WO1986003756A1

WO1986003756A1 - Molecular weight distribution modification in tubular reactor

Info

Publication number: WO1986003756A1
Application number: PCT/US1985/002528
Authority: WO
Inventors: Charles Cozewith; Shiaw Ju; Gary William Verstrate
Original assignee: Exxon Research And Engineering Company
Priority date: 1984-12-14
Filing date: 1985-12-16
Publication date: 1986-07-03
Also published as: KR870700641A; EP0204840A1; KR900008459B1; EP0204840A4; AU5301086A; JPS62501155A; AU579446B2; CA1272846A

Abstract

Novel copolymers of alpha-olefins comprised of intramolecularly heterogeneous and intermolecularly homogeneous copolymer claims prepared by a process as outlined schematically in Fig. 1.

Description

MOLECULAR WEIGHT DISTRIBUTION MODIFICATION IN A TUBULAR REACTOR

CROSS REFERENCE TO RELATED APPLICATIONS

This application is a continuation-in-part of

Application Serial Number 681,951, filed December 14,

1985, which in turn is a continuation-in-part of Serial

Number 504,582, filed June 15, 1983, the disclosure of which are herein incorporated by reference thereto.

MOLECULAR WEIGHT DISTRIBUTION MODIFICATION

IN TUBULAR REACTOR

Background of the Invention

The present invention relates to novel copolymers of alpha-olefins. More specifically, it relates to novel copolymers of ethylene with other alpha-olefins which have a polymodal molecular weight distribution wherein individual nodes comprising the polymer have narrow molecular weight distributions.

For convenience, certain terms that are repeated throughout the present specification are defined below:

(a) Inter-CD defines compositional variation, in terms of ethylene content, among polymer chains. It is expressed as the minimum deviation (analogous to a standard deviation) in terms of weight percent ethylene from the average ethylene composition for a given copolymer sample needed to include a given weight percent of the total copolymer sample which is obtained by excluding equal weight fractions from both ends of the distribution. The deviation need not be symmetrical. When expressed as a single number, for example, 15% Inter-CD, it shall mean the larger of the positive or negative deviations. For example, for a Gaussian compositional distribution, 95.5% of the polymer is within 20 wt% ethylene of the mean if the standard deviation is 10%. The Inter-CD for 95.5 wt% of the polymer is 20 wt% ethylene for such a sample.

(b) Intra-CD is the compositional variation, in terms of ethylene, within a copolymer chain. It is expressed as the minimum difference in weight (wt) % ethylene that exists between two portions of a single copolymer chain, each portion comprising at least 5 wt% of the chain.

(c) Molecular weight distribution (MWD) is a measure of the range of molecular weights within a given copolymer sample. It is characterized in terms of at least one of the ratios of weight average to number average molecular weight, M_w/M_n, and Z average to weight average molecular weight, M_z/M_w, where:

Ni is the number of molecules of weight Mi.

Ethylene-propylene copolymers, particularly elastomers, are important commercial products. Two basic types of ethylene-propylene copolymers are commercially available; ethylene propylene copolymers and ethylene propylene terpolymers. Ethylene-propylene copolymers (EPM) are saturated compounds requiring vulcanization with free radical generators such as organic peroxides. Ethylene-propylene terpolymers (EPDM) contain a small amount of non-conjugated diolefin, such as dicyclopentadiene; 1,4-hexadiene or ethylidene norbornene, which provides sufficient unsaturation to permit vulcanization with sulfur. Such ethylene-propylene polymers that include at least two monomers, i.e., EPM and EPDM, will be hereinafter collectively referred to as ethylene-propylene copolymers.

These copolymers have outstanding resistance to weathering, good heat aging properties and the ability to be compounded with large quantities of fillers and plasticizers resulting in low cost compounds which are particularly useful in automotive and industrial mechanical goods applications. Typical automotive uses are tire sidewalls, inner tubes, radiator and heater hose, vacuum tubing, weather stripping, sponge doorseals and Viscosity Index (V.I.) improvers for lubricating oil compositions. Typical mechanical goods uses are for appliance, industrial and garden hoses, both molded and extruded sponge parts, gaskets and seals and conveyor belt covers. These copolymers also find use in adhesives, appliance parts as in hoses and gaskets, wire and cable and plastics blending.

As can be seen from the above, based on their respective properties, EPM and EPDM find many, varied uses. It is known that the properties of such copolymers which make them useful in a particular application are, in turn, determined by their composition and structure. For example, the ultimate properties of an EPM and EPDM copolymer are determined by such factors as composition, compositional distribution, sequence distribution, molecular weight, and molecular weight distribution (MWD).

The efficiency of peroxide curing depends on composition. As the ethylene level increases, it can be shown that the "chemical" crosslinks per peroxide molecule increases. Ethylene content also influences the rheological and processing properties, because crystallinity, which acts as physical crosslinks, can be introduced. The crystallinity present at very high ethylene contents may hinder processability and may make the cured product too "hard" at temperatures below the crystalline melting point to be useful as a rubber.

Milling behavior of EPM or EPDM copolymers varies radically with MWD. Narrow MWD copolymers crumble on a mill, whereas broad MWD materials will band under conditions encountered in normal processing operations. At the shear rates encountered in processing equipment, broader MWD copolymer has a substantially lower viscosity than narrower MWD copolymer of the same weight average molecular weight or low strain rate viscosity. Thus, there exists a continuing need for discovering polymers with unique properties and compositions.

For elastomer applications the processability is often measured by the Mooney viscosity. The lower this quantity the easier the elastomer is to mix and fabricate. It is desirable to have low Mooney yet to maintain a high number average molecular weight, M_n , so that the polymers form good rubber networks upon cross-linking. For EP and EPDM, narrowing the molecular weight distribution results in the production of polymer with higher number average molecular weight at a given Mooney than the broader distribution polymer. In certain cases, the poor milling, calendering or extrusion behavior that results from the narrow MWD must be ameliorated. Rather than perform a MWD broadening which includes low molecular weight components which reduce M_n, it is possible to broaden the MWD without disproportionately lowering M_n. This is done by superposing one or more narrow MWD modes, i.e., different Mooney components, each of which contains no appreciable amount of low molecular weight polymer. The result is a polymodal molecular weight distribution comprised of narrow MWD polymer fractions of different molecular weights.

The present invention is drawn to a novel copolymer of ethylene and at least one other alpha-olefin monomer which copolymer is composed of several such MWD components each of which is very narrow. It is well known that the breadth of the MWD can be characterized by the ratios of various molecular weight averages . For example, an indication of the narrow MWD of each component in accordance with the present invention is that the ratio of weight to number average molecular weight

(M_w/M_n) is less than 2. Alternatively, a ratio of the Z-average molecular weight to the weight average molecular weight (M_z/M_w) of less than 1.8 typifies a narrow MWD in accordance with the present invention. It is known that the property advantages of copolymers in accordance with the present invention are related to these ratios. Small weight fractions of material can disproportionately influence these ratios while not significantly altering the property advantages which depend on them. For instance, the presence of a small weight fraction (e . g . , 2% ) of low molecular weight copolymer can dep r ress M_n, and thereby raise M_w/M_n above 2 while maintaining M_z/M_w less than 1.8. Therefore, the component polymers, in accordance with the present invention, are characterized by having at least one of two characteristics; M_w. /M_n less than 2 and M_z/M_w less than 1.8.

To obtain narrow MWD, the copolymers in accordance with the present invention are preferably made in a tubular reactor. It has been discovered that to produce such copolymers requires the use of numerous heretofore undisclosed method steps conducted within heretofore undisclosed preferred ranges. Accordingly, the present invention is also drawn to a method for making the novel copolymers of the present invention.

Description of the Prior Art

Representative prior art dealing with tubular reactors to make copolymers are as follows:

In "Polymerization of ethylene and propylene to amorphous copolymers with catalysts of vanadium oxychloride and alkyl aluminum halides"; E. Junghanns, A. Gumboldt and G. Bier; Makromol. Chem, v. 58 (12/12/62): 18-42, the use of a tubular reactor to produce ethylene-propylene copolymer is disclosed in which the composition varies along the chain length. More specifically, this reference discloses the production in a tubular reactor of amorphous ethylene-propylene copolymers using Ziegler catalysts prepared from vanadium compound and aluminum alkyl. It is disclosed that at the beginning of the tube ethylene is preferentially polymerized, and if no additional make-up of the monomer mixture is made during the polymerization the concentration of monomers changes in favor of propylene along the tube. It is. further disclosed that since these changes in concentration take place during chain propagation, copolymer chains are produced which contain more ethylene on one end than at the other end. It is also disclosed that copolymers made in a tube are chemically non-uniform, but fairly uniform with respect to molecular weight distribution. Using the data reported in their Figure 17 for copolymer prepared in the tube, it was estimated that the M_w/M_n ratio for this copolymer was 1.6.

"Laminar Flow Polymerization of EPDM Polymer"; J.F. Wehner; ACS Symposium Series 65 (1978); pp 140-152 discloses the results of computer simulation work undertaken to determine the effect of tubular reactor solution polymerization with Ziegler catalysts on the molecular weight distribution of the polymer product. The specific polymer simulated was an elastomeric terpolymer of ethylene-propylene-1, 4-hexadiene. On page 149, it is stated that since the monomers have different reactivities, a polymer of varying composition is obtained as the monomers are depleted. However, whether the composition varies inter- or intramolecularly is not distinguished. In Table III on page 148, various polymers having M_w/M_n of about 1.3 are predicted. In the third paragraph on page 144, it is stated that as the tube diameter increases, the polymer molecular weight is too low to be of practical interest, and it is predicted that the reactor will plug. It is implied in the first paragraph on page 149 that the compositional dispersity produced in a tube would be detrimental to product quality.

U.S. 3,681,306 is drawn to a process for producing ethylene/higher alpha-olefin copolymers having good processability, by polymerization in at least two consecutive reactor stages. According to this reference, this two-stage process provides a simple polymerization process that permits tailor-making ethylene/alpha-olefin copolymers having predetermined properties, particularly those contributing to processability in commercial applications such as cold-flow, high green strength and millability. Allegedly, the disclosed process is particularly adapted for producing elastomeric copolymers, such as ethylene/ propylene/5-ethylidene-2-norbornene, using any of the coordination catalysts useful for making EPDM. The preferred process uses one tubular reactor followed by one pot reactor. However, it is also disclosed that one tubular reactor could be used, but operated at different reaction conditions to simulate two stages. As is seen from the disclosure at column 2, lines 14-20, the process makes polymers of broader MWD than those made in a single stage reactor. Although intermediate polymer from the first (pipeline) reactor is disclosed as having a ratio of M_w/M_n of about

2 (column 5, lines 54-57) the final polymers produced by the process have an M_w/M_n of 2.4 to 5.

U.S. 3,625,658 co Closon discloses a closed circuit tubular reactor apparatus with high recirculation rates of the reactants which can be used to make elastomers of ethylene and propylene. With particular reference to Fig. 1 of the patent, a hinged support 10 for vertical leg 1 of the reactor allows for horizontal expansion of the bottom leg thereof and prevents harmful deformations due to thermal expansions, particularly those experienced during reactor clean out. U.S. 4,065,520 to Bailey et al. discloses the use of a batch reactor to make ethylene copolymers, including elastomers, having broad compositional distributions. Several feed tanks for the reactor are arranged in series, with the feed to each being varied to make the polymer. The products made have crystalline to semi-crystalline to amorphous regions and gradient changes in between. The catalyst system can comprise vanadium compounds alone or in combination with titanium compounds and is exemplified by vanadium oxy-tri-chloride and diisobutyl aluminum chloride. In all of the examples, titanium compounds are used. In several examples, hydrogen and diethyl zinc, known transfer agents, are used. The polymer chains produced have a compositionally disperse first length and uniform second length. Subsequent lengths have various other compositional distributions.

In "Estimation of Long-Chain Branching in Ethylene-Propylene Terpolymers from Infinite-Dilution Viscoelastic Properties"; Y. Mitsuda, J. Schrag, and J. Ferry ; J. Appl . Pol . Sci . , 18 , 193 (1974 ) narrow MWD copolymers of ethylene-propylene are disclosed. For example, in TABLE II on page 198, EPDM copolymers are disclosed which have M_w/M_n of from 1.19 to 1.32.

In "The Effect of Molecular Weight and Molecular Weight Distribution on the Non-Newtonian Behavior of Ethylene-Propylene-Diene Polymers; Trans. Soc. Rheol., 14, 83 (1970); C.K. Shih, a whole series of compositionally homogeneous fractions were prepared and disclosed. For example, the data in TABLE I discloses polymer Sample B as having a high degree of homogeneity. Also, based on the reported data, the MWD of the sample is very narrow. However, the polymers are not disclosed as having intramolecular dispersity.

Molecular weight distribution (MWD) is a very important characteristic of ethylene-propylene copolymers and terpolymers. Favorable distributions result in polymers which can have both faster cures and better processing characteristics. An optimum combination of these properties is achieved where the polymers have a polymodal molecular weight distribution and a polymodal compositional distribution.

