US20200318283A1 - Metal nanoparticle enhanced semiconductor film for functionalized textiles - Google Patents
Metal nanoparticle enhanced semiconductor film for functionalized textiles Download PDFInfo
- Publication number
- US20200318283A1 US20200318283A1 US16/843,789 US202016843789A US2020318283A1 US 20200318283 A1 US20200318283 A1 US 20200318283A1 US 202016843789 A US202016843789 A US 202016843789A US 2020318283 A1 US2020318283 A1 US 2020318283A1
- Authority
- US
- United States
- Prior art keywords
- coated
- tio
- nanoparticles
- textile
- metallic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
- The present application claims priority to U.S. Ser. No. 62/830,953, filed Apr. 8, 2019, and to U.S. Ser. No. 16/818,751, filed Mar. 13, 2020, the contents of which are specifically incorporated herein by reference.
- This invention was made with government support under D01_W911SR-14-2-0001-0003 awarded by the Department of Defense. The government has certain rights in the invention.
- This invention relates to the field of surface coatings and methods for providing a surface coating to a material, as a method of treating a material, for example a textile material, such that at least one surface of the material comprises a nanostructured coating, is provided. The invention also relates to the field of nanostructured coatings that are self-cleaning, anti-microbial (anti-bacterial, anti-viral), and radiation-protective. The invention further relates to the field of semiconducting metal oxide thin film coatings, as a semiconducting metal oxide thin film coating comprising metallic nanoparticle incorporated to a semiconducting film is provided, the film providing an active photocatalyst layer imparting the above characteristics to a surface having the film provided thereon. The invention also relates to the field of methods for providing a thin film to a surface, as a method for generating a thin, homogenous, nanostructured film of titanium dioxide on a cellulosic substrate, and generating noble metal nanoparticles (silver and gold) directly on the titanium oxide surface to provide a treated surface, is presented. The treated surface enhances photocatalytic activity at the surface, and renders the treated surface self-cleaning and antimicrobial. A surface treated with a titanium dioxide coating process alone does not possess these characteristics. The invention also relates to methods of treating materials and surfaces of other natural or synthetic substrates, other semiconductor-based thin films, and the use and incorporation of other noble/common metallic nanoparticles.
- Conventional fabric treatment methods aim to provide stain resistance, extend the lifetime of the textile material, or provide anti-microbial action through the use of chemicals that seal and protect the fabric, or through treatment methods that leave the fabric innately resistant to stains. Treatment methods that rely on semiconducting materials being deposited on a textile typically rely on complicated methods ill-suited to scaling to industrial scale, and also typically yield a textile material that is impregnated by and/or decorated with discrete semiconductor nanotubes or nanoparticles, which both have the disadvantage of being more readily removed from the fabric and less photocatalytically active than a thin, uniform film. Sol-gel based treatment techniques are one of the developed procedures for depositing a surface photocatalytic coating on textile materials.
- Medical and disaster associated protective gear, including masks, garments, hospital draping materials, and the like, remain at best of limited protective effectivity, especially in regards virus and virus related pathologies. Research in this area reports that particles having a size of 0.04 to 0.2 μm can penetrate commonly used surgical (medical) and personal use masks. The particle size of the coronavirus responsible for SARS has been estimated to be within the range of 0.08 to 0.14 μm. Therefore, conventional surgical masks and personal use masks are not effective for blocking the penetration of the coronavirus. Assuming that SARS-CoV-2 has a similar size, currently available surgical masks are unlikely to effectively filter this virus. The size and concentrations of SARS-CoV-2 in aerosols generated during coughing remain unknown.
- When noting greater contamination on the outside versus the inside of the mask, investigators have speculated the contamination may be due to the aerodynamic features of the mask, or the small aerosols of SARS-CoV-2 generated during a high-velocity cough.
- While these and other findings reinforce the importance of hand hygiene after touching the outside of masks, it also highlights the grave deficiencies in current, widely used public health protective devices, including face masks, in shielding the user and the public at large from virus exposure and spread. More effective materials are needed in the medical arts to create personal protective devices, such as masks and protective garments, to control and/or reduce the spread of viral diseases.
- While some improvements have been made in the development of advanced textile materials with a photocatalytic film or layer, current methods and techniques remain ill-suited for large scale production, and fail to provide more than limited self-cleaning, anti-microbial, anti-viral and/or radiation-protective properties. Accordingly, a need continues to exist in the medical arts for improved textiles and fiber materials amenable to large scale production, and that preferably are self-cleaning, anti-microbial, anti-viral and possess radiation-protective properties.
- The present invention provides a solution to the various problems and limitations in the medical arts. The method and system disclosed herein provides for the generation of a nanostructured photocatalytic system on at least one surface of a textile material, for example a cotton textile material, using an elegant and scalable method. The techniques described herein provide for the construction of a nanostructured photocatalytic system on a surface using a sol-gel based synthetic method. A semiconducting thin film (e.g., a thickness of about 1 mM) is thereby deposited on the surface of the textile (e.g., a fabric), and thereby facilitates photocatalytic chemical reactions to occur on the surface, beneficially providing for the absorption of UV light. In this manner, penetration of materials may be prevented by UV radiation. Noble metal nanoparticles are directly grown on the semiconducting thin film surface by using a solution-based coating method, followed by irradiation with UV light. This method holds several advantages over alternative metal particle incorporation techniques, as this method reduces and/or prevents the formation of noble metal precursors. The initial deposited semiconducting layer at the surface acts to reduce the noble metal precursors, and serves to permit the direct growth of nanostructured gold nanoparticles and/or nanostructured silver nanoparticles directly on the semiconducting thin film surface. This semiconducting thin film surface may be advantageously provided onto the surface of any variety of natural fiber materials, such as natural cotton fibers. In turn, these treated functionalized fibers provide for fabrication of functionalized textile materials, that may be used in the production of any variety of products, including personal protective equipment.
- The noble metal nanoparticles are variably sized, which allows for the absorption (and thus the photochemical utilization) of a range of incident radiation that wouldn't be absorbed by the semiconducting oxide layer alone. These nanoparticles are also capable as acting as electron acceptors for the photo-generated electrons from the oxide surface, which absorbs incident high-energy UV radiation. The nanoparticles thus help to reduce charge recombination and also generate additional excitons from the absorption of incident light at a longer wavelength than that absorbed by the semiconducting material. The tandem semiconducting oxide layer/nanoparticle system exhibits more efficient photocatalytic performance than other methods, and the synthetic techniques used in this invention are facile and scalable.
- According to one embodiment of the present invention, a method is provided for the deposition of a thin, uniform semiconducting film, and subsequent decoration of said film with noble metal nanoparticles grown directly on the semiconducting film surface.
- According to one embodiment of the present invention, this method provides a means for the large-scale facile manufacture of textile materials with said coating, which lends the finished materials self-cleaning, antimicrobial, antiviral and UV-protective properties.
