WO1991000152A1 - Corrosion protective agent and a method for applying the same - Google Patents
Corrosion protective agent and a method for applying the same Download PDFInfo
- Publication number
- WO1991000152A1 WO1991000152A1 PCT/SE1990/000447 SE9000447W WO9100152A1 WO 1991000152 A1 WO1991000152 A1 WO 1991000152A1 SE 9000447 W SE9000447 W SE 9000447W WO 9100152 A1 WO9100152 A1 WO 9100152A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- composition
- composition according
- corrosion
- spraying
- fillers
- Prior art date
Abstract
Description
Claims