US20230257445A9 - Preparation Method for Collagen Hydrogel - Google Patents

Preparation Method for Collagen Hydrogel Download PDF

Info

Publication number
US20230257445A9
US20230257445A9 US17/169,631 US202117169631A US2023257445A9 US 20230257445 A9 US20230257445 A9 US 20230257445A9 US 202117169631 A US202117169631 A US 202117169631A US 2023257445 A9 US2023257445 A9 US 2023257445A9
Authority
US
United States
Prior art keywords
collagen
coli
helix
hydrogel
seq
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
US17/169,631
Other versions
US11780905B2 (en
US20210163576A1 (en
Inventor
Fei Xu
Jinyuan HU
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangnan University
Original Assignee
Jiangnan University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangnan University filed Critical Jiangnan University
Assigned to JIANGNAN UNIVERSITY reassignment JIANGNAN UNIVERSITY ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: HU, JINYUAN, XU, FEI
Publication of US20210163576A1 publication Critical patent/US20210163576A1/en
Publication of US20230257445A9 publication Critical patent/US20230257445A9/en
Application granted granted Critical
Publication of US11780905B2 publication Critical patent/US11780905B2/en
Active legal-status Critical Current
Adjusted expiration legal-status Critical

Abstract

Disclosed is a preparation method for collagen hydrogel and belongs to the technical field of gene engineering. On the basis of E3 and K3 heterologous α-helices at an N end and a C end, a continuous Gly-Xaa-Yaa triplet collagen sequence is inserted therebetween to form a three-segment chimeric collagen E3-collagen-K3 mode. Self-assembly is driven by the interaction of the E3 and K3 heterologous α-helices at the N end and the C end to form the end-to-end reticulated porous collagen hydrogel. The method of the disclosure can prepare collagen with a clean source, the collagen hydrogel can be formed by self-assembly of the collagen, the preparation process is simple, and the collagen hydrogel can be produced on a large scale at low cost and has a wide application prospect in the field of biological materials.

Description

    TECHNICAL FIELD
  • The disclosure herein relates to a preparation method for collagen hydrogel, and belongs to the technical field of gene engineering.
    • BACKGROUND
  • Collagen, a triple helix formed by intertwining three chains, is the most abundant protein in mammals and accounts for ⅓ of human proteins, and can be highly specifically assembled to form collagen fibers, and as the main component of an extracellular matrix, it can control the growth and differentiation of cells, and can be used for repairing and regenerating human tissues and organs. Collagen hydrogel is a biodegradable water-rich three-dimensional material that can provide biological signals and serve as a cell scaffold to provide a microenvironment required for cell growth, differentiation and migration, and can be used as an articular cartilage filler.
  • Currently, there are mainly five sources of collagen as follows. At present, the most important source is animal skin extraction, the price is low, but it tends to carry disease sources. Chemically synthesized polypeptide has high controllability and purity, the most obvious disadvantages are that the price is high, the length is limited, and it is not suitable for batch production. Expression via eukaryotic systems such as transgenic plants and mammalian cells has the advantages that correct folding of proteins can be guided and complex post-translational processing functions are provided, but the common problems are high culture cost, long period, low expression amount and difficulty in large-scale production. A microbial expression system has obvious advantages of low cost, high expression amount and the appearance. Recent studies have shown that more and more mammal and bacterial collagen has been proved to be efficiently and heterologously expressed in hosts such as bacteria and yeast, and correctly folded into collagen triple helices. Recombinant collagen has potential applications in the production of biomaterials, but it lacks the driving force of self-assembly to form higher structures and fails to form a higher structure, which limits its applications in biomaterials and tissue engineering. Barbara Brodsky and Magnus Hook et al. have demonstrated that modified collagen can serve as a substrate for fibroblasts, endothelial cells and smooth muscle cells by heterologous expression of collagen Scl2 with integrin action sites inserted in Streptococcus pyogenes in E. coli [1,2]. Molly M. Stevens et al. have studied that by inserting hyaluronic acid and chondroitin sulfate binding sites in an Scl2 sequence, followed by cross-linking using metal matrix hydrolase 7 (MMP7) sensitive peptides, biodegradable hydrogel is formed, which is expected to be useful in the regeneration of articular cartilage[3].
