US20150325467A1 - Methods for fabricating integrated circuits including barrier layers for interconnect structures - Google Patents
Methods for fabricating integrated circuits including barrier layers for interconnect structures Download PDFInfo
- Publication number
- US20150325467A1 US20150325467A1 US14/272,787 US201414272787A US2015325467A1 US 20150325467 A1 US20150325467 A1 US 20150325467A1 US 201414272787 A US201414272787 A US 201414272787A US 2015325467 A1 US2015325467 A1 US 2015325467A1
- Authority
- US
- United States
- Prior art keywords
- layer
- liner
- depositing
- forming
- overlying
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
- The technical field relates generally to methods for fabricating integrated circuits, and more particularly relates to methods for fabricating integrated circuits including forming a robust barrier layer such as for a back-end-of-the-line interconnect structure.
- Integrated circuits (ICs) typically include a plurality of semiconductor devices and interconnect wiring. Networks of metal interconnect wiring are often used to connect the semiconductor devices from the semiconductor portion of the substrate. Multiple levels of metal interconnect wiring form a plurality of metallization layers above the semiconductor portion of the substrate and are connected together to form a back-end-of-the-line (“BEOL”) interconnect structure. Within such a structure, metal lines run parallel to the substrate in the metallization layers and conductive vias run perpendicular to the substrate between the metallization layers to interconnect the metal lines.
- High performance of contemporary ICs may be achieved using a highly conductive metal, such as copper (Cu), as the interconnect metal of the BEOL interconnect structure, which also employs a low dielectric constant material or dielectric material as an interlevel dielectric (ILD) layer or layers to insulate the interconnect wires from each other. To help prevent migration of the interconnect metal into the ILD layer, a barrier-forming material, such as tantalum nitride (TaN), is deposited onto the dielectric material to form a barrier layer. A metal liner material, such as tantalum (Ta) or the like, is deposited overlying the barrier layer to form a metal liner layer to help hold the highly conductive interconnect metal to the barrier layer and the underlying dielectric material. Then, a conductive metal seed layer, such as a layer of copper (Cu) or copper alloy, is formed on the metal liner layer and the highly conductive metal (e.g., Cu) is deposited over the conductive metal seed layer to form a metal interconnect wire. Unfortunately, many conventional approaches for forming the barrier layers for such interconnect structures can (1) damage the underlying dielectric material of the ILD layer, (2) produce non-conformal barrier layers that are too thin or discontinuous particularly along vertical walls or too thick particularly around corners of the ILD layer, and/or (3) form relatively low density barrier layers that have undesirably high resistivity and/or are susceptible to damage by impurities, such as oxygen (O), carbon (C), or the like, that are produced during subsequent deposition of the liner.
- Accordingly, it is desirable to provide methods for fabricating integrated circuits including forming barrier layers that are more robust such as for back-end-of-the-line interconnect structures. Furthermore, other desirable features and characteristics of the present invention will become apparent from the subsequent detailed description and the appended claims, taken in conjunction with the accompanying drawings and this background.
- Methods for fabricating integrated circuits are provided herein. In accordance with an exemplary embodiment, a method for fabricating an integrated circuit includes forming a barrier layer overlying a metal line of a metallization layer above a semiconductor substrate using an atomic layer deposition (ALD) process and a physical vapor deposition (PVD) process. A liner-forming material is deposited overlying the barrier layer to form a liner. A conductive metal is deposited overlying the liner.
- In accordance with another exemplary embodiment, a method for fabricating an integrated circuit is provided. The method includes etching a via-hole through an ILD layer of dielectric material to expose a metal line of a metallization layer above a semiconductor substrate. A first tantalum nitride (TaN) layer is deposited into the via-hole overlying the metal line using an atomic layer deposition (ALD) process. A second TaN layer is deposited into the via-hole overlying the first TaN layer using a physical vapor deposition (PVD) process to form a barrier layer. The barrier layer includes the first and second TaN layers. A liner is formed in the via-hole overlying the barrier layer. A conductive metal seed layer is deposited into the via-hole overlying the liner. A remaining portion of the via-hole is filled with a conductive metal fill overlying the conductive metal seed layer.
