WO1982002854A1 - Color developer sheet for no-carbon copying paper - Google Patents

Color developer sheet for no-carbon copying paper Download PDF

Info

Publication number
WO1982002854A1
WO1982002854A1 PCT/JP1982/000043 JP8200043W WO8202854A1 WO 1982002854 A1 WO1982002854 A1 WO 1982002854A1 JP 8200043 W JP8200043 W JP 8200043W WO 8202854 A1 WO8202854 A1 WO 8202854A1
Authority
WO
WIPO (PCT)
Prior art keywords
sheet
water
weight
color
developer sheet
Prior art date
Application number
PCT/JP1982/000043
Other languages
French (fr)
Japanese (ja)
Inventor
Paper Mills Ltd Mitsubishi
Original Assignee
Torii Takahiro
Senoh Hideaki
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Torii Takahiro, Senoh Hideaki filed Critical Torii Takahiro
Publication of WO1982002854A1 publication Critical patent/WO1982002854A1/en

Abstract

A color developer sheet for no-carbon copying paper having excellent color-developing ability and storage stability as well as improved surface strength, which is obtained by providing activated clay-containing color developer layer on a base paper which has been treated with a water-soluble alkali.

Description

明 誊 ノ ー カ ー ボ ン複写羝用顕色剤 シ ー ト  Light color developer sheet for copy machine
技 術 分. 野 Technical field
本発明は ノ 一 カ ー ボ ン複写 S用顕色剤 シ ト に関し、 特に発色性、 保存性等を向上させたノ ー 力 ボ ン複写 紙用顕色剤 シー ト に関する。 背 - dK 術  The present invention relates to a developer sheet for non-carbon copying, and more particularly to a developer sheet for copying paper with improved color development and preservability. Profile-dk art
ノ ーカー ボ ン複写羝は公知であ り 、 該ノ ー カ ー ボ ン 複写 は例えば米国特許第 2 7 1 2 5 0 '7 号、 同 第 2 8 0 (3 4 5 7 号、 同第 3 4 1 8 2 5 0 号明細書な どに記載されて る よ う に電子供与性、 袪吸着性及び 呈色 （ 発色 ） 反応性を有する 無色有機化合物 （ 以下癸 色剤 と称する ) の有機溶媒の溶液を含有したマ イ ク 口 カ プ セ ル と 電子受容性の反応性吸着物質 （ 以下頭色剤 と 称する ：） ¾利用した も のであ る。  Noker carbon copying is known. For example, U.S. Pat. Nos. 2,712,250 and 7,280 (3,457,3). An organic solvent for a colorless organic compound (hereinafter referred to as a coloring agent) having electron-donating, adsorbing, and coloring (color-forming) reactivity as described in, for example, JP-A-218250. And a reactive adsorbent with electron accepting properties (hereinafter referred to as a head coloring agent) containing the above solution.
従来 よ り マ イ ク ロ カ： 7° セ ルィヒ ¾ コ ア セ ルぺー シ ヨ ン 法、 イ ン サイ チュー （in situ) 法、 界面重合法な どに よ り おこなわれて り 、 癸色剤と し てはク リ ス タ ルノぐ ィ ォ レ ツ ト ラ ク ト ン 、 3 ， 3 - ビ ス （ P ー ジ メ チ ル ァ ミ ノ フ エ ニ ル ） ナ フ タ リ ド 、 3 - ( p - ジ メ チ ル ア ミ ノ フ エ - ノレ ） 一 3 - C 2 - メ チ ノレ イ ン ド ー ノレ - 3 - ィ ル ：） - ό - ジ メ チ ノレ ア ミ ノ フ タ ラ イ ド の よ う な ト リ ァ  Traditionally, microcaution: 7 ° C This method has been carried out by using a cellulose acetate method, an in situ method, an interfacial polymerization method, etc. These include crystallographic tracks, 3, 3-bis (P-methylmethylaminophenyl) naphthalide, 3- ( p-Dimethylaminophenol-North) 1-C2 -Methylindolene-North- 3-yl :)-ジ -Dimethylinylamine phthalate Trier like