A significant amount of effort has been expended by the polymer industry in an attempt to produce such polymodal ethylene-propylene polymers. Generally, these efforts have been directed toward physical blends of polymers having different MWD or by sequential polymerization in a multiple reactor system. For example, a polymerization is carried out in a first reaction stage to produce a polymer of a particular MWD and composition with a subsequent polymerization in a second reactor stage to produce a polymer of a different MWD from that of the first stage and , if de s ired , of a different monomer composition. Representative prior art dealing with the preparation of bimodal MWD ethylene-propylene copolymers are as follows:

British Patent No. 1,233,599 is illustrative of two stage polymerization processes. While copolymers of ethylene are incidently disclosed, the examples and disclosure are directed toward polyethylene homopolymers and crystalline copolymers, e.g., 95Z ethylene. The preferred catalysts are vanadium compounds such as vanadyl halide, vanadium tetrachloride or vanadium tris-(acetyl-acetonate) in conjunction with an aluminum compound, e.g., Br₂AlCH Br₂. The different MWDs are obtained by using differing amounts of hydrogen in the first and second stage polymerization. U.S. Patent No. 4,078,131 discloses an ethylene-propylene rubber composition having a bimodal distribution in molecular weights comprising two polymer fractions each having a wide distribution of molecular weights and a monomer composition different from that of the other principal fractions. The polymers are further characterized in that they are formed of: (a) a first principal fraction comprising from about 30% to about 85Z (by weight referred to the total weight of elastomers) of molecular weight fractions having an intrinsic viscosity distribution of from about 0.2 to about 3, and average intrinsic viscosity between about 0.8 to about 1.5, an average propylene content between about 36 to about 52% by weight, and a termonomer content of between 0% and about 5%, and of (b) a second fraction comprising about 70% to about 15% by weight of molecular weight fractions having an intrinsic viscosity distribution from about 3 to about 15, an average intrinsic viscosity of about 3.5 to about 7, and average propylene content of between about 26% to about 32% by weight and a termonomer content of about 0 to about 5%.

The polymers are prepared by carrying out polymerization in two separate reactors connected in series. The catalyst systems utilized include organic and inorganic component of a transition metal of Group 4A to 8A of the Mendeleev periodic table of the elements, e.g., VOCl₃, VCl₄, vanadium esters and acetyl acetonates. Co-catalysts include organoaluminum compounds or mixtures of compounds, e.g., aluminum alkyIs.

U.S. Patent 3,681,306 discloses a two stage polymerization process for the preparation of ethylene- propylene co-and terpolymers. In one embodiment the first stage is a "pipe reactor" and the second stage is a back-mixed pot reactor. The polymerization is carried out so that the average ethylene/alpha olefin ratio in one state is at least 1.3 tines the average ratio of the other stage. Any of the coordination catalysts know to be useful in producing EPDM polymers is said to be effective for the process.

U.S. Patent No. 4,259,468 discloses a broad molecular weight ethylene-propylene-diene rubber prepared using as a catalyst (a) the alcohol reaction product of vanadium oxytrichloride and (b) a mixture of aluminum sesquichloride and ethylaluminum dichloride. The polymer is characterized in that the higher molecular weight fraction contains a larger proportion of the diene than does the lower molecular weight fraction. The polymer has an intrinsic viscosity of about 1.0 to about 6.0 dl/g and a weight average molecular weight/number ratio of about 3 to about 15.

U.S. Patent No. 4,306,401 discloses a method of manufacture of EPDM type terpolymers which utilizes a two stage polymerization process. Substantially all of the non-conjugated diene monomer is fed to the first stage thereby producing a polymer having a non-uniform diene content.

Brief Description of the Drawings

The accompanying drawings depict, for illustration purposes only, processes embodied by the present invention, wherein:

Fig. 1 is a schematic representation of a process for producing polymer in accordance with the present invention.

Fig. 2 schematically illustrates a polymodal MWD polymer comprising narrow MWD polymers for each mode,

Fig. 3 is a graphical illustration of a technique for determining Intra-CD of a copolymer,

Fig. 4 graphically illustrates various copolymer structures that can be attained using processes in accordance with the present invention. Detailed Description of the Invention

The instant invention relates to a novel copolymer of ethylene and at least one other alpha-olefin monomer, which copolymer is a superposition of two or more copolymers, each of which has a MWD characterized by having at least one of two characteristics; an M_w/M_n of less than 2 and M_z/M_w of less than 1.8.

As already noted, copolymers in accordance with the present invention are comprised of ethylene and at least one other alpha-olefin. Such alpha-olefins can include those containing 3 to 18 carbon atoms. Alpha-olefins of 3 to 6 carbons are preferred becavse of economic considerations.

Illustrative non-limiting examples of alpha olefins useful in the practice of this invention are propylene, butene-1, pentene-1, hexene-1, heptene-1, octene-1, dodecene-1, etc. The most preferred copolymers in accordance with the present invention are those comprised of ethylene and propylene or ethylene, propylene and non-conjugated diene.

As is well known to those skilled in the art, copolymers of ethylene and higher alpha-olefins such as propylene often include other polymerizable monomers. Typical of these other monomers can be non-conj ugated dienes. Illustrative non-limiting examples of such non-conjugated dienes are: a. straight chain acyclic dienes such as: 1,4-hexadiene; 1,6-octadiene; b. branched chain acyclic dienes such as: 5-methyl-1, 4-hexadiene; 3,7-dimethyl-1, 6- octadiene; 3,7-dimethyl-1,7-octadiene and the mixed isomers of dihydro-myrcene;

c. single ring alicyclic dienes such as: 1,4-cyclohexadiene; 1,5-cyclooctadiene; and 1,5-cyclododecadiene; d. multi-ring alicyclic fused and bridged ring dienes such as: tetrahydroindene; methyltetrahydroindene; dicyclopentadiene; bi- cyclo-(2,2,1)-hepta-2,5-diene; alkenyl, alkylidene, cycloalkenyl and cycloalkylidene norbornenes such as 5-methylene-2-norbornene (MNB), 5-ethylidene-2-norbornene (ENB), 5-propylidene-2-norbornene, 5-isopropylidene-2-norbornene, 5-(4-cyclopentenyl)-2-norbornene; 5-cyclohexylidene-2-norbornene.

Of the non-conjugated dienes typically used to prepare these copolymers, dienes containing at least one of the double bonds in a strained ring are preferred. The most preferred diene is 5-ethylidene-2-norbornene (EMB) . The amount of diene (wt. basis) in the copolymer can be about 0% to 20% with 0% to 15% being preferred. The most preferred range is 0% to 10%.

As already noted, the most preferred copolymer in accordance with the present invention is ethylene-propylene or ethylene-propylene non-conjugated diene. In either event, the average ethylene content of each component of these copolymers can be as lew as about 10Z on a weight basis. The preferred minimum ethylene content is about 25%. A more preferred minimum is about 30%. The maximum ethylene content can be about 90% on a weight basis. The preferred maximum is about 85%, with the cost preferred being about 80%.

The molecular weight of the component copolymer made in accordance with the present invention can vary over a wide range. The weight average molecular weight (M_w) can be as low as about 2,000. The preferred minimum is about 10,000. The most preferred minimum is about 20,000. The maximum weight average molecular weight can be as high as about 12,000,000. The preferred maximum is about 1,000,000. The most preferred maximum is about 750,000. Another feature of the copolymers made in accordance with the present invention is that the molecular weight distribution (MWD) of each component is very narrow, as characterized by having at least one of two characteristics; a ratio of Mw/Mn of less than 2 and a ratio of M_z/M_w of less than 1.8. The M_w/M_n ratio for the whole copolymer can range from about 1 to about 50. The M_w and MWD of the copolymer is controlled by adjusting the M_w and weight fraction of polymer that make up the individual narrow MWD components. In a preferred embodiment, the M_w of any two adjacent MWD modes should differ by at least 50% and any one mode chould comprise at least 10 wt% of the total copolymer. As it relates to EPM and EPDM, a typical advantage of such copolymers composed of several modes having narrow MWD is that when compounded and vulcanized, faster cure and better physical properties result than when copolymers having lower M_n for a given Mooney are used.

Processes in accordance with the present invention produce copolymer by polymerization of a reaction mixture comprised of catalyst, ethylene, at least one additional alpha-olefin monomer, and optionally, a non- conjugated diene. Solution polymerizations are preferred.

Any known solvent for the reaction mixture that is effective for the purpose can be used in conducting solution polymerizations in accordance with the present invention. For example, suitable solvents are hydrocarbon solvents such as aliphatic, cycloaliphatic and aromatic hydrocarbon solvents, or halogenated analogs of such solvents. The preferred solvents are C₄ to C₁₂, straight chain or branched chain, saturated hydrocarbons, C₅ to C₉ saturated alicyclic or aromatic hydrocarbons or C₂ to C₆ halogenated hydrocarbons. Most preferred are C₆ to C₁₂, straight chain or branched chain hydrocarbons, particularly hexane. Nonlimiting illustrative examples of such solvents are butane, pentane, hexane, heptane, cyclopentane, cyclohexane, cycloheptane, methyl cyclopentane, methyl cyclohexane, isooctane, benzene, toluene, xylene, chloroform, chlorobenzenes, tetrachloroethylene, dichloroethane and trichloroethane.

A number of processes can be used to prepare the copolymer products of this invention. These processes are based on carrying out the copolymerization in a batch or tubular reactor. As described in our copending patent application, Serial Number 504,582, copolymers of narrow MWD with M_w /M_n less than 2. 0 or M_z /M_w less than 1.8 can be obtained by operating such reactors at certain specified conditions. Firstly, in the course of the polymerization, substantially no mixing must occur between polymer chains that have been initiated at different times. This condition is defined as "mix free." Tubular reactors are well known and are designed to minimize mixing of the reactants in the direction of flow. As a result, reactant concentration will vary along the reactor length. In contrast, the reaction mixture in a continuous flow stirred tank reactor (CFSTR) is blended with the incoming feed to produce a solution of essentially uniform composition everywhere in the reactor. Consequently, the growing chains in a portion of the reaction mixture will have a variety of ages and thus a single CFSTR is not suitable for the process of this invention. However, it is well known that 3 or more stirred tanks in series with all of the catalyst fed to the first reactor can approximate the performance of a tubular reactor. Accordingly, such tanks in series are considered to be in accordance with the present invention.

A batch reactor is a suitable reaction vessel in which to carry out the process of this invention, preferably equipped with adequate agitation. The catalyst, solvent, and monomer are added to the reactor at the start of the polymerization. The charge of reactants is then left to polymerize for a time long enough to produce the desired product. For economic reasons, a tubular reactor is preferred to a batch reactor for carrying out the processes of this invention.

In addition to the importance of the reactor system to make narrow MWD component copolymers the polymerization should be conducted in a manner such that for each component or mode in the MWD: a. the catalyst system produces essentially one active catalyst species, b. the reaction mixture is essentially free of chain transfer agents, and c. for each mode the polymer chains are essentially all initiated simultaneously, which is at the same time for a batch reactor or at the same point along the length of the tube for a tubular reactor.

The desired polymer can also be obtained if additional solvent and reactants (e.g., at least one of the ethylene, alpha-olefin and diene) are added either along the length of a tubular reactor or during the course of polymerization in a batch reactor. Operating in this fashion can be desirable in certain circumstances to control the polymerization rate or polymer composition. However, it is necessary to add the catalyst at the inlet or specific locations of the tube or at the onset of or at specific times in batch reactor operation to meet the requirement that for each mode essentially all polymer chains are initiated simultaneously.

Accordingly, narrow MWD component copolymers are produced by carrying out a polymerization reaction:

(a) in a least one mix free reactor,

(b) using catalyst systems such that each component or mode in the MWD is produced by essentially one active catalyst species,

(c) using at least one reaction mixture which is essentially transfer agent-free, and (d) in such a manner and under conditions sufficient to initiate propagation of essentially all polymer chains made with a particular catalyst species simultaneously.

To produce the multimodal MWD polymer of this invention, these polymerization conditions are used to generate each of the narrow MWD modes that comprise the final polymer product. A number of techniques are available for achieving this:

1) In a single mix free reactor operated as described above, portions of the polymer product can be withdrawn after varying times in a batch reactor or at varying distances along a tubular reactor representing different average molecular weights and these portions can be blended.

2) Mix free reactors can be operated either in parallel or sequentially and the products blended.

3) Two or more catalysts that form narrow MWD polymer of differing molecular weight can be added at the onset of polymerization in a mixfree reactor. Each catalyst must meet the requirements of minimizing chain transfer and initiating simultaneous propagation of all the chains produced by that catalyst.

4) A catalyst system that generates multiple active catalyst species can be added at the start of the polymerization. Each catalyst species produced must give simultaneous chain initiation and minimize chain transfer.

