US20150303251A1 - Bonded epitaxial oxide structures for compound semiconductor on silicon substrates - Google Patents
Bonded epitaxial oxide structures for compound semiconductor on silicon substrates Download PDFInfo
- Publication number
- US20150303251A1 US20150303251A1 US14/732,705 US201514732705A US2015303251A1 US 20150303251 A1 US20150303251 A1 US 20150303251A1 US 201514732705 A US201514732705 A US 201514732705A US 2015303251 A1 US2015303251 A1 US 2015303251A1
- Authority
- US
- United States
- Prior art keywords
- layer
- oxide layer
- compound semiconductor
- epitaxial oxide
- epitaxial
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
Description
- This patent application is a divisional of U.S. patent application Ser. No. 13/965,178 filed Aug. 12, 2013, entitled “BONDED EPITAXIAL OXIDE STRUCTURES FOR COMPOUND SEMICONDUCTOR ON SILICON SUBSTRATES.” The complete disclosure of the aforementioned U.S. patent application Ser. No. 13/965,178 is expressly incorporated herein by reference in its entirety for all purposes.
- The present disclosure relates to the physical sciences, and, more particularly, to semiconductor on insulator structures and methods of fabrication thereof.
- Wafer bonding of some semiconductor materials to a silicon substrate can be problematic for a number of reasons. Differences in thermal expansion coefficients and lattice mismatches are among the reasons for such difficulties in wafer bonding. One layer transfer wafer bonding process that has been employed for some applications is known as the SmartCut® process. The process involves the implantation of ions within a monocrystalline silicon wafer. The ions, typically hydrogen ions (H+), form a layer of microbubbles parallel to the wafer surface that later functions as a cleavage plane. U.S. Pat. No. 5,374,564, which is incorporated by reference herein, discloses such a process. As discussed in U.S. Pat. No. 5,882,987, also incorporated by reference herein, an oxide layer is thermally grown on the device wafer surface prior to ion implantation during the SmartCut® fabrication process. The device wafer is bonded to a silicon handle wafer, after which annealing steps are conducted. The device wafer is fractured along the hydride rich plane. The exposed surface following such fracture is polished, for example by chemical mechanical polishing (CMP), to obtain a smooth surface. U.S. Pat. No. 6,326,285, also incorporated by reference herein, discloses techniques for silicon on insulator fabrication, including hydrogen implantation, wafer bonding, and cleaving along the hydrogen layer.
- Many applications benefit from the use of semiconductor materials other than silicon. Device layers comprising III-V semiconductor materials may, for example, be grown on germanium substrates. II-VI semiconductor materials are also employed in some applications as device layers. Some semiconductor materials are not available as bulk structures as their mechanical properties (e.g. weight, brittleness) do not facilitate such use.
- Principles of the present disclosure provide an exemplary fabrication method that includes growing a first epitaxial layer of a desired compound semiconductor material on a substrate, growing an epitaxial oxide layer on and lattice matched to the layer of the desired compound semiconductor material, and forming a cleavage plane in the layer of the desired semiconductor material via implantation, thereby forming a first structure comprising the substrate, the layer of the desired compound semiconductor material having the cleavage plane, and the epitaxial oxide layer. The method further includes bonding the first structure to a handle wafer and causing a fracture along the cleavage plane, thereby forming a second structure comprising the handle wafer, the epitaxial oxide layer, and a portion of the layer of desired compound semiconductor material. The portion of the layer of desired compound semiconductor material is removed from the second structure and a second epitaxial layer of the desired compound semiconductor material is grown on the epitaxial oxide layer.
- An exemplary structure provided in accordance with the principles expressed herein includes a handle substrate, an epitaxial oxide layer, the epitaxial oxide layer being bonded directly or indirectly to the handle substrate, and a compound semiconductor layer adjoining and lattice matched to the epitaxial oxide layer.
- A structure in accordance with a further embodiment includes a germanium base, one or more compound semiconductor layers adjoining the germanium base, the one or more compound semiconductor layers including a top layer of a desired compound semiconductor material, and an epitaxial oxide layer adjoining and lattice matched to the top layer.
