USRE32411E - Rosin derivatives used as dispersants - Google Patents

Rosin derivatives used as dispersants Download PDF

Info

Publication number
USRE32411E
USRE32411E US06/762,350 US76235085A USRE32411E US RE32411 E USRE32411 E US RE32411E US 76235085 A US76235085 A US 76235085A US RE32411 E USRE32411 E US RE32411E
Authority
US
United States
Prior art keywords
iaddend
iadd
composition
polyester
pigment
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
US06/762,350
Inventor
G. Fredrick Hutter
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Flint Ink Corp
Original Assignee
BASF Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US06/399,643 external-priority patent/US4415705A/en
Application filed by BASF Corp filed Critical BASF Corp
Priority to US06/762,350 priority Critical patent/USRE32411E/en
Application granted granted Critical
Publication of USRE32411E publication Critical patent/USRE32411E/en
Assigned to FLINT INK CORPORATION reassignment FLINT INK CORPORATION ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: BASF CORPORATION
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

High-solids pigment concentrates are disclosed containing a novel dispersing agent formed by reacting a poly (lower alkylene) imine, having molecular weight of 1,000 to 15,000 with a .[.polyester.]. .Iadd.composition containing free carboxylic acid groups said composition .Iaddend.comprising .[.the esterification product of.]. .Iadd.a low molecular weight composition formed by heating .Iaddend.hydroxystearic acid, or its oligomer, with tall oil rosin.