ΟΜΡί ' リ ル メ タ ン フ タ ラ イ ド系ィヒ合物、 メ チ レ ン ル 一 のぺ ン イ ノレ 、 ァ ニ ソ ィ ル、 ピ ノ"？ ロ イ ノレ誘導体な どの メ チ レ ン ブ ル ー の ァ シ ル誘導体系ィヒ合物、 3 - ジ ェ チ ル ァ ミ ノ ー ό ー メ チ ノレ ー 7 - ク ロ ロ フ ノレ オ ラ ン 、 3 — シ ェ チ ル ァ ミ ノ - 7 - ヅ ペ ン ジ ル ァ ミ ノ フ ル オ ラ ン の よ う なキサ ン テ ン系化合物な どが使用されてお り 、 前記の 顕色剤 と し ては一殺に漦性白土、 活佺白土、 ァ タ パル ジ ャ ィ ト 、 ゼォ ラ イ ト 、 ベ ン ト ナ イ ト な どの固体漦ゃ、 ノ ラ タ ー シ ャ リ ー ブ チ ル フ エ ノ ー ル樹 月旨、 ハ° ラ フ エ - ル フ エ ノ ー ル樹脂、 ノ ラ オ ク チ ル フ エ ノ ー ル樹脂など の フ エ ノ ー ル 樹 II、 或 4 コ ノ、ク鼓、 タ ン ニ ン鼓、 マ α ン 鼓、 マ レ イ ン鼓、 没食子漦、 ス ル フ ァ 二 ル漦など の有機化合物、 さ ら には安息香鼓、 サ リ チル漦、 置換 サ リ チ ル鷇、 ナ フ ト ェ漦、 ジ フ ェ ン漦な どの芳香族力. ル ボ ン ^、 又はそれら の金属化合物な どが^いられて る。 ΟΜΡί ' Methylable compounds such as lilmethan phthalide compounds, methyl alcohol, anisol, and pino "? -Acetyl derivative-based compound, 3 -ethylamine 7 -Chlorofluoronorane, 3 —Sethylamino-7 -Xanthene-based compounds such as pentamethylaminofuran are used, and as the above-mentioned color developing agent, clay and active clay are used to eliminate漦 ゃ Solids such as clay, attapulgite, zeolite, bentonite, etc. 漦 ゃ, ノ タ ラ 旨 月 旨° Phenolic tree II, such as phenolic resin, phenolic resin, phenolic resin, etc. α 鼓Organic compounds such as Rein drum, gallic and surfer, as well as Benzo, Salicyl, Substituted salicyl, Naphtho, and Diphen Aromatic powers, such as rubons or their metal compounds.
これら顕色剤の う ち特性上よ り 実際に好ま し く 使用 されて る も のは活性白土、 フ エ ノ ー ル樹脂及び置換 サ リ チ ル鼓 （ 塩 ：） である。  Among these developers, those which are actually used more favorably in terms of properties are activated clay, phenolic resin and substituted salicyl drum (salt :).
これら顕色剤の う ち有機頹色剤の フ エ ノ ー ル樹脂や 量渙サ リ チ ル ( 塩 ） の場合は原羝の pHに よって癸色 性、 保存性は釤響を受けに く が印刷適性が悪 く 、 又 化学合成品であ り コ ス ト 高と なる。  Among these developers, in the case of phenolic resin or lysine salicyl (salt), which is an organic coloring agent, the sheep color and the storage stability are not affected by the pH of the raw material. However, the printability is poor, and the cost is high because it is a chemically synthesized product.
一方焦機頭色剤の活性白土はィ ン キ吸収倥の如き 印 刷適性に優れ、 コ ス ト 安であ るが、 顕色剤シ ー ト を作 る と き、 白土の活性を よ り 強 く する ため塗液は一般に ア ル 力 リ 性にする が原紙の pHが低 と 頭色剤 シー ト の On the other hand, activated clay, which is a burner head coloring agent, has excellent printability and is inexpensive, as is the case with the ink-absorbing tatami, but produces a developer sheet. In general, the coating liquid is made alkaline to enhance the activity of the clay, but the pH of the base paper is low and the
PHが低下し発色性、 保存性が悪 と う 欠点があ る。  There is a drawback that the pH is lowered and the coloring and storage properties are poor.
特に原羝 目 方が大 き 程.、 癸色性、 保存性は惡 く な り やすい。  In particular, the greater the size of the original sea cucumber, the more it will tend to be less shiny and preserved.