- As used herein, “facilitating” an action includes performing the action, making the action easier, helping to carry the action out, or causing the action to be performed. Thus, by way of example and not limitation, instructions executing on one processor might facilitate an action carried out by instructions executing on a remote processor, by sending appropriate data or commands to cause or aid the action to be performed. For the avoidance of doubt, where an actor facilitates an action by other than performing the action, the action is nevertheless performed by some entity or combination of entities. Semiconductor structures and fabrication methods as disclosed herein can provide substantial beneficial technical effects. For example, one or more embodiments may provide one or more of the following advantages:
-
- Avoidance of ion implantation defects in a semiconductor layer;
- Relaxed compound semiconductor-on-insulator structure feasible;
- Facilitate compound semiconductor growth through use of an epitaxial oxide layer;
- Facilitate use of silicon handle wafer with a compound semiconductor layer;
- Possible reuse of donor structure;
- Enabling III-V or II-VI semiconductors on large scale wafers (e.g. 200, 300, 450 mm).
- These and other features and advantages will become apparent from the following detailed description of illustrative embodiments thereof, which is to be read in connection with the accompanying drawings.
-
FIG. 1 is a schematic sectional view of a lattice engineered semiconductor stack grown on a semiconductor substrate; -
FIG. 2 is a schematic sectional view showing the growth of a layer of compound semiconductor material on the structure shown inFIG. 1 ; -
FIG. 3 is a schematic sectional view showing the growth of a lattice matched epitaxial oxide layer on the top semiconductor layer of the structure shown inFIG. 2 ; -
FIG. 4 is a schematic sectional view showing the implantation of hydrogen into the top semiconductor layer; -
FIG. 5 is a schematic sectional view showing the wafer bonding of the structure to a silicon handle layer; -
FIG. 6 is a schematic sectional view showing the structure obtained following wafer bonding; -
FIG. 7 is a schematic sectional view showing cleavage of the semiconductor layer along the layer of implanted hydrogen; -
FIG. 8 is a schematic sectional view showing the structure following cleavage of the semiconductor layer; -
FIG. 9 is a schematic sectional view showing removal of the compound semiconductor layer from the epitaxial oxide layer of the structure shown inFIG. 8 ; -
FIG. 10 is a schematic sectional view showing regrowth of the compound semiconductor layer on the epitaxial oxide layer of the structure; -
FIG. 11 is a schematic sectional view showing an alternative embodiment of the structure shown inFIG. 4 that includes an etch stop layer; -
FIG. 12 is a schematic sectional view showing an alternative embodiment wherein a silicon oxide layer is provided on the structure shown inFIG. 3 ; -
FIG. 13 is a schematic sectional view showing the implantation of hydrogen into the top semiconductor layer of the structure shown inFIG. 12 ; -
FIG. 14 is a schematic sectional view showing the wafer bonding of the structure shown inFIG. 13 to a silicon handle layer; -
FIG. 15 is a schematic sectional view showing the structure following the step of wafer bonding; -
FIG. 16 is a schematic sectional view showing cleavage of the semiconductor layer along the layer of implanted hydrogen shown inFIG. 15 ; -
FIG. 17 is a schematic sectional view showing the structure following cleavage of the top semiconductor layer along the layer of implanted hydrogen; -
FIG. 18 is a schematic sectional view showing removal of the residual top semiconductor layer from the structure shown inFIG. 17 ; -
FIG. 19 is a schematic sectional view showing regrowth of the top semiconductor layer from the structure shown inFIG. 18 ; -
FIG. 20 is a schematic sectional view showing the donor wafer following cleavage along the layer of implanted hydrogen; -
FIG. 21 is a schematic sectional view showing the donor wafer depicted inFIG. 20 following chemical mechanical polishing of the top semiconductor layer; -
FIG. 22 is a schematic sectional view showing regrowth of the top semiconductor layer on the structure shown inFIG. 21 ; -
FIG. 23 is a schematic sectional view showing regrowth of an epitaxial oxide layer on the top semiconductor layer of the structure shown inFIG. 22 ; -
FIGS. 24-27 illustrate exemplary schematic steps for fabricating a compound semiconductor on a silicon substrate that involve growing epitaxial Ge/SiGe on a silicon substrate, and -
FIG. 28 is a schematic sectional view illustrating an alternative structure obtained using the structure shown inFIG. 25 . - A III-V or II-VI compound semiconductor-on-insulator layer free of ion implantation defects is obtained in accordance with one or more exemplary embodiments through the regrowth of a semiconductor layer on an epitaxial oxide layer that retains lattice information from previous association with a layer of the same semiconductor material that comprises the regrown layer. Compound semiconductor-on-insulator structures are provided in exemplary embodiments, such as InGaAs-on-insulator, GaAs-on-insulator, ZnSe-on-insulator and InP-on-insulator, supported by a handle comprised of silicon, glass, quartz, sapphire or other suitable material.
