US20230299154A1 - Method of forming contact structures - Google Patents
Method of forming contact structures Download PDFInfo
- Publication number
- US20230299154A1 US20230299154A1 US18/321,609 US202318321609A US2023299154A1 US 20230299154 A1 US20230299154 A1 US 20230299154A1 US 202318321609 A US202318321609 A US 202318321609A US 2023299154 A1 US2023299154 A1 US 2023299154A1
- Authority
- US
- United States
- Prior art keywords
- source
- layer
- contact
- drain contact
- gate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A method according to the present disclosure includes receiving a workpiece that includes a first gate structure including a first cap layer thereon, a first source/drain contact adjacent the first gate structure, a second gate structure including a second cap layer thereon, a second source/drain contact, an etch stop layer (ESL) over the first source/drain contact and the second source/drain contact, and a first dielectric layer over the ESL. The method further includes forming a butted contact opening to expose the first cap layer and the first source/drain contact, forming a butted contact in the butted contact opening, after the forming of the butted contact, depositing a second dielectric layer, forming a source/drain contact via opening through the second dielectric layer, the ESL layer, and the first dielectric layer to expose the second source/drain contact, and forming a source/drain contact via in the source/drain contact via opening.
Description
- The present application is a divisional application of U.S. Pat. Application No. 17/229,069, filed Apr. 13, 2021, which claims the benefit of U.S. Provisional Application No. 63/151,108, entitled “Method of Forming Contact Structures,” filed Feb. 19, 2021, each of which is herein incorporated by reference in its entirety.
- The integrated circuit (IC) industry has experienced exponential growth. Technological advances in IC materials and design have produced generations of ICs, where each generation has smaller and more complex circuits than the previous generation. In the course of IC evolution, functional density (i.e., the number of interconnected devices per chip area) has generally increased while geometry size (i.e., the smallest component (or line) that can be created using a fabrication process) has decreased. This scaling down process generally provides benefits by increasing production efficiency and lowering associated costs.
- As scaling down of IC devices continues, dimensions of contact vias, such as gate contact via and source/drain contact vias, are becoming smaller and smaller. While advanced lithography techniques allow formation of high-aspect-ratio contact via openings, filling of conductive materials in the high-aspect-ratio via openings has proven challenging. Additionally, deposition of a metal fill layer on different metal surfaces may experience different deposition rates, resulting in unsatisfactory metal filling or voids. While existing methods for forming contacts to transistors are adequate for their intended purposes, they are not satisfactory in all aspects.
- The present disclosure is best understood from the following detailed description when read with the accompanying figures. It is emphasized that, in accordance with the standard practice in the industry, various features are not drawn to scale and are used for illustration purposes only. In fact, the dimensions of the various features may be arbitrarily increased or reduced for clarity of discussion.
-
FIG. 1 is a flow chart of a method for fabricating a common rail contact, according to various aspects of the present disclosure. -
FIGS. 2-14 are fragmentary cross-sectional views of a workpiece at various stages of fabrication of the method inFIG. 1 , according to various aspects of the present disclosure. -
FIG. 15 is a fragmentary top view of a semiconductor device that includes gate contacts, source/drain contact vias, and butted contacts, according to various aspects of the present disclosure. - The following disclosure provides many different embodiments, or examples, for implementing different features of the provided subject matter. Specific examples of components and arrangements are described below to simplify the present disclosure. These are, of course, merely examples and are not intended to be limiting. For example, the formation of a first feature over or on a second feature in the description that follows may include embodiments in which the first and second features are formed in direct contact, and may also include embodiments in which additional features may be formed between the first and second features, such that the first and second features may not be in direct contact. In addition, the present disclosure may repeat reference numerals and/or letters in the various examples. This repetition is for the purpose of simplicity and clarity and does not in itself dictate a relationship between the various embodiments and/or configurations discussed.
- Spatially relative terms, such as “beneath,” “below,” “lower,” “above,” “upper” and the like, may be used herein for ease of description to describe one element or feature’s relationship to another element(s) or feature(s) as illustrated in the figures. The spatially relative terms are intended to encompass different orientations of the device in use or operation in addition to the orientation depicted in the figures. The apparatus may be otherwise oriented (rotated 90 degrees or at other orientations) and the spatially relative descriptors used herein may likewise be interpreted accordingly.
- Further, when a number or a range of numbers is described with “about,” “approximate,” and the like, the term is intended to encompass numbers that are within a reasonable range considering variations that inherently arise during manufacturing as understood by one of ordinary skill in the art. For example, the number or range of numbers encompasses a reasonable range including the number described, such as within +/-10% of the number described, based on known manufacturing tolerances associated with manufacturing a feature having a characteristic associated with the number. For example, a material layer having a thickness of “about 5 nm” can encompass a dimension range from 4.25 nm to 5.75 nm where manufacturing tolerances associated with depositing the material layer are known to be +/-15% by one of ordinary skill in the art. Still further, the present disclosure may repeat reference numerals and/or letters in the various examples. This repetition is for the purpose of simplicity and clarity and does not in itself dictate a relationship between the various embodiments and/or configurations discussed.
- As dimensions of semiconductor devices continue to scale down, use of a local interconnect structure to couple a gate structure and an adjacent source/drain contact becomes commonplace. In some examples, the gate structure is capped by a cap layer that is different from a composition of the source/drain contact. During the formation of the local interconnect structure, a fill layer is deposited by chemical vapor deposition (CVD) or a selective deposition method. It is observed that the fill layer may be deposited faster on the source/drain contact than over the cap layer. Additionally, before the metal fill process to form the local interconnect structure, surfaces of the source/drain contact and the cap layer may be exposed to various oxidation or reduction atmosphere. The difference in reductivity between different materials may also contribute to the differential deposition rates. The different deposition rates on different surfaces may cause the local interconnect structure to have poor contact to the gate structure.
