US20200140696A1 - Low reflectance powder coating compositions - Google Patents

Low reflectance powder coating compositions Download PDF

Info

Publication number
US20200140696A1
US20200140696A1 US16/556,574 US201916556574A US2020140696A1 US 20200140696 A1 US20200140696 A1 US 20200140696A1 US 201916556574 A US201916556574 A US 201916556574A US 2020140696 A1 US2020140696 A1 US 2020140696A1
Authority
US
United States
Prior art keywords
coating composition
acrylic
powder
powder coating
resin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US16/556,574
Inventor
Edmund J. Mahn
Mark E. Walker
Mark J. Wytiaz
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Swimc LLC
Original Assignee
Swimc LLC
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Swimc LLC filed Critical Swimc LLC
Priority to US16/556,574 priority Critical patent/US20200140696A1/en
Publication of US20200140696A1 publication Critical patent/US20200140696A1/en
Priority to US17/477,072 priority patent/US20220204779A1/en
Abandoned legal-status Critical Current

Abstract

A powder coating composition comprising:
    • (a) a first acrylic powder resin having a hydroxyl value of at least about 180;
    • (b) a second acrylic powder resin having a hydroxyl value between about 45 and about 80;
    • (c) a crosslinker reactive with the hydroxyl functional acrylic resins; and
    • (d) an acicular filler.