5) Additional catalyst and monomer, if desired, can be added at varying lengths along a tubular reactor or times in a batch reactor to initiate the formation of additional MWD modes. The catalysts can be the same or different, as long as chains are initiated simultaneously and chain transfer is minimized.

6) For catalyst system that show a decay in activity as a function of time due to deactivation, catalyst reactivator can be added during the course of the polymerization to regenerate the dead catalyst and form a new mode of narrow MWD copolymer.

Catalyst reactivators are well known in the art for increasing the productivity of vanadium Ziegler catalysts. These materials rejuvenate catalyst sites that have become inert due to termination reactions and thereby cause reinitiation of polymer chain growth. When added to a reactor operating according to the process of this invention, catalyst reactivators have an effect similar to that of adding a second catalyst feed. Many reactivators are known, and examples of suitable materials can be found in U.S. Patents 3,622,548, 3,629,212, 3,723,348, 4,168,358, 4,181,790 and 4,361,686. Esters of chlorinated organic acids are preferred reactivators for use with the vanadium catalyst systems of this invention. Especially preferred is butyl perchlorocrotanate.

In the processes of this invention that utilize multiple catalysts or multiple catalyst additions during the course of polymerization the mix free condition of the reactor refers to the polymer chains of each individual mode of the MWD and not to the polymer as a whole.

A preferred multiple catalyst system comprises VCl₄ combined with VOCl₃ and an alkyl aluminum sesquihalide as a cocatalyst. The resultant polymer is a bimodal MWD polymer.

Since the present invention is considered to be most preferred in the context of ethylene-propylene (EPM) or ethylene-propylene-diene (EPDM) copolymers, it will be described in detail in the context of EPM and/or EPDM.

Copolymer in accordance with the present invention is preferably made in a tubular reactor. When produced in a tubular reactor with monomer feed only at the tube inlet, it is known that at the beginning of the tubular reactor ethylene, due to its high reactivity, will be preferentially polymerized. However, the concentration of monomers changes along the tube in favor of propylene as the ethylene is depleted. The result is copolymer chains which are higher in ethylene concentration in the chain segments grown near the reactor inlet (as defined at the point at which the polymerization reaction commences), and higher in propylene concentration in the chain segments formed near the reactor outlet. An illustrative copolymer chain of ethylene- propylene is schematically presented below the E representing ethylene constituents and P representing propylene constituents in the chain:

1 2 3 4

Segment: E-E-E-E-P-E-E-E-P-P-E-E-P-P-P-E-P-P-P-P As can be seen from this illustrative schematic chain, the far left-hand segment (1) thereof represents that portion of the chain formed at the reactor inlet where the reaction mixture is proportionately richer in the more reactive constituent ethylene. This segment comprises four ethylene molecules and one propylene molecule. However, as subsequent segments are formed from left to right with the more reactive ethylene being depleted and the reaction mixture proportionately increasing in propylene concentration, the subsequent chain segments become more concentrated in propylene. The resulting chain is intramolecularly heterogeneous.

In the event that more than two monomers are used, e.g., in the production of EPDM using a diene termonomer, for purposes of describing the present invention all properties related to homogeneity and. heterogeneity will refer to the relative ratio of ethylene to the other monomers in the chain. The property, of the copolymer discussed herein, related to intramolecular compositional dispersity (compositional variation within a chain) shall be referred to as Intra-CD, and that related to intermolecular compositional dispersity (compositional variation between chains) shall be referred to as Inter-CD.

For copolymers in accordance with the present invention, composition can vary between chains as well as along the length of the chain. In one embodiment of this invention, the Inter-CD can be characterized by the difference in composition between some fraction of the copolymer and the average composition, as well as by the total difference in composition between the copolymer fractions containing the highest and lowest quantity of ethylene. Techniques for measuring the breadth of the Inter-CD are known as illustrated by Junghanns, et al., wherein a p-xylene-dimethylformamide solvent/non-solvent was used to fractionate copolymer into fractions of differing intermolecular composition. Other solvent/non- solvent systems can be used, such as hexane-2-propanol, as will be discussed in more detail below.

In one embodiment of this invention, the Inter-CD of the individual component copolymers in accordance with the present invention is such that 95 wt% of the copolymer chains have an ethylene composition that differs from the average component weight percent ethylene composition by 15 wt% or less. The preferred Inter-CD is about 13% or less, with the most preferred being about 10% or less. In comparison, Junghanns, et al., found that their tubular reactor copolymer had an Inter-CD of greater than 15 wt%. Broadly, in one embodiment of this invention, the Intra-CD of copolymer in accordance with the present invention is such that at least two portions of an individual component intramolecularly heterogeneous chain, each portion comprising at least 5 wt% of the chain, differ in composition from one another by at least 5 wt% ethylene. Unless otherwise indicated, this property of Intra-CD as referred to herein is based upon at least two 5 wt% portions of copolymer chain. The Intra-CD of copolymer in accordance with the present invention can be such that at least two portions of copolymer chain differ by at least 10 wt% ethylene. Differences of at least 20 wt%, as well as of at least 40 wt% ethylene are also considered to be in accordance with the present invention.

The experimental procedure for determining Intra-CD is as follows. First, the Inter-CD is established as described below, then the polymer chain is broken into fragments along its contour and the Inter-CD of the fragments is determined. The difference in the two results is due to Intra-CD as can be seen in the illustrative example below.

Consider a heterogeneous sample polymer containing 30 monomer units. It consists of 3 molecules designated A, B, C.

A EEEEPEEEPEEEPPEEPPEPPPEPPPPPPP B EEEEEPEEEPEEEPPEEEPPPEPPPEEPPP C EEPEEEPEEEPEEEPEEEPPEEPPPEEPPP Molecule A is 36.8 wt% ethylene, B is 46.6%, and C is 50% ethylene. The average ethylene content for the mixture is 44.3%. For this sample the Inter-CD is such that the highest ethylene polymer contains 5.7% more ethylene than the average while the lowest ethylene content polymer contains 7.5% less ethylene than the average. Or, in other words, 100 wt% of the polymer is within +5.7% and -7.5% ethylene about an average of 44.3%. Accordingly, the Inter-CD is 7.5% when the given wtZ of the polymer is 100%. The distribution may be represented graphically as by curve 1 in Figure 3.

If the chains are broken into fragments, there will be a new Inter-CD. For simplicity, consider first breaking only molecule A into fragments shown by the slashes as follows:

EEEEP/EEEPE/EEPPE/EPPEP/PPEPP/PPPPP Portions of 72.7%, 72.7%, 50%, 30.8%, 14.3% and 0% ethylene are obtained. If molecules B and C are similarly broken and the weight fractions of similar composition are grouped the new Inter-CD shown by curve 2 in Figure 3 is obtained. The difference between the two curves in the figure is due to Intra-CD.

Consideration of such data, especially near the end point ranges, demonstrates that for this sample at least 5% of the chain contour represented by the cumulative weight % range (a) differs in composition from another section by at least 15% ethylene shown as (b), the difference between the two curves. The difference is composition represented by (b) cannot be intermolecular. If it were, the separation process for the original polymer would have revealed the higher ethylene contents seen only for the degraded chain.

The compositional differences shown by (b) and (d) in the figure between original and fragmented chains give minimum values for Intra-CD. The Intra-CD must be at least that great, for chain sections have been isolated which are the given difference in composition (b) or (d) from the highest or lowest composition polymer isolated from the original. We know in this example that the original polymer represented at (b) had sections of 72.7% ethylene and 0% ethylene in the same chain. It is highly likely that due to the inefficiency of the fractionation process any real polymer with Intra-CD examined will have sections of lower or higher ethylene connected along its contour than that shown by the end points of the fractionation of the original polymer. Thus, this procedure determines a lower bound for Intra-CD. To enhance the detection, the original whole polymer can be fractionated (e.g., separate molecule A from molecule B from molecule C in the hypothetical example) with these fractions refractionated until they show no (or less) Inter-CD. Subsequent fragmentation of this intermolecularly homogeneous fraction now reveals the total Intra-CD. In principle, for the example, if molecule A were isolated, fragmented, fractionated and analyzed, the Intra-CD for the chain sections would be 72.7-0% = 72.7% rather than 72.7-50% = 22.7% seen by fractionating the whole mixture of molecules A, B and C.

In order to determine the fraction of a polymer which is intramolecularly heterogeneous in a mixture of polymers combined from several sources or as several modes in the case described here, the mixture must be separated into fractions which show no further heterogenity upon subsequent fractionation. These fractions are subsequently fractured and fractionated to reveal which are heterogeneous.

The fragments into which the original polymer is broken should be large enough to avoid end effects and to give a reasonable opportunity for the normal statistical distribution of segments to form over a given monomer conversion range in the polymerization. Intervals of ca 5 wt% of the polymer are convenient. For example, at an average polymer molecular weight of about 10⁵, fragments of ca 5000 molecular weight are appropriate. A detailed mathematical analysis of plug flow or batch polymerization indicates that the rate of change of composition along the polymer chain contour will be most severe at high ethylene conversions near the end of the polymerization. The shortest fragments are needed here to show the low propylene content sections.

The best available technique for determination of compositional dispersity for non-polar polymers is solvent/non-solvent fractionation which is based on the thermodynamics of phase separation. This technique is described in "Polymer Fractionation," M. Cantow editor, Academic 1967, p. 341 ff and in H. Inagaki, T. Tanaku, Developments in Polymer Characterization, 3, 1. (1982). These are incorporated herein by reference.

For non-crystalline copolymers of ethylene and propylene, molecular weight governs insolubility more than does composition in a solvent/non-solvent solution. High molecular weight polymer is less soluble in a given solvent mix. Also, there is a systematic correlation of molecular weight with ethylene content for the polymers described herein. Since ethylene polymerizes much more rapidly than propylene, high ethylene polymer also tends to be high in molecular weight. Additionally, chains rich in ethylene tend to be. less soluble in hydrocarbon/polar non-solvent mixtures than propylene-rich chains. Thus the high molecular weight, high ethylene chains are easily separated on the basis of thermodynamics.

A fractionation procedure is as follows: Unfragmented polymer is dissolved in n-hexane at 23 °C to form ca a 1% solution (1 g polymer/100 cc hexane). Isopropyl alcohol is titrated into the solution until turbidity appears at which time the precipitate is allowed to settle. The supernatant liquid is removed and the precipitate is dried by pressing between Mylar (polyethylene terphthalate) film at 150°C. Ethylene content is determined by ASTM method D-3900. Titration is resumed and subsequent fractions are recovered an analyzed until 100% of the polymer is collected. The titrations are ideally controlled to produce fractions of 5-10% by weight of the original polymer especially at the extremes of composition.

To demonstrate the breadth of the distribution, the data are plotted as % ethylene versus the cumulative weight of polymer as defined by the sum of half the weight % of the fraction of that composition plus the total weight % of the previously collected fractions.

Another portion of the original polymer is broken into fragments. A suitable method for doing this is by thermal degradation according to the following procedure: In a sealed container in a nitrogen-purged oven, a 2 mm thick layer of the polymer is heated for 60 minutes at 330°C. This should be adequate to reduce a 10 molecular weight polymer to fragments of ca 5000 molecular weight. Such degradation does not change the average ethylene content of the polymer. This polymer is fractionated by the same procedure as the high molecular weight precursor. Ethylene content is measured, as well as molecular weight on selected fractions.

Ethylene content is measured by ASTM-D3900 for ethylene-propylene-copolymers between 35 and 85 wt% ethylene. Above 85% ASTM-D2238 can be used to obtain methyl group concentrations which are related to percent ethylene in an unambiguous manner for ethylene-propylene copolymers. When comonomers other than propylene are employed no ASTM tests covering a wide range of ethylene contents are available, however, proton and carbon 13 nuclear magnetic resonance can be employed to determine the composition of such polymers. These are absolute techniques requiring no calibration when operated such that all nucleii contribute equally to the spectra. For ranges not covered by the ASTM tests for ethylene-propylene copolymers, these nuclear magnetic resonance methods can also be used.

Molecular weight and molecular weight distribution are measured using a Waters 150 gel permeation chromatograph equipped with a Chromatix KMX-6 on-line light scattering photometer. The system is used at 135 °C with 1,2,4, trichlorobenzene as mobile phase. Showdex (Showa-Denko America, Inc.) polystyrene gel columns 802, 803, 804 and 805 are used. This technique is discussed in "Liquid Chromatography of Polymers and Related Materials III," J. Cazes editor. Marcel Dekker, 1981, p. 207 (incorporated herein by reference). No corrections for column spreading are employed; however, data on generally accepted standards, e.g., National Bureau of Standards Polyethene 1484 and anionically produced hydrogenated polyisoprenes (an alternating ethylene-propylene copolymer) demonstrate that such corrections on Mw/Mn or M_z/M_w are less than .05 unit.

Mw/Mn is calculated from an elution time-molecular weight relationship whereas M_z/M_w is evaluated using the light scattering photometer. The numerical analyses can be performed using the commercially available computer softwear GPC2 , MOLWT2 available form LDC/Milton Roy-Riviera Beach, Florida.