- According to one embodiment of the present invention, a method is provided for the direct reduction of gold chloride and silver nitrate (gold and silver nanoparticle precursors) on the semiconducting surface under intense UV radiation during the manufacturing process, thus enabling the direct growth of the nanoparticles on the oxide surface and improving manufacturing time compared to the utilization of various chemical reducing agents and/or the separate growth of the nanoparticles and subsequent deposition onto the semiconductor-coated fabric, which would further complicate manufacture.
- According to one embodiment of the present invention, a method is provided for coating all fibrous/non-fibrous textile materials with a semiconducting layer and nanoparticles to lend them anti-microbial, self-cleaning, and radiation-protective properties.
- The present invention advances the art of treating textile materials with the aim of obtaining a textile material that has self-cleaning, anti-microbial, or radiation protective properties, and, in addition, provides an improved method for the application of the coating in a scalable manufacturing process.
- Other aspects and advantages of the present invention will be apparent from the following detailed description of the preferred embodiments of the accompanying drawing figures.
- A clear understanding of the methodology employed and results obtained by this novel treatment technique can be had by referencing the appended drawings which illustrate the method and results of the innovative treatment technique, although it will be understood that such drawings depict preferred embodiments of the invention and, therefore, are not to be considered as limiting its scope with regard to other embodiments which the invention is capable of contemplating.
- Accordingly, in the accompanying drawing, which forms a part of the specification and is to be read in conjunction therewith in which like reference numerals are used to indicate like or similar parts in the various views:
-
FIG. 1 is a schematic representation of a methodology used to construct a metallic nanoparticle semiconducting film-coated textile material in accordance with one embodiment of the present invention; -
FIG. 2 is a schematic representation of a methodology used to deposit the semiconducting film onto a textile material in accordance with one embodiment of the present invention; -
FIG. 3 is an SEM image showing an uncoated pristine fiber material at low and high magnification (a, b) and a TiO2 coated fiber material at low and high magnification (c, d) in accordance with one embodiment of the present invention; -
FIG. 4A is a schematic representation of a methodology used to deposit and/or grow metallic nanoparticles directly on the surface of fiber material having a semiconducting layer coated thereon in accordance with one embodiment of the present invention; -
FIG. 4B is a schematic representation of a methodology used to deposit and/or grow metallic nanoparticles directly on the surface of fiber material having a semiconducting layer coated thereon in accordance with another embodiment of the present invention; -
FIG. 5 is a SEM image showing an Ag—TiO2 coated fiber material at low and high magnification (e, f) and an Au—TiO2 coated fiber material a low and high magnification (g, h) in accordance with one embodiment of the present invention; -
FIG. 6 is a graph containing the ultraviolet and visible absorption spectra of an uncoated pristine fiber material, a TiO2 coated fiber material, an Ag—TiO2 coated fiber material, and an Au—TiO2 coated fiber material in accordance with one embodiment of the present invention; -
FIG. 7 is a graph showing XRD spectra for (a) pre-exposure Ag—TiO2 coated fiber material, (b) pre-exposure Au—TiO2 coated fiber material, (c) pre-exposure TiO2 coated fiber material, (d) pre-exposure pristine uncoated fiber material, and (e) post-exposure TiO2 coated fiber material in accordance with one embodiment of the present invention; -
FIG. 8 is a graph showing the ultraviolet and visible absorption spectra of (a) Ag—TiO2 coated fiber material, (b) Au—TiO2 coated fiber material, (c) TiO2 coated fiber material, and (d) pristine uncoated fiber material, after staining with methylene blue dye and exposure to simulated solar light (1.5 sun intensity) over a measured interval of time to quantify the self-cleaning efficacy in accordance with one embodiment of the present invention; -
FIG. 9 is a graph showing the rate of stain extinction of (a) Ag—TiO2 coated fiber material, (b) Au—TiO2 coated fiber material, (c) TiO2 coated fiber material, and (d) pristine uncoated fiber material, after staining with methylene blue dye and exposure to simulated solar light (1.5 sun intensity) over a measured interval of time in accordance with one embodiment of the present invention; -
FIG. 10 is a graph showing the C/CO data for a Ag—TiO2 coated fiber material over repeated cycles of staining and UV exposure in accordance with one embodiment of the present invention; -
FIG. 11 is a graph of the FTIR spectra for Au—TiO2 coated fiber material after repeated exposure to simulated solar light for exposure times of (a) no exposure, (b) two hours, (c) four hours, (d) six hours, and (e) ten hours in accordance with one embodiment of the present invention; -
FIG. 12 is an image of a Kirby-Baur disk diffusion test for antimicrobial activity with (a) Au—TiO2 coated fiber material, (b) Ag—TiO2 coated fiber material, and (c) pristine uncoated fiber material in accordance with one embodiment of the present invention; and -
FIG. 13 is a schematic representation of the antimicrobial activity of Au—TiO2 coated fiber material before and after light exposure in accordance with one embodiment of the present invention. - The invention will now be described with reference to the drawing figures, in which like reference numerals refer to like parts throughout. For purposes of clarity in illustrating the characteristics of the present invention, proportional relationships of the elements have not necessarily been maintained in the drawing figures.
- The following detailed description of the invention references specific embodiments in which the invention can be practiced. The embodiments are intended to describe aspects of the invention in sufficient detail to enable those skilled in the art to practice the invention. Other embodiments can be utilized and changes can be made without departing from the scope of the present invention. The present invention is defined by the appended claims and the description is, therefore, not to be taken in a limiting sense and shall not limit the scope of equivalents to which such claims are entitled.
