US20180212259A1 - Fuel cell microseal and a method of manufacture thereof - Google Patents
Fuel cell microseal and a method of manufacture thereof Download PDFInfo
- Publication number
- US20180212259A1 US20180212259A1 US15/412,085 US201715412085A US2018212259A1 US 20180212259 A1 US20180212259 A1 US 20180212259A1 US 201715412085 A US201715412085 A US 201715412085A US 2018212259 A1 US2018212259 A1 US 2018212259A1
- Authority
- US
- United States
- Prior art keywords
- microseal
- metal bead
- substantially horizontal
- horizontal surface
- seal joint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A microseal for a metal bead seal joint includes a substantially horizontal surface, first and second substantially vertical surfaces disposed on opposite ends of the substantially horizontal surface, and a contoured surface operatively configured to adhere to a portion of a metal bead. The contoured surface may be disposed opposite the substantially horizontal surface and may be integral to the first and second substantially vertical surfaces. The substantially horizontal surface may be operatively configured to substantially maintain its horizontal surface orientation in both a compression state and a non-compression state.
Description
- The present disclosure relates to fuel cell microseals, and in particular, a fuel cell microseal to prevent buckling in the metal bead integrally formed into a fuel cell plate.
- Fuel cells are used as an electrical power source in many applications. In particular, fuel cells are proposed for use in automobiles to replace internal combustion engines. A commonly used fuel cell design uses a solid polymer electrolyte (SPE) membrane or proton exchange membrane (PEM), to provide ion transport between the anode and cathode.
- Fuel cells in general are electrochemical devices that convert the chemical energy of a fuel (hydrogen, methanol, etc.) and an oxidant (air or pure oxygen) in the presence of a catalyst into electricity, heat, and water. Fuel cells produce clean energy throughout the electrochemical conversion of the fuel. Therefore, they are environmentally friendly because of the zero or very low emissions. Moreover, fuel cells are high power systems, generating anywhere from a few watts to hundreds of kilowatts with efficiencies much higher than conventional internal combustion engines. Fuel cells also produce low noise because they have few moving parts.
- In proton exchange membrane fuel cells, hydrogen is supplied to the anode as fuel and oxygen is supplied to the cathode as the oxidant. The oxygen can either be in pure form (O2) or air (a mixture of O2 and N2). PEM fuel cells typically have a membrane electrode assembly (MEA) in which a solid polymer membrane has an anode catalyst on one face and a cathode catalyst on the opposite face. The anode and cathode layers of a typical PEM fuel cell are formed of porous conductive materials, such as woven graphite, graphitized sheets, or carbon paper to enable the fuel to disperse over the surface of the membrane facing the fuel supply electrode. Each electrode has finely divided catalyst particles (for example, platinum particles), supported on carbon particles, to promote oxidation of hydrogen at the anode and reduction of oxygen at the cathode. Protons flow from the anode through the ionically conductive polymer membrane to the cathode where they combine with oxygen to form water, which is discharged from the cell. The MEA is sandwiched between a pair of porous gas diffusion layers (“GDL”), which in turn are sandwiched between a pair of non-porous, electrically conductive elements or plates (i.e., flow field plates). The plates function as current collectors for the anode and the cathode and contain appropriate channels and openings formed therein for distributing the fuel cell's gaseous reactants over the surface of respective anode and cathode catalysts. In order to produce electricity efficiently, the polymer electrolyte membrane of a PEM fuel cell must be thin, chemically stable, proton transmissive, non-electrically conductive, and gas impermeable. In typical applications, individual fuel cells are stacked in series in order to provide the required level of electrical power.
- Embodiments of the conventional electrochemical cell also include hardware components, e.g., plates, for reactant flow separation, current collection, compression and cooling (or heating). A bipolar plate provides multiple functions: (a) distributes reactant flow at the anode or cathode, (b) collects electrical current from operating anode/cathode surfaces, and (c) prevents mixing or cross-over of the anode and cathode reactants in single cells. An assembly of two or more of these single cells is called a stack. A cooling plate (often integral with the bipolar plate) primarily distributes coolant flow in a stack. The number and sizing of single cells in a fuel cell stack is generally selected based on the system power requirements. For convenient assembly and/or dis-assembly of a fuel cell stack with large voltage or power output, multiple sub-stacks or modules, can be combined to form the stack. The modules represent stacks of single cells in some number less than what ultimately results in the completed stack, as is well understood by those of ordinary skill in the art. When the stack forms a PEM fuel cell, the stack is often referred to as a PEM stack.
