US20180135356A9 - Polycrystalline compacts including crushed diamond nanoparticles, cutting elements and earth boring tools including such compacts, and methods of forming same - Google Patents
Polycrystalline compacts including crushed diamond nanoparticles, cutting elements and earth boring tools including such compacts, and methods of forming same Download PDFInfo
- Publication number
- US20180135356A9 US20180135356A9 US13/935,263 US201313935263A US2018135356A9 US 20180135356 A9 US20180135356 A9 US 20180135356A9 US 201313935263 A US201313935263 A US 201313935263A US 2018135356 A9 US2018135356 A9 US 2018135356A9
- Authority
- US
- United States
- Prior art keywords
- diamond
- grains
- crushed
- nanoparticles
- polycrystalline
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
- The present disclosure relates generally to polycrystalline diamond compacts, which may be used, for example, as cutting elements for earth-boring tools, and more particularly to polycrystalline diamond compacts including diamond nanoparticles, to methods of forming such compacts, and to cutting elements and earth-boring tools comprising such compacts.
- Earth-boring tools for forming wellbores in subterranean earth formations generally include a plurality of cutting elements secured to a body. For example, fixed-cutter earth-boring rotary drill bits (also referred to as “drag bits”) include a plurality of cutting elements fixedly attached to a bit body of the drill bit. Roller cone earth-boring rotary drill bits may include cones mounted on bearing pins extending from legs of a bit body such that each cone is capable of rotating about the bearing pin on which it is mounted. A plurality of cutting elements may be mounted to each cone of the drill bit. In other words, earth-boring tools typically include a bit body to which cutting elements are attached.
- The cutting elements used in such earth-boring tools often include polycrystalline diamond compacts (often referred to as “PDCs”), which act as cutting faces of a polycrystalline diamond material. Polycrystalline diamond material is material that includes inter-bonded particles in the form of grains or crystals of diamond material. In other words, polycrystalline diamond material includes direct, inter-granular bonds between the grains or crystals of diamond material. The terms “grain,” “crystal,” and “particle” are used synonymously and interchangeably herein.
- PDC cutting elements are conventionally formed by sintering and bonding together relatively small diamond grains under conditions of high temperature and high pressure in the presence of a catalyst (e.g., cobalt, iron, nickel, or alloys and mixtures thereof) to form a layer (referred to as a “compact” or “table”) of polycrystalline diamond (PCD) material on a cutting element substrate. These processes are often referred to as high-temperature/high-pressure (HTHP) processes. The cutting element substrate may comprise a cermet material (i.e., a ceramic-metal composite material) such as, for example, cobalt-cemented tungsten carbide. In such instances, the cobalt (or other catalyst material) in the cutting element substrate may liquefy and diffuse into the diamond grains during sintering and serve as a catalyst (which may also be characterized as a binder) for forming the inter-granular diamond-to-diamond bonds, and the resulting diamond table, from the diamond grains. In other methods, powdered catalyst material may be mixed with the diamond grains prior to sintering the grains together in an HTHP process.
- Upon formation of a diamond table using an HTHP process, catalyst material may remain in interstitial spaces between the grains of diamond in the resulting PDC. The presence of the catalyst material in the diamond table may contribute to thermal damage in the diamond table when the cutting element is heated during use, due to friction at the contact point between the cutting element and the formation.
- Polycrystalline diamond (PCD) typically contains more than 80 volume percent sintered diamond grains, with the balance a binder phase. As noted above, this binder phase is conventionally provided via infiltration from a supporting cemented carbide substrate, but may also be incorporated into the starting diamond powder as an admixture. The diamond grains typically lie within the 1 to 50 micron size range, but there is significant interest in incorporating a nanodiamond grain component, which may comprise a substantial portion, for increased PCD abrasion resistance, fracture toughness, and thermal stability. Such enhanced performance is believed to be attributable to increased diamond percent volume, augmented diamond particle interbonding, and reduction in catalyst material volume in the PCD.
- However, challenges exist when trying to incorporate nanoparticles in bulk sintering processes including PCD. During polycrystalline diamond compact synthesis, for example, the diamond nanoparticles may dissolve in the liquid state, infiltrating binder from the substrate or admixed binder under HTHP process conditions, resulting in the loss of the beneficial characteristics of abrasion resistance, fracture toughness, and thermal stability provided by the presence of the diamond nanoparticles. Further, when a conventional cobalt-cemented tungsten carbide substrate is employed, sintering quality may be compromised due to the loss of binder volume available to the sintering process. This phenomenon becomes more evident when relatively higher concentrations of diamond nanoparticles, for example greater than about ten percent by volume, are employed to form PCD. In addition, the presence of tightly packed diamond nanoparticles in a volume of diamond grains undergoing HTHP processing inhibits infiltration of liquid-state binder from the substrate through the diamond table, causing a less well sintered region in the diamond table as distance increases from the interface between the diamond table and the substrate, resulting in poor abrasion resistance and compromised mechanical integrity of the diamond table.