- A substrate having a desired lattice orientation is obtained, possibly miscut to a desired off-axis angle. In one exemplary embodiment, a <100> germanium substrate with miscut of about six (6) degrees is employed to avoid anti-phase domains (APD). Referring to
FIG. 1 , a lattice engineered semiconductor stack is epitaxially grown on thesubstrate 40. In one exemplary embodiment, a GaAs to InGaAs stack is grown on thesubstrate 40. The stack includes aGaAs layer 42 that adjoins the germanium substrate and a graded GaAs toInGaAs layer 44 adjoining theGaAs layer 42. Germanium and gallium arsenide have closely matching crystallographic properties that facilitate epitaxial growth. - Referring to
FIG. 2 , alayer 46 of semiconductor material having the composition intended for the final desired structure is grown on the stack shown inFIG. 1 . In one exemplary embodiment, the semiconductormaterial forming layer 46 is InGaAs. Thelayers semiconductor layer 46 is relatively thick, for example about a half micron (0.5 μm) in one or more embodiments to reduce potential defects. - A
crystalline oxide layer 48 is grown epitaxially on thesemiconductor layer 46 having the desired composition for the ultimately completed structure. In one exemplary embodiment, anepitaxial oxide layer 48 is grown. Theoxide layer 48 is accordingly lattice matched to theunderlying semiconductor layer 46. The structure shown inFIG. 3 is thereby obtained. - Exemplary epitaxial oxide materials grown on the
underlying semiconductor layer 46 include rare earth oxides (e.g., cerium oxide (CeO2), lanthanum oxide (La2O3), yttrium oxide (Y2O3), gadolinium oxide (Gd2O3), europium oxide (Eu2O3), and terbium oxide (Tb2O3)). In some embodiments, thecrystalline oxide layer 48 includes combinations of rare earth oxides (e.g., a material such as ABO3, where ‘A’ and ‘B’ may be any rare earth metal (e.g., lanthanum scandium oxide (LaScO3)). In yet another embodiment, thecrystalline oxide layer 48 may include aluminum oxide Al2O3 or aluminum oxide compounds (e.g., lanthanum aluminum LaAlO3). In yet other embodiments, thecrystalline oxide layer 48 includes Perovskites (e.g. strontium titanate (SrTiO3) or barium titanate (BaTiO3)) which may be deposited by pulsed laser deposition (PLD). It is understood that the descriptions of crystalline oxide layers provided herein are for illustrative purposes, and that other crystalline oxide layers or layer combinations may be used in accordance with other embodiments. - For the example of an
InGaAs semiconductor layer 46, InGaAs with 53% indium (In0.53Ga0.47As) is a commonly used III-V InGaAs compound as its lattice is matched to InP and can therefore easily be grown on InP. InP is typically available only as small diameter wafers having maximum four or five inch diameters. Employing similar principles as described in U.S. Pat. No. 6,852,575 with one lattice matching another one as a function of a multiple of the overlying lattice, theepitaxial oxide layer 48 could include 91.9% strontium titanate (SrTiO3) with 8.1% Barium titanate (BaTiO3) to lattice match 53% InGaAs. Strontium titanate is cubic and Barium titanate is tetragonal, so the compound is cubic. Three unit cells of this epitaxial oxide compound will have the same lattice constant as two unit cells of the 53% InGaAs. - A further exemplary embodiment includes a II-VI semiconductor layer, namely ZnSe, as grown by a MBE (molecular beam epitaxy) process as described in U.S. Pat. No. 7,071,087. The '087 patent is incorporated by reference herein. ZnSe has a lattice constant close to germanium and accordingly can be grown directly on germanium. Growing a relatively thick (e.g. 100-500 nm) ZnSe layer will relax the ZnSe to its natural unstrained lattice parameters. A lathanium/yttrium compound epitaxial oxide is formed on the semiconductor layer using methodology familiar to those of skill in the art. The epitaxial oxide in one exemplary embodiment includes 95% La2O3 and 5% Y2O3 for matching at two times the lattice constant of ZnSe. MBE can be employed for forming the oxide layer on ZnSe. U.S. Pat. No. 6,852,575, which is incorporated by reference herewith, discusses the linear interpolation of La2O3 and Y2O3 and an alloy created therefrom.