- In a conventional PEM stack assembly, sealing of hardware components and active cells, for effective separation of anode and cathode reactant-flows and prevention of their leakage and intermixing, is a critical technical issue with direct impact on stack performance and reliability. These factors, in addition to sealing system design and design for manufacturability have a direct impact on the overall PEM fuel cell system cost.
- Leakage or cross-mixing of reactants and coolant between different cells and multiple elements of a single cell is conventionally prevented by compressive or adhesive seals, which in some instances make use of elastomeric and/or adhesive materials. For example, in U.S. Pat. No. 6,080,503, membrane electrode assembly (MEA) surfaces around the electro-active area are adhesively bonded together with support plates. The adhesive bond is formed of an adhesive agent that encapsulates the edge portion of the MEA. In another example, in U.S. Pat. No. 5,176,966, seals are formed by impregnating the backing layer (gas diffusion layer or GDL) of the electrodes with a sealant material (silicon rubber) which circumscribes the fluid-flow openings and the electro-active portion of the MEAs. Alternatively, the sealant material is deposited into the groves formed on the outer surface of the MEA electrodes; the grooves circumscribing the fluid-flow openings and the electro-active portions of the MEAs.
- Whether compressive or adhesive, the relevant materials are generally placed upon, fitted, formed or applied to the surfaces being sealed. These processes are labor intensive, costly, and not conducive to high volume manufacturing. The variability of these processes may also compromise reliability/durability of the seals, resulting in poor manufacturing yields. Additionally, for high temperature stack assemblies, these sealing processes and/or materials would have compatibility and/or durability issues due to highly concentrated acidic environments and/or high operating temperatures (e.g., 120° C. to 250° C.).
- An adhesive sealant based PEM stack assembly process has been described in a World Publication WO 02/43173 based on U.S. patent application Ser. No. 09/908,359, which involves three steps of sealant application to produce a resin-bonded (encapsulated) PEM stack. These three steps are: (1) sealing the unused manifold openings/ports on each of the fluid flow plates with flow-field structure (for example, on the cathode flow-field surface, ports for fuel and coolant flow are sealed about their perimeter to prevent the mixing of these input streams); (2) sealing all ports within the MEAs to prevent the leakage of reactants within the MEA layers; and (3) sealing a remainder of the desired seal surfaces in the stack assembly. The sealing of the remainder of seal surfaces involves layering of all the pre-sealed components within a mold or fixture, introduction of a curable resin (sealant) around the periphery, and forcing the resin into the stacked assembly (cassette) using vacuum transfer molding or injection molding technique. Once cured, the resin provides the structural support and edge sealing over the entire assembly. The resulting fuel cell cassette/stack is held between the compression plates with manifolding and means of compression.
- Further advancement of the three-step PEM stack/cassette assembly process is described in the U.S. Pat. No. 7,306,864, which can be conveniently utilized for high volume stack manufacturing using single-step injection molding. In this approach, all the stack components including support plates, plates for stack cooling, compression and current collection, and MEAs, are appropriately layered up and placed in a mold. The sealant material (2-part silicon or other adhesive resin) is forced into the intricate openings (using pressure or vacuum), while the stacked assembly is held under an optimal pressure for minimal resistance between each electrical contact surfaces. When the viscous sealant material fills all the desired sealing spaces (including MEA edges) including the space surrounding the stack assembly, the mold is placed in a low temperature oven to cure the resin. The encapsulated stack is then taken out from the mold.