- In some embodiments, a method of fabricating polycrystalline diamond includes encapsulating micron-sized diamond grains and crushed diamond nanoparticles in a canister, and subjecting the encapsulated diamond particles and crushed diamond nanoparticles in the presence of a binder to a pressure of at least 5.0 GPa and a temperature of at least 1000° C. to form inter-granular bonds between the diamond grains and the diamond nanoparticles.
- A polycrystalline compact includes a plurality of grains of diamond material and a plurality of crushed diamond nanoparticles disposed in interstitial spaces between, and bonded to, the plurality of grains of diamond material. The plurality of crushed diamond nanoparticles are bonded to the grains of diamond material by subjecting the crushed diamond nanoparticles and the grains of diamond material in the presence of a binder to a pressure of at least 5.0 GPa and a temperature of at least 1000° C.
- An earth-boring tool includes a bit body and a polycrystalline diamond compact secured to the bit body. The polycrystalline compact comprises a plurality of grains of diamond material and a plurality of crushed diamond nanoparticles disposed in interstitial spaces between and bonded to, the grains of diamond material. The plurality of crushed diamond nanoparticles are bonded to the grains of diamond material by subjecting the crushed diamond nanoparticles and the grains of diamond material in the presence of a binder to a pressure of at least 5.0 GPa and a temperature of at least 1000° C.
- While the specification concludes with claims particularly pointing out and distinctly claiming what are regarded as embodiments of the disclosure, various features and advantages of embodiments of the disclosure may be more readily ascertained from the following description of some embodiments of the disclosure when read in conjunction with the accompanying drawings, in which:
-
FIG. 1A is a partial cut-away perspective view illustrating an embodiment of a cutting element comprising a polycrystalline compact of the present disclosure; -
FIG. 1B is a simplified drawing showing how a microstructure of the polycrystalline compact ofFIG. 1A may appear under magnification, and illustrates inter-bonded and interspersed larger and smaller grains of hard material; -
FIG. 2 is a simplified cross-sectional view illustrating a mixture of diamond grains and diamond nanoparticles encapsulated within a container in preparation for subjecting the container and the mixture therein to an HTHP sintering process to form a polycrystalline diamond compact cutting element; and -
FIG. 3 is a perspective view of an embodiment of a fixed-cutter earth-boring rotary drill bit that includes a plurality of polycrystalline compacts like that shown inFIGS. 1A and 1B . - The illustrations presented herein are not actual views of any particular polycrystalline compact, microstructure of a polycrystalline compact, particle, cutting element, or earth-boring tool, and are not drawn to scale, but are merely idealized representations employed to describe the present disclosure. Additionally, elements common between figures may retain the same numerical designation.
- As used herein, the term “earth-boring tool” means and includes any type of bit or tool used for drilling during the formation or enlargement of a wellbore and includes, for example, rotary drill bits, percussion bits, core bits, eccentric bits, bi-center bits, reamers, mills, drag bits, roller-cone bits, hybrid bits, and other drilling bits and tools known in the art.
- As used herein, the term “particle” means and includes any coherent volume of solid matter having an average dimension of about 2 mm or less. Grains (i.e., crystals) and coated grains are types of particles. As used herein, the term “nanoparticle” means and includes any particle having an average particle diameter of about 500 nm or less. Nanoparticles include grains in a polycrystalline hard material having an average grain size of about 500 nm or less.
- As used herein, the term “nanodiamond” means and includes any single or polycrystalline or agglomeration of nanocrystalline carbon material comprising a mixture of sp-3 and sp-2 bonded carbon wherein the individual particle or crystal whether singular or part of an agglomerate is primarily made up of sp-3 bonds. Commercially, nanodiamonds are derived from detonation sources (UDD or ultra-dispersed diamond) and crushed sources and can be naturally occurring or manufactured synthetically. Naturally occurring nanodiamond includes the natural lonsdaleite phase identified with meteoric deposits.
- As used herein, the term “crushed nanodiamond” means and includes synthetic or natural nanocrystalline diamond, or combinations thereof, that has been ground, milled, attrited, or otherwise comminuted from a larger-sized diamond crystal to form single-crystal particles or agglomerations of single-crystal particles.