- In accordance with another exemplary embodiment, a method for fabricating an integrated circuit is provided. The method includes forming a barrier layer overlying a metal line of a metallization layer above a semiconductor substrate. Forming the barrier layer includes depositing a first tantalum nitride (TaN) layer overlying the metal line using an atomic layer deposition (ALD) process. An upper portion of the first TaN layer is a densified by depositing a second TaN layer overlying the first TaN layer using a physical vapor deposition (PVD) process. A liner is formed overlying the barrier layer. A conductive metal is deposited overlying the liner.
- The various embodiments will hereinafter be described in conjunction with the following drawing figures, wherein like numerals denote like elements, and wherein:
-
FIGS. 1-10 illustrate, in cross-sectional views, an integrated circuit and a method for fabricating an integrated circuit during various intermediate fabrication stages in accordance with an exemplary embodiment. - The following Detailed Description is merely exemplary in nature and is not intended to limit the various embodiments or the application and uses thereof. Furthermore, there is no intention to be bound by any theory presented in the preceding background or the following detailed description.
- Various embodiments contemplated herein relate to methods for fabricating integrated circuits including forming a back-end-of-the-line (BEOL) interconnect structure. Formation of the BEOL interconnect structure includes etching a via-hole through an ILD layer of dielectric material (e.g., a relatively porous dielectric material) to expose sidewalls of the ILD layer and a metal line of a metallization layer above a semiconductor substrate. A barrier layer is formed in the via-hole overlying the sidewalls of the ILD layer and the metal line using an atomic layer deposition (ALD) process and a physical vapor deposition (PVD) process. In an exemplary embodiment, the barrier layer is formed by depositing a barrier-forming material such as tantalum nitride (TaN) into the via-hole using the ALD process to form a first layer that overlies the sidewalls of the ILD layer and the metal line. In an exemplary embodiment, it has been found that by depositing the barrier-forming material using the ALD process, the first layer is conformal having a relatively uniform thickness along the metal line and the sidewalls of the ILD layer. Additional barrier-forming material (e.g., TaN) is then deposited into the via-hole using the PVD process to form a second layer that overlies the first layer. In an exemplary embodiment, it has been found that by depositing the additional barrier-forming material using the PVD process, at least an upper portion of the first layer is densified by ion bombardment of the additional barrier-forming material onto the upper surface of the first layer to form the barrier layer with a relatively dense (densified) upper portion that includes the second layer and the upper portion of the first layer. As such, the barrier layer is more robust than typical barrier layers that are formed by conventional processes in that the first layer is conformal providing a continuous barrier along the sidewalls of the of the ILD layer to help protect the underlying dielectric material and the densified upper portion of the barrier layer has a relatively high density with desirably lower resistivity and/or is less susceptible to damage by impurities during subsequent processing. A liner is then formed in the via-hole overlying the barrier layer. A conductive metal seed layer is deposited into the via-hole overlying the liner and a remaining portion of the via-hole is filled with a conductive metal fill overlying the conductive metal seed layer to form an interconnect structure.