ま た これら の現象は癸色剤に よ り 異な り 、 一般に ク リ ス タ ルノヾ ィ ォ レ ツ ト ラ ク ト ン 、 5 , 3 - ビ ス （ ？ - ヅ メ チ ル ァ ミ ノ フ エ - ル ；） - ナ フ タ リ ド、 3 - C p - ジ メ チ ル ァ ミ ノ フ エ ニ ル ） - 3 一 ( 2 - メ チ ル イ ン ド 一ル ー 5 - ィ ル ） - ό - シ * メ チ ル ァ ミ ノ フ タ ラ イ ドの よ う な ト リ ア リ ル メ タ ン フ タ ラ イ ド系ィヒ合物ゃメ チ レ ン フ, ノレ一の ペ ン イ ノレ 、 ァ - ン ィ ル 、 ピ ノ ロ イ ノレ誘導 体な どの メ チ レ ン ブ ル ー の ァ シ ル誘導体系ィヒ合物はこ の現象が起こ り やす く 、 5 - ヅ ェ チ ル ァ ミ ノ - 6 - メ チ ノレ - 7 — ク ロ ロ ブ ノレ オ ラ ン や 3 — シ ェ チ ノレ ア ミ ノ ー  Moreover, these phenomena are different depending on the coloring agent, and generally, crystal noretrotactic lactones and 5,3-bis (?-ヅ methylaminophene) are used. -);-Naphthalide, 3-Cp-dimethylaminophenyl-3-1 (2-methylindole 5-yl)-ό -Trimethylmethan phthalide compounds, such as methylaminophthalide, methylene, and phenol A methyl derivative, such as an acyl derivative, a vinyl derivative, or a pinol derivative, is liable to cause this phenomenon. MINNO-6-METHNORE-7-Kurob-No-Lore
7 - シ ベ ン グ ル ア ミ ノ フ ル オ ラ ン の よ う なキ サ ン テ ン 系は起 こ り に く 。  Xanthen systems such as the 7-Single Amino Full Orane are unlikely to occur.
通.常の實色に発色する ノ ー カ ー ボ ン複写羝用顕色剤  No. A color developer that produces a normal real color.
シ ー ト'の発色剤 と し ては ク リ ス タ ルバ イ オ レ ツ ト ラ ク Crystal violent track as a sheet's color former
ト ン 、 ペ ン ソ ィ ル ロ イ コ メ チ レ ン ブ ル ー を組合せて使 用 して る ので前記の発色性、 保存住は特に問題 と な 従来 よ り これら の問題点 ¾改良するた めの方法と し て、 特公昭 4 1 - 2 5 7 3 号、 同 4 1 - 1 6 2 0 2号、 同 4 2 — 8 8 1 1 号、 同 4 3 - 1 0 0 9 1 号、 同 48- The color development and preservation of the living room are particularly problematic because they are used in combination with the tongue and pen-soil coconut muffler. The methods for this are as follows: Japanese Patent Publication No. 41-25703, No.41-162, No.42-8811, No.43-10091, Same 48-
( O PI ヽ δ 3 2 0 ό 号公辑な どに記载されて る よ う に漦性 白土或いはこれに類似の粘土類を銥羧にて処理し漦に 可溶のア ル ミ ナ 、 鉄、 その他の塩基性成分を溶出 して その表面積を 2 0 0 ^以上と する こ と が挙げられ る。 ま たこの よ う にし て作られた活性白土はあ らたに 亜銥、 マ グ ネ シ ウ ムな どの塩類を混合し ても使用する こ とができ る。 (O PI ヽ As described in the δ 3220 No.2 publication, etc., clay, or similar clay, is treated with water and is soluble in aluminum, iron, and other metals. The elution of the basic component is performed to increase the surface area to 200 ^ or more. Activated clay made in this way can be used even if it is mixed with a salt such as zinc or magnesium.
この よ う な活性白土に水 加え分散し、 ア ル カ リ 或 はア ル カ リ 土類金属の 化物、 水漦化物、 炭 塩或 は ア ン モ ニ ア、 ァ ミ ン な ど の ア ル 力 ひ 性物質を添加 混合し てア ル 力 リ 性-と しバイ ン ダ ーを加えて塗液と し 原羝に塗抹する 方法、 又、 活性.白土に水を加えて分散 しパイ ン ダ ー ¾加えて得た塗液を原紙に塗抹し更にそ の表面にア ル 力 リ 或 はア ル力 リ 土類金属の黎化物、 水漦化物、 炭漦塩な どのア ル カ リ 物質の水溶液或 は 懸濁液を塗抹、 或 は噴霧し て表面 ¾ ア ル カ リ 性とす 'る 方 があるが効杲は得られな 。  Water is added to such activated clay to disperse it, and alkali or alkaline earth metal compounds, hydrates, carbonates, ammonia, ammonia, etc. Add an active substance and mix it to make it stronger, add a binder to make a coating liquid and spread it on the original tongue.ー 抹 The obtained coating liquid is smeared on the base paper, and the surface is coated with alkaline or alkaline substances such as alkaline earth metals, such as rehydrated, hydrated and carbonated salts. There is a method of smearing or spraying an aqueous solution or suspension to make the surface alkaline, but no effect is obtained.