- Referring to
FIGS. 4-7 , a process similar to the SmartCut® process discussed above using hydrogen implantation is conducted, though within a III-V or II-VI material in one or more exemplary embodiments rather than silicon. Ahydrogen layer 50 is formed in thetop semiconductor layer 46 via ion implantation through theepitaxial oxide layer 48, as shown inFIG. 4 . Thehydrogen layer 50 is generally parallel to the top surface of thesemiconductor layer 46. The semiconductor layer has sufficient thickness to allow thehydrogen layer 50 to be formed between the top and bottom surfaces thereof. In one or more alternative embodiments, inert gas ions are implanted within thesemiconductor layer 46 rather than hydrogen. The SmartCut® process does not work as well on all types of semiconductor materials as it does with respect to <100> silicon. With respect to III-V materials formed on miscut substrates, the cutting of the III-V material will not be along an ideal path. Moreover, the electrical properties of III-V materials can be effectively destroyed by hydrogen implantation by forming electrically active states. The processes described herein allow the use of ion implantation with respect to III-V and other compound semiconductor materials despite such inherent problems. - Referring to
FIGS. 5 and 6 , asilicon handle wafer 52, which is bulk silicon with an optional thermal oxide layer in one or more embodiments, is positioned in opposing relation to the exposed surface of theepitaxial oxide layer 48. Conventional wafer bonding techniques familiar to those of skill in the art are employed to bond thehandle wafer 52 to theepitaxial oxide layer 48. U.S. Pat. No. 7,560,361, which is incorporated by reference herein, discloses applicable wafer bonding procedures. The structure shown schematically inFIG. 6 is thereby obtained. Thehandle wafer 52 may optionally include a thermal oxide layer or a dielectric surface layer (not shown), either of which may be silicon dioxide (SiO2) in the case of a silicon handle wafer, that bonds with the epitaxial oxide layer. - Referring to
FIG. 7 , the structure is fractured along the cleavage plane defined by thehydrogen layer 50 or any alternative implanted ion layer that may be provided using techniques familiar to those of skill in the art. For example, as further discussed in U.S. Pat. No. 7,560,361, fracturing along an implant region in a semiconductor layer can be accomplished by annealing the structure that includes the semiconductor layer at an appropriate temperature following the step of wafer bonding. The annealing may be supplemented by the application of a mechanical force to fracture the structure along the implanted cleavage plane. First andsecond structures first structure 60, which is employed in fabricating the ultimately desired structure, includes thesilicon handle wafer 52, theepitaxial oxide layer 48, and a residual portion of thesemiconductor layer 46, as shown inFIG. 8 . Theresidual semiconductor layer 46 of thestructure 60 is shown as including a rough, defective surface. The second structure includes theoriginal substrate 40, the lattice engineered semiconductor stack, and a residual portion of thesemiconductor layer 46. As discussed hereafter, thesecond structure 70 can be reused. - Referring to
FIG. 9 , the defectiveresidual layer 46 of semiconductor material is removed by, for example, selective etching, RIE (reactive ion etching) or CMP (chemical mechanical polishing). The type of etch depends on the III-V or II-VI semiconductor material employed. For InGaAs, a wet etch process employing a citric Acid/H2O2 mixture that selectively etches InGaAs is an option. For dry etching (RIE), a SiCl4/SiF4/HBr based selective dry etch may be employed. Having been grown epitaxially on thesemiconductor layer 46 prior to ion implantation and being lattice matched thereto, as discussed above, theepitaxial oxide layer 48 retains the lattice information of thesemiconductor layer 46 following its removal. Thestructure 80 includes thesilicon handle 52 and theepitaxial oxide layer 48 once thesemiconductor layer 46 has been removed. - A