- The present disclosure provides method to form a butted contact to couple a gate structure with an adjacent source/drain contact before formation of a source/drain contact via and formation of a gate contact. A butted contact opening for the butted contact has a low aspect ratio and metal filling into the butted contact opening is performed using a combination of physical vapor deposition (PVD) and chemical vapor deposition (CVD). As a result, top surfaces of the source/drain contact via and the gate contact are higher than a top surface of the butted contact. Embodiments of the present disclosure may reduce or eliminate issues associated with differential deposition rates on different surfaces. Methods of the present disclosure reduce the possibility of void formation.
- The various aspects of the present disclosure will now be described in more detail with reference to the figures. In that regard,
FIG. 1 is a flowchart illustrating amethod 100 of forming contact structures according to embodiments of the present disclosure.Method 100 is merely an example and is not intended to limit the present disclosure to what is explicitly illustrated inmethod 100. Additional steps can be provided before, during and after themethod 100, and some steps described can be replaced, eliminated, or moved around for additional embodiments of the method. Not all steps are described herein in detail for reasons of simplicity.Method 100 is described below in conjunction withFIGS. 2-14 , which are fragmentary cross-sectional views of aworkpiece 200 at different stages of fabrication according to embodiments of themethod 100 inFIG. 1 . For avoidance of doubts, the X, Y and Z directions inFIGS. 2-14 are perpendicular to one another and are used consistently throughoutFIGS. 2-14 . Because theworkpiece 200 will be fabricated into a semiconductor device or a semiconductor structure, theworkpiece 200 may be referred to herein as asemiconductor device 200 or asemiconductor structure 200 as the context requires. Throughout the present disclosure, like reference numerals denote like features unless otherwise excepted. - Referring to
FIGS. 1 and 2 ,method 100 includes ablock 102 where aworkpiece 200 is received. Theworkpiece 200 includes asubstrate 202. In the depicted embodiment,substrate 202 includes silicon (Si). Alternatively or additionally,substrate 202 may include another elementary semiconductor, such as germanium (Ge); a compound semiconductor, such as silicon carbide (SiC), gallium arsenide (GaAs), gallium phosphide (GaP), indium phosphide (InP), indium arsenide (InAs), and/or indium antimonide (InSb); an alloy semiconductor, such as silicon germanium (SiGe), gallium arsenic phosphide (GaAsP), aluminum indium arsenide (AlInAs), aluminum gallium arsenide (AlGaAs), gallium indium arsenide (GaInAs), gallium indium phosphide (GaInP), and/or gallium indium arsenic phosphide (GaInAsP); or combinations thereof. In some implementations,substrate 202 includes one or more group III-V materials, one or more group II-VI materials, or combinations thereof. In some implementations,substrate 202 is a semiconductor-on-insulator substrate, such as a silicon-on-insulator (SOI) substrate, a silicon germanium-on-insulator (SGOI) substrate, or a germanium-on-insulator (GeOI) substrate. Semiconductor-on-insulator substrates can be fabricated using implantation of oxygen (SIMOX), wafer bonding, and/or other suitable methods.Substrate 202 can include various doped regions (not shown) configured according to design requirements ofsemiconductor device 200, such as p-type doped regions, n-type doped regions, or combinations thereof. P-type doped regions (for example, p-type wells) include p-type dopants, such as boron (B), boron difluoride (BF2), other p-type dopant, or combinations thereof. N-type doped regions (for example, n-type wells) include n-type dopants, such as phosphorus (P), arsenic (As), other n-type dopant, or combinations thereof. An ion implantation process, a diffusion process, and/or other suitable doping process can be performed to form the various doped regions. Thesubstrate 202 is shown in dotted lines inFIG. 2 and is omitted fromFIGS. 3-14 for simplicity. - As shown in
FIG. 2 , theworkpiece 200 includes anactive region 204 of a multi-gate device, such as a fin-type field effect transistors (FinFET) or a multi-bridge-channel (MBC) transistor. When theactive region 204 is for a FinFET, theactive region 204 may be a fin element (or fin structure) that extends lengthwise along the X. When theactive region 204 is for an MBC transistor, the active region may be a vertical stack of channel members, each of which extends lengthwise along the X direction. Because a gate structure of an MBC transistor wraps around each of the channel regions, an MBC transistor may also be referred to as a surrounding gate transistor (SGT) or a gate-all-around (GAA) transistor. The channel members come in forms of nanostructures, such as nanosheets, nanowires, or nanorods. Theactive region 204 may be formed from patterning thesubstrate 202 or one or more epitaxial layers deposited over thesubstrate 202. In the depicted embodiment, theactive region 204 is formed from patterning a portion of thesubstrate 202 and includes silicon (Si). Although not explicitly shown in the figures, an isolation feature may be formed between theactive region 204 and adjacent active regions (not explicitly shown). In some embodiments, the isolation feature may include silicon oxide, silicon nitride, silicon oxynitride, fluorine-doped silicate glass (FSG), a low-k dielectric, combinations thereof, and/or other suitable materials. - As shown in
FIG. 2 , theworkpiece 200 further includes a first gate structure 206-1, a second gate structure 206-2, and a third gate structure 206-3 that are disposed overchannel regions 10 of theactive region 204. For ease of references, the first gate structure 206-1, the second gate structure 206-2, and the third gate structure 206-3 may be collectively referred to asgate structures 206. Thechannel regions 10 of theactive region 204 are interleaved by source/drain regions 20. Each of thechannel regions 10 interposes two source/drain regions 20. Thegate structures 206 wrap overchannel regions 10 of theactive region 204. When theactive region 204 includes a vertical stack of channel members, thegate structures 206 wraps around each of the channel members. While not explicitly shown in the figures, each of thegate structures 206 includes a gate dielectric layer and a gate electrode over the gate dielectric. The gate dielectric layer may include an interfacial layer and a high-k dielectric layer. In some instances, the interfacial layer may include silicon oxide. The high-k dielectric layer is formed