更に改良する ために特開昭 4 8 ― 9 8 9 1 5号 〔待 公昭 5 · 2 - 6 6 4 5号）、特開昭 5 2 - 8 ό 8 0 7 号公 報な どに記載されて る よ う に原紙と して抽 ffi pHが  For further improvement, it is described in, for example, JP-A-48-98915 (Machi, No.5, 2-6,645) and JP-A-52-8,807. As the base paper, the extraction ffi pH is
0 . 0 乃至 9， 0 の中性羝を使用する 方法、 及び特公昭  Method of using neutral glue from 0.0 to 9.0, and
5 2 - 2 9 6 4 9 号公報に記載されて る よ う に活性 白土塗液を塗採する前に原衹に下引 き 層 （uaier coating ) と してア ル力 リ 土類金属の水不溶性塩或 は難溶性塩、 又は酸化物又は水漦化物な どをパイ ン ダ 混合し て  5 2-2 9 6 4 9 As described in the official gazette, before application of the activated clay coating liquid, the surface of the earth is coated with an alkaline earth metal as a uaier coating. Water-insoluble or sparingly soluble salts, or oxides or hydrates, etc.
Ο ΡΙ 塗抹する 方法な どがあ るがま だ充分な効杲は得られて な 。 発 明 の 開 示 Ο ΡΙ There is a method of smearing, etc., but I have not yet obtained a sufficient effect. Disclosure of the invention
本'癸明の 目 的は活性白土使用のノ ー カー ボ ン複写羝 用頹色剤 シー ト の発色性、 保存性を向上させる こ と に The purpose of this is to improve the color development and preservability of the colorant sheet for activated carbon clay copying.
«3 る 。 «3
本癸明者らは種 々研究した結果、 水溶'性ア ルカ リ で 処理した 紙に活性白土含有頭色剤層を設ける こ と に よ り 発色性、 保存性に非常に優れ、 又、 表面強度 も 向 上したノ ー カー ボ ン複写羝用顕色剤 シー ト が得られる こ と を見出 し た。 . 発明を実施するための最良の形態  As a result of various studies, the present KIKI-Akira found that by providing an activated clay-containing head coloring agent layer on paper treated with a water-soluble alkali, it was extremely excellent in color development and preservation. It has been found that a developer sheet for a carbon black copying machine with improved strength can be obtained. BEST MODE FOR CARRYING OUT THE INVENTION
本癸明に使用する水溶性ア ル力 リ と し ては水^化 リ チ ウ ム 、 水酸化カ リ ウ ム 、 水酸ィヒナ ト リ ウ ム 、 ケ ィ 漦 ナ ト リ ゥ 厶な どの無機ア ル 力 リ ゃモ ノ エ タ ノ ー ル ア ミ ン ト リ エ タ ノ ー ルァ ミ ンな どの有機ア ル 力 リ がある。 その中で も特に効果の著し も のはケ ィ 漦ナ ト リ ゥ ム であ る。 原羝に水溶性ア ル カ リ を処理する 方法と し て は、 サ イ ズ： 7° レ ス 、 エアーナ イ フ コ ー タ ー、 ロ ー ルコ 一 タ ー、 ケ * 一 ト ロ ー ル コ ー タ ーな ど： ^あ る力 iこれら に 限定される も のではな 。 水溶性ア ル カ リ の最適 pHは 原紙に処理したの ちの処理原羝の抽出 pHが好ま し く は The water-soluble alloys used in the present invention include inorganic materials such as lithium hydroxide, potassium hydroxide, sodium hydroxide, and potassium nitrate. There are organic lamps such as aluminum lamps, aluminum lamps, etc. Among them, the key effect is the key stream. The method of treating the water-soluble alcohol on the original sashimi is as follows: size: 7 ° less, air knife coater, roll coater, roll coater Data, etc .: A certain force i It is not limited to these. The optimum pH of the water-soluble alcohol is preferably the extraction pH of the treated raw material after processing on the base paper.