Description

This invention relates to compounds which are useful as dispersing agents in preparing high-solids pigment concentrates for use in the manufacture of lithographic inks, and to concentrates and inks containing such compounds.
Due to the economics of the ink business today, it is highly desirable to be able to process pigments into high-solids concentrates. Typically, such concentrates would contain from 40 to 60% pigment. Ideally, they could be let down in a wide variety of vehicles in order to produce a wide range of finished inks.
The economic advantages offered by such concentrates are two-fold. First, they would greatly reduce the inventory of intermediates which must be carried by an ink plant. Only one intermediate dispersion would be needed for each pigment, versus the several which are now typically used. Second, energy consumption would be considerably reduced. The higher the pigment concentration at which dispersion can be effected, the less the total volume of material that must be processed through a mill, and therefore the less total energy consumed in processing the pigment.
Traditionally, vehicles for lithographic inks are composed of alkyl resins and/or rosin derivatives, together with high-boiling hydrocarbon solvents. It is known in the art that satisfactory dispersions containing 40 to 60% pigment cannot be prepared using such traditional vehicle components alone. Usually mixtures at such solids levels cannot be processed in standard milling equipment. In the few cases where they can be processed, they yield dispersions with unacceptable rheological properties, i.e. dispersions which cannot be pumped or otherwise conveniently transferred from one vessel to another. Such dispersions usually also show inferior color development, and poor aging stability.
Recently attempts have been made to overcome the above-described problems by using compounds which are better dispersants for pigments than are the traditional alkyd resins and rosin derivatives. For example U.S. Pat. No. 4,224,212 describes the use of dispersing agents attained by reacting a poly (lower alkylene) imine with a polyester having free carboxylic acid groups to form reaction products containing at least two polyester chains attached to each poly (lower alkylene) imine chain. Preferred polyesters are the polyesters of an hydroxy carboxylic acid of the formula HO--R--COOH where R is a divalent aliphatic radical containing at least 8 carbon atoms and in which there are at least 4 carbon atoms between the hydroxy and carboxylic acid groups. Preferred polyesters are also the polyesters formed from a mixture of aforementioned hydroxy carboxylic acids with a carboxylic acid which is free from hydroxy groups. Specific examples of hydroxy carboxylic acids mentioned in U.S. Pat. No. 4,224,212 are ricinoleic acid, a mixture of 9- and 10-hydroxystearic acid (obtained by sulphation of oleic acid followed by hydrolysis), and 12-hydroxystearic acid, and especially the commercially available hydrogenated castor oil fatty acid which contains minor amounts of stearic acid and palmitic acid. Specifically mentioned carboxylic acids free from hydroxy groups are alkyl and alkenyl carboxylic acids containing a chain of 8 to 20 carbon atoms, e.g. lauric acid, palmitic acid, stearic acid and oleic acid.
An especially preferred polyester disclosed in U.S. Pat. No. 4,224,212 is one prepared from commercial 12-hydroxy stearic acid having a number average molecular weight of about 1600, which corresponds to an oligomer containing an average of 4 to 5 molecules of polymerized 12-hydroxystearic acid and one molecule of esterified stearic acid. The stearic acid comes from the commercial grade of hydroxystearic acid which always contains some stearic acid. The preferred polyester is reacted with the polyethylene imine in the weight ratio of 1 to 10 parts polyester for each part of polyethylene imine.
The polyethylene imines preferred in the above cited prior art patent are either the substantially linear form or a branched form, especially a highly branched form in which at least 20% of the nitrogen atoms are present in tertiary amino groups, for example PEI600 (mol. wt. 50,000) and Polymin P (mol. wt. 50,000) and their methylated derivatives. The methylation is used apparently to convert some of the secondary amino nitrogen atoms to tertiary amino groups.
U.S. Pat. No. 4,224,212 further describes the preparation of pigment dispersion in liquid hydrocarbon using the above-described dispersing agents. The patent discloses that 5 to 50% by weight of dispersing agent, based on pigment can be used in the preparation of the dispersions; however, the patentees prefer 15 to 40% by weight of dispersant and illustrate by example only 15 to 30% by weight of dispersant based on pigment. The dispersions contain 20 to 50% by weight of pigment. The relatively high level of dispersing agent required renders these dispersions unsuitable for use in bases for lithographic ink production. Since their composition varies considerably from that of conventional vehicle components such as alkyds and rosin derivatives, the presence of such large quantities of these agents in a lithographic ink has a detrimental effect on such physico-chemical properties as tack and drying rate. Furthermore, the high amine content of these agents makes them hydrophilic, and the presence of large quantities of hydrophilic compounds in a lithographic ink causes problems of emulsification during printing.
It has now been discovered that very desirable dispersing agents can be made by reacting low molecular weight polyethylene imine with .Iadd.a .Iaddend.low molecular weight .[.polyesters.]. .Iadd.composition .Iaddend.formed by .[.esterifying.]. .Iadd.heating .Iaddend.commercial 12-hydroxystearic and tall oil rosin in the ratio of one mole of tall oil rosin and from one to six moles of 12-hydroxystearic acid.[.. The esterification is carried out by heating.]. at 200° to 205° C. for 12 hours in the presence of 0.1% dibutyltin oxide catalyst. .[.The structure of the polyester can be represented by the formula ##STR1## where ##STR2## is the rosin acid radical and the stearyl radical, and where n=1 to 6..].
The dispersing agent is formed by reacting the above .[.polyester.]. .Iadd.composition .Iaddend.with a low molecular weight polyethylene imine, e.g. molecular weight about 1,000 to 15,000, by heating for 6 hours at 150°-155° C. to give a viscous liquid. The ratio of .[.polyester.]. .Iadd.the composition .Iaddend.to polyethylene imine is preferably on the order of 75 to 99% by weight of the .[.polyester.]. .Iadd.composition .Iaddend.and 25 to 1% of the polyethylene imine. Such dispersing agents are very desirable for making high concentration pigment dispersions, or bases, for preparing printing inks, especially lithographic printing inks.
Although the rosin modified .[.polyester.]. .Iadd.composition.Iaddend./polyethylene imine dispersant as described has some similarity to the dispersants described in U.S. Pat. No. 4,224,212, it is to be noted that the rosin acid molecule is not linear and therefore does not give the "polyester chain" that is described in the patent. In view of the complex nature of the resinous acids contained in rosin it is not possible to anticipate exactly how it would behave in the .[.reaction.]. .Iadd.composition .Iaddend.with hydroxystearic acid. In fact it has been noted that not all rosins react with hydroxystearic acid to give the same products when further reacted with polyethylene imine. Dispersants made by reacting tall oil rosin .[.esters of.]. .Iadd.and .Iaddend.hydroxystearic acid oligomers with polyethylene imine have been found to be unexpectedly superior to products made from the wood rosin and gum rosin.
Furthermore, the above-described rosin derivatives are effective dispersants at a level of only 1-10% based on the weight of pigment, when used in conjunction with conventional rosin derivatives and/or alkyd resins. At such low levels, the dispersants are almost entirely adsorbed on the pigment surface and are therefore not free to cause emulsification problems during printing. Dispersants prepared according to the teaching of U.S. Pat. No. 4,224,212, when used at these low levels, give concentrates with unacceptable rheological properties.
The following examples in which the parts are by weight are given to illustrate further the invention.
EXAMPLE 1 Preparation of a Rosin-Based Dispersant
.[.An ester.]. .Iadd.A rosin based dispersant .Iaddend.is prepared by .[.reacting.]. .Iadd.heating .Iaddend.2340 parts of commercial 12-hydroxystearic acid with 756 parts of tall oil rosin (Unitol NCY Grade, available from Union Camp Corp.) at 200°-205° C. for 12 hours using 3.1 parts of dibutyltin oxide catalyst. 935 parts of the resulting .[.ester.]. .Iadd.composition .Iaddend.are then reacted with 65 parts of polyethylene imine having a molecular weight of 1200 at 150°-155° C. for six hours to form a rosin-modified dispersing agent in accordance with the invention.
EXAMPLE 2 Black Pigment Concentrate A carbon black dispersion was prepared from 
______________________________________                                    
Varnish (30% Alkyd resin,                                                 
                   16         parts                                       
30 Pentalyn G and 40%                                                     
Magie 470 oil)                                                            
Alkyd resin (as above)                                                    
                   9          parts                                       
Antioxidant (15% Phenol.                                                  
