US20170348633A1 - Gas separation device with nanocomposite membrane - Google Patents
Gas separation device with nanocomposite membrane Download PDFInfo
- Publication number
- US20170348633A1 US20170348633A1 US15/683,225 US201715683225A US2017348633A1 US 20170348633 A1 US20170348633 A1 US 20170348633A1 US 201715683225 A US201715683225 A US 201715683225A US 2017348633 A1 US2017348633 A1 US 2017348633A1
- Authority
- US
- United States
- Prior art keywords
- gas
- membrane
- nanocomposite
- permeance
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A nanocomposite membrane including an α-Al2O3 membrane support, a γ-Al2O3 intermediate layer that is 300-1200 nm thick and coats a surface of the membrane support, and a nanocomposite layer including SiO2 and Y2O3 that is 25-150 nm thick and coats a surface of the intermediate layer, wherein the nanocomposite layer is porous with an average largest radius micropore of 0.2-0.6 nm. A method of manufacturing the nanocomposite membrane, whereby the membrane support is coated with the γ-Al2O3, a silica source is hydrolyzed with a mixture of water, an alcohol solvent, and a Y source with a sol-gel technique to yield a Si/Y sol-gel, the membrane support is dip coated with the Si/Y sol-gel, and the nanocomposite membrane is calcined. A method of separating a mixture of gas, whereby the mixture of gas is introduced into a permeance cell and fed through the nanocomposite membrane.
Description
- The present invention relates to a nanocomposite membrane with a Si—Y nanocomposite layer on an alumina support. The present invention also relates to a dip coating method of making the nanocomposite membrane and a method of separating a mixture of gases with the nanocomposite membrane.
- The “background” description provided herein is for the purpose of generally presenting the context of the disclosure. Work of the presently named inventors, to the extent it is described in this background section, as well as aspects of the description which may not otherwise qualify as prior art at the time of filing, are neither expressly or impliedly admitted as prior art against the present invention.
- Many believe that the world will have a hydrogen based economy in the future. Hydrogen gas combines with oxygen gas to produce water, and in the process releases a substantial quantity of energy:
-
H2(g)+½O2(g)(spark)→H2O(g) ΔH=−242 kJ/mol - Unlike electricity, hydrogen is an advantageous energy source as it can be transmitted by pipelines over long distances and it consumes less energy to transmit than the same amount of energy in the form of electricity. Hydrogen is widely used in various fields of industries, such as chemical, steel, and oil refining and petro-chemical industries. It is also a clean alternative energy source, leading many to predict an increase in hydrogen demand in the near future. Hydrogen is the simplest element and most plentiful gas in the universe. Yet hydrogen never occurs by itself in nature, and always combines with other elements such as oxygen and carbon. Hydrogen can be separated from the mixed gas using one of several adsorption technologies such as pressure swing adsorption (PSA). Due to the higher operation temperature and several complicated purification steps, the cost to produce H2 with these current technologies is too high for it to be an alternative to conventional hydrocarbon fuels. About 50% of the world's hydrogen is produced from natural gas CH4 by means of steam-reforming reactions, which are commonly operated at around 800° C. If hydrogen (H2) can be selectively removed from the reforming reactor through a H2-permselective membrane, the thermodynamic equilibrium can be shifted to the product side, resulting in a higher conversion of CH4 to H2 even at lower temperatures (˜500° C.). Microporous ceramic membranes with molecular sieve-like properties for gas separation have attracted tremendous attention because of their high durability at elevated temperatures and in severe corrosive environments compared with polymer membranes, See A. J. Burggraff, “Fundamentals of Inorganic Membrane Science and Technology”, Membrane Science and Technology Series, Vol. 4. Elsevier, Amsterdam, (1996), incorporated herein by reference in its entirety.
- In particular, start-of the-art microporous silica membranes have been reported to separate hydrogen from other larger gas molecules by a simple molecular sieving effect. The multilayer membrane reactors can be used for methane-reforming reactions for hydrogen production and conversion enhancement in dehydrogenation chemistry. See T. Tsuru, K. Yamaguchi, T. Yoshioka, and M. Asaeda, “Methane Steam Reforming by Microporous Catalytic Membrane Reactors”, AIChE J., 50, 2794-805 (2005), incorporated herein by reference in its entirety. The pore diameter and the thickness of the membranes have been successfully controlled via methods including chemical vapor deposition (CVD), sol-gel techniques, and polymer precursor methods, See M. Nomura, H. Aida, S. Gopalakrishnan, T. I. Sugawara, S. Nakao, S. Yamazaki, T. Inada and Y. Iwamoto, “Steam stability of a silica membrane prepared by counter diffusion chemical vapor deposition”, Desalination 193, 1-7(2006); R. M. de Vos and H. Verweij, “High-Selectivity, High-Flux Silica Membranes for Gas Separation”, Science 279, 1710-1711 (1998); Y. Iwamoto, K. Sato, T. Kato, T. Inada, Y. Kubo, “A hydrogen-permselective amorphous silica membrane derived from polysilazane”, J. Euro. Ceram. Soc. 25, 257-264 (2005), each incorporated herein by reference in their entirety. Ultra microporous silica membranes can be synthesized by sol-gel or CVD methods and are cheap to produce. However, there is often a trade-off between permeability and selectivity in both types of membranes, as sol-gel membranes deliver higher fluxes while CVD membranes higher selectivities.
- Recently, oxide-based nanoparticle-dispersed amorphous silica membranes have been synthesized and designed also for gas separation applications in industries such as coal gasification, steam methane reforming, water-gas shift reaction and fuel cell systems, See M. Kanezashi and M. Asaeda, “Hydrogen permeation characteristics and stability of Ni-doped silica membranes in steam at higher temperature”, J. Membr. Sci. 271, 86-92 (2006); L. Barrelli, G. Bidini, F. Gallorini, S. Servilli, Hydrogen production through sorption-enhanced steam methane reforming and membrane technology: a review, Energy 33, 554 (2008), each incorporated herein by reference in their entirety. Typically these industries may require gas separation at temperatures preferably between 100° C. and 500° C., which can be met by the employment of silica or metal-based membranes. In the last two decades, gas-separation membranes have been developed using various materials, such as palladium and its alloys, silica and alumina, etc. Palladium membranes formed on porous alumina supports by the electro-less plating techniques and the MOCVD methods were reported to show high H2-permselectivity at 300°-500° C., but they have some disadvantages, such as degradation of H2-separation performance, for example, in the presence of hydrocarbons at high temperatures, See E. Kikuchi, Palladium/Ceramic Membranes for Selective Hydrogen Permeation and Their Application to Membrane Reactor, Catal. Today, 25, 333-337 (1995), incorporated herein by reference in its entirety. In order to improve the stability of Pd membranes against the chemical poisoning and mechanical load, Pd alloys (Pd—Ag, Pd—Ni, Pd—Nb) have been employed for metal membranes. In addition to problems with cost, these Pd alloy membranes still have high temperature stability problems, See C.-S. Jun, K.-H. Lee, Palladium and palladium alloy composite membranes prepared by metal-organic chemical vapor deposition method (cold-wall), J. Membr. Sci. 176, 121 (2000), incorporated herein by reference in its entirety.