- With reference to
FIG. 1A ,microseal material 124 is transferred to a metal bead 120 through ascreen 122. The final shape of thetraditional microseal 114 is controlled by bead shape (gravity), stencil design, ink viscosity, and surface energy. Unfortunately, as shown inFIG. 1B , when the metal bead buckles, seal contact is not guaranteed, especially in the center region where the metal bead 116 buckles. Failure to maintain seal contact reduces robustness against misalignment ofcenter axes 117 as shown inFIG. 1C . Given a set of metal properties and metal bead geometry including metal thickness specifications, it may not be possible to improve the buckling load of the metal bead sufficiently, by altering the metal form alone. - Accordingly, there is a need for a new fuel cell microseal design which may improve seal contact width and increase robustness against misalignment which further reduces the risk of developing leaks in the fuel cell.
- The present disclosure provides for a microseal for a metal bead seal joint in accordance with various embodiments. A first embodiment of the microseal may include a substantially horizontal surface, first and second substantially vertical surfaces disposed on opposite ends of the substantially horizontal surface and a contoured surface. The contoured surface may be disposed opposite the substantially horizontal surface and may be integral to the first and second substantially vertical surfaces. The substantially horizontal surface may be operatively configured to substantially maintain its substantially horizontal surface orientation in both a compressed state and an un-compressed state.
- A metal bead seal joint for a fuel cell plate, the metal bead seal joint includes a first metal bead having a first microseal and a second metal bead having a second microseal. The second metal bead having a second microseal may be compressed against at least a portion of the first microseal and the first metal bead. Each of the first and second microseals include a contoured surface adhered to each associated metal bead and a substantially horizontal surface disposed opposite to the contoured surface. The contoured surface and the substantially horizontal surface for each microseal (or first and second microseals) define a microseal thickness which may vary along the width of the microseal.
- The present disclosure and its particular features and advantages will become more apparent from the following detailed description considered with reference to the accompanying drawings.
- These and other features and advantages of the present disclosure will be apparent from the following detailed description, best mode, claims, and accompanying drawings in which:
-
FIG. 1A is a schematic cross-sectional view of a traditional microseal for a metal bead seal where the seal is applied to the bead via a stenciling process. -
FIG. 1B is a schematic cross-sectional view of the traditional microseal ofFIG. 1A when the bead and the seal are in compression. -
FIG. 1C is a schematic cross-sectional view of the traditional metal bead seal joint having the traditional microseals when the beads and the seals are misaligned, while not in compression. -
FIG. 2A is a schematic cross-sectional view of a first embodiment of a microseal in accordance to the present disclosure, where the metal bead and the microseal are not in compression. -
FIG. 2B is a schematic cross-sectional view of the first embodiment of a microseal inFIG. 2A , where the metal bead and the microseal are compressed. -
FIG. 3A is a schematic cross-sectional view of a microseal in accordance with a first embodiment manufacturing method of the present disclosure where the microseal material is applied to the metal bead. -
FIG. 3B is a schematic cross-sectional view of a microseal in accordance with a first embodiment manufacturing method of the present disclosure, where a load is evenly applied to the microseal material to form a substantially horizontal surface.FIG. 4A is a schematic cross-sectional view of a microseal in accordance to with a second embodiment manufacturing method of the present disclosure where the microseal material is applied to the metal bead in a first and a second application. -
FIG. 4B is a schematic cross-sectional view of a microseal in accordance with the second embodiment manufacturing method of the present disclosure where a substantially horizontal surface is formed in the microseal material. -
FIG. 5 is a schematic cross-sectional view of the traditional metal bead seal joint having the microseals in accordance with the various embodiments of the present disclosure where the beads and the seals are not in compression and misaligned. -
FIG. 6 is an example process flow chart which illustrates an example, non-limiting method of manufacturing the first embodiment microseal of the present disclosure. -
FIG. 7 is an example process flow chart which illustrates an example, non-limiting method of manufacturing the second embodiment microseal of the present disclosure. - Like reference numerals refer to like parts throughout the description of several views of the drawings.
- Reference will now be made in detail to presently preferred compositions, embodiments and methods of the present disclosure, which constitute the best modes of practicing the present disclosure presently known to the inventors. The figures are not necessarily to scale. However, it is to be understood that the disclosed embodiments are merely exemplary of the present disclosure that may be embodied in various and alternative forms. Therefore, specific details disclosed herein are not to be interpreted as limiting, but merely as a representative basis for any aspect of the present disclosure and/or as a representative basis for teaching one skilled in the art to variously employ the present disclosure.