- As used herein, the term “polycrystalline hard material” means and includes any material comprising a plurality of grains or crystals of the material that are bonded directly together by inter-granular bonds. The crystal structures of the individual grains of polycrystalline hard material may be randomly oriented in space within the polycrystalline hard material.
- As used herein, the teem “polycrystalline compact” means and includes any structure comprising a polycrystalline hard material comprising inter-granular bonds formed by a process that involves application of pressure (e.g., compaction) to the precursor material or materials used to form the polycrystalline hard material.
- As used herein, the term “inter-granular bond” means and includes any direct atomic bond (e.g., covalent, metallic, etc.) between atoms in adjacent grains of material.
- As used herein, the terms “catalyst material,” “binder material,” “binder,” and “metallic binder” each mean and include any material that is capable of catalyzing the formation of inter-granular bonds between grains of hard material during a sintering process (e.g., an HTHP process). For example, catalyst materials for diamond include cobalt, iron, nickel, other elements from Group VIII-A of the periodic table of the elements, and alloys thereof including without limitations Co—Ni, Co—Fe, Ni—Fe, INCONEL® and HASTALLOY® alloys.
- As used herein, the term “hard material” means and includes any material having a Knoop hardness value of about 3,000 Kgf/mm2 (29,420 MPa) or more. Hard materials include, for example, diamond and cubic boron nitride.
-
FIG. 1A is a simplified, partially cut-away perspective view of an embodiment of a cuttingelement 10 of the present disclosure. The cuttingelement 10 includes a polycrystalline compact in the form of a layer of hard polycrystallinehard material 12, also known in the art as a polycrystalline table, that is provided on (e.g., formed on or attached to) a supportingsubstrate 16 with aninterface 14 therebetween. Though the cuttingelement 10 in the embodiment depicted inFIG. 1A is cylindrical or disc-shaped, in other embodiments, the cuttingelement 10 may have any desirable shape, such as a dome, cone, chisel, etc. - In some embodiments, the polycrystalline
hard material 12 comprises polycrystalline diamond. In such embodiments, the cuttingelement 10 may be referred to as a PDC cutting element. -
FIG. 1B is an enlarged simplified view illustrating how a microstructure of the polycrystalline hard material 12 (FIG. 1A ) of the cuttingelement 10 may appear under magnification. As discussed in further detail below, the polycrystallinehard material 12 may include inter-bonded micron-sized grains 18 of diamond material. The polycrystallinehard material 12 also includes other, smaller crushed diamond particles 19 (e.g., diamond nanoparticles (nanodiamond)) disposed ininterstitial spaces 22 between the micron-sizedinter-bonded grains 18 of diamond material and inter-bonded therewith as indicated at 26. In some embodiments, and as shown inFIG. 1B , thegrains 18 of diamond material in the polycrystallinehard material 12 may have a substantially uniform, mono-modal grain size distribution, and the crusheddiamond nanoparticles 19 may likewise be of substantially uniform size. In some embodiments, acatalyst material 24 may reside in regions ofinterstitial spaces 22 unoccupied bycrushed diamond nanoparticles 19. - In additional embodiments, one or both of the
grains 18 and crusheddiamond nanoparticles 19 of the polycrystallinehard material 12 may have a multi-modal (e.g., bi-modal, tri-modal, etc.) grain size distribution. For example, the polycrystallinehard material 12 may comprise a multi-modal grain size distribution as disclosed in at least one of U.S. Patent Application Publication No. US 2011/0031034 A1, published Feb. 10, 2011, and titled “Polycrystalline Compacts Including In-Situ Nucleated Grains, Earth-Boring Tools Including Such Compacts, and Methods of Forming Such Compacts and Tools;” U.S. Patent Application Publication No. US 2011/0061942 A1, published Mar. 17, 2011, and titled “Polycrystalline Compacts Having Material Disposed in Interstitial Spaces Therein, Cutting Elements and Earth-Boring Tools Including Such Compacts, and Methods of Forming Such Compacts;” and U.S. Patent Application Publication No. US 2011/0088954 A1, published Apr. 21, 2011, and titled “Polycrystalline Compacts Including Nanoparticulate Inclusions, Cutting Elements and Earth-Boring Tools Including Such Compacts, and Methods of Forming Such Compacts;” the disclosures of each of which are incorporated herein in their entireties by this reference. - More specifically, polycrystalline