Description

  • This invention is a continuation of U.S. application Ser. No. 13/798,329 filed on Mar. 13, 2013 and entitled “LOW REFLECTANCE POWDER COATING COMPOSITIONS”, which was made with Government support under Contract Number W912HQ-12-C-0013 awarded by the U.S. Army Corps of Engineers, HECSA. The Government has certain rights in this invention.
  • Very low gloss powder coatings are desirable for a variety of uses including automotive interior parts, wheel rims, bumpers, firearms, and military applications and other articles where low reflectance is desired. A particular requirement of some military applications involves resistance to penetration by chemical warfare agents according to military specifications such as MIL-PRF-32348. For some military and commercial applications it is useful to provide a coating composition which when applied to a substrate and cured will have a 60° gloss less than 1 and an 85° gloss less than 7, for example, 3.5 or less.
  • This invention therefore relates to a low gloss powder coating composition comprising:
      • (a) a first acrylic powder resin having a hydroxyl value of at least about 180;
      • (b) a second acrylic powder resin having a hydroxyl value between about 45 and 80, for example, about 60;
      • (c) a crosslinker reactive with the hydroxyl functional acrylic resins; and
      • (d) an acicular filler, such as wollastonite.
        For certain embodiments of this invention it is useful to have the weight ratio of the first acrylic powder resin to the second acrylic powder resin be greater than about 0.5, for example about 1.0.
  • One aspect of this invention involves the selection of two different hydroxyl functional acrylic powder resins having varying hydroxyl values. The production of acrylic polymers of a given hydroxyl number is well known within the art. The hydroxyl functional acrylic polymers of this invention are obtained in a customary manner, for example, by polymerizing at least one hydroxyl functional monomer, typically a hydroxyl functional (meth)acrylate such as hydroxyethyl or hydroxypropyl (meth)acrylate, along with other copolymerizable unsaturated monomers. Representative copolymerizable monomers include vinyl compounds such as styrene, methylstyrene, vinyl acetate, and the unsaturated alkyl esters of (meth)acrylic acids. Suitable alkyl (meth)acrylate monomers include, for example, methyl (meth)acrylate, ethyl (meth)acrylate, butyl (meth)acrylate, propyl (meth)acrylate, 2-ethyl hexyl (meth)acrylate, cyclohexyl (meth)acrylate, decyl (meth)acrylate, isodecyl (meth)acrylate, benzyl (meth)acrylate, isobornyl (meth)acrylate, neopentyl (meth)acrylate, and 1-adamatyl methacrylate. By selecting the level of hydroxyl functional monomer which is incorporated into the acrylic powder resins, any given hydroxyl value can be selected. The polymers can be formulated to any useful glass transition temperature. For some applications it is useful to have a Tg of at least 35° C., and sometimes at least 40° C. for each of the hydroxy functional acrylic resins. For some applications it is useful to have the resin with the higher hydroxyl number have a Tg of at least 45° C. or higher to provide ever greater resistance to chemical agents.
  • For this invention, a first hydroxyl functional acrylic powder resin will be produced having a hydroxyl value of at least about 180, and a second hydroxyl functional acrylic polymer resin will be produced having a hydroxyl value between about 45 and about 80. These resins are then combined with a suitable crosslinking agent reactive with hydroxyl groups, such as a blocked isocyanate or uretdione, to provide the powder coating composition. For some embodiments of this invention, the first acrylic powder resin will have a hydroxyl value between about 180 and about 300, and for some embodiments of this invention it is useful for the second acrylic powder resin to have a hydroxyl value between about 45 and 60, for some embodiments about 60. In another useful embodiment, the first acrylic powder resin will have a hydroxyl value that is at least about 150 higher than the hydroxyl value of the second acrylic powder resin, for example, at least about 150 to about 240 higher, further for example, at least about 170 to about 190 higher.
  • For those applications requiring resistance to chemical agents it is often useful to provide a weight ratio of the first acrylic powder resin to the second acrylic powder resin greater than 0.5, for example, greater than 0.8, further for example about 1.0. Typically, for the combination of the first acrylic powder resin and the second acrylic powder resin, between about 33.3 weight percent and 66.6 weight percent of the total amount of hydroxy functional acrylic resin would be the first acrylic powder resin. For some applications, between about 50 and 66.6 percent by weight of the combined weight of the first and second acrylic resins would be the second acrylic powder resin.
  • The powder coating composition of the present invention also includes a crosslinker reactive with the hydroxyl functional acrylic resins. In one useful embodiment a crosslinker having isocyanate functionality is used. Isocyanate compounds useful in the compositions of this invention have at least one isocyanate group per molecule. Polyisocyanate crosslinkers may be prepared by modifying simple aliphatic, cycloaliphatic, araliphatic and/or aromatic diisocyanates, being constructed from at least two diisocyanates, and having a uretdione, isocyanurate, allophanate, biuret, iminooxadiazinedione and/or oxadiazinetrione structure. Suitable diisocyanates for preparing such polyisocyanates are any desired diisocyanates of the molecular weight range 140 to 400 g/mol that are obtainable by phosgenation or by phosgene-free processes, as for example by thermal urethane cleavage, and have aliphatically, cycloaliphatically, araliphatically and/or aromatically attached isocyanate groups, such as 1,4-diisocyanatobutane, 1,6-diisocyanatohexane (HDI), 2-methyl-1,5-diisocyanatopentane, 1,5-diisocyanato-2,2-dimethylpentane, 2,2,4- and 2,4,4-trimethyl-1,6-diisocyanatohexane, 1,10-diisocyanatodecane, 1,3- and 1,4-diisocyanatocyclohexane, 1,3- and 1,4-bis(isocyanatomethyl)cyclohexane, 1-isocyanato-3,3,5-trimethyl-5-isocyanato-methylcyclohexane (isophorone diisocyanate, IPDI), 4,4′-diisocyanatodicyclohexylmethane, 1-isocyanato-1-methyl-4(3)-isocyanatomethylcyclohexane, bis(isocyanatomethyl)norbornane, 1,3- and 1,4-bis(2-isocyanatoprop-2-yl)benzene (TMXDI), 2,4- and 2,6-diisocyanatotoluene (TDI), 2,4′- and 4,4′-diisocyanatodiphenylmethane (MDI), 1,5-diisocyanatonaphthalene or any desired mixtures of such diisocyanates. Useful polyisocyanates or polyisocyanate mixtures may contain exclusively aliphatically and/or cycloaliphatically attached isocyante groups.