- Except in the examples, or where otherwise expressly indicated, all numerical quantities in this description indicating amounts of material or conditions of reaction and/or use are to be understood as modified by the word “about” in describing the broadest scope of the present disclosure. Practice within the numerical limits stated is generally preferred. Also, unless expressly stated to the contrary: percent, “parts of,” and ratio values are by weight; the description of a group or class of materials as suitable or preferred for a given purpose in connection with the present disclosure implies that mixtures of any two or more of the members of the group or class are equally suitable or preferred; the first definition of an acronym or other abbreviation applies to all subsequent uses herein of the same abbreviation and applies mutatis mutandis to normal grammatical variations of the initially defined abbreviation; and, unless expressly stated to the contrary, measurement of a property is determined by the same technique as previously or later referenced for the same property.
- It is also to be understood that this present disclosure is not limited to the specific embodiments and methods described below, as specific components and/or conditions may, of course, vary. Furthermore, the terminology used herein is used only for the purpose of describing particular embodiments of the present disclosure and is not intended to be limiting in any way.
- It must also be noted that, as used in the specification and the appended claims, the singular form “a,” “an,” and “the” comprise plural referents unless the context clearly indicates otherwise. For example, reference to a component in the singular is intended to comprise a plurality of components.
- The term “comprising” is synonymous with “including,” “having,” “containing,” or “characterized by.” These terms are inclusive and open-ended and do not exclude additional, unrecited elements or method steps.
- The phrase “consisting of” excludes any element, step, or ingredient not specified in the claim. When this phrase appears in a clause of the body of a claim, rather than immediately following the preamble, it limits only the element set forth in that clause; other elements are not excluded from the claim as a whole.
- The phrase “consisting essentially of” limits the scope of a claim to the specified materials or steps, plus those that do not materially affect the basic and novel characteristic(s) of the claimed subject matter.
- The terms “comprising”, “consisting of”, and “consisting essentially of” can be alternatively used. Where one of these three terms is used, the presently disclosed and claimed subject matter can include the use of either of the other two terms.
- Throughout this application, where publications are referenced, the disclosures of these publications in their entireties are hereby incorporated by reference into this application to more fully describe the state of the art to which this present disclosure pertains.
- The following detailed description is merely exemplary in nature and is not intended to limit the present disclosure or the application and uses of the present disclosure. Furthermore, there is no intention to be bound by any theory presented in the preceding background or the following detailed description.
- With reference to
FIGS. 2A, 4B and 5 , the present disclosure provides for animproved microseal design 14 which better maintains the joint between metal beads in a fuel cell plate. As shown, themicroseal 14 includes a substantiallyhorizontal surface 22, first and substantially vertical surfaces and acontoured surface 32. The first substantiallyvertical surface 18 may be disposed afirst end 36 of the substantiallyhorizontal surface 22. The second substantiallyvertical surface 20 may be disposed at asecond end 38 of the substantiallyhorizontal surface 22. The contouredsurface 32 may be disposed opposite the substantiallyhorizontal surface 22 as shown in the aforementioned figures. The contouredsurface 32 is integral to the first and second substantiallyvertical surfaces vertical surfaces surface 32 is operatively configured to adhere to a portion of ametal bead 16 as themetal bead 16 is compressed as shown inFIG. 2B underload 19. - With reference to
FIG. 2A , amicroseal 14 according to various embodiments of the present disclosure is shown in an uncompressed state. The microseal material may be formed from any number of elastomer materials, including, but not limited to EPDM, HNBR, NBR, VMQ, FVMQ, and FKM, therefore, themicroseal 14 in general compresses when a load is applied.FIG. 2B illustrates themicroseal 14 under a compression load or in a compressed state. As shown in bothFIGS. 2A and 2B , the substantiallyhorizontal surface 22 is operatively configured to maintain a substantially flat surface orientation when subjected to a vertical load—in both the compressed state and the uncompressed state. The entire surface area of the contouredsurface 32 of themicroseal 14 is operatively configured to flex together with theimproved microseal 14 when aload 19 is applied as illustrated inFIGS. 2A and 2B . - The contoured