Since the tubular reactor is the preferred reactor system for carrying out processes in accordance with the present invention, the following illustrative descriptions and examples are drawn to that system, but will apply to other reactor systems as will readily occur to those skilled in the art having the benefit of the present disclosure.

In practicing processes in accordance with the present invention, use is preferably made of at least one tubular reactor. Thus, in its simplest form, such a process would make use of but a single reactor. However, more than one reactor can be used, either in parallel, or in series with multiple monomer feeds.

For example, various structures can be prepared by adding additional monomer(s) during the course of the polymerization, as shown in Fig. 4, wherein composition is plotted versus position along the contour length of a polymer chain. The structure shown in curve 1 is obtained by feeding all of the monomers to the tubular reactor inlet or at the start of a batch reaction. In comparison, the structure depicted in curve 2 can be made by adding additional ethylene at a point along the tube or at a time in a batch reactor, where the chains have reached about half their length. Curve 3 requires multiple feed additions. The structure depicted by curve 4 can be formed if additional comonomer rather than ethylene is added. This structure permits a whole ethylene composition range to be omitted from the chain. In each case, a third or more comonomers may be added.

The composition of the catalyst used to produce alpha-olefin copolymers has a profound effect on copolymer product properties such as compositional dispersity and MWD. The catalyst utilized in practicing processes in accordance with the present invention should be such as to yield a controlled number of active species, each of which must be capable of simultaneous initiation of chains and must minimize chain transfer. Each active catalyst species generated either by multiple catalyst feeds or by a single catalyst feed that generates multiple active species must produce copolymer product in accordance with the present invention, e.g., a copolymer of narrow MWD. The extent to which a catalyst species contributes to the polymerization can be readily determined using the below described techniques for characterizing catalyst according to the number of active catalyst species.

Techniques for characterizing catalyst according to the number of active catalyst species are within the skill of the art, as evidenced by an article entitled "Ethylene-Propylene Copolymers. Reactivity Ratio, Evaluation and Significance," C. Cozewith and G. Ver Strate, Macromolecules, 4, 482 (1971), which is incorporated herein by reference.

It is disclosed by the authors that copolymers made in a continuous flow stirred reactor (CFSTR) should have an MWD characterized by M_w/M_n=2 and a narrow intermolecular compositional distribution when one active catalyst species is present. By a combination of fractionation and gel permeation chromatography (GPC) it is shown that for single active species catalysts the compositions of the fractions vary no more than ±3% about the average and the MWD (weight to number average ratio) for these samples approaches two (2). It is this latter characteristic (M_w/M_n of about 2) that is deemed the more important in identifying a single active catalyst species. On the other hand, other catalysts gave copolymer with an compositional variation greater than ±10% about the average and multi-modal MWD often with M_w/M_n greater than 10. These other catalysts are deemed to have more than one active species.

Catalyst systems to be used in carrying out processes in accordance with the present invention may be Ziegler catalysts, which may typically include components selected from:

(a) a compound of a transition metal, i.e., a metal of Groups I-B, III-B, IVB, VB, VIB, VIIB and VIII of the Periodic Table, and (b) an organometal compound of a metal of Groups I-A, II-A, II-B and III-A of the Periodic Table.

The preferred catalyst system in practicing processes in accordance with the present invention comprises hydrocarbon-soluble vanadium compound in which the vanadium valence is 3 to 5 and organo-aluminum compound, with the provision that the catalyst system yields one active catalyst species which has the capability to produce narrow MWD copolymers as described above. At least one of the vanadium compound/organo- aluminum pair selected must also contain a valence- bonded halogen.

In terms of formulas, vanadium compounds useful in practicing processes in accordance with the present invention could be:

(I) VOCl_x(OR) _3-x where x = 0-3 and R = a hydrocarbon radical;

(II) VCl₄;

(III) VO(AcAc)₂, where AcAc = acetyl acetonate;

(IV) V(AcAc)₃;

(V) VOCl_x(AcAc)_3-x, where x = 1 or 2 ; and (VI) VCl₃.nB,

Where n = 2-3 and B = Lewis base capable of making hydrocarbon-soluble complexes with VCl₃, such as tetrahydrofuran, 2-methyl-tetrahydrofuran and dimethyl pyridine.

In formula I above, R preferably represents a C₁ to C₁₀ aliphatic, alicyclic or aromatic hydrocarbon radical such as ethyl (Et), phenyl, isopropyl, butyl, propyl, n-butyl, i-butyl, t-butyl, hexyl, cyclohexyl, octyl, naphthyl, etc. Non-limiting, illustrative examples of formula (1) and (2) compounds are vanadyl tri-halides, alkoxy halides and alkoxides such as VOCl₃, VOCl₂(OBu) where Bu = butyl, and VO(OC₂H₅)₃. The most preferred vanadium compounds are VCl₄, VOCl₃, and VOCl₂(OR).

As already noted, the co-catalyst is preferably organo-aluminum compound. In terms of chemical formulas, these compounds could be as follows: AlR₃, Al(OR')R₂, AlR₂Cl, R₂Al-O-AlR'₂, AlR'RCl AlR₂I; Al₂R₃Cl₃ AlRCl₂ , and mixtures thereof where R and R' represent hydrocarbon radicals, the same or different, as described above with respect to the vanadium compound formula. The most preferred organo-aluminum compound is an aluminum alkyl sesquichloride such as Al₂Et₃Cl₃ or Al₂(iBu)₃- Cl₃. In one embodiment of the invention the aluminum compound can be described by the formula AlR_nX_3-n where R is as previously defined, X is halogen, preferably chlorine and n can vary from 1 to 2.

When catalysts are desired that produce a single active species, catalysts comprised of VOCl₃ or VCl₄ with Al₂R₂Cl₃, preferably where R is ethyl, have been shewn to be particularly effective. For best catalyst performance, the molar amounts of catalyst components added to the reaction mixture should provide a molar ratio of aluminum/vanadium (Al/V) of at least about 2. The preferred minimum Al/V is about 4. The maximum Al/V is based primarily on the considerations of catalyst expense and the desire to minimize the amount of chain transfer that may be caused by the organo-aluminum compound (as explained in detail below). Since, as is known certain organo-aluminum compounds act as chain transfer agents, if too much is present in the reaction mixture the Mw/Mn of the copolymer may rise above 2.

Based on these considerations, the maximum Al/V can be about 25, however, a maximum of about 17 is more preferred. The most preferred maximum is about 15.

Chain transfer agents for the Ziegler-catalyzed polymerization of alpha-olefins are well known and are illustrated, by way of example, by hydrogen or diethyl zinc for the production of EPM and EPDM. Such agents are very commonly used to control the molecular weight of EPM and EPDM produced in continuous flow stirred reactors. For the essentially single active species Ziegler catalyst systems used in accordance with the present invention, addition of chain transfer agents to a CFSTR reduces the polymer molecular weight but does not affect the molecular weight distribution. On the other hand, chain transfer reactions during tubular reactor polymerization in accordance with the present invention broaden polymer molecular weight distribution. Thus the presence of chain transfer agents in the reaction mixture should be minimized or omitted altogether. Although difficult to generalize for all possible reactions, the amount of chain transfer agent used should be limited to those amounts that provide copolymer product in accordance with the desired limits as regards MWD and compositional dispersity. It is believed that the maximum amount of chain transfer agent present in the reaction mixture could be as high as about 0.2 mol/mol of transition metal, e.g., vanadium, again provided that the resulting copolymer product is in accordance with the desired limits as regards MWD and compositional dispersity. Even in the absence of added chain transfer agent, chain transfer reactions can occur because propylene and organo-aluminum cocatalyst can also act as chain transfer agents. In general, among the organo-aluminum compounds that in combination with the vanadium compound yield just one active species, the organo-aluminum compound that gives the highest copolymer molecular weight at acceptable catalyst activity should be chosen. Furthermore, if the Al/V ratio has an effect on the molecular weight of copolymer product, that A1/V should be used which gives the highest molecular weight also at acceptable catalyst activity. Chain transfer with propylene can best be limited by avoiding excessive temperature during the polymerization as described below.

Molecular weight distribution is also broadened by catalyst deactivation during the course of the polymerization which leads to termination of growing chains. It is well known that the vanadium-based Ziegler catalysts used in accordance with the present invention are subject to such deactivation reactions which depend to an extent upon the composition of the catalyst. Although the relationship between active catalyst lifetime and catalyst system composition is not known at present, for any given catalyst, deactivation can be reduced by using the shortest residence time and lowest temperature in the reactor that will produce the desired monomer conversions.

Polymerizations in accordance with the present invention should be conducted in such a manner and under conditions sufficient to initiate propagation of essentially all copolymer chains for each particular catalyst species simultaneously. This can be accomplished by utilizing the process steps and conditions described below. The catalyst components are preferably premixed, that is, reacted to form active catalyst outside of the reactor, to ensure rapid chain initiation. Aging of the premixed catalyst system, that is, the time spent by the catalyst components (e.g., vanadium compound and ergεnoaluminum) in contact with one another outside of the reactor, must be kept within certain limits. If not aged for a sufficient period of time, the components will not have reacted with each other sufficiently to yield an adequate quantity of active catalyst species, with the result of continued catalyst species formation in the reactor, resulting in non-simultaneour chain initiation. Also, it is known that the activity of the catalyst species will decrease with time so that the aging must be kept below a maximum limit. The minimum aging period, depending on such factors as concentration of catalyst components, temperature and mixing equipment, can be as low as about 0.1 second. The maximum aging period is that period of aging after which the catalyst species has been deactivated to the point where it cannot effectively be used in the polymerization process. In practice there is no appreciable advantage in allowing the catalyst to age longer than a time sufficient to fully react all of the available catalyst components thereby generating all of the active catalyst species which will be available for polymerization. Generally, the aging time will ordinarily be about 0.1 seconds to about 200 seconds or even longer, usually about 0.5 seconds to 100 seconds, preferably about 1 second to 50 seconds. The premixing performed at low temperature such as 40 ºC or below. It is preferred that the mixing be performed at 25°C or below, with 15°C or below being most preferred.

Where more than one catalyst is combined into a single catalyst feed stream, each catalyst and cocatalyst can be premixed separately. The several pre-mixed streams of catalysts species are then combined and fed to the reactor. Alternately, the several pre-mixed catalyst feed streams can be fed separately to different points along the reactor.

The temperature of the reaction mixture should also be kept with certain limits. The temperature at the reactor inlet should be high enough to provide complete, rapid chain initiation at the start of the polymerization reaction. The length of time the reaction mixture spends at high temperature must be short enought to minimize the amount of undesirable chain transfer and catalyst deactivation reactions.

Temperature control of the reaction mixture is complicated somewhat by the fact that the polymerization reaction generates large quantities of heat. This problem is, preferably, taken care of by using prechilled feed to the reactor to absorb the heat of polymerization. With this technique, the reactor is operated adiabatically and the temperature is allowed to increase during the course of polymerization. As an alternative to feed prechill, heat can be removed from the reaction mixture, for example, by a heat exchanger surrounding at least a portion of the reactor or by well-known autorefrigeration techniques in the case of batch reactors or multiple stirred reactors in series.

Where an adiabatic reactor operation is used, the inlet temperature of the reactor feed can be about -80°C to about 50°C. The outlet temperature of the reaction mixture can be as high as about 200°C. The preferred maximum outlet temperature is about 70°C. The most preferred maximum is about 50°C. In the absence of reactor cooling, such as by a cooling jacket, to remove the heat of polymerization, the temperature of the reaction mixture will increase from reactor inlet to outlet by an amount dependent upon the heat of polymerization, reaction mixture specific heat and the percent of copolymer in the reaction mixture (weight of copolymer per weight of solvent). For ethylene-propylene copolymerization in hexane the temperature rise is about 13°C per weight percent of copolymer.

Having the benefit of the above disclosure, those skilled in the art can determine the operating temperature conditions for making copolymer in accordance with the present invention. For example, assume an adiabatic reactor and an outlet temperature of 35°C are desired for an ethylene-propylene reaction mixture in hexane containing 5% copolymer. The reaction mixture will increase in temperature by about 13°C for each weight percent copolymer or 5 weight percent x 13°C/wt% = 65°C. To maintain an outlet temperature of 35°C, it will thus require a feed that has been prechilled to 35°C-65°C = -30°C. In the instance that external cooling is used to absorb the heat of polymerization, the feed inlet temperature could be higher with the other, temperature constraints described above otherwise being applicable.

