US20230392229A1 - High-strength steel strip having excellent workability, and method for manufacturing same - Google Patents
High-strength steel strip having excellent workability, and method for manufacturing same Download PDFInfo
- Publication number
- US20230392229A1 US20230392229A1 US18/032,328 US202118032328A US2023392229A1 US 20230392229 A1 US20230392229 A1 US 20230392229A1 US 202118032328 A US202118032328 A US 202118032328A US 2023392229 A1 US2023392229 A1 US 2023392229A1
- Authority
- US
- United States
- Prior art keywords
- steel strip
- steel
- relational expression
- less
- cooling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Links
- 229910000831 Steel Inorganic materials 0.000 title claims abstract description 187
- 239000010959 steel Substances 0.000 title claims abstract description 187
- 238000004519 manufacturing process Methods 0.000 title claims abstract description 26
- 238000000034 method Methods 0.000 title claims abstract description 25
- 238000001816 cooling Methods 0.000 claims description 73
- 230000014509 gene expression Effects 0.000 claims description 63
- 229910001562 pearlite Inorganic materials 0.000 claims description 35
- 238000005098 hot rolling Methods 0.000 claims description 33
- 150000001247 metal acetylides Chemical class 0.000 claims description 28
- 229910000859 α-Fe Inorganic materials 0.000 claims description 27
- 229910001563 bainite Inorganic materials 0.000 claims description 22
- 230000009467 reduction Effects 0.000 claims description 17
- 238000005275 alloying Methods 0.000 claims description 16
- 239000012535 impurity Substances 0.000 claims description 10
- 229910001566 austenite Inorganic materials 0.000 claims description 9
- 229910000734 martensite Inorganic materials 0.000 claims description 8
- 238000003303 reheating Methods 0.000 claims description 8
- XLYOFNOQVPJJNP-UHFFFAOYSA-N water Substances O XLYOFNOQVPJJNP-UHFFFAOYSA-N 0.000 claims description 6
- 238000005336 cracking Methods 0.000 abstract 1
- 230000000052 comparative effect Effects 0.000 description 48
- 239000011572 manganese Substances 0.000 description 44
- 239000010936 titanium Substances 0.000 description 41
- 239000010955 niobium Substances 0.000 description 40
- 239000011651 chromium Substances 0.000 description 27
- 230000000694 effects Effects 0.000 description 20
- 238000005728 strengthening Methods 0.000 description 14
- 230000015572 biosynthetic process Effects 0.000 description 13
- 238000005096 rolling process Methods 0.000 description 13
- IJGRMHOSHXDMSA-UHFFFAOYSA-N Atomic nitrogen Chemical compound N#N IJGRMHOSHXDMSA-UHFFFAOYSA-N 0.000 description 12
- 230000006866 deterioration Effects 0.000 description 12
- 239000000463 material Substances 0.000 description 12
- 239000002244 precipitate Substances 0.000 description 11
- 238000005204 segregation Methods 0.000 description 11
- 229910045601 alloy Inorganic materials 0.000 description 10
- 239000000956 alloy Substances 0.000 description 10
- 230000000875 corresponding effect Effects 0.000 description 10
- 229910052719 titanium Inorganic materials 0.000 description 10
- 229910052799 carbon Inorganic materials 0.000 description 9
- 229910052748 manganese Inorganic materials 0.000 description 9
- 239000000047 product Substances 0.000 description 9
- 230000009466 transformation Effects 0.000 description 9
- 229910052758 niobium Inorganic materials 0.000 description 8
- 239000006104 solid solution Substances 0.000 description 8
- 229910052782 aluminium Inorganic materials 0.000 description 7
- 238000009826 distribution Methods 0.000 description 7
- 239000000203 mixture Substances 0.000 description 7
- 229910052710 silicon Inorganic materials 0.000 description 7
- 229910052717 sulfur Inorganic materials 0.000 description 7
- OKTJSMMVPCPJKN-UHFFFAOYSA-N Carbon Chemical compound [C] OKTJSMMVPCPJKN-UHFFFAOYSA-N 0.000 description 6
- XUIMIQQOPSSXEZ-UHFFFAOYSA-N Silicon Chemical compound [Si] XUIMIQQOPSSXEZ-UHFFFAOYSA-N 0.000 description 6
- RTAQQCXQSZGOHL-UHFFFAOYSA-N Titanium Chemical compound [Ti] RTAQQCXQSZGOHL-UHFFFAOYSA-N 0.000 description 6
- 229910052804 chromium Inorganic materials 0.000 description 6
- 229910052757 nitrogen Inorganic materials 0.000 description 6
- 229910052698 phosphorus Inorganic materials 0.000 description 6
- 238000001953 recrystallisation Methods 0.000 description 6
- 239000010703 silicon Substances 0.000 description 6
- VYZAMTAEIAYCRO-UHFFFAOYSA-N Chromium Chemical compound [Cr] VYZAMTAEIAYCRO-UHFFFAOYSA-N 0.000 description 5
- PWHULOQIROXLJO-UHFFFAOYSA-N Manganese Chemical compound [Mn] PWHULOQIROXLJO-UHFFFAOYSA-N 0.000 description 5
- OAICVXFJPJFONN-UHFFFAOYSA-N Phosphorus Chemical compound [P] OAICVXFJPJFONN-UHFFFAOYSA-N 0.000 description 5
- NINIDFKCEFEMDL-UHFFFAOYSA-N Sulfur Chemical compound [S] NINIDFKCEFEMDL-UHFFFAOYSA-N 0.000 description 5
- GUCVJGMIXFAOAE-UHFFFAOYSA-N niobium atom Chemical compound [Nb] GUCVJGMIXFAOAE-UHFFFAOYSA-N 0.000 description 5
- 239000011574 phosphorus Substances 0.000 description 5
- 238000001556 precipitation Methods 0.000 description 5
- 239000011593 sulfur Substances 0.000 description 5
- ATJFFYVFTNAWJD-UHFFFAOYSA-N Tin Chemical compound [Sn] ATJFFYVFTNAWJD-UHFFFAOYSA-N 0.000 description 4
- XAGFODPZIPBFFR-UHFFFAOYSA-N aluminium Chemical compound [Al] XAGFODPZIPBFFR-UHFFFAOYSA-N 0.000 description 4
- XEEYBQQBJWHFJM-UHFFFAOYSA-N iron Substances [Fe] XEEYBQQBJWHFJM-UHFFFAOYSA-N 0.000 description 4
- 239000011159 matrix material Substances 0.000 description 4
- 230000003111 delayed effect Effects 0.000 description 3
- 239000002436 steel type Substances 0.000 description 3
- 238000005266 casting Methods 0.000 description 2
- 150000001768 cations Chemical class 0.000 description 2