  • In one useful embodiment, the isocyanate crosslinker is a blocked isocyanate. Blocked isocyanate are prepared by reacting polyisocyanates with a reagent so that the polyisocyanate is stable at room temperature. Upon exposure to heat, the blocking group will dissociate to regenerate the isocyanate functionality. Suitable blocking groups may be selected from alcohols, caprolactam, phenols, methyl ethyl ketoxime, and active methylene compounds.
  • The ratio of equivalents of isocyanate to active hydrogen can be widely varied within the practice of this invention. The polyisocyanate will typically be present at a level to provide about 1.0 to about 2.0, for example, about 1.0 to about 1.5, equivalents of isocyanate for each equivalent of active hydrogen from the acrylic powder resins.
  • Additionally, it has been found that the use of an acicular filler, such as wollastonite, as a flattening pigment is useful in meeting the very low gloss and chemical resistance requirements of these coatings. Typically, the acicular filler, such as wollastonite, would be present at a weight solids percent of at least 10 percent and for some embodiments, at least 15 percent, and for some embodiments at least 25 percent of the total weight solids of the coating. For some applications it is useful to use a level of acicular filler, such as wollastonite, between about 10 and 35 percent by weight of the total weight solids of the final powder coating composition comprising the resins, the crosslinker and pigments.
  • Additional pigments such as titanium dioxide, metallic pigments, iron oxides, carbon black, organic pigments etc. can also be included. The coatings may also contain extender pigments, including polymeric extender pigments provided they are stable at the processing and cure temperatures of the powder coatings.
  • Additives such as flow agents, degassing agents, antistatic agents, plasticizers, light stabilizers, light absorbers, catalysts etc. can also be added. In one useful embodiment of the invention, the coating composition is substantially free of UV absorbers and hindered amine light stabilizers.
  • The powder coatings of this invention can be prepared by typical means well known in the art such as by first melt blending the ingredients of the coating compositions in an extruder at a suitable temperature. The extrudate is then cooled and pulverized.
  • The application of the powder coatings can be made by any means well known in the art for powder coatings such as by electrostatic spraying or by the use of a fluidized bed to any suitable substrate. If desired, the substrate can optionally be preheated prior to application of the powder coating composition. Once the coating composition has been applied to the substrate, the coating is cured by heating at a temperature and for a length of time sufficient to cause the reactants to form an insoluble polymer network. Typical cure temperatures would normally range from about 100° C. to about 250° C. for a period of about 10 to about 30 minutes. Suitable substitutes include any substrate which is not adversely affected by the cure time and temperature and would typically include metal, glass and plastic substrates. If desired, the substrate can be pretreated and/or coated with one or more suitable primer coats before application of the coatings of this invention.
  • The following examples illustrate embodiments and practices of advantage to a more complete understanding of the invention. Low reflectance powder coating compositions may be prepared as shown in Table 1. Unless otherwise stated, “parts” means parts-by-weight and “percent” is percent-by-weight, and equivalent weight is on a weight solids basis.
  • Coating compositions as set forth in Table 1 may be prepared by blending and extruding the listed raw materials. The extrudate may then be cooled and fractured to produce a powder coating which may be applied to a suitable substrate and baked before testing for gloss and other properties.
  • RAW MATERIAL EX. #1 EX. #2
    Hydroxy 150 184
    functional
    acrylic1
    Hydroxy 150 184
    functional
    acrylic2
    Blocked 349 281
    isocyanate3
    Flow agent4 10 10
    Benzoin 5 5
    Wollastonite 210 210
    Surfactant5 4 4
    Hindered 20
    Amine Light
    Stabilizer6
    UV Absorber7 40
    Iron oxide 47.5 47.5
    black pigment
    Carbon black 2.5 2.5
    powder
    Gloss 60/85 0.4/2.4 0.5/3.2
    1Acrylic powder resin having a hydroxyl number of 60.
    2Acrylic powder resin having a hydroxyl number of 250.
    3Vestagon ™B 1530 e-caprolactam blocked IPDI commercially available from Degussa.
    4Resiflow P-67 flow agent commercially available from Estron Chemical.
    5SURFYNOL ® 104S surfactant commercially available from Air Products.
    6TINUVIN ® 144 HALS commercially available from BASF
    7TINUVIN ® 928 commercially available from BASF
  • While this invention has been described by a specific number of embodiments, other variations and modifications may be made without departing from the spirit and scope of the invention as set forth in the appended claims.