of dielectric materials having a high dielectric constant, for example, greater than a dielectric constant of silicon oxide (k ≈ 3.9). Exemplary high-k dielectric materials for the high-k dielectric layer include hafnium oxide (HfO), titanium oxide (TiO2), hafnium zirconium oxide (HfZrO), tantalum oxide (Ta2O5), hafnium silicon oxide (HfSiO4), zirconium oxide (ZrO2), zirconium silicon oxide (ZrSiO2), lanthanum oxide (La2O3), aluminum oxide (Al2O3), zirconium oxide (ZrO), yttrium oxide (Y2O3), SrTiO3 (STO), BaTiO3 (BTO), BaZrO, hafnium lanthanum oxide (HfLaO), lanthanum silicon oxide (LaSiO), aluminum silicon oxide (AlSiO), hafnium tantalum oxide (HfTaO), hafnium titanium oxide (HfTiO), (Ba,Sr)TiO3 (BST), silicon nitride (SiN), silicon oxynitride (SiON), combinations thereof, or other suitable material. In one embodiment, the high-k dielectric layer is formed of hafnium oxide (HfO). The gate electrode may include multiple layers, such as work function layers, glue/barrier layers, and/or metal fill (or bulk) layers. A work function layer includes a conductive material tuned to have a desired work function (such as an n-type work function or a p-type work function), such as n-type work function materials and/or p-type work function materials. P-type work function materials include TiN, TaN, Ru, Mo, Al, WN, ZrSi2, MoSi2, TaSi2, NiSi2, WN, other p-type work function material, or combinations thereof. N-type work function materials include Ti, Al, Ag, Mn, Zr, TiAl, TiAlC, TaC, TaCN, TaSiN, TaAl, TaAlC, TiAlN, other n-type work function material, or combinations thereof. A glue/barrier layer can include a material that promotes adhesion between adjacent layers, such as the work function layer and the metal fill layer, and/or a material that blocks and/or reduces diffusion between gate layers, such as such as the work function layer and the metal fill layer. For example, the glue/barrier layer includes metal (for example, W, Al, Ta, Ti, Ni, Cu, Co, other suitable metal, or combinations thereof), metal oxides, metal nitrides (for example, TiN), or combinations thereof. A metal fill layer can include a suitable conductive material, such as aluminum (Al), copper (Cu), tungsten (W), ruthenium (Ru), titanium (Ti), a suitable metal, or a combination thereof. The metal fill layer may be omitted when the work function materials take up all of the gate openings. - Sidewalls of each of the
gate structures 206 are lined by agate spacer 210. Thegate spacer 210 may be a single layer or a multi-layer. In some embodiments, thegate spacer 210 may include silicon carbonitride, silicon oxycarbide, silicon oxycarbonitride, or silicon nitride. In some embodiments, a gate replacement or a gate last process may be used to form thegate structures 206. In an example gate last process, dummy gate stacks are formed overchannel regions 10 of theactive region 204. Thegate spacer 210 is then deposited over theworkpiece 200, including over sidewalls of the dummy gate stacks. An anisotropic etch process is then performed to recess the source/drain regions 20 to form source/drain trenches, leaving behind thegate spacer 210 extending along sidewalls of the dummy gate stacks. After formation of the source/drain trenches, a first source/drain feature 205-1 and a second source/drain feature 205-2 are deposited into the source/drain trenches in the source/drain regions 20. The first source/drain feature 205-1 and the second source/drain feature 205-2 may be formed vapor-phase epitaxy (VPE), ultra-high vacuum CVD (UHV-CVD), LPCVD, and/or PECVD, molecular beam epitaxy (MBE), or other suitable epitaxy processes, or combinations thereof. The source/drain features may also be referred to as epitaxial features. Depending on the design of thesemiconductor device 200, the first source/drain feature 205-1 and the second source/drain feature 205-2 may be n-type or p-type. When they are n-type, they may include silicon (Si) doped with an n-type dopant, such as phosphorus (P) or arsenic (As). When they are p-type, they may include silicon germanium (SiGe) doped with a p-type dopant, such as boron (B) or boron difluoride (BF2). In some implementations, annealing processes may be performed to activate dopants in the first source/drain feature 205-1 and the second source/drain feature 205-2. In the depicted embodiments, the first source/drain feature 205-1 and the second source/drain feature 205-2 may include phosphorus-doped silicon (Si:P) or boron-doped silicon germanium (SiGe:B). - After the formation of the source/drain features (such as the first source/drain feature 205-1 and the second source/drain feature 205-2), a contact etch stop layer (CESL) 212 and a first interlayer dielectric (ILD)
layer 214 are deposited over theworkpiece 200. In some embodiments, theCESL 212 may include silicon nitride, silicon oxynitride, and/or other materials known in the art. TheCESL 212 may be deposited using atomic layer deposition (ALD), plasma-enhanced ALD (PEALD), plasma-enhanced chemical vapor deposition (PECVD), and/or other suitable deposition processes. Thefirst ILD layer 214 may include materials such as tetraethylorthosilicate (TEOS) oxide, un-doped silicate glass, or doped silicon oxide such as borophosphosilicate glass (BPSG), fused silica glass (FSG), phosphosilicate glass (PSG), boron doped silicon glass (BSG), and/or other suitable dielectric materials. Thefirst ILD layer 214 may be deposited over theCESL 212 by CVD, flowable CVD (FCVD), spin-on coating, or other suitable deposition technique. Theworkpiece 200 is then planarized using a chemical mechanical polishing (CMP) process to expose the dummy gate stacks. The dummy gate stacks are then removed and replaced with thegate structures 206, the composition of which is described above. - The
gate structures 206 are capped by acap layer 208. In some embodiments, thecap layer 208 may include fluorine-free tungsten (FFW) that is deposited using chemical vapor deposition (CVD) or metal organic chemical vapor deposition (MOCVD). As shown inFIG. 2 , theworkpiece 200 may also include a self-aligned capping (SAC)layer 216 over thecap layer 208. In some embodiments, theSAC layer 216 may include silicon oxide, silicon nitride, silicon carbide, silicon carbonitride, silicon oxynitride, silicon oxycarbonitride, aluminum oxide, aluminum nitride, aluminum oxynitride, zirconium oxide, zirconium nitride, zirconium aluminum oxide, hafnium oxide, or a suitable dielectric material. TheSAC layer 216 may be deposited using CVD, ALD, PEALD, or a suitable method. - Referring now to