semiconductor layer 82 having substantially the same composition as the originally depositedsemiconductor layer 46 is grown on the exposed surface of theoxide layer 48 of thestructure 80. Thenew semiconductor layer 82, not having been subject to ion implantation, is free of defects that would result from such processing. A relaxed compound semiconductor-on-insulator structure 90 is formed in one or more embodiments, as shown inFIG. 10 . Exemplary embodiments of thestructure 90 include 300 mm InGaAs-on-insulator, GaAs-on-insulator and InP-on-insulator wafers. Other compound-on-insulator structures are obtainable, as those of skill in the art will appreciate. II-VI semiconductor layers can be employed in the fabrication of alternative structures, for example ZnSe-on-insulator structures, using techniques similar to those described herein. (SeeFIGS. 24-27 and discussion below.) The specific examples provided herein are accordingly to be considered exemplary as opposed to limiting. -
FIG. 11 shows an exemplary embodiment of astructure 100 including anetch stop layer 102 buried within thesemiconductor layer 46. Thestructure 100 is otherwise the same as that shown inFIG. 4 following ion implantation within thesemiconductor layer 46. Theetch stop layer 102 has the same composition as theepitaxial oxide layer 48 in some embodiments. An etch stop layer can possibly be formed by growing a doped layer in some embodiments. The choice of the etch stop layer depends on the III-V or II-VI material chosen. For InGaAs, InP could act as etch stop layer, since it has the same lattice constant as 53% InGaAs but different chemical properties. For embodiments employing ZnSe, as discussed further below, a buried Ge layer in the relaxed ZnSe could be employed as an etch stop layer. -
FIGS. 12-19 show steps of an exemplary process that includes the formation of an amorphous oxide layer on an epitaxial oxide layer. The same reference numerals are employed to designate elements also found in the structures shown inFIGS. 1-11 . Referring toFIG. 12 , anamorphous oxide layer 104 such as silicon oxide is deposited on the exposed surface of theepitaxial oxide layer 48 of the structure shown inFIG. 3 . This process is well known in art and includes, for example, LPCVD oxide deposition, with optional densification anneal. Other oxide deposition processes would also be feasible. Silicon oxide is preferred in one or more embodiments, but other oxides or nitrides would be acceptable if optimized. Ahydrogen layer 50 or layer of inert gas ions is implanted within thesemiconductor layer 46 and through the oxide layers 48, 102 forming a cleavage plane, as shown inFIG. 13 . - Referring to
FIG. 14 , the structure obtained following deposition of the silicon oxide layer is positioned in opposing relation to asilicon handle wafer 52. The structure is wafer bonded to the handle wafer such that thesilicon oxide layer 104 is bonded to the handle wafer. As discussed above, the handle wafer may itself include a surface oxide layer (not shown), in which case thesilicon oxide layer 104 would bond to the silicon oxide surface layer on the handle wafer. Techniques for wafer bonding of silicon oxide to silicon are well known to those of skill in the art. The use of a silicon oxide layer on the epitaxial oxide layer allows the use of such conventional techniques. - A fracture is created within the
semiconductor layer 46 along the cleavage plane formed by thehydrogen layer 50 in one or more exemplary embodiments, splitting the structure shown inFIG. 15 into afirst structure 110 and asecond structure 70 as shown inFIG. 16 . Thefirst structure 110 includes the silicon handle layer, theoxide layer 104 bonded to the handle layer, the epitaxial oxide layer, and a residual portion of thecompound semiconductor layer 46 on which theepitaxial oxide layer 48 was formed. Thefirst structure 110 is shown inFIG. 17 with the rough, defective surface of the semiconductor layer portion schematically illustrated. Thesecond structure 70 can be reused. - The rough, defective portion of the semiconductor layer remaining on the
first structure 110 is removed as shown inFIG. 18 . Asemiconductor layer 82 having substantially the same composition as the originally depositedsemiconductor layer 46 is epitaxially grown on the exposed surface of the lattice matchedoxide layer 48 of thestructure 120 as shown inFIG. 19 . As described above with respect to the structure shown inFIG. 10 , a substantially perfect, relaxed compound semiconductor-on-insulator structure is provided. - The processes disclosed herein facilitate reuse of the