9 . 0 以上、 特に好ま し く は 9 . 0 乃至 9. 5 であ る。 0 抽 ffipHが 9.0 以下では優れた効學は得られず、 9.5 以上では原羝のセ ル α —スが侵され、 黄変が漦し く 顕 色剤シー ト 用原羝と して不充分な場合がある。 9.0 or more, particularly preferably 9.0 to 9.5. 0 When the extraction pH is 9.0 or less, excellent efficacy cannot be obtained, and when the extraction efficiency is 9.5 or more, the cells α-source of the original water are attacked, and the yellowing is low, and it is not enough as a raw material for developer sheet. It may be.
顕色剤シー ト ^原羝とは 性原羝、 中性原羝である。 鼓 fe原羝は水で 0.2 滠度に分散されたパル 7°  The developer sheet ^ Hara Shibori is a genhara shirin and a neutral hara shirin. Gufehara is a pal 7 ° dispersed in water 0.2 °
( 4 5° SR 叩群 ） 1 0 0 0重量部に 1 多 ロ ジ ン ( 播磨化成㈱製、 ハ ーサイ ズ L 一 5 0 ) 2.0 重量部と 1 ^ 硫漦ア ル ミ - ゥ ム （ 浅田化学㈱製、 液体琉黎パ ン ド ） 0.0 重量部を添加し湿強度を保ち、 抨量が 4 0 Z 2 になる よ う に抄羝する こ と に よ り 得られる。 (45 ° SR tapping group) 1 part per 100 parts by weight (manufactured by Harima Kasei Co., Ltd., Harsize L-150) 2.0 parts by weight and 1 ^ sulfur aluminum-pharmaceutical (Asada Made by Chemical Co., Ltd., liquid Ryuri Pand) It can be obtained by adding 0.0 parts by weight to maintain the wet strength and extracting the weight to 40 Z 2 .
中性原.羝は水で 0.2 淺度に分散されたパル  Neutral.Shin is 0.2 pallets dispersed in water.
C NBEP、 4 5。 SR 叩解 ） 1 0 0 0重量部に 1 ア ル キ ル ケ テ ンダイ マー 〔 デ ィ ッ ク ノ、一キ ュ レ ス社製、 ア コ 一ペ ル 3 ό 0 ) 4重量部と 1 カチオ ン デ ン プ。 ン （ ナ シ ョ ナルス タ ーチ社製、 ケ ィ ト ー 2 ) 4重量部を添加 し坪量が 4 0 / 2 にな る よ う 抄羝する こ と に よ り 得られる。 C NBEP, 4 5. SR beating) 1 alkyl keten dimer (Dick No., manufactured by Ikurasu Co., Ltd., acoustic 3 一 0) in 100 parts by weight 4 parts by weight and 1 cation Dump. (Category 2 manufactured by National Starch Co., Ltd.) can be obtained by adding 4 parts by weight and extracting the weight so that the basis weight becomes 40/2.
一殺に これら原羝の抽 ffipHは漦性原羝で 3.5 乃至 4.5 であ り 、 中性原羝では 0.0 乃至 8.0 であ る。  The killing efficiencies of these genra are 3.5 to 4.5 in the case of 漦 hara, and 0.0 to 8.0 in the case of neutral.
本発钥における抽 ίϋρΗと は熱水拍出 pHを意味し、 了ェ s - p - 8 1 5 3 に従って試驗片を熱水抽出し ： ris - P 一 8 1 1 3 に規定する pH測定装置及び ； ris ― z - 8 8 0 2の 7 に規定する ガ ラ ス電極を用 測定した。  The extraction ρΗ in the present invention means the hot water ejection pH, and the test piece is extracted with hot water according to s-p-81 53: pH measuring device specified in ris-P-1811 Ris-z-880 The glass electrode specified in 7 of 802 was measured.
ー設に活性白土使用の頭色剤シー ト 用塗液は活拴白 土を水に分散したのち、 分散液の pHが活性白土が最適  -The coating solution for the head colorant sheet that uses activated clay is the most suitable.
O PI な発色瀵度を示すま て調整 （ pH 8.5 乃至 1 0.0 ：) しデ O PI Adjust (pH 8.5 to 10.0 :) until the color intensity is high.