- One of the major concerns with silica-derived membranes relate to their structural integrity and stability for wet gas stream exposure which is generally the case in industrial gas processing. The morphology of silica has been shown to alter upon exposure to steam, mainly directly attributed to the collapse of small pores and expansion of larger pores, resulting in a loss of selectivity, See S. Giessler, L. Jordan, J. C. Diniz da Costa, G. Q. Lu, Performance of hydrophobic and hydrophilic silica membrane reactors for the water gas shift reaction, Sep. Purif. Technol. 32 (1-3), 255 (2003); I. Himai, H. Morimoto, A. Tominaga, H. Hiraschima, Structural changes in sol-gel derived SiO2 and TiO2 films by exposure to water vapour, J. Sol-Gel Sci. Technol., 10, 45. (1997); R. K. Iler, The Chemistry of Silica; Wiley & Sons: New York, (1979), each incorporated herein by reference in their entirety. To address this problem, some research groups have incorporated templates into the silica film whereby the membrane films were calcined in non-oxidizing atmospheres, See G. P. Fotou, Y. S. Lin and S. E. Pratsinis, Hydrothermal stability of pure and modified microporous silica membranes, J. Mater. Sci. 30, 2803-2808 (1995), incorporated herein by reference in its entirety. As a result, template silica membranes imparted hydro stable properties, accompanied by structural modifications. For instance, gas selectivity was lowered as covalent ligand methyl template in methyl triethoxysilane led to the formation of slightly larger pore sizes, See M. Nomura, K. Ono, S. Gopalakrishnan, T. Sugawara, and S.-I. Nakao, Preparation of a Stable Silica Membrane by a Counter Diffusion Chemical Vapor Deposition Method, J. Membr. Sci., 251, 151-8 (2005), incorporated herein by reference in its entirety. It has been reported that silica membranes prepared by using CVD technique from methyltriethoxysilane showed high hydrothermal stability with a steam pressure of 75 kPa at 500° C., See M. Nomura, H. Aida, S. Gopalakrishnan, T. Sugawara, S-I. Nakao, S. Yamazaki, T. Inada, Y. Iwamoto, Steam stability of a silica membrane prepared by counter-diffusion chemical vapor deposition, Desalination 193, 1-7 (2006), incorporated herein by reference in its entirety. Moreover, it was found that γ-Al2O3-doped silica composite membranes can withstand hydrothermal conditions because of the strong network generated by the formation of Si—O—Al linkages, See Y. Gu, P. Harcarlioglu and S. T. Oyama, Hydrothermally stable silica-alumina composite membranes for hydrogen separation, J. Membr. Sci. 310, 28-37(2008), incorporated herein by reference in its entirety. The use of hexyl tri-ethyl ammonium bromide has also improved the hydrothermal stability of membranes when the materials were prepared by sol-gel processes, See M. C. Duke, J. C. Diniz da Costa, G. Q. (Max) Lu, M. Petch, and P. Gray, Carbonised Template Molecular Sieve Silica Membranes in Fuel Processing Systems: Permeation, Hydrostability and Regeneration, J. Membr. Sci., 241, 325-33 (2004), incorporated herein by reference in its entirety. The presence of carbon in the silica matrix can create a hydrophobic surface, which can control the free motion of silanol groups in the silica network at high temperatures and eventually reducing the densification of the silica network, See R. Igi, T. Yoshioka, Y. H. Ikuhara, Y. Iwamoto, and T. Tsuru, Characterization of Co-Doped Silica for Improved Hydrothermal Stability and Application to Hydrogen Separation Membranes at High Temperatures, J. Am. Ceram. Soc., 91, 9, 2975-2981 (2008), incorporated herein by reference in its entirety. In order to improve the ability of silica membranes in steam, inorganic oxides, such as TiO2, ZrO2, Fe2O3, Al2O3, NiO, etc. were also tested by doping with silica, See C. H. Chang, R. Gopalan and Y. S. Lin, A Comparative Study on thermal and Hydrothermal Stability of Alumina, Titania and Zirconia Membranes, J. Membrane Sci., 91, 27-45 (1994), incorporated herein by reference in its entirety. Of these metal-doped membranes, Ni-doped silica membranes showed relatively high H2-permence and high stability against water vapor at 35-300° C., suggesting the effectiveness of the addition of nickel oxides to silica for the membrane stability against steam at higher temperatures. Kanezashi and Asaeda found the incorporation of 33% nickel doping to improve hydrothermal stability, See M. Kanezashi and M. Asaeda, “Hydrogen permeation characteristics and stability of Ni-doped silica membranes in steam at high temperature”, J. Membr. Sci. 271, 86-93 (2006), incorporated herein by reference in its entirety. However, both hydrogen and nitrogen permeance decreased by 60% and 93%, respectively upon exposure to high temperature water vapor, favoring high H2/N2 selectivity. Duke et al. reported improved gas selectivity by exposing to steam silica membranes with carbonized templates derived from C6 surfactant triethylhexyl ammonium bromide, See M. C. Duke, J. C. Diniz da Costa, D. D. Do, P. G. Gray, G. Q. Lu, Hydrothermally robust molecular sieve silica for wet gas separation, Adv. Func. Mater. 16, 1215-20 (2006), incorporated herein by reference in its entirety. Gu et al. achieved enhanced hydrothermal stability using 3% alumina doping in CVD membranes, however, 45% hydrogen permeance reduction was observed after long-term exposure to steam, See Y. Gu, P. Harcarlioglu and S. T. Oyama, Hydrothermally stable silica-alumina composite membranes for hydrogen separation, J. Membr. Sci. 310, 28-37 (2008), incorporated herein by reference in its entirety.
- Nanocrystalline Y2O3 has been mostly investigated for applications in the field of de-NOx catalysts and phosphors for lighting, See M. Fokema and J. Y Ying, The selective catalytic reduction of nitric oxide with methane over scandium oxide, yttrium oxide and lanthanum oxide, App. Catal. B. 18, 71-77 (1998); Md. H. Zahir, T. Suzuki, Y. Fujishiro, and M. Awano, Synthesis and characterization of Sm3+-doped Y(OH)3 and Y2O3 nanowires and their NO reduction activity, J. of Alloys and Comp. 476, 335-340 (2009); C. Cannas, M. Casu, A. Musinu, G. Piccaluga, A. Speghini and M. Bettinelli, Synthesis, characterization and optical spectroscopy of a Y2O3—SiO2 nanocomposite doped with Eu3+, J. Non-Crystalline Solids 306, 193-199 (2002), each incorporated herein by reference in their entirety. The development of Y2O3 thin films has aroused great interest for their excellent properties such as high dielectric constant, low absorption, chemical stability and excellent thermal conductivity make them adequate for numerous technological applications. Different properties can be observed in rare earth doped films compared with bulk materials, making them interesting to study. Zahir et al. reported that Y2O3-alone showed quite high and stable catalytic activity for NO reduction at 500° C. in the presence of water vapor, See Md. H. Zahir, T. Suzuki, Y. Fujishiro, and M. Awano, Synthesis and characterization of Sm3+-doped Y(OH)3 and Y2O3 nanowires and their NO reduction activity, J. of Alloys and Comp. 476, 335-340 (2009), which is incorporated herein by reference in its entirety. Boffa et al. recently developed a niobia-silica mixed oxide microporous membrane that combines the open percolative pore structure of silica with increased thermal stability, and has a high selectivity for CO2, See V. Boffa, H. L. Castricum, R. Garcia, R. Schmuhl, A. V. Petukhov, D. H. A. Blank, and J. E. ten Elshof, Structure and Growth of Polymeric Niobia-Silica Mixed-Oxide Sols for Microporous Molecular Sieving Membranes: A SAXS Study, Chem. Mater., 21 (9), 1822-1828 (2009), incorporated herein by reference in its entirety.
- In view of the forgoing, the objective of the present invention is to provide a nanocomposite membrane with a Si—Y nanocomposite layer on an alumina support, a dip coating method of making the nanocomposite membrane, and a method of separating a mixture of gases with the nanocomposite membrane.
- According to a first aspect the present disclosure relates to a nanocomposite membrane including i) a membrane support comprising tubular α-Al2O3 ii) an intermediate layer comprising γ-Al2O3, wherein the intermediate layer is 300-1200 nm thick and coats a surface of the membrane support iii) a nanocomposite layer comprising SiO2 and Y2O3, wherein the nanocomposite layer is 25-150 nm thick and coats a surface of the intermediate layer, and wherein the nanocomposite layer is porous with an average largest radius micropore of 0.2-0.6 nm.
- In one embodiment, the intermediate layer comprises at least two distinct γ-Al2O3 layers, each distinct γ-Al2O3 layer being 150-600 nm thick.
- In one embodiment, the Y2O3 is in the form of nanoparticles with a largest dimension of 1-6 nm, the nanocomposite layer is in the form of a SiO2 matrix, and the Y2O3 nanoparticles are dispersed in or deposited onto the SiO2 matrix.
- In one embodiment, the nanocomposite layer is porous with an average mesopore radius of 1-4 nm.
- In one embodiment, the molar ratio of Si:Y in the nanocomposite membrane is 1:1 to 5:1.
- In one embodiment, the nanocomposite membrane has a membrane permeance of 1e−8−1e−6 mol/m2·sec·Pa for a first gas, and a membrane permeance of 1e−10−1e−9 mol/m2·sec·Pa for a second gas when a mixture of gas comprising the first gas and the second gas is fed through the nanocomposite membrane at a temperature of 100-650° C.
- In one embodiment, the first gas is H2, He, or both, and the second gas is N2, CO2, or both.
- In one embodiment, the nanocomposite membrane has a membrane permeance of 1e−8−1e−6 mol/m2·sec·Pa for a first gas, and a membrane permeance of 1e−101e−9 mol/m2·sec·Pa for a second gas when a mixture of gas comprising the first gas, the second gas, and up to 5 wt % of steam relative to the total weight of the mixture of gas is fed through the nanocomposite membrane.
- In one embodiment, the nanocomposite membrane has a permselectivity ranging from 60-400, wherein the permselectivity is calculated as the permeance of the first gas divided the permeance of the second gas.
- According to a second aspect, the present disclosure relates to a method of manufacturing the nanocomposite membrane, in one or more of its embodiments, by i) coating the membrane support comprising tubular α-Al2O3 with the γ-Al2O3 to form a membrane support coated with the intermediate layer ii) hydrolyzing a silica source with a mixture comprising water, an alcohol solvent, and a Y source with a sol-gel technique to yield a Si/Y sol-gel iii) dip coating the membrane support coated with the intermediate layer with the Si/Y sol-gel by a dip coating method and iv) calcining in the presence of oxygen at 500-700° C.
- In one embodiment, the membrane support is coated at least two times with the γ-Al2O3 to form an intermediate layer comprising at least two distinct γ-Al2O3 layers, each distinct γ-Al2O3 layer being 150-600 nm thick.
- In one embodiment, the method further comprises repeating the dip coating and the calcining.
- In one embodiment, the molar ratio of the silica source to the Y source is 1:1 to 5:1.
- In one embodiment, the silica source is tetraethyl orthosilicate and the Y source is Yttrium(III) nitrate or hydrates thereof.
- In one embodiment, the method further comprises adjusting the pH of the mixture to 0.5-4 by adding a mineral acid during the hydrolyzing.