- The present invention is directed to noble metal particles, such as gold and/or silver, titanium dioxide coated fibers or
textile materials 10.Such fibers 10 of the present invention have been shown to have substantial benefits, including being self-cleaning, anti-microbial, and protective against UV radiation. The present invention is also directed to amethod 100 for constructing metallic nanoparticle and semiconductor layer textile materials. According to one embodiment,method 100 includes procedures for depositing and/or growing gold/silver nanoparticles onto a nanostructured titanium dioxide (TiO2) film applied to a textile material or fiber surface. As described in greater detail herein, themethod 100 of the present invention can be utilized to apply a uniform and high surface area film of TiO2 onto a cotton fiber or other textile material, and subsequently directly incorporate gold/silver nanoparticles on the nanostructured TiO2 surface of the fiber/textile material. Themethod 100 described herein can produce a TiO2 film that is substantially homogenous with uniformly distributed Au/Ag nanoparticles on the TiO2 film distributed using photocatalytic reduction method. - According to one embodiment the Ag—TiO2 coated
textile material 10 of the present invention was observed to have the largest improvement in rate of stain extinction compared to the untreated fibers with a methylene blue stain. According to one embodiment, the Au and/or Ag—TiO2 coatedtextile material 10 of the present invention were observed to have the largest improvement versus untreated fibers when stained with Congo red. The Ag/Au—TiO2 coatedtextile material 10 can maintain consistent photocatalytic activity over multiple cycles and have resistance to degradation, which was verified using Fourier transform infrared spectroscopy (FTIR). The Ag/Au—TiO2 coatedtextile material 10 are also configured for efficient anti-microbial activity, which was confirmed by exposure of the fibers to bacterial culture (Escherichia Coli) and direct observation of antimicrobial activity. - As described herein, the present invention is directed to a
method 100 for depositing and/or growing nanostructured gold and silver nanoparticles on the surface of natural fibers (i.e., textile materials) that have been coated with TiO2. The TiO2 coating can be applied utilizing a sol-gel based method that uniformly coats the fiber material; however, other methods can also be suitably be used. TiO2 is a well-known photo-catalyst that has been extensively tested and shown to effectively decompose a wide range of organic substances under irradiation with solar light, including methylene blue, isothiazolin-3-ones, formaldehyde, acid orange, phenol, coffee/wine stains, and even the chemical warfare agent Soman. The innate photocatalytic effectiveness of TiO2 is very high, even under artificial room lighting a layer of TiO2 possesses sufficient photocatalytic activity to completely mineralize an approximately 1 μm thick hydrocarbon layer every hour, and therefore can be suitable for a surface photocatalytic coating to produce self-cleaning fibers and textile materials. - The gold and silver nanoparticles can be applied via direct reduction of AuCl3 and/or AgNO3 by UV radiation as described herein. Ag/Au—TiO2 coated
fibers 10 created throughmethod 100 of the present invention have demonstrated self-cleansing and anti-microbial properties. Silver nanoparticles have been shown to have antibacterial activity and have been shown to reduce the incidence of electron/hole recombination when used in conjunction with TiO2, which should improve photocatalytic activity. Gold nanoparticles have been shown to decrease the bandgap of TiO2 which improves overall photocatalytic activity and allows for the photocatalytic destruction of certain organic under visible-only/UV filtered lighting conditions where a TiO2 coating alone is ineffective. As described herein,method 100 of the present invention is directed to procedures for successfully depositing and growing gold and silver nanoparticles onto a TiO2 coating layer that coats the surface of a textile or fiber material. - Referring to
FIG. 1 ,method 100 according to one embodiment of the present invention is illustrated schematically. As shown,method 100 begins with aninitial step 200 that includes providing a fiber/textile material and coating the textile material with a TiO2 coating. As further shown inFIG. 1 ,method 100 includes asubsequent step 300 that includes depositing gold and/or silver nanoparticles onto the surface of the TiO2 fiber/textile material.Method 100 andsteps method 100 for providing an Au/Ag—TiO2 coatedfiber material 10 will now be described in greater detail with reference to the several figures. - Referring to
FIG. 2 ,step 200 and the methodology for coating the fiber or textile material (referred to herein as a fiber material for simplicity) with a thin film of titanium dioxide via a sol-gel method can take place in several steps as described below. Atstep 202, the fiber material can be washed and cleaned. According to one embodiment the fiber material atstep 202 can be thoroughly cleaned via washing with acetone at an elevated temperature for a suitable period of time (e.g., hours) to remove any impurities that may be present (such as natural fats). In other embodiments, any suitable cleaning method can also be utilized. Next, atstep 204, the fiber can be dried. According to one embodiment, the drying process ofstep 204 can include drying the fiber material at room temperature or other suitable temperature for a suitable period of time (for example, 12 hours). - Next, at step 206, a TiO2 nanosol coating solution can be prepared for coating the fiber material. The coating solution can include the preparation of two solutions: solution A and solution B. As shown by
step 206A, solution A can be prepared by combining approximately 2% by volume acetic acid and 12% by volume titanium isopropoxide in approximately 86% by volume 2-propanol and mix vigorously for approximately 30 minutes as represented bystep 206C. According to one embodiment, solution A can comprise 50 mL of 2-propanol, 1 mL of acetic acid, and 5.91 mL of titanium isopropoxide; however, it is recognized that other percentage-by-volume amounts can suitably be used. As shown bystep 206B, solution B can be prepared by combining approximately 6% by volume of concentrated hydrochloric acid and approximately 1.5% ultrapure water in approximately 92.5% of 2-propanol and mix vigorously for approximately 30 minutes as represented bystep 206C. According to one embodiment, solution B can comprise 50 mL of 2-propanol, 3 mL concentrated hydrochloric acid, and 0.72 mL of ultrapure water; however, it is recognized that other percentage-by-volume amounts can suitably be used. - Next, at
step 208, solutions A and B can be mixed together and combined. According to one embodiment,step 208 includes the procedure of slowly adding solution B into solution A while under vigorous stirring (e.g., 400-800 rpm) solution A until the solutions A and B are thoroughly combined to form the nanosol coating solution. - Next, at
step 210, the fiber material can be immersed in the nanosol coating solution for approximately 30 seconds and removed. Depending on the particular application ofmethod 100, the prepared nanosol coating solution can continued to be used for as long as 7 days before it loses its integrity and precipitating out TiO2 and becoming qualitatively opaque instead of transparent. The ability to reuse the prepared nanosol coating solution for an extended period of time and provide cost and efficiency benefits for large-scale productions of Au/Ag—TiO2 coatedfiber material 10. - Next, at
step 212, the fiber material can be dried. According to one embodiment, the drying process atstep 212 can include drying the fiber material for approximately 24 hours at room temperature under normal atmospheric conditions. - Next, at step 214, the fiber material can be calcined in order to remove any residual solvent. According to one embodiment, as shown in
FIG. 2 , step 214 can include a sub-step 214A where the fiber material is calcined at approximately 65° C. for approximately 10 minutes and a sub-step 214B where the fiber material is calcined at approximately 90-95° C. for approximately 5 minutes under normal atmospheric conditions. - Next, at
step 216, the calcined fiber material can be hydrothermally treated to remove excess oxide left behind from the nanosol coating process. According to one embodiment, the process atstep 216 can include boiling the fiber material in ultrapure water for a period of approximately 3 hours. -