                   1          parts                                       
85% Magie 535)                                                            
Magiesol 52        10.5       parts                                       
Magie 535 oil      10.5       parts                                       
Carbon black pellets                                                      
                   50         parts                                       
(Regal 300I)                                                              
Rosin modified Dispersant                                                 
                   3          parts                                       
as in Ex. 1                                                               
______________________________________                                    
 by premixing the ingredients with a high speed disc disperser and then
 milling the ingredients in a Netzsch horizontal pin mill using 85% volume
 loading of 0.45 millimeter carbon steel shot as the grinding media and a
 feed rate of 10 pounds per hour.
The concentrate has a Brookfield viscosity of 282 poise initially and 368 poise after three days aging. It flows readily by gravity and can be handled by pumps commonly used in the art.
The alkyd resin used in the above example is a 68.5% linseed oil modified trimethylol ethane-isophthalic acid alkyd having an acid number of 10-12 and viscosity of z5-z6.
Magie 470 oil used in the above example is a petroleum hydrocarbon solvent having a distillation range of 462° to 516° F. (239°-269° C.).
Magie 535 oil used in the above example is a petroleum hydrocabon solvent having a distillation range of 510° to 600° F. (265° to 315° C.).
MagieSol 52 is a hydrocarbon solvent consisting essentially of saturated non-aromatic hydrocarbon having a distillation range of 508°-580° F. (264° to 305° C.).
Pentalyn G as used in the above example is described by the supplier as a hard thermoplastic resin which is a maleic-modified pentaerythritol ester of rosin. It has a softening point of 130°-140° C. (Hercules drop method).
EXAMPLE 3 Comparative Concentrate with No Dispersant
A concentrate made according to the formula in Example 2 but containing no dispersant could be premixed and milled only with extreme difficulty. Premixing was tedious because the pigment could only be added slowly by increments. Milling was slow and erratic; it could only be accomplished at an average feed rate of 5.4 lb./hour. The finished dispersion had a viscosity of 1170 poise and was extremely difficult to handle.
EXAMPLE 4 Comparative Concentrate with Non-Rosin Dispersant
A concentrate was made according to the formula in Example 2, substituting a dispersant made according to the teaching of U.S. Pat. No. 4,224,212, i.e., a dispersant as described in Example 1, but with stearic acid in place of the tall oil rosin. While premixing was easier than with no dispersant (Ex. 3), it was considerably more difficult than in Example 2. The pigment had to be added much more slowly to keep the premix flowing. Milling of this premix was also considerably more erratic than in the case of Example 2. The final dispersion had a viscosity of 226 poise, but it would not flow by gravity, and it thickened to 548 poise on standing for three days.
EXAMPLE 5 Preparation of Quickset Ink
An ink was prepared from
______________________________________                                    
Black concentrate    40.0      parts                                      
(as in Ex. 2)                                                             
Antioxidant (15% phenol,                                                  
                     1.0       parts                                      
85% Magie 535)                                                            
Drier (Mooney Ten-Cem Blend                                               
                     2.5       parts                                      
KK-804, containing 2.5--2.6% Zn, 0.75-0.85% Ca and                        
8.0-8.2% CO)                                                              
Wax compound (84.6% wax, .5%                                              
                     6.0       parts                                      
antioxidant as above, 14.9%                                               
Magie 535)                                                                
Varnish (19% Pentalyn 833,                                                
                     27.0      parts                                      
19% Filtrez 693 and 67%                                                   
linseed oil)                                                              
Varnish (42.5% Resin M93,                                                 
                     23.5      parts                                      
modified phenolic, 27.5%                                                  
linseed oil, 30% Magie 535)                                               
______________________________________
The above ingredients were mixed in a simple paddle mixer. The resulting ink had excellent printing properties. It showed sufficient penetration on porous stock to facilitate drying of the ink and in this respect was superior to an ink with similar composition except that it contained the stearic/hydroxystearic acid/polyethylene imine dispersant instead of the rosin modified disperant of the present invention. Similarly, prints made with ink had better gloss and density than the corresponding ink made with the stearic acid modified dispersant.
Pentalyn 833 as used in the above example is a phenolic-modified, rosin-derived resin having a softening point of 182°-188° C. (Hercules drop method).
Filtrez 693 as used in the above Example is described by the supplier as a rosin modified phenolic resin having a ring and ball melting point of 175° C. and an acid number of 11-12.
EXAMPLE 6 Preparation of a News Ink
A news ink was prepared from
______________________________________                                    
Black concentrate   38.0      parts                                       
(as in Ex. 2)                                                             
Nuso 250            45.0      parts                                       
Varnish (50% Nevchem 140,                                                 
                    14.0      parts                                       
50% Nuso 250)                                                             
Magie 535 oil       3.0       parts                                       
______________________________________
The above ingredients were mixed in a simple paddle mixer. This ink showed faster solvent penetration into the stock when printed, and therefore faster drying, than did an identical ink employing a concentrate employing the stearic/hydroxystearic acid dispersant.
Nevchem 140 is an alkylated aromatic hydrocarbon resin having a ring and ball softening point of 142° C. (288° F.).
Nuso 250 is a hydrocarbon oil of approximately 400 average molecular weight.
EXAMPLE 7 Heat-set Web Offset Ink
Further to illustrate the formulation flexibility of the concentrates discussed above, a heat-set ink was prepared from
______________________________________                                    
Black concentrate     31.5     parts                                      
(as in Ex. 2)                                                             
Varnish [33% Filtrez 623                                                  
                      5.0      parts                                      
resin, 67% alkyd, (90.8%                                                  
linseed oil, 5.1% fumaric                                                 
acid, 4.1% glycerin)]                                                     
Varnish (59.0% Nevroz 1520,                                               
                      48.5     parts                                      
1.5% glyceryl mono-oleate,                                                
0.6% aluminum isopropylate,                                               
0.3% tridecyl alcohol, 38.6%                                              
Magie 47 oil)                                                             
Linseed oil           3.0      parts                                      
Wax compound 30.0% polyethylene                                           
                      6.0      parts                                      
wax, 10.0% Magiesol 52, 60.0%                                             
varnish [43.9% Magie 470 oil,                                             
43.0% K1387 resin, 4.7% Penta-                                            
lyn G, 1.8% tridecyl alcohol,                                             
6.6% gellant compound (39.5%                                              
tridecyl alcohol, 21.5% phthalic                                          
anhydride, 26.0% Magie 470 oil,                                           
13.0% aluminum isopropylate)]                                             
Magie 470 oil         5.0      parts                                      
Antioxidant (85% Magie 535 oil,                                           
                      1.0      part                                       
15% phenol)                                                               
______________________________________
The ingredients were mixed with a simple paddle mixer. The resulting ink had excellent printing properties.
K1387 is an ink resin supplied by Lawter Chemical Co.
Nevroz 1520 is a hydrocarbon resin supplied by Neville Chemical Co.

