US20190127532A1 - Polymeric material comprising modified lignin - Google Patents
Polymeric material comprising modified lignin Download PDFInfo
- Publication number
- US20190127532A1 US20190127532A1 US16/228,770 US201816228770A US2019127532A1 US 20190127532 A1 US20190127532 A1 US 20190127532A1 US 201816228770 A US201816228770 A US 201816228770A US 2019127532 A1 US2019127532 A1 US 2019127532A1
- Authority
- US
- United States
- Prior art keywords
- lignin
- polymer
- modified
- less
- linker
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A polymeric material comprising a first polymer and a second polymer where the first polymer is a natural or a synthetic polymer and the second polymer is modified lignin. The modified lignin is modified with an alkyl containing group via linker wherein the linker is an ether group and wherein the alkyl containing group is derived from fatty acid methyl ester.
Description
- This application Is A Divisional Of application Ser. No. 16/312,255, Entitled “Polymeric Material Comprising Modified Lignin”, Filed Dec. 20, 2018, Which Application Claims Priority To Pct/Se2017/051282, Entitled “Polymeric Material Comprising Modified Lignin”, Filed Dec. 15, 2017, Which application Claims Priority To Sweden Patent Application Ser. Nos. 1651653-6, Filed Dec. 15, 2016 And 1750733-6, Filed Jun. 9, 2017. The Entire Disclosures Of Which Are Hereby Incorporated By Reference. Any Disclaimer That May Have Occurred During The Prosecution Of The Above-Referenced Applications Is Hereby Expressly Rescinded, And Reconsideration Of All Relevant Art Is Respectfully Requested.
- The present invention relates to a polymeric material comprising modified lignin. The material may be injection moulded and exhibits very good mechanical properties.
- There is a need for more renewable plastic materials and lignin is potential polymer to be used. However a problem with lignin is its miscibility and compatibility with other polymer such as polyolefins.
- Lignin is the most available natural polymer next to cellulose. Lignin is found in the cell walls of fibrous plants and woods along with cellulose and hemicellulose. Lignin acts as a matrix material for polysaccharides, micro-fibrils and fibres and provides strength to plant stem. It is a high molecular weight phenolic macromolecule containing three different types of monolignol monomers p-coumaryl alcohol, coniferyl alcohol and sinapyl alcohol.
- WO2015/168571 discloses functionalized lignin that may be used in thermoplastics. The lignin is functionalized during reactive extraction leading using for example ethanol and an acid. Still there is no disclosure how the functionalized lignin may be used together with a thermoplastic.
- In order for a polymer or polymer mixture to be processed by compression moulding or injection moulding it should be thermally stable at elevated temperatures. This is a problem for many natural polymers even when they have been modified.
- The aim of the present invention is to overcome the drawbacks of the prior art and present a material comprising a renewable source, lignin, and where the material may be processed using conventional techniques such as extrusion and injection moulding.
- In a first aspect the present invention relates to a polymeric material comprising a first polymer and a second polymer wherein the first polymer is a natural or a synthetic polymer and the second polymer is modified lignin;
- wherein the modified lignin is modified by alkylation of the lignin via a linker wherein the linker is selected from an ether, ester, ketone, acetal, methylene, methyne, olefin, amide, thioester, thioether, imide, imidamide, carbamate, carbamothioic acid, sulfonyl, sulfonamide, silyl oxy, silyl ether, phenoxide, furan, phosphorous acid, quaternary ammonium or hetero cycles; preferably wherein the modified lignin is modified with an alkyl containing group via a linker wherein the linker is an ether group and wherein the alkyl containing group is derived from fatty acid methyl ester.
- In a second aspect the present invention relates to an injection moulded or extruded product comprising the polymeric material according to the present invention.
- In a third aspect the present invention relates to a compatibilizer comprising modified lignin wherein the modified lignin is modified by alkylation of the lignin via a linker wherein the linker is selected from an ether, ester, ketone, acetal, methylene, methyne, olefin, amide, thioester, thioether, imide, imidamide, carbamate, carbamothioic acid, sulfonyl, sulfonamide, silyl oxy, silyl ether, phenoxide, furan, phosphorous acid, quaternary ammonium or hetero cycles; preferably wherein the modified lignin is modified with an alkyl containing group via a linker wherein the linker is an ether group and wherein the alkyl containing group is derived from fatty acid methyl ester.
- In a fourth aspect the present invention relates to a method of extruding the material according to the present invention comprising:
-
- mixing the first polymer and the second polymer and optionally a compatibilizer wherein the first polymer is a natural or a synthetic polymer and the second polymer is modified lignin; and
- extruding the formed mixture at a temperature of at least 100° C., preferably at least 170° C. or at least 180° C.;
- optionally cutting the extruded material into pellets; and
- drying the obtained extruded material.
- In a fifth aspect the present invention relates to a method of injection moulding a product of the material according to the present invention wherein the method comprises:
-
- providing pellets or powder of the present material; and
- injection moulding the pellets or powder into a desired shape at a temperature of at least 100° C., preferably at least 180° C. or at least 200° C.
- All the embodiments herein are applicable to all the aspects.
-
FIG. 1 —TGA weight loss and derivative weight loss curves of RFL20L and RFL40S analysed in air atmosphere -
FIG. 2 —TGA weight loss and derivative weight loss curves of RFL40S analysed in N2 and air atmosphere -
FIG. 3 —TGA weight loss and derivative weight loss curves of RFL100SA and RFL100SB analysed in N2 atmosphere -
FIG. 4 —TGA weight loss and derivative weight loss curves of RFL100SE analysed in N2 atmosphere -
FIG. 5 —TGA weight loss and derivative weight loss curves of RFL100SE in comparison to RFL100SA and RFL100SB analysed in N2 atmosphere -
FIG. 6 —Isothermal TGA weight loss curves of RFL40S, RFL100SE and RFL100SB at 180° C. analysed in N2 atmosphere -
FIG. 7 —Isothermal TGA weight loss curves of RFL100SE and RFL100SB at 220° C. analysed in N2 atmosphere -
FIG. 8 —Isothermal TGA weight loss curves of RFL100SE and RFL100SB at 180° C. and 220° C. analysed in N2 atmosphere -
FIG. 9 —DSC curves of RFL40S -
FIG. 10 —DSC heating and cooling curves of RFL100SB -
FIG. 11 —DSC heating and cooling curves of RFL100SE -
FIG. 12 —Tensile strength of reference PP and PP-Renol compounds -
FIG. 13 —Tensile modulus of reference PP and PP-Renol compounds -
FIG. 14 —Elongation at yield of reference PP and PP-Renol compounds -
FIG. 15 —Impact strength of reference PP and PP-Renol compounds -
FIG. 16 —Schematic view of possible linker groups -
FIG. 17 —Schematic view of lignin modified with a quaternary ammonium -
FIG. 18 —Schematic view of lignin -
FIG. 19 —shows a schematic view of the functionalized lignin according to present invention. - In the present application the term “lignin” means a polymer comprising coumaryl alcohol, coniferyl alcohol and sinapyl alcohol monomers.
FIG. 18 discloses a schematic picture of a part of lignin. - In the present application the term “linker” or “linker group” are used interchangeably and means any group which can connect lignin with an alkyl containing group. Non-limiting examples of a linker is ester, ether, amide and carbamide.
- In the present application the term “compatibilizer” denotes a compound that promotes adhesion between polymers which otherwise are less compatible.