hard material 12 may include interspersed andinter-bonded diamond grains 18 and crusheddiamond nanoparticles 19 that form a three-dimensional network of diamond material. Thediamond grains 18 and/or the smaller crusheddiamond nanoparticles 19 may have average particle dimensions (e.g., mean diameters) of about 1 mm or less, about 0.1 mm or less, about 0.01 mm or less, about 1 μm or less, about 0.1 μm or less, or even about 0.01 μm or less. That is, thelarger diamond grains 18 may include micron-sized diamond particles (diamond grains in a range from about 1 μm to about 500 μm (0.5 mm)) and submicron-sized diamond particles (diamond grains in a range from about 500 nm (0.5 μm) to about 1 μm). The crusheddiamond nanoparticles 19 may have an average particle diameter of about 500 nm or less, such as from about 5 nm to about 150 nm. The crusheddiamond nanoparticles 19 may each be single-crystal diamond, and may be substantially free of non-diamond carbon. - In some embodiments; the
larger diamond grains 18 may be one or both of micron-sized diamond particles and submicron-sized particles. Interstitial spaces are present between theinter-bonded diamond grains 18 and the crusheddiamond nanoparticles 19 of the polycrystallinehard material 12. These interstitial spaces may be at least partially filled with a solid substance, such as a metal solvent catalyst material 24 (e.g., iron, cobalt, nickel, or an alloy or mixture thereof). In other embodiments, the interstitial spaces may include empty voids within the polycrystallinehard material 12 free of a solid or liquid substance (although a gas, such as air, may be present in the voids). Such empty voids may be formed by removing (e.g., leaching) solid material out from the interstitial spaces after forming the polycrystallinehard material 12. In yet further embodiments, the interstitial spaces may be at least partially filled with a solid substance in one or more regions of the polycrystalline hard material, while the interstitial spaces in one or more regions of the polycrystallinehard material 12 include empty voids. - As known in the art, the average grain size of grains within a microstructure may be determined by measuring grains of the microstructure under magnification. For example, a scanning electron microscope (SEM), a field emission scanning electron microscope (FESEM), or a transmission electron microscope (TEM) may be used to view or image a surface of a polycrystalline hard material 12 (e.g., a polished and etched surface of the polycrystalline hard material 12). Commercially available vision systems are often used with such microscopy systems, and these vision systems are capable of measuring the average grain size of grains within a microstructure.
- Referring again to
FIGS. 1A and 1B , the volume occupied by the crusheddiamond nanoparticles 19 in the polycrystallinehard material 12 may be in a range extending from about 0.01% to about 99% of the volume of the polycrystallinehard material 12, such as from about 0.05% to about 50% of the volume of the polycrystallinehard material 12, or from about 0.1% to about 10% of the volume of the polycrystallinehard material 12. The weight percentage of the crusheddiamond nanoparticles 19 in the polycrystallinehard material 12 may be in a range extending from about 0.01% to about 99% by weight, such as from about 0.05% to about 50% by weight or from about 0.1% to about 10% by weight. - In embodiments in which the polycrystalline
hard material 12 includes polycrystalline diamond, thecatalyst material 24 may be a Group VIII-A element (e.g., iron, cobalt, nickel, etc.) or an alloy thereof, and thecatalyst material 24 may be between about one tenth of one percent (0.1%) and about ten percent (10%) by volume of the polycrystallinehard material 12. - The layer of polycrystalline
hard material 12 of the cuttingelement 10 may be formed using HTHP processes. Such processes, and systems for carrying out such processes, are generally known in the art and not described in detail herein. In some embodiments, the polycrystallinehard material 12 may be formed on a supporting substrate 16 (as shown inFIG. 