Because of heat removal and reactor temperature limitations, the preferred maximum copolymer concentration at the reactor outlet when this is the only stream drawn from the reactor is 25 wt/100 wt diluent. The most preferred maximum concentration is 15 wt/100 wt. When multiple streams of reaction mixture are withdrawn from the reactor ' and each part of the reaction mixture withdrawn is blended with other parts of reaction mixture withdrawn, the blend so formed has a preferred maximum copolymer concentration of about 25 wt./100 wt. of diluent. The most preferred maximum is 15 wt./100 wt. diluent. In the case of either single or multiple product stream withdrawal, there is no lower limit to concentration due to reactor operability, but for economic reasons it. is preferred to have a copolymer concentration of at least 2 wt/100 wt. Most preferred is a concentration of at least 3 wt/100 wt. The rate of flow of the reaction mixture through the reactor should be high enough to provide good mixing of the reactants in the radial direction and minimize mixing in the axial direction. Good radial mixing is beneficial to minimize radial temperature gradients due to the heat generated by the polymerization reaction. Radial temperature gradients will tend to broaden the molecular weight distribution of the copolymer since the polymerization rate is faster in the high temperature regions resulting from poor heat dissipation. The artisan will recognize that achievement of these objectives is difficult in the case of highly viscous solutions. This problem can be overcome to some extent through the use of radial mixing devices such as static mixers (e.g., these produced by the Kenics Corporation).

Residence time of the reaction mixture in the mix-free reactor can vary over a wide range. The minimum can be .as low as about 1 second. A preferred minimum is about 10 seconds. The most preferred minimum is about 15 seconds. The maximum can be as high as about 3600 seconds. A preferred maximum is about 1800 seconds. The most preferred maximum is about 900 seconds.

With reference to the accompanying drawings, particularly Fig 1, reference numeral 1 refers to a premixing device for premixing the catalyst components. For purposes of illustration, it is assumed that a copolymer of ethylene and propylene (EPM) is to be produced using as catalyst components vanadium tetrachloride and ethyl aluminum sesquichloride. The polymerization is an adiabatic, solution polymerization process using hexane solvent for both the catalyst system and the reaction mixture.

The premixing device 1 comprises a temperature control bath 2, a fluid flow conduit 3 and mixing device 4 (e.g., a mixing tee). To mixing device 4 are fed hexane solvent, vanadium tetrachloride and ethyl aluminum sesqui chloride through feed conduits 5, 6 and 7, respectively. Upon being mixed in mixing device 4, the resulting catalyst mixture is caused to flow within conduit 3, optionally in the form of a coiled tube, for a time long enough to produce the active catalyst species at the temperature set by the temperature bath. The temperature of the bath is set to give the desired catalyst solution temperature in conduit 3 at the outlet of the bath.

Upon leaving the premixing device, the catalyst solution flows through conduit 8 into mixing zone 9 to provide an intimate mixing with hexane solvent and reactants (ethylene and propylene) which are fed through conduit 10. Any suitable mixing device can be used, such as a mechanical mixer, orifice mixer or mixing tee. For economic reasons, the mixing tee is preferred. The residence time of the reaction mixture in mixing zone 9 is kept short enough to prevent significant polymer formation therein before being fed through conduit 11 to tubular reactor 12. Alternatively, streams 8 and 10 can be fed directly to the inlet of reactor 12 if the flow rates are high enough to accomplish the desired level of intimate mixing. The hexane with dissolved monomers may be cooled upstream of mixing zone 9 to provide the desired feed temperature at the reactor inlet.

The tubular reactor is shown with optional feed and take off points. Where the catalyst comprises only a single polymer species one or more take off points, 13, are used to withdraw polymer fractions at different points along the polymerization path. In order to maintain constant flow, additional solvent may be added to make up the volume of material withdrawn. Additional catalyst and monomer can be introduced through line, 14, or line, 15. The polymer withdrawn through line, 13, is combined with all other fractions withdrawn and collected with the reactor effluent for deashing and finishing. Where more than one catalyst species is used, multiple premixing devices, 1, are used. The mixed catalyst can be directed to mixing zone, 9, for mixing with additional catalyst species and monomer or the effluent from the premixing devices can be combined prior to the mixing zone.

Where a mixture of VCl₄ and VOCl₃ is used as the catalyst species in conjunction with ethylaluminum sesquichloride (EASC), the molar ratio of VCl₄/VOCl₃ can be about 0.01 to about 100, more preferably about 0.1 to about 10, most preferably about 0.5 to about 5. The amount of the total polymer and the molecular weight of each component will be determined by the ratio and the feed locations and take off points along the reactor.

The molar ratio of alkyl aluminum sesquihalide to vanadium components (VCl₄ plus VOCl₃) can be about 1 to about 40, preferably about 2 to about 40, more preferably about 4 to about 20, most preferably about 4 to about 10, e.g., about 5 to about 10. The alkyl group of the sesquihalide is preferably a C₁-C₆ alkyl group, preferably ethyl. The halide can be bromine, chlorine or iodine, preferably chlorine. The preferred aluminum co-catalyst is ethylaluminum sesquichloride (EASC). In this system the two independent, non-interacting, mutually compatible catalyst systems are VCl₄/EASC and VOCI₃/EASC.

In a preferred embodiment, a Lewis base moderator is incorporated into the catalyst system. The molar ratio of base to vanadium can be about 0 to about 5/1, preferably about 0.5/1 to about 2/1, more preferably about 1/1 to about 1.5/1. Illustrative, non- limiting examples of Lewis bases suitable for use in the practice of this invention are NH₃, phenol, cyclohexanone, tetrahydrofuran, acetylacetone, ethyl silicate and tri-n-butyl-phosphate. The Lewis base suppresses some long chain branching reactions when EPDM terpolymers are prepared. The polymer derived from the process of this invention is deashed and finished using conventional methods. Where the polymodal MWD is achieved by withdrawing product and different points or times from the reactor, the polymer streams are preferably blended and a single deashing and finishing process used. The result is a thoroughly mixed, homogeneous polymer blend. Alternately, each process stream can be finished independently and combined by mechanical mixing.

Having thus described the above illustrative reactor system, it will readily occur to the artisan that many variations can be made within the scope of the present invention. For example, the placement and number of multiple feed sites, the choice of temperature profile during polymerization and the concentrations of reactants can be varied to suit the end-use application.

By practicing processes in accordance with the present invention, ethylene-alpha-olefin copolymers having polymodal MWD with each molecular weight fraction having very narrow MWD can be made by direct polymerization. Although narrow MWD copolymers can be made using other known techniques, such as by fractionation or mechanical degradation, these techniques are considered to be impractical to the extent of being unsuitable for commercial-scale operation. With respect to EPDM made in accordance with the present invention, the products have enhanced cure properties at a given Mooney Viscosity.

Where the polymodal molecular weight distribution is achieved by withdrawing polymer fractions from the reactor, it will be evident from reference to this disclosure that it is critical when or where polymer is withdrawn from the reaction zone. This can be determined without undue experimentation. For example, a pilot plant scale tubular reactor can be equipped with a multiplicity of take off points. By running the reactor and withdrawing polymer samples from the system, molecular weight of the polymer at points along the reactor can be determined.

By converting the distance along the tube to time of reaction after introduction of catalyst, a plot can be made of molecular weight as a function of reaction time for a given catalyst/monomer/solvent system. The molecular weight/reaction time plot can be used to position take off points. For flexibility in selecting the product characteristics of a particular polymodal MWD product, a multiplicity of take off points can be installed, not all of which will be used in preparing a particular product with predetermined specifications.

Similarly, inlet ports can be located at different locations for the introduction of additional mcnomer or catalyst streams. By introducing fresh catalyst and monomer downstream of the inlet, the MWD of the polymer will be modified. So long as the polymerization is carried out in this manner the polymer will be a polymodal MWD polymer of narrow MWD modes . Similar results are achieved by introducing fresh premixed catalyst with the additional monomer feed.

It will be evident from this disclosure to those skilled in the art that the polymodal MWD polymers of this invention can be prepared by blending the product of runs prepared under different conditions or using different catalyst. For example, one polymerization can be conducted using VCl₄ /EASC as the catalyst and another conducted using VOCI₃/EASC as the catalyst. The product of the two runs can then be blended to form a bimodal MWD polymer blend. Other variations can be used to generate polymer species of different M_w to prepare polymodal MWD compositions.

The advantages of the instant invention may be mere readily appreciated by reference to the following examples. Example I

This example illustrates the method of this invention for preparing an EPM wherein polymer product is removed from the reactor at a point intermediate between the reactor inlet and outlet. The polymerization was conducted in a 3/8 in. diameter tube and the residence time in the reactor was 30 seconds. A take off port was located downstream of the inlet at a distance equivalent to 1 second residence time.

Hexane was used as the solvent, VCl₄ as the catalyst, and Al₂Et₃Cl₃ as the cocatalyst. Hexane is purified prior to use by passing over 4A molecular sieves (Union Carbide, Linde Div. 4A 1/16" pellets) and silica gel (W.R. Grace Co. , Davidson Chemical Div. , PA-400 20-4 mesh) to remove polar impurities which act as catalyst poisons. Gaseous, ethylene and propylene is passed over hot (270°C) CuO (Harshaw Chemical Co., C01900 ¼" spheres) to remove oxygen followed by molecular sieve treatment for water removal and then combined with hexane upstream of the reactor and passed through a chiller which provided a low enough temperature to completely dissolve the monomers in the hexane.

A catalyst solution is prepared by dissolving 18.5 g of vanadium tetrachloride, VCl₄, in 5.0 1. of purified n-hexane. The cocatalyst consists of 142 g of ethylaluminum sesquichloride, Al₂Et₃Cl₃, in 5.0 1. of purified hexane. The two solutions are premixed at 10°C and aged for 8 seconds. Typical feed rates and reacting conditions are shown in Table I.

A product stream is withdrawn from the take off port at about 17 kg/hr and blended with effluent frcm the reactor outlet. Approximately 20 wt% of the polymer in the effluent came from the take off port. The molecular weight of the product from the take off pert is about one-half of that from the reactor outlet with a similar MWD (M_w/M_n = 1.4, M_z/M_w = 1.3). The product is deashed and stripped. The resulting polymer is a bimodal MWD EPM with a theoretical M_w/M_n = 1.96 and M_z/M_w = 1.46.

Example II

Example I is repeated except that no effluent is taken from the take off port and two reactors in parallel are used. The feed rates listed in Table 1 are split so that 17 kg./hr are passed through the reactor with one second residence time, and the remaining feed goes to the other reactor. The residence times in these two reactors are 1 and 30 seconds, respectively. Otherwise all conditions are the same as in Example I. The effluents frαn the reactor outlets are blended. After steady state is achieved, the blend is deashed, washed and stripped of solvent. The resulting polymer is a bimodal MWD EPM with a theoretical MWD as in Example I. Example III

Example I is repeated except that no effluent is taken from the take off port and VOCI₃/EASC is used as an additional catalyst.

The second catalyst solution is prepared by dissolving 18.5g of VOCI₃ in 5.0 1. of purified hexane. The cocatalyst consists of 142g of Al₂Et₃Cl₃ in 5.0 1. of purified hexane. The VCl₄ and VOCl₃ are blended with cocatalysts in separate premixing units and aged for ten seconds. The two premixed catalyst streams are then mixed with the monomer/ hexane stream and fed into the reactor. Reactor residence time is 50 seconds. Otherwise all conditions are the same as in Example I. After steady state is achieved, the reactor effluent is deashed, washed and stripped of solvent. The resulting polymer is a bimodal MWD EPM.

Example IV

Example I is repeated except that no effluent is taken from the take off port. The catalyst system used is vanadium oxytrichloride (VOCI₃) and diethylaluminum chloride (AlEt₂Cl). Otherwise all conditions are the same as in Example I. This catalyst system produces at least two independent catalyst species, each of which initiates a separate MWD mode. After steady state is achieved, the reactor effluent is deashed, washed and stripped of solvent. The resulting polymer is a polymodal MWD EPM.

Example V Example I is repeated except that no take off port effluent is collected and the catalyst and feed streams are split. About 2/3 of the monomer/hexane stream and 2/3 of the premixed catalyst are mixed and fed to the reactor inlet and the remaining 1/3 of the monomer/hexane feed is mixed with the remaining catalyst stream and fed into the reactor at a point midway between the reactor inlet and outlet. The EPM product is a polymodal MWD polymer.

Example VI

Example I is repeated except that no effluent is taken from the take off port and a catalyst reactivator is used. The catalyst reactivator solution is prepared by dissolving 30.5g of butyl perchlorocrotonate in 3.0 1 of purified hexane. This solution is fed into the reactor, at 3.6 g/hr along with 50 g/hr of ethylene, at a point midway between the reactor inlet and outlet. Otherwise all conditions are the same as in Example I. After steady state is achieved, the effluent is deashed, washed and stripped of solvent. The resulting product is a polymodal MWD EPM.

It will be appreciated by those skilled in the art who have reference to this disclosure that where reference is made to the beginning of polymerization, in a continuous process, this is intended to mean the time at which catalyst is introduced. Similarly, the end of the polymerization in a tubular reactor means at the point where the polymerization is terminated.

Where reference is made to blends being made by combining product or reaction mixtures withdrawn from the reactor at one or more times after the start of polymerization with product from the "reactor outlet" or "completion of polymerization" this language is intended to include the last product or reaction mixture withdrawn from the reactor for the purpose of forming the blend whether or not the last product or reaction mixture is obtained from the physical reactor outlet or at the actual completion of polymerization, notwithstanding the fact that product from the actual reactor outlet or actual completion of polymerization is used for some purpose other than blending with fractions of polymer withdrawn.