- 238000005530 etching Methods 0.000 description 2
- 230000000704 physical effect Effects 0.000 description 2
- 238000007670 refining Methods 0.000 description 2
- 238000007711 solidification Methods 0.000 description 2
- 230000008023 solidification Effects 0.000 description 2
- 238000009628 steelmaking Methods 0.000 description 2
- 241000219307 Atriplex rosea Species 0.000 description 1
- 230000002159 abnormal effect Effects 0.000 description 1
- -1 and thus Substances 0.000 description 1
- 239000002131 composite material Substances 0.000 description 1
- 238000009749 continuous casting Methods 0.000 description 1
- 230000002596 correlated effect Effects 0.000 description 1
- 239000013078 crystal Substances 0.000 description 1
- 238000002425 crystallisation Methods 0.000 description 1
- 230000008025 crystallization Effects 0.000 description 1
- 238000005520 cutting process Methods 0.000 description 1
- 230000003247 decreasing effect Effects 0.000 description 1
- 230000007547 defect Effects 0.000 description 1
- 230000001419 dependent effect Effects 0.000 description 1
- 239000012467 final product Substances 0.000 description 1
- 238000010438 heat treatment Methods 0.000 description 1
- 229910052750 molybdenum Inorganic materials 0.000 description 1
- 230000003287 optical effect Effects 0.000 description 1
- 229910001568 polygonal ferrite Inorganic materials 0.000 description 1
- 238000004321 preservation Methods 0.000 description 1
- 230000001737 promoting effect Effects 0.000 description 1
- 239000004018 propan-1,2-diol esters of fatty acids Substances 0.000 description 1
- 239000000243 solution Substances 0.000 description 1
- 229910052720 vanadium Inorganic materials 0.000 description 1
- 208000016261 weight loss Diseases 0.000 description 1
Images
Classifications
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
- C21D9/52—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for wires; for strips ; for rods of unlimited length
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
- C21D1/02—Hardening articles or materials formed by forging or rolling, with no further heating beyond that required for the formation
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
- C21D1/18—Hardening; Quenching with or without subsequent tempering
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
- C21D1/56—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering characterised by the quenching agents
- C21D1/60—Aqueous agents
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
- C21D1/56—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering characterised by the quenching agents
- C21D1/613—Gases; Liquefied or solidified normally gaseous material
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D6/00—Heat treatment of ferrous alloys
- C21D6/002—Heat treatment of ferrous alloys containing Cr
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D6/00—Heat treatment of ferrous alloys
- C21D6/005—Heat treatment of ferrous alloys containing Mn
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D6/00—Heat treatment of ferrous alloys
- C21D6/008—Heat treatment of ferrous alloys containing Si
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0205—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips of ferrous alloys
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
- C21D8/0226—Hot rolling
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
- C21D8/0263—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment following hot rolling
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
- C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
- C21D8/04—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing
- C21D8/0421—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing characterised by the working steps
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
- C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/001—Ferrous alloys, e.g. steel alloys containing N
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/26—Ferrous alloys, e.g. steel alloys containing chromium with niobium or tantalum
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/28—Ferrous alloys, e.g. steel alloys containing chromium with titanium or zirconium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/38—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of manganese
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D2211/00—Microstructure comprising significant phases
- C21D2211/001—Austenite
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D2211/00—Microstructure comprising significant phases
- C21D2211/002—Bainite
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D2211/00—Microstructure comprising significant phases
- C21D2211/005—Ferrite
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D2211/00—Microstructure comprising significant phases
- C21D2211/008—Martensite
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D2211/00—Microstructure comprising significant phases
- C21D2211/009—Pearlite
Definitions
- the present disclosure relates to a steel strip and a method for manufacturing the same, and more particularly, to a steel strip having high strength characteristics and excellent workability and a method for manufacturing the same.
- a plate having a thickness of 12 to 14 mm and a tensile strength of 440 MPa or more and manufactured by a thick plate process has been mainly used, but recently, a technique using a high-strength steel material having a tensile strength of 550 MPa or more has been developed for weight reductions and high strength.
- a technique using a high-strength steel material having a tensile strength of 550 MPa or more has been developed for weight reductions and high strength.