  • 1. An, B., et al., The influence of specific binding of collagen-silk chimeras to silk biomaterials on hMSC behavior. Biomaterials, 2013. 34(2): p. 402-412.
  • 2. Seo, N., et al., An engineered α1 integrin-binding collagenous sequence. Journal of Biological Chemistry, 2010. 285(40): p. 31046-31054.
  • 3. Cosgriff-Hernandez, E., et al., Bioactive hydrogels based on Designer Collagens. Acta Biomaterialia, 2010. 6(10): p. 3969-3977.
    • SUMMARY
  • According to the present disclosure, high-aggregation self-assembly of collagen is promoted to form collagen hydrogel by fusing and expressing E3 and K3 heterologous α-helices at an N end and a C end of the collagen.
  • The present disclosure provides a collagen molecule, and a peptide chain forming the collagen molecule has the following structure:
  • (a) an E3 α helix, a V-domain, a plurality of repeated GXYs and a K3 α helix contained in sequence; and
  • (b) a protein derived from (a) by deleting, substituting, increasing or decreasing one or more amino acids of CL-domain on the basis of (a), and having functional properties of (a).
  • In one implementation, the peptide chain forming the collagen molecule has the following structure:
  • (a)
  • Figure US20230257445A9-20230817-C00001
  • where an amino acid sequence includes: an E3 α helical structure, a V-domain, a collagen region with repeated amino acid units (GXYs), and a K3 α helical structure in sequence; an amino acid sequence of the V-domain is set forth as SEQ ID NO:1; an amino acid sequence of the E3 α helical structure is EISALEKEISALEKEISALEK; an amino acid sequence of the K3 α helical structure is KISALKEKISALKEKISALKE; the (GXY)m is the collagen region, and m is an integer≥2; and an amino acid sequence of the (GXY)m includes, but is not limited to, the sequence set forth as SEQ ID NO:4, or a repeated sequence including a plurality of sequences set forth as SEQ ID NO:4; and
  • (b) a protein derived from (a) by deleting, substituting, increasing or decreasing one or more amino acids of the collagen region on the basis of (a), and having functional properties of (a).
  • In one implementation, 6×His tags are further fused in front of the E3 α helix.
  • In one implementation, the E3 α helix and the K3 α helix are respectively fused and linked with the collagen region through flexible linker peptide; and the flexible linker peptide includes, but is not limited to, glycine.
  • The present disclosure further provides collagen hydrogel formed by self-assembly of trimeric collagen molecules.
  • The present disclosure further provides a gene encoding the collagen molecule or encoding a peptide chain of the collagen molecule.
  • In one implementation, the gene includes a nucleotide sequence set forth as any one of SEQ ID NOS:9-12.
  • The present disclosure further provides a plasmid or cell carrying a gene.
  • In one implementation, the plasmid includes, but is not limited to: pColdIII plasmids and pET plasmids.
  • In one implementation, the plasmid is pColdIII.
  • In one implementation, the cell is an E. coli cell, including, but not limited to, E. coli BL21, E. coli BL21(DE3), E. coli JM109, E. coli DH5α, or E. coli TOP10.
  • The present disclosure further provides a preparation method for type I collagen hydrogel, and the method includes the following steps:
  • (1) synthesizing a gene encoding a chimeric α-helical collagen peptide chain;
  • (2) linking the gene synthesized in step (1) with a vector, and transforming the gene into a target cell for expression and purification; and
  • (3) dialyzing a collagen solution obtained in step (2) at 0˜4° C.