original substrate 40 and the lattice engineered semiconductor stack formed thereon.FIG. 20 shows one of the structures obtained following separation of thefirst structure 60 from thesecond structure 70 along the cleavage plane defined by the exemplary implantedhydrogen layer 50. Such separation is shown inFIG. 7 . Thestructure 70 is subjected to touch-up chemical mechanical planarization (CMP) to obtain the structure shown inFIG. 21 . Aportion 46A of theresidual semiconductor layer 46 remains on the semiconductor stack in some embodiments. The lattice of theplanarized semiconductor layer 46A is sufficiently defect-free for growing thenew semiconductor layer 46B on which the epitaxial oxide layer is later formed. Growing the III-V or II-VI semiconductor material thick traps possible defects at the lower interface and the top portion is defect free. - As shown in
FIG. 22 , asemiconductor layer 46B having substantially or exactly the same composition as the originally formedsemiconductor layer 46 is grown on the structure. The thickness of thesemiconductor layer 46B should be sufficient such that it is substantially free of defects at the top surface. A semiconductor layer thickness of about half a micron (0.5 g) is provided in one or more embodiments. - An
oxide layer 48 is grown epitaxially on the surface of thesemiconductor layer 46B, forming thestructure 130 shown inFIG. 23 . Thestructure 130 can be further processed as described above with respect toFIGS. 4-10 to form a relaxed compound semiconductor-on-insulator structure. Standard size wafers (e.g. 300 mm) having, for example, III-V material-on-insulator or II-VI material-on-insulator structures can be fabricated using the techniques described herein. - As discussed above, the
handle wafer 52 in some embodiments is a silicon wafer. Structures including silicon wafers are suitable for many types of electronic devices. Glass, quartz, or sapphire handle wafers may be employed in other embodiments where greater transparency is desired. Light emitting diodes and solar cells are among the applications that could benefit from a substantially transparent handle layer. - Referring to
FIGS. 24-27 , exemplary steps for forming a structure including a ZnSe semiconductor layer are illustrated. Asilicon substrate 152 is obtained, as shown inFIG. 24 . The substrate can be in the form of a 200 mm or 300 mm wafer in one or more embodiments. A thick (e.g. 1-2 μm)germanium layer 156 is grown on thesubstrate 152. An optionalSiGe seed layer 154, as shown inFIG. 25 , may first be grown on thesubstrate 152 to facilitate growth of thegermanium layer 156. The seed layer, if employed, contains a high percentage (e.g. 30-80%, more preferably 40-60% germanium) of germanium. The thickness of the seed layer is between 5-50 nm in one or more embodiments. The process is familiar to those of skill in the art. U.S. Pat. No. 7,071,087 discloses an exemplary process for forming a germanium layer on an off-cut silicon substrate using SiGe seed layer(s) having higher germanium content. While seed layer(s) having such higher germanium content may alternatively be employed to form the seed layer(s) 154, better initial seed layer growth and lower incubation times are observed by using SiGe having the germanium content in the preferred (40-60%) range. - As shown in
FIG. 26 , alayer 158 of desired semiconductor material such as a Group II-VI or Group III-V material is grown on thethick germanium layer 156. In the illustrative embodiment, a II-VI material, namely zinc selenide (ZnSe) is grown on the germanium layer. Growth of a ZnSe layer on germanium is known to the art. An exemplary technique is disclosed in U.S. Pat. No. 7,071,087, which is incorporated by reference herein. The ZnSe layer has a thickness of 100-500 nm in one or more embodiments. Anepitaxial oxide layer 160 is grown on theZnSe layer 158 to obtain thestructure 150 shown inFIG. 27 . Growth of an epitaxial oxide layer on ZnSe using MBE is discussed above. In this embodiment, the lattice grading (relaxation) and defect trapping at the bottom of thesemiconductor layer 158 will take place in thegermanium layer 156. Thestructure 150 is subjected to ion implantation through the epitaxial oxide layer to form a cleavage plane in thesemiconductor layer 158.FIG. 4 and the related discussion in the patent specification describe such a procedure. Process steps described above with respect toFIGS. 5-10 are performed to obtain a structure as shown inFIG. 10 with a ZnSe semiconductor layer as opposed to the InGaAs layer semiconductor layer shown therein. Optionally, a silicon oxide layer (not shown) may be formed on theepitaxial oxide layer 160 to facilitate wafer bonding as discussed above with respect toFIGS. 12-15 . - While the embodiments shown in
