US20170197271A1 - Repair material preform - Google Patents
Repair material preform Download PDFInfo
- Publication number
- US20170197271A1 US20170197271A1 US15/472,922 US201715472922A US2017197271A1 US 20170197271 A1 US20170197271 A1 US 20170197271A1 US 201715472922 A US201715472922 A US 201715472922A US 2017197271 A1 US2017197271 A1 US 2017197271A1
- Authority
- US
- United States
- Prior art keywords
- preform
- repair material
- repair
- metal component
- sealing interface
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Description
- This application is a divisional application of, and claims priority to, U.S. application Ser. No. 14/687,613, filed Apr. 15, 2015 and titled “REPAIR MATERIAL PREFORM,” which is hereby incorporated by reference in its entirety. The '613 Application claims the benefit of U.S. Provisional Application No. 61/991,291, entitled “REPAIR MATERIAL PREFORM,” filed on May 9, 2014. The '613 Application and the '291 Application are hereby incorporated by reference in their entirety.
- The present disclosure relates to the repair of metal components, such as seals, within gas turbine engines, and more particularly to the repair of damaged portions of a blade outer air seal assembly (“BOAS” assembly) located within a gas turbine engine.
- Gas turbine engines generally include a compressor to pressurize inflowing air, a combustor to burn a fuel in the presence of the pressurized air, and a turbine to extract energy from the resulting combustion gases. The turbine may include multiple rotatable turbine blade arrays separated by multiple stationary vane arrays. A turbine blade array may be disposed radially inward of an annular BOAS assembly. Frequently, portions of the BOAS assembly—such as seals within the assembly—may be damaged, e.g., by oxidation erosion.
- A structural element for repairing a metal component may comprise a preform configured to receive repair material and repair a damaged portion of a metal component, wherein the metal component melts at a first temperature and the repair material melts at a second temperature that is lower than the first temperature, and wherein the preform comprises one of a wear resistance and an oxidation resistance that is greater than one of a wear resistance and an oxidation resistance of the repair material. The preform may comprise the same material as the metal component. The preform may comprise an alloy including cobalt or nickel. The repair material may comprise an additive material, such as boron. The heat applied to the preform may be approximately 40 degrees Fahrenheit less than the melting point of the first metal material of the metal component. Upon application of heat to the preform, the additive material may diffuse into the preform.
- The subject matter of the present disclosure is particularly pointed out and distinctly claimed in the concluding portion of the specification. A more complete understanding of the present disclosure, however, may best be obtained by referring to the detailed description and claims when considered in connection with the drawing figures, wherein like numerals denote like elements.
-
FIG. 1A illustrates a cross-sectional view of a jet engine in accordance with various embodiments; -
FIG. 1B illustrates a cross-sectional view of a turbine portion of a jet engine in accordance with various embodiments; -
FIG. 1C illustrates a perspective view of a segment of a BOAS assembly having damaged sealing interface in accordance with various embodiments; -
FIG. 1D illustrates a perspective view of a damaged sealing interface in accordance with various embodiments; -
FIG. 2A illustrates a preform in accordance with various embodiments; -
FIG. 2B illustrates a perspective view of a portion of a BOAS assembly having a sealing interface in the process of being repaired in accordance with various embodiments; -
FIG. 2C illustrates a perspective view of a repaired sealing interface in accordance with various embodiments; and -
FIG. 3 illustrates a method for repairing a damaged portion of a sealing interface in accordance with various embodiments. - The detailed description of exemplary embodiments herein makes reference to the accompanying drawings, which show exemplary embodiments by way of illustration and their best mode. While these exemplary embodiments are described in sufficient detail to enable those skilled in the art to practice the inventions, it should be understood that other embodiments may be realized and that logical and mechanical changes may be made without departing from the spirit and scope of the inventions. Thus, the detailed description herein is presented for purposes of illustration only and not for limitation. For example, any reference to singular includes plural embodiments, and any reference to more than one component or step may include a singular embodiment or step. Also, any reference to attached, fixed, connected or the like may include permanent, removable, temporary, partial, full and/or any other possible attachment option.
- In addition, although the description provided herein may focus on a particular aircraft component (e.g., a sealing interface comprising a portion of a BOAS assembly), those of ordinary skill will appreciate that the methods and techniques for repairing damaged components may apply to a wide variety of components.
- As used herein, “aft” refers to the direction associated with the tail (e.g., the back end) of an aircraft, or generally, to the direction of exhaust of the gas turbine. As used herein, “forward” refers to the directed associated with the nose (e.g., the front end) of an aircraft, or generally, to the direction of flight or motion.
- Jet engines often include one or more stages of BOAS and vane assemblies. Each BOAS and vane assembly may comprise one or more sections or segments. A segment of a BOAS assembly may be disposed radially outward of a turbine blade and/or a plurality of turbine blades relative to an engine axis. A BOAS assembly may thus comprise an annular structure comprising a plurality of BOAS assembly segments, each BOAS assembly segment disposed radially about one or more of a plurality of turbine blades, each of which may rotate, during operation, within the BOAS assembly.