1A ) of cemented tungsten carbide or another suitable substrate material in a conventional HTHP process of the type described, by way of non-limiting example, in U.S. Pat. No. 3,745,623, issued Jul. 17, 1973, and titled “Diamond Tools for Machining,” or may be formed as a freestanding polycrystalline hard material 12 (i.e., without the supporting substrate 16) in a similar conventional HTHP process as described, by way of non-limiting example, in U.S. Pat. No. 5,127,923, issued Jul. 7, 1992, and titled “Composite Abrasive Compact Having High Thermal Stability,” the disclosures of each of which are incorporated herein in their entireties by this reference. In some embodiments, thecatalyst material 24 may be supplied from the supportingsubstrate 16 during an HTHP process used to form the polycrystallinehard material 12. For example, thesubstrate 16 may comprise a diamond enhanced cobalt-cemented tungsten carbide material as described in U.S. Patent Application Publication No. US 2011/0226532 A1, published Sep. 22, 2011, and titled “Insert for an Attack Tool, Method for Making Same and Tools Incorporating Same;” and U.S. Patent Application 2011/0020163, published Jan. 27, 2011, and titled “Super-Hard Enhanced Hard-Metals;” the disclosures of each of which are incorporated herein in their entireties by this reference. The cobalt of the cobalt-cemented tungsten carbide may serve as thecatalyst material 24 during the HTHP process. -
FIG. 2 is a simplified cross-sectional view illustrating a mixture of diamond grains and diamond nanoparticles encapsulated within a container in preparation for subjecting the container and the mixture therein to an HTHP sintering process to form a polycrystalline diamond compact cutting element, such as the cuttingelement 10 shown inFIGS. 1A and 1B . As depicted inFIG. 2 ,diamond grains 118 may be positioned within a canister 100 (e.g., a metal canister) prior to undergoing the HTHP process used to form polycrystallinehard material 12. Thediamond grains 118 may include grains or crystals of micron- and/or submicron-sized diamond (e.g., diamond grit), which will ultimately form thediamond grains 18 in the sintered polycrystalline hard material 12 (seeFIGS. 1A and 1B ). -
Crushed diamond nanoparticles 119 also may be present in the spaces between thediamond grains 118 in thecanister 100. As shown inFIG. 2 , thecanister 100 may include aninner cup 102 in which the diamond grains and the crusheddiamond nanoparticles 119 may be provided. If the cuttingelement 10 is to include asubstrate 16, asubstrate blank 116 may, optionally also be provided in theinner cup 102 over or under thediamond grains 118 and the crusheddiamond nanoparticles 119, and may ultimately be encapsulated in thecanister 100. Thecanister 118 may include atop end piece 104 and abottom end piece 106, which may be assembled and bonded together (e.g., swage bonded) around theinner cup 102 with thediamond grains 118, the crusheddiamond nanoparticles 119, and the optional substrate blank 116 therein. - To form the polycrystalline hard material 12 (
FIG. 1A ) in an HTHP process, a particulate mixture including the diamond grains 118 (i.e., particles of micron-sized diamond material) and the crusheddiamond nanoparticles 119 may be subjected to elevated temperatures (e.g., temperatures greater than about 1,000° C.) and elevated pressures (e.g., pressures greater than about 5.0 gigapascals (GPa)). These conditions may promote the formation ofinter-granular bonds 26 between thediamond grains 118 and the crusheddiamond nanoparticles 119 without entirely consuming the crusheddiamond nanoparticles 119. In some embodiments, the particulate mixture may be subjected to a pressure greater than about 6.0 GPa, greater than about 8.0 GPa, or even greater than about 10.0 GPa. The particulate mixture may be subjected to a temperature from about 1,200° C. to about 2,000° C., such as a temperature greater than about 1,500° C., in the HTHP process. HTHP conditions may be maintained for a period of time from about thirty (30) seconds to about sixty (60) minutes to sinter the particles and form the polycrystallinehard material 12. - In some embodiments, the particulate mixture may include a powder or a powder-like substance. In other embodiments, however, the particulate mixture, which may comprise a solution, slurry, gel, or paste, may be processed by (e.g., on or in) another material form, such as a tape or film, which, after stacking to a selected thickness, and undergoing subsequent thermal and or chemical processes to remove the one or more organic processing aids, may be subjected to an HTHP process. One or more organic materials (e.g., processing aids) also may be included with the particulate mixture to facilitate processing. For example, some suitable materials are described in U.S. Patent Application Publication No. US 2012/0211284 A1, published Aug. 23, 2012, and titled “Methods of Forming Polycrystalline Compacts, Cutting Elements and Earth-Boring Tools,” the disclosure of which is incorporated herein in its entirety by this reference.