FIG. 3 illustrates the effect of the TiO2 coating process described instep 200.FIGS. 3(a) and 3(b) provide SEM images at low and high magnification, respectively of a cotton fiber material that was not treated with the TiO2 coating ofstep 200.FIGS. 3(c) and 3(d) provide SEM images at low and high magnification, respectively, of a TiO2 coated cotton fiber material that was treated with the TiO2 coating ofstep 200. The differences between (a) and (b) ofFIG. 3 and (c) and (d) demonstrate how the coating process ofstep 200 creates a thin, essentially uniform coating on the surface of the fiber material, and that the coating process ofstep 200 results in quality adhesion of the coating to the surface of the fiber material without significant cracking or other surface deformities. The coating process ofstep 200 can also result in a coating that is thin enough so as to allow for flexing of the fiber material without the coating cracking or becoming separated from the fiber material surface. - Referring to
FIGS. 4A and 4B , step 300 of themethod 100 for constructing Ag/Au—TiO2 coatedfibers 10 is described in greater detail. As schematically illustrated inFIG. 4A and described below, step 300 can include several steps for depositing/growing gold and/or silver nanoparticles on the surface of the TiO2 coated fiber material. Step 300 can begin atstep 302 where a metallic nanoparticle precursor solution is prepared. According to one embodiment, the precursor is prepared by diluting a solution of gold chloride (AuCl3) with ultrapure water to create a 100 mL precursor solution of 1 mM AuCl3. According to another embodiment, the precursor is prepared by diluting a solution of silver nitrate (AgNO3) in ultrapure water to create a 100 mL precursor solution of 1 mM AgNO3. In other embodiments, greater or lesser concentrations of gold chloride or silver nitrate can suitably be used to for the precursor solution. - Next, at
step 304, the TiO2 coated fiber material can be immersed in the precursor solution for a suitable period of time and then removed. According to one embodiment, the preferred time period is approximately 30 seconds. - Next, at
step 306, the metallic nanoparticle-TiO2 coated fiber material (i.e., AuCL3—TiO2 coated fiber material or AgNO3—TiO2 coated fiber material) can be allowed to dry for a suitable period of time. According to one embodiment, duringstep 306, the coated fiber material is left to dry at room temperature under normal atmospheric conditions for approximately 24 hours (however, other temperatures, conditions and time periods can also be suitably used during step 306). - Next, at
step 308, the metallic precursor solution-TiO2 coated fiber material is exposed to - UV radiation for a suitable period of time as shown in
FIG. 4A . According to one embodiment, the AuCL3 or AgNO3—TiO2 coated fiber material is exposed to approximately 254 nm UV radiation for approximately 30 minutes. According to one embodiment, the UV radiation is applied for approximately 15 minutes on each side of the coated fiber material as shown inFIG. 4B . Other suitable time periods for UV radiation exposure can also be suitable used in alternative embodiments. Step 308 can act to photocatalytically reduce the metallic nanoparticle precursors deposited via a solvent-based method, and can essentially activate the photocatalytic surface. The semiconducting oxide material (TiO2) is most photocatalytically active and/or capable of reducing the metallic nanoparticle precursors when irradiated with UV light, so intense UV light can be preferable used for initial creation of the nanoparticles. -
FIG. 5 illustrates the effect of the metallic nanoparticle application process described instep 300 where metallic nanoparticles (e.g., Au or Ag nanoparticles) are deposited and/or grown the TiO2 coated surface of the fiber material. As shown inFIGS. 3(a) and (b) and described above, the fiber material includes natural surface folds , which increase the exposed surface area of the fiber material and can improve photocatalytic efficiency by providing more sites for photoreactions to take place and for the anchoring of nanoparticles. As shown inFIGS. 3(c) and (d), the application of the TiO2 coating on the surface of the fiber material results in a slight reduction in the fold definition. Subsequently, as illustrated inFIGS. 5(e)-(h) , after the TiO2-coated fiber material is immersed in the metallic nanoparticle precursor solution, removed, dried and exposed to UV radiation through steps 302-308, the growth of metallic nanoparticles gold and silver nanoparticles on the TiO2 coated fiber materials is visible on the SEM images ofFIGS. 5 .FIGS. 5(e) and (f) show Ag—TiO2 coatedfiber material 10 at low and high magnification, respectively, whileFIGS. 5(g) and (h) show Au—TiO2 coatedfiber material 10 at low and high magnification, respectively. - Referring to
FIG. 6 , the UV-Visible absorption spectra of Ag/Au—TiO2 coatedfiber materials 10 prepared following the steps ofmethod 100 outlined above is shown, and the clear offset of the gold and silver nanoparticle coated fiber material is visible. As shown inFIG. 6 , the relatively wide absorption peaks of the gold and silver nanoparticle peaks is due to the range of nanoparticle sizes generated by the reduction method used above. Peak width and peak offset can be both important for the photocatalytic efficacy of the textile coating. It is apparent that the absorption contribution of the nanoparticles allows the semiconducting layer to absorb incident near-UV/visible photons which enhance the photocatalytic efficiency. -
FIG. 6 illustrates the development of Au and Ag nanoparticles under UV radiation where the Ag/Au—TiO2 coatedfiber materials 10 were formed using 5 mM precursor solutions of AgNO3 and AuCl3. The gold peak in the embodiment illustrated inFIG. 6 is at 547 nm, which matches what would be expected if the gold nanoparticles took on roughly spherical shapes and have an average size of 60-80 nm (calculated utilizing available data concerning nanoparticle size and max wavelength of UV—vis absorption). Further, the width of the peak indicates that nanoparticles constituting a range of sizes were directly generated on the TiO2 surface coating. The silver nanoparticle peak in the embodiment illustrated inFIG. 6 is at 440 nm, which matches what would be expected if the average size of the nanoparticles were between 40 and 50 nm. The intense absorption present in the UV—vis spectra of all TiO2 coated samples in the UV region is due to the absorption profile of plain TiO2. Because the gold and silver nanoparticle peaks occur in the visible region of the spectra it should be noted that the fiber materials may take on a characteristic purple (in the case of gold) or brown (in the case of silver) color after deposition of the nanoparticles but prior to staining, which matches the coloration found in the literature when dealing with comparatively large gold and silver nanoparticles.FIG. 6 further illustrates UV protective properties of the Ag/Au—TiO2 coatedfiber materials 10 over untreated cotton, as the absorption of all samples but pristine can be seen to dramatically increase in the UV region of the spectra. -
FIG. 7 illustrates the XRD spectra for (a) pre-exposure Ag—TiO2 coated fiber materials, (b) pre-exposure Au—TiO2 coated fiber materials, (c) pre-exposure TiO2 coated fiber materials, (d) pre-exposure pristine uncoated fiber materials, and (e) post-exposure TiO2 coated fiber materials. -
FIG. 8 illustrates the UV-Vis absorption spectra of (a) Ag—TiO2 coated fiber materials, (b) Au—TiO2 coated fiber materials, (c) TiO2 coated fiber materials, and (d) pristine uncoated fiber materials after staining with methylene blue dye and exposing the fiber material to simulated full-spectrum solar light (1.5 sun intensity) over a variety of time intervals. The area contained by the peak can be directly related to the intensity of the appearance of the stain on the fiber material and thereby also to the concentration of the dye molecules remaining on the surface of the Ag/Au—TiO2 coated fiber materials by Beer's law. As also shown inFIG. 8 , the rate of stain extinction/fiber self-cleaning is dramatically increased on the Ag/Au—TiO2 coated fiber materials as the methylene blue stain is being destroyed by the Ag/Au—TiO2 coating at a faster rate than what occurs with the pristine uncoated fiber material. - As shown in
FIG. 9 , the breakdown of methylene blue proceeds much more rapidly for the fiber samples that have been coated with TiO2, and further improvement of the rate of decay is obtained when gold or silver nanoparticles are deposited on the TiO2-coated fibers.FIG. 9 illustrates the integration of the area contained by the peaks inFIG. 8 and allows for determination of the rate of stain removal from the textile materials. The rate of stain removal observed for the Ag/Au—TiO2 coated fiber materials is of the first order, and was observed to proceed more rapidly for the Ag/Au—TiO2 coated fiber materials than for either the only TiO2 coated fiber materials or the untreated fiber material, providing direct quantitative verification of the enhancement in photocatalytic activity obtained with this treatment methodology. The extinction of methylene the adsorbed stain can be seen to follow a roughly first order rate of decay, where the rate of decay can be determined by ln([C]/[C]0)=−kt (illustrated by the plot ofFIG. 9 ). -