- Each BOAS segment may couple to an adjacent BOAS segment to form the annular BOAS assembly described above by way of a plurality of sealing interfaces. Over time, some of these sealing interfaces may erode or otherwise wear away (e.g., via an oxidation erosion process), such that a seal formed between one or more consecutive BOAS segments may fail to contain the pressure and temperature of the combustion gasses within the high pressure turbine. This loss of pressure may result, in addition to damage to the BOAS assembly, in a loss of fuel efficiency.
- Accordingly, with reference to
FIG. 1A , a jet engine (e.g., a gas turbine engine) 100 is shown. - The
jet engine 100 may extend, from forward to aft, along the central axis marked A-A′. In general terms, a jet engine may comprise acompressor section 102, acombustion chamber 104, and aturbine section 106. Air may flow through the compressor section 102 (which may comprise a plurality of compressor blades) and into thecombustion chamber 104, where the air is mixed with a fuel source and may be ignited to produce hot combustion gasses. These hot combustion gasses may drive a series of turbine blades within theturbine section 106, which in turn drive, for example, one or more compressor section blades mechanically coupled thereto. -
FIG. 1B shows an area within theturbine section 106 that includes aBOAS assembly 108. - The
BOAS assembly 108 may comprise a plurality ofBOAS segments 110, as described above and as shown, atFIG. 1C . Eachsegment 110 may couple to an adjacent segment to form an annular BOAS assembly that is concentrically situated about a plurality of turbine blades, each radially extending away from the axis A-A′. - As described above, and as shown with respect to
FIG. 1C , aBOAS segment 110 may comprise a sealinginterface 112. The sealinginterface 112 may erode over time (e.g., where the sealinginterface 112 comprises cobalt or nickel, via an oxidation erosion process), such that the interface may form an incomplete seal with an adjacent sealing interface (e.g., comprising an adjacent BOAS segment). - As illustrated in
FIG. 1D , sealinginterface 112 may comprise a damagedportion 114. In various embodiments, damagedportion 114 may comprise an edge of the sealinginterface 112 which has eroded or abraded away such that the sealing interface is incomplete or altered from its original form. As this occurs air may bleed from the turbine during operation, resulting in a loss of efficiency. - The damaged
portion 114 of sealinginterface 112 may, in various embodiments, be repaired by restoring or replacing the eroded or lost material with arepair material 116. Further, the damagedportion 114 may be surrounded by a protective layer of desired thickness. For example, as will be discussed below and with brief reference toFIG. 2B , a layer ofpreform 202 may remain around some or all of damagedportion 114. In such embodiments, the protective layer may have beneficial properties. - In various embodiments, a
repair material 116 may comprise a combination of two or more materials. For example, in various embodiments, arepair material 116 may comprise a first material and an additive material. In various embodiments, the first material may comprise the same material as the metal component being repaired, the first material also referred to as the “parent material.” Stated another way, the first material may comprise at least one metal species that is also present in the metal component being repaired. For example, in various embodiments, the sealing interface 112 (i.e., the metal component being repaired) may comprise cobalt or nickel and the first material of therepair material 116 may comprise cobalt or nickel. - In various embodiments, the additive material may act to lower the melting point of the
repair material 116 relative to the melting point of the first material alone. In various embodiments, the additive material may comprise any material capable of lowering the melting temperature of therepair material 116 relative to a composition of nickel (the first material) alone by between about 10 and 60 degrees Fahrenheit. In various embodiments, the melting point may be lowered by between about 20 to 50 degrees Fahrenheit. Further, the melting point may be lowered by approximately 40 degrees Fahrenheit. For example, the additive material may comprise boron. In various embodiments, therepair material 116 may further comprise a variety of binders and other inclusions and may take the form of, for example, a paste, a powder, and/or the like. - Typically, for the first material within the
repair material 116 to form a metallurgical bond with the parent material of the sealinginterface 112, it is beneficial for the additive material (e.g., boron) to leach or diffuse into the parent material of the sealinginterface 112. Thus, although the application ofrepair material 116 to a damaged portion of a sealing interface may repair the portion, the melting temperature of the repaired portion may also be reduced by the diffusion of boron into the parent material. This may also result in diminished metal properties in the repaired area. - With reference to
FIGS. 2A-2C andFIG. 3 (describing a repair method 300), a damagedportion 114 may be repaired in a manner which may prevent or reduce the effect described above. Apreform 202 may be configured to surround and reproduce or substantially reproduce the initial, undamaged shape of damagedportion 114. For example, step 302 ofrepair method 300 may comprisepositioning preform 202 relative to sealinginterface 112 such that arepair material 116 may be injected intopreform 202 to repair damagedportion 114. Further, preform 202 may comprise a mold configured to reconstruct a shape of the damaged portion of the metal component. - In various embodiments, step 304 of
repair method 300 comprises injecting arepair material 116 intopreform 202. In various embodiments,preform 202 comprises the parent material of sealinginterface 112. Additive material in therepair material 116 may diffuse intopreform 202 rather than the parent material of damagedportion 114 of sealinginterface 112. Further, even wherepreform 202 does not comprise the parent material (e.g., where the shaped cavity comprises a metal other than, for example, cobalt or nickel), boron may migrate during a diffusion method intopreform 202 rather than the parent material of damagedportion 114. -
