US20150030826A1 - Method for creating a textured bond coat surface - Google Patents
Method for creating a textured bond coat surface Download PDFInfo
- Publication number
- US20150030826A1 US20150030826A1 US13/951,542 US201313951542A US2015030826A1 US 20150030826 A1 US20150030826 A1 US 20150030826A1 US 201313951542 A US201313951542 A US 201313951542A US 2015030826 A1 US2015030826 A1 US 2015030826A1
- Authority
- US
- United States
- Prior art keywords
- layer
- particles
- depositing
- bond coat
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A method for forming a textured bond coat surface (48) for a thermal barrier coating system (44) of a gas turbine component (34). The method includes selectively melting portions of a layer of alloy particles (16) with a patterned energy beam (20) to form successive layers of alloy material (16′, 16″) until a desired surface geometric feature (26) is achieved. The energy beam pattern may be indexed between layers to form a protruding undercut (28) in the geometric feature. The patterned energy beam may be formed by directing laser energy from a diode laser (30) through a cartridge filter (32). Particles of a flux material (18) may be melted along with the alloy particles to form a protective layer of slag (22) over the melted and cooling alloy material.
Description
- This invention relates generally to the field of materials technology, and more particularly to a method for creating a textured surface in a bond coat of a thermal barrier coating system.
- Ceramic thermal barrier coating systems are used on gas turbine engine hot gas path components to protect the underlying metal alloy substrate from combustion gas temperatures that exceed the safe operating temperature of the alloy. A typical thermal barrier coating system may include a bond coat, such as an MCrAlY material, deposited onto the substrate alloy and a ceramic topcoat, such as yttria stabilized zirconia, deposited onto the bond coat. It is known that strong adhesion between the layers of such systems is critical for proper functioning and long life of the coating system, and that a degree of surface roughness in the interface between the layers provides a beneficial mechanical interlock in that regard.
- Bond coat material is often deposited by a spray process, such as High Velocity Oxy-Fuel (HVOF) or Air Plasma Spray (APS). It is known to control spray parameters when depositing a bond coat layer in order to achieve a degree of surface roughness in the deposited coating. However, the degree of roughness and the shape of the surface features in the deposited coating that are created by controlling the spray parameters are limited.
- It is also known to texture the surface of a bond coat layer prior to the deposition of a ceramic insulating layer by using a material removal process, such as laser ablation, micromachining or photolithography, such as described in U.S. Pat. No. 5,723,078. As the firing temperatures of advance gas turbine engines continue to increase, further improvements in thermal barrier coating systems and methods of applying such coatings are desired.
- The invention is explained in the following description in view of the drawings that show:
-
FIGS. 1-5 illustrate sequential steps for depositing a coating onto a substrate with a surface texture including geometric features having protruding undercuts. -
FIG. 6 illustrates a layer of thermal barrier coating material deposited over a textured surface of a bond coat material. -
FIG. 7 illustrates a layer of bond coat material deposited over a textured surface of a superalloy component with an overlying layer of ceramic thermal barrier coating material. - The present inventors have recognized that known bond coat texturing processes that rely upon material removal are inherently inefficient because unwanted material is first deposited and is then removed. The methods of the present invention cause material to be initially deposited in a way that creates the desired texture pattern. Furthermore, because the methods of the present invention create a textured surface by depositing a plurality of layers of material, a wide range of surface feature geometries, including undercuts, are made possible.