- In one embodiment, the calcining is followed by cooling at a cooling rate of 0.1° C./min to 1.5° C./min to form the nanocomposite membrane.
- According to a third aspect, the present disclosure relates to a method of separating a mixture of gas comprising a first gas and a second gas involving i) introducing the mixture of gas into a gas feed side of a permeance cell comprising the gas feed side, a permeate side that opposes the gas feed side, and the nanocomposite membrane of the present disclosure, in one or more of its embodiments, wherein the nanocomposite layer of the nanocomposite membrane faces toward the gas feed side and forms a permeable barrier between the gas feed side and permeate side ii) applying a vacuum to the permeate side and iii) separating the first gas from the second gas by allowing the first gas to pass through the nanocomposite membrane and collect in the permeate side, and prohibiting the second gas from passing through the nanocomposite membrane and collect in the gas feed side.
- In one embodiment, the first gas has a permeance through the nanocomposite membrane of 1e−8−1e−6 mol/m2·sec·Pa and the second gas has a permeance through the nanocomposite membrane of 1e−10−1e−9 mol/m2·sec·Pa at 100-500° C.
- In one embodiment, the first gas is H2, He, or both, and the second gas is N2, CO2, or both.
- In one embodiment, a partial pressure of the mixture of gas introduced into the gas feed side is 110-200 kPa.
- The foregoing paragraphs have been provided by way of general introduction, and are not intended to limit the scope of the following claims. The described embodiments, together with further advantages, will be best understood by reference to the following detailed description taken in conjunction with the accompanying drawings.
- A more complete appreciation of the disclosure and many of the attendant advantages thereof will be readily obtained as the same becomes better understood by reference to the following detailed description when considered in connection with the accompanying drawings, wherein:
-
FIG. 1 shows powder X-ray diffraction patterns for the (a) SiO2 sample and the Si—Y—O composites of various Y content (b) Si/Y (2/1), (c) Si/Y (3/1) and (d) Si/Y (4/1) fired at 600° C. in air. -
FIG. 2 is a graph of TGA showing relative weight loss vs. T for Si/Y (3/1) as-prepared sample. -
FIG. 3A is a SEM image of a cross-section of Y-doped SiO2 membrane Si/Y (3/1). -
FIG. 3B is a SEM image of a cross-section γ-Al2O3 and its thickness. -
FIG. 3C is an enlarged SEM image of α-Al2O3. -
FIG. 4 is a TEM image of Si/Y (3/1) membrane cross section showing a first and a second layer of γ-Al2O3. -
FIG. 5A shows temperature dependence of gas permeances (H2, N2, He and CO2) for SiO2. -
FIG. 5B shows temperature dependence of gas permeances (H2, N2, He and CO2) for Y-doped SiO2 membranes under dry conditions. -
FIG. 6A shows time course of gas permeance through SiO2 (500° C., 150 kPa). -
FIG. 6B shows time course of gas permeance through Y-doped silica membranes in steam atmospheres (500° C., 150 kPa). -
FIG. 7A shows N2 adsorption/desorption isotherm for SiO2 powder sample before hydrothermal treatment at 500° C. for 4 h. -
FIG. 7B shows N2 adsorption/desorption isotherm for SiO2 powder sample after hydrothermal treatment at 500° C. for 4 h. -
FIG. 8A shows the BJH pore-size distributions of SiO2 powder sample before hydrothermal treatment at 500° C. for 4 h. -
FIG. 8B shows the BJH pore-size distributions of SiO2 powder sample after hydrothermal treatment at 500° C. for 4 h. -
FIG. 9A shows N2 adsorption/desorption isotherm for Si/Y (3/1) powder sample before hydrothermal treatment at 500° C. for 4 h. -
FIG. 9B shows N2 adsorption/desorption isotherm for Si/Y (3/1) powder sample after hydrothermal treatment at 500° C. for 4 h. -
FIG. 10A shows BJH pore-size distributions of Si/Y (3/1) powder sample before hydrothermal treatment at 500° C. for 4 h. -
FIG. 10B shows BJH pore-size distributions of Si/Y (3/1) powder sample after hydrothermal treatment at 500° C. for 4 h. -
FIG. 11 shows N2 permeance (measured by nano-permporometer) as a function of Kelvin radius of Si/Y (3/1) membranes before () and after (O) hydrothermal treatment for 4 h. -
FIG. 12 shows pore size distribution measured by nano-permporometer of Si/Y (3/1) membranes before () and after (O) hydrothermal treatment for 4 h. - Referring now to the drawings.
- According to a first aspect the present disclosure relates to a nanocomposite membrane including a membrane support comprising tubular α-Al2O3. High purity α-Al2O3 is known to have chemical stability in acid, base and other reactive environments and also has high thermal and hydrothermal stability. High purity α-Al2O3 is used in various inorganic membranes, and is a preferred material from which to make membrane supports. The tubular α-Al2O3 support has no restriction other than it must be macroporous. As used herein, “macroporous” refers to porous materials with largest pore diameters ranging from 50-1000 nm. In one embodiment, the tubular α-Al2O3 support comprises macrospores with diameters ranging from about 50-1000 nm, preferably 60-800 nm, preferably 70-600 nm, preferably 80-400 nm, preferably 90-200 nm, preferably 95-150 nm. The α-Al2O3 membrane support, according to one embodiment, includes a first end, a second end, and an inner channel having surfaces defined by porous walls and extending through the support from the first end to the second end. According to another embodiment, the α-alumina membrane support is in the form of a honeycomb monolith. An α-Al2O3 support comprising “an inner channel” includes a support comprising one inner channel as well as a support comprising a plurality of inner channels, such as a plurality of parallel inner channels extending through the support from the first end to the second end. The inner channels may be in the form of capillary structures. Alternatively, the inner channels may be in the form of a non-capillary structure where the channels are formed as a porous labyrinth within a matrix of α-Al2O3 or a bulk structure of α-Al2O3 particles (see for example
FIG. 3C ). - The tubular α-Al2O3 support may be in the shape of a cylinder with an inner diameter of 4-10 mm, preferably 5-9 mm, more preferably 6-8 mm and an outer diameter of 5-13 mm, preferably 7-12 mm, preferably 9-11 mm, and may have a wall thickness ranging from about 1 mm to about 3 mm. Pall Corporation provides alumina supports in single tube and multi-channel form under the product name Membralox®. The cylindrical shape of the membrane support may be made by a variety of methods, for example an extrusion and sintering process. In one embodiment, the tubular α-Al2O3 support may be in the shape of a disk for placement inside of a permeance cell. In this scenario a macro surface of the α-Al2O3 surface is substantially flat. The tubular α-Al2O3 may have a % porosity of 20-60%, or 25-55%, or 30-50%, or 35-45% and the surface area preferably may be in the range of 100-400 m2/g, or 150-350 m2/g, measured by the B.E.T. method. The pore volume of the α-Al2O3 in one embodiment is in the range of 0.5-1.5 ml/g, 0.6-1.3 ml/g, 0.7-1.1 ml/g measured by nitrogen adsorption.
- In addition to α-Al2O3, the membrane support may instead be made from materials that are known to be porous or that can be made to be porous. For example, other alumina polymorphs may be used in addition to, or in lieu of α-Al2O3, including γ-Al2O3, η-Al2O3, θ-Al2O3, χ-Al2O3, κ-Al2O3, and δ-Al2O3, or mixtures thereof. Other exemplary non-alumina membrane support materials may include, but are not limited to silica, titania, magnesia, zirconia, zeolites, carbon, phosphorus, gallium, germanium, yttria, niobia, lanthana, stainless steel and combinations thereof. The membrane support preferably comprises at least 90%, 95% or 98% by weight based on the total weight of the membrane support of α-Al2O3. The membrane support preferably consists of α-Al2O3.
- The nanocomposite membrane also includes an intermediate layer comprising γ-Al2O3, wherein the intermediate layer is 300-1200 nm, preferably 400-1100 nm, more preferably 500-1000 nm, more preferably 600-900 nm, more preferably 650-800 nm thick and coats a surface of the membrane support. The intermediate layer may be obtained from a boehmite sol (i.e. aluminum oxide hydroxide, γ-AlO(OH) mineral). The intermediate layer may form a thin and defect-free coating of the α-Al2O3 substrate that covers the roughness or bumpy surface of the α-Al2O3 support. In one embodiment, the intermediate layer is distinct from the membrane support, whereby the γ-Al2O3 material does not penetrate inside of the α-Al2O3 support. The intermediate layer preferably covers greater than 95%, greater than 96%, greater than 97%, greater than 98%, greater than 99%, greater than 99.5% of the surface of the membrane support.
- In this disclosure, “porosity” is an index showing a ratio of void volume with respect to an volume of the support layer. The porosity can be calculated, for example, by taking a photograph of the cross sectional structure, measuring a total void area using the photograph, and calculating the porosity as a ratio of void area with respect to an entire cross sectional area of the support or layer of interest in the nanocomposite membrane. Alternatively, the porosity can be measured and/or calculated using N2 adsorption/desorption isotherms (e.g. using Barret-Joyner-Halenda or non-local density functional theory), permporometry methods, and the like.
