US20210348324A1 - Method of making polyester fabric treated with a cbd powder - Google Patents

Method of making polyester fabric treated with a cbd powder Download PDF

Info

Publication number
US20210348324A1
US20210348324A1 US16/660,911 US201916660911A US2021348324A1 US 20210348324 A1 US20210348324 A1 US 20210348324A1 US 201916660911 A US201916660911 A US 201916660911A US 2021348324 A1 US2021348324 A1 US 2021348324A1
Authority
US
United States
Prior art keywords
cbd
water
polyester fabric
powder
treating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
US16/660,911
Other versions
US11186944B1 (en
Inventor
Jesse Salem
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sam Salem And Son LLC
Original Assignee
Sam Salem And Son LLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sam Salem And Son LLC filed Critical Sam Salem And Son LLC
Priority to US16/660,911 priority Critical patent/US11186944B1/en
Publication of US20210348324A1 publication Critical patent/US20210348324A1/en
Application granted granted Critical
Publication of US11186944B1 publication Critical patent/US11186944B1/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

This invention relates to a method for making polyester fabric treated with a CBD powder to provide a novel CBD finish on the polyester fabric. The polyester fabric is treated with a CBD powder to provide a novel finish. The treatment process includes a washing step, wherein the treating CBD water is added to a water channel before the finishing step. Then, the polyester fabric is passed through the water channel having the treating CBD water in the ratio of 1:1000, which is one gram of CBD powder to each 1000 grams of water. The flow rate of the treating CBD water has a ratio of 5:1000, which adds 5 grams of CBD powder to each 1000 grams of water in order to apply the correct treatment of CBD water. In addition, the polyester fabric moves at a speed of approximately 20 meters per minute through the water channel, and the bathing treatment has a normal temperature of 30-35° C. The maximum temperature of the drying machine is 220° C., but has a preferred range of 170-220° C. In addition, the polyester fabric passes through the drying machine at a speed of 20 meters per minute.