FIG. 10 illustrates repeated testing cycles of the Ag/Au—TiO2 coated fiber materials to illustrate that the photocatalytic activity of the Ag/Au—TiO2 coated fiber materials does not decrease over time. As shown, following three cycles of staining followed by exposure to simulated sunlight until the stain was virtually eliminated, the Ag/Au—TiO2 coated fiber materials displayed remarkable consistency of stain removal over multiple cycles, with the obtained rate constants of stain removal being virtually the same. As further illustrated byFIG. 10 , the kinetic rates of stain degradation do not change over multiple staining cycles for the Ag/Au—TiO2 coated fiber materials, and the photo-catalytic activity of the produced Ag/Au—TiO2 coating is stable even over a significant length of time. -
FIG. 11 illustrates FTIR spectra of the Ag/Au—TiO2 coated fiber materials after repeated exposure to simulated solar light for exposure times of (a) no exposure, (b) two hours, (c) four hours, (d) six hours, and (e) ten hours. As shown, the spectra for the Ag/Au—TiO2 coated fiber materials remains unchanged over time indicating minimal degradation. Additionally, the surface coating is not being damaged during the process of stain removal, and the photocatalytic activity of the Ag/Au—TiO2 coated fiber materials appear to remain roughly unchanged over multiple staining/stain removal events. The concentration of the stain also has no apparent effect on the rate of stain removal, as staining for the first two cycles was performed using a 0.001% w/v methylene blue solution, and staining for the third cycle used a 0.1% w/v solution and no difference in extinction rate was observed. This suggests that the photocatalytic activity of the Ag/Au—TiO2 coating does not decrease with increased stain saturation, at least at practical levels of staining. - Staining with Congo red was also performed to evaluate the photocatalytic performance with a different, less easily broken-down stain. In general, the extinction of Congo red can be seen to proceed more slowly than methylene blue, with the rate of extinction of Congo red stained on pristine fiber material being roughly half that of methylene blue stained on pristine fiber material. The improvement in the rate of stain extinction of the Ag/Au—TiO2 coated fiber materials over the pristine fiber material was also less pronounced when Congo red was tested, with a 1 mM Ag/Au—TiO2 coated fiber material sample demonstrating the best performance in this case with a 65% improvement in the rate of stain removal when compared to the pristine fiber material. Congo red taking longer to degrade is expected as it has been found to take roughly twice as long as methylene blue to photocatalytically degrade, however the decrease in the photocatalytic effect of the Ag/Au—TiO2 coated fiber materials is notable. This effect can be partially accounted for by the fact that Congo red, while having its main absorption peak at 496 nm, also has two absorption peaks in the UV region at 236 and 338 nm. Because of this, it is likely that some of the incident photocatalytically useful UV and near UV radiation was absorbed by the Congo red stain itself rather than interacting with the Ag/Au—TiO2 coating layer, decreasing the apparent efficiency of the catalytic coating. Compounds such as Congo red which absorb high-energy incident radiation are a good example of why Au/Ag nanoparticle-based photosensitizers are important for photocatalytic applications; by decreasing the bandgap of TiO2 and increasing the wavelength range in which photons can be harnessed for photocatalysis, compounds which inherently absorb high-energy incident photons can still be degraded. This is likely the reason that the majority of the nanoparticle coated samples displayed better performance than the fiber material coated with TiO2 only when stained with Congo red.
- Additionally, the Au—TiO2 coated fiber materials displayed markedly better photocatalytic activity than the Ag—TiO2 coated fiber materials when stained with Congo red (S7), and the reason for this could be explained by the higher wavelength of the gold nanoparticle peak relative to the silver peak, and thus the decreased overlap with the Congo red peaks. This strongly suggests that electron transfer is taking place between the gold nanoparticles and the TiO2 coating, and that the gold nanoparticles are acting as photosensitizers. A complicating factor in interpreting the kinetic data directly is the non-first order rate of stain extinction observed for the samples not impregnated with nanoparticles, which was also observed in previous works. This complicates direct comparison of the kinetic constants with one another however qualitatively it can still be seen that the rate of stain extinction is improved for the metallic nanoparticle impregnated samples (See
FIG. 8 ). - The fiber materials' stability of photocatalytic activity over time, and confirmation that the cellulose was not being photocatalytically destroyed was provided by FTIR analysis of the Au—TiO2 coated fiber materials at regular intervals after UV exposure (See
FIG. 11 ). Degradation of the fiber would be evidenced by changes in the FTIR spectra corresponding to destruction of the cellulosic backbone, however no changes in the spectra are observed. Characteristic peaks that can be observed include a broad O—H stretching band at 3378 cm−1, the C—H stretching band at 2900 cm−1, and the H—O—H bending band at 1650 cm−1, which is observed to be more intense in the Au—TiO2 coated fiber material than in the pristine fiber material, however this may also be due to the somewhat hydrophobic nature of the potassium bromide used to prepare the fibers for FTIR analysis. The TiO2 band is expected to appear at ˜700 cm−1, and indeed the Au—TiO2 absorption spectra lack the “dip” observed in the spectra of pristine cotton near 700 cm−1, which suggests that the TiO2 while not immediately visible is indeed present as a relatively broad peak. Reduction of the intensity of C—H stretching band at 2900 cm−1 was also observed. Overall, the consistency of the FTIR spectra after ten hours of exposure to simulated solar light suggests that the Au—TiO2 coated fibers possesses long-term photo stability. - Referring to
FIGS. 12 and 13 , the antimicrobial properties of the prepared fabric material were examined via the Kirby-Baur disk diffusion method using gram negative E. Coli. bacteria. The nanoparticle coated fiber samples are expected to show antimicrobial activity in addition to the stain cleansing properties. As shown inFIG. 12 , a zone of exclusion is clearly visible around the Au—TiO2 coated fiber material (a) and the semiconductor and Ag—TiO2 coated fiber material (b), but not around the TiO2 coated fiber material alone (c), indicating that the metallic nanoparticles directly grown on the semiconducting surface lend the material antimicrobial properties. - Testing of the anti-microbial properties of the Ag/Au—TiO2 coated fiber materials demonstrated that the prepared fiber samples were resistant to gram negative E. coli microbial contamination as evidenced by the zone of inhibition that was present around the fibers after inoculation and incubation of the plates (See
FIG. 12 ). It should be noted that the degree of coli inhibition for the gold and silver nanoparticle coated samples was about equivalent. This result was expected given the widespread study and utilization of silver nanoparticles for their bactericidal properties, and the recent utilization of gold nanoparticles for the same purpose. The TiO2 and pristine cotton fiber material samples exhibited little to no bacterial inhibition, which is notable as some limited degree of bactericidal activity would be expected simply from the reducing/oxidizing potential generated by the TiO2 layer, and while the oxide alone likely generates some antimicrobial activity, it is apparently much more pronounced with the gold and silver nanoparticle containing samples. It is likely however that bacteria located directly on the illuminated fiber samples coated with TiO2 only would be quickly removed by the oxidizing power of the TiO2 and the reactive species generated at the surface, as E. coli, Staphylococcus aureus, and Pseudomonas aeruginosa, the bacteria responsible for common skin infections/MRSA (methicillin-resistant Staphylococcus aureus) and hospital-acquired antibiotic resistant infections respectively, have each been experimentally observed to be killed rapidly on illuminated TiO2 surfaces. - Furthermore the toxic compounds produced by bacteria can themselves be certainly decomposed by the catalytic action of TiO2. However, this localized effect is insufficient if the fiber is to be deployed as clothing material, as the entirety of the fiber should be kept free from microbes, not just the outermost exposed surface, thus the relatively large zone of exclusion provided by the incorporation of gold and silver nanoparticles is desirable. One proven mechanism of bactericidal action for both gold and silver nanoparticles includes the disruption of cysteine/disulfide bonds in the proteins on the exterior of bacterial cell walls leading to decreased cell wall integrity, direct inhibition of ATP production, ribosomal activity, and DNA degradation.