- In a preferred embodiment, the γ-Al2O3 is mesoporous. As used herein, “mesoporous” refers to porous materials with largest pore diameters ranging from about 2-50 nm. The intermediate layer may comprises mesopores with diameters ranging from about 2-50 nm, preferably 3-45 nm, preferably 4-40 nm, preferably 5-35 nm. The intermediate layer of the present disclosure may have a % porosity of 30-70%, or 35-65%, or 40-65% and a surface area preferably may be in the range of 200-400 m2/g, or 250-395 m2/g, or 300-390 m2/g measured by the B.E.T. method. The pore volume of the intermediate layer comprising γ-Al2O3 in one embodiment is in the range of 0.3-1.0 ml/g, preferably 0.35-0.8 ml/g, more preferably 0.35-0.6 ml/g measured by nitrogen adsorption.
- The intermediate layer comprising γ-Al2O3 can be a single layer or a multilayer. In one embodiment, the intermediate layer comprises at least two distinct γ-Al2O3 layers, each distinct γ-Al2O3 layer being 150-600 nm, preferably 200-550 nm, more preferably 250-500 nm, more preferably 300-450 nm, more preferably 325-400 nm thick. When multilayers of γ-Al2O3 are present, the layers may have decreasing pore sizes. In a preferred embodiment, the pore sizes of the multilayers are substantially similar, but vary in terms of coverage density, wherein the γ-Al2O3 layers that are separated the furthest from the α-Al2O3 support have a higher density. For example, if the α-Al2O3 support is coated with a first layer of γ-Al2O3, followed by a second layer of γ-Al2O3 that coats the first layer γ-Al2O3, the second layer of γ-Al2O3 is advantageously be more dense than the first layer.
- The nanocomposite membrane also includes a nanocomposite layer comprising SiO2 and Y2O3, wherein the nanocomposite layer is 25-150 nm, preferably 50-145 nm, preferably 75-140 nm, preferably 80-135 nm, preferably 85-130 nm, preferably 90-125 nm, preferably 95-120 nm thick and coats a surface of the intermediate layer. In one embodiment the nanocomposite layer is both mesoporous and microporous, and therefore includes a mixture of both mesopores and micropores. The term “microporous” refers to porous materials with largest pore diameters ranging from about 0.2 nm to about 2 nm. In one embodiment, the micropores in the nanocomposite layer have an average largest radius of 0.2-0.6 nm, preferably 0.2-0.5 nm, preferably 0.2-0.4 nm, preferably 0.2-0.3 nm. In one embodiment, the mesopores in the nanocomposite layer have an average mesopore radius of 1-4 nm, preferably 2-4 nm, preferably 3-4 nm. The nanocomposite layer preferably covers greater than 95%, greater than 96%, greater than 97%, greater than 98%, greater than 99%, greater than 99.5% of the surface of the intermediate layer.
- The Y2O3 present in the nanocomposite layer is preferably in the form of a nanomaterial (having a size between 1 and 100 nm). The Y2O3 nanomaterial may be in the form of various shapes, for example nanoparticles, nanosheets, nanoplatelets, nanocrystals, nanospheres, nanorectangles, nanotriangles, nanopentagons, nanohexagons, nanoprisms, nanodisks, nanocubes, nanowires, nanofibers, nanoribbons, nanorods, nanotubes, nanocylinders, nanograunules, nanowhiskers, nanofibers, nanoflakes, nanofoils, nanopowders, nanoboxes, nanostars, tetrapods, nanobelts, nanourchins, nanoflowers, etc. and mixtures thereof.
- In one embodiment, the Y2O3 is in the form of nanoparticles with a largest dimension of 1-6 nm, preferably 1-5 nm, preferably 1-4 nm, more preferably 2-3 nm. The nanocomposite layer may be in the form of a SiO2 matrix, whereby the Y2O3 nanoparticles are dispersed in or deposited onto the SiO2 matrix. It is preferable for the Y2O3 nanoparticles to be insoluble in the SiO2 matrix. Due to the insolubility, these Y-metal ions may compete for non-bridging oxygen in the SiO2 matrix to complete their coordination.
- In one embodiment, the molar ratio of Si:Y in the nanocomposite membrane is 1:1 to 5:1, preferably 1.5:1 to 4.5:1, preferably 2:1 to 4:1, preferably 2.5:1 to 3.5:1. In a preferred embodiment, the molar ratio of Si:Y in the nanocomposite membrane is about 3:1. The about 3:1 Si:Y ratio is preferred in the nanocomposite membrane because the pore size distribution of the nanocomposite layer is substantially the same before hydrothermal treatment and after hydrothermal treatment involving heating the nanocomposite membrane to at least 600° C., at least 550° C., at least 500° C. for at least 12 hr, at least 14 hr, at least 16 hr, at least 18 hr, at least 20 hr. The hydrothermal treatment may also include the addition of steam, for example about 3 wt % of steam relative to the total weight of a gaseous atmosphere used during the thermal hydrotreatment. In one embodiment, the pore radius (including both micropores and mesopores) in the nanocomposite layer differ by no more than 10%, 9%, 8%, 7%, 6%, 5%, 4%, 3%, 2%, 1% before and after the hydrothermal treatment.
- It should be clear to those skilled in the art that oxides of yttrium are not the only materials that can be combined with silica in the nanocomposite layer. Other oxides that can be employed are those of B, Al, P, Ga, Ge, As, In, Sn, Sb, Sc, Ti, V, Zr, Nb, La, Hf, Ce, Dy, Er, Eu, Gd, Nd, Sm, Yb, and Ta, that can form bonds with silica. Similarly, it should be clear those skilled in the art that the combinations are not restricted to binary combinations, and that multiple component combinations are possible.
- In a macro view, the shape of the nanocomposite membrane is not meant to be limiting, and the membrane may be in the form of various shapes, for example, flat (e.g. for a disc-shaped membrane), bent, curved (e.g. a cylinder shaped membrane), rippled, etc. The shape of the membrane may be constructed by forming or shaping the membrane support for a particular application, then coating the membrane support by the methods discussed hereinafter.
- As used herein, “permeance” or “membrane permeance” is defined as the degree to which the nanocomposite membrane transmits a gas across the nanocomposite membrane, and is represented by the ratio of gas flux, J (mol/m2s) with a steam pressure of 150 kPa. In one embodiment, the nanocomposite membrane has a membrane permeance of 1e−8−1e−6 mol/m2·sec·Pa, preferably 1e−8−8e−7 mol/m2·sec·Pa, preferably 1e−8−6e−7 mol/m2·sec·Pa, preferably 1e−8−4e−7 mol/m2·sec·Pa, preferably 1e−8−3e−7 mol/m2·sec·Pa for a first gas, and a membrane permeance of 1e−10−1e−9 mol/m2·sec·Pa, preferably 2e−10−1e−9 mol/m2·sec·Pa, preferably 4e−10−1e−9 mol/m2·sec·Pa, preferably 6e−10−1e−9 mol/m2·sec·Pa for a second gas when a mixture of gas comprising the first gas and the second gas is fed through the nanocomposite membrane at a temperature of 100-650° C. The first gas may be H2, He, or both. The second gas may be N2, CO2, or both. For example, under these conditions the nanocomposite membrane has a membrane permeance of 4e−8−4e−7 mol/m2·sec·Pa when the first gas is He, and 1e−8−9e−8 mol/m2·sec·Pa when the first gas is H2. Further in one example, the nanocomposite membrane has a membrane permeance of 5e−10−1e−9 mol/m2·sec·Pa when the second gas is N2, and 5e−10−1e−9 mol/m2·sec·Pa when the second gas is CO2. In one embodiment, the membrane permeance of the nanocomposite membrane is determined after first drying the nanocomposite membrane for at least 1 hour, preferably at least 2 hours, more preferably at least 3 hours at a temperature of at least 100° C., preferably at least 200° C., more preferably at least 300° C. to remove adsorbed water from the micropores and/or mesopores of the nanocomposite layer.
- In one embodiment, the nanocomposite membrane has a membrane permeance of 1e−8−1e−6 mol/m2·sec·Pa, preferably 1e−8−8e−7 mol/m2·sec·Pa, preferably 1e−8−6e−7 mol/m2·sec·Pa, preferably 1e−8−4e−7 mol/m2·sec·Pa, preferably 1e−8−3e7 mol/m2·sec·Pa for a first gas, and a membrane permeance of 1e−10−1e−9 mol/m2·sec·Pa, preferably 2e−10−1e−9 mol/m2·sec·Pa, preferably 4e−10−1e−9 mol/m2·sec·Pa, preferably 6e−10−1e−9 mol/m2·sec·Pa for a second gas when a mixture of gas comprising the first gas, the second gas, and steam is fed through the nanocomposite membrane. In one embodiment, up to 10 wt %, preferably up to 7 wt %, preferably up to 5 wt %, preferably up 4 wt %, preferably up to 3 wt % of steam is present in the mixture of gas, relative to the total weight of the mixture of gas. For example, under these conditions the nanocomposite membrane has a membrane permeance of 1e−7−1e−6 mol/m2·sec·Pa when the first gas is He, and 5e−8−9e−8 mol/m2·sec·Pa when the first gas is H2. Further in one example, the nanocomposite membrane has a membrane permeance of 5e−10−8e−9 mol/m2·sec·Pa when the second gas is N2, and 5e−10−8e−9 mol/m2·sec·Pa when the second gas is CO2.