- an ultra-thick steel material having a thickness of 15 to 25 mm that is applied to a large commercial vehicle, a special vehicle, and a heavy equipment part has been manufactured by a thick plate process, but a measure to apply a hot rolling process has been required to secure price competitiveness.
- Patent Document 1 has proposed a technique in which an austenite region is subjected to general hot rolling and then coiling is performed at a high temperature to form a ferrite phase as a matrix structure and a fine precipitate so as to secure strength and ductility
- Patent Document 2 has proposed a technique in which a coiling temperature is cooled to a temperature at which a bainite phase is formed as a matrix structure so as not to generate a coarse pearlite structure, and then coiling is performed.
- Patent Document 3 has proposed a technique of refining austenite grains through reductions of two or more times at 20 to 40% in a non-recrystallized region during hot rolling by using Ti, Nb, and the like.
- alloy components such as Si, Mn, Al, Mo, and Cr, which are mainly used in the above techniques for manufacturing high-strength thick steel, are effective in improving strength, but when a large amount of alloy components are added, segregation and non-uniformity of the microstructure occur, resulting in deterioration of workability, and microcracks generated on a shear surface easily propagate in a fatigue environment, resulting in breakage of parts.
- microstructure non-uniformity between a thickness surface portion and a central portion may be increased, such that a local stress concentration is increased and a propagation speed of cracks in a fatigue environment is also increased, resulting in deterioration of durability.
- precipitate-forming elements such as Ti, Nb, and V in order to refine grains of the thick steel material and obtain a precipitation strengthening effect, and when a cooling rate is not controlled during cooling after coiling at a high temperature of 500 to 700° C. at which precipitates are easily formed or hot rolling, coarse carbides are formed in the thickness central portion of the thick steel material, such that the quality of the shear surface is deteriorated.
- the application of a reduction amount of 20 to 40% twice or more in the non-recrystallized region during hot rolling may be easily applied to a thin product, but it is difficult to apply when manufacturing a thick product with a small total rolling reduction compared to the thin product.
- An aspect of the present disclosure is to provide a high-strength steel strip having excellent yield strength and elongation and prevents cracks when formed because a uniform microstructure is secured during a hot-rolling process of a steel material, and a method for manufacturing the same.
- a steel strip contains, by wt %, 0.05 to 0.15% of C, 0.01 to 1.0% of Si, 1.0 to 2.0% of Mn, 0.005 to 1.0% of Cr, 0.01 to 0.1% of Al, 0.001 to 0.02% of P, 0.001 to 0.01% of S, 0.001 to 0.01% of N, 0.005 to 0.11% of Ti, 0.005 to 0.07% of Nb, and a balance of Fe and unavoidable impurities,
- a surface portion (where t represents a thickness of the steel strip) in a range of 0 to t/4 and a central portion (not including t/4) in a range of t/4 to t/2 based on a cross section each contain, by area %, 90% or more of ferrite and bainite in total, less than 5% of pearlite and carbides having a diameter of 0.5 ⁇ m or more, and less than 5% of a martensite and austenite (MA) phase, as a microstructure,
- the thickness of the steel strip may be 15 mm or more.
- the pearlite and the carbides having a diameter of 0.5 ⁇ m or more may be 3% or less and the MA phase may be 3% or less, in terms of area % in the central portion of the steel strip.
- the bainite may be 20% or less, the pearlite and the carbides having a diameter of 0.5 ⁇ m or more may be less than 2%, and the MA phase may be 3% or less, in terms of area % in the surface portion of the steel strip.
- a difference between an average hardness value and a maximum hardness value of hardness values measured at intervals of 0.5 mm from a point located at 0.5 mm directly below a surface of a specimen to a point located at 0.5 mm directly below a back surface based on an arbitrary line perpendicular to a thickness cross section of the steel strip may be 20 Hv or less.
- a method for manufacturing a steel strip includes: reheating a steel slab containing, by wt %, 0.05 to 0.15% of C, 0.01 to 1.0% of Si, 1.0 to 2.0% of Mn, 0.005 to 1.0% of Cr, 0.01 to 0.1% of Al, 0.001 to 0.02% of P, 0.001 to 0.01% of S, 0.001 to 0.01% of N, 0.005 to 0.11% of Ti, 0.005 to 0.07% of Nb, and a balance of Fe and unavoidable impurities, and satisfying an R value defined in the following Relational Expression 1 of 0.3 to 1.0;
- the reheating may be performed in a temperature range of 1,200 to 1,350° C.
- the cooling rate may be 80° C./sec or less.
- air cooling or water cooling may be performed to a temperature range of room temperature to 200° C.
- a high-strength steel strip used for structural members of a large commercial vehicle, such as a wheel rim, a disk, members, and a frame, and a method for manufacturing the same.
- FIG. 1 illustrates products (YSxT-El) of a yield strength and an elongation and differences ( ⁇ H) between an average hardness value and a maximum hardness value at thickness cross sections of Inventive Steels and Comparative Steels.
- FIGS. 2 and 3 illustrate hardness value distributions at the thickness cross sections of Inventive Steels and Comparative Steels, respectively.
- the inventors of the present disclosure have investigated a distribution of microstructures and detailed material changes for each thickness direction according to components and hot rolling and cooling conditions for ultra-thick rolled steel materials having various components.
- the inventors of the present disclosure have found that a measure of imparting excellent yield strength and ductility to a thick hot-rolled steel strip, and in particular, have found that in a microstructure of a steel strip having a certain thickness or more, uniformity is secured and thus a hardness distribution in a thickness direction may be constant, thereby completing the present disclosure.