- Free radical generation has also been proposed to be an active bactericidal mechanism for silver nanoparticles. The reaction between silver nanoparticles and the membrane structures of both gram positive and gram negative are not fully understood, however the formation of “pits” in the out membranes due to the presence of silver nanoparticles, leading to increased membrane permittivity and ultimately cell death have been observed. However there remains a strong argument for the free radicals generated by silver nanoparticles to be the main causal mechanism behind the antimicrobial effects, as the inclusion of an antioxidant in one study was found to eliminate the anti-microbial action of silver nanoparticles. Furthermore it has been suggested that the evolution of silver ions produced from the silver nanoparticles via their oxidation by the holes produced on the TiO2 layer may be another mechanism by which the TTiO2/Ag nanoparticle hybrid surface exhibits antimicrobial activity, as a similar mechanism has been observed with TTiO2/copper hybrid surfaces. Our results suggest that some combination of the above outlined plays an active role in improving the antimicrobial activity of the nanoparticle coated fiber samples, and further elucidation of the mechanism behind the observed antimicrobial properties could be had testing the nanoparticle coated fibers in the presence of an antioxidant. The gold and silver nanoparticle coated fiber materials showed similar antibacterial activity.
FIG. 13 demonstrates the mechanism behind the most active bactericidal pathway in this photocatalytically active material, namely, the generation of electrons and holes that react through the mechanisms outlined above to destroy bacteria in proximity to the photocatalytically active nanostructured surface. - In some embodiments, the method provides for treating a textile fiber material with a sol-gel based method, as outlined above, so as to facilitate the deposit of a semiconducting thin film (TiO2) on at least one surface of the textile material. In this manner, metallic (Ag/Au) nanoparticles, for example silver, gold or both silver and gold, metallic nanoparticles are grown directly on the oxide surface via the photocatalytic reduction method outlined above. This treatment method provides for the creation of a photocatalytically active fiber material, that is scalable using techniques carried out at normal atmospheric pressure (about 1 atmospheric pressure), and require only that the material be capable of withstanding 95° C. temperatures for a short period of time. Another important feature of the
method 100 is the use of the nanoparticles to allow the absorption and photocatalytic utilization of near-UV and visible incident photons which improves photocatalytic activity by allowing for the useful harnessing of more incident light. The metallic nanoparticles impart an antimicrobial feature to the surface of a material, for example the surface of a fiber material, another unique feature imparted to the surfaces and fiber materials provided as part of the invention. - The present invention allows for the treatment of fibrous and non-fibrous textile materials and the production of a hybrid semiconductor/metallic nanoparticle based photocatalytic (self-cleaning), antimicrobial, and UV radiation protective system on the textile surface. The treatment technique allows the textile material to be treated without the use of either vacuum or pressurized conditions, and the textile material is required only to withstand dry annealing at 95° C. and hydrothermal treatment in boiling water, both mild conditions compared to more exotic treatment methodologies.
- The present example demonstrates the utility of the present invention for providing personal protective equipment (PPE), fabricated with the herein described functionalized textile materials. Personal protective equipment (PPE) refers to protective clothing, helmets, gloves, face shields, goggles, facemasks and/or respirators or other equipment designed to protect the wearer from injury or the spread of infection or illness. In particular applications, the infection and/or illnesses may comprise infections or illnesses caused by bacteria, viruses (including corona virus), fungus and other related infectious agents.
- PPE is commonly used in health care settings such as hospitals, doctor's offices and clinical labs. When used properly, PPE acts as a barrier between infectious materials such as viral and bacterial contaminants and your skin, mouth, nose, or eyes (mucous membranes). The barrier has the potential to block transmission of contaminants from blood, body fluids, or respiratory secretions. PPE may also protect patients who are at high risk for contracting infections through a surgical procedure or who have a medical condition, such as, an immunodeficiency, from being exposed to substances or potentially infectious material brought in by visitors and healthcare workers. When used properly and with other infection control practices such as hand-washing, using alcohol-based hand sanitizers, and covering coughs and sneezes, it minimizes the spread of infection from one person to another. Effective use of PPE includes properly removing and disposing of contaminated PPE to prevent exposing both the wearer and other people to infection.
- When an infection outbreak affects a broad population in the United States, the Centers for Disease Control and Prevention (CDC), is responsible for making specific recommendations for infection control measures in different circumstances and settings.
- The health and medical protective devices and garments prepared with the textiles described herein prevent the passage of virus and virus particles, as well as other infectious and potentially harmful materials and fumes, to a subject. The treated textiles described herein have particular application as medically protective garments and devices. By way of example, such garments and devises comprise surgical masks, personal protective masks, dressing gowns, surgical drapes, face masks, surgical medical devices, sneeze guards, medical and clinical setting room dividers, and the like.
- An embodiment of the present invention may include a medical mask such as a disposable anesthesia face mask, ventilation mask, sleep apnea mask or respiratory mask (a “medical mask”). The mask may include a cup-like shell or receptacle member terminating at a peripheral edge with a circumferential flange, and an annular donut-shaped hollow cushion or seal member affixed or otherwise permanently attached to the flange. The seal member may be inflatable.
- The shell or shell member may preferably be transparent to permit viewing therethrough. The shell member may be shaped suitably to define a nose reception portion, a mouth reception portion, and a chin reception portion. The shell member may include a first passageway extending from the shell member from in a direction opposite to the flange for coupling to a breathing circuit, and a second passageway that may extend in a direction opposite to the flange for output. Embodiments of an anesthesia or ventilation mask may be connect the output passageway to a flexible tube which, in turn, is adapted to be connected to a monitoring machine, such as to a CO2 monitoring machine or capnograph.
- In some embodiments, the face mask nasal portion may have a first width, the face mask mouth portion may have a second width greater than the first width, and the face mask chin portion may have a third width greater than the second width, giving the face mask shell a characteristic pear-shaped configuration. The nasal, mouth and chin portions may be continuous and form the cup-like extent of the shell or receptacle component.
- Embodiments may include a headband. The mask may have lateral projections on the flange or two sides of the shell for accommodating a suitable elastic head strap that may adjustably be coupled to the projections to thereby retaining the strap to the mask. The tension in the elastic headband when attached may provide a stable suspension system securely maintaining the mask assembly in place before or during surgery and enabling anesthesia personnel to attend to other tasks using both hands free. This also applies if the mask and band are used for sleep apnea or during a breathing treatment.