- In one embodiment, the membrane permeance of the nanocomposite membrane changes by less than 5%, preferably less than 4%, preferably less than 3%, preferably less than 2%, preferably less than 1.5%, preferably less than 1% in terms of both the first gas and the second gas in the presence of steam when the permeance is evaluated for up to 25 hours, up to 30 hours, up to 35 hours at temperature of about 500° C. The presence of the Y2O3 nanoparticles in the nanocomposite layer may form a rigid network of Si—O—Y atoms, whereby the Y atoms impart stability to the SiO2 matrix and prevent collapsing and/or expanding of the pores (i.e. both micropores and mesopores) present within the nanocomposite layer. This rigidity may provide stable permeance through the nanocomposite membrane of the present disclosure.
- In one embodiment, the nanocomposite membrane has a permselectivity ranging from 600-400, or 62-395, or 64-390, or 66-388, or 70-386 wherein the permselectivity is calculated as the permeance of the first gas divided the permeance of the second gas.
- According to a second aspect, the present disclosure relates to a method of manufacturing the nanocomposite membrane, in one or more of its embodiments, by coating the membrane support comprising tubular α-Al2O3 with γ-Al2O3 to form a membrane support coated with the intermediate layer.
- A sol is defined here as collection of suspended particles. The disclosure uses a single dilute sol dipping solution or a series of sol dipping solutions containing sols of the same or different particle sizes. The dipping solutions are used to coat a support. Each coating procedure may be followed by a calcination step. For example, the tubular α-Al2O3 may be coated with the γ-Al2O3 using a boehmite (AlOOH) sol (γ-Al2O3). Boehmite sols may be prepared by carefully controlling the hydrolysis of aluminum alkoxides (e.g. aluminum isopropoxide). Further acid peptization techniques may also be used to control the particle size of the resulting boehmite precipitate. For example, the following procedure may be used for preparing the membrane support coated with the intermediate layer. A quantity of aluminum isopropoxide is added to distilled water at room temperature. The mixture is heated to 80° C. with 0.5 h with high speed stirring and is maintained at this temperature for 3-24 h for the hydrolysis of the isopropoxide and the formation of a boehmite (AlOOH) precipitate. The precipitate is then heated to 90-95° C. and is peptized using a quantity of acetic acid with a molar ratio of acetic acid/aluminum isopropoxide in the range of 0.04-0.15. Peptization refers to the breakup of large oxide precipitate particles by acid treatment. The membrane support coated with the intermediate layer is than prepared by coating the α-Al2O3 support with the γ-Al2O3 particles so as to make its external pore structure (in the surface region) more uniform. A single layer of the γ-Al2O3 particles may be used of varying or constant size. Alternatively, multiple layers of the γ-Al2O3 particles of the same or different size may be used.
- In one embodiment, the membrane support is coated at least two times with the γ-Al2O3 to form an intermediate layer comprising at least two distinct γ-Al2O3 layers, each distinct γ-Al2O3 layer being 150-600 nm, preferably 200-550 nm, more preferably 250-500 nm, more preferably 300-450 nm, more preferably 325-400 nm thick.
- The method also involves hydrolyzing a silica source with a mixture comprising water, an alcohol solvent, and a Y source with a sol-gel technique to yield a Si/Y sol-gel. In one embodiment, the silica source is tetraethyl orthosilicate (TEOS). The silica source is not restricted to TEOS and may also be tetramethylorthosilicate (TMOS), ethyltriethoxysilane, silane, chlorosilane, and combinations thereof. In one embodiment, the silica source is added to the mixture, which can be performed portion-wise, in one batch, or through any slow addition technique known to those of ordinary skill in the art. The alcohol solvent may include methanol, ethanol, propanol, isopropanol, butanol, and the like, preferably ethanol. Hydrolyzing the silica source may take place for 0.5-24 hours, or 1-20 hours, or 2-16 hours, or 3-12 hours.
- In one embodiment, the Y source is yttrium(III) nitrate of hydrates thereof. Although, other sources of Yttrium may be used in the present method, including, but not limited to yttrium fluoride, yttrium chloride, yttrium iodide, yttrium acetate, yttrium trifluoromethanesulfonate, yttrium acetylacetonate, yttrium carbonate, and yttrium trifluoroaceate, and hydrates thereof. In one embodiment, the molar ratio of the silica source to the Y source is 1:1 to 5:1, preferably 1.5:1 to 4.5:1, preferably 2:1 to 4:1, preferably 2.5:1 to 3.5:1.
- In one embodiment, the method further comprises adjusting the pH of the mixture to 0.5-4, preferably 0.7-3, preferably 0.9-2, preferably 1.1-1.5, preferably about 1.2 by adding a mineral acid during the hydrolyzing. Exemplary mineral acids include hydrochloric acid, nitric acid, phosphoric acid, sulfuric acid, boric acid, hydrofluoric acid, hydrobromic acid, perchloric acid, hydroiodic acid, and the like. In a preferred embodiment, the mineral acid is nitric acid. After adjusting the pH, hydrolyzing the silica source may be resumed for an additional 0.5-24 hours, or 1-20 hours, or 2-16 hours, or 3-12 hours.
- The method also involves dip coating the membrane support coated with the intermediate layer with the Si/Y sol-gel by a dip coating method. the dip-coating method may involve one or more of i) immersing the substrate (e.g. the membrane support coated with the intermediate layer) into the Si/Y sol-gel at a constant speed ii) holding the substrate inside the Si/Y sol-gel for a predetermined amount of time, such as more than 1 second, more than 2 seconds, more than 3 seconds, for than 4 seconds, more than 5 seconds, more than 10 seconds, more than 30 seconds, more than 1 minute, more than 5 minutes to absorb a portion of Si/Y sol onto at least one surface of the substrate (e.g. the membrane support coated with the intermediate layer) iii) withdrawing the substrate coated with the Si/Y sol from the Si/Y sol-gel at a constant speed, wherein the speed determines the thickness of the coating, with faster withdrawal giving thicker coating material) iv) draining excess liquid from the surface of the coated substrate v) evaporating the solvent from the Si/Y sol that coats the substrate, forming the thin layer of the nanocomposite layer. For volatile solvents, such as alcohols, evaporation may begin during the withdrawing and draining steps. In one embodiment, the dip-coating method is performed in a continuous fashion, whereby the steps are carried out directly after one another.
- The method for manufacturing the nanocomposite membrane then involves calcining in the presence of oxygen at 500-700° C., preferably 525-675° C., preferably 550-650° C., preferably 575-625° C. In one embodiment, prior to the calcining, the Y present in the nanocomposite layer may be fully reduced to the pure metal by a flow of hydrogen at elevated temperature, then the reduced Y may be calcined in air or in the presence of O2 to form the Y2O3 nanoparticles. In one embodiment, the calcining is followed by cooling at a cooling rate of 0.1° C./min to 1.5° C./min, preferably 0.2° C./min to 1.0° C./min, preferably 0.3° C./min to 0.7° C./min to form the nanocomposite membrane. In one embodiment, the method further comprises repeating the dip coating and the calcining.
- According to a third aspect, the present disclosure relates to a method of separating a mixture of gas comprising a first gas and a second gas involving introducing the mixture of gas into a gas feed side of a permeance cell comprising the gas feed side, a permeate side that opposes the gas feed side, and the nanocomposite membrane of the present disclosure, in one or more of its embodiments, wherein the nanocomposite layer of the nanocomposite membrane faces toward the gas feed side and forms a permeable barrier between the gas feed side and permeate side. In one embodiment, the mixture of gas introduced into the gas feed side of the permeance cell has a partial pressure of 110-200 kPa, preferably 120-190 kPa, more preferably 130-180 kPa, even more preferably 140-160 kPa. Alternatively, the partial pressure of the mixture of gas introduced into the gas feed side of the permeance cell is about atmospheric pressure (i.e. about 101.3 kPa). In one embodiment, the method also involves applying a vacuum to the permeate side of the permeance cell. In one embodiment, the mixture of gas is heated to a temperature of 100-500° C., preferably 150-475° C., preferably 200-450° C. for the method of separating. In one embodiment, the first gas is H2, He, or both, and the second gas is N2, CO2, or both.
- The permeance cell used for separating the mixture of gas may be any shape so long as the nanocomposite membrane can be secured inside the permeance cell to accomplish the gas mixture separation. For example, the permeance cell may be a cylindrical membrane module. The permeance cell may also include, for example, at least one flow-control valve to control the flow of the mixture of gas introduced into the cell, a vacuum pump or related vacuum-generating device to provide the vacuum to the permeate side, a water source and a plunger pump for introducing water in the form of steam into the permeance cell in addition to the mixture of gas, a constant temperature furnace (e.g. a clamshell furnace, a tube furnace, etc.) for heating the mixture of gas and/or for converting the water source into steam, ferrules (e.g. graphite ferrules) for securing the nanocomposite membrane in place within the permeance cell, gas feed lines, permeate lines, and retentate lines (i.e. lines connected to the gas feed side of the permeance cell) for transporting various gases in and out of the permeance cell, and any other component that is known to those of ordinary skill in the art of permeance cells and gas-gas separations.