-
FIG. 1 is a partial cross-sectional view of agas turbine component 10 having a relativelysmooth surface 12 to which it is desired to add a textured surface geometry. Thesurface 12 may be a surface of an existing bond coat material layer that is to be textured, or it may be the surface of a superalloy substrate over which a layer of bond coat material is to be applied. A layer ofpowder 14 is deposited onto thesurface 12. The layer ofpowder 14 includes particles of ametal alloy 16 and particles of aflux material 18. Themetal alloy 16 may be superalloy material for the embodiment where the surface of the superalloy substrate is to be textured, or it may be a bond coat material for the embodiment where the surface of a bond coat is to be textured. Theflux material 18 is applied to provide cleansing and atmospheric protection functions during a subsequent melting step. Accordingly, the particles ofmetal alloy 16 and particles offlux material 18 may be mixed together and applied as a single layer in one embodiment, or mixed and applied simultaneously by directing a spray of metal alloy particles and a spray of flux material particles simultaneously toward the surface. Alternatively, the particles ofmetal alloy 16 may be applied to thesurface 12 first and then covered by the particles offlux material 18 in another embodiment. -
FIG. 2 illustrates the layer ofpowder 14 being exposed to a pattern ofenergy 20 to melt selected regions of the layer ofpowder 14 to form a pattern of themetal alloy 16′ covered byslag 22 on thesurface 12. Upon cooling, theslag 22 andexcess powder 14 are removed to reveal thecomponent 10 with atextured surface 12′, as illustrated inFIG. 3 . - The steps of
FIGS. 1 and 2 may then be repeated, as illustrated inFIG. 4 to add a further layer ofmetal alloy 16″. Note that the pattern ofenergy 20′ inFIG. 4 is somewhat different than the pattern ofenergy 20 inFIG. 2 , and as a result, the second layer of depositedmetal alloy 16″ has aregion 24 that is indexed from and somewhat cantilevered beyond the first layer of depositedmetal alloy 16′. The heat input of theenergy 20 is selected such that the region of melting does not extend to a full depth of the layer ofpowder 14 in thecantilevered region 24. Such indexing of the pattern ofenergy 20 between layers can be repeated for additional layers as desired to create a desired finaltextured surface 12″ havinggeometric features 26 including protrudingundercuts 28, as illustrated inFIG. 5 . One skilled in the art will appreciate that any surface geometric feature will provide a degree of mechanical interlocking with a subsequently applied overcoat layer (i.e. bond coat or thermal barrier coating), and that afeature 26 with a protruding undercut 28 may be especially beneficial in that regard. -
FIG. 6 illustrates thecomponent 10 after the further deposit of a layer ofmaterial 31 over thesurface 12″ having the layer ofgeometric features 26. In this illustration, thesurface 12″ is bond coat material and the layer ofmaterial 31 is a ceramic thermal barrier coating material wherein the protruding undercuts 28 function to mechanically anchor theceramic material 31. One will appreciate that the bond coat material may be deposited onto a superalloy substrate that is not illustrated in this view. -
FIG. 7 is a partial cross-sectional illustration of agas turbine component 34 wherein a layer ofbond coat material 36 is deposited over atextured surface 38 of asuperalloy substrate 40 with an overlying layer of ceramic thermalbarrier coating material 42 to form a thermalbarrier coating system 44. Thesurface 38 is textured by the addition ofgeometric features 46 that were deposited by the process described above. Note that the texturing ofsurface 38 is reflected in a more subtle but still effective texturing of thesurface 48 of thebond coat material 36. Advantageously, when thesuperalloy substrate 40 is a cast product and the superalloy material is one of the many difficult to weld materials that are commonly used for gas turbine engine components, the process described herein facilitates the joining of additional superalloy material to form thegeometric features 46 with a greatly reduced risk of cracking and higher degree of geometric precision that could otherwise be achieved by using a welding additive process, as more fully described below. - The layer of
powder 14 may be one to several millimeters in thickness in some embodiments rather than the fraction of a millimeter typical with known selective laser melting and sintering processes. Typical powdered prior art flux materials have particle sizes ranging from 0.5-2 mm, for example. However, the powderedalloy material 16 may have a particle size range (mesh size range) of from 0.02-0.04 mm or 0.02-0.08 mm or other sub-range therein. This difference in mesh size range may work well in the embodiment where the materials constitute separate layers; however, in the embodiment where the particles are mixed together before being applied to thesurface 12, it may be advantageous for the powderedalloy material 38 and the powderedflux material 40 to have overlapping mesh size ranges, or to have the same mesh size range in order to facilitate mixing and feeding of the powders and to provide improved flux coverage during the melting process. - The
flux material 18 and resultant layer ofslag 22 provide a number of functions that are beneficial during the melting process. First, they function to shield both the region of molten material and the solidified (but still hot)alloy material 16′ from the atmosphere as the material cools. The slag floats to the surface to separate the molten or hot metal from the atmosphere, and the flux may be formulated to produce a shielding gas in some embodiments, thereby avoiding or minimizing the use of expensive inert gas. Second, theslag 22 acts as a blanket that allows thesolidified alloy material 16′ to cool slowly and evenly, thereby reducing residual stresses that can contribute to cracking. Third, theslag 22 helps to shape the pool ofmolten alloy 16′. Fourth, theflux material 18 provides a cleansing effect for removing trace impurities such as sulfur and phosphorous that contribute to cracking. Such cleansing includes de-oxidation of themetal alloy powder 16. Because theflux powder 18 is in intimate contact with thealloy powder 16, it is especially effective in accomplishing this function. Furthermore, theflux material 18 may provide energy absorption and trapping functions to more effectively convert thebeam energy 20 into heat energy, thus facilitating a precise control of heat input, such as within 1-2%, and a resultant tight control of material temperature during the process. Finally, the flux may be formulated to compensate for loss of volatized elements during processing or to actively contribute elements to the deposit that are not otherwise provided by the alloy powder itself. - The patterned