- Compatibilizers are widely used to increase the miscibility of otherwise immiscible polymers or polymers that do not mix so well.
- Lignin
- The lignin according to the present invention is obtained from any suitable biomass. A schematic structure of lignin is seen in
FIG. 18 . The biomass may be treated with pulping processes or organosolv processes for example. Biomass includes, but is not limited to wood, fruits, vegetables, processing waste, chaff, grain, grasses, corn, corn husks, weeds, aquatic plants, hay, paper, paper products, recycled paper, shell, brown coal, algae, straw, bark or nut shells, lignocellulosic material, lignin and any cellulose containing biological material or material of biological origin. In one embodiment the biomass is wood, preferably particulate wood such as saw dust or wood chips. The wood may be any kind of wood, hard or soft wood, coniferous tree or broad-leaf tree. A non-limiting list of woods would be pine, birch, spruce, maple, ash, mountain ash, redwood, alder, elm, oak, larch, yew, chestnut, olive, cypress, banyan, sycamore, cherry, apple, pear, hawthorn, magnolia, sequoia, walnut, karri, coolabah and beech. - It is preferred that the biomass contains as much lignin as possible. The Kappa number estimates the amount of chemicals required during bleaching of wood pulp in order to obtain a pulp with a given degree of whiteness. Since the amount of bleach needed is related to the lignin content of the pulp, the Kappa number can be used to monitor the effectiveness of the lignin-extraction phase of the pulping process. It is approximately proportional to the residual lignin content of the pulp.
-
K≈c*l - K: Kappa number; c: constant≈6.57 (dependent on process and wood); l: lignin content in percent. The Kappa number is determined by ISO 302:2004. The kappa number may be 20 or higher, or 40 or higher, or 60 or higher. In one embodiment the kappa number is 10-100.
- The biomass material may be a mixture of biomass materials and in one embodiment the biomass material is black or red liquor, or materials obtained from black or red liquor. Black and red liquor contains cellulose, hemi cellulose and lignin and derivatives thereof. The composition according to the present invention may comprise black or red liquor, or lignin obtained from black or red liquor.
- Black liquor comprises four main groups of organic substances, around 30-45 weight % ligneous material, 25-35 weight % saccharine acids, about 10 weight % formic and acetic acid, 3-5 weight % extractives, about 1 weight % methanol, and many inorganic elements and sulphur. The exact composition of the liquor varies and depends on the cooking conditions in the production process and the feedstock. Red liquor comprises the ions from the sulfite process (calcium, sodium, magnesium or ammonium), sulfonated lignin, hemicellulose and low molecular resins.
- The lignin according to the present invention may be Kraft lignin (lignin obtained from the Kraft process), sulfonated lignin, Lignoboost® lignin, precipitated lignin, filtrated lignin, acetosolv lignin or organosolv lignin. In one embodiment the lignin is Kraft lignin, acetosolv lignin or organosolv lignin. In another embodiment the lignin is Kraft lignin. In another embodiment the lignin is organosolv lignin. In another embodiment the lignin obtained as residual material from ethanol production. The lignin may be in particulate form with a particle size of 5 mm or less, or 1 mm or less.
- Native lignin or Kraft lignin is not soluble in most organic solvents, fatty acids or oils. Instead prior art have presented various techniques to depolymerize and covert the depolymerized lignin into components soluble in the wanted media.
- The weight average molecular weight (mass) (Mw) of the lignin according to the present invention may be 30,000 g/mol or less, such as not more than 20,000 g/mol, or not more than 10,000 g/mol, or not more than 5,000 g/mol, or not more than 2,000 g/mol, but preferably higher than 1,000 g/mol, or higher than 1,200 g/mol, or higher than 1,500 g/mol. In one embodiment the number average molecular weight of the lignin is between 1,000 and 4,000 g/mol, or between 1,500 and 3,500 g/mol.
- Modified or Derivatized Lignin
- The lignin according to the present invention is modified or derivatized with an alkyl containing group. The alkyl containing group may be but is not limited to an alkyl group, an alkyl ester, an alkyl ether or any other group comprising an alkyl group or section or block. The alkyl containing group is connected to the lignin via a linker group which is derived from a hydroxyl group or connected to an aryl group on the lignin according to the following schematic chemical structures:
- where the lignin is schematically represented by the R″ and the aryl (structure 1 and 2) or aliphatic (structure 3) groups respectively, L and L′ are the linkers and R and R′ are the alkyl containing groups. Since lignin has aliphatic hydroxyl groups as well as aromatic hydroxyl groups the linker L may be at an aliphatic part of lignin (structure 3). The linker L′ may also be connected direct to the aryl group in lignin, i.e. not via a hydroxyl group (structure 2). R″ may be hydrogen, alkyl, aryl or alkoxy group or any other group found in lignin. The aryl group of the lignin may comprise more than one R″.
- The linker (L) may be an ether, ester, ketone, acetal, methylene, methyne, olefin, amide, thioester, thioether, imide, imidamide, carbamate, carbamothioic acid, sulfonyl, sulfonamide, silyl oxy, silyl ether, phenoxide, furan, phosphorous acid, quaternary ammonium or hetero cycles or any other group. In one embodiment the linker is ether. In one embodiment the linker is ester. In one embodiment the linker is ketone. In one embodiment the linker is acetal. In one embodiment the linker is methylene. In one embodiment the linker is methyne. In one embodiment the linker is olefin. In one embodiment the linker is amide. In one embodiment the linker is thioester. In one embodiment the linker is thioether. In one embodiment the linker is imide. In one embodiment the linker is imidamide. In one embodiment the linker is sulfonyl. In one embodiment the linker is quaternary ammonium. In one embodiment the linker L′ is a ketone. In one embodiment the linker L′ is an aldehyde.
FIG. 16 discloses a non-limiting list of possible linkers. InFIG. 16 the aryl groups represents lignin and the linker may be derived from an aliphatic hydroxyl group as well. Depending on the linking group and the linking agent the linker may be connected to the lignin chain at different parts such as via hydroxyl groups or the aryl groups.FIG. 19 shows a schematic view of the functionalized lignin according to present invention. - In one embodiment the lignin is modified with alkyl containing groups and where some of the alkyl containing groups are linked to the lignin via an ether linker and some of the alkyl containing groups are linked via an ester linker. The amount of ether linkages may be 10-90%, such as 20% or higher, or 40% or higher, or 60% or higher, or 90% or lower or 70% or lower of the total amount of linkers. In one embodiment the amount of ether linkages is 40-60%. The amount of ester linkages may be 10-90%, such as 20% or higher, or 40% or higher, or 60% or higher, or 90% or lower or 70% or lower of the total amount of linkers. In one embodiment the amount of ether linkages is 40-60%. By functionalizing using different linkers the functionalization will be less dependent on the availability of the functional group and reagents but still obtain a soluble and/or miscible lignin product. Using different linkers may also make the process and the final product cheaper due to that the amount of more expensive reagents may be reduced but still obtain a soluble and/or miscible product for example.
- When the lignin is bound to a quaternary ammonium the bond between the lignin and the quaternary ammonium is ionic. The quaternary ammonium may be any quaternary ammonium having the general formula
- where each R1 to R4 are individually selected from a hydrogen, alkyl, alkoxy alkyl, alkyl alkoxy alkyl or alkyl ester wherein at least one of R1 to R4 is alkyl, alkoxy alkyl, alkyl alkoxy alkyl or alkyl ester. In one embodiment R1 is a methyl group or hydrogen. In another embodiment each R2 to R4 are alkyl groups. In one embodiment each R2 to R4 comprises a C6 or longer alkyl group, or a C12 or longer alkyl group. In one embodiment comprises R3 and R4 a C12 or longer alkyl group.