-
FIGS. 1-10 illustrate, in cross-sectional view, an integrated circuit (IC) 10 during various fabrication stages. The described process steps, procedures, and materials are to be considered only as exemplary embodiments designed to illustrate to one of ordinary skill in the art methods for practicing the invention; the invention is not limited to these exemplary embodiments. Various steps in the manufacture of ICs are well known and so, in the interest of brevity, many conventional steps will only be mentioned briefly herein or will be omitted entirely without providing the well-known process details. -
FIG. 1 illustrates a portion of theIC 10 during an intermediate fabrication stage in accordance with an exemplary embodiment. The IC 10 includes asemiconductor substrate 12. As used herein, the term ‘semiconductor substrate’ will be used to encompass semiconductor materials conventionally used in the semiconductor industry from which to make electrical devices. Semiconductor materials include monocrystalline silicon materials, such as the relatively pure or lightly impurity-doped monocrystalline silicon materials typically used in the semiconductor industry, as well as polycrystalline silicon materials, and silicon admixed with other elements such as germanium, carbon, and the like. In addition, ‘semiconductor material’ encompasses other materials such as relatively pure and impurity-doped germanium, gallium arsenide, zinc oxide, glass, and the like. The semiconductor material is preferably a silicon substrate. The silicon substrate may be a bulk silicon wafer or may be a thin layer of silicon on an insulating layer (commonly known as silicon-on-insulator or SOI) that, in turn, is supported by a carrier wafer. - Additionally, the IC 10 includes a
semiconductor device layer 14 that may be made up of active areas (not shown) in which a plurality of active and/or passive circuit elements (not shown), such as transistors, capacitors, resistors, and the like may be formed. It should be appreciated that thesemiconductor device layer 14, even if including a substantially silicon-based material layer, may include other semiconducting materials, such as germanium, carbon, and the like, in addition to appropriate dopant species for establishing the requisite active area conductivity type for the circuit elements. - As illustrated, the IC 10 also includes a
contact layer 16 that may be formed above thesemiconductor device layer 14. In an exemplary embodiment, the contact layer is an interlevel dielectric (ILD) layer of dielectric material (e.g., porous dielectric material of silicon dioxide, silicon nitride, silicon oxynitride or the like) with a plurality of contact vias (not shown) formed therethrough as is well known in the art. Typically, the contact vias provide conductive electrical connections between one or more of the various circuit elements (not shown) disposed along thesemiconductor device layer 14 to vias within an ILD layer 18 (discussed below). - As illustrated in
FIG. 1 , above thesemiconductor substrate 12 and thecontact layer 16, theIC 10 includes ametallization layer 17 that is disposed in theILD layer 18 of dielectric material (e.g., porous dielectric material of silicon dioxide, silicon nitride, silicon oxynitride or the like). The vias withincontact layer 16 are in electrical connection with the vias withinILD layer 18 and, accordingly, establish electrical connection between the electrical devices ofsemiconductor device layer 14 andmetallization layer 17. It is to be appreciated that theIC 10 may include two metallization layers or more than two metallization layers, depending on the overall device requirements. - Overlying the
ILD layer 18 and themetallization layer 17 is an N-doped silicon carbide (SiCN)layer 20, anoverlying ILD layer 22 of dielectric material (e.g., porous dielectric material of silicon dioxide, silicon nitride, silicon oxynitride or the like), and an overlying hard mask layer 23 (e.g., silicon dioxide or the like). In an exemplary embodiment, the ILD layers 18 and 22 are each relatively thick independently with a thickness of from about 200 to about 1500 nm, and the N-dopedSiCN layer 20 has a thickness of from about 10 to about 50 mm. Themetallization layer 17 includes ametal line 28. While only one metal line is shown inFIG. 1 for illustrative purposes, it is to be appreciated that themetallization layer 17 can include a plurality of discrete and spaced apart metal lines similarly configured to themetal line 28 that form part of aBEOL interconnect structure 34 disposed above thecontact layer 16. Themetal line 28 is formed of a conductive metal fill 36 and a barrier/liner 38. The conductive metal fill 36 is a highly conductive material such as copper and the barrier/liner 38 is one or more layers of a barrier- and/or liner-forming material(s) such as tantalum (Ta), tantalum nitride (TaN), titanium (Ti), and/or titanium nitride (TiN) to help inhibit or prevent diffusion of the conductive metal fill 36 into theILD layer 18 and/or to help hold the conductive metal fill 36 to theILD layer 18. - As illustrated, a