Claims (16)

We claim:
1. A powder coating composition comprising:
(a) a first hydroxyl functional acrylic powder resin having a hydroxyl value of at least about 180;
(b) a second hydroxyl functional acrylic powder resin having a hydroxyl value between about 45 and about 80;
(c) a crosslinker reactive with the first and second hydroxyl functional acrylic resins; and
(d) an acicular filler;
and wherein the weight ratio of the first acrylic powder resin to the second acrylic powder resin is greater than 0.5.
2. The powder coating composition of claim 1 wherein the coating composition when applied to a substrate and cured will have a 60° gloss less than 1 and an 85° gloss 3.5 or less.
3. The powder coating composition of claim 1 wherein the first acrylic powder resin has a hydroxyl value between 180 and 250.
4. The powder coating composition of claim 1 wherein the second acrylic powder resin has a hydroxyl value between 45 and 60.
5. The powder coating composition of claim 1 wherein the second acrylic powder resin has a hydroxyl value of about 60.
6. The powder coating composition of claim 1 wherein the acicular filler is wollastonite.
7. The powder coating composition of claim 1 wherein the wollastonite is present at a level of at least 10% by weight solids of the coating composition.
8. The powder coating composition of claim 1 wherein the wollastonite is present at a level of at least 15% by weight solids of the coating composition.
9. The powder coating composition of claim 1 wherein the wollastonite is present at a level of at least 25% by weight solids of the coating composition.
10. The powder coating composition of claim 1 wherein the first acrylic powder resin and the second acrylic powder resin each have a Tg of at least 35° C.
11. The powder coating composition of claim 1 wherein the first acrylic powder resin has a Tg of at least 45° C.
12. The powder coating composition of claim 1 wherein the first acrylic polymer is present at a level to provide between about 33.3 weight percent and 85.1 weight percent of the total combined weight of the first acrylic polymer and the second acrylic polymer.
13. The powder coating composition of claim 1 wherein the first acrylic polymer is present at a level to provide between about 33.3 weight percent and 66.6 weight percent of the total combined weight of the first acrylic polymer and the second acrylic polymer.
14. The powder coating composition of claim 1 wherein the crosslinker is an isocyanate compound.
15. The powder coating composition of claim 14 wherein the isocyanate compound is present at a level to provide about 1.0 to about 1.5 equivalents of isocyanate functionality for each equivalent of active hydrogen of the first and second hydroxyl functional acrylic resins.
16. A process of coating a substrate which process comprises:
(i) applying a powder coating composition to a substrate; and
(ii) heating the coated substrate at a temperature and for a length of time sufficient to cause the composition to form an insoluble polymer network;
and wherein the powder coating composition comprises:
(a) a first hydroxyl functional acrylic powder resin having a hydroxyl value of at least about 180;
(b) a second hydroxyl functional acrylic powder resin having a hydroxyl value between about 45 and about 80;
(c) a crosslinker reactive with the hydroxyl functional acrylic resins; and
(d) wollastonite;
and wherein the weight ratio of the first acrylic powder resin to the second acrylic powder resin is greater than 0.5.
US16/556,574 2013-03-13 2019-08-30 Low reflectance powder coating compositions Abandoned US20200140696A1 (en)