- The method also involves separating the first gas from the second gas by allowing the first gas to pass through the nanocomposite membrane and collect in the permeate side, and prohibiting the second gas from passing through the nanocomposite membrane and collect in the gas feed side.
- In one embodiment, the first gas has a permeance through the nanocomposite membrane of 1e−8−1e−6 mol/m2·sec·Pa, preferably 1e−8−8e−7 mol/m2·sec·Pa, preferably 1e−8−6e−7 mol/m2·sec·Pa, preferably 1e−8−4e−7 mol/m2·sec·Pa, preferably 1e−8−3e−7 mol/m2·sec·Pa and the second gas has a permeance through the nanocomposite membrane of 1e−10−1e−9 mol/m2·sec·Pa, preferably 2e−10−1e−9 mol/m2·sec·Pa, preferably 4e−10−1e−9 mol/m2·sec·Pa, preferably 6e−10−1e−9 mol/m2·sec·Pa at 100-500° C.
- In one embodiment, the method further involves exposing the nanocomposite membrane to a steam N2 steam at 400-600° C., preferably 420-580° C., more preferably 440-560° C., followed by drying the nanocomposite membrane by exposing the nanocomposite membrane to a dry N2 stream at the same temperature prior to the separating. The permeance may then be calculated from an observed pressure difference across the nanocomposite membrane and the permeation rate, which may be obtained using a calibrated critical nozzle placed in between the permeation cell and the vacuum pump or vacuum generating device.
- The examples below are intended to further illustrate protocols for preparing, characterizing and using the nanocomposite membrane and are not intended to limit the scope of the claims.
- The complete preparation of γ-Al2O3 (Intermediate layer) and coating procedure over α-Al2O3 support is described elsewhere. See Md. H. Zahir, K. Sato, and Y. Iwamoto, “Development of Hydrothermally Stable Derived La2O3-Doped Ga2O3—Al2O3 Composite Mesoporous Membrane”, J. Membr. Sci. 247, 95-101 (2005); Md. H. Zahir, K. Sato, H. Mori, Y. Iwamoto, M. Nomura, and S. Nakao, Preparation and properties of hydrothermally stable-alumina-based composite mesoporous membranes, J. Am. Ceram. Soc. 89, 2874-2780 (2006), each incorporated herein by reference in their entirety. A tubular type support was used for the membrane fabrication.
- Synthesis Y2O3-Doped SiO2 Nanocrystalline Precursor by Sol-Gel Method for Top Layer
- Synthesis composition of the reactants is an important factor in deciding the structure of the final membrane. The changes in reactant parameters can influence the porosity of the gel and the gas permeation behavior of the membrane. Sol-gel synthesis parameters are also important to realize membranes with minimum defects and hence high selectivity. Silica sols were synthesized herein by a single step hydrolysis process as reported by Uhlmann et al. See D. Uhlmann, S. Liu, B. P. Ladewig and J. C. Diniz da Costa, Cobalt-doped silica membranes for gas separation, J. Membr. Sci. 326 316-321 (2009), incorporated herein by reference in its entirety. The degree of hydrolysis and condensation was varied by changing the amount of catalyst, the amount of water used, and by aging the sol at room temperature.
- TEOS was hydrolyzed and condensed in an ethanol solution mixed with known amounts of Y(NO3)2.6H2O and water. Y-doped silica sol with a composition of Si/Y ratio (3/1) was prepared as follows. First, 8.34 g of TEOS was added to a mixture of 50 g of ethanol and 11.49 g of Y(NO3)2.6H2O, followed by hydrolysis and condensation of 12 h. Additional water was added to bring the total weight to 500 g. The pH of the sol solution was adjusted to pH 1.2 by the addition of 2.0 g of HNO3, and the mixture was subjected to another 12 h condensation.
- Si/Y colloidal sols were coated on the substrate by dip coating methods and fired for 1 h at 600° C. in air with a heating and cooling rate of 0.5° C./min. The whole process of dipping and calcining is repeated once to repair any defects in the first silica membrane layer. The SiO2 membrane was also fabricated by using the same procedure and these samples are called as-prepared samples.
- Y2O3-doped silica gels were prepared using the quick-drying process. Briefly, Y-doped silica sols were dropped into a Pt dish maintained at 180° C., resulting in gel formation via an instantaneous drying process. Dry gels were fired in air at 600° C. for 1 h. The dry gels were ground in an agate mortar and then analyzed using XRD analysis. XRD patterns were identified using an x-ray diffractometer (Rigaku Denki Co., Tokyo, Japan, RINT-2000V) with a CuKα radiation source of 50 keV and 200 mA with a monochromator over a diffraction angle range 2θ from 10 to 80° at a scan rate of 2°/min. Nitrogen adsorption and desorption experiments were conducted using the Quantachrome Autosorb-IC automated gas sorption system (Quantachrome Instruments Co., Boynton Beach, Fla.). Before the measurements, the samples were first degassed at 350° C. for 3 h under vacuum. The pore-size distribution measurements were conducted directly on the membrane by nano-permporometer (Seika, Japan).
- To understand the hydrothermal stability of the CZA system, the as-prepared samples were exposed to steam using a Teflon-lined stainless-steel autoclave, maintaining 3 vol % wet (steam) gas streams were fed to the heated module at 500° C. All samples were heat treated at 500° C. because the multilayered-membrane reactor system could be operated at 500° C. 5 Steam was generated from a water reservoir kept at 80° C.
- Membrane gas permeance was performed in the temperature range of 100-500° C. Prior to the permeance measurements the membranes were dried for 3 hours at 300° C. to remove adsorbed water from the micropores. Multilayer tubular support was placed in stainless-steel permeance cells with the micropores top-layer at the feed side. The permeance is defined as ratio of the gas flux, J (mol/m2s) with steam pressure of 150 kPa.
- Hydrothermal stability tests of the membranes were performed observing gas permeance changes for temperatures ranging from 100°-500° C. A mixture of gas was fed on the outside (upstream) of a cylindrical membrane module under atmospheric pressure, while the permeate side (downstream) was evacuated by a vacuum pump. The feed gas flow rate was controlled by the flow control-valve before introducing water from a plunger pump. And the feed was preheated in a constant temperature furnace before fed to the test section through a thin bed of glass beads. The partial pressure of H2O in the feed gas stream was kept at 150 kPa. After exposing the membrane to the streamed N2 stream at 500° C. for specified time intervals, the membrane was dried completely in a pure N2 stream at the same temperature before observing single gas permeance (N2, H2, He). The permeance was calculated from the observed pressure difference across the membrane and the permeation rate, which was obtained by a calibrated critical nozzle placed between the permeation cell and the vacuum pump. After specified time intervals of hydrothermal stability tests, the temperature dependency of single gas permeance (N2, H2, He and CO2) was observed in a
temperature range 300°-500° C. More than five measurements were made and the average value was recorded. - It has been reported that the rare-earths (RE) ions in silicate probably enter as network modifiers due to the poor solubility of RE into the silica matrix. Due to insolubility, these metal ions compete for non-bridging oxygen in order to complete their coordination. Very recently, a limited number of research works has been published on high quality metal-doped silica membranes. This includes doping the silica matrix with nickel and cobalt. In all cases the metal oxide in the silica matrices of the membranes were chemically reduced to pure metal by a flow of hydrogen at elevated temperature, particularly in the case of Ni-doped silica. Formation of nanocrystalline RE silicates (RE=Y) inside or at the surface of amorphous SiO2 matrix could be possible upon heat treatment in air.
FIG. 1 shows XRD spectra of SiO2 and Y-doped SiO2 powder samples calcined at 600° C. in air for 1 h. They are typical of amorphous materials and are very similar to the pattern of amorphous silica. No peculiar evolution was observed after heat treatment up to 600° C. X-ray diffraction patterns of SiO2 and Y-doped SiO2 are similar and all spectra have only one dispersive broad peak, which indicates that all samples are non-crystalline solids. The heat treatment of samples in air using a furnace at 600° C. for 1 h has minimal effect on the structure of un-doped and doped silica. However, the broad peak was shifted slightly to the higher diffraction angle when the Si/Y was (1/4). The peak intensity of Si/Y (3/1) was less than that of the un-doped SiO2. This result also suggested that Y-doped into SiO2 existed as like noncrystalline compounds, such as extremely fine particles that are undetectable by XRD or as Y composites with SiO2. Since there is no evolution either of the Y-based nanoparticles or of the SiO2 after heat treatment at 600° C. Therefore, we have decided to fully investigate only the sample heated at 600° C., which is characterized by a lower amount of the defects typical of sol-gel silica. - Initially, we have synthesized SiO2 and Y-doped SiO2 powders samples of various Y contents (Si/Y=4/1, 3/1 and 2/1) by sol-gel techniques. Although it has been reported that the N2 adsorption isotherm of the silica gel produced a bi-modal pore size distribution according to the Horvath-kawazoe (H-K) analysis, See G. Horváth, K. Kawazoe, Method for the calculation of effective pore size distribution in molecular sieve carbon, J. Chem. Eng. Jpn. 16, 470-475 (1983), incorporated herein by reference in its entirety. However, such a distribution for the SiO2 sample was not observed. The detail pore size distribution under dry and wet conditions are given in the following section. In the case of Si/Y (2/1) sample had a bimodal pore size distribution with pore diameter ca. 5 nm. Moreover, the pore volume was decreased after hydrothermal treatment of Si/Y (2/1). A sharp peak was observed with narrow pore size distribution for the Si/Y (4/1). The pore volume was also decreased after hydrothermal treatment of Si/Y (4/1) sample. In the case of Si/Y (3/1), the pore size distribution was unchanged before and after hydrothermal treatment. Therefore, the remaining data were collected by Si/Y (3/1) sample. The SiO2 sample was tested for the purpose of comparison.