  • In one implementation, the preparation method includes the following steps:
  • (1) constructing collagen recombinant plasmids: synthesizing genes VB, E3-VB-K3, E3-VBB-K3 and E3-VBBB—K3 encoding collagen set forth as SEQ ID NOS:9-12 respectively, and constructing the genes on plasmids pColdIII-Tu respectively, where the pColdIII-Tu is obtained by mutating plasmids pColdIII to introduce an Nco I site by taking
  • pCOLD-TU(Nco I)-S:
    CTCGAGGGATCCGAATTCA (set forth as SEQ ID NO: 13)
    and
    pCOLD-TU(Nco I)-A:
    GAGCTCCATGGGCACTTTG (set forth as SEQ ID NO: 14)
    as primers;
  • (2) transforming: transforming the recombinant plasmids into E. coli BL21(DE3) respectively;
  • (3) inducing expression: culturing a single colony in an LB liquid culture medium overnight, then transferring into a TB liquid culture medium at an inoculation amount of 1%, culturing for 24 h at 37° C., adding IPTG, inducing for 10 h at 25° C., and inducing for 14 h at 15° C.;
  • (4) purifying: collecting fermented bacteria, resuspending the bacteria by using a phosphate buffer solution, crushing cells by using an ultrasonic cell crusher under an ice bath condition, centrifuging at 10,000 rpm for 20 min at 4° C. to remove cell fragments, and filtering a supernatant by using a microporous filter membrane to remove impurities; injecting a sample into a His-trap hp affinity chromatography column (5 mL) mounted on a protein purifier, then flushing by eight column volumes with a washing solution, increasing imidazole content in an elution buffer solution stepwise (140 mM, 164 mM and 400 mM) to elute proteins, and collecting appearance proteins at a 400 mM imidazole concentration; and
  • (5) dialyzing a collagen solution obtained in step (4) by using ultrapure water or a 10 mM phosphate buffer solution at 4° C.
  • In one implementation, the dialysis is to dialyze collagen with a molecular weight cut-off greater than or equal to 7 kDa.
  • The present disclosure further provides application of collagen in preparation of hydrogel.
  • In one implementation, the application is to condition the collagen for dialysis in water or a phosphate buffer solution such that after a concentration is greater than or equal to 10 mg/mL, the hydrogel is formed after standing for 3 days at 4° C.
  • The present disclosure further provides a method for controlling a swelling property or a mechanical property of hydrogel. The method is configured to control the number of amino acids of (GXY)m in collagen molecules expressed by microbial cells, where m is 27, 54 and 81, corresponding to a region B in Streptococcus pyogenes collagen Scl1, double-length B and triple-length B respectively, and then the hydrogel is prepared from the collagen molecules produced by microbial fermentation.
  • The collagen, the gene, the plasmid, the cell or the preparation method provided by the present disclosure can be applied to the fields of biology, chemical industry, food, medicine, biological materials, tissue engineering, cosmetics and the like.
  • Beneficial effects: 1. On the basis of N-end and C-end heterologous α helix E3 and K3 sequences, a continuous Gly-Xaa-Yaa triplet collagen sequence is inserted therebetween to form a three-segment chimeric collagen E3 α-helix-V-collagen-K3 α-helix with α helices at the N end and the C end respectively. Self-assembly is driven by interaction of E3 and K3 heterologous α helices at the N end and the C end to form the collagen hydrogel.
  • 2. According to the present disclosure, the collagen sequence involved in the present disclosure is expressed by E. coli cold shock to prepare the collagen hydrogel which can be self-assembled from a clean source, the preparation process is simple, and the collagen hydrogel can be produced on a large scale at low cost. The preparation method and a sequence design mode thereof are provided for preparing the collagen hydrogel, a collagen region of the sequence can be replaced and expanded, a platform is provided for research and application based on the collagen hydrogel, and the collagen hydrogel has a wide prospect in biomaterial application.
  • 3. The present disclosure also regulates a gel property and water content of the hydrogel by adjusting a sequence length of the collagen region. The mechanical property and water content of the collagen hydrogel can be controlled by controlling the collagen region to be of 27, 54 and 81 Gly-Xaa-Yaa triplets.
    • BRIEF DESCRIPTION OF FIGURES
  • FIG. 1A is a pattern diagram of a three-segment chimeric sequence E3-collagen-K3, the lengths of collagen regions of the three sequences being of 27, 54 and 79 GXY triplets respectively which correspond to single-length, double-length and triple-length collagen Scl2-B sequences;
  • FIG. 1B is a double-enzyme digestion verification diagram of a recombinant plasmid;
  • FIG. 1C is purified collagen SDS-PAGE.