- % indicating a content of each element is based on weight.
- a steel strip according to an aspect of the present disclosure may contain, by wt %, 0.05 to 0.15% of C, 0.01 to 1.0% of Si, 1.0 to 2.0% of Mn, 0.005 to 1.0% of Cr, 0.01 to 0.1% of Al, 0.001 to 0.02% of P, 0.001 to 0.01% of S, 0.001 to 0.01% of N, 0.005 to 0.11% of Ti, 0.005 to 0.07% of Nb, and a balance of Fe and unavoidable impurities.
- Carbon (C) is the most economical and effective element for strengthening steel, and when the amount of C added is increased, a precipitation strengthening effect or a bainite phase fraction is increased, resulting in an increase in tensile strength.
- a thickness of a hot-rolled steel strip is increased, a cooling rate in a thickness central portion becomes slow during cooling after hot rolling, and thus, when a content of carbon (C) is large, coarse carbides or pearlite is easily formed.
- the content of carbon (C) may be 0.05 to 0.15%. More preferably, the content of carbon (C) may be 0.06% or more and may be 0.12% or less.
- Silicon (Si) has an effect of deoxidizing molten steel and a solid solution strengthening effect, and is only an element advantageous for improving the workability by delaying formation of coarse carbides.
- a content of silicon (Si) is less than 0.01%, the solid solution strengthening effect is insufficient, and the effect of delaying formation of carbides is also insufficient, such that it is difficult to improve the workability.
- a phase transformation temperature is increased, such that during hot rolling of a low-temperature region of an ultra-thick steel material, coarse grains are easily formed due to rolling of a local ferrite region in a surface portion, a red scale by silicon (Si) is formed on a surface of the steel strip, such that the surface quality of the steel strip is significantly deteriorated and ductility and weldability are also deteriorated.
- the content of silicon (Si) may be 0.01 to 1.0%. More preferably, the content of silicon (Si) may be 0.1% or more and may be 0.9% or less.
- manganese (Mn) is an element that is effective in strengthening solid solution of steel, and facilitates formation of a bainite phase during cooling after hot rolling by increasing hardenability of steel.
- a content of manganese (Mn) is less than 1.0%, the above effect according to the addition may not be obtained, and when the content thereof exceeds 2.0%, the hardenability is significantly increased, such that martensite phase transformation is likely to occur, and formation of pearlite is promoted during high-temperature coiling.
- a segregation portion is significantly developed in a thickness central portion when a slab is cast.
- the content of manganese (Mn) may be 1.0 to 2.0%. More preferably, the content of manganese (Mn) may be 1.1% or more.
- Chromium (Cr) is an element that strengthens solid solution of steel, and serves to help formation of bainite by delaying ferrite phase transformation during cooling.
- a content of chromium (Cr) is less than 0.005%, the above effect according to the addition may not be obtained, and when the content thereof exceeds 1.0%, the ferrite transformation is excessively delayed to form a martensite phase, resulting in deterioration of an elongation.
- the segregation portion is significantly developed in the thickness central portion, and a microstructure in the thickness direction is non-uniform, resulting in deterioration of the workability and durability.
- the content of chromium (Cr) may be 0.005 to 1.0%. More preferably, the content of chromium (Cr) may be 0.1% or more and may be 0.9% or less.
- Aluminum (Al) is an element mainly added for deoxidation.
- a content of aluminum (Al) is less than 0.01%, the addition effect is insufficient, and when the content thereof exceeds 0.1%, Al is combined with N to form AlN, such that corner cracks are likely to occur in the slab during continuous casting, and defects due to inclusion formation are likely to occur.
- the content of aluminum (Al) may be 0.01 to 0.1%.
- phosphorus (P) is an element having solid solution strengthening and ferrite transformation promoting effects at the same time.
- a content of phosphorus (P) exceeds 0.02%, brittleness occurs due to grain boundary segregation, and microcracks are likely to occur when formed, and the workability and durability are significantly deteriorated.
- a content of phosphorus (P) of less than 0.001% a lot of manufacturing cost is required, which is economically unfavorable and is insufficient to obtain strength.
- the content of phosphorus (P) may be 0.001 to 0.02%.
- Sulfur (S) is an impurity present in steel.
- S is combined with Mn and the like to form a non-metallic inclusion. Accordingly, microcracks are likely to occur during steel cutting processing, and the workability and durability are deteriorated.
- S sulfur
- the content of sulfur (S) may be 0.001 to 0.01%.
- Nitrogen (N) is a typical solid solution strengthening element together with C, and forms coarse precipitates together with Ti, Al, and the like.
- the solid solution strengthening effect of nitrogen (N) is superior to that of C, toughness is significantly decreased as the amount of nitrogen (N) in steel is increased. Therefore, an upper limit thereof is set to 0.01%.
- an upper limit thereof is set to 0.01%.
- N nitrogen
- the content of nitrogen (N) may be 0.001 to 0.01%.
- Titanium (Ti) is a typical precipitation strengthening element, and forms coarse TiN in steel with strong affinity with N. TiN has an effect of suppressing a growth of grains during a heat process for hot rolling.
- titanium (Ti) remaining after reacting with N is solid-dissolved in steel and combined with C to form TiC precipitates, and thus, Ti is useful for improving the strength of steel.