Description

    FIELD OF THE INVENTION
  • This invention relates to a method for making polyester fabric treated with a CBD powder.
    • BACKGROUND OF THE INVENTION
  • This invention relates to a method for making polyester fabric treated with a CBD powder. Polyester fabric is a commonly used fabric. However, in the present invention, a novel treatment method is used to treat the polyester fabric with CBD powder.
    • DESCRIPTION OF THE PRIOR ART
  • Japanese Pat. No. JPH02289136 (A) to Ueno Kenichi entitled “Cotton-Bast Fiber Blended Yarn and Production Thereof” issued on Nov. 29, 1990. The '136 Japanese patent, discloses a blended yarn suitable as a raw material for clothing such as shirts by passing each specified fineness of hemp fiber and cotton fiber from a raw state through a mixing and blowing, a card and a comber to remove a specified amount of short fiber followed by passing through a roving frame and a fine spinning frame into yarn. Preferably the hemp fiber is 3.0-7.0 denier in fineness and the cotton fiber is <=1.8 denier in fineness are passed from their raw state through a mixing and blowing, a card, and a comber to remove 10-20 wt. % of short fiber followed by passing through a roving frame and a fine spinning frame into yarn, thus obtaining the objective blended yarn comprising (A) hemp fiber 28-42 mm in average fiber length and 3.0-7.0 denier in fineness and (B) cotton fiber 28-42 mm in average fiber length and <=1.8 denier in fineness, with the hemp fiber accounting 10-60 wt. % of the entire yarn.
  • Abandoned U.S. Patent App. Pub. No. 2009/0173054 to Scott H. Silver entitled “Composite Cotton and Hemp Yarn and Method for Making the Same” was published on Jul. 9, 2009 and is now abandoned. The '054 patent application discloses a composite hemp and cotton yarn formed by blending hemp fibers with cotton fibers which have been regenerated from waste cotton material such as trimmings and cuttings from the apparel manufacturing industry. The fibers are cleaned and blended, then carded to align the fibers into strands. Depending on the size and texture of the desired yarn, the fibers are stretched and drawn into slivers prior to spinning to join the fibers together. The hemp fibers are up to three time longer than the regenerated cotton fibers, so that the hemp fibers overlap and braid onto the regenerated cotton fibers during spinning. The resultant yarn is stronger and more absorbent than yarns made solely out of regenerated cotton fibers or a blend of cotton and acrylic or cotton and polyester fibers. The finished yarn is between 30 and 45% recycled and regenerated cotton fibers which are generally shorter than the natural hemp fibers.
    • OBJECTS OF THE INVENTION
  • It is an object of the present invention to provide a novel method of treating polyester fabric with a CBD powder.
  • It is another object of the present invention to potentially provide a better rest.
  • It is another object of the present invention to potentially relieve anxiety.
    • SUMMARY OF THE INVENTION
  • This invention relates to a method for making polyester fabric treated with a CBD powder to provide a novel CBD finish on the polyester fabric. The polyester fabric is treated with a CBD powder to provide a novel finish. The treatment process includes a washing step, wherein the treating CBD water is added to a water channel before the finishing step. Then, the polyester fabric is passed through the water channel having the treating CBD water in the ratio of 1:1000, which is one gram of CBD powder to each 1000 grains of water. The flow rate of the treating CBD water has a ratio of 5:1000, which adds 5 grains of CBD powder to each 1000 grams of water in order to apply the correct treatment of CBD water. In addition, the polyester fabric moves at a speed of approximately 20 meters per minute through the water channel, and the bathing treatment has a normal temperature of 30-35° C. The maximum temperature of the drying machine is 220° C., but has a preferred range of 170-220° C. In addition, the polyester fabric passes through the drying machine at a speed of 20 meters per minute.
    • DETAILED DESCRIPTION OF THE EMBODIMENTS
  • This invention relates to a method for making polyester fabric treated with a CBD powder. The present invention relates to making and treating a polyester fabric treated with a CBD powder to obtain a CBD finish on the polyester fabric using a novel CBD treatment process.
  • The treatment process includes the following steps for treating the polyester fabric. The first step includes singeing the fabric, desizing it, washing it, and bleaching it. Then the polyester fabric may have a white finish, or it is mercerized and then color dyed.
  • After that, the polyester fabric is then finished with CBD powder at 160° C. Then, the CBD treated polyester fabric is sanforized.
  • The CBD treatment process of the present invention is further described in the 3 embodiments set forth below.
    • First Embodiment
  • In this first embodiment, during the washing step, the treating CBD water is added to the water channel before the finishing step. The polyester fabric is passed through the water channel having the treating CBD water in the ratio of 1:1000, which is 1 gram of CBD powder to each 1000 grams of water. Also, the flow rate of the treating CBD water has a ratio of 5:1000, which adds 5 grams of CBD powder to each 1000 grams of water in order to apply the correct treatment of CBD water.
  • In addition, the polyester fabric moves at a speed of approximately 20 meters per minute through the water channel, and the bathing treatment has a normal temperature of 30-35° C.
    • Second Embodiment
  • When the polyester fabric passes through the roller, the temperature setting is 30-35° C.
    • Third Embodiment
  • The process starts with the machine temperature having a setting of 140° C. Also, the maximum temperature of the drying machine is 220° C., and has a preferred range of 170-220° C. The polyester fabric passes through the drying machine in approximately 2 minutes and the drying machine is running at a speed of 20 meters per minute.
  • In this manner, the CBD powder is added to the polyester fabric in the most efficient manner.
  • For all of the embodiments, it is noted that even though the CBD powder dissolves in the water, the treated polyester fabric can be washed only 10 times. After that, the CBD powder does not stay in the fabric.
    • Operation of the Invention
  • This invention relates to a polyester fabric having treated with CBD powder, and a method for making same. The invention includes treating a polyester fabric with a CBD powder to provide a CBD finish using a CBD treatment process. The polyester fabric is treated with a CBD powder at 160° C. The treatment process includes a washing step, wherein the treating CBD water is added to a water channel before the finishing step. Then, the polyester fabric is passed through the water channel having the treating CBD water in the ratio of 1:1000, which is one gram of CBD powder to each 1000 grams of water. The flow rate of the treating CBD water has a ratio of 5:1000, which adds 5 grams of CBD powder to each 1000 grams of water in order to apply the correct treatment of CBD water. In addition, the polyester fabric moves at a speed of approximately 20 meters per minute through the water channel, and the bathing treatment has a normal temperature of 30-35° C. The maximum temperature of the drying machine is 220° C., but has a preferred range of 170-220° C. In addition, the polyester fabric passes through the drying machine at a speed of 20 meters per minute.
    • ADVANTAGES OF THE PRESENT INVENTION
  • It is an advantage of the present invention to provide a novel method of treating polyester fabric with a CBD powder.
  • Another advantage of the present invention is to potentially provide a better rest.
  • Another advantage of the present invention is to potentially relieve anxiety.
  • A latitude of modification, change and substitution is intended in the foregoing disclosure, and in some instances, some features of the invention will be employed without a corresponding use of other features. Accordingly, it is appropriate that the appended claims be construed broadly and in a manner consistent with the spirit and scope of the invention herein.

Claims (1)

What is claimed is:
1) This invention relates to a method for making polyester fabric treated with a CBD powder:
a) said polyester fabric is treated with said CBD powder to provide a CBD finish using a CBD treatment process;
b) said polyester fabric is treated with said CBD powder at 160° C.;
c) said treatment process includes a washing step, wherein the treating CBD water is added to a water channel before a finishing step;
d) said polyester fabric is then passed through said water channel having the treating CBD water in the ratio of 1:1000, which is one gram of CBD powder to each 1000 grams of water;
e) the flow rate of the treating CBD water through said water channel has a ratio of 5:1000, which adds 5 grams of CBD powder to each 1000 grams of water in order to apply the correct treatment of CBD water;
f) said polyester fabric moves at a speed of approximately 20 meters per minute through said water channel;
g) the bathing treatment has a normal temperature of 30-35° C.;
h) the maximum temperature of the drying step is 220° C., and has a preferred range of 170-220° C.; and
i) said polyester fabric passes through the drying step at a speed of 20 meters per minute, in order to complete said treatment process.
US16/660,911 2019-10-23 2019-10-23 Method of making polyester fabric treated with a CBD powder Active US11186944B1 (en)