  • FIG. 2A is MALDI-TOF molecular weight identification of designed collagen VB;
  • FIG. 2B is MALDI-TOF molecular weight identification of designed collagen E3-VB-K3;
  • FIG. 2C is MALDI-TOF molecular weight identification of designed collagen E3-VBB-K3;
  • FIG. 2D is MALDI-TOF molecular weight identification of designed collagen E3-VBBB-K3;
  • FIG. 3A is circular dichroism spectrum full-wavelength scanning spectrum of designed collagen;
  • FIG. 3B is a circular dichroism spectrum thermal change curve of designed collagen.
  • FIG. 4A is differential scanning calorimetry (DSC) measurement of designed collagen VB at low (L) and high (H) concentrations;
  • FIG. 4B is differential scanning calorimetry (DSC) measurement of designed collagen E3-VB-K3 at low (L) and high (H) concentrations;
  • FIG. 4C is differential scanning calorimetry (DSC) measurement of designed collagen E3-VBB-K3 at low (L) and high (H) concentrations;
  • FIG. 4D is differential scanning calorimetry (DSC) measurement of designed collagen E3-VBBB-K3 at low (L) and high (H) concentrations.
  • FIG. 5A is a hydration particle size of VB self-assembled polymer at different times as determined by dynamic light scattering;
  • FIG. 5B is a hydration particle size of E3-VB-K3 self-assembled polymer at different times as determined by dynamic light scattering;
  • FIG. 5C is a hydration particle size of E3-VBB-K3 self-assembled polymer at different times as determined by dynamic light scattering;
  • FIG. 5D is a hydration particle size of E3-VBBB-K3 self-assembled polymer at different times as determined by dynamic light scattering;
  • FIG. 6A is a scanning electron micrograph of collagen hydrogel and a hydrogel image for E3-VB-K3;
  • FIG. 6B is a scanning electron micrograph of collagen hydrogel and a hydrogel image for E3-VBB-K3;
  • FIG. 6C is a scanning electron micrograph of collagen hydrogel and a hydrogel image for E3-VBBB-K3;
    •  DETAILED DESCRIPTION
  • Materials and methods used in the present disclosure are as follows.
  • 1) Culture media:
  • LB solid culture medium: 15 g/L agar, 10 g/L tryptone, 5 g/L yeast extract powder, and 10 g/L NaCl, where pH is 7.0.
  • LB liquid culture medium: 10 g/L tryptone, 5 g/L yeast extract powder, 10 g/L of NaCl, where pH is 7.0.
  • TB liquid culture medium: 12 g/L tryptone, 24 g yeast extract powder, 4 mL glycerol, 2.31 g KH2PO4, and 12.54 g K2HPO4, where pH is 7.5, and a volume is set to 1 L.
  • 2) A bacteria culture method:
  • E. Coli seed culture conditions: single colonies grown by plate streaking are inoculated into the LB liquid culture medium, a liquid loading amount is 10%, a 250 mL shake flask is adopted for culture, a culture temperature is 37° C., a culture time is 10 h, and a rotation speed is 200 rpm.
  • Fermentation culture conditions of a pET28a recombinant strain: the TB culture medium is adopted, a liquid loading amount of the culture medium is 20%, an inoculation amount is 1%, a 500 mL shake flask is adopted for culture, a culture temperature is 25° C., when OD600 reaches 2.5 h, IPTG with a final concentration of 1 mM is adopted for induction, an induction temperature is 35° C., an induction time is 24 h, and a rotation speed is 200 rpm.
  • Fermentation culture conditions of a pCold recombinant strain: the TB culture medium is adopted, a liquid loading amount of the culture medium is 20%, an inoculation amount is 1%, a 500 mL shake flask is adopted for culture, IPTG with a final concentration of 1 mM is adopted for induction after the strain is cultured for 24 h at 37° C., induction is performed for 10 h at 25° C. and then performed for 14 h at 15° C., and a rotation speed is 200 rpm.