- Embodiments of a mask may be adapted to be fitted to the user's face with the chin portion of the face being received in a cavity near the bottom of the mask. T-shaped posts that hold the headband may be located on the flange member upwardly near the nose portion of the mask assembly. The lateral projections hold the strap to form a loop that holds the mask in place on the user's face.
- An embodiment of a face mask may be made from the textile materials described herein, and will have the ability to prevent the passage of small agents, such as virus , virus particles and bacteria, through the textile, thus shielding the wearer from exposure to such agents through the mouth and nose.
- Embodiments of masks may include a general environmental usage mask, an anesthesia mask, ventilation mask, sleep apnea mask, and/or a respiratory therapy mask. Embodiments of masks may be disposable, or reusable, and may have a strap or straps to hold the mask in place when desired. Embodiments may be of sufficient size to cover a subjects nose and mouth, and if desired, chin area. Embodiments may have a pneumatic sealing cushion, to promote comfort in the subject wearing the mask, as well as to prevent leakage of air or gases from and to the subject once the mask is positioned on the subject. Particular embodiments may include gas input ports or output ports, and may optionally further include a layer of the treated textile material covering the ports, so as to preclude and filer gases as they are released to a wearer through the ports, such as during oxygen administration, for example.
- The present example demonstrates that the present process and treatment may be provided onto the surface of an existing article of personal protective equipment, such as a mask.
- Conventional commercially available face masks made of a tight-weave cotton, were treated according to the methods described herein to include a thin, 1 mM, Ag—TiO2 film or an Au—TiO2 film. These treated cotton masks were then examined for stability of the deposited thin film.
- The results demonstrated that the methods used provided for the successful deposition of a thin semi-conductive layer and growth of a uniform layer of metal nanostructured particles to the surface.
- As demonstrated in the following examples, cotton materials/textiles treated as described herein were also observed to be stable and resistant to degradation and/or deterioration from multiple machine washings with fabric detergents, did not demonstrate delamination of the films, and were resistant to significant fiber degradation upon exposure to high temperatures (up to 90° C. for 3 or more hours). The present surface treatments are therefore amendable to conventional autoclave conditions.
- The present example demonstrates that the articles treated to include the functionalized surfaces are stable, may be washed using conventional methods, such as in a conventional washing machine with detergents, and may also be sterilized after use with white or ultraviolet light.
- After use of a mask, for example, that has been treated to include the herein described thin film semiconductor layer and noble metal nanoparticle materials, the mask may be placed in an area where white light (e.g., daylight) is available to the surface. The semi-conductive nature of the film permits the surface to neutralize and/or destroy microbes that may have become exposed to the surface of the material, such as to destroy virus or bacteria. This decontaminating action may also be provided upon exposure of the material textile to ultraviolet light. This presents yet another advantage of the present materials and products as protective garments and equipment, as ultraviolet light is not required to decontaminate the surface, and may be accomplished by providing simple white light.
- PPE (face masks) having a treated functionalized surface were washed 35 cycles with detergent.
- After the series of 35 wash cycles, it was observed that the functionalized surfaces of these materials maintained at least 85% of their original functionalized textile properties, and no significant fiber degradation was observed.
- The constructions described above and illustrated in the drawings are presented by way of example only and are not intended to limit the concepts and principles of the present invention. Thus, there has been shown and described several embodiments of a novel invention. As is evident from the foregoing description, certain aspects of the present invention are not limited by the particular details of the examples illustrated herein, and it is therefore contemplated that other modifications and applications, or equivalents thereof, will occur to those skilled in the art. The terms “having” and “including” and similar terms as used in the foregoing specification are used in the sense of “optional” or “may include” and not as “required”. Many changes, modifications, variations and other uses and applications of the present construction will, however, become apparent to those skilled in the art after considering the specification and the accompanying drawings. All such changes, modifications, variations and other uses and applications which do not depart from the spirit and scope of the invention are deemed to be covered by the invention which is limited only by the claims which follow.
- The following references are specifically incorporated herein by reference.
- 1. H. Tokuhisa, S. Tsukamoto, S. Morita, S. Ise, M. Tomita, N. Shirakawa, Appl. Surf. Sci. 400 (2017) 64-70, https://doi.org/10.1016/j.apsusc.2016.11.213.Z.
- 2. Li, J. Meng, W. Wang, Z. Wang, M. Li, T. Chen, C.-J. Liu, Carbohydr. Polym. 161 (2017) 270-276, https://doi.org/10.1016/j.carbpol.2017.01.020.
- 3. M. R. Nateghi, M. Shateri-Khalilabad, Silver nanowire-functionalized cotton fabric, Carbohydr. Polym. 117 (2015) 160-168, https://doi.org/10.1016/j.carbpol.2014.09.057.
- 4. T. Yuranova, D. Laub, J. Kiwi, Catal. Today 122 (2007) 109-117, https://doi.org/10.1016/j.cattod.2007.01.040.
- 5. A. Fujishima, K. Honda, Nature 238 (1972) 37-38, https://doi.org/10.1038/238037a0.
- 6. A. Houas, H. Lachheb, M. Ksibi, E. Elaloui, C. Guillard, J.-M. Appl. Catal. B: Environ. 31 (2001) 145-157, https://doi.org/10.1016/S0926-3373(00)00276-9.
- 7. V. Kandavelu, H. Kastien, K. R. Thampi, Appl. Catal. B: Environ. 48 (2004) 101-111, https://doi.org/10.1016/j apcatb.2003.09.022.
- 8. C. H. Ao, S. C. Lee, J. Z. Yu, J. H. Xu, Appl. Catal. B: Environ. 54 (2004) 41-50, https://doi.org/10.1016/j.apcatb.2004.06.004.
- 9. M. Stylidi, D. I. Kondarides, X. E. Verykios, Appl. Catal. B: Environ. 47 (2004) 189-201, https://doi.org/10.1016/j.apcatb.2003.09.014.
- 10. M. Alvaro, C. Aprile, M. Benitez, E. Carbonell, H. Garcia, J. Phys. Chem. B 110 (2006) 6661-6665, https://doi.org/10.1021/jp0573240.
- 11. A. Bozzi, T. Yuranova, J. Kiwi, J. Photochem. Photobiol. A Chem. 172 (2005) 27-34.
- 12. M. Alvaro, B. Cojocaru, A. A. Ismail, N. Petrea, B. Ferrer, F. A. Harraz, V. I. Parvulescu, H. Garcia, Appl. Catal. B Environ. 99 (2010) 191-197, https://doi.org/10.1016/j.apcatb.2010.06.019.
- 13. A. Fujishima, T. N. Rao, D. A. Tryk, J. Photochem. Photobiol. C Photochem. Rev. 1 (2000) 1-21, https://doi.org/10.1016/S1389-5567(00)00002-2.
- 14. T. Yuranova, A. G. Rincon, A. Bozzi, S. Parra, C. Pulgarin, P. Albers, J. Kiwi, J. Photochem. Photobiol. A Chem. 161 (2003) 27-34, https://doi.org/10. 1016/S1010-6030(03)00204-1.