- In one embodiment the quaternary ammonium is a [alkyl]2N(CH3)2 + or [alkyl ester]2N(CH3)2 + or [alkyl]3N(CH3)+ or [alkyl ester]3N(CH3)+ where the alkyl is a C7 or longer alkyl. In one embodiment the counter ion to the quaternary ammonium is not chloride. In another embodiment the counter ion is HSO4. In another embodiment the quaternary ammonium is tricaprylylmethyl ammonium chloride, [CH3(CH2)17]2N(CH3)2HSO4, (CH3(CH2) s)2N+(CH3)2)Cl−, [CH3(CH2)7]3NCH3Cl, or [alkyl]2N(CH3)2HSO4 or [alkyl ester]2N(CH3)2HSO4.
FIG. 17 discloses a schematic picture of lignin modified with a quaternary ammonium. - The alkyl section of the alkyl containing group of the modified lignin may be a C1 or longer alkyl group, such as or C2 or longer, or a C3 or longer group, or C4 or longer, or C5 or longer, or C6 or longer, or C7 or longer, or C8 or longer, or C9 or longer, or C10 or longer, or C12 or longer, or C14 or longer, or C16 or longer, or C18 or longer. In one embodiment the alkyl containing group is a C14-C18 alkyl group. In one embodiment the alkyl containing group is an alkyl group. In one embodiment the alkyl containing group is derived from fatty acid methyl ester (FAME). The fatty acid methyl ester (FAME) is preferably unsaturated. The FAME may be derived from vegetable oils such as palm, soybean, rapeseed, sunflower, peanut, cottonseed, palm kernel, coconut or olive oil. FAME obtained from natural sources such as plants, vegetables or animals is usually a mixture of fatty acid compounds having different length such as C14-C20. In one embodiment a majority of the fatty acid methyl esters is a C14-C18 unsaturated fatty acid methyl ester. In one embodiment the FAME is methyl cis-9-octadecanoate or the FAME is a mixture comprising methyl cis-9-octadecanoate.
- The degree of modification of the hydroxyl groups expressed as number of equivalents to lignin repeating units. The number of equivalents may be 0.2 or higher, or 0.4 or higher, or 0.6 or higher, or 0.8 or higher. In this application the repeating unit of lignin is assumed to have a molecular weight of 180 g/mol. The degree of modification of the lignin when the lignin is modified via an ether linkage may be quite low and still be miscible with the first polymer. In one embodiment the number of equivalents may be 0.05-0.2, such as 0.1-0.15.
- An advantage of the modified lignin according to the present invention is its thermal stability. In one embodiment the modified lignin is thermally stable at temperatures of at least 150° C., or at least 180° C., or at least 200° C., or at least 220° C., or at least 240° C.
- The modified lignin according to the present invention may have a weight average molecular weight (Mw) of 1,000 g/mol or higher, or 1,200 g/mol or higher, or 1,500 g/mol or higher, or 1,800 g/mol or higher, or 2,000 g/mol or higher, or 2,500 g/mol or higher, or 3,500 g/mol or higher but less than 10,000 g/mol, or less than 6,000 g/mol. In one embodiment the number average molecular weight (Mn) is 1,500 to 4,000 g/mol, or 2,200 g/mol to 3,700 g/mol.
- Molecular weight in the present application is determined using GPC (Gel Permeation Chromatography) operated at 20° C. and at flow rate of 1 ml/min using THF as solvent. Polystyrene Standard RedayCal Set M(p) 250-70000 (16 standards) (Sigma product no: 76552). The colons are Styragel THF (pre-colon),
Styragel HR 3 THF (7.8×300 mm), Styragel HR 1 THF (7.8×300 mm), Styragel HR 0.5 THF (7.8×300 mm) all from Waters. - Preparation of the Lignin
- The present inventors found that by alkylating the hydroxyl groups or other parts of the lignin the miscibility of the lignin in other polymers increased drastically. The preparation of the modified lignin has been described in detail in PCT/SE2016/050584, WO2015094099 and WO2016072915 which are hereby incorporated by reference.
- The material according to the present invention may be prepared by first preparing the lignin that is modified or derivatized with an alkyl containing group via a linker followed by mixing said modified lignin with the first polymer. The modification may be done in a suitable solvent. The modified lignin may be isolated from the modification reaction mixture or the modified lignin may be left in the reaction mixture when mixed with the first polymer. The mixing can be done by stirring or shaking or in any other suitable way and the slurry is then heated. Any catalyst and any other unwanted components may be removed afterwards using any suitable technique.
- The modification may be performed at 50° C. and 350° C., such as 50° C. or higher, or 80° C. or higher or 100° C. or higher, or 120° C. or higher, or 150° C. or higher, but not higher than 350° C., or 250° C. or lower, or 200° C. or lower, or 180° C. or lower.
- When the linker is an ester group the modification agent may be a carboxylic acid or an anhydride. The esterification of the lignin may be performed in a suitable solvent leaving a homogenous composition of solvent and esterified lignin, and optionally catalyst. When the esterification is performed in a fatty acid and together with an esterification agent such as an anhydride the obtained esterified lignin is believed to comprise ester groups derived from the anhydride alone but also ester groups derived from an anhydride bond to a first fatty acid. In order to remove any acid groups of remaining fatty acids any suitable method may be used. For example an alcohol such as methanol may be added.
- The esterified lignin may be isolated by precipitation in for example hexane or water. When the degree of substitution (esterification) is high, for example 50% or more, and the lignin is substituted with C2-C4 ester groups the esterified lignin may be treated with a base for example NaHCO3 (aq.) before precipitation in order to remove free acid. When the lignin is substituted with longer ester groups celite may be used. The esterified lignin according to the present invention may also be separated from metals and other additives or catalysts by simply rinsing the lignin in an aqueous solution or water. For many industries the amount of metals should be as low as possible since metals may damage the machinery or disturb the process.
- The esterification agent may be a carboxylic acid or an anhydride. The esterification agents preferably contain an unsaturated bond. Non-limiting examples of carboxylic acids are fatty acids or C2-C42 carboxylic esters, preferably C4 to C22 such as C18, and non-limiting examples of anhydrides are C4 to C42 anhydrides. The ester groups may therefore be C2-C42 or C4-C42 preferably C4-C22 such as C18. Another important factor is the availability and the cost of the esterification agent. The catalyst for the esterification may be a nitrogen containing aromatic heterocycle such as N-methyl imidazole or pyridine, or the catalyst may be a metal acetylacetonate such as TiO(acac)2 or Fe(acac)3. In one embodiment the catalyst is DMAP (4-dimethylaminopryidine). Esterification may also be done by transesterification.
- When the linker is an ether group the modification agent may be an epoxide. In one embodiment the epoxide is an alkyl epoxide for example a C5 or longer alkyl epoxide, or a C12 or longer alkyl epoxide, or C18 or longer alkyl epoxide. In one embodiment the epoxide is a fatty acid epoxide such as fatty acid methyl ester (FAME). The fatty acid methyl ester (FAME) is preferably unsaturated. In one embodiment the fatty acid methyl ester is a C14-C20 unsaturated fatty acid methyl ester. In one embodiment the FAME epoxide is methyl cis-9-octadecanoate epoxide or the FAME epoxide is a mixture comprising methyl cis-9-octadecanoate epoxide.