    • Embodiment 1 Sequence Design and Sample Preparation
  • Designing is performed according to a structure shown by E3-V-(GXY)m-K3, where E3 α-helix represents EISALEKEISALEKEISALEK, V-domain represents a globular domain guiding the correct folding of a collagen region, (GXY)m represents the collagen region capable of being designed and changed, and K3 α-helix represents KISALKEKISALKEKISALKE; and the specific steps are as follows.
  • (1) The E3 α-helix at an N end and the K3 α-helix at a C end are used as fixed sequence motifs, and the variable collagen region and the globular V-domain guiding the correct folding of the collagen region are inserted between the E3 α-helix and the K3 α-helix at the C end to obtain a three-segment chimeric sequence, abbreviated as E3-Vcollagen-K3 as shown in FIG. 1A. Collagen Scl2 (Genbank ID: AAL50184.1) from Streptococcus pyogenes is used as bacterial collagen in a collagen regional sequence in the present embodiment, and an Scl2 collagen region is divided into three equal-length regions A, B and C. In the present embodiment, designed CL domains are B, BB (two repeated B regions) and BBB (three repeated B regions) respectively.
  • (2) The globular V-domain (set forth as SEQ ID NO:1) derived from Scl2 is inserted at the N end of the collagen sequence and used for guiding the correct folding of a collagen triple helix, an integrin binding site is inserted between the collagen sequences for realizing a biological function, and 6×His is inserted at the N end of the entire sequence for purification.
  • An amino acid sequence is designed as follows:
  • VB (containing 6xHis tags):
    HHHHHHADEQEEKAKVRTELIQELAQGLGGIEKKNFPTLGDEDLDHTYMT
    KLLTYLQEREQAENSWRKRLLKGIQDHALDPGPRGEQGPQGLPGKDGEAG
    AQGPAGPMGPAGFPGERGEKGEPGTQGAKGDRGETGPVGPRGERGEAGPA
    GKDGERGPVGPAG;
    E3-VB-K3 (containing 6xHis tags):
    HHHHHHGEISALEKEISALEKEISALEKGGGGGGGADEQEEKAKVRTELI
    QELAQGLGGIEKKNFPTLGDEDLDHTYMTKLLTYLQEREQAENSWRKRLL
    KGIQDHALDPGPRGEQGPQGLPGKDGEAGAQGPAGPMGPAGFPGERGEKG
    EPGTQGAKGDRGETGPVGPRGERGEAGPAGKDGERGPVGPAGGGGGGGGK
    ISALKEKISALKEKISALKE;
    E3-VBB-K3 (containing 6xHis tags):
    HHHHHHGEISALEKEISALEKEISALEKGGGGGGGADEQEEKAKVRTELI
    QELAQGLGGIEKKNFPTLGDEDLDHTYMTKLLTYLQEREQAENSWRKRLL
    KGIQDHALDPGPRGEQGPQGLPGKDGEAGAQGPAGPMGPAGFPGERGEKG
    EPGTQGAKGDRGETGPVGPRGERGEAGPAGKDGERGPVGPAGPRGEQGPQ
    GLPGKDGEAGAQGPAGPMGPAGFPGERGEKGEPGTQGAKGDRGETGPVGP
    RGERGEAGPAGKDGERGPVGPAGGGGGGGGKISALKEKISALKEKISALK
    E;
    E3-VBBB-K3 (containing 6xHis tags):
    HHHHHHGEISALEKEISALEKEISALEKGGGGGGGADEQEEKAKVRTELI
    QELAQGLGGIEKKNFPTLGDEDLDHTYMTKLLTYLQEREQAENSWRKRLL
    KGIQDHALDPGPRGEQGPQGLPGKDGEAGAQGPAGPMGPAGFPGERGEKG
    EPGTQGAKGDRGETGPVGPRGERGEAGPAGKDGERGPVGPAGPRGEQGPQ
    GLPGKDGEAGAQGPAGPMGPAGFPGERGEKGEPGTQGAKGDRGETGPVGP
    RGERGEAGPAGKDGERGPVGPAGPRGEQGPQGLPGKDGEAGAQGPAGPMG
    PAGFPGERGEKGEPGTQGAKGDRGETGPVGPRGERGEAGPAGKDGERGPV
    GPAGGGGGGGGKISALKEKISALKEKISALKE;
  • Genes encoding the above amino acid sequence are synthesized. A nucleotide sequence encoding VB is set forth as SEQ ID NO:9; a gene sequence encoding E3-VB-K3 is set forth as SEQ ID NO:10; a gene sequence encoding E3-VBB-K3 is set forth as SEQ ID NO:11; a gene sequence encoding E3-VBBB-K3 is set forth as SEQ ID NO:12; and the nucleotide sequences shown above each contain a 5′ Nco I digestion site, a 5′ flanking sequence GC, and a 3′ Bam HI digestion site respectively. The synthesized genes are respectively inserted between NcoI and BamHI of pCOLD III-Tu plasmids to obtain corresponding recombinant collagen plasmids, then the recombinant plasmids are respectively transformed into E. coli BL21(DE3) competent cells by a CaCl2 method, an LB plate containing antibiotics is coated, culturing and screening are performed, and a recombinant strain for preparing hybrid collagen is obtained; and the plasmids pCOLD III-Tu are obtained by mutating plasmids pColdIII to introduce the Nco I site by taking pCOLD-TU(Nco I)-S: CTCGAGGGATCCGAATTCA (set forth as SEQ ID NO:13) and pCOLD-TU(Nco I)-A: GAGCTCCATGGGCACTTTG (set forth as SEQ ID NO:14) as primers.