FIGS. 1 and 3 ,method 100 includes ablock 104 where a first source/drain contact 224-1 is formed to couple to the first source/drain feature 205-1 and a second source/drain contact 224-2 is formed to couple to the second source/drain feature 205-2.Block 104 includes formation of source/drain contact openings over the source/drain regions 20 through thefirst ILD layer 214 and theCESL 212 and formation of the first source/drain contact 224-1 and the second source/drain contact 224-2 in the source/drain contact openings. The formation of the source/drain contact opening may include use of lithography processes and/or etching processes. In some implementations, the lithography processes include forming a resist layer over theworkpiece 200, exposing the resist layer to pattern radiation, and developing the exposed resist layer, thereby forming a patterned resist layer. Theworkpiece 200 is then subject to a dry etch process using the patterned resist layer as a masking element to expose a portion of the first source/drain feature 205-1 and a portion of the second source/drain feature 205-2. The dry etch process atblock 104 may include use of a fluorine-containing gas (e.g., CF4, SF6, CH2F2, CHF3, and/or C2F6), a chlorine-containing gas (e.g., Cl2, CHCl3, CCl4, and/or BCl3), a hydrocarbon species (e.g. CH4), a bromine-containing gas (e.g., HBr and/or CHBr3), an iodine-containing gas, other suitable gases and/or plasmas, and/or combinations thereof. After the formation of the source/drain contact opening, asilicide layer 218 is formed in the source/drain contact openings. In some instances, thesilicide layer 218 may include titanium silicide, cobalt silicide, nickel silicide, tantalum silicide, or tungsten silicide. Thereafter, ametal fill layer 222 is deposited using a bottom-up selective CVD over thesilicide layer 218 to form the first source/drain contact 224-1 over the first source/drain feature 205-1 and the second source/drain contact 224-2 over the second source/drain feature 205-2. It is noted that, because of the use of the bottom-up selective CVD, no barrier layer is deposited before the deposition of themetal fill layer 222. Bottom-up selective CVD provides a metal-on-metal, selective deposition of metal that has a slower deposition rate of regular CVD. Themetal fill layer 222 may include ruthenium (Ru), cobalt (Co), nickel (Ni), or copper (Co). In the depicted embodiment, themetal fill layer 222 includes cobalt (Co). After the deposition of themetal fill layer 222, a chemical mechanical polishing (CMP) process may be performed to remove excess materials and define the final shape of the first source/drain contact 224-1 and the second source/drain contact 224-2. After the CMP process, a top surface of theworkpiece 200 is substantially planar. - Referring now to
FIGS. 1 and 4 , themethod 100 includes ablock 106 where a middle etch stop layer (MESL) 226 and a second interlayer dielectric (ILD)layer 228 are deposited over theworkpiece 200. Atblock 106, theMESL 226 and the second interlayer dielectric (ILD)layer 228 are sequentially deposited over theworkpiece 200. In some embodiments, the composition and formation process of theMESL 226 may be similar to those of theCESL 212 and the composition and formation process of thesecond ILD layer 228 may be similar to those of thefirst ILD layer 214. - Referring to
FIGS. 1 and 5 ,method 100 includes ablock 108 where abutted contact opening 230 is formed to expose acap layer 208 over the first gate structure 206-1 and the first source/drain contact 224-1. In an example process, a patterned photoresist layer may be formed over theworkpiece 200 to expose the area directly over the first gate structure 206-1 and the first source/drain contact 224-1. Theworkpiece 200 is then anisotropically etched using the patterned photoresist layer as an etch mask. Because the anisotropic etch atblock 108 is selective to thesecond ILD layer 228, theMESL 226, and theSAC layer 216, the end point of thebutted contact opening 230 may fall on a top surface of the first source/drain contact 224-1 and a top surface of thecap layer 208 over the first gate structure 206-1. As a result, thebutted contact opening 230 illustrated inFIG. 5 is formed. Thebutted contact opening 230 exposes not only the first source/drain contact 224-1 but also thecap layer 208 over the first gate structure 206-1. The anisotropic etch process atblock 108 may be a dry etch that uses oxygen (O2), nitrogen (N2), a fluorine-containing gas (e.g., CF4, SF6, NF3, BF3, CH2F2, CHF3, and/or C2F6), a chlorine-containing gas (e.g., Cl2, CHCl3, CCl4, and/or BCl3), a hydrocarbon species (e.g. CH4), a bromine-containing gas (e.g., HBr and/or CHBr3), an iodine-containing gas, other suitable gases and/or plasmas, and/or combinations thereof. In some embodiments, after the formation of thebutted contact opening 230, a pre-clean process may be performed to remove oxide from the first source/drain contact 224-1 and thecap layer 208. - Referring to
FIGS. 1 and 6 ,method 100 includes ablock 110 where abutted contact 232 is formed in thebutted contact opening 230. Operations atblock 110 include deposition of abarrier layer 231 and a metal fill layer into thebutted contact opening 230 and planarization of theworkpiece 200 to remove excess metal material. Atblock 110, thebarrier layer 231 may be deposited using physical vapor deposition (PVD) and a metal fill layer may be deposited over thebarrier layer 231 using chemical vapor deposition (CVD). In some embodiments, thebarrier layer 231 may include a metal nitride, such as titanium nitride (TiN) and the metal fill layer over thebarrier layer 231 may include tungsten (W). It is noted that the deposition process of thebutted contact 232 is different from the deposition of the source/drain contact. As described above, the source/drain contacts (such as the first source/drain contact 224-1) are deposited using bottom-up selective CVD and are barrier-free, while thebutted contact 232 is deposited using CVD and includes thebarrier layer 231. After the deposition of the metal material, theworkpiece 200 is planarized by, for example, a CMP process until all metal material over thesecond ILD layer 228 is removed. After the planarization, thebutted contact 232 is formed in thebutted contact opening 230. The butted contact 232 (or thebarrier layer 231 of thebutted contact 232, to be precise) is in direct contact with thesecond ILD layer 228, theMESL 226, themetal fill layer 222 of the first source/drain contact 224-1, thegate spacer 210, theSAC layer 216, and thecap layer 208 over the first gate structure 206-1. Because thecap layer 208 is electrically conductive, thebutted contact 232 that lands on the first source/drain contact 224-1 and thecap layer 208 is electrically coupled to the first source/drain contact 224-1 and the first gate structure 206-1. - Referring to