- a content of titanium (Ti) is less than 0.005%, the above effect is not obtained, and when the content thereof exceeds 0.11%, a local stress concentration occurs when formed due to generation of coarse TiN and coarsening of the precipitates, such that cracks are likely to occur.
- the content of titanium (Ti) may be 0.005 to 0.11%. More preferably, the content of titanium (Ti) may be 0.01% or more and may be 0.1% or less.
- Niobium (Nb) is a typical precipitation strengthening element together with Ti, and precipitates during hot rolling and thus is effective in improving the strength and impact toughness of steel due to a grain refinement effect caused by recrystallization delay.
- a content of niobium (Nb) is less than 0.005%, the above effect is not obtained, and when the content thereof exceeds 0.07%, the workability and durability are deteriorated due to formation of elongated grains and formation of coarse composite precipitates caused by excessive recrystallization delay during hot rolling.
- the content of niobium (Nb) may be 0.005 to 0.07%. More preferably, the content of niobium (Nb) may be 0.01% or more.
- the steel material of the present disclosure may contain a balance of iron (Fe) and unavoidable impurities in addition to the composition described above. Since the unavoidable impurities may be unintentionally incorporated in a general manufacturing process, the unavoidable impurities may not be excluded. Since these impurities are known to those skilled in a general steel manufacturing field, all the contents thereof are not particularly described in the present specification.
- an R value defined in the following Relational Expression 1 may be 0.3 to 1.0.
- Mn forms MnS, which is a non-metallic inclusion, together with Sn, and MnS is elongated during rolling, which causes significant deterioration of the workability of the final product.
- Si suppresses formation of coarse carbides and has a large solid solution strengthening effect even with a small amount of alloy, and Nb and Ti form fine precipitates and have an effect of refining a grain size, which is effective in solving the segregation and grain boundary embrittlement problems.
- a lower limit of the R value may be 0.5 and an upper limit of the R value may be 0.8.
- % indicating a fraction of a microstructure is based on area.
- a surface portion (where t represents a thickness of the steel strip) in a range of 0 to t/4 and a central portion (not including t/4) in a range of t/4 to t/2 based on a cross section each contain, by area %, 90% or more of ferrite and bainite in total, less than 5% of pearlite and carbides having a diameter of 0.5 ⁇ m or more, and less than 5% of a martensite and austenite (MA) phase, as a microstructure.
- MA martensite and austenite
- a microstructure of high-strength steel is determined during cooling. Bainite and a martensite and austenite (MA) phase are easily formed in a surface portion where a cooling rate is fast, whereas coarse carbides and pearlite are easily formed in a central portion where the cooling rate is slow.
- MA martensite and austenite
- the MA phase formed in the surface portion is a hard phase and exhibits a higher hardness than that of the surrounding microstructure, such that a non-uniform hardness distribution occurs, and microcracks occur due to a difference in hardness between the MA phase and the matrix structure when formed.
- the coarse carbides and pearlite formed in the central portion exhibit a higher hardness than that of the surrounding microstructure and are simultaneously brittle, which causes microcracks during shear formation.
- a fraction of the pearlite and carbides having a diameter of 0.5 ⁇ m or more is limited to less than 5%, and a fraction of the MA phase is limited to less than 5%.
- the fractions of the pearlite and carbides having a diameter of 0.5 ⁇ m or more and the MA phase may be equally applied to each of the surface portion and the central portion.
- containing 90% or more of ferrite and bainite is to suppress formation of unnecessary coarse carbides and pearlite so as to have a uniform hardness distribution for each thickness position and to secure excellent yield strength and elongation, and when less than 90% of ferrite and bainite are contained, it is difficult to secure the product value (YSxT-El) of the yield strength and the elongation targeted in the present disclosure. Therefore, in the present disclosure, 90% or more of ferrite and bainite in total may be contained.
- the pearlite and carbides having a diameter of 0.5 ⁇ m or more may be 3% or less and the MA phase may be 3% or less, and in the surface portion, the bainite may be 20% or less, the pearlite and carbides having a diameter of 0.5 ⁇ m or more may be less than 2%, and the MA phase may be 3% or less.
- the microstructure has the same characteristics in the surface portion and the central portion of the steel, and the microstructure proposed in the present disclosure is equally applied to the entire steel.
- the surface portion means a region in a range of 0 to t/4 (t represents a thickness of the steel strip) based on the cross section
- the central portion means a region in a range of t/4 to t/2 (not including t/4).
- Steel according to an aspect of the present disclosure may be manufactured by subjecting a steel slab satisfying the alloy composition described above to reheating, hot rolling, first cooling, coiling, and second cooling.
- a steel slab satisfying the alloy composition described above may be reheated in a temperature range of 1,200 to 1,350° C.
- the reheated steel slab may be hot-rolled in a temperature range of 800 to 1,150° C. at a reduction ratio of 20 to 50%, and the rolling may be finished in a temperature range of Tn ⁇ 50 to Tn defined in the following Relational Expression 2.
- the hot rolling temperature exceeds 1,150° C.
- the temperature of the steel strip is excessively increased, such that the grain size is coarsened and the surface quality of the hot-rolled steel strip is deteriorated.
- the temperature is lower than 800° C.
- elongated grains are developed due to excessive recrystallization delay, resulting in severe anisotropy and deterioration of the workability, and when rolling is performed at a temperature below an austenite temperature range, a non-uniform microstructure is developed more severely. Therefore, microcracks are likely to occur in non-uniform portions when formed, which also causes deterioration of the ductility.