- In some embodiments, the crushed
diamond nanoparticles 119 may be functionalized with one or more functional groups, such as to control or prevent agglomeration and promote uniform or controlled distribution into the pre-HPHT macro diamond synthesis chemistry. For example, functionalization of the crusheddiamond nanoparticles 119 may be performed as described in U.S. Patent Application Publication No. US 2013/0068541, published Mar. 21, 2013, and titled “Methods of Fabricating Polycrystalline Diamond, and Cutting Elements and Earth-Boring Tools Comprising Polycrystalline Diamond;” U.S. Pat. No. 8,003,215, issued Aug. 23, 2011, and titled “Fluorinated Nanodiamond as a Precursor for Solid Substrate Surface Coating Using Wet Chemistry;” U.S. Pat. No. 7,858,186, issued Dec. 28, 2010, and titled “Fluorinated Nanodiamond as a Precursor for Solid Substrate Surface Coating Using Wet Chemistry;” and U.S. Pat. No. 7,820,130, issued Oct. 26, 2010, and titled “Functionalization of Nanodiamond Powder Through Fluorination and Subsequent Derivatization Reactions;” the disclosures of each of which are incorporated herein in their entirety by this reference. - The crushed
diamond nanoparticles 119 may be added to thecanister 100 as a dry bulk powder, a wet aqueous medium, a solvent-based medium, or any other form. For example, the crusheddiamond nanoparticles 119 may be in a composition having the form of a liquid (e.g., a suspension or slurry), gel, paste, etc. The crusheddiamond nanoparticles 119 may be cleaned and distributed in a liquid or solution by magnetic stirring, ball milling, attrition milling, ultrasonication, or any other method or combination of methods. Dispersed and/or stabilized liquids, gels, or pastes can be dried, sieved, pressed, or injection molded, for example, into die capsules for vacuum heat treating and subsequent HPHT processing. - In the
canister 100, before applying pressure, thediamond grains 118 may have a packing fraction from about 80% to about 99% (i.e., with a void space of between about 20% and about 1% of the total volume), such as from about 85% to about 95% (i.e., with a void space of between about 5% and about 15% of the total volume). The crusheddiamond nanoparticles 119 may occupy void space between the diamond grains 118 (e.g., micron-sized diamond), such that the crusheddiamond nanoparticles 119 are in proximity to thediamond grains 118. For example, in some embodiments the diamond nanoparticles may substantially fill the void space between thediamond grains 118. In other embodiments, abinder 24′ (e.g., a metallic binder) may partially fill the void space between thediamond grains 118. A conventional HTHP process for forming the polycrystallinehard material 12 and the cuttingelement 10 is then performed. - Optionally, the catalyst material 24 (e.g., a portion of the
binder 24′) may be removed from the as-formed polycrystallinehard material 12 after the HTHP process using processes known in the art. For example, a leaching process may be used to remove thecatalyst material 24 from theinterstitial spaces 22 between thegrains 18 of diamond material and crusheddiamond nanoparticles 19 in at least a portion of the polycrystallinehard material 12. By way of example and not limitation, a portion of the polycrystallinehard material 12 may be leached using a leaching agent and process such as those described more fully in, for example, U.S. Pat. No. 5,127,923, previously incorporated herein by reference, and U.S. Pat. No. 4,224,380, issued Sep. 23, 1980, and titled “Temperature Resistant Abrasive Compact and Method for Making Same,”, the disclosure of which is incorporated herein in its entirety by this reference. Specifically, aqua regia (a mixture of concentrated nitric acid (HNO3) and concentrated hydrochloric acid (HCl)) may be used to at least substantially removecatalyst material 24 from theinterstitial spaces 22. It is also known to use boiling hydrochloric acid (HCl) and boiling hydrofluoric acid (HF) as leaching agents. One particularly suitable leaching agent is hydrochloric acid (HCl) at a temperature of above about 110° C., which may be provided in contact with the polycrystallinehard material 12 for a period of about two (2) hours to about sixty (60) hours, depending upon the size of the body of polycrystallinehard material 12. After leaching the polycrystallinehard material 12, theinterstitial spaces 22 between theinter-bonded grains 18 of hard material within the polycrystallinehard material 12 subjected to the leaching process may be at least substantially free ofcatalyst material 24 used to catalyze formation ofinter-granular bonds 26 between the grains in the polycrystallinehard material 12. The leaching process may applied to only a portion of the polycrystallinehard material 12, or to the entire body of the polycrystallinehard material 12. - Embodiments of cutting