Claims (8)

What is claimed is:
1. A dispersing agent formed by reacting a poly (lower alkylene) imine, having mol. wt. of 1,000 to 15,000 with a .[.polyester.]. .Iadd.composition .Iaddend.containing free carboxylic acid groups, said .[.polyester.]. .Iadd.composition .Iaddend.comprising .[.the esterification product of.]. .Iadd.a low molecular weight composition formed by heating .Iaddend.hydroxy stearic acid, or its oligomer, with tall oil rosin.
2. A dispersing agent according to claim 1 wherein the .[.esterification.]. .Iadd.reacting .Iaddend.is carried out by heating at 150° to 155° C. for 6 hours.
3. A dispersing agent according to claim 1 wherein the .[.polyester is the reaction product of.]. .Iadd.composition is formed by heating .Iaddend.1 mole of tall oil rosin with 2 moles of commercial 12-hydroxystearic acid containing approximately 12% of stearic acid.
4. A dispersing agent according to claim 3 wherein the poly (lower alkylene) imine is polyethylene imine having a molecular weight of 1200.
5. A pigment dispersion suitable for use in preparing inks, said dispersion comprising 40 to 60% by weight pigment, 6 to 18% by weight of alkyd resin, 0 to 6% by weight of non-alkyd resin, 2 to 10% by weight of .[.rosin modified polyester-polyimine.]. dispersing agent wherein said dispersing agent is formed by reacting a poly (lower alkylene) imine, having mol. wt. of 1,000 to 15,000 with a .[.polyester.]. .Iadd.composition .Iaddend.containing free carboxylic acid groups, said .[.polyester.]. .Iadd.composition .Iaddend.comprising .[.the esterification product of.]. .Iadd.a low molecular weight composition formed by heating .Iaddend.hydroxy stearic acid, or its oligomer, with tall oil rosin and enough solvent to total 100%.
6. A dispersion as in claim 5 wherein the pigment is carbon black.
7. A printing ink comprising pigment dispersed in an ink vehicle comprised of a liquid petroleum hydrocarbon solution of an ink resin and 1 to 10%, by weight, based pigment, of the dispersing agent of claim 1.
8. A printing ink as in claim 7 wherein the pigment is carbon black.
US06/762,350 1982-07-19 1985-08-02 Rosin derivatives used as dispersants Expired - Fee Related USRE32411E (en)