ン ン 、 カ ゼ イ ン 、 ア ラ ビ ア ゴ ム 、 ゼ ラ チ ン 、 ボ リ ビ - ノレ ア ノレ コ ー ノレ 、 カ ノレ ポ キ シ メ チ ノレ セ ノレ ロ ー ス 、 ス チ レ ン無水マ レ イ ン鼓の ア ル 力 リ 塩、 ラ テ ッ ク スな どの バ イ ン ダ ー を加えて塗液とする。  , Casein, arabia rubber, zelatin, bolivino-norre-norre-co-nore, canole-pox-methy-no-seno-lorose, styrene-anhydrous Add a binder such as salt and latex to make a coating solution.
パイ ン ダ一の使用量は塗抹方法又は塗.液裊度に よ り 異なる が活性白土 1 a Q 重量部に対し て 5 篁量部以上 で通常は 1 5 乃至 3 0 重量部であ る。 塗抹量は原紙の 目 方に よ り 異な るが塗液固形分 4 / 2 以上て通 The amount of the binder used varies depending on the method of coating or the concentration of the coating solution. However, the amount of the binder is more than 5 parts by weight per 1 part by weight of 1 aQ of activated clay and usually 15 to 30 parts by weight. Smear amount is Ru different Ri by the eye side of the base paper Te coating solution solids 4/2 or more communication
常は 0.0 乃至 1 3.0 9 / 2 である。 Normally is 0.0 to 1 3.0 9/2.
以下、 具体例につ て述べる。 尚、 発色剤 シー ト は 市販ノ ー カ ー ボ ン複写羝甩上周羝「三菱 NCR羝上 - 4 0 ブ ル ー 」 を使用し た。  Hereinafter, specific examples will be described. The color former sheet used was a commercially available Noker Carbon Co., Ltd., "Nitsubishi NCR Kamijo-40 Blue".
実施例 1 Example 1
水 9 2.5 重量部に 1 号ケ イ ^ナ ト リ ゥ ム 7.5 重量部 を完全に溶 したのち、 前記の例示し た 4 0 9 / mZ After completely dissolving 7.5 parts by weight of No. 1 key-nutridium in 92.5 parts by weight of water, the above-mentioned 409 / mZ
の中性原羝 （ 熱水抽 ffi pH 7.2 ) に熱水抽出 pHが 9.3 に な る よ う サイ ズ レ ス し た （ これを処理法 A と う ：)。 The neutral pH of hot water (hot water extraction ffi pH 7.2) was sized so that the hot water extraction pH would be 9.3 (this is called treatment method A :).
次に ·水 1 0 0 重量部に ピ α リ ン鼓ナ ト リ ゥ ム 0.5 重 量部を加え完全に溶辫し た のち活性白土 1 0 0 重量部 を徐々 に添加し よ く 分散したの ち 1 0 漦化デン ン  Next, 100 parts by weight of water, 0.5 parts by weight of pi-aluminum sodium were added and completely dissolved, and then 100 parts by weight of activated clay was gradually added and dispersed well. 10 Density
( 日本食品㈱製、 MS - 3 8 0 0 ) を 4 0 重量部、 ス チ レ ン ブ タ ジ エ ン ラ テ ッ ク ス （ ダ ウ ケ ミ カ ル 製、  (Manufactured by Nippon Shokuhin Co., Ltd., MS-380) is 40 parts by weight, and Styrenbutadiene latex (manufactured by Dow Chemical,
Dow 6 3 6 ) ¾ 2 0 重量部 （ 固形分 ） 加えよ く 混和し たの ち、 2 0 カ セ イ ン ーダで pHを 9.5 と した Dow 6 3 6) ¾ 20 parts by weight (solid content) After adding well and mixing, the pH was adjusted to 9.5 with a 20 cascade.