FIGS. 1-7 , 11, and 12-16 employ agermanium substrate 40, athick germanium layer 156 formed on a silicon substrate as described above with respect toFIGS. 24 and 25 may alternatively be used to fabricate astructure 90 such as shown inFIG. 10 . The use of a silicon structure in this manner facilitates 200-300 mm wafer application to the process. The silicon substrate is off-cut six degrees in some embodiments. Astructure 170 as shown inFIG. 28 would accordingly be obtained by forming theGaAs layer 42, the gradedlayer 44, theInGaAs layer 46 and theepitaxial oxide layer 48 on thegermanium layer 156. Exemplary thickness ranges for the various layers are provided inFIG. 28 . As indicated, the GaAs layer may be about 500 nm in thickness and the gradedlayer 44 between 1-5 μm. The InGaAs layer in the exemplary embodiment is between 100-500 nm in thickness and the epitaxial oxide layer is about 100 nm. Further processing such as ion implantation within the InGaAs layer, wafer bonding, fracturing along a cleavage plane, etc. would be performed using thestructure 170 in the same manner described above with respect toFIGS. 4-10 . - Given the discussion thus far, an exemplary fabrication method includes growing a lattice engineered
semiconductor stack substrate 40, growing afirst epitaxial layer 46 of a desired semiconductor material on a top surface of the stack, growing anepitaxial oxide layer 48 on the desired semiconductor material, and forming a cleavage plane in the desired semiconductor layer via implantation, thereby forming a first structure comprising the substrate, the lattice engineered semiconductor stack, the layer of desired semiconductor material including the cleavage plane, and the epitaxial oxide layer. An exemplary first structure is shown inFIG. 4 . The method further includes bonding the first structure to ahandle wafer 52 and causing a fracture along the cleavage plane, thereby forming a second structure comprising the handle wafer, the epitaxial oxide layer, and a portion of the layer of desired semiconductor material. An exemplary second structure is shown inFIG. 8 . The residual portion of the layer of desired semiconductor material is removed from the second structure. Asecond epitaxial layer 82 of the desired semiconductor material is grown on the epitaxial oxide layer. Theexemplary structures FIGS. 10 and 19 , respectively, can be obtained through such a fabrication method. The desired semiconductor layer comprises group III-V materials in some embodiments and group II-VI materials in other embodiments. The lattice engineered semiconductor stack comprises a graded layer of group III-V compounds in embodiments where the desired semiconductor layer is comprised of a group III-V material such as InGaAs. The fabrication method includes forming an oxide layer such as silicon oxide on the epitaxial oxide layer in some embodiments wherein the step of bonding the first structure to thehandle wafer 52 further includes bonding theoxide layer 104 to thehandle wafer 52, such as shown inFIG. 15 . As discussed above, thestructure 70 including thesubstrate 40 can optionally be reused. The fabrication method may further include obtaining athird structure 70 comprising the substrate, the lattice engineered semiconductor stack, and a residual layer of the desired semiconductor material obtained from the fracture along the cleavage plane, planarizing a surface of the residual layer, growing afurther layer 46B comprising the desired semiconductor material on the planarized surface of theresidual layer 46A, and growing a further epitaxial oxide layer on the further layer comprising the desired semiconductor material. Theexemplary structure 130 shown inFIG. 23 can be produced in this manner. One or more embodiments of the method further includes of forming an etch stop layer within the first epitaxial layer of the desired semiconductor material as shown inFIG. 11 . The cleavage plane comprises hydrogen in one or more embodiments and is implanted above the etch stop layer in embodiments where an etch stop layer is employed. - A further exemplary method includes growing a first epitaxial layer of a desired compound semiconductor material on a substrate.