FIG. 19b shows a schematic view over a modified lignin where the modification has been done for example via an epoxy group on for example a fatty acid. This epoxy group is formed via the unsaturated bond found in for example FAME using well known chemistry. The etherification may be performed at 80° C. or higher, or 120° C. or higher, or 150° C. or higher, or 180° C. or higher, preferably at 350° C. or lower, or at 250° C. or lower, or at 200° C. or lower. The etherification of the lignin may be done in a suitable solvent forming a homogenous composition of solvent and ether functionalized lignin, and optionally catalyst. The catalyst and any other unwanted components may be removed afterwards. - The etherification may be done by first mixing the lignin with an amine forming a first mixture and then heating the first mixture. To the first mixture an epoxide is then added and a second mixture is obtained which is then heated. The formed ether functionalized lignin is then mixed with the first polymer in order to form the material according to the present invention. The amine may be an alkyl amine for example a C5 or longer alkyl amine, or a C12 or longer alkyl amine. In one embodiment the amine is dodecylamine. The temperature at which the first and the second mixtures are heated may be 100° C. or higher, or 150° C. or higher, or 180° C. or higher. The mixture may be pressurized or refluxed. The amine may be added in a 2:1 to 0.5:1 weight ratio to the lignin, such as 1.10:1 to 0.90:1 or close to 1:1. The epoxide may be added in a 2:1 to 0.5:1 weight ratio to the first mixture, such as 1.10:1 to 0.90:1 or close to 1:1.
- The etherification may also be done by mixing lignin with a primary or a secondary epoxide forming a first mixture and then heating the first mixture. To the first mixture may an anhydride be added forming a second mixture which is then heated. The primary or secondary epoxide may be an alkyl epoxide for example a C5 or longer alkyl epoxide, or a C12 or longer alkyl epoxide, or C18 or longer alkyl epoxide. In one embodiment the alkyl epoxide is a C5-C18, or a C6-C14, or a C8-C12. In one embodiment the epoxide is a fatty acid epoxide. The anhydride may be a C4-C10 anhydride. The temperature at which the first and the second mixtures are heated may be 100° C. or higher, or 150° C. or higher, or 180° C. or higher. The mixture may be pressurized or refluxed. The epoxide may be added in a 2:1 to 0.5:1 weight ratio to the first mixture, such as 1.10:1 to 0.90:1 or close to 1:1. The anhydride may be added in a 2:1 to 0.5:1 weight ratio to the lignin. The etherified lignin may be further purified by recrystallization.
- When the lignin is functionalized via both ester and ether linkers the etherification is preferably done before the esterification.
- When the linker is a quaternary ammonium the modified lignin may be prepared by mixing the lignin and the quaternary ammonium salt during heating, optionally together with a solvent, followed by adding the oil and mixing. The obtained mixture may be washed using water or acid. By using quaternary ammonium as a linker lignosulfonate may be brought into solution in various solvents.
- The hydroxyl groups of lignin may be divided into aliphatic hydroxyls (ROH), condensed phenol (PhOH), phenol and acids. The degree of substitution, i.e. the degree of hydroxyl groups that has been converted into ester groups, may be from 10% to 100%, for example 20% or more, 30% or more, or 40% or more, or 60% or more or 80% or more, or 99% or more, or 100%. When the solvent comprises an organic solvent the degree of substitution does not have to be as high, for example 10-60% or 20-40%.
- One advantage of the present invention is that a higher amount of lignin may be dissolved in a solvent and in many different solvents and thereby facilitating blending or mixing the lignin with various polymers. The amount of lignin in the composition or mixture may be 1 weight % or more, or 2 weight % or more, or 4 weight % or more, or 5 weight % or more, or 7 weight % or more, or 10 weight % or more, or 12 weight % or more, or 15 weight % or more, or 20 weight % or more, or 25 weight % or more, or 30 weight % or more, or 40 weight % or more, or 50 weight % or more, or 60 weight % or more, or 70 weight % or more, or 75 weight % or more. In one embodiment the lignin content is 10-40 weight % such as 15-35 weight %.
- In one embodiment the lignin is dearomatized. For example the lignin is dearomatized to at least 40%, or at least 50%, or at least 60%, or at least 70%, or at least 80%, or at least 90%, or at least 95%, or at least 99%.
- The Material
- The present invention relates to a material comprising a first polymer and a second polymer wherein the first polymer is a natural or a synthetic polymer and the second polymer is modified lignin. The modification of the modified lignin is done by alkylation of the lignin via a linker wherein the linker is selected from an ether, ester, ketone, acetal, methylene, methyne, olefin, amide, thioester, thioether, imide, imidamide, carbamate, carbamothioic acid, sulfonyl, sulfonamide, silyl oxy, silyl ether, phenoxide, furan, phosphorous acid, quaternary ammonium or hetero cycles
- In one embodiment the material comprises a first polymer and a second polymer wherein the first polymer is a natural or a synthetic polymer and the second polymer is modified lignin; wherein the modified lignin is modified with an alkyl containing group via linker wherein the linker is an ether group and wherein the alkyl containing group is derived from fatty acid methyl ester.
- It was unexpected that the polymeric material according to the present invention could be processed so well. Additionally no compatibilizer was needed which makes the material less expensive and more environmentally friendly. The amount of any additional compatibilizer may be 7 wt % or less, or 5 wt % or less, or 3 wt % or less, or 2 wt % or less, or 1 wt % or less, or 0.5 wt % or less. In one embodiment the material is essentially free from any additional compatibilizer.
- The first polymer may be any suitable natural or synthetic polymer. In one embodiment the polymer is a polyolefin such as polyethylene or polypropylene. In another embodiment the first polymer is a polyester such as polyethylene terephthalate. In another embodiment the first polymer is a polynitrile such as polyacrylonitrile (PAN). In another embodiment the first polymer is a polycarbonate.
- The amount of first polymer in the material may be 1-99 wt %, such as 3 wt % or more, or 5 wt % or more, or 10 wt % or more, or 15 wt % or more, or 20 wt % or more, or 25 wt % or more, or 30 wt or more, or 35 wt % or more, or 40 wt % or more, or 45 wt % or more, or 50 wt % or more, or 90 wt % or less, or 85 wt % or less, or 80 wt % or less, or 75 wt % or less, or 70 wt % or less, or 65 wt % or less, or 60 wt % or less.
- The amount of modified lignin in the material may be 1-99 wt %, such as 3 wt % or more, or 5 wt % or more, or 10 wt % or more, or 15 wt % or more, or 20 wt % or more, or 25 wt % or more, or 30 wt or more, or 35 wt % or more, or 40 wt % or more, or 45 wt % or more, or 50 wt % or more, or 90 wt % or less, or 85 wt % or less, or 80 wt % or less, or 75 wt % or less, or 70 wt % or less, or 65 wt % or less, or 60 wt % or less.
- In one embodiment the material comprises a polyolefin such as polypropylene and modified lignin; wherein the modified lignin is either modified with an alkyl containing group via a linker wherein the linker is an ether group and wherein the alkyl containing group is derived from fatty acid methyl ester, or wherein the modified lignin is modified with a fatty acid via an ester group; and wherein the amount of polyolefin is 70-90 wt % such as 75-85 wt % and wherein the amount of modified lignin is 10-30 wt % such as 15-25 wt %.