OMPI  OMPI
、Ί νιρο j 塗液を処理法 A の如 く 処理し た原羝に塗抹量が 8 9- / 2 ( 固形分 ） と なる よ う にブ レー ド コ ー タ ーで塗抹し た ο , Ί νιρο j The coating liquid was smeared with a blade coater so that the amount of smear would be 89- / 2 (solids) on the original tongue treated as in Method A ο
実施例 2 Example 2
水 9 5 重量部 に モ ノ エ タ ノ ー ルア ミ ン 5重量部を完 全に溶解したの ち 4 0 9- / TO2 の中性原紙 （ 熱水抽出 ρΗ ό·8 ) に熱水拍出 ρΗが 9， 3 にな る よ う に サ イ ズゲ レ ス し た。 （ これを処理法 Β と う ：） After completely dissolving 5 parts by weight of monoethanolamine in 95 parts by weight of water, hot water was added to neutral base paper (hot water extraction ρΗ ό · 8) of 409- / TO 2 The size was adjusted so that the output ρΗ became 9.3. (Let's call this processing method :)
次に塗液は実施例 1 の如 く 同様に作製し この塗液を 処理法 Β の如 く 処理し た原羝に塗抹量が 8 ^ ,Ζ 7 ^ (固 形分 ） となる よ う にブ レー ド コ ー タ ー で塗 し た。 Then coating liquid is spread amount如rather treated raw羝processing method Β The coating liquid was prepared in the same manner rather如Example 1 8 ^, Ζ 7 ^ Ni Let 's become (solid content) Painted with blade coater.
比較例 1 Comparative Example 1
塗液は実施例 1'と 同様に作製し、 4 (3 ^ Ζ 2 の^ ' 性原羝 （ 熱水抽出 ρΗ 4.0 ) に塗抹量が 8 ^ノ 2 ( 固 形分 ：） とな る よ う に ブ レ ー ド コ ー タ ー て塗抹した。 The coating liquid was prepared in the same manner as in Example 1 ', and the amount of smearing on 4 (3 ^ Ζ 2 ^') (hot water extraction ρ Η 4.0) was 8 ^ 2 2 (solid content:). I smeared it with a blade coater.
比較例 2 Comparative Example 2
塗液は笑施例 1 と 同様に作製し- 4 0 / ^ の中性 原羝 ( 熱水抽出 ρΗ 7,2 ) に塗抹量が 8.0 3 Z mZ 〔 固 形分 ） となる よ う ブ レ ー ド コ ー タ ー で塗拔し た。 The coating liquid was prepared in the same manner as in Example 1, and the amount of smear was adjusted to 8.0 3 Z mZ (solid component) on a neutral raw water (hot water extraction ρΗ 7,2) at −40 / ^. I painted it with a code coater.
比較例 5 Comparative Example 5
水 9 0 重量部に鼓化マグネ シ ゥ ム 1 α重量部を添加 し ょ く 分散したのち 1 0 ^の MS - 3 8 0 0 5 0重 量部加え よ く 混和し下引 き mと し.この液 ¾ 4 0 9 ZmZ の中性原羝 （ 熱水抽出 7 .2 ) に塗抹量が 1 / Add 1α parts by weight of magnesium bead to 90 parts by weight of water, disperse the mixture, and then add 10 parts by weight of MS-380 to 500 parts by weight. In this solution, the amount of smear on 1/9 Z mZ neutral solution (hot water extraction 7.2) was 1 /
( 固形分 ） と なる よ う に ェァ ー ナ イ フ コ ー タ ー で塗抹  (Solid content) with a nail-life coater
( OMPI し た （ これを c - 支持体と う ：） 。 (OMPI (This is called c-support :).
次に塗液は実施例 1 と 同様に作製 し、 c - 支持体に 塗抹量が 8 ^ 2 ( 固形分 ：） と なる よ う にブ レー ド コ ー タ ー で塗抹した。 試験結果 Next, a coating solution was prepared in the same manner as in Example 1, and smeared on a c-support with a blade coater so that the coating amount was 8 ^ 2 (solid content :). Test results
この様に し て得られた顕色剤 シー ト につ て下記の よ う な方法に て試験 · 測定した。  The developer sheet thus obtained was tested and measured by the following methods.
0 発 滠度 0 shots
顕色剤シー ト を前述の発色羝と 合わせて 9 6 αιの圧'力でカ レ ン ダ ーを通し て発色させ日 本電色測 色色差計にて反射率を測定した。 色濃度 - 色部の反射率 X 0 0  The color of the developer sheet was combined with the above-mentioned color shading by using a calender with a pressure of 96 αι, and the reflectance was measured with a Japanese colorimeter. Color density-reflectance of color part X 0 0
^ -m 白羝部の反射率 Ί u u ^ - the reflectance of the m white羝部Ί uu
( 力 レ ンダーを通し て発色させた後 1 時間後の発色 部 数値が小さい程発色擾度は高 こ と を示す。 (Coloring part 1 hour after coloring through the power render The smaller the numerical value, the higher the coloration disturbance.