elements 10 of the present disclosure that include a polycrystalline compact comprising polycrystallinehard material 12 formed of inter-bonded micron-sized grains 18 of diamond material and crusheddiamond nanoparticles 19, as previously described herein, such as the cuttingelement 10 illustrated inFIG. 1A , may be formed and secured to an earth-boring tool such as a rotary drill bit, a percussion bit, a coring bit, an eccentric bit, a reamer tool, a milling tool, etc., for use in forming wellbores in subterranean formations. As a non-limiting example,FIG. 3 illustrates a fixed cutter type earth-boringrotary drill bit 36 that includes a plurality of cuttingelements 10, each of which includes a polycrystalline compact comprising polycrystallinehard material 12 on asubstrate 16, as previously described herein. The earth-boringrotary drill bit 36 includes abit body 38, and the cuttingelements 10, which include polycrystalline hard material 12 (seeFIG. 1A ), are bonded to thebit body 38. The cuttingelements 10 may be brazed (or otherwise secured) within pockets formed in the outer surface of thebit body 38. - The use of crushed
diamond nanoparticles 119 in the formation of cuttingelements 10 may result in polycrystallinehard material 12 having crusheddiamond nanoparticles 19 remaining after HPHT processing. The crusheddiamond nanoparticles 19 of the polycrystallinehard material 12 may increase the overall density and abrasion resistance of the polycrystallinehard material 12. Because crushing may form diamond nanoparticles having relatively lower concentrations of non-diamond carbon than other methods of forming diamond nanoparticles, the resulting polycrystallinehard material 12 may be relatively more pure than polycrystalline hard materials formed from other types of diamond nanoparticles (e.g., detonation nanodiamond tends to include polycrystalline nanodiamond agglomerates and non-diamond carbon). During the formation of polycrystallinehard material 12 from crusheddiamond nanoparticles 119, dissolution of diamond (including the crushed diamond nanoparticles 119) in the binder may occur at a lower rate than in conventional processes. Thus, polycrystallinehard materials 12 formed from crusheddiamond nanoparticles 19 may havemore diamond nanoparticles 19 remaining after HPHT processing than similar polycrystalline hard materials formed from similar amounts of other types of diamond nanoparticles. Furthermore, the crusheddiamond nanoparticles 19 remaining after HPHT processing may be closer to the size of the crusheddiamond nanoparticles 119 than would be expected when other types of diamond nanoparticles are used. - Polycrystalline hard materials that include crushed diamond nanoparticles in interstitial spaces between and bonded to the inter-bonded, larger grains of diamond material, as described herein, may exhibit improved thermal stability and improved mechanical durability in terms of abrasion resistance and impact resistance, relative to previously known polycrystalline hard materials. By including crushed diamond nanoparticles in the interstitial spaces between the inter-bonded grains of hard material, less catalyst material may be disposed in interstitial spaces between the grains in a resulting polycrystalline hard material, which may improve one or both of the thermal stability and the mechanical durability of the ultimate polycrystalline hard material.
- Additional non-limiting example embodiments of the disclosure are described below.
- A method of fabricating polycrystalline diamond comprising encapsulating micron-sized diamond grains and crushed diamond nanoparticles in a canister and subjecting the micron-sized diamond grains and the crushed diamond nanoparticles in the presence of a binder to a pressure of at least 5.0 GPa and a temperature of at least 1000° C. to form inter-granular bonds between the micron-sized diamond grains and the crushed diamond nanoparticles.
- The method of Embodiment 1, wherein encapsulating micron-sized diamond grains and crushed diamond nanoparticles in a canister comprises mixing the binder with the micron-sized diamond grains and the crushed diamond nanoparticles.
- The method of Embodiment 1 or Embodiment 2, further comprising at least partially filling a volume between the micron-sized diamond grains with the binder.
- The method of any of Embodiments 1 through 3, wherein encapsulating micron-sized diamond grains and crushed diamond nanoparticles in a canister comprises encapsulating micron-sized diamond grains having an average particle diameter of about 1 mm or less with crushed diamond nanoparticles having an average particle diameter of about 500 nm or less.
- The method of any of Embodiments 1 through 4, wherein encapsulating micron-sized diamond grains and crushed diamond nanoparticles in a canister comprises encapsulating micron-sized diamond grains with a plurality of single-crystal crushed diamond nanoparticles.
- The method of any of Embodiments 1 through 5, wherein encapsulating micron-sized diamond grains and crushed diamond nanoparticles in a canister comprises encapsulating micron-sized diamond grains with functionalized crushed diamond nanoparticles.
- The method of any of Embodiments 1 through 6, further comprising leaching at least a portion of the binder from the polycrystalline diamond.
- The method of any of Embodiments 1 through 7, wherein subjecting the micron-sized diamond grains and the crushed diamond nanoparticles in the presence of a binder to a pressure of at least 5.0 GPa and a temperature of at least 1000° C. comprises forming inter-granular bonds between the micron-sized diamond grains and the crushed diamond nanoparticles without consuming the crushed diamond nanoparticles.