Claims

WHAT IS CLAIMED IS:

1. In a polymerization process for producing copolymer from a reaction mixture comprised of catalyst and a monomer feed comprising ethylene, at least one other alpha-olefin monomer and, optionally, a non-conjugated diene, the improvement which comprises producing a polymodal MWD copolymer by conducting the polymerization:

(a) in at least one reactor, said reactor being a substantially mix free reactor;

(b) with essentially one active catalyst species;

(c) using at least one reaction mixture which is essentially transfer-agent free;

(d) in such a manner and under conditions sufficient to initiate propagation of essentially all copolymer chains simultaneously;

(e) withdrawing a part of the reaction mixture- containing copolymer from the reactor at, at least two predetermined times after the start of polymerization; and

(f) blending the polymer withdrawn at each such predetermined time; thereby producing a polymodal MWD copolymer comprising at least two different molecular weight modes wherein each mode has a narrow MWD and at least one of two characteristics, (1) an M_w/M_n of less than 2 and (2)

M_z/M_w of less than 1.8.

2. The process according to claim 1 wherein the reactor comprises a tubular reactor having a multiplicity of take off ports.

3. The process according to claim 2 wherein the polymer from said take off port and reactor outlet are blended by combining the reaction mixtures collected, and subsequently recovering the polymer from the combined reaction mixture.

4. The process according to claim 1 wherein the catalyst comprises a Ziegler catalyst.

5. The process according to claim 4 wherein the catalyst comprises a hydrocarbon-soluble vanadium compound and an organo-aluminum compound which react to form essentially one active catalyst species, at least one of the vanadium compound and organo-aluminum compound containing a valence-bonded halogen.

6. The process according to claim 1 wherein the temperature of the reaction mixture at the initiation of polymerization is about -80°C to 50°C.

7. The process according to claim 1 wherein the maximum temperature of the reaction mixture at the completion of polymerization is about 200°C.

8. The process according to claim 4 wherein the. polymerization is a solution polymerization.

9. The process according to claim 4 wherein the catalyst components are premixed.

10. The process according to claim 9 wherein the premixed catalyst components are aged for at least 0.5 seconds.

11. The process according to claim 5 wherein the mole ratio of aluminum to vanadium in the catalyst is about 2 to 25.

12. The process according to claim 1 wherein the polymerization is conducted in a solvent for the reaction mixture; each part of the reaction mixture withdrawn being blended with other parts withdrawn; the blend so formed having a copolymer concentration of about 3 to about 15% on a weight copolymer per weight of solvent basis.

13. The process according to claim 1 wherein the maximum temperature of the reaction mixture at the completion of polymerization is about 50°C.

14. The process according to claim 9 wherein the catalyst comprises components that are premixed and then aged for about 1 to 50 seconds.

15. The process according to claim 5 wherein the mole ratio of aluminum to vanadium in the catalyst is about 4 to 15.

16. The process according to claim 11 wherein the polymerization is conducted in a solvent for the reaction mixture, and wherein each part of the reaction mixture withdrawn from the reactor is blended with other parts withdrawn, and the blend so formed has a copolymer concentration of about 3% to 10% on a weight of polymer per weight of solvent basis.

17. The process according to claim 5 wherein the catalyst comprises:

(a) hydrocarbon-soluble vanadium compound selected from the group consisting of:

VOCl_x(OR)_3-x, where x=0-3 and R=hydrocarbon radical;

VCI₄ , V0(AcAc)₂, where AcAc=acetyl acetonate

V(AcAc)₃, where AcAc=acetyl acetonate

VOCl_χ(AcAc)_3-χ, where x=1 or 2 and AcAc=acetyl acetonate, and

VCl₃.nB, where n=2 to 3 and B=Lewis base capable of forming hydrocarbon-soluble complexes with

VCl₃; and

(b) an organo-aluminum compound selected from the group consisting of:

^AlR3 AlR₂Cl,

Al₂R₃CL₃,

AlRCl₂,

AlR'RCl,

Al(OR')R₂,

R₂Al-OAlR'₂,

AlR₂I and mixtures thereof, where R and R' are hydrocarbon radicals.

18. The process according to claim 5 wherein the catalyst comprises VCl₄ and Al₂R₃Cl₃ wherein R is a hydrocarbyl moiety.

19. The process according to claim 1 wherein the temperature of the reaction mixture at the completion of polymerization is about 70°C.

20. The process according to claim 1 wherein the polymerization is adiabatic.

21. The process according to claim 1, which is continuous and is conducted in hexane solvent.

22. The process according to claim 1 wherein said polymerization is conducted in at least one tubular reactor.

23. The process according to claim 22 wherein said reaction mixture further comprises diene, and wherein at least one of said ethylene, other alpha-olefin monomer and diene are fed to said tubular reactor at multiple feed sites.

24. The process according to claim 18 wherein R is ethyl.

25. The product prepared according to the process of claim 1.

26. The product according to claim 25 wherein said copolymer product is cured.

27. The product according to claim 25 wherein said copolymer product is blended with basestock lubricating oil.

28. The product according to claim 27 wherein said copolymer product is blended with the basestock lubricating oil in an amount from about .001 to 49 wt%. copolymer based on oil plus copolymer.

29. A method for preparing a polymodal MWD ethylene copolymer which comprises:

(a) conducting the polymerization in a substantially mix free reactor;

(b) using at least two catalysts, each of which initiates growth of polymer chains that attain a different average molecular weight than that initiated by the other catalyst;

(c) using at least one reaction mixture comprising ethylene, at least one alpha-olefin monomer and, optionally, a non-conjugated diene, said reaction mixture being essentially transfer-agent free;

(d) in such a manner and under such conditions sufficient to initiate propagation of essentially all copolymer chains made by a particular catalyst species simultaneously; thereby producing a polymodal MWD ethylene copolymer comprising at least two different molecular weight modes wherein each mode having a narrow MWD and at least one of two characteristics, (1) an M_w/M_n of less than 2 and (2) M_z/M_w of less than 1.8.

30. The process according to claim 29 wherein the catalyst comprises a Ziegler catalyst.

31. The process according to claim 29 wherein each catalyst comprises a hydrocarbon-soluble vanadium ccrpound and an organo-aluminum compound which react to form essentially one active catalyst species, at least one of the vanadium compound and organo aluminum compound containing a valence-bonded halogen.

32. The process according to claim 31 wherein each catalyst comprises:

VOCl_x(OR)_3-x' where x=0 to 3 and R=hydrocarbon radical;

VCI₄ ; VO (AcAc)₂, where AcAc=acetyl acetonate;

V(AcAc)₃ where AcAc=acetyl acetonate;

VOCl_x(AcAc)_3-x where x=1 or 2 and AcAc=acetyl acetonate; and

VCl₃.nB, where n=2 to 3 and B=Lewis base capable of forming hydrocarbon-soluble complexes with VCl₃; and

(b) organo-aluminum compound selected from the group consisting of:

AlR₃

AlR₂Cl,

Al₂R₃CL₃, AlRCl₂ ,

AlR'RCl,

Al(OR')R₂, R₂Al-OAIR'₂,

AlR₂I and mixtures thereof, where R and R' are hydrocarbon radicals.

33. The process according to claim 32 wherein a first catalyst comprises VCl₄ and Al₂R₃Cl₃; and a second catalyst comprises VOCI₃ and Al₂R'₃Cl₃ where R and R' are the same or different hydrocarbyl moiety.

34. The process according to claim 33 wherein R and R' are ethyl.

35. The process according to claim 29 wherein the reactor is a tubular reactor.

36. The process according to claim 29 wherein the temperature of the reaction mixture at the initiation of polymerization is about -80°C to 50°C.

37. The process according to claim 29 wherein the maximum temperature of the reaction mixture at the completion of polymerization is about 200°C.

38. The process according to claim 32 wherein the polymerization is a solution polymerization.

39. The process according to claim 30 wherein the catalyst components are premixed.

40. The process according to claim 31 wherein the mole ratio of aluminum to vanadium in the catalyst is about 2 to 25.

41. The process according to claim 39 wherein the catalyst components are premixed and then aged for at least 0.5 seconds.

42. The process according to claim 38 wherein the polymerization is conducted in a solvent for the reaction mixture wherein the copolymer concentration in the reaction mixture at the completion of polymerization is about 3 to about 15% on a weight copolymer per weight of solvent basis.

43. The process according to claim 29 wherein the maximum temperature of the reaction mixture at the completion of polymerization is about 50°C.

44. The process according to claim 39 wherein the catalyst comprises components that are premixed and then aged for about 1 to 50 seconds.

45. The process according to claim 38 wherein the mole ratio of aluminum to vanadium in the catalyst is about 4 to 15.

46. The process according to claim 45 wherein the polymerization is conducted in a solvent for the reaction mixture, and wherein the copolymer concentration in the reaction mixture at the completion of polymerization is about 3% to 10% on a weight of polymer per weight of solvent basis.

47. The process according to claim 29 wherein the maximum temperature of the reaction mixture at the completion of polymerization is about 70°C.

48. The process according to claim 29 wherein the polymerization is adiabatic.

49. The process according to claim 29 wherein the polymerization is continuous and is conducted in hexane solvent.

50. The process according to claim 49 wherein said reaction mixture further comprises diene, and wherein at least one of said ethylene, other alpha-olefin monomer and diene are fed to said tubular reactor at multiple feed sites.

51. In a polymerization process for producing copolymer from a reaction mixture comprised of catalyst and a monomer feed comprising ethylene, at least one other alpha-olefin monomer, and optionally, at least one non-conjugated diene, the improvement which comprises producing a polymodal MWD copolymer by conducting the polymerization:

(a) in at least two reactors, said reactors each being a substantially mix free; (b) with essentially one active catalyst species in each reactor;

(c) using at least one reaction mixture in each reactor which is essentially transferagent free in each reactor;

(e) blending the polymers from each reactor; and

(f) recovering the blended polymers; thereby producing a polymodal MWD ethylene copolymer comprising at least two different molecular weight modes wherein each mode having a narrow MWD and at least one of two characteristics, (1) an M_w/M_n of less than 2 and and M_z/M_w of less than 1.8.

52. The process according to claim 51 wherein the catalyst comprises a Ziegler catalyst.

53. The process according to claim 52 wherein each catalyst species comprises a hydrocarbon-soluble vanadium compound and an organo-aluminum compound which react to form essentially one active catalyst species, at least one of the vanadium compound and organo aluminum compound containing a valence-bonded halogen.

54. The process according to claim 53 wherein each catalyst comprises:

VOCI_x(OR)_3-x, where x=0-3 and R=hydrocarbon radical;

VCI₄; VO (AcAc)₂, where AcAc=acetyl acetonate

V(AcAc)₃, where AcAc=acetyl acetonate

VOCl_x(AcAc)_3-x, where x=1 or 2 and AcAc-acetyl acetonate; and

VCl₃.nB, where n=2-3 and B=Lewis base capable of forming hydrocarbon-soluble complexes with VCI₃; and

(b) organo-aluminum compound selected from the group consisting of:

AIR₃ AIR₂Cl,

AlRCl₂,

AlR'RCl,

Al(OR')R₂,

R₂Al-OAlR'₂,

AlR₂I and mixtures thereof where R and R' are the same or different hydrocarbyl radicals.

55. The process according to claim 53 wherein a catalyst comprising VCl₄ and Al₂R₃CI₃ is used in a first reactor and a catalyst comprising VOCI₃ and Al₂R'₃Cl₃ is used in a second reactor wherein R and R' are the same or different hydrocarbyl moiety.

56. The process according to claim 55 wherein R and R' are ethyl.

57. The process according to claim 51 wherein the reactor is a tubular reactor.

58. The process according to claim 52 wherein the catalyst components are premixed.

59. The process according to claim 52 wherein the catalyst components are premixed and then aged.

60. The process according to claim 51 wherein the temperature of the reaction mixture at the initiation of polymerization is about -80°C to 50°C.

61. The process according to claim 51 wherein the maximum temperature of the reaction mixture at the completion of polymerization is about 200°C.

62. The process according to claim 59 wherein the catalyst components are aged for at least 0.5 seconds.

63. The process according to claim 52 wherein the mole ratio of aluminum ro vanadium in the catalyst is about 2 to 25.

64. The process according to claim 51 wherein the polymerization is a solution polymerization.

65. The process according to claim 51 wherein the polymerization is conducted in a solvent for the reaction mixture; and wherein the copolymer concentration in the reaction mixture at the completion of polymerization in each reactor is about 3 to about 15% on a weight copolymer per weight of solvent basis.

66. The process according to claim 51 wherein the maximum outlet temperature of the reaction mixture at the completion of polymerization is about 50°C.

67. The process according to claim 59 wherein the catalyst comprises components that are premixed and then aged for about 1 to 50 seconds.