- a rolling end temperature exceeds Tn
- the microstructure of the steel is coarsened and non-uniform.
- Tn the temperature is lower than Tn ⁇ 50
- a fraction of a fine ferrite phase is increased due to the promotion of ferrite phase transformation in the surface portion where the temperature is relatively low, but an elongated grain shape is formed, which causes cracks to propagate quickly, and a non-uniform microstructure may remain in the central portion, resulting in unfavorable durability.
- the rolling end temperature determined by Relational Expression 2 of the present disclosure means a temperature of the hot-rolled steel strip at the end of hot rolling.
- a reduction amount in the hot-rolling temperature range may be 20 to 50%.
- the reduction amount is less than 20%, it is difficult to obtain the recrystallization delay effect and thus non-uniform coarse grains are easily formed, and when the reduction amount exceeds 50%, an excessively elongated microstructure is formed and carbides are formed along the grain boundaries, such that cracks are likely to occur along the grain boundaries when formed. In addition, fine precipitates are also reduced and the precipitation strengthening effect is also reduced.
- the hot-rolled steel strip may be subjected to first cooling to a temperature range of 450 to 550° C. at a cooling rate equal to or higher than CR Min defined in the following Relational Expression 3, and then the cooled hot-rolled steel strip may be coiled.
- a temperature range from immediately after the hot rolling to the cooling end temperature corresponds to a temperature section in which the ferrite phase transformation occurs during cooling. Since a cooling rate in the thickness central portion is slower than that in the thickness surface portion of the rolled strip, a coarse ferrite phase and coarse carbides are formed in the thickness central portion, and thus the steel strip has a non-uniform microstructure. Therefore, in order to suppress this, in the present disclosure, it is required to perform cooling faster than a specific cooling rate (CR Min ).
- CR Min specific cooling rate
- the cooling rate determined by Relational Expression 3 of the present disclosure means a cooling rate of the hot-rolled steel strip after hot rolling.
- a pearlite phase is formed as a band structure or a large amount of coarse carbides are formed, which causes deterioration of the workability and durability, and when the temperatures are lower than 450° C., a martensite phase and an MA phase are excessively formed, which causes deterioration of the workability and durability.
- the coiled steel strip may be subjected to second cooling to a temperature range of room temperature to 200° C., and the second cooling may be air cooling or water cooling.
- air cooling means cooling performed in the air at room temperature and a cooling rate of 0.001 to 10° C./hour. Even in a case where the cooling rate exceeds 10° C./hour, when it complies with the coiling temperature and the first cooling conditions, transformation of some of the untransformed phases in the steel into an MA phase may be suppressed. Therefore, water cooling may be performed.
- water cooling means cooling performed by charging a coil into a water bath at room temperature.
- a separate heating and heat preservation facility and the like are required, which is economically unfavorable. Therefore, a lower limit of the cooling rate may be 0.001° C./hour.
- the steel strip of the present disclosure manufactured as described above is a steel strip having a thickness of 10 mm or more, more preferably, may have a thickness of 15 mm or more, and may be a steel strip having an upper limit of a thickness of 25 mm.
- a difference between an average hardness value and a maximum hardness value of hardness values measured at intervals of 0.5 mm from a point located at 0.5 mm directly below a surface of a specimen to a point located at 0.5 mm directly below a back surface based on an arbitrary line perpendicular to a thickness cross section of the steel strip may be 20 Hv or less, and more preferably, the average hardness value may be 160 to 300 Hv.
- the product (YSxT-E) value of the yield strength and the elongation is 16,000 MPa ⁇ % or more, high strength and excellent workability may be provided.
- Table 2 shows the values of the rolling end temperature (FDT), the total reduction amount (%), the coiling temperature (CT), the cooling rate (CR*) up to the coiling temperature, which is the cooling end temperature after hot rolling, Tn and Tn ⁇ 50 defined in Relational Expression 2, and the minimum cooling rate (CR Min ) defined in Relational Expression 3 of the steel types shown in Table 1.
- the reheating temperature, the hot rolling temperature, and the cooling rate of the steel strip after coiling not shown in Table 2 were equally applied as 1,250° C., 800 to 1,150° C., and 1° C./hour, respectively.
- microstructure characteristics and mechanical properties of the steel types are shown in Tables 3 and 4.
- the microstructure shown in Table 3 is a result of analysis at a point located at 0.5 mm directly below a surface and a central portion of the hot-rolled strip.
- the surface portion means a range of 0 to t/4 based on the thickness (t)
- the central portion means a range of t/4 to t/2 (not including t/4).
- the microstructure in the surface portion is a result of analysis at a point located at 0.5 mm directly below the surface
- the microstructure in the central portion is a result of analysis at t/2, which is a thickness central portion.
- the area fraction of the MA phase was measured after etching by Lepera etching method using an optical microscope and an image analyzer and was analyzed at 1,000 magnification.
- the area fractions of the martensite and austenite phase (MA), ferrite phase (F), bainite phase (B), and pearlite phase (P) were analyzed using a scanning electron microscope (SEM) at 3,000 to 5,000 magnification.
- ferrite (F) is polygonal ferrite having an equiaxed crystal shape
- bainite (B) means a ferrite phase observed in a low-temperature region such as bainite, acicular ferrite, or bainitic ferrite.
- an area fraction of pearlite (P) means the sum of area fractions of pearlite and carbides having a size of 0.5 ⁇ m or more.