保存性  Shelf life
①耐塩 ビ シ ー ト 性 ①Salt resistance
市販の塩 ビ シ ー ト （ ジ ォ ク チ ル フ タ レ ー ト 3 0 を含む塩 ビシー ト ；)と 、カ レ ン ダ ーを通し て凳色 させた発色部をかさね合わせ 0.1 ^Ζαιの圧力を 加え ό 0 °Gに 2 4 時間放置したのち反射率を測定 した。 塩ビシートとかさね合わせた  Combine a commercially available PVC sheet (PVC sheet containing dioctyl phthalate 30) with the color-developed part that has been colored through a calendar to 0.1 ^ 0.1αι. After applying pressure and leaving it at ό0 ° G for 24 hours, the reflectance was measured. Upholstered with PVC sheet
耐塩 ビ 発色部の反射率  PVC resistance Reflection of colored part
シート性： X 1 0 0 Sheet properties: X 1 0 0
( ） 塩ビシートとかさね合わせた () Overlaid with PVC sheet
白紙部の反射率 ②耐窒素鼓化物 （ NO∑ ガ ス ） 性 、 市販の窒素漦化物 （ ΝΟχ ガス ） 8 0 0 ppm 中に 来発色の頹色剤シー ト ¾ 3 0 分放置後に発色紙と 合わせて 9 ό Z COTの圧力でカ レ ン ダ ーを通して 凳色させ "！ 時間後に反射率 ¾測定した。 発色部の反射率 Blank sheet reflectance ② Nitrogen tamper (NO∑ gas) resistance, commercially available nitrogen oxidant (ΝΟχ gas) in 800 ppm of coloring agent sheet 後 に After standing for 30 minutes, add 9 ό Z together with colored paper The color was colored through the calendar at the pressure of the COT. "! After a while, the reflectance was measured. The reflectance of the colored portion
耐窒素鼓化物性 = X 0 0  Nitrogen tampering resistance = X 0 0
白羝部の反射率  The reflectance of the white shabu
0 表面強度 0 Surface strength
I&T 試験器 （ 熊谷理機睇製 ） ¾使用し て ェ？ ι ' ¾ 4 イ ン キ B ス リ ン グ で測定した。 その強度を強 順 に o 、 @、 厶 印と した。 袠 1 I & T tester (made by Kumagai Rikijin) て Use it? ι '¾ Measured at 4 inch B sling. The strengths are indicated by o, @, and rum in order.袠 1
Figure imgf000012_0001
Figure imgf000012_0001
表 1 から あ き らかな よ う に本癸明の水溶性アルカ リ を 原羝に処理する こ と に よ り 発色滠度、 保存性及び表面 強度が非常に向上する こ と が判明した。 As is clear from Table 1, it was found that the coloring intensity, preservability, and surface strength were greatly improved by treating the water-soluble alkali of Hon-ki-maki with the raw material.

Claims

請 求 の 範 园  Scope of claim
1. 鼋子供与性無色有機化合物を吸着 し て癸色する 吸着物質である活性白土含有顕色剤層を原羝上に設け てな'る ノ ー カ ー ボ ン複写羝用顕色剤 シー ト にお て、 前記原羝が予め水溶性ア ル力 リ で処理されて， る こ と を特徵とする ノ ー カ ーボ ン複写羝用頹色剤 シー ト 。 1. Adsorption of colorless organic compounds that donate electrons and coloration. A color developer layer containing activated clay, which is an adsorbent, is provided on the original tongue. A colorant sheet for a non-carbon carbon copy, which is characterized in that the raw rice is previously treated with a water-soluble alloy.
Z 処理した原羝の抽出 pH ( jis p - 8 1 3 3法 ） が 9.0〜 9.5 セある、 請求の範囲第 1 項記載の ノ ー力 一ボ ン複写羝用顕色剤 シー ト 。  2. The developer sheet for a black and white copying machine according to claim 1, wherein the extraction pH of the Z-treated raw rice stalk is 9.0 to 9.5 cells (jis p-8133 method).
5. 水溶性ア ル カ リ がケ ィ 鼓ナ ト リ ゥ ムである、 It 求の範囲第 1 項記載の ノ 一カ ー ボ ン複写羝用顕色剤シ 一 ト o  5. The developer sheet for non-carbon copying as described in item 1 of the scope of the claim, wherein the water-soluble alkali is a ketone sodium.
OMPI  OMPI
PCT/JP1982/000043 1981-02-18 1982-02-17 Color developer sheet for no-carbon copying paper WO1982002854A1 (en)