68. The process according to claim 53 wherein the mole ratio of aluminum to vanadium in the catalyst is about 4 to 15.

69. The process according to claim 68 wherein the polymerization is conducted in a solvent for the reaction mixture, and wherein the copolymer concentration in the reaction mixture at the completion of polymerization in each reactor is about 3% to 10% on a weight of polymer per weight of solvent basis.

70. The process according to claim 51 wherein the maximum temperature of the reaction mixture at the completion of polymerization is about 70°C.

71. The process according to claim 51 wherein the polymerization is adiabatic.

72. The process according to claim 51 wherein the polymerization process is continuous and is conducted in hexane solvent.

73. The process according to claim 57 wherein said reaction mixture further comprises diene, and wherein at least one of said ethylene, other alpha- olefin monomer and diene are fed to said tubular reactor at multiple feed sites.

74. In a polymerization process for producing copolymer from a reaction mixture comprised of catalyst and a monomer feed comprising ethylene, at least one other alpha-olefin monomer, and optionally, at least one non-conjugated diene the improvement which comprises producing a polymodal MWD copolymer by conducting the polymerization:

(a) a substantially mix free reactor;

(b) with essentially one active catalyst species wherein said catalyst species exhibits a decay in activity with respect to polymerization time;

(d) in such a manner and under conditions sufficient to initiate propagation of essentially all copolymer chains formed from the catalyst species simultaneously;

(e) adding a catalyst reactivator to the reaction mixture after polymerization has progressed for a finite time; and

(f) recovering polymer at the completion of polymerization; thereby producing a polymodal MWD ethylene copolymer comprising at least two different molecular weight modes wherein each mode having a narrow MWD and at least one of two characteristics, (1) an M_w/M_n of less than 2 and and M_z/M_w of less than 1.8.

75. The process according to claim 74 wherein the catalyst comprises a Ziegler catalyst.

76. The process according to claim 75 wherein catalyst comprises a hydrocarbon-soluble vanadium compound and an organo-aluminum compound which react to form es s entiayly one active catalys t species , at leas t one of the vanadium compound and organo aluminum compound containing a valence-bonded halogen.

77. The process according to claim 76 wherein the catalyst comprises:

VOCl_x(OR)_3-x, where x=0-3 and R=hydrocarbon radical;

VCI₄;

VO (AcAc)₂, where AcAc=acetyl acetonate

V(AcAc)₃, where AcAc=acetyl acetonate

VOCl_x(AcAc)_3-x, where x=l or 2 and AcAc-acetyl acetonate; and

VCl₃.nB, where n=2-3 and B=Lewis base capable of forming hydrocarbon-soluble complexes with VCl₃; and

(b) organo-aluminum compound selected from the group consisting of:

AIR₃

AIR₂CI,

AI₂R₃CI₃,

AIRCI₂,

AlR'RCl,

AI(OR')R₂,

R₂AI-OAOR'₂, AIR₂I and mixtures thereof where R and R' are hydrocarbon radicals.

78. The process according to claim 76 wherein the catalyst comprises a VCl₄ and Al₂R₃CI₃ wherein R is a hydrocarbyl moiety.

79. The process according to claim 78 wherein R is ethyl.

80. The process according to claim 74 wherein the reactor is a tubular reactor having a first inlet port and at least one additional inlet port downstream of the first inlet port, catalyst reactivator being added through said additional inlet port.

81. The process according to claim 74 wherein the reactor is a batch reactor and the catalyst reactivator is added at a finite time after initiation of polymerization.

82. The process according to claim 74 wherein the temperature of the reaction mixture at the initiation of polymerization is about -80°C to 50°C.

83. The process according to claim 74 wherein the maximum temperature of the reaction mixture at the completion of polymerization is about 200°C.

84. The process according to claim 74 wherein the polymerization is a solution polymerization.

85. The process according to claim 75 wherein the catalyst components are premixed.

86. The process according to claim 85 wherein the catalyst components are premixed and then aged.

87. The process according to claim 86 wherein the premixed catalyst components are aged for at least 0.5 seconds.

88. The process according to claim 75 wherein the mole ratio of aluminum to vanadium in the catalyst is about 2 to 25.

89. The process according to claim 74 wherein the polymerization is conducted in a solvent for the reaction mixture and wherein the copolymer concentration in the reaction mixture at the completion of polymerization is about 3 to about 15% on a weight copolymer per weight solvent basis.

90. The process according to claim 74 wherein the maximum at the completion of polymerization temperature of the reaction mixture is about 50 °C.

91. The process according to claim 85 wherein the catalyst comprises components that are premixed and then aged for about 1 to 50 seconds.

92. The process according to claim 85 wherein the mole ratio of aluminum to vanadium in the catalyst is about 4 to 15.

93. The process according to claim 92 wherein the polymerization is conducted in a solvent for the reaction mixture, and wherein the copolymer concentration in the reaction mixture at the completion of polymerization is about 3Z to 10% on a weight of polymer per weight of solvent basis.

94. The process according to claim 74 wherein the maximum temperature of the reaction mixture at the completion of polymerization is about 70°C.

95. The process according to claim 74 wherein the polymerization is adiabatic.

96. The process according to claim 74 which is continuous and is conducted in hexane solvent.

97. The process according to claim 74 wherein the reactor is a tubular reactor.

98. The process according to claim 97 wherein the catalyst reactivator is introduced to said tubular reactor at multiple additional inlet ports said reactivator being optionally introduced with additional monomer.

99. In a polymerization process for producing copolymer from a reaction mixture comprised of catalyst and a monomer feed comprising ethylene and at least one other alpha-olefin monomer, and optionally at least one non-conjugated diene, the improvement which comprises producing a polymodal MWD copolymer by conducting the polymerization:

(b) with essentially one catalyst system which generates multiple active catalyst species each catalyst species initiating the growth of polymer chains that attain a different average molecular weight than those produced by other catalyst species;

(c) using at least one reaction mixture which is essentially transfer-agent free; (d) in such a manner and under conditions sufficient to initiate propagation of essentially all copolymer chains made with a particular catalyst species simultaneously;

(e) recovering polymer at the completion of polymerization; thereby producing a polymodal MWD ethylene copolymer comprising at least two different molecular weight modes wherein each mode has a narrow MWD and at least one of two characteristics, (1) an M_w/M_n of less than 2 and and M_z/M_w of less than 1.8.

100. The process according to claim 99 wherein the catalyst comprises a Ziegler catalyst.

101. The process according to claim 99 wherein said catalyst comprises a hydrocarbon-soluble vanadium compound and an organo-aluminum compound which react to form essentially at least two active catalyst species, at least one of the vanadium compound and organo aluminum compound containing a valence-bonded halogen.

102. The process according to claim 101 wherein the catalyst comprises:

VOCI_x(OR)_3-x' where x=0-3 and R=hydrocarbon radical;

VCI₄;

VO (AcAc)₂, where AcAc=acetyl acetonate V(AcAc)₃, where AcAc=acetyl acetonate

VOCl_x(AcAc)_3-x, where x=1 or 2 and AcAc-acetyl acetonate; and

(b) organo-aluminum compound selected from the group consisting of:

AIR₃ AIR₂CI, AI₂R₃CI₃, AIRCI₂, AlR'RCl, AI(OR')R₂, R₂AI-OAIR'₂

AIR₂I and mixtures thereof, where R and R' are hydrocarbon radicals.

103. The process according to claim 102 wherein the catalyst comprises VOCI₃ and AIR₂CI where R is a hydrocarbyl moeity.

104. The process according to claim 103 wherein R is ethyl.

105. The process according to claim 99 where¬in the reactor is a tubular reactor.

106. The process according to claim 99 wherein the temperature of the reaction mixture at the initiation of polymerization is about -80°C to 50°C.

107. The process according to claim 99 wherein the maximum temperature of the reaction mixture at the completion of polymerization is about 200°C.

108. The process according to claim 99 wherein the polymerization is a solution polymerization.

109. The process according to claim 100 wherein the catalyst components are premixed.

110. The process according to claim 109 wherein the catalyst components are premixed and then aged.

111. The process according to claim 110 wherein the catalyst components are aged for about 0.5 seconds.

112. The process according to claim 101 wherein the mole ratio of aluminum to vanadium in the catalyst is about 2 to 25.

113. The process according to claim 108 wherein the polymerization is conducted in a solvent for the reaction mixture; and wherein the copolymer concentration in the reaction mixture at the completion of polymerization is about 3 to 15% on a weight copolymer per weight of solvent basis.

114. The process according to claim 109 wherein the catalyst comprises components that are premixed and then aged for about 1 to 50 seconds.

115. The process according to claim 109 wherein the mole ratio of aluminum to vanadium in the catalyst is about 4 to 15.

116. The process according to claim 99 wherein the polymerization is conducted in a solvent for the reaction mixture, and wherein the copolymer concentration in the reaction mixture at the completion of polymerization is about 3% to 10% on a weight of polymer per weight of solvent basis.

117. The process according to claim 99 wherein the maximum temperature of the reaction mixture at the completion of polymerization is about 70°C.

118. The process according to claim 99 wherein the polymerization is adiabatic.

119. The process according to claim 99 which is continuous and is conducted in hexane solvent.

120. The process according to claim 105 wherein said reaction mixture further comprises diene, and wherein at least one of said ethylene, other alpha- olefin monomer and diene are fed to said tubular reactor at multiple feed sites.

121. In a polymerization process for producing copolymer from a reaction mixture comprised of catalyst and a monomer feed comprising ethylene at least one other alpha-olefin monomer and optionally at least one non conjugated diene, the improvement which comprises producing a polymodal MWD copolymer by conducting the polymerization:

(b) using at least one reaction mixture which is essentially transfer-agent free;

(c) with at least one first catalyst in suchh a manner and under conditions sufficient to initiate propagation of essentially all copolymer chains simultaneously; (d) introducing at least one additional catalyst feed together with additional monomer at one or more finite times after initiation of polymerization; thereby initiating additional copolymer chains wherein the propagation of essentially all such additional copolymer chains is initiated simultaneously and wherein the additional catalyst feed is the same or different than the first catalyst; thereby producing a polymodal MWD ethylene copolymer comprising at least two different molecular weight modes wherein each mode having a narrow MWD and at least one of two characteristics, (1) an M_w/M_n of less than 2 and and M_z/M_w of less than 1.8.

122. The process according to claim 121 wherein the catalyst comprises a Ziegler catalyst.

123. The process according to claim 120 wherein each catalyst comprises a hydrocarbon-soluble vanadium compound and an organo-aluminum compound which react to form essentially one active catalyst species, at least one of the vanadium compound and organo aluminum compound containing a valence-bonded halogen.

124. The process according to claim 123 wherein each catalyst comprises:

VOCI_x(OR)_3-x' where x=0-3 and R=hydrocarbon radical;

VCI₄; VO (AcAc)₂, where AcAc=acetyl acetonate

V(AcAc)₃, where AcAc=acetyl acetonate

VOCI_x(AcAc)_3-x, where x=1 or 2 and AcAc-acetyl acetonate; and

(b) organo-aluminum compound selected from the group consisting of:

AIR₃ AIR₂CI, AI₂R₃CI₃, AIRCI₂ , AlR'RCl, AI(OR')R₂, R₂AI-OAIR₂

AIR₂I and mixtures thereof, where R and R' are hydrocarbon radicals.

125. The process according to claim 124 wherein the catalyst comprises VCl₄ and Al₂R₃CI₃ or VOCI₃ and Al₂R_'3Cl₃ wherein R and R' are the same or different hydrocarbyl moeity.

126. The process according to claim 124 wherein R and R' are ethyl.

127. The process according to claim 125 wherein the reactor is a tubular reactor having a reactor inlet and at least one sidestream inlet port downstream of the reactor inlet, additional catalyst, and optionally, additional monomer being added through said sidestream inlet port.

128. The process according to claim 127 wherein the additional catalyst is the same catalyst species as that added at the initiation of polymerization.

129. The process according to claim 123 wherein said additional catalyst is a different catalyst species than that introduced at the initiation of polymerization.

130. The process according to claim 121 wherein the temperature of the reaction mixture at the initiation of polymerization is about -80°C to 50°C.

131. The process according to claim 121 wherein the maximum temperature of the reaction mixture at the completion of polymerization is about 200°C.

132. The process according to claim 121 wherein the polymerization is a solution polymerization.

133. The process according to claim 122 wherein the catalyst components are premixed.

134. The process according to claim 133 wherein the catalyst components are premixed and then aged for at least 0.5 seconds.

135. The process according to claim 133 wherein the catalyst components are premixed then aged.

136. The process according to claim 123 wherein the mole ratio of aluminum to vanadium in the catalyst is about 2 to 25.

137. The process according to claim 132 wherein the polymerization is conducted in a solvent for the reaction mixture, and wherein the copolymer concentration in the reaction mixture at the completion of polymerization is about 3 to about 15% on a weight copolymer per weight of solvent basis.

138. The process according to claim 121 wherein the maximum temperature of the reaction mixture at the completion of polymerization is about 50°C.