- YS, TS, and T-El in Table 4 mean 0.2% off-set yield strength, tensile strength, elongation at break, respectively, which are test results obtained by taking a JIS No. 5 standard test piece parallel to a rolling direction.
- the hardness at a cross section of the specimen is measured and shown together. The hardness was measured at intervals of 0.5 mm from a point located at 0.5 mm directly below a surface of the specimen to a point located at 0.5 mm directly below a back surface based on an arbitrary line perpendicular to a thickness cross section of the specimen with a Micro-vickers tester, and a load of 500 g was applied.
- Table 4 shows a maximum hardness value and an average hardness value at the thickness cross section among the measured hardness values, and a difference between two hardness values is shown. Peak (number) means the number of portions where the difference between the hardness value and the average hardness value at the thickness point exceeds 20 Hv.
- FIG. 1 illustrates products of the yield strength and the elongation and differences between the average hardness value and the maximum hardness value at the thickness cross sections of Inventive Steels and Comparative Steels. It could be confirmed that in Inventive Steels, the difference in hardness value was 20 Hv or less, and the value of YS x T-El was 16,000 MPa-% or more.
- FIGS. 2 and 3 illustrate the hardness value distributions at the thickness cross sections of Inventive Steels and Comparative Steels, respectively.
- Comparative Steels it could be confirmed that the hardness value of the thickness central portion was relatively low compared to that of the surface portion, and the difference according to the thickness position was also large.
- Comparative Steel 2 since the content of Mn was small, segregation in the thickness direction of the rolled steel strip or coarse carbides and non-uniform pearlite were not formed, but the yield strength and the tensile strength were insufficient, and thus, the properties targeted in the present disclosure were not obtained.
- Comparative Steel 3 since the content of Mn was excessive, bainite was formed in the surface portion due to high hardenability, whereas pearlite was excessively formed in the central portion, and elongated MnS inclusions were also observed. In particular, when the hardness was measured in the thickness direction, a locally high hardness difference was exhibited, and the ductility was also insufficient.
- Comparative Steel 4 was a case in which the content of P was out of the range proposed in the present disclosure, and Relational Expression 1 was not satisfied at the same time.
- the range proposed in the present disclosure was satisfied, and the strength and the elongation were also excellent, but when the hardness was measured, a local hardness difference was exhibited, which may cause a high possibility of brittleness when used after manufacturing parts.
- Comparative Steel 6 satisfied the alloy component range of the present disclosure, but did not satisfy Relational Expression 1. In this case, segregation of the components was not observed, an MA phase and coarse carbides were hardly formed in the microstructure, and only fine pearlite was observed around grain boundaries. Therefore, the hardness distribution in the thickness direction was also relatively uniform. However, the hardness value targeted in the present disclosure was not secured.
- Comparative Steels 7 and 8 did not satisfy Relational Expression 2 and the reduction ratio.
- the rolling was terminated in a temperature range satisfying Relational Expression 2, but a non-uniform microstructure was formed during cooling due to an insufficient reduction ratio. Therefore, the compositional fraction of the microstructure satisfied the present disclosure, but coarse grains were mixed in the ferrite matrix structure, resulting in a low yield strength. The durability of the steel having such a microstructure may be deteriorated during use of parts.
- Comparative Steels 9 and 10 the coiling temperature conditions were not satisfied.
- the cooling end temperature and the coiling temperature were higher than those of the temperature ranges proposed in the present disclosure, it was confirmed that pearlite was locally formed, and in particular, the pearlite band structure was observed in the central portion. Therefore, when the hardness in the thickness direction was measured, a locally high hardness difference was shown.
- the cooling end temperature and the coiling temperature were lower than those of the ranges proposed in the present disclosure.
- bainite was excessively formed in the microstructure in the surface portion, and the elongation was insufficient.
- Comparative Steel 11 in which the cooling rate conditions of the cooling rate relational expression 3 were not satisfied and the cooling rate during cooling after hot rolling was lower than the range of the present disclosure, pearlite and coarse carbides were formed in the thickness central portion, and thus a locally high hardness difference was shown.
- Comparative Steels 12 and 13 the reduction amount and cooling end temperature conditions were not satisfied.
- the reduction amount was insufficient in a temperature range in which recrystallization was delayed during hot rolling, and the coiling temperature was low, such that the size of the ferrite grains was non-uniform and bainite in the microstructure in the surface portion was excessively formed.
- pearlite was also locally observed in the central portion, resulting in a low elongation.
- the reduction amount was insufficient in the temperature region in which crystallization was delayed, the coiling temperature was high, and the cooling rate did not satisfy Relational Expression 3. Therefore, it was confirmed that the microstructure was non-uniform, pearlite was formed as a band structure, and the yield strength was low.