FIGS. 1 and 7 ,method 100 includes ablock 112 where athird ILD layer 234 is deposited over theworkpiece 200. Like thefirst ILD layer 214 and thesecond ILD layer 228, thethird ILD layer 234 may include materials such as tetraethylorthosilicate (TEOS) oxide, un-doped silicate glass, or doped silicon oxide such as borophosphosilicate glass (BPSG), fused silica glass (FSG), phosphosilicate glass (PSG), boron doped silicon glass (BSG), and/or other suitable dielectric materials. Thethird ILD layer 234 may be deposited over thesecond ILD layer 228 and thebutted contact 232 by CVD, flowable CVD (FCVD), spin-on coating, or other suitable deposition technique. - Referring to
FIGS. 1 and 8 ,method 100 includes ablock 114 where a source/drain contact viaopening 236 is formed to expose the second source/drain contact 224-2. The formation of the source/drain contact viaopening 236 may include photolithography processes and etch processes. The photolithography processes form an etch mask that includes an opening directly over the second source/drain contact 224-2. Referring toFIG. 8 , a dry etch process is then performed to etch completely through thethird ILD layer 234, thesecond ILD layer 228, and theMESL 226 to expose a top surface of themetal fill layer 222 of the second source/drain contact 224-2. An example dry etch process atblock 114 may include use of oxygen (O2), nitrogen (N2), hydrogen (H2), a fluorine-containing gas (e.g., CF4, SF6, NF3, BF3, CH2F2, CHF3, and/or C2F6), a chlorine-containing gas (e.g., Cl2, CHCl3, CCl4, and/or BCl3), a bromine-containing gas (e.g., HBr and/or CHBr3), an iodine-containing gas, other suitable gases and/or plasmas, and/or combinations thereof. In one embodiment, the source/drain contact viaopening 236 is etched using a nitrogen plasma, a hydrogen plasma, or both. - Referring to
FIGS. 1 and 9 ,method 100 includes ablock 116 where the second source/drain contact 224-2 is recessed. A selective wet etch process may be performed to selectively recess themetal fill layer 222 of the second source/drain contact 224-2 to extend the source/drain contact via opening 236 into the second source/drain contact 224-2. In some implementations, the selective wet etch process includes use of deionized (DI) water, nitric acid (HNO3), hydrogen peroxide (H2O2), hydrochloride (HCl), or isopropyl alcohol (IPA). In one embodiment, themetal fill layer 222 is formed of cobalt (Co) and the recess atblock 116 is performed using hydrogen peroxide (H2O2). As shown inFIG. 9 , due to the isotropic nature of the wet etch process, a top surface of themetal fill layer 222 of the second source/drain contact 224-2 becomes concave or crater-like. In some embodiments represented inFIG. 9 , after the recess, a portion of the source/drain contact viaopening 236 may undercut theMESL 226 around the second source/drain contact 224-2. The recess atblock 116 may improve adhesion and increase the interface surface area with the to-be-formed source/drain contact via 240 (to be described below). - Referring to
FIGS. 1 and 10 ,method 100 includes ablock 118 where a source/drain contact via 240 is formed in the source/drain contact viaopening 236. Operations atblock 118 may include metal deposition and surface planarization. In an example process, a metal fill layer is deposited over theworkpiece 200, including in the source/drain contact viaopening 236. In some embodiments, the metal fill layer may include tungsten (W) or ruthenium (Ru). In the depicted embodiment, the metal fill layer includes tungsten (W). In some implementation, the metal fill layer may be deposited using bottom-up selective CVD or a suitable deposition technique. After the deposition of the metal fill layer, a CMP process is performed to planarize theworkpiece 200 to remove excess materials and to form the source/drain contact via 240. As shown inFIG. 10 , the source/drain contact via 240 extends through thethird ILD layer 234, thesecond ILD layer 228, andMESL 226. Due to the recess process atblock 116, the source/drain contact via 240 partially extends into themetal fill layer 222 of the second source/drain contact 224-2 and may undercut theMESL 226 around edges of the second source/drain contact 224-2. In some embodiments represented inFIG. 10 , a top surface of the source/drain contact via 240 is higher than a top surface of thebutted contact 232 by a difference substantially equal to a thickness of thethird ILD layer 234. - Referring to
FIGS. 1 and 11 ,method 100 includes ablock 120 where a fourth dielectric layer 242 is deposited over theworkpiece 200. Like thefirst ILD layer 214 and thesecond ILD layer 228, the fourth ILD layer 242 may include materials such as tetraethylorthosilicate (TEOS) oxide, un-doped silicate glass, or doped silicon oxide such as borophosphosilicate glass (BPSG), fused silica glass (FSG), phosphosilicate glass (PSG), boron doped silicon glass (BSG), and/or other suitable dielectric materials. The fourth ILD layer 242 may be deposited over thethird ILD layer 234 and a top surface of the source/drain contact via 240 by CVD, flowable CVD (FCVD), spin-on coating, or other suitable deposition technique. - Referring to
FIGS. 1 and 12 ,method 100 includes ablock 122 where agate contact opening 244 is formed to expose thecap layer 208 on the second gate structure 206-2. Formation of thegate contact openings 244 through the fourth ILD layer 242, thethird ILD layer 234, thesecond ILD layer 228, theMESL 226, and theSAC layer 216 over the second gate structure 206-2 or the third gate structure 206-3 may include use of lithography processes and/or etching processes. The lithography processes include forming a resist layer over the fourth ILD layer 242, exposing the resist layer to pattern radiation, and developing the exposed resist layer, thereby forming a patterned resist layer. Theworkpiece 200 is then etched in a dry etch process using the patterned resist layer as an etch mask. An example dry etch process forblock 122 may include use of oxygen (O2), nitrogen (N2), hydrogen (H2), a fluorine-containing gas (e.g., CF4, SF6, NF3, BF3, CH2F2, CHF3, and/or C2F6), a chlorine-containing gas (e.g., Cl2, CHCl3, CCl4, and/or BCl3), a bromine-containing gas (e.g., HBr and/or CHBr3), an iodine-containing gas, other suitable gases and/or plasmas, and/or combinations thereof. After the dry etch process, the patterned resist layer may be removed by ashing. A wet clean process may be performed to remove debris on thecap layer 208 over the second gate structure 206-2 and the third gate structure 206-3. In some implementations, the wet clean process may include use of deionized (DI) water or isopropyl alcohol (IPA). - Referring to