- 15. A. Bozzi, T. Yuranova, I. Guasaquillo, D. Laub, J. Kiwi, J. Photochem. Photobiol. A Chem. 174 (2005) 156-164, https://doi.org/10.1016/j. jphotochem.2005.03.019.
- 16. N. Veronovski, M. Sfiligoj-Smole, J.L. Viota, Characterization of TiO2/TiO2—SiO2 coated cellulose textiles, Text. Res. J. 80 (2010) 55-62, https://doi.org/10.1177/0040517509104012.
- 17. M. J. Uddin, F. Cesano, F. Bonino, S. Bordiga, G. Spoto, D. Scarano, A. Zecchina, Photoactive TiO2 films on cellulose fibres: synthesis and characterization, J. Photochem. Photobiol. A Chem. 189 (2007) 286-294, https://doi.org/10.1016/j. jphotochem.2007.02.015.
- 18. M. S. A. Amin, M. J. Uddin, M. A. Islam, Removal of azo dye by synthesized TiO2 nanoparticles, Nanomater. Environ. 1 (2012) 18-22, https://doi.org/10.2478/ nanome-2012-0003.
- 19. A. Fujishima, X. Zhang, D. A. Tryk, TiO2 photocatalysis and related surface phenomena, Surf. Sci. Rep. 63 (2008) 515-582, https://doi.org/10.1016/j.surfrep. 2008.10.001.
- 20. Y. Tamaki, A. Furube, M. Murai, K. Hara, R. Katoh, M. Tachiya, Phys. Chem. Chem. Phys. 9 (2007) 1453-1460, https://doi.org/10.1039/B617552J.
- 21. P. L. Taylor, A. L. Ussher, R. E. Burrell, Biomaterials 26 (2005) 7221-7229, https://doi. org/10.1016/j.biomaterials.2005.05.040.
- 22. Hui-Lei Wang, J. Inorg. Mater. 31 (5) (2016) 555-560, https://doi.org/10.15541/jim20150535.
- 23. M. J. Uddin, F. Cesano, D. Scarano, F. Bonino, G. Agostini, G. Spoto, S. Bordiga, A. Zecchina, J. Photochem. Photobiol. A Chem. 199 (2008) 64-72, https://doi.org/10.1016/j.jphotochem.2008.05.004.
- 24. P. Priecel, H. Adekunle Salami, R. H. Padilla, Z. Zhong, J. A. Lopez-Sanchez, Chin. J. Catal. 37 (2016) 1619-1650, https://doi.org/10.1016/51872-2067(16)62475-0.
- 25. S. Boufi, A. M. Ferraria, A. M. B. do Rego, N. Battaglini, F. Herbst, M. R. Vilar, Carbohydr. Polym. 86 (2011) 1586-1594, https://doi.org/10.1016/j. carbpol.2011.06.067.
- 26. C. Renz, Uber die Einwirkung von Oxyden auf Silbernitrat and Goldchlorid im Licht, HCA. 15 (1932) 1077-1084, https://doi.org/10.1002/h1ca.193201501118.
- 27. S. Eustis, M. A. El-Sayed, Chem. Soc. Rev. 35 (2006) 209-217, https://doi.org/10.1039/B514191E.
- 28. W. Haiss, N. T. K. Thanh, J. Aveyard, D. G. Fernig, Anal. Chem. 79 (2007) 4215-4221, https://doi.org/10.1021/ac0702084.
- 29. Gold Nanoparticles: Properties and Applications, Sigma-Aldrich. (n.d.). http://www. sigmaaldrich.com/technical-documents/articles/materials-science/nanomaterials/gold-nanoparticles.html. (Accessed 20 Apr. 2017).
- 30. Silver Nanoparticles: Properties and Applications, Sigma-Aldrich. (n.d.). http://www.sigmaaldrich.com/materials-science/nanomaterials/silver-nanoparticles. html (Accessed 12 Apr. 2017).
- 31. M. A. Moharram, T. Z. Abou El Nasr, N. A. Hakeem, J. Polym. Sci. B Polym. Lett. Ed. 19 (1981) 183-187, https://doi.org/10.1002/pol.1981.130190405.
- 32. J. Cenens, R. A. Schoonheydt, Clays Clay Miner. 36 (1988) 214-224.
- 33. P. T. Hoang, S. T. J. Aishee, G. Grissom, A. Touhami, H. J. Moore, M. J. Uddin, MRS Adv. 2 (2017) 791-798, https://doi.org/10.1557/adv.2017.151.
- 34. H. Lachheb, E. Puzenat, A. Houas, M. Ksibi, E. Elaloui, C. Guillard, J.-M. Herrmann, Appl. Catal. B Environ. 39 (2002) 75-90, https://doi.org/10.1016/50926-3373(02) 00078-4.
- 35. H. Zhu, R. Jiang, L. Xiao, Y. Chang, Y. Guan, X. Li, G. Zeng, J. Hazard. Mater. 169 (2009) 933-940, https://doi.org/10.1016/j.jhazmat.2009.04.037.
- 36. C. Chung, M. Lee, E. K. Choe, Carbohydr. Polym. 58 (2004) 417-420, https://doi.org/10.1016/j.carbpol .2004.08.005.
- 37. R. Beranek, H. Kisch, Photochem. Photobiol. Sci. 7 (2008) 40-48, https://doi. org/10.1039/b711658f.
- 38. Visible 405 nm SLD light photo-destroys methicillin-resistant Staphylococcus aureus (MRSA) in vitro.—PubMed—NCBI, (n.d.). https://www.ncbi.nlm.nih.gov/pubmed/19065556 (Accessed 7 Jun. 2018).
- 39. E. Pizzo, A. Di Maro, A new age for biomedical applications of Ribosome inactivating Proteins (RIPs): from bioconjugate to nanoconstructs, J. Biomed. Sci. 23 (2016), https://doi.org/10.1186/s12929-016-0272-1.
- 40. Y. Cui, Y. Zhao, Y. Tian, W. Zhang, X. Lu, X. Jiang, Biomaterials 33 (2012) 2327-2333, https://doi.org/10.1016/j.biomaterials.2011.11.057.
- 41. J. S. Kim, E. Kuk, K. N. Yu, J.-H. Kim, S. J. Park, H. J. Lee, S. H. Kim, Y. K. Park, Y. H. Park, C.-Y. Hwang, Y.-K. Kim, Y.-S. Lee, D. H. Jeong, M.-H. Cho, Nanomed. Nanotechnol. Biol. Med. 3 (2007) 95-101, https://doi.org/10.1016/j.nano.2006.12.001.
- 42. K. Sunada, T. Watanabe, K. Hashimoto, Environ. Sci. Technol. 37 (2003) 4785-4789, https://doi.org/10.1021/es034106g.
- 43. X. Li, S .M. Robinson, A. Gupta, K. Saha, Z. Jiang, D. F. Moyano, A. Sahar, M. A. Riley, V. M. Rotello, ACS Nano 8 (2014) 10682-10686, https://doi.org/10.1021/nn5042625.
Claims (23)