FIGS. 2 and 28 show anepitaxial layer 46 wherein the desired compound semiconductor material is InGaAs grown on a gradedlayer 44 on a germanium substrate. In an alternative embodiment, the desired compound semiconductor material is ZnSe grown directly on thegermanium layer 156 on asilicon substrate 152 as shown inFIG. 26 . An epitaxial oxide layer (48 inFIGS. 3 and 28 , 160 inFIG. 27 ) is grown on and lattice matched to the layer of the desired compound semiconductor material. A cleavage plane is formed in the layer of the desired semiconductor material via implantation, thereby forming a first structure comprising the substrate, the layer of the desired compound semiconductor material having the formed cleavage plane, and the epitaxial oxide layer.FIGS. 4 and 13 illustrate exemplary first structures. Once subjected to ion implantation, the embodiments ofFIGS. 27 and 28 would also form first structures. The first structure is bonded to ahandle wafer 52. The method further includes causing a fracture along the cleavage plane, thereby forming a second structure comprising the handle wafer, the epitaxial oxide layer, and a portion of the layer of desired compound semiconductor material. Exemplary second structures are shown inFIGS. 8 and 17 . The portion of the layer of desired compound semiconductor material is removed from the second structure and a second epitaxial layer of the desired compound semiconductor material is grown on the epitaxial oxide layer.FIGS. 18-19 respectively show removal of the residual portion of the desired semiconductor material and growth of asecond epitaxial layer 82 of the desired compound semiconductor material. - An exemplary structure provided in accordance with the disclosed embodiments includes a
crystalline semiconductor substrate 40, a lattice engineeredsemiconductor stack first region 42 adjoining the substrate and substantially lattice matched to the substrate and a second region not lattice matched to the substrate and defining a top surface of the semiconductor stack. A compound semiconductor layer adjoins and is substantially lattice matched to the top surface of the semiconductor stack. In some embodiments, a compound semiconductor layer such as aZnSe layer 158 is grown directly on athick germanium layer 156 rather than a gradedcompound semiconductor layer 44. Anepitaxial oxide layer 48 adjoins thecompound semiconductor layer 46.FIG. 3 shows such one exemplary structure.FIG. 27 shows analternative structure 150 including anepitaxial oxide layer 160 adjoining acompound semiconductor layer 158. The structure further includes an implanted cleavage plane layer within the compound semiconductor layer, which in some embodiments comprises an implantedhydrogen layer 50. One or more embodiments of the structure further include asilicon oxide layer 104 on theepitaxial oxide layer 48 such as shown inFIG. 13 . The compound semiconductor layer is comprised of a group III-V material in one or more embodiments and a group II-VI material in alternative embodiments. The exemplary structure may further include a handle wafer which is, in some embodiments, bonded to thesilicon oxide layer 104. - A further exemplary structure includes or consists of a handle substrate, an epitaxial oxide layer, the
epitaxial oxide layer 48 being bonded directly or indirectly to the handle substrate, and a compound semiconductor layer adjoining the epitaxial oxide layer and lattice matched to the epitaxial oxide layer. In some embodiments such as shown inFIG. 19 , anoxide layer 104 is between the handle substrate and the epitaxial oxide layer, adjoining both. The oxide layer is directly bonded to the handle substrate in such embodiments. The compound semiconductor layer is formed from group III-V materials in some embodiments. In other embodiments, the compound semiconductor layer is a layer of group II-VI materials such as ZnSe. - A further structure provided in accordance with the disclosure includes a germanium base, one or more compound semiconductor layers adjoining the germanium base, the one or more compound semiconductor layers including a top layer of a desired compound semiconductor material, and an epitaxial oxide layer adjoining and lattice matched to the top layer.
FIG. 27 shows anexemplary structure 150 including onecompound semiconductor layer 158 that adjoins a germanium layer formed on a silicon substrate. In other embodiments, the germanium base is a germanium substrate such as thesubstrate 40 shown inFIGS. 1-7 . Theepitaxial oxide layer 160 adjoins and is lattice matched to thecompound semiconductor layer 158, which is ZnSe in one or more exemplary embodiments.FIG. 28 provides a schematic illustration of an alternative embodiment of the further structure. In this embodiment, thestructure 170 includes multiple compound semiconductor layers adjoining thegermanium layer 156, thetop layer 46 being a layer of the desired compound semiconductor material. - The terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting of the invention. As used herein, the singular forms “a”, “an” and “the” are intended to include the plural forms as well, unless the context clearly indicates otherwise. It will be further understood that the terms “comprises” and/or “comprising,” when used in this specification, specify the presence of stated features, steps, operations, elements, and/or components, but do not preclude the presence or addition of one or more other features, steps, operations, elements, components, and/or groups thereof Terms such as “above” and “below” are used to indicate relative positioning of elements or structures to each other as opposed to relative elevation.
- The corresponding structures, materials, acts, and equivalents of all means or step plus function elements in the claims below are intended to include any structure, material, or act for performing the function in combination with other claimed elements as specifically claimed. The description of the various embodiments has been presented for purposes of illustration and description, but is not intended to be exhaustive or limited to the forms disclosed. Many modifications and variations will be apparent to those of ordinary skill in the art without departing from the scope and spirit of the invention. The embodiments were chosen and described in order to best explain the principles of the invention and the practical application, and to enable others of ordinary skill in the art to understand the various embodiments with various modifications as are suited to the particular use contemplated.
Claims (10)