FIGS. 1, 13 and 14 ,method 100 includes ablock 124 where agate contact 250 is formed in thegate contact opening 244. Thegate contact 250 may include ametal fill layer 248. Themetal fill layer 248 for thegate contact 250 may include tungsten (W) or ruthenium (Ru) and may be deposited using bottom-up selective CVD. After themetal fill layer 248 is deposited over theworkpiece 200 as shown inFIG. 13 , theworkpiece 200 is planarized in a CMP process to form thegate contacts 250 as shown inFIG. 14 . The planarization atblock 124 is performed until top surfaces of thegate contacts 250, the source/drain contact via 240, and thethird ILD layer 234 are coplanar. Top surfaces of thegate contacts 250, the source/drain contact via 240, and thethird ILD layer 234 are all higher than the top surface of thebutted contact 232 by a thickness T of thethird ILD layer 234. In some instances, the thickness T of thethird ILD layer 234 inFIG. 14 may be between about 5 nm and about 45 nm. When the thickness of thethird ILD layer 234 is greater than 45 nm, the aspect ratios of thegate contact openings 244 or the source/drain contact viaopenings 236 may be too large for satisfactory metal filling. When the thickness of thethird ILD layer 234 is smaller than 5 nm, thebutted contact 232 may not be sufficiently insulated from overlying metal lines or contact structures. - Reference is still made to
FIG. 14 . According to the present disclosure, thebutted contact 232 includes a lower portion that extends into theSAC layer 216 over the first gate structure 206-1 and an upper portion disposed above the first source/drain contact 224-1 and the lower portion. The lower portion of thebutted contact 232 is disposed between twoadjacent gate spacers 210 and is in contact with thecap layer 208 on the first gate structure 206-1. The upper portion of thebutted contact 232 is disposed in theMESL 226 and thesecond ILD layer 228. As shown inFIG. 14 , along the Z direction perpendicular to the substrate 202 (shown inFIG. 2 ), the lower portion has a first height H1 and the upper portion has a second height H2. In the depicted embodiment, the first height H1 substantially corresponds to the thickness of theSAC layer 216 and falls in a range between about 10 nm and about 25 nm. When the thickness of theSAC layer 216 is greater than 25 nm, the additional etching required to breach theSAC layer 216 may punch through the first source/drain contact 224-1 when forming thebutted contact opening 230. When the thickness of theSAC layer 216 is smaller than 10 nm, thebutted contact opening 230 may expand laterally, leading to undesirable coupling to adjacent gate contacts. The second height H2 of the upper portion substantially corresponds to the total thickness of theMESL 226 and thesecond ILD layer 228 and may be between about 30 nm and about 40 nm. When the second height H2 is smaller than 30 nm, formation of thebutted contact opening 230 may damage the first gate structure 206-1 and thecap layer 208. When the second height H2 is greater than 40, thebutted contact opening 230 may not satisfactorily expose thecap layer 208 over the first gate structure 206-1. Thebutted contact 232 has a third height H3 that is the sum of the first height H1 of the lower portion and the second height H2 of the upper portion. In some instances, the third height H3 may be between about 40 nm and 60 nm. The lower portion has a first top opening width W1 along the X direction and the upper portion has a second opening width W2 along the X direction. In some instances, the first top opening width W1 may be between about 10 nm and about 25 nm and the second top opening width W2 may be between about 14 nm and about 40 nm. When the second top opening width W2 is smaller than 14 nm, thebutted contact 232 may have a poor landing on the first source/drain contact 224-1. When the second top opening width W2 is greater than 40 nm, thebutted contact 232 may come in contact with a neighboring gate contacts, resulting in undesirable electrical connection. As a whole, thebutted contact 232 of the present disclosure has a nominal aspect ratio (i.e., the third height H3 divided by the second top opening width W2 or H3/W2) between about 0.9 and about 2. It can be seen that if a hypothetical butted contact also extends through thethird ILD layer 234 with the thickness T, its aspect ratio would be calculated as a sum of the third height H3 and the thickness T, divided by the second opening width W2. Such a hypothetical butted contact would have a nominal aspect ratio between about 1.5 and 3, which would impede satisfactory metal filling in its lower portion and may result in voids and defects. Such voids and defects may increase the contact resistance. -
FIG. 14 depicts that thebutted contact 232, the source/drain contact via 240, and thegate contacts 250 are shown along the same cross-section. In some embodiments, while the shapes, depths, and relative vertical positions may remain the same, thebutted contact 232, the source/drain contact via 240, and thegate contacts 250 may not be on the same cross section.FIG. 15 provides an example where the buttedcontacts 232, the source/drain contact vias 240, and thegate contacts 250 of asemiconductor device 200 do not necessarily appear on a cross section. Thesemiconductor device 200 inFIG. 15 includes a plurality ofgate structures 206 extending lengthwise along the Y direction, a plurality ofactive regions 204 extending lengthwise along the X direction, and a plurality of source/drain contacts 224 extending lengthwise along the Y direction. Thesemiconductor device 200 includes a plurality of buttedcontacts 232, a plurality of source/drain contact vias 240, and a plurality ofgate contacts 250. Each of the buttedcontacts 232 spans over and is electrically coupled to agate structure 206 and an adjacent source/drain contact 224. Each of the source/drain contact vias 240 is disposed directly on a source/drain contact 224. Each of thegate contacts 250 is disposed directly over and electrically coupled to agate structure 206. As shown inFIG. 15 , a cross-section that cuts across abutted contact 232 along the X direction does not cut through any of the source/drain contact vias 240 or any of thegate contacts 250. - The butted contact and methods of the present disclosure provide several benefits. For example, the butted contact opening that expose a gate structure and an adjacent source/drain contact is not as deep as the source/drain contact via opening or the gate contact opening. As such, the butted contact opening has a smaller aspect ratio that is conducive to satisfactory metal filling. The butted contact may be formed of tungsten (W) and may be deposited using a combination of PVD and CVD. The smaller aspect ratio and the two-stage metal filling improves the integrity of the butted contact and reduce contact resistance to the gate structure.