surface 32 and the substantiallyhorizontal surface 22 for allmicroseals 14 of the present disclosure define amicroseal thickness Microseal thickness 28 is the thickness in the uncompressed state whilemicroseal thickness 28′ is the thickness in the compressed state. As shown inFIG. 2A , themicroseal thickness 28 is greater at anedge region 26 than themicroseal thickness 28 at acenter region 30 in the uncompressed state. Theedge region 26 may be defined as the region of the microseal 14 which is proximate to each of the first and the second substantially vertical surfaces and thecenter region 30 may be disposed between theedge region 26 for the first substantiallyvertical surface 18 and theedge region 26 for the second substantiallyvertical surface 20. As shown inFIG. 2A andFIG. 5 , themicroseal thickness 28 varies along a width of the substantiallyhorizontal surface 22 when the microseal is initially disposed on themetal bead 16. Themicroseal thickness 28 is greater at or proximate to each of the first and second substantially vertical walls (edge region 26) than themicroseal thickness 28 in thecenter region 30 of the microseal. However, as shown inFIG. 2A , in the first embodiment design where themicroseal 14 is a molded part which may be affixed to ametal bead 16. - Referring now to
FIG. 5 , a metal bead seal joint 40 for a fuel cell plate is shown wherein microseals 14 ofFIGS. 2A and 2B are implemented. As shown, afirst metal bead 16 has afirst microseal 14 which is adhered to at least a portion of thefirst metal bead 16. Asecond metal bead 16′ having asecond microseal 14 is also shown wherein thesecond microseal 14′ which is adhered to at least a portion of thesecond metal bead 16′. Thesecond metal bead 16′ and thesecond microseal 14′ may be compressed against at least a portion of thefirst microseal 14 and thefirst metal bead 16. - The
microseals FIG. 5 similarly each include a substantiallyhorizontal surface 22, first and second substantiallyvertical surfaces contoured surface 32. The first substantiallyvertical surface 18 may be disposed at afirst end 36 of the substantiallyhorizontal surface 22 and the second substantiallyvertical surface 20 may be disposed at asecond end 38 of the substantiallyhorizontal surface 22. As shown, the contouredsurface 32 may be disposed opposite the substantiallyhorizontal surface 22 at the opposite ends 42 of the first and second substantiallyvertical surfaces surface 32 may be integral to the first and second substantiallyvertical surfaces - With reference to
FIG. 5 , themicroseal 14 ofFIG. 2A is shown in a metal bead seal joint 40 each of the first substantiallyhorizontal surfaces 22 are operatively configured to maintain a substantially flat orientation in a compressed state (shown inFIG. 2B andFIG. 5 ) as well as a non-compressed state (shown inFIG. 2A ). Accordingly, the metal bead seal joint 40 maintains contact between eachmetal bead metal beads FIG. 5 . As shown, each of the first and second substantiallyvertical surfaces surface 32 are operatively configured to have a surface orientation which may or may not change between the compression and non-compression states while the substantiallyhorizontal surface 22 maintains its orientation. It is understood that the orientation of the first and second substantiallyvertical surfaces surface 32 may change given that each contoured surface 32 (for the first andsecond microseals portion 44 of one of the first andsecond metal beads contoured surface 32 is operatively configured to flex as the first andsecond metal beads vertical surfaces metal bead FIG. 2B . - Accordingly, the new microseal shape (formed from the first and second
vertical surfaces surface 32 and the horizontal surface 22) more effectively distributes and transfers the vertical compressive load to the side-walls 23 in themetal bead 16. The redistribution of theload 19 keeps the “substantiallyhorizontal surface 22” of the microseal 14 “substantially horizontal” during compression. This improved load transfer and distribution then also increases the buckling load of the sealing joint 40. - Referring again to
FIG. 5 , each of the contouredsurface 32 and the substantiallyhorizontal surface 22 for each of the first andsecond microseals microseal thickness 28. Furthermore, themicroseal thickness 28 may vary along a width of themicroseal thickness 28 increases toward first and second edges of the seal (“edge regions 26”), and thethickness 28 in thecenter region 30 of themicroseal 14 is relatively lower to theedge regions 26. In compression,microseal thickness 28′ may still vary along thewidth 45. However, thethickness 28′ under compression may be less varied due to the compression (or vertical load). - With reference now to