- In another embodiment the material comprises a polyester such as polyethylene terephtalate and modified lignin; wherein the modified lignin is either modified with an alkyl containing group via a linker wherein the linker is an ether group and wherein the alkyl containing group is derived from fatty acid methyl ester, or wherein the modified lignin is modified with a fatty acid via an ester group; and wherein the amount of polyester is 70-95 wt % such as 80-90 wt % and wherein the amount of modified lignin is 5-30 wt % such as 10-20 wt %.
- In yet another embodiment the material comprises a polynitrile such as polyacrylonitrile (PAN) and modified lignin; wherein the modified lignin is either modified with an alkyl containing group via a linker wherein the linker is an ether group and wherein the alkyl containing group is derived from fatty acid methyl ester, or wherein the modified lignin is modified with a fatty acid via an ester group; and wherein the amount of polynitrile is 40-60 wt % such as 45-55 wt % or 50 wt % and wherein the amount of modified lignin is 40-60 wt % such as 45-55 wt % or 50 wt %.
- The obtained material of the modified lignin and the polyolefin, such as polypropylene, or the polyester showed very good mechanical properties.
- A study showed that the material could be processed through extrusion and injection moulding without any problem, even without any added compatibilizer. The modified lignin could be compounded together with the first polymer followed by extrusion at sufficiently high temperatures such as at 180-250° C. The extrusion can be done using a twin screw extruder. The obtained extruded product may be turned into pellets or powder which may then be dried using any suitable technique.
- Injection moulding of the present material may also be done at temperatures above 180° C. or even at 200° C. or higher without any increase in viscosity or pressure. In one embodiment the temperature is 180-250° C. The starting material for the injection moulding may be the pellets or powder obtained from the extrusion described above. Injection moulding facilitates that the more complex shapes and structures may be prepared from the present material.
- An additional advantage of the present material is that it has a pleasant smell.
- Applications
- The present modified lignin may be used as a compatibilizer. The modified lignin may be mixed with polymers or mixtures of polymers in solution, dry state or in melt. The polymers may be a polyolefin, polyester or a polynitrile. The amount of modified lignin may be 0.1-10 wt %, such as 0.5-5 wt %.
- 1. Renol Preparation
- 1.1 an Example of how to Prepare Renol of Esterified Lignin—Stearic Acid Esters.
- Full substitution: According to the general procedure of esterification, following amounts were used: Lignin type A2 (1.00 g, 1 eq.), stearic anhydride (6.12 g, 2 eq.), 1-methylimidazole (0.1 ml) and dioxane (15 ml). For purification, celite (50 g) was used with 0.5 M solution of NaHCO3 (400 ml). Some tetrahydrofuran was added to wet the celite. The ester was washed off with neat hexane to give 1.97 g of stearic acid ester as a brown solid.
- Partial substitutions: According to the general procedure of esterification, following amounts were used: Lignin type A2 (1.00 g, 1 eq.), stearic anhydride (0.31 or 0.92 g, 0.1 or 0.3 eq.), 1-methylimidazole (0.1 ml) and dioxane (10 ml). After the reaction the esters were purified according to the general purification of partially substituted esters. 0.1 and 0.3-eq. reactions afforded 1.12 g and 1.01 g respectively of the corresponding esters as brown powders.
- 1.2 an Example of how to Prepare Renol of Etherified Lignin
- The general procedure is
-
- adding Kraft lignin 0.25 g, epoxide 0.25 g to a 25 ml microwave vial
- capping the vial and flush with nitrogen for 10 min
- stir the solution mixture at 150° C. under nitrogen for 14 h
- dissolve with
toluene 20 ml and then centrifuge - dissolve toluene-insoluble material with chloroform and then filter.
- To acid precipitated lignin from black liquor was a primary epoxide (C18) added in a 1:3.8 weight % proportion (lignin:epoxide) forming a mixture and heated at 150 or 200° C., respectively, for 5 hours.
- The obtained etherified lignin may be further purified by recrystallization.
- 1.3 Preparation of Modified Lignin, Ether
- FAME-epoxide (methyl cis-9-octadecanoate, 600.0 g) was added to pre-dried (at 60° C. over night) Kraft lignin (600.0 g). The suspension was stirred mechanically and heated in an oil bath at 50° C. and the reaction flask was evacuated to 20 mbar. The temperature of oil bath was increased to 190° C. over 2 hours. After 45 min at 190° C. more FAME-epoxide (130.0 g) was added and heating at reduced pressure was continued for 1 hour. The product was poured out while hot on a stainless-steel plate and cooled to room temperature to give 1232.8 g of a dark brown brittle material.
- The product was crushed to smaller pieces and dissolved overnight in ethyl acetate (1.5 L) on a shaker after which pentane (5.0 L) was added in a steady stream while vigorously stirring the solution. The obtained suspension was filtered and the obtained cake was washed in portions with pentane (totally 3.0 L). After drying at room temperature in air 692.0 g of product was obtained as a light brown powder.
- 1.4 Preparation of Modified Lignin, Ether
- FAME-epoxide (methyl cis-9-octadecanoate, 250.0 g) was added to pre-dried (at 60° C. over night) Kraft lignin (162.5 g). The suspension was stirred mechanically and heated in an oil bath at 50° C. and the reaction flask was evacuated to 20 mbar. The temperature of oil bath was increased to 190° C. over 2 hours. After 45 min at 190° C. more FAME-epoxide (130.0 g) was added and heating at reduced pressure was continued for 1 hour. The product was poured out while hot on a stainless-steel plate and cooled to room temperature to give 1232.8 g of a dark brown brittle material.
- The product was washed with water four times during heating and stirring and then dried.
- 2. Characterization
- 2.1 Materials
- Four different grades of Renol® (modified lignin) were received from RenFuel AB. The general characteristics of Renol® are presented in Table 1.
- 2.2 Methods
- 2.2.1 Thermogravimetric Analysis (TGA)
- Thermogravimetric analysis (TGA) on Renol samples was carried out using Q500 from TA instruments. In this method, change in the mass of the materials is measured as a function of the temperature or time while the test specimen is subjected to a controlled temperature program in air or nitrogen atmosphere. Thermograms obtained from TGA analysis provides the information related to the thermal stability of material. About 20 mg of the sample is subjected for TGA analysis. TGA analysis was performed on the samples between room temperature and 550° C. with heating rate of 10° C./min in both air and nitrogen atmospheres.
- 2.2.2 Differential Scanning Calorimetry (DSC)
- Differential Scanning Calorimetry (DSC) on the Renol samples was performed using Netzsch 204-F1 instrument. DSC technique is used to determine glass transition temperature, melting and crystallization behaviour of material subjected to heat under controlled temperature program and atmosphere. About 3-4 mg of the powdered sample was subjected for DSC analysis. The analysis involved 3 cycles of heating and cooling cycles in the following order, 1. Heating the sample from room temperature to 150° C., 2. Cooling from 150° C. to −10° C. and 3. Heating the sample from −10° C. to 150° C. with heating and cooling rate of 10° C./min.
