USRE38505E1 - Nonwoven fabrics having raised portions - Google Patents
Nonwoven fabrics having raised portions Download PDFInfo
- Publication number
- USRE38505E1 USRE38505E1 US09/414,230 US41423099A USRE38505E US RE38505 E1 USRE38505 E1 US RE38505E1 US 41423099 A US41423099 A US 41423099A US RE38505 E USRE38505 E US RE38505E
- Authority
- US
- United States
- Prior art keywords
- background portion
- raised
- raised portion
- basis weight
- background
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
Description
Claims (42)