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Mechanical Engineering (AREA)
- Materials Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Physics & Mathematics (AREA)
- Thermal Sciences (AREA)
- Crystallography & Structural Chemistry (AREA)
- Heat Treatment Of Steel (AREA)
- Heat Treatment Of Sheet Steel (AREA)
Applications Claiming Priority (3)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
KR1020200138314A KR102409896B1 (ko) | 2020-10-23 | 2020-10-23 | 성형성이 우수한 고강도 후물 강판 및 그 제조방법 |
KR10-2020-0138314 | 2020-10-23 | ||
PCT/KR2021/014695 WO2022086166A1 (ko) | 2020-10-23 | 2021-10-20 | 성형성이 우수한 고강도 후물 강판 및 그 제조방법 |
Publications (1)
Publication Number | Publication Date |
---|---|
US20230392229A1 true US20230392229A1 (en) | 2023-12-07 |
Family
ID=81290889
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
US18/032,328 Pending US20230392229A1 (en) | 2020-10-23 | 2021-10-20 | High-strength steel strip having excellent workability, and method for manufacturing same |
Country Status (6)
Country | Link |
---|---|
US (1) | US20230392229A1 (de) |
EP (1) | EP4234747A1 (de) |
JP (1) | JP2023546216A (de) |
KR (1) | KR102409896B1 (de) |
CN (1) | CN116568845A (de) |
WO (1) | WO2022086166A1 (de) |
Family Cites Families (9)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP3477955B2 (ja) | 1995-11-17 | 2003-12-10 | Jfeスチール株式会社 | 極微細組織を有する高張力熱延鋼板の製造方法 |
JP3888128B2 (ja) | 2000-10-31 | 2007-02-28 | Jfeスチール株式会社 | 材質均一性に優れた高成形性高張力熱延鋼板ならびにその製造方法および加工方法 |
JP5724267B2 (ja) | 2010-09-17 | 2015-05-27 | Jfeスチール株式会社 | 打抜き加工性に優れた高強度熱延鋼板およびその製造方法 |
JP6354274B2 (ja) | 2014-04-11 | 2018-07-11 | 新日鐵住金株式会社 | 熱延鋼板およびその製造方法 |
KR101897932B1 (ko) * | 2014-07-14 | 2018-09-12 | 신닛테츠스미킨 카부시키카이샤 | 열연 강판 |
KR102045641B1 (ko) * | 2017-12-22 | 2019-11-15 | 주식회사 포스코 | 저온에서의 내파괴 특성이 우수한 극지 환경용 고강도 강재 및 그 제조방법 |
CN109207695B (zh) * | 2018-08-27 | 2020-07-14 | 南京钢铁股份有限公司 | 一种降低x80m级管线钢硬度的生产方法 |
KR102131527B1 (ko) * | 2018-11-26 | 2020-07-08 | 주식회사 포스코 | 내구성이 우수한 고강도 강재 및 이의 제조방법 |
KR102119975B1 (ko) * | 2018-11-29 | 2020-06-08 | 주식회사 포스코 | 저온인성과 연신율이 우수하며, 항복비가 작은 후물 고강도 라인파이프용 강재 및 그 제조방법 |
-
2020
- 2020-10-23 KR KR1020200138314A patent/KR102409896B1/ko active IP Right Grant
-
2021
- 2021-10-20 WO PCT/KR2021/014695 patent/WO2022086166A1/ko active Application Filing
- 2021-10-20 CN CN202180072724.5A patent/CN116568845A/zh active Pending
- 2021-10-20 US US18/032,328 patent/US20230392229A1/en active Pending
- 2021-10-20 EP EP21883234.3A patent/EP4234747A1/de active Pending
- 2021-10-20 JP JP2023524172A patent/JP2023546216A/ja active Pending
Also Published As
Publication number | Publication date |
---|---|
JP2023546216A (ja) | 2023-11-01 |
KR102409896B1 (ko) | 2022-06-20 |
KR20220053943A (ko) | 2022-05-02 |
WO2022086166A1 (ko) | 2022-04-28 |
EP4234747A1 (de) | 2023-08-30 |
CN116568845A (zh) | 2023-08-08 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
CN113166893B (zh) | 耐久性优异的高强度钢材及其制造方法 | |
EP3730647B1 (de) | Hochfestes warmgewalztes stahlblech mit hervorragender biegbarkeit und niedrigtieftemperaturbeständigkeit sowie verfahren zur herstellung davon | |
JP4901623B2 (ja) | 打ち抜き穴広げ性に優れた高強度薄鋼板およびその製造方法 | |
US11466336B2 (en) | High-strength steel sheet having excellent burring workability in low temperature range and manufacturing method therefor | |
US20220403489A1 (en) | Thick composite-phase steel having excellent durability and manufacturing method therefor | |
CN113692456B (zh) | 剪切加工性优异的超高强度钢板及其制造方法 | |
JP6066023B1 (ja) | 熱延鋼板、フルハード冷延鋼板及び熱延鋼板の製造方法 | |
EP4219784A1 (de) | Hochfestes dickes warmgewalztes stahlblech und verfahren zur herstellung davon | |
JP6684905B2 (ja) | 剪断加工性に優れた高強度冷延鋼板及びその製造方法 | |
US20220389548A1 (en) | High-strength steel having high yield ratio and excellent durability, and method for manufacturing same | |
US20230392229A1 (en) | High-strength steel strip having excellent workability, and method for manufacturing same | |
KR102328392B1 (ko) | 펀칭 가공부 단면품질이 우수한 초고강도 강판 및 그 제조방법 | |
KR101443442B1 (ko) | 고강도 냉연강판 및 그 제조 방법 | |
CN116368253A (zh) | 热稳定性优异的高强度钢板及其制造方法 | |
KR20210063135A (ko) | 내구성 및 연신율이 우수한 후물 변태조직강 및 그 제조방법 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
AS | Assignment |
Owner name: POSCO CO., LTD, KOREA, REPUBLIC OF Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:KIM, SUNG-IL;NA, HYUN-TAEK;REEL/FRAME:063348/0165 Effective date: 20221206 |
|
STPP | Information on status: patent application and granting procedure in general |
Free format text: DOCKETED NEW CASE - READY FOR EXAMINATION |