Preform 202 may further comprise a material having beneficial properties. For example, preform 202 may comprise an alloy, including an alloy containing the parent material and additional metals, which provides improved resistance to wear and/or improved resistance to oxidation. In various embodiments,preform 202 comprises an alloy containing cobalt or nickel. Although described with reference to specific materials, preform 202 may comprise any material or combination of materials suitable for use in a gas turbine environment. - In various embodiments,
preform 202 comprises any shape that is suitable for repairing a particular component. For example, preform 202 may comprise a rectangular shape configured to reproduce the initial, undamaged shape of damagedportion 114 of sealinginterface 112. However, any configuration ofpreform 202 that may repair or reproduce the initial, undamaged shape of damagedportion 114 of sealinginterface 112 is within the scope of the present disclosure. - In various embodiments, step 306 of
repair method 300 may comprise applying heat to preform 202. Aspreform 202 is heated to the melting temperature of the repair material 116 (which, again, may be approximately 40 degrees Fahrenheit lower than the melting point of the parent material of sealinginterface 112 and/or preform 202), the first material in therepair material 116 may melt to form a metallurgical bond between therepair material 116 and the parent material comprising sealinginterface 112, while the additive material (e.g., boron) may diffuse intopreform 202. Thus, the repaired sealinginterface 112 may retain its original melting point and temperature resistance. - Step 308 of
repair method 300 may comprise, for example, removing a portion ofpreform 202 from the repaired sealinginterface 112. In various embodiments, a portion ofpreform 202 is machined away from sealinginterface 112. - In various embodiments,
repair method 300 may further comprise a leaving a layer of material with enhanced properties step 310. With reference toFIG. 2C , after machining a portion ofpreform 202 away from sealinginterface 112, alayer 220 ofpreform 202 remains bonded to sealinginterface 112.Layer 220 may comprise characteristics and/or properties that are beneficial to sealinginterface 112, such as, for example, improved oxidation resistance and/or improved wear resistance. For example, as discussed in relation to preform 202,layer 220 may comprise an alloy including cobalt or nickel or other materials that provide improved resistance to wear and/or improved resistance to oxidation. - A repaired sealing
interface 112 is shown mounted to aBOAS segment 110 inFIG. 2C . - Furthermore, the
repair method 300 may, in various embodiments, be especially useful in the restoration of tall and/or thin components (e.g., approximately 0.040 inches (or 0.1016 centimeters) and smaller). - Benefits, other advantages, and solutions to problems have been described herein with regard to specific embodiments. Furthermore, the connecting lines shown in the various figures contained herein are intended to represent exemplary functional relationships and/or physical couplings between the various elements. It should be noted that many alternative or additional functional relationships or physical connections can be present in a practical system. However, the benefits, advantages, solutions to problems, and any elements that may cause any benefit, advantage, or solution to occur or become more pronounced are not to be construed as critical, required, or essential features or elements of the inventions. The scope of the inventions is accordingly to be limited by nothing other than the appended claims, in which reference to an element in the singular is not intended to mean “one and only one” unless explicitly so stated, but rather “one or more.” Moreover, where a phrase similar to “at least one of A, B, or C” is used in the claims, it is intended that the phrase be interpreted to mean that A alone may be present in an embodiment, B alone may be present in an embodiment, C alone may be present in an embodiment, or that any combination of the elements A, B and C may be present in a single embodiment; for example, A and B, A and C, B and C, or A and B and C. Different cross-hatching is used throughout the figures to denote different parts but not necessarily to denote the same or different materials.
- Systems, methods and apparatus are provided herein. In the detailed description herein, references to “one embodiment,” “an embodiment,” “an example embodiment,” etc., indicate that the embodiment described can include a particular feature, structure, or characteristic, but every embodiment may not necessarily include the particular feature, structure, or characteristic. Moreover, such phrases are not necessarily referring to the same embodiment. Further, when a particular feature, structure, or characteristic is described in connection with an embodiment, it is submitted that it is within the knowledge of one skilled in the art to affect such feature, structure, or characteristic in connection with other embodiments whether or not explicitly described. After reading the description, it will be apparent to one skilled in the relevant art(s) how to implement the disclosure in alternative embodiments.
- Furthermore, no element, component, or method step in the present disclosure is intended to be dedicated to the public regardless of whether the element, component, or method step is explicitly recited in the claims. No claim element herein is to be construed under the provisions of 35 U.S.C. 112(f), unless the element is expressly recited using the phrase “means for.” As used herein, the terms “comprises,” “comprising,” or any other variation thereof, are intended to cover a non-exclusive inclusion, such that a process, method, article, or apparatus that comprises a list of elements does not include only those elements but can include other elements not expressly listed or inherent to such process, method, article, or apparatus.
Claims (6)