- The present disclosure provides for many different embodiments. In one embodiment, a method is provided. The method includes receiving a workpiece that includes a first gate structure including a first cap layer thereon, a first source/drain contact adjacent the first gate structure, a second gate structure including a second cap layer thereon, a second source/drain contact, an etch stop layer (ESL) over the first source/drain contact and the second source/drain contact, and a first dielectric layer over the ESL. The method further includes forming a butted contact opening to expose the first cap layer and the first source/drain contact, forming a butted contact in the butted contact opening, after the forming of the butted contact, depositing a second dielectric layer, forming a source/drain contact via opening through the second dielectric layer, the ESL layer, and the first dielectric layer to expose the second source/drain contact, and forming a source/drain contact via in the source/drain contact via opening.
- In some embodiments, the method may further include after the forming of the source/drain contact via, depositing a third dielectric layer over the source/drain contact via, forming a gate contact via opening to expose the second cap layer, and forming a gate contact via in the gate contact via opening. In some embodiments, the method may further include before the forming of the source/drain contact via, recessing the second source/drain contact. In some implementations, the recessing of the second source/drain contact includes use of hydrogen peroxide. In some instances, the first cap layer and the second cap layer include fluorine-free tungsten. In some embodiments, the first source/drain contact and the second source/drain contact include cobalt. In some embodiments, the forming of the butted contact includes depositing a barrier over the butted contact opening using physical vapor deposition (PVD) and depositing a metal fill layer over the barrier layer using chemical vapor deposition (CVD), and planarizing the deposited metal fill layer. In some embodiments, after the planarizing, a top surface of the butted contact is coplanar with a top surface of the first dielectric layer. In some implementations, the metal fill layer includes tungsten.
- In another embodiment, a method is provided. The method includes receiving a workpiece that includes a first gate structure, a first source/drain contact adjacent the first gate structure, a second gate structure, a second source/drain contact, an etch stop layer (ESL) over the first source/drain contact and the second source/drain contact, and a first dielectric layer over the ESL. The method may further include forming a butted contact to couple to the first gate structure and the first source/drain contact, depositing a second dielectric layer over the first dielectric layer and the butted contact, forming a source/drain contact via through the second dielectric layer, the first dielectric layer, and the ESL layer to couple the second source/drain contact, depositing a third dielectric layer over the source/drain contact via and the second dielectric layer, and forming a gate contact through the third dielectric layer, the second dielectric layer, the first dielectric layer, and the ESL layer to couple the second gate structure.
- In some embodiments, the method may further include after the forming of the gate contact, planarizing the workpiece until a top surface of the gate contact is coplanar with a top surface of the source/drain contact via. In some implementations, the workpiece may further include a first cap layer over the first gate structure, a second cap layer over the second gate structure, a first self-aligned capping (SAC) layer over the first cap layer, and a second SAC layer over the second cap layer. In some embodiments, a portion of the butted contact extends through the first SAC layer to land on the first cap layer. In some implementations, the gate contact extends through the second SAC layer to land on the second cap layer. In some embodiments, the forming of the butted contact includes forming a butted contact opening to expose a top surface of the first source/drain contact and the first cap layer, depositing a barrier layer over the butted contact opening using physical vapor deposition (PVD), depositing a metal fill layer over the barrier layer using chemical vapor deposition (CVD), and planarizing the deposited metal fill layer. In some embodiments, the metal fill layer includes tungsten.
- In still another embodiment, a semiconductor structure is provided. The semiconductor structure includes a first gate structure comprising a first cap layer thereon, a first source/drain contact adjacent the first gate structure, a second gate structure comprising a second cap layer thereon, a second source/drain contact, an etch stop layer (ESL) over the first source/drain contact and the second source/drain contact, a first dielectric layer over the ESL, a second dielectric layer over the first dielectric layer, a butted contact spanning over the first gate structure and the first source/drain contact, the butted contact being in contact with the first source/drain contact and the first cap layer, a source/drain contact via disposed over the second source/drain contact, and a gate contact disposed over the second cap layer. The second dielectric layer is disposed directly on a top surface of the butted contact.
- In some embodiments, the first source/drain contact and the second source/drain contact include cobalt. In some instances, the first cap layer and the second cap layer include fluorine-free tungsten. In some embodiments, the butted contact includes tungsten.
- The foregoing outlines features of several embodiments so that those skilled in the art may better understand the aspects of the present disclosure. Those skilled in the art should appreciate that they may readily use the present disclosure as a basis for designing or modifying other processes and structures for carrying out the same purposes and/or achieving the same advantages of the embodiments introduced herein. Those skilled in the art should also realize that such equivalent constructions do not depart from the spirit and scope of the present disclosure, and that they may make various changes, substitutions, and alterations herein without departing from the spirit and scope of the present disclosure.