- TG curve of Si/Y (3/1) powder sample is shown in
FIG. 2 . The mass loss which takes place below 100° C. is probably due to the physical desorption of water and the evaporation of Si/Y nanocomposite. From the TG-DTA curves, it has been observed that four major weight losses for this nanocomposite. Abrupt decomposition was not observed in this case. The huge loss of weight was located in between 200° and 480° C. After this, further weight loss of 7.09% was found to be up totemperature 500° C. Overall there was a total weight loss of 45 wt % when Si/Y gels were heated from room temperature to 550° C. Therefore, all the samples were calcined at 600° C. for 1 h in air. A dehydrates at ca. 90° C., successively loses organic molecules by two steps in the temperature range of 97-350° C., with a sharp exothermic peak. The sharpest exothermic peak is located in between 120 and 125° C. Another exothermic peak was observed at around 290° C. A weak exothermic peak in the last step of the decomposition was close to 500° C. The possible processes that take place as the temperature increases are elimination of physically adsorbed water and ethanol, oxidation of residual organics, relaxation of the silica skeleton, condensation of adjacent hydroxyls and segregated hydroxyls, and viscous sintering, in that order. -
FIG. 3A shows a SEM photo of typical cross-section of a Y-doped silica membrane (Si/Y=3/1). A thin Y-doped silica layer effective for the selective gas permeation can be seen on an α-Al2O3 particle-γ-Al2O3. The γ-Al2O3 (coated twice, about 2.5 μm thick) intermediate layer (FIG. 3B , covering completely the roughness (bumps) of the support surface (FIG. 3C ). The thickness of this active separation layer was less than ˜100 nm, obtained after 2 times dipping. The TEM micrograph indicates that the γ-Al2O3 layer has a very clear two types of layers due to two times coating of γ-Al2O3 as shown inFIG. 4 . Each layer thickness was approximately 350 nm. The color difference between the two γ-Al2O3 layers was highly visible which is shown in TEM micrograph. The second layer has a lighter appearance. Since capillary forces play an important role in the layer formation, this additional layer can result in a denser second γ-Al2O3. The color difference is not caused by a difference in pore size. This was checked by permporometry in previous work, See Md. H. Zahir, S. Fujisaki, K. Sato, T. Nagano and Y. Iwamoto, Mesoporous CeO2—ZrO2-y-Al2O3 nanocomposite membranes exhibiting remarkable hydrothermal stability, Desalination and Water Treatment, 2, 223-230 (2009), incorporated herein by reference in its entirety. The boehmite sol did not penetrate inside the macroporous α-Al2O3 support, which might be due to the quick heat treatment process. Vos et al. also reported a TEM image of doubly coated γ-Al2O3, however, the image did not give visible difference between first layer and α-Al2O3 support, See R. M. de Vos, H. Verweij, Improved performance of silica membranes for gas separation, Journal of Membrane Science 143, 37-51(1998), incorporated herein by reference in its entirety. The methods disclosed herein are quite effective to make a thin separation layer without any appreciable pinholes as shown in the following section. -
FIGS. 5A and 5B shows dry gases permeance results for SiO2 and Y-doped SiO2 membranes as a function of temperature. The permeance data are not corrected for the support resistance since the permeance through the support is significantly higher than through the silica layer. H2, CO2 and N2 permeance are independent of the pressure. H2 and CO2 permeance are slightly dependent on pressure, if a smaller pressure difference than 0.5 bar is used. This effect is found over the whole temperature range. The membranes have reproducible high permeances (3.21×10−7 mol/m2s kPa) for He and much lower permeances for CO2, and N2. The SiO2 membranes showed a slight increase of permeance with increasing temperature for He, H2, and a slight decrease for CO2 and N2. Typically the permeation of gases followed an activated transport flux or temperature dependency, with best helium permeation result of 3.11×10−7 mol/m2s kPa for SiO2 membrane. The permeance and Fα values obtained compare favorably with literature results. He permeance at 200° C. is 2.44×10−7 mol/m2s kPa with Fα>210 for He/CO2. Previously reported values were 1.6×10−6 mol/m2·s·Pa and 43, respectively. The SiO2 calcined at 600° C. have a Fα=154 for H2/CO2 with a H2 permeance of 6×10−8 mol/m2s kPa at 400° C. The permselectivities for H2/CO2, H2/N2 and N2/O2 increase with increasing temperature for both SiO2 and Y-doped SiO2 membrane as shown inFIGS. 5A and 5B . The observed increasing permeance clearly indicates that the dominant mechanism of each gas permeance is the activated diffusion. In the case of activated diffusion, molecules permeate through micropores while being exposed to repelling forces from the pore walls, and molecules that have enough kinetic energy to overcome the repelling force can permeate the pores. The permeances of He and H2 for both SiO2 and Y-doped SiO2 membranes show the characteristics of slightly activated permeation, while the N2-permences behaved just like the Knudsen's permeation mechanism, suggesting the N2-permeation through a few pinholes still left in the membrane. The permeation of a gas molecule in a porous medium leads to decreasing permeance with increasing temperature and this mechanism called Knudsen diffusion and/or viscous flow. - The permeances of He, H2, N2, and CO2 are 9.1×10−7 mol/m2sPa, 5.89×10−7 mol/m2sPa, 2.36×10−8 mol/m2s kPa, and 2.32×10−8 mol/m2sPa, respectively were observed for SiO2 membrane at 500° C., and the permselectivity of H2/N2 was measured to be 26. On the other hand, the permselectivity of H2/N2, was measured to be 70 for Y-doped SiO2 membrane. It is obvious that the permselectivities of Y2O3 doped SiO2 membrane are much higher than the un-doped SiO2 membrane. It means the doping of Y into the SiO2 network has highly positive effect.
FIG. 5B also indicates a slight increase of permeance with temperature, which can be described as an apparent thermal activation (Ea) of the permeance of all gases, except CO2 and N2. This demonstrates that Ea is not necessarily always positive. The CO2 permeance is nearly constant with temperature and even seems to decrease at higher temperatures. The permeance of the Y-doped SiO2 membranes were in most cases independent of pressure. The Y-doped SiO2 membranes had an H2 permeance of 8.73×10−8 mol/m2s kPa at 500° C. The smaller Y-doped SiO2 permeance was observed might be due to densification of the structure and a smaller pore size. -
FIGS. 6A and 6B shows the permeation performance for SiO2 and Y-doped SiO2 membranes under steam atmosphere as function of time. The effect of hydrothermal treatment with a 3 vol % steam stream on the membranes at 500° C. is shown inFIGS. 6A and 6B . In the first 2 h, the permeances of He and H2 decreased slightly and reached to the steady-state values of around 1.6×10−5 and 4.6×10−6 mol/m2s kPa, respectively for SiO2 and Y-doped SiO2 (FIG. 6B ). After the first measurement at 0 h, the remainder of the permeance data was obtained under hydrothermal conditions. The CO2 gas permeance of SiO2 drastically increased, i.e., from 1.21 to 1.15×10−9 mol/m2s kPa after 2 h hydrothermal treatment (a). The high permeance of SiO2 might be due to the presence of pin hole and/or creaks and it was formed during the wet atmosphere for 20 h, which lead to the degradation of the resulting molecular sieve-like property. - Vos et al. investigated the hydrothermal stability of commercial SiO2 membranes by H2 gas permeation. They found that the H2 gas permeances increased rapidly, as with hydrothermal treatment. The results indicate that the SiO2 is not a good candidate for use as separation layer for gas separation membranes. The top layer must be stable under hydrothermal conditions to minimize the defects of the microporous top layer. During hydrothermal treatment for Y-doped silica membrane, two distinguishable phenomena were observed: a slight decrease in permeance for 2 h upon introduction of a stream containing steam. After the first 2 h, the permeance of Si/Y (3/1) membrane had decreased only ca. 1% for all the gases tested in the presence of steam.
FIG. 6B shows that the gas permeance of Si/Y (3/1) was stable under hydrothermal conditions at 500° C. for 20 h. This can be considered a remarkable result. The H2 permeance of Y-doped SiO2 membranes was 6.89×10−8 mol/m2s kPa with a H2/N2 permeance ratio of 92, while the values observed for the SiO2 membranes were 1.48×10−7 mol/m2s kPa and only 7, respectively. Y-doped SiO2 membranes clearly showed higher selectivity than SiO2 membranes under steam conditions. No appreciable difference in the gas permeation characteristics and in the stability against steam at 500° C. was observed between the Y-doped SiO2 membrane fired in steamed atmosphere at 550° C. and that at 650° C. These results suggest that the Y doping are quite effective for the prevention of further densification of amorphous Y-doped silica networks or for the membrane stability in wide temperature range. - Cannas et al. reported that the 2-3 nm nanoparticles of Y are formed by sol-gel synthesis process, strongly interacting with the SiO2 matrix at the interface. The initial densification of the silica network under hydrothermal conditions probably related to a number of factors including: (i) the surface composition; (ii) the local structure and the distribution of the dispersed Si—O—Y species; (iii) the nature of the inter[31]mediate layer; and (iv) parameters related to sol preparation procedures. The real parameters for densification could be breaking down of siloxane network, generation and/or reshuffle of silanol groups, and subsequent recombination and reorganization of silanol groups into the siloxane network. The initial slight decrease of the permeance was occurred probably due to the above reasons. After 2 h hydrothermal condition the gas permeance was stable.