139. The process according to claim 132 wherein the catalyst comprises components that are premixed and then aged for about 1 to 50 seconds.

140. The process according to claim 133 wherein the mole ratio of aluminum to vanadium in the catalyst is about 4 to 15.

141. The process according to claim 140 wherein the polymerization is conducted in a solvent for the reaction mixture and wherein the copolymer concentration in the reaction mixture at the completion of polymerization is about 3 to 10% on a weight of polymer per weight of solvent basis.

142. The process according to claim 121 wherein the maximum outlet temperature of the reaction mixture at the completion of polymerization is about

70°C.

143. The process according to claim 121 wherein the polymerization is adiabatic.

144. The process according to claim 121 wherein the polymerization is a continuous process and is conducted in hexane solvent.

145. The process according to claim 121 wherein the polymerization is conducted in at least one tubular reactor.

146. The process according to claim 1 wherein the catalyst species is derived from the reaction of VCl₄ and an aluminum compound of the formula Al₂R₃X₃ wherein X is halogen and R is a hydrocarbyl radical.

147. The process according to claim 146 wherein the aluminum compound is ethyl aluminum sesquichloride.

148. The process according to claim 29 wherein one of the catalyst species is derived from the reaction of VCl₄ and an aluminum compound of the formula AI₂R₃X₃ and wherein a second catalyst species is derived from the reaction of VOCI₃ with an aluminum compound of the formula Al₂R₃X₃ wherein X is halogen and R is a hydrocarbyl radical.

149. The process according to claim 148 wherein the aluminum compound is ethyl aluminum sesquichloride.

150. The process according to claim 51 wherein the catalyst species is derived from the reaction of VCl₄ and an aluminum compound of the formula Al₂R₃X₃ wherein X is halogen and R is a hydrocarbyl radical.

151. The process according to claim 148 wherein the aluminum compound is ethyl aluminum sesquichloride.

152. The process according to claim 74 wherein the catalyst species is derived from the reaction of VCl₄ and an aluminum compound of the formula Al₂R₃X₃ wherein X is halogen and R is a hydrocarbyl radical.

153. The process according to claim 152 wherein the aluminum compound is ethyl aluminum sesquichloride.

154. The process according to claim 99 wherein the catalyst species is derived from the reaction of VOCI₃ and an aluminum compound of the formula AIR₂X wherein X is halogen and R is a hydrocarbyl radical.

155. The process according to claim 154 wherein the aluminum compound is diethy1 aluminum chloride.

156. The process according to claim 121 wherein the catalyst species is derived from the reaction of VCl₄ and an aluminum compound of the formula Al₂R₃X₃ wherein X is halogen and R is a hydrocarbyl radical.

157. The process according to claim 156 wherein the aluminum compound is ethyl aluminum sesquichloride.

158. The product according to claim 25 wherein the polymodal polymer comprises at least two MWD modes, the M_w of any two adjacent modes differing from one another by at least 50% and any one mode comprising at least 10 wt% of the total polymer.

159. The product prepared according to the process of claim 29.

160. The product according to claim 159 wherein the polymodal polymer comprises at leat two MWD modes, the 11 of any two adjacent modes differing from one another by at leat 50% and any one mode comprising at least 10 wt% of the total polymer.

161. The product prepared according to the process of claim 51.

162. The product according to claim 161 wherein the polymodal polymer comprises at leat two MWD modes, the M_w of any two adjacent modes differing from one another by at leat 50% and any one mode comprising at least 10 wt% of the total polymer.

163. The product prepared according to the process of claim 74.

164. The product according to claim 163 wherein the polymodal polymer comprises at leat two MWD modes, the M_w of any two adjacent modes differing from one another by at leat 50% and any one mode comprising at least 10 wt% of the total polymer.

165. The product prepared according to the process of claim 99.

166. The product according to claim 165 wherein the polymodal polymer comprises at leat two MWD modes, the M_w of any two adjacent modes differing from one another by at leat 50% and any one mode comprising at least 10 wt% of the total polymer.

167. The product prepared according to the process of claim 121.

168. The product according to claim 167 wherein the polymodal polymer comprises at leat two MWD modes, the M_w of any two adjacent modes differing from one another by at leat 50% and any one mode comprising at least 10 wt% of the total polymer.

169. The proces s according to claim 1 wherein the catalyst species is derived from the reaction of

VCl₄ and an aluminum compound of the formula AIR_nX_3-n, wherein n can vary from 1 to 2, X is halogen and R is a hydrocarbyl radical.

170. The process according to claim 31 wherein the aluminum compound has the formula AIR_nX_3-n , wherein n can vary from 1 to 2, X is halogen R is a hydrocarbyl radical.

171. The process according to claim 51 wherein the catalyst species is derived from the reaction of

VCl₄, and an aluminum compound of the formula AIR_nX_3-n' wherein n can vary from 1 to 2, X is halogen and R is a hydrocarbyl radical.

172. The process according to claim 74 wherein the catalyst species is derived from the reaction of

173. The process according to claim 99 wherein the catalyst species is derived from the reaction of

VOCl₃ and an aluminum compound of the formula AIR_nX_3-n' wherein n can vary from 1 to 2, X is halogen and R is a hydrocarbyl radical. CLAIMS 174 to 181 were missing from the international application as originally filed.

182. The product according to claim 163 wherein the copolymer is cured.

183. The product according to claim 163 wherein said copolymer product is blended with base stock lubricating oil.

184. The product according to claim 183 wherein said copolymer product is blended with the base stock lubricating oil in an amount from about 0.001 to about 49 wt% copolymer based on the oil plus copolymer.

185. The product according to claim 165 wherein the copolymer is cured.

186. The product according to claim 165 wherein said copolymer product is blended with base stock lubricating oil.

187. The product according to claim 186 wherein said copolymer product is blended with the base stock lubricating oil in an amount from about 0.001 to about 49 wt% copolymer based on the oil plus copolymer.

188. The product according to claim 167 wherein the copolymer is cured.

189. The product according to claim 167 wherein said copolymer product is blended with base stock lubricating oil.

190. The product according to claim 189 wherein said copolymer product is blended with the base stock lubricating oil in an amount from about 0.001 to about 49 wt% copolymer based on the oil plus copolymer.

191. The process according to claim 9 wherein the catalyst components are premixed and then aged.

192. The process according to claim 35 wherein said reaction mixture further comprises diene, and wherein at least one of said ethylene, other alpha olefin monomer and diene is fed to said tubular reactor at multiple feed sites.

193. The process according to claim 74 wherein said polymerization is conducted in a tubular reactor.

194. The process according to claim 193 wherein said reaction mixture further comprises diene, and wherein at least one of said ethylene, other alpha olefin monomer and diene is fed to said tubular reactor at multiple feed sites.

195. The process according to claim 99 wherein said polymerization is conducted in at least one tubular reactor.

196. The process according to claim 195 wherein said reaction mixture further comprises diene, and wherein at least one of said ethylene, other alpha olefin and diene is fed to said tubular reactor at multiple fied sites.

197. The process according to claim 121 wherein said polymerization is conducted in at least one tubular reactor.

198. The process according to claim 197 wherein said reaction mixture further comprises diene, and wherein at least one of said ethylene, other alpha olefin and diene is fed to said tubular reactor at multiple feed sites.

199. The process according to claim 145 wherein said reaction mixture further comprises diene, and wherein at least one of said ethylene, other alpha olefin monomer and diene are fed to said tubular reactor at multiple feed sites.

200. The process according to claim 97 wherein said reaction mixture further comprises diene, and wherein at least one of said ethylene, other alpha-olefin monomer and diene is fed to said tubular reactor at multiple feed sites.

201. The process according to claim 107 wherein the maximum temperature of the reaction mixture is 50°C.

202. A copolymer of ethylene and at least one other alpha-olefin monomer, which copolymer is a superposition of two or more copolymer modes each of which has a MWD characterized by having at least one of the following characteristics: a M_w/M_n of less than 2 and M_z/M_w of less than 1.8.

203. The copolymer as defined by claim 202 wherein each of said copolymer modes has a M_w/M_n of less than 2 and M_z/M_w of less than 1.8.

204. The copolymer as defined by claim 202 wherein said alpha-olefin monomer contains 3-18 carbon atoms.

205. The copolymer as defined by claim 204 wherein said alpha-olefin monomer contains 3-6 carbons.

206. The copolymer as defined by claim 204 wherein said alpha-olefin is selected from the group consisting of propylene, butene-1, pentene-1, hexene-1, heptene-1, octene-1, and dodecene-1.

207. The copolymer as defined by claim 206 wherein said alpha-olefin is propylene.

208. The copolymer as defined by claim 202 consisting essentially of ethylene and propylene.

209. The copolymer as defined by claim 202 consisting essentially of ethylene, propylene and non-conjugated diene.

210. The copolymer as defined by claim 209 wherein said non-conjugated diene is a straight chain acyclic diene.

211. The copolymer as defined by claim 210 wherein said straight chain acyclic diene is selected from the group consisting of 1,4-hexadiene and 1,6-octadiene.

212. The copolymer as defined by claim 210 wherein said non-conjugated diene is a branched chain acyclic diene.

213. The copolymer as defined by claim 212 wherein said branched chain acyclic diene is selected from the group consisting of: 5-methyl-1, 4-hexadiene; 3,7-dimethyl-1, 6- octadiene; 3,7-dimethyl-1, 7-octadiene and the mixed isomers of dihydro-myrcene.

214. The copolymer as defined by claim 209 wherein said non-conjugated diene is a single ring diene.

215. The copolymer as defined by claim 214 wherein said single ring diene is selected from the group consisting of: 1,4-cyclohexadiene; 1,5-cyclooctadiene; and 1,5-cyclododecadiene.

216. The copolymer as defined by claim 203 wherein said non-conjugated diene is a multi-ring fused or bridged ring diene.

217. The copolymer as defined by claim 216 wherein said multi-ring alicyclic fused or bridged ring diene is selected from the group consisting of: tetrahydroindene; methyltetrahydroindene; dicyσlopentadiene; bi-cyclo-(2,2,1) -hepta-2, 5-diene; alkenyl, alkylidene, cycloalkenyl and cycloalkylidene norbornenes such as 5-methylene-2-norbornene (MNB) , 5-ethylidene-2-norbomene (ENB) , 5-propylidene-2-norbornene, 5-isopropylidene-2-norbornene, 5-(4-cyclopentenyl)-2-norbornene; and 5-cyclohexylidene-2-norbornene.

218. The copolymer as defined by claim 209 wherein said non-conjugated diene is 5-ethylidene-2-norbornene.

219. The copolymer as defined by claim 209 wherein the amount of non-conjugated diene on a weight basis of said copolymer is about 0-20%.

220. The copolymer as defined by claim 219 wherein the amount of diene on a weight basis of the copolymer is about 0-15%.

221. The copolymer as defined by claim 220 wherein the amount of diene on a weight basis of the copolymer is about 0-10%.

222. The copolymer as defined by claim 202 wherein the average ethylene content of each copolymer mode is at least 10% on a weight basis.

223. The copolymer as defined by claim 222 wherein each copolymer mode comprises at least about 30% ethylene.

224. The copolymer as defined by claim 222 wherein each copolymer mode comprises less than about 90% ethylene.

225. The copolymer as defined by claim 202 wherein the weight average molecular weight of each mode is between about 2,000-12,000,000.

226. The copolymer as defined by claim 225 wherein the weight average molecular weight of each mode is between about 10,000-1,000,000.

227. The copolymer as defined by claim 226 wherein the weight average molecular weight of each mode is between about 20,000-750,000.

228. The copolymer as defined by claim 202 wherein the M_w/M_n ratio for the whole copolymer is about 1-50.

229. The copolymer as defined by claim 202 wherein the M_w of any two adjacent copolymer MWD modes differs, by at least 50%.

230. The copolymer as defined by claim 229 wherein each mode comprises at least 10% by weight of the total copolymer.

231. A basestock lubricating oil blended with the copolymer product according to claim 202.

232. The basestock lubricating oil as defined by claim 231 wherein said copolymer product is blended in an amount of 0.001 to about 49 weight percent copolymer based upon oil plus copolymer.

233. A cured copolymer as defined by claim 202.

234. A cured copolymer as defined by claim 209.

235. The copolymer as defined by claim 202 wherein the Intra-CD of at least one of said modes is greater than 5%.

236. The copolymer as defined by claim 235 wherein the Intra-CD of at least one of said modes is greater than 15%.

237. The copolymer as defined by claim 209 wherein the Intra-CD of at least one of said modes is greater than 5%.

238. The copolymer as defined by claim 237 wherein the Intra-CD of at least one of said modes is greater than 5%.

239. A cured copolymer as defined by any one of claims 235-238.

240. A basestock lubricating oil blended with the copolymer product according to any one of claims 235-238.

241. The basestock lubricating oil as defined by claim 240 wherein said copolymer product is blended in an amount of 0.001 to about 49 weight percent copolymer based upon oil plus copolymer.