Claims (20)
1. A semiconductor structure, comprising:
a first gate structure comprising a first cap layer thereon;
a first source/drain contact adjacent the first gate structure;
a second gate structure comprising a second cap layer thereon;
a second source/drain contact;
an etch stop layer (ESL) over the first source/drain contact and the second source/drain contact;
a first dielectric layer over the ESL;
a second dielectric layer over the first dielectric layer;
a butted contact spanning over the first gate structure and the first source/drain contact, the butted contact being in contact with the first source/drain contact and the first cap layer;
a source/drain contact via disposed over the second source/drain contact; and
a gate contact disposed over the second cap layer,
wherein the second dielectric layer is disposed directly on a top surface of the butted contact.
2. The semiconductor structure of claim 1 , wherein the first source/drain contact and the second source/drain contact comprise cobalt and are free of a barrier layer.
3. The semiconductor structure of claim 1 , wherein the first cap layer and the second cap layer comprise fluorine-free tungsten.
4. The semiconductor structure of claim 1 , wherein the butted contact comprises tungsten.
5. The semiconductor structure of claim 1 , wherein a top surface of the butted contact and a top surface of the first dielectric layer are coplanar.
6. The semiconductor structure of claim 1 , further comprising:
a dielectric capping layer disposed over the first cap layer.
7. The semiconductor structure of claim 6 , further comprising:
a first gate spacer and a second gate spacer sandwiching the first gate structure, the first cap layer, and the dielectric capping layer.
8. The semiconductor structure of claim 7 , wherein the butted contact comprises:
an upper portion disposed in the ESL and the first dielectric layer; and
a lower portion extending downward from the upper portion through the dielectric capping layer,
wherein a bottom surface of the upper portion lands on a top surface of the first gate spacer and a top surface of the first source/drain contact,
wherein a bottom surface of the lower portion lands on the first cap layer.
9. The semiconductor structure of claim 1 , wherein a portion of the source/drain contact via extends into the second source/drain contact and undercuts the ESL.
10. A semiconductor structure, comprising:
a first active region and a second active region aligned lengthwise along a first direction and spaced apart from one another;
a first gate segment extending lengthwise along a second direction perpendicular to the first direction and wrapping over a channel region of the first active region;
a second gate segment extending lengthwise along the second direction and wrapping over a channel region of the second active region;
a first source/drain contact extending lengthwise along the second direction over a source/drain region of the first active region;
a second source/drain contact extending lengthwise along the second direction over a source/drain region of the second active region;
a first butted contact including a first lower portion in contact with the first gate segment and a first upper portion spanning over and contacting the first source/drain contact; and
a second butted contact including a second lower portion in contact with the second gate segment and a second upper portion spanning over and contacting the second source/drain contact.
11. The semiconductor structure of claim 10 ,
wherein the first active region comprises a first fin structure,
wherein the second active region comprises a second fin structure.
12. The semiconductor structure of claim 10 ,
wherein the first active region comprises a first vertical stack of nanostructures,
wherein the second active region comprises a second vertical stack of nanostructures.
13. The semiconductor structure of claim 10 , further comprising:
a third active region extending lengthwise along the first direction;
a third gate segment extending lengthwise along the second direction and wrapping over a first channel region of the third active region;
a fourth gate segment extending lengthwise along the second direction and wrapping over a second channel region of the third active region; and
a third source/drain contact extending lengthwise along the second direction and disposed between the third gate segment and the fourth gate segment,
wherein the third gate segment and the first gate segment are aligned along the second direction,
wherein the fourth gate segment and the second gate segment are aligned along the second direction.
14. The semiconductor structure of claim 13 , further comprising:
an etch stop layer (ESL) disposed over a top surface of the third source/drain contact; and
a source/drain contact via extending through the ESL to contact the third source/drain contact.
15. The semiconductor structure of claim 14 , wherein a portion of the source/drain contact via extends into the third source/drain contact and undercuts the ESL.
16. A structure, comprising:
an active region extending lengthwise along a first direction and comprising a source/drain region and a channel region adjacent the source/drain region;
a source/drain feature disposed over the source/drain region;
a first gate structure disposed over the channel region;
a metal cap layer over the first gate structure;
a dielectric capping layer over the metal cap layer;
a first gate spacer disposed along and in contact with sidewalls of the first gate structure, the metal cap layer and the dielectric capping layer;
a contact etch stop layer (CESL) disposed along and in contact with the first gate spacer and a top surface of the source/drain feature;
a first interlayer dielectric layer (ILD) over the CESL;
a source/drain contact extending through the first ILD and the CESL to contact the source/drain feature by way of a silicide feature;
an etch stop layer (ESL) disposed over a top surface of the CESL, a top surface of the first ILD layer, and a top surface of the dielectric capping layer;
a second ILD layer over the ESL; and
a local interconnect structure comprising:
a lower portion extending through the dielectric capping layer to contact the metal cap layer, and
an upper portion over the lower portion and a top surface of the source/drain contact,
wherein a top surface of the upper portion is coplanar with a top surface of the second ILD layer.
17. The structure of claim 16 , wherein the metal cap layer comprises tungsten.
18. The structure of claim 16 , wherein the dielectric capping layer comprises silicon oxide, silicon nitride, silicon carbide, silicon carbonitride, silicon oxynitride, silicon oxycarbonitride, aluminum oxide, aluminum nitride, aluminum oxynitride, zirconium oxide, zirconium nitride, zirconium aluminum oxide, or hafnium oxide.
19. The structure of claim 16 , wherein the local interconnect structure comprises:
a barrier layer; and
a metal fill layer over the barrier layer,
wherein the metal fill layer is spaced apart from the second ILD, the ESL, the first gate spacer, and the dielectric capping layer by the barrier layer.
20. The structure of claim 19 ,
wherein the barrier layer comprises titanium nitride,
wherein the metal fill layer comprises tungsten.