metal line trench 40 is formed into an upper portion of theILD layer 22. Aligned with and opened to themetal line trench 40, is a via-hole 42 that extends through theILD layer 22 to expose anupper surface 44 of themetal line 28. - The illustrated portion of the
BEOL interconnect structure 34 may be formed on the basis of well-known techniques. In an exemplary embodiment, theILD layer 18 is formed by depositing a dielectric material such as silicon dioxide or the like that includes some impurities (e.g., carbon or the like) overlying thecontact layer 16 using a chemical vapor deposition (CVD) process and treating the dielectric material for example with UV radiation to out gas the impurities and form porosity in theILD layer 18 to further lower the dielectric constant of the dielectric material. The top surface of theILD layer 18 is planarized using a chemical mechanical planarization (CMP) process. Next, theILD layer 18 is patterned and etched using, for example, a dry etching process to form a metal line trench. The trench is then filled by depositing a barrier/liner-forming material(s) and the conductive metal fill 36 into the metal line trench using a physical vapor deposition (PVD) process (or an atomic layer deposition (ALD) process) and an electrochemical plating (ECP) process, respectively, to form themetal line 28. Any overburden of conductive metal fill 36 and/or barrier/liner-forming material(s) is removed by CMP. Next, the N-dopedSiCN layer 20 is deposited overlying theILD layer 18 and themetal line 28 using a CVD process. TheILD layer 22 is then formed (e.g., via depositing and treating a dielectric material as discussed above in relation to the ILD layer 18) over the N-dopedSiCN layer 20 followed by CMP to expose an upper-surface portion 39 of theILD layer 22. Thehard mask layer 23 is then deposited for example by the decomposition of a source material such as tetraethylorthosilicate (TEOS). Themetal line trench 40 and the via-hole 42 are formed using well-known lithography and etching techniques (e.g., dry etching techniques such as plasma etching or the like) to pattern thehard mask layer 23 and selectively remove portions of theILD layer 22. - The process continues as illustrated in
FIG. 2 by forming abarrier layer 45 overlying a top surface of thehard mask layer 23, thesidewalls ILD layer 22 that define the via-hole 42 and themetal line trench 40, and theupper surface 44 of themetal line 28 using an ALD process and a PVD process. In an exemplary embodiment and with reference also toFIG. 3A , thebarrier layer 45 is formed by initially depositing a barrier-formingmaterial 49 overlying the top surface of thehard mask layer 23, thesidewalls ILD layer 22, and theupper surface 44 of themetal line 28 to form alayer 50. In an exemplary embodiment, the barrier-formingmaterial 49 includes TaN and is deposited using the ALD process to form thelayer 50. In an exemplary embodiment, thelayer 50 has a thickness (indicated by double headed arrow 52) of from about 3 to about 30 Å, for example, from about 5 to about 10 Å. In an exemplary embodiment, it has been found that by depositing thelayer 50 using the ALD process thelayer 50 is conformal, providing continuous coverage along thesidewalls ILD layer 22 and over themetal line 28, and has a relatively low density. In an exemplary embodiment, thelayer 50 has a density of from about 8 to about 12 g/cm3, such as from about 9 to about 11 g/cm3, for example about 10 g/cm3. - With reference to FIGS. 2 and 3B-3C, an additional barrier-forming
material 54 is deposited overlying thelayer 50 to form thelayer 56. In an exemplary embodiment, the additional barrier-formingmaterial 54 includes TaN and is deposited using the PVD process to form thelayer 56. In an exemplary embodiment, thelayer 56 has a thickness (indicated by single headed arrows 58) of from about 3 to about 30 Å, for example, from about 5 to about 20 Å. In an exemplary embodiment, it has been surprisingly found that by depositing thelayer 56 using the PVD process thelayer 56 has a relatively high density and further, at least anupper portion 60 of thelayer 50 is densified by being ion bombarded by the additional barrier-formingmaterial 54 to produce thebarrier layer 45 with a densifiedupper portion 62 that includes thelayer 56 and theupper portion 60 of the layer 50 (shown inFIG. 3C ). In an exemplary embodiment, the densifiedupper portion 62 of thebarrier layer 45 has a relatively low resistivity compared to conventional barrier layers and/or is less susceptible to damage by impurities such as carbon (C), oxygen (O), and the like that may be produced during subsequent processing. In an exemplary embodiment, thelayer 56 and theupper portion 60 of thelayer 50 have a density of from about 13 to about 15 g/cm3. In an exemplary embodiment, the densifiedupper portion 62 of thebarrier layer 45 has a thickness (indicated by double headed arrow 64) of from about 5 to about 103 Å and theupper portion 60 of thelayer 50 that is densified has a thickness (indicated by double headed arrow 66) of from about 2 to about 100 Å. - The process continues as illustrated in