- The method of any of Embodiments 1 through 8, wherein subjecting the micron-sized diamond grains and the crushed diamond nanoparticles in the presence of a binder to a pressure of at least 5.0 GPa and a temperature of at least 1000° C. comprises subjecting the micron-sized diamond grains and the crushed diamond nanoparticles in the presence of a metallic binder to a pressure of at least 5.0 GPa and a temperature of at least 1000° C.
- A polycrystalline compact comprising a plurality of grains of diamond material and a plurality of crushed diamond nanoparticles disposed in interstitial spaces between, and bonded to, the plurality of grains of diamond material. The plurality of crushed diamond nanoparticles are bonded to the grains of diamond material by subjecting the crushed diamond nanoparticles and the grains of diamond material in the presence of a binder to a pressure of at least 5.0 GPa and a temperature of at least 1000° C.
- The polycrystalline compact of
Embodiment 10, wherein the polycrystalline compact is formed by encapsulating the plurality of grains of diamond material and the plurality of crushed diamond nanoparticles in a canister. - The polycrystalline compact of
Embodiment 10 or Embodiment 11, wherein the polycrystalline compact is formed by mixing the binder with the plurality of grains of diamond material and the plurality of crushed diamond nanoparticles. - The polycrystalline compact of any of
Embodiments 10 through 12, wherein the polycrystalline compact is formed by at least partially filling a volume between the plurality of grains of diamond material with the binder. - The polycrystalline compact of any of
Embodiments 10 through 13, wherein the plurality of crushed diamond nanoparticles has an average particle diameter of about 500 nm or less. - The polycrystalline compact of
Embodiment 14, wherein the plurality of crushed diamond nanoparticles has an average particle diameter from about 5 nm to about 150 nm. - The polycrystalline compact of any of
Embodiments 10 through 15, wherein the plurality of crushed diamond nanoparticles comprises a plurality of single-crystal diamond particles. - The polycrystalline compact of any of
Embodiments 10 through 16, wherein the polycrystalline compact is formed by leaching at least a portion of the binder from the polycrystalline compact. - The polycrystalline compact of any of
Embodiments 10 through 17, wherein the polycrystalline compact is substantially free of non-diamond carbon. - The polycrystalline compact of any of
Embodiments 10 through 18, wherein the plurality of crushed diamond nanoparticles are bonded to the grains of diamond material by subjecting the crushed diamond nanoparticles and the grains of diamond material in the presence of a metallic binder to a pressure of at least 5.0 GPa and a temperature of at least 1000° C. - An earth-boring tool comprising a bit body and a polycrystalline diamond compact secured to the bit body. The polycrystalline diamond compact comprises a plurality of grains of diamond material and a plurality of crushed diamond nanoparticles disposed in interstitial spaces between and bonded to, the grains of diamond material. The plurality of diamond nanoparticles are bonded to the grains of diamond material by subjecting the crushed diamond nanoparticles and the grains of diamond material in the presence of a binder to a pressure of at least 5.0 GPa and a temperature of at least 1000° C.
- The earth-boring tool of Embodiment 20, wherein the polycrystalline compact is formed by encapsulating the plurality of grains of diamond material and the plurality of crushed diamond nanoparticles in a canister.
- The earth-boring tool of Embodiment 20 or Embodiment 21, wherein the polycrystalline compact is formed by mixing the binder with the plurality of grains of diamond material and the plurality of diamond nanoparticles.
- The earth-boring tool of any of Embodiments 20 through 2022 wherein the polycrystalline compact is formed by at least partially filling a volume between the plurality of grains of diamond material with the binder.
- The earth-boring tool of any of Embodiments 20 through 23, wherein the polycrystalline compact comprises a leached polycrystalline compact.
- The earth-boring tool of any of Embodiments 20 through 24, wherein the polycrystalline compact is substantially free of non-diamond carbon.
- The earth-boring tool of any of Embodiments 20 through 25, wherein the plurality of crushed diamond nanoparticles are bonded to the grains of diamond material by subjecting the crushed diamond nanoparticles and the grains of diamond material in the presence of a metallic binder to a pressure of at least 5.0 GPa and a temperature of at least 1000° C.
- While the present disclosure has been described herein with respect to certain embodiments, those of ordinary skill in the art will recognize and appreciate that it is not so limited. Rather, many additions, deletions, and modifications to the embodiments described herein may be made without departing from the scope of the invention as hereinafter claimed, including legal equivalents. In addition, features from one embodiment may be combined with features of another embodiment while still being encompassed within the scope of the invention as contemplated by the inventor. Further, embodiments of the disclosure have utility with different and various bit profiles, as well as various cutting element types and configurations.
Claims (20)