-
TABLE 1 General characteristics of Renol received from RenFuel AB 100% 100% Property/ Renol 20% 40% derivatised derivatised grade lignin lignin lignin lignin Derivatisation Oleic acid Oleic acid Stearic acid fatty acid w/etherification Code RFL20L RFL40S RFL100SA & RFL100SE-II RFL100SB Physical state Liquid Semi-solid/ Solid, Solid, highly viscous powder powder Composition 20:80 40:80 Stearic acid Etherified [Lignin: [Lignin: ester of lignin Oleic acid] Oleic acid] lignin Solvent Oleic acid Oleic acid None None Functional Aliphatic Aliphatic Esters Ether groups and aromatic and aromatic Aliphatic hydroxyls, hydroxyls, hydroxyls carboxylic carboxylic (from ring acid, ester, acid, ester, opening of double double epoxide) bonds, etc. bonds, etc. Other volatiles Acetic acid Acetic acid None None and catalyst and catalyst - 2.3 Results and Discussion
- 2.3.1 TGA of Ester Modified Renols
- TGA weight loss and derivative weight loss curves of RFL20L and RFL40S are presented in
FIG. 1 . The analysis was performed under air atmosphere. It is clear from the thermograms that the samples are undergoing two step thermal degradation. First step of thermal degradation occurs between 180-350° C. and the second one at above the 350° C. The first thermal degradation could be mainly due to oleic acid fraction and the second degradation is due to lignin fraction. Lignin is a complex macromolecule and is known to undergo thermal degradation in wide temperature range. - The size of the peak responsible for oleic acid fraction degradation in the derivative curve for RFL20L is larger than the RFL40L indicating higher fraction of oleic acid in RFL20L compared to RFL40S. Further, the size of the peak responsible for lignin in derivative curve for RFL40S is higher than the RFL20L indicating more lignin fraction in RFL40S compared to RFL40S.
- The residual mass obtained at end of the thermal analysis (@550° C.) for RFL20L and RFL40S respectively are 5.3% and 15.3% respectively. This means that RFL40S has about 10% higher residue after thermal analysis indication higher lignin content which generally produces char on thermal degradation. Some typical TGA characteristics such as temperature at 5% weight loss, onset of thermal degradation, residual mass, etc. are presented in Table 2.
- TGA weight loss and derivative weight loss curves of RFL40S subjected for thermal analysis in presence of air and N2 atmosphere are presented in
FIG. 2 (TGA weight loss and derivative weight loss curves of RFL40S). It can be noticed from the thermograms that the sample undergoes almost similar decomposition both in air and N2 atmospheres until 480° C. However, after 480° C., the sample analysed in N2 atmosphere showed no considerable weight loss whereas the sample analysed in air atmosphere showed gradual weight loss indicating further oxidative decomposition. -
TABLE 2 TGA characteristics of RFL20L and RFL40S materials (oleic acid derivatised Renols) Sample/ RLF20L RFL40S Characteristics Unit Air N2 Air N2 Temp at 5% weight ° C. 218 Not 218 213 loss analysed Start of ° C. 150 Not 150 120 decomposition analysed Onset of 1st ° C. 243 Not 212 207 decomposition analysed Delta weight of 1st wt-% 70 Not 37 34 component analysed Onset of 2nd ° C. 394 Not 400 387 decomposition analysed Residual @550° C. wt-% 5 Not 17 18 analysed - The TGA weight loss and derivative weight loss curves of RFL100SA and RFL100SB are presented in
FIG. 3 . The analysis was performed in duplicate under N2 atmosphere. It is clear from the thermograms that the two samples presented slightly different weight loss behaviour. Similar to RFL40S, both the samples presented two step degradation behaviour, one due to fatty acid fraction degradation between 180-350° C. and other one due to lignin degradation above 350° C. Among two samples, RFL100SA presented slightly higher thermal stability and thermograms of two parallels were very similar. On the other hand, RFL100SB observed to be slightly less thermal stable. In addition, the samples presented small weight loss at around 75 C due to loss of small volatile fraction. Further, the parallel samples presented slightly different weight loss curve for first degradation step indicating presence of fatty acid fraction slightly different among the samples. These results indicate the sample RFL100SB is slightly inhomogeneous with respect to fatty acid content. TGA characteristics of the samples is presented in Table 3. - 2.3.2 TGA of Ether Modified Renols
- The TGA weight loss and derivative weight loss curves of two parallel samples of RFL100SE-11 are presented in
FIG. 4 to 7 . -
FIG. 4 . The sample presented a weight loss in wide temperature range, 100-480° C. Above 480° C., the weight loss was not significant. Unlike other samples (ester modified lignins), RFL100SE presented weight loss in 3 steps. The first step of decomposition occurs between the temperature 100-300° C., the second decomposition occurs between 300-375° C. and last decomposition occurs between 375-475° C. First two decomposition steps could be due to ether components and last one could be due to the gradual decomposition due to part of lignin. Further, the amount of residue left on thermal decomposition of parallel samples is slightly different indication slight inhomogeneity in the samples. This could be obvious due to complex nature of lignin. TGA characteristics of the samples is presented in Table 3. -
TABLE 3 TGA characteristics of RFL100SA, RFL100SB and RFL100SE-II materials Sample/ RFL100SA RFL100SB RFL100SE-II Characteristics Unit N2 N2 N2 Temp at 5% ° C. 222 213 193 weight loss Start of ° C. 135 146 100 decomposition Onset of 1st ° C. 226 215 205 decomposition Delta weight wt-% 40 40/45 34 of 1st component Onset of 2nd ° C. 379 359/416 314/376 decomposition Residual @550° C. wt-% 19 14/25 24/28 - The TGA weight loss and derivative weight loss curves of RFL100SE in comparison to RFL100SA and RFL100SB are presented in
FIG. 5 . Different thermal degradation behaviour of ether modified lignin is clearly seen inFIG. 5 in comparison to ester modified lignin indicating ether modified lignin is different in composition compared to ester modified lignin. - 2.3.3 Isothermal TGA
- In order to understand the thermal stability of Renol samples better and in particular at processing temperatures of commodity polymers, isothermal TGA was also performed. Isothermal thermograms of parallel samples of RFL40S, RFL100SB and RFL100SE, analysed at 180° C. are presented in
FIG. 6 . On the other hand, RFL40S and RFL100SB presented similar isothermal weight loss curves. In case of RFL100SB, two parallels showed slightly different isothermal weight loss curves similar toFIG. 3 indicating inhomogeneity. However, isothermal weight loss curves for RFL40S were quite same. When the isothermal weight loss curves are observed very closely, it takes about 5-8 minutes for 5% weight loss for RFL100SE. Whereas for RFL40S and RFL100SB, it takes about 20-25 minutes for same 5% weight loss under isothermal TGA at 180° C. - Isothermal TGA analysis was also performed at 220° C. on both RFL100SB and RFL100SE samples. The resulting isothermal weight loss curves of the samples is presented in the
FIGS. 7 and 8 .FIG. 1 —TGA weight loss and derivative weight loss curves of RFL20L and RFL40S analysed in air atmosphere -
FIG. 2 —TGA weight loss and derivative weight loss curves of RFL40S analysed in N2 and air atmosphere -
FIG. 3 —TGA weight loss and derivative weight loss curves of RFL100SA and RFL100SB analysed in N2 atmosphere -
FIG. 4 —TGA weight loss and derivative weight loss curves of RFL100SE analysed in N2 atmosphere -
FIG. 5 —TGA weight loss and derivative weight loss curves of RFL100SE in comparison to RFL100SA and RFL100SB analysed in N2 atmosphere -
FIG. 6 —Isothermal TGA weight loss curves of RFL40S, RFL100SE and RFL100SB at 180° C. analysed in N2 atmosphere -
FIG. 7 The isothermal weight loss behaviour of the samples was quite different at 220° C. compared to 180° C. Though the sample RFL100SE showed slightly higher initial weight loss, it was not very significant after 20 minutes of isothermal TGA at 220° C. whereas RFL100SB showed continuous weight loss until 30 minutes of isothermal TGA at 220° C. At end of 60 minutes of isothermal TGA at 220° C., the total weight loss in case of RFL100SE is lower than the RFL100SB. - The results of isothermal TGA are better visualized in
FIG. 8 where isothermal weight loss curves for analysis at 180° C. and 220° C. are presented. The isothermal weight loss for RFL100SB is reasonably low at 180° C. and significantly high at 220° C. indicating low thermal stability of the material at higher temperatures. In case of RFL100SE, the isothermal weight loss at 220° C. is not very significant compared to 180° C. - The results of isothermal TGA indicates that both Renols are suitable to process with commodity polymers such as PE and PP. The highest processing temperature for these materials is typically around 220° C. In addition, the residence time of the material in the barrel during extrusion processing is generally less than couple of minutes. Therefore, the decomposition of Renols during extrusion processing with PE and PP should be insignificant.