  • After recombinant strains are respectively induced to be fermented, a fermentation broth is centrifuged at 8,000 rpm for 5 min, and fermented bacteria are collected. The bacteria are resuspended in a phosphate buffer solution, cells are crushed by an ultrasonic cell crusher under an ice bath condition and centrifuged at 10,000 rpm for 20 min at 4° C. to remove cell fragments, and a supernatant is filtered through a microporous filter membrane (0.45 μm) to remove impurities. A sample is injected into a 5 mL His-trap hp affinity chromatography column mounted on a protein purifier, then 8 column volumes are flushed with a washing solution, imidazole content in an elution buffer solution is increased stepwise (140 mM and 400 mM) to elute proteins, and appearance proteins are collected and subjected to SDS-PAGE electrophoresis analysis. Desalting is then performed through a desalting column, freeze drying is performed, a small amount of lyophilized powder is taken and dissolved in water, and SDS-PAGE and Maldi-tof are adopted for identification. FIG. 1C shows that single bands are detected in all the purified proteins by SDS-PAGE, and since collagen is a rod-like protein and a protein Marker is a globular molecule, a molecular weight shown by SDS-PAGE is larger than an expected molecular weight position. As shown in FIGS. 2(A)-(D), a molecular weight obtained by mass spectrometry is consistent with a theoretical molecular weight, and collagen with a correct molecular weight is obtained.
    • Embodiment 2 Secondary Structure Determination of Collagen
  • The collagen prepared in Embodiment 1 is formulated to a concentration of 1 mg/mL respectively. Then the collagen is subjected to standing for 24 h or more at 4° C., and circular dichroism spectrum full-wavelength scanning is performed in a 1 mm cuvette at 4° C. with a wavelength from 190 nm to 260 nm, and a wavelength interval of 1 nm, and the scanning remains for 5 s at each wavelength. A thermal change experiment measures at 220 nm at a temperature ranging from 4° C. to 80° C., equilibration is performed at each temperature for 8 s, and a temperature increasing rate is 1° C./6 min. A typical collagen triple helix CD spectrum shows a positive absorption peak at 220 nm, a variable globular domain used for guiding folding is rich in α-helix, and there are characteristic negative absorption peaks at 208 nm and 222 nm.
  • As shown in FIG. 3A and FIG. 3B, under full-wavelength scanning, the designed protein of Embodiment 1 shows superposition absorption signals of the α-helices and a collagen triple helix, and has the characteristic absorption peaks around 220 nm; the results of the thermal change experiment show that with the increase of temperature, a characteristic absorption value at 220 nm is changed sharply at 30-40° C., which is manifested as destroyed secondary structure of the collagen. That is, the triple helix is uncoiled. The results of the CD full spectrum and the thermal change experiment show that the three-segment chimeric collagen designed in Embodiment 1 can be correctly folded to form a collagen triple helix structure, and has high thermal stability.