FIG. 4 by depositing a liner-formingmaterial 68 overlying thebarrier layer 45 to form aliner 70. In an exemplary embodiment, the liner-formingmaterial 68 includes tantalum (Ta) and is deposited by a PVD process. In another embodiment, the liner-formingmaterial 68 includes ruthenium (Ru), cobalt (Co), or a combination thereof and is deposited by a CVD process, an ALD process, or a PVD process. In an exemplary embodiment, theliner 70 has a thickness of from about 20 to about 400 Å. - Referring to
FIG. 5 , a conductive metal seed layer 72 (e.g., Cu) is deposited overlying theliner 70. In an exemplary embodiment, the conductivemetal seed layer 72 is deposited using a PVD process. As illustrated inFIG. 6 , a remaining portion of the via-hole 42 and themetal line trench 40 are filled with a conductive metal fill 74 (e.g., copper or copper alloy) to form a via 76 and ametal line 78, respectively, to define themetallization layer 19. The process continues by planarizing theIC 10 using a CMP process to remove any overburden conductive metal fill 74, thehard mask layer 23, and excess portions of the conductivemetal seed layer 72, theliner 70, and thebarrier layer 45 and to exposeILD layer 22, as illustrated inFIG. 7 . - In an alternative embodiment, after depositing the liner-forming
material 68 as illustrated inFIG. 4 , for example to a thickness of about 10 to about 200 Å, portions of the liner-formingmaterial 68 are etched back to form a partially etchedliner layer 80 as illustrated inFIG. 8 . In an exemplary embodiment, etching back the portions of the liner-formingmaterial 68 removes a thickness of from about 10 to about 100 Å of liner-formingmaterial 68 to form the partially etchedliner layer 80. In an exemplary embodiment, a dry etching process (e.g., plasma etching process) is used to remove the portions of the liner-formingmaterial 68 and form the partially etchedliner layer 80. - Referring to
FIGS. 8-9 , additional liner-forming material 82 (e.g., Ta via a PVD process or Ru and/or Co via a CVD process) is then deposited overlying the partially etchedliner layer 80 to complete formation of theliner 70. In an exemplary embodiment, a thickness of from about 10 to about 200 Å of the additional liner-formingmaterial 82 is deposited overlying the partially etchedliner layer 80 to form theliner 70. In an exemplary embodiment and as illustrated, a portion of thebarrier layer 45 directly above themetal line 28 is removed during the etch back process of the portions of the liner-formingmaterial 68 so that theliner 70 can be formed penetrating (e.g., gouging or punching through) into themetal line 28 to help lower an overall resistance of theBEOL interconnect structure 34. - The process continues as illustrated in
FIG. 10 by depositing the conductivemetal seed layer 72 overlying theliner 70 and filling the remaining portion of the via-hole 42 and themetal line trench 40 with the conductive metal fill 74 to form the via 76 and themetal line 78 and to define themetallization layer 19 as described above in relation toFIGS. 5-6 . TheIC 10 is then planarized by a CMP process to remove any excess conductive metal fill 74, thehard mask layer 23, and excess portions of the conductivemetal seed layer 72, theliner 70, and thebarrier layer 45 and exposeILD layer 22. Accordingly, methods for fabricating integrated circuits including forming a robust barrier layer such as for a back-end-of-the-line interconnect structure have been described. - While at least one exemplary embodiment has been presented in the foregoing detailed description of the disclosure, it should be appreciated that a vast number of variations exist. It should also be appreciated that the exemplary embodiment or exemplary embodiments are only examples, and are not intended to limit the scope, applicability, or configuration of the disclosure in any way. Rather, the foregoing detailed description will provide those skilled in the art with a convenient road map for implementing an exemplary embodiment of the disclosure. It being understood that various changes may be made in the function and arrangement of elements described in an exemplary embodiment without departing from the scope of the disclosure as set forth in the appended claims.
Claims (20)