- 2.4 Differential Scanning Calorimetry (DSC)
- Differential Scanning Calorimetry (DSC) analysis was performed on selected Renol samples in order to determine glass transition temperature (if any), melt temperature and crystallization temperature. DSC curve of RFL40S is presented in
FIG. 9 . No significant transitions were observed in DSC curves but a small peak was observed in second heating curve at around 11° C. however, the responsible transition for this peak is not clear. - The DSC heating and cooling curves of RFL100SB and RFL100SE-II respectively presented in
FIG. 10 andFIG. 11 . Both Renol samples presented almost similar curves. No peak was observed for glass transition for both the materials. Unlike RFL40S, RFL100SB and RFL100SE Renol samples observed to be crystalline materials. The samples presented melt temperature at around 70° C. and recrystallization temperature at around 52° C. -
TABLE 4 Thermogravimetric analysis results of the ether modified Renols Property Unit RFL100SE-II Temp, at 5% weight loss ° C. 250 Start of decomposition ° C. 170 Onset of 1st decomposition ° C. 240 Delta Weight of 1st component Wt % 15 Onset of 2nd decomposition ° C. 326 Residual @550° C. Wt % 34 - Results:
- The weight loss curve of RFL100SE-II are presented in
FIG. 4 . It is clear from theFIG. 1 that the two parallel samples presented reasonably good reproducibility indicating the RFL100SE-II sample is homogeneous with respect to composition. - Table 1 presents the typical TGA analysis results for ether modified samples.
- 3. Materials
- 3.1 Renol Materials
- Based on the desktop study and the thermal analysis results, two types of Renol was used
-
- RFL100SB and
- RFL100SE-II
- One kilo of each of the two materials was used and was in completely dried form. No further drying was performed on the received materials.
- 3.2 Polypropylene (PP) Resin
- The polypropylene matrix utilized for the technical study is nucleated heterophasic copolymer “Polypropylene PPC10641” from Total Polymers. The resin has a melt flow of 44 g/10 min (230° C./2.16 kg) and density of 0.900 g/cm3. The material has a high fluidity, good mechanical properties and is suitable for high speed injection moulding of food packaging. The pellets were milled into a powder and later utilized in producing compounds with Renol samples.
- 3.3 Compatibilizer
- Maleic anhydride grafted polypropylene (MA-g-PP), Exxelor PO 1020 from Exxon Mobil Chemicals was investigated as a compatibilizer in the technical study of developing a polypropylene-Renol composites. Exxelor PO 1020 has high maleic anhydride content with melt flow of 110 g/10 min (190° C./1.2 kg) and density of 0.905 g/cm3. This compatibilizer is designed to develop composites of polypropylene with glass fibre or natural fibres, and the blends of polypropylene with other polar polymers. The compatibilizer is known to improve the interfacial adhesion between polypropylene and reinforcement leading to improved mechanical properties.
- 3.4 Preparing Material
- i. Compounding of Renols with PP
- Renol samples were compounded into PP by melt extrusion technique. Compositions of the different PP-Renol compounds prepared in this study are presented in Table 5.
- Procedure: The required amounts of milled PP, Renol and MA-g-PP are weighed and mixed well by using food processing blender. The mixture was melt extruded using twin screw Prism 16 extruder with L/D is equal to 25. The extrusion was performed at 180° C. and the screw speed of 500 rpm. The polymer string was cooled in water bath and pelletized. The compound pellets were dried at 110° C. for overnight to remove any absorbed moisture from the samples.
- ii. Injection Moulding
- The dried PP-Renol composite pellets were injection moulded into ISO standard specimens tensile testing and impact testing. Injection moulding was performed on Arburg injection moulding machine under ISO standard recommendations.
- iii. Tensile Property Testing
- Tensile testing on the PP-Renol composite samples was performed on Zwick Z010 according to ISO 527. A multipurpose type 1B injection moulded dog-bone specimens were utilized for testing. Five parallel measurements were made at room temperature. Tensile properties such as tensile strength, modulus, elongation at yield, etc. were measured from the stress-strain curves.
- iv. Impact Strength Testing
- Charpy impact strength on the PP-Renol samples was measured on Resilvis 125 Cryo according to ISO 179-1. A notched specimen was made from the injection moulded bars and utilized in testing. Five parallel measurements were made at room temperature. Amount of energy absorbed by the sample before it break were measured in addition to recording of type of failure such as C-complete, P-partial, and N-no break.
-
TABLE 5 Composition of the PP-Renol compounds made PP Renol Sl. resin loading Compatibilizer No Sample # (wt-%) Renol type (wt %) Compatibilizer loading (wt-%) 1 RLPP# 000100 NA — NA — (ref) 2 RLPP# 00178 RFL100SB 20 Exxelor 1020 2 3 RLPP# 00280 RFL100SB 20 NA — 4 RLPP# 00378 RFL100SE- 20 Exxelor 1020 2 II 5 RLPP# 00480 RFL100SE- 20 NA — II *Sl = sample, PP = polypropylene - 3.5 Results and Discussion
- All composite samples had a loading of 20 wt % Renol which was considered a “safe” filler loading. The main parameter that was varied was the compatibilizer. The purpose was to evaluate
-
- fit for processing
- need for compatibilizer
- 3.5.1 Processing
- Compounding trials of PP with Renol went smooth. No considerable viscosity build-up in extruder screw barrel and hence no increase in temperature in screw barrel was observed. In general, processing of plastics with fillers leads to high shear forces in the barrel which leads to increase in temperature of the barrel and difficulty in processing. However, during processing of Renols with PP no such observations were made. The PP-Renol composite pellets are obtained as brown coloured pellets obtained on compounding of PP with Renol. The brown colour on the PP-Renol compounds with RFL100SB were slightly less compared to the pellets obtained with RFL100SE-II.
- In order to investigate the mechanical properties of PP-Renol composite samples, the pellets were injection moulded into standard ISO dog-bone shaped specimens.
- When the specimens were closely observed, the dark colouration of PP-Renol composites in RFL100SE are less intense compared to RFL100SB (contrary to pellets). The test bars were homogeneously coloured (visual observation).