    • Embodiment 3 Detection of Intermolecular Interaction by a Differential Scanning Calorimetry
  • Collagen E3-VB-K3, E3-VBB-K3 and E3-VBBB-K3 purifying solutions prepared in Embodiment 1 are dialyzed by 10 mM PB in a dialysis bag with a molecular weight cut-off of 7 kDa. In the process of dialysis, collagen molecules are continuously aggregated to form a precipitate, the precipitate is collected and prepared into a 10 mg/mL solution, VB cannot be aggregated to form a precipitate in the process of dialysis, and the VB prepared by freeze drying is prepared into a solution with the same concentration. A concentration of a sample with a low concentration is 1.5 mg/mL. Then the sample stands for 24 h or more at 4° C., a thermal change temperature is measured by a differential scanning calorimetry, a temperature scan range is 0-100° C., and a temperature increasing rate is 1° C./min. As shown in FIG. 4A˜4D, only a thermal change temperature of a triple helix of the VB is detected as 30.34° C. at the low concentration, and similar to the CD results. At a high concentration, a thermal change peak of 45.16° C. is also detected and is a thermal change temperature of a globular domain, which proves that a collagen region and a guided folding domain are both correctly folded and the structure is stable. Only thermal change temperatures of triple helix regions are detected in E3-VB-K3, E3-VBB-K3 and E3-VBBB-K3 at the low concentration, which proves that collagen regions are folded correctly to form stable triple helices. At the high concentration, in addition to the thermal change temperature at which the triple helix is uncoiled, a gradual transition temperature can be detected, which may be due to the heterogeneity of molecule interaction of E3 and K3.
    • Embodiment 4 Self-Assembly of Collagen
  • Collagen VB, E3-VB-K3, E3-VBB-K3 and E3-VBBB-K3 solutions are prepared according to the method of Embodiment 1, a buffer solution is replaced with 10 mM PB by using a HiTrap desalting column, the solution stands in a 4° C. refrigerator and is sampled every 12 h for measuring a hydration particle size thereof by dynamic light scattering. The process of self-assembly is observed, and the results show that, as in FIG. 5A˜5D, a VB particle size does not change along with time, and particle sizes of E3-VB-K3, E3-VBB-K3 and E3-VBBB-K3 are gradually increased along with the time, which indicates that small molecules of collagen are continuously self-assembled and aggregated into large particles along with the time, where the particle size of the E3-VB-K3 after being self-assembled for 24-48 h can reach 4,883 nm; and the results of the aggregation process also show that a proportion of large particles becomes larger along with the time. The particle size of the E3-VBB-K3 after being self-assembled for 24-48 h can reach 5,560 nm; and the particle size of the E3-VBBB-K3 after being self-assembled for 24-48 h can reach 5,560 nm.
    • Embodiment 5 Internal Structure and Mechanical Property of Hydrogel
  • Collagen E3-VB-K3, E3-VBB-K3 and E3-VBBB-K3 purifying solutions prepared in Embodiment 1 are respectively dialyzed by 10 mM PB in a dialysis bag with a molecular weight cut-off of 7 kDa to obtain collagen hydrogel E3-VB-K3, E3-VBB-K3 and E3-VBBB-K3. As shown in FIG. 5A˜5D, after a protein concentration is higher than 10 mg/mL, E3-VB-K3, E3-VBB-K3, and E3-VBBB-K3 are translucent hydrogel, and samples do not flow in an inverted transparent centrifuge tube to form the collagen hydrogel. After a small amount of hydrogel is taken and frozen by liquid nitrogen, the samples are freeze-dried in a freeze-dryer, and the internal structure of the collagen hydrogel is observed by a scanning electron microscope after gold is sprayed on cross sections. As shown in FIG. 6A˜6C, the hydrogel samples of E3-VB-K3, E3-VBB-K3 and E3-VBBB-K3 all appear as loose porous collagen sponge, which can provide a good three-dimensional microenvironment for growth and differentiation of cells. The mechanical and rheological properties of hydrogel are tested. At a low concentration (<5 mg/mL), both E3-VB-K3 and E3-VBB-K3 are both liquid, and a storage modulus G′ is less than a loss modulus G″; E3-VBBB-K3 reaches a gel point at a concentration of 5 mg/mL and at an angular frequency of 0.25 rad/s, and then appears as soft hydrogel when G′ is greater than G′; and compared with the E3-VB-K3 and the E3-VBB-K3, by lengthening a collagen region, the solid content of the obtained hydrogel can be reduced. At a high concentration (>16 mg/mL), the E3-VB-K3, the E3-VBB-K3 and the E3-VBBB-K3 all appear as the hydrogel. For the E3-VBBB-K3, a saturation concentration thereof is 11.6 mg/mL, showing better water content, and for the E3-VB-K3, by increasing the concentration of the hydrogel, solid gel (as shown in FIG. 6A˜6C) showing low water content and high mechanical strength can be prepared.

