerte. De plus, on peut mélanger un métal de base en poudre avec une masse à infiltrer de manière réactive afin d'y former une porosité supplémentaire. Le corps autoporteur poreux formé selon la technique d'infiltration réactive de l'invention doit présenter au moins une certaine porosité interconnectée pouvant être remplie, dans une étape ultérieure, d'un métal supplémentaire, augmentant ainsi le pourcentage volumique du métal de base dans le corps au détriment de la porosité.
PCT/US1991/004949 1990-07-12 1991-07-12 Corps en ceramique composites a teneur accrue en metal WO1992000932A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
US07/960,408 US5500182A (en) 1991-07-12 1991-07-12 Ceramic composite bodies with increased metal content

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US55129390A 1990-07-12 1990-07-12
US551,293 1990-07-12

Publications (1)

Publication Number Publication Date
WO1992000932A1 true WO1992000932A1 (fr) 1992-01-23

Family

ID=24200666

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US1991/004949 WO1992000932A1 (fr) 1990-07-12 1991-07-12 Corps en ceramique composites a teneur accrue en metal

Country Status (2)

Country Link
JP (1) JPH05508380A (fr)
WO (1) WO1992000932A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2007059568A1 (fr) * 2005-11-22 2007-05-31 Composite Alloy Products Pty Ltd Procede de production de composites metalliques dans une atmosphere inerte et composites ainsi produits

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0250210A2 (fr) * 1986-06-17 1987-12-23 The Regents Of The University Of California Procédé de fabrication de matériaux composites métallo-céramiques et matériaux composites ainsi obtenus
EP0322341A2 (fr) * 1987-12-23 1989-06-28 Lanxide Technology Company, Lp. Procédé pour fabriquer des pièces céramiques composites et en modifier les propriétés

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0250210A2 (fr) * 1986-06-17 1987-12-23 The Regents Of The University Of California Procédé de fabrication de matériaux composites métallo-céramiques et matériaux composites ainsi obtenus
EP0322341A2 (fr) * 1987-12-23 1989-06-28 Lanxide Technology Company, Lp. Procédé pour fabriquer des pièces céramiques composites et en modifier les propriétés

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2007059568A1 (fr) * 2005-11-22 2007-05-31 Composite Alloy Products Pty Ltd Procede de production de composites metalliques dans une atmosphere inerte et composites ainsi produits

Also Published As

Publication number Publication date
JPH05508380A (ja) 1993-11-25

Similar Documents

Publication Publication Date Title
EP0378500B1 (fr) Procédé pour la fabrication de corps autoportants et produits ainsi produits
US5296419A (en) Self-supporting composite bodies
US5019539A (en) Process for preparing self-supporting bodies having controlled porosity and graded properties and products produced thereby
EP0378499B1 (fr) Procédé pour la fabrication d'articles autoportants et produits obtenus selon ce procédé
EP0322336B1 (fr) Procédé pour fabriquer des pièces autoporteuses et produits ainsi obtenus
US5017334A (en) Process for preparing self-supporting bodies and products produced thereby
US5010044A (en) Process for preparing self-supporting bodies and products produced thereby
US5011063A (en) Method of bonding a ceramic composite body to a second body and articles produced thereby
US4978644A (en) Process for preparing self-supporting bodies and products made thereby
US5403790A (en) Additives for property modification in ceramic composite bodies
US5238883A (en) Process for preparing self-supporting bodies and products produced thereby
US5104029A (en) Method of bonding a ceramic composite body to a second body and articles produced thereby
US5187128A (en) Process for preparing self-supporting bodies
US5288670A (en) Process for preparing self-supporting ceramic composite bodies and bodies produced thereby
US5500182A (en) Ceramic composite bodies with increased metal content
US5232040A (en) Method for reducing metal content of self-supporting composite bodies and articles formed thereby
US5120684A (en) Pressure assisted technique for forming self-supporting composite bodies and articles formed thereby
US5435966A (en) Reduced metal content ceramic composite bodies
WO1992000932A1 (fr) Corps en ceramique composites a teneur accrue en metal
WO1992000939A2 (fr) Corps composites en ceramique a teneur reduite en metal
EP0378501A1 (fr) Procédé pour lier une pièce céramique composite à une deuxième pièce et produits ainsi obtenus
US5264401A (en) Pressure assisted technique for forming self-supporting composite bodies and articles formed thereby
WO1992000933A1 (fr) Additifs de modification de proprietes dans des corps ceramiques composites

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): CA JP US

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): AT BE CH DE DK ES FR GB GR IT LU NL SE

NENP Non-entry into the national phase

Ref country code: CA