- 3.5.2 Mechanical Properties
- The tensile properties are shown in Table 6. Variation of tensile strength, modulus and elongation at yield for different samples respectively presented in
FIG. 13 Figure. The tensile strength of PP-Renol samples is slightly lower than (about 20%) the reference PP sample. Among the two types of Renols, ether-modified lignin presented slightly better tensile properties compared to ester-modified Renols. MA-g-PP compatibilizer has no or very little influence on the tensile strength PP-Renol samples. The tensile modulus of PP-ester Renol samples is lower than (about 30%) the reference PP. In case of ether-modified Renol-PP, the tensile modulus was in the order of reference PP. No influence of compatibilizer on tensile modulus was observed. The elongation at yield for PP-ester Renols is in the order of PP whereas PP-ether Renols was lower than (up to 74%) reference PP. The influence of compatibilizer on elongation properties was not significant. -
TABLE 6 Tensile modulus, tensile strength and elongation at yield of PP and PP- Renol compounds Tensile Tensile strength Elongation at modulus at yield yield Sl. (MPa) (MPa) (%) No Sample # Renol type Value STD Value STD Value STD 1 RLPP# 000None 1730 6 25.0 0.0 5.5 0.0 2 RLPP# 001Ester- 1200 3 20.3 0.0 5.9 0.0 modified 3 RLPP# 002Ester- 1200 4 20.0 0.0 5.9 0.0 modified 4 RLPP# 003Ether- 1730 5 23.8 0.0 2.3 0.0 modified 5 RLPP# 004Ether- 1740 5 22.3 0.1 2.0 0.0 modified - Impact properties of reference PP and PP-Renol compounds are presented in 7 and
FIG. 15 . Impact properties of PP-Renol are lower than (up to 57%) the reference PP. Utilization of MA-g-PP compatibilizer in PP-Renols slightly reduces the impact properties. -
TABLE 7 Impact strength of reference PP and PP-Renol compounds Impact strength @23° C. (KJ/m2) S1. No Sample # Value STD Comment on failure 1 RLPP# 0005.8 0.7 Complete break 2 RLPP# 0013.5 0.2 Complete break 3 RLPP# 0023.7 0.4 Complete break 4 RLPP# 0032.5 0.1 Complete break 5 RLPP# 0043.8 0.2 Complete break - 4. Injection Moulding
- A PP-Renol compound was made in 2.5 kg quantity for the
recipe RLPP # 002. As described in the earlier section, PP-Renol compound was produced by melt extrusion process. Milled PP and Renol was physically mixed first and later compounded in Prism 16 twin screw extruder. The resulting compound was injection moulded into a box/cup in both natural colour and green colour in Angel injection moulding machine. In order to produce cup in green colour, the PP-Renol compound was mixed with 5 wt-% green colour masterbatch based on polyethylene carrier and later injection moulded at 200° C. The demonstrator processing went very smooth. However, the smell of the boxes was slightly higher than the smell of the pellets produced during extrusion processing and test specimens produces by injection moulding. This strong smell of boxes could be due to slightly higher processing temperature (200° C.) compared to compounding temperature (180° C.). - 5. Polyester and Modified Lignin
- A granular sample of PET (1.60 g, Aldrich Chemistry prod. nr.: 429252), containing 30% glass particles as reinforcer, was melted under argon in a liquid sand bath at 280° C. To the melt was modified lignin (178 mg) obtained from Example 1.4 above added and mixed for 3 minutes. On cooling a uniform material was obtained.
- 6. Polyester and Modified Lignin
- A sample of PET (1.60 g, from a soft drink bottle) was melted under argon in a liquid sand bath at 280° C. To the melt was added modified lignin (400 mg) obtained from Example 2 above added and mixed for 3 minutes. On cooling a uniform material was obtained.
- 7. Polynitrile and Modified Lignin
- Modified lignin (obtained from Example 1.4 above), 40 mg, was mixed with 40 mg PAN (polyacrylonitrile) and 0.7 ml DMF and left during stirring at room temperature overnight. DMF was distilled off at 100° C. and vacuum (20 mbar).
Claims (15)
1. A polymeric material comprising a first polymer and a second polymer wherein the first polymer is a natural or a synthetic polymer and the second polymer is modified lignin;
wherein the modified lignin is modified by alkylation of the lignin via a linker
wherein the linker is an ester; wherein the esterification is obtained using an esterification agent wherein said esterification agent is a fatty acid containing an unsaturated bond.
2. The material according to claim 1 wherein the amount of modified lignin is 1-99 wt %, such as 3 wt % or more, or 5 wt % or more, or 10 wt % or more, or 15 wt % or more, or 20 wt % or more, or 25 wt % or more, or 30 wt or more, or 35 wt % or more, or 40 wt % or more, or 45 wt % or more, or 50 wt % or more, or 90 wt % or less, or 85 wt % or less, or 80 wt % or less, or 75 wt % or less, or 70 wt % or less, or 65 wt % or less, or 60 wt % or less.
3. The material according to any one of claims 1 to 2 wherein the first polymer is a polyolefin.
4. The material according to claim 3 wherein the polyolefin is polyethylene or polypropylene.
5. The material according to any one of claim 1 or 2 wherein the first polymer is a polyester such as polyethylene terephthalate or a polynitrile such as polyacrylonitrile (PAN), or a polycarbonate.
6. The material according to claim 3 wherein the amount of the first polymer is 1-99 wt %, such as 3 wt % or more, or 5 wt % or more, or 10 wt % or more, or 15 wt % or more, or 20 wt % or more, or 25 wt % or more, or 30 wt or more, or 35 wt % or more, or 40 wt % or more, or 45 wt % or more, or 50 wt % or more, or 90 wt % or less, or 85 wt % or less, or 80 wt % or less, or 75 wt % or less, or 70 wt % or less, or 65 wt % or less, or 60 wt % or less.
7. The material according to any one of the preceding claims wherein alkyl group is a C4 or longer alkyl groups such as a C6 or longer, or C8 or longer, or C10 or longer, or C12 or longer, or C14 or longer, or C16 or longer, or C18 or longer.
8. The material according to claim 1 wherein the alkyl group is a C14-C18 alkyl group.
9. The material according to any one of the preceding claims wherein the modified lignin is thermally stable at temperatures up to 150° C., or up to 180° C., or up to 200° C., or up to 220° C., or up to 240° C.
10. The material according to any one of the preceding claims wherein the lignin is Kraft lignin.
11. The material according to the present invention wherein the material does not contain any additional compatibilizer.
12. An extruded or injection moulded product comprising the polymeric material according to any one of claims 1 to 11 .
13. A compatibilizer for polymeric materials comprising modified lignin wherein the modified lignin is modified with an alkyl containing group via linker wherein the modified lignin is modified by alkylation of the lignin via a linker wherein the linker is an ester.
14. A method of extruding the material according to the present invention comprising:
mixing the first polymer and the second polymer and optionally a compatibilizer wherein the first polymer is a natural or a synthetic polymer and the second polymer is modified lignin; and
extruding the formed mixture at a temperature of at least 100° C., preferably at least 170° C. or at least 180° C.;
optionally cutting the extruded material into pellets; and
drying the obtained extruded material.
15. A method of injection moulding a product of the material according to the present invention wherein the method comprises:
providing pellets or powder of the present material; and
injection moulding the pellets or powder into a desired shape at a temperature of at least 100° C., or preferably at least 180° C. or at least 200° C.