Claims (11)

What is claimed is:
1. A collagen molecule, comprising:
a protein chain (a) having an E3 α helix, a V-domain, a plurality of repeated amino acids GXY and a K3 α helix in sequence from an N end to a C end; or
a protein chain (b) derived from the protein chain (a) by deleting, substituting, increasing or decreasing one or more amino acids of CL-domain on the basis of the protein chain (a), and the protein chain (b) has functional properties of the protein chain (a);
wherein the V-domain has an amino acid sequence set forth as SEQ ID NO:1;
the E3 α helix has one or more amino acid sequences set forth as SEQ ID NO:2; and
the K3 α helix has one or more amino acid sequences set forth as SEQ ID NO:3.
2. The collagen molecule according to claim 1, wherein the protein chain (a) or (b) of the collagen molecule has an amino acid sequence set forth as any one of SEQ ID NOS:5-8.
3. The collagen molecule according to claim 2, further comprising 6×His tags fused in front of the E3 α helix.
4. The collagen molecule according to claim 3, wherein the E3 α helix and the K3 α helix are separately fused and linked with a collagen region through flexible linker peptide; and the flexible linker peptide comprises glycine.
5. A method for preparing type I collagen-like hydrogel, comprising the following steps:
(1) synthesizing a gene encoding a chimeric α-helical collagen peptide chain;
(2) linking the gene synthesized in step (1) with a vector, and transforming the gene into a target cell for expression and purification; and
(3) dialyzing a collagen solution obtained in step (2) at 0-4° C.
6. The method according to claim 5, wherein a nucleotide sequence of the gene is set forth as any one of SEQ ID NOS:9-12.
7. The method according to claim 5, wherein the vector is pColdIII plasmids or pET plasmids.
8. The method according to claim 5, wherein the target cell is an Escherichia coli (E. coli) cell, comprising E. coli BL21, E. coli BL21(DE3), E. coli JM109, E. coli DH5a, or E. coli TOP10.
9. The method according to claim 5, wherein the vector is pColdIII; and the target cell is E. coli BL21(DE3).
10. The method according to claim 5, wherein collagen is conditioned for dialysis in water or a phosphate buffer solution to obtain an aggregate, and after a concentration is greater than or equal to 10 mg/mL, the hydrogel is formed after standing for at least 3 days at 4° C.
11. The method according to claim 5, further comprising:
(1) synthesizing genes encoding collagen set forth as SEQ ID NOS:9-12, respectively, and constructing the genes on plasmids pColdIII-Tu, respectively;
(2) transforming: transforming recombinant plasmids into E. coli BL21(DE3), respectively;
(3) inducing expression: culturing a single colony in a liquid culture medium and inducting expression of a protein by using IPTG;
(4) purifying: collecting fermented bacteria, crushing cells, centrifuging to remove cell fragments and filtering a supernatant to remove impurities; and performing chromatography on samples with impurities removed, and eluting and collecting a target protein; and
(5) dialyzing a collagen solution obtained in step (4) by using ultrapure water or a phosphate buffer solution.
US17/169,631 2020-06-29 2021-02-08 Preparation method for collagen hydrogel Active 2041-06-25 US11780905B2 (en)