- A possible reason to prevent the further densification of a silica network by doping Y, it was thought that the Y probably exist as metal ions or it could be tiny crystals because the observed XRD showed merely amorphous pattern and/or covalently bound compounds such as Si—O—Y, which seems fabricate a rigid network of Si—O—Y linkage under steam atmosphere and eventually the pores were not collapse and/or expand. As a result a stable permeance was observed under hydrothermal conditions. These are the main reasons for the stable permeance. Some other factors cannot be neglected for example doped Y might reduce the attach of H2O vapor and prevent thermally induced movement of silanol groups, such as alternation. It means Y doping can control the free motion of silanol groups. The large increase of Fα for H2/CO2 from 54 to 101 for Y-doped membrane might be due to a decrease of terminal hydroxyl groups at the internal surface of the silica and/or higher calcination temperatures lead to lower hydroxyl concentrations. A decrease of the amount of hydroxyls makes the material more hydrophobic, which may result in a lower (surface) occupation and, hence, a lower CO2 permeance. Zahir et al. and Duke et al. also reported the same phenomena probably occurred for metal-doped γ-Al2O3 membranes and carbonized-template silica membranes. It is known that the silica has inadequate thermal and hydrothermal stability to enable practical application. As oxygen forms more stable bonds with transition metals than with silicon, mixed oxide networks are more stable than amorphous silicon oxide. Boffa et al. recently developed a niobia-silica mixed oxide microporous membrane that was found to be more stable under hydrothermal conditions than the silica membrane, See V. Boffa, D. H. A. Blank, J. E. ten Elshof, Hydrothermal stability of microporous silica and niobia-silica membranes, J. of Membrane Science 319, 256-263(2008), incorporated herein by reference in its entirety. This is probably the result of the incorporation of Nb ions the silica matrix, which yields hydrothermally stable Nb—O—Si bonds.
- The appearances of the N2 adsorption/desorption isotherms of SiO2 sample before (
FIG. 7A ) and after hydrothermal treatment (FIG. 7B ) primarily suggest pore structures consisting of either solely micropores or purely mesopores; in reality, most of these samples consist of a combination of micropores and mesopores, as is evident from the PSD results obtained from the NLDFT approach. The SiO2 can be classified as mostly mesoporous by virtue of the associated Type IV isotherm. Both samples exhibits similar isotherm with an H1-Type hysteresis loop at P/Po=0.45 to 0.8. The corresponding curve represents a narrow pore-size distribution with an average pore radius at around 3.5 nm, which indicates the existence of a mesoporous structure. By applying the Barrett-Joyner-Halenda (BJH) method to the distribution branch of the isotherm, we obtained the pore seize distribution of SiO2 sample before (FIG. 8A ) and after hydrothermally treatment (FIG. 8B ). The pore-size distribution curve for both samples had one peak. The pore diameter of SiO2 has been shifted to a higher value after hydrothermal treatment and a significant decrease in the pore volume was observed (FIG. 8A ). In the case of Si/Y (3/1) sample, the isotherm shows type I isotherm which characteristic for microporous materials as shown inFIGS. 9A and 9B . A sharp pore size distribution with an average Kelvin radius of 2.4 nm was found for the Si/Y (3/1) sample, as shown inFIG. 10A . Most of the published results revealed that the pore size distribution of SiO2 and/or γ-Al2O3 shift to the higher value after hydrothermal treatment, however, in the case of Si/Y (3/1) sample, the sharp peak shifted little bit towards lower value as shown inFIG. 10B . The pore volume was slightly decreased after hydrothermal treatment. However, the pore size distribution was almost unchanged after hydrothermal treatment for Si/Y (3/1). - It should be mentioned though that the results for unsupported material (powder samples) cannot be transferred quantitatively to the supported membrane situation. They can only be of qualitative use to show trends in changes in pore structure with processing. It must be clear that the supported SiO2 layer cannot be expected to have the same structure as similar processed unsupported SiO2 material, since the forces present during the drying process of both materials are different. The N2 permeation and the calculated pore size distribution (PSD), obtained by permporometry, for a supported as-prepared microporous Si/Y (3/1) membrane are shown in
FIG. 11 andFIG. 12 . The calculated PSDs show the distribution of the total number of pores within a certain range. It can be seen that the permeation at large Kelvin radii was almost zero, and that a strongly increased permeation was observed at around 0.2-0.3 nm. This implies that no pores or only a few pores were present with Kelvin radii larger than 0.4 nm. The PSD of the Si/Y (3/1) membrane was found to be almost unchanged even after the 20 h steam exposure at 500° C. as shown inFIG. 12 . To the best of our knowledge, no permporometry measurement has yet been performed on Y doped SiO2 based composite-supported membranes after hydrothermal treatment. - Yttria-doped silica membranes were synthesized using tetraethyl orthosilicate-derived sol mixed with yttrium nitrate hexahydrate. Subsequently, these solutions were used in the preparation of hydrogen separation microporous membranes with enhanced hydrothermal stability at 500° C. under a steam pressure of 150 kPa. Very high permeance obtained for N2 and O2 of 2.2 and 5×10−8 mol/m2s kPa, respectively, offer perspectives on dedicated air purification and/or separation in which larger impurity molecules are blocked by molecular sieving effects. Y-doped SiO2 hydrogen separation membranes showed improved hydrothermal stability and high selectivity, compared with SiO2 membranes.
Claims (13)
1. A gas separation device, comprising:
a permeance cell having an upstream feed end and a downstream permeate end, and a nanocomposite membrane between the upstream feed end and the downstream permeate end of the permeance cell,
wherein the nanocomposite membrane is configured to separate a first gas having high permeance through the nanocomposite membrane from a second gas having low permeance through the nanocomposite membrane;
wherein the nanocomposite membrane comprises:
a tubular α-Al2O3 membrane support comprising;
an intermediate layer comprising γ-Al2O3, wherein the intermediate layer is 300-1200 nm thick and coats a surface of the tubular α-Al2O3 membrane support;
a nanocomposite layer comprising SiO2 and Y2O3, wherein the nanocomposite layer is 25-150 nm thick and coats a surface of the intermediate layer;
wherein the nanocomposite layer is porous with an average largest radius micropore of 0.2-0.6 nm.
2. The gas separation device of claim 1 , wherein the intermediate layer comprises at least two distinct γ-Al2O3 layers, each distinct γ-Al2O3 layer being 150-600 nm thick.
3. The gas separation device of claim 1 , wherein the Y2O3 is in the form of nanoparticles with a largest dimension of 1-6 nm, the nanocomposite layer is in the form of a SiO2 matrix, and the Y2O3 nanoparticles are dispersed in or deposited onto the SiO2 matrix.
4. The gas separation device of claim 3 , wherein the nanocomposite layer is porous with an average mesopore radius of 1-4 nm.
5. The gas separation device of claim 1 , wherein the molar ratio of Si:Y in the nanocomposite membrane is 1:1 to 5:1.
6. The gas separation device of claim 1 , wherein the nanocomposite membrane has a membrane permeance of 1e−8−1e−6 mol/m2·sec·Pa for the first gas, and a membrane permeance of 1e−10−1e−9 mol/m2·sec·Pa for the second gas when a mixture of gas comprising the first gas and the second gas is fed through the permeance cell at a temperature of 100-650° C.
7. The gas separation device of claim 6 , wherein the first gas is H2, He, or both, and the second gas is N2, CO2, or both.
8. The gas separation device of claim 1 , wherein the nanocomposite membrane has a membrane permeance of 1e−8−1e−6 mol/m2·sec·Pa for the first gas, and a membrane permeance of 1e−10−1e−9 mol/m2·sec·Pa for the second gas when a mixture of gas comprising the first gas, the second gas, and up to 5 wt % of steam relative to the total weight of the mixture of gas is fed through the nanocomposite membrane.
9-16. (canceled)
17. A method of separating a mixture of gas comprising a first gas and a second gas, comprising:
introducing the mixture of gas into the upstream feed end of the permeance cell of the gas separation device of claim 1 , wherein the nanocomposite layer of the nanocomposite membrane faces toward the upstream feed end and forms a permeable barrier between the upstream feed end and the downstream permeate end;
applying a vacuum to the downstream permeate end; and
separating the first gas from the second gas by allowing the first gas to pass through the nanocomposite membrane and to the downstream permeate end, and prohibiting the second gas from passing through the nanocomposite membrane.
18. (canceled)
19. The method of claim 17 , wherein the first gas is H2, He, or both, and the second gas is N2, CO2, or both.
20. (canceled)