FIG. 6 , afirst embodiment method 62 to manufacture amicroseal 14 is shown. Thefirst embodiment method 62 includes the steps of: (1) applying a first application of a microseal material to a metal bead wherein the microseal material is in aviscous state 70; (2) forming a substantially horizontal surface in themicroseal material 74; and (3) curing themicroseal material 78. These steps are shown in solid inFIG. 6 while the other steps are shown in phantom to indicate additional steps which may be implemented. - The additional steps for the
first embodiment method 62 may include: (1) partially curing the first application of themicroseal material 76; (2) applying a compression load across a width of the partially curedmicroseal material 72—thereby forming a substantially horizontal surface as described above—while continuing to cure the microseal material; (3) removing thecompression load 78; and (4) fully curing the first application of the microseal material thereby forming amicroseal 80. - With reference to
FIGS. 3A and 3B , themicroseal 14 is shown according to the first embodiment method of manufacture. As shown inFIG. 3A , themicroseal material 24 produced under the first embodiment method of manufacture (shown inFIG. 6 ) is initially applied to the metal bead in a liquid or viscous state optionally via ascreen mesh stencil 50. Upon initial application and due to its viscous nature, thetop surface 48 is not initially substantially horizontal (or straight) as shown inFIG. 2A . Themicroseal material 24 is allowed to partially cure so that themicroseal material 24 is in a gel-like state. Once the gel-like state is achieved, a compression load (or plate) 46 may be applied evenly across thetop surface 48 of themicroseal material 24 thereby forming a substantiallyhorizontal surface 22 as shown inFIG. 3B . As described, theload 46 shown inFIG. 3B may be maintained while themicroseal material 24 continues to cure or until themicroseal material 24 is fully cured as shown inFIG. 6 . In themicroseal 14 ofFIG. 3B , the substantiallyvertical surfaces - With reference to
FIG. 7 , asecond embodiment method 62′ to manufacture a fuel cell microseal includes the steps of: (1) applying a first application of a microseal material to a metal bead wherein the microseal material is in aviscous state 82; (2) applying a second application of the microseal material to the metal bead adjacent to the first application of the microseal material wherein the microseal material from the first and second applications are in aviscous state 84; (3) forming a substantially horizontal surface in themicroseal material 86; and (4) curing themicroseal material 88. It is understood that in the step of forming a substantially horizontal surface instep 86, the first and second applications of microseal material (elements FIG. 4A ) are operatively configured to flow toward one another thereby forming the substantially horizontal surface 22 (shown inFIG. 4B ). - With reference to
FIG. 4A , the first andsecond applications viscous microseal material 24 are illustrated where thefirst application 52 and thesecond application 54 are adjacent to each other. InFIG. 4A , ascreen 50 is used to feed themicroseal material 24 onto themetal bead 16.FIG. 4B illustrates theend resulting microseal 14 once the first andsecond applications horizontal surface 22. It is to be understood that the end resulting microseals 14 inFIGS. 2A, 3B, and 4A have the same or similar configurations wherein themicroseal thickness 28 varies along a width 56 of the substantiallyhorizontal surface 22 when themicroseal 14 is disposed on themetal bead 16 in a non-compressed state (shown inFIGS. 2A and 4B ). Themicroseal thickness 28 is greater at or proximate to each of the first and second substantially vertical walls (edge region 26) than themicroseal thickness 28 in thecenter region 30 of the microseal. - While at least one exemplary embodiment has been presented in the foregoing detailed description, it should be appreciated that a vast number of variations exist. It should also be appreciated that the exemplary embodiment or exemplary embodiments are only examples, and are not intended to limit the scope, applicability, or configuration of the disclosure in any way. Rather, the foregoing detailed description will provide those skilled in the art with a convenient road map for implementing the exemplary embodiment or exemplary embodiments. It should be understood that various changes can be made in the function and arrangement of elements without departing from the scope of the disclosure as set forth in the appended claims and the legal equivalents thereof.
Claims (17)
1. A microseal for a metal bead seal joint, the microseal comprising:
a substantially horizontal surface;
a first substantially vertical surface disposed at a first end of the substantially horizontal surface and a second substantially vertical surface disposed at a second end of the substantially horizontal surface; and
a contoured surface disposed opposite the substantially horizontal surface, the contoured surface being integral to the first and second substantially vertical surfaces and being operatively configured to adhere to a portion of a metal bead.
2. The microseal for a metal bead seal joint as defined in claim 1 wherein the substantially horizontal surface is operatively configured to maintain a substantially flat surface orientation when subjected to a vertical load.
3. The microseal for a metal bead seal joint as defined in claim 1 wherein the contoured surface and the substantially horizontal surface define a microseal thickness.
4. The microseal for a metal bead seal joint as defined in claim 2 wherein an entire surface area of the contoured surface is operatively configured to flex together with a metal bead.
5. The microseal for a metal bead seal joint as defined in claim 3 wherein the microseal thickness is greater at an edge region than the microseal thickness at a center region, the edge region being proximate to each of the first and the second substantially vertical surfaces and the center region being disposed between the edge region for the first substantially vertical wall and the edge region for the second substantially vertical wall.
6. The microseal for a metal bead seal joint as defined in claim 3 wherein the microseal thickness varies along a width of the substantially horizontal surface.
7. A metal bead seal joint for a fuel cell plate, the metal bead seal joint comprising:
a first metal bead having a first microseal; and
a second metal bead having a second microseal compressed against at least a portion of the first microseal and the first metal bead.
8. The metal bead seal joint for a fuel cell plate as defined in claim 7 wherein each of the first and second microseals further comprise
a substantially horizontal surface;
a first substantially vertical surface disposed at a first end of the substantially horizontal surface and a second substantially vertical surface disposed at a second end of the substantially horizontal surface; and
a contoured surface disposed opposite the substantially horizontal surface, the contoured surface being integral to the first and second substantially vertical surfaces.
9. The metal bead seal joint for a fuel cell plate as defined in claim 8 wherein each of the first substantially horizontal surfaces are operatively configured to maintain a substantially flat orientation in a compression state as well as a non-compression state.
10. The metal bead seal joint for a fuel cell plate as defined in claim 9 wherein each of the first and second substantially vertical surfaces and the contoured surface are operatively configured to have a surface orientation which changes between the compression and non-compression states.
11. The metal bead seal joint for a fuel cell plate as defined in claim 8 wherein each of the contoured surface and the substantially horizontal surface for each of the first and second microseals define a microseal thickness.
12. The metal bead seal joint for a fuel cell plate as defined in claim 10 wherein each contoured surface is operatively configured to adhere to at least a portion of one of the first and second metal beads, and each contoured surface is operatively configured to flex as the first and second metal beads flex under compression.
13. The metal bead seal joint for a fuel cell plate as defined in claim 11 wherein each microseal is operatively configured to have a microseal thickness which varies along a width of the microseal prior to compression.
14. A method for manufacturing a microseal, the method comprising the steps of:
applying a first application of a microseal material to a metal bead wherein the microseal material is in a viscous state;
forming a substantially horizontal surface in the microseal material; and
curing the microseal material.
15. The method for manufacturing a microseal as defined in claim 14 , further comprising the steps of:
partially curing the first application of the microseal material;
applying a compression load across a width of the microseal material during the curing process;
removing the compression load; and
fully curing the first application of the microseal material thereby forming a microseal.
16. The method for manufacturing a microseal as defined in claim 14 , further comprising the step of:
applying a second application of the microseal material to the metal bead adjacent to the first application of the microseal material wherein the microseal material from the first and second applications is in a viscous state.
17. The method for manufacturing a microseal as defined in claim 16 wherein the first and second applications of microseal material are operatively configured to flow toward one another thereby forming the substantially horizontal surface.