energy beam 20 may be produced by adiode laser 30 having a generally rectangular cross-sectional shape, although other known types of energy beams may be used, such as electron beam, plasma beam, one or more circular laser beams, a scanned laser beam (scanned one, two or three dimensionally), an integrated laser beam, etc. The rectangular shape may be particularly advantageous for embodiments having a relatively large area to be textured. The broad area beam produced by a diode laser helps to reduce weld heat input, heat affected zone, dilution from the substrate and residual stresses, all of which reduce the tendency for the cracking effects normally associated with superalloy repair. The laser energy may be patterned by any known beam shaping optics, such as acartridge filter 32 having pre-determine openings. Thecartridge 32 used to deposit the first layer of material inFIG. 2 is conveniently changed to acartridge 32′ having a somewhat different pattern of openings for depositing the second layer inFIG. 4 . Optical conditions and hardware optics used to generate a broad area laser exposure may include but are not limited to: defocusing of the laser beam; use of diode lasers that generate rectangular energy sources at focus; use of integrating optics such as segmented mirrors to generate rectangular energy sources at focus; scanning (rastering) of the laser beam in one or more dimensions; and the use of focusing optics of variable beam diameter (e.g. 0.5 mm at focus for fine detailed work varied to 2.0 mm at focus for less detailed work). The motion of the optics and/or substrate may be programmed as in a selective laser melting or sintering process to build a custom shape layer deposit. Advantages of this process over known laser melting or sintering processes include: high deposition rates and thick deposit in each processing layer; improved shielding that extends over the hot deposited metal without the need for inert gas; flux will enhance cleansing of the deposit of constituents that otherwise may lead to cracking; flux will enhance laser beam absorption and minimize reflection back to processing equipment; slag formation will shape and support the deposit, preserve heat and slow the cooling rate, thereby reducing residual stresses; flux may compensate for elemental losses or add alloying elements, and powder and flux pre-placement or feeding can efficiently be conducted selectively because the thickness of the deposit greatly reduces the time involved in total part building. - Flux materials which could be used include commercially available fluxes such as those sold under the names Lincolnweld P2007, Bohler Soudokay NiCrW-412, ESAB OK 10.16 or 10.90, Special Metals NT100, Oerlikon OP76, Sandvik 50SW or SAS1. The flux particles may be ground to a desired smaller mesh size range before use. Any available structural alloy, superalloy or bond coat material that is appropriate for thermal barrier coating systems may be used.
- While various embodiments of the present invention have been shown and described herein, it will be obvious that such embodiments are provided by way of example only. Numerous variations, changes and substitutions may be made without departing from the invention herein. Accordingly, it is intended that the invention be limited only by the spirit and scope of the appended claims.
Claims (17)
1. A method for forming a textured bond coat surface for a thermal barrier coating system, the method comprising:
depositing a layer of powder comprising particles of a metal alloy and particles of a flux material onto a surface;
selectively melting portions of the layer of powder with an energy beam to form a pattern of the metal alloy covered by a layer of slag on the surface;
removing the layer of slag; and
repeating the depositing and selectively melting steps if required to achieve a desired textured surface.
2. The method of claim 1 , where the depositing step comprises depositing the layer of powder to comprise particles of a bond coat material and particles of a flux material to form the desired textured surface on a bond coat layer.
3. The method of claim 1 , further comprising:
depositing the layer of powder to comprise particles of a superalloy material and particles of a flux material onto the surface of a superalloy substrate to create the desired textured surface on the superalloy substrate; and
depositing a layer of bond coat material over the textured superalloy substrate surface.
4. The method of claim 1 , wherein the step of selectively melting comprises directing a laser energy beam toward the layer of powder through beam shaping optics.
5. The method of claim 1 , wherein the step of depositing comprises pre-placing a layer of mixed metal alloy and flux material particles onto the surface.
6. The method of claim 1 , wherein the step of depositing comprises simultaneously directing a spray of metal alloy particles and a spray of flux material particles onto the surface.
7. The method of claim 1 , wherein the step of depositing comprises depositing a layer of particles of the metal alloy onto the surface and then depositing a layer of particles of the flux material onto the layer of particles of the metal alloy.
8. The method of claim 1 , further comprising selecting the particles of metal alloy and the particles of flux material to have overlapping mesh size ranges.
9. The method of claim 1 , further comprising forming the desired textured surface to include a geometric feature comprising a protruding undercut by:
selectively melting portions of a first layer of powder with the energy beam having a first pattern to form a first layer of the geometric feature; and
selectively melting portions of a second layer of powder with the energy beam having a second pattern indexed from the first pattern to form a second layer of the geometric feature cantilevered beyond the first layer to at least partially define the protruding undercut.
10. A gas turbine engine component comprising a thermal barrier coating system comprising the geometric feature formed by the method of claim 9 .
11. A method for forming a textured surface for a thermal barrier coating system, the method comprising:
depositing particles of a bond coat material onto a surface;
selectively melting portions of the bond coat material particles with an energy beam pattern to form a first layer of a desired textured surface of the bond coat material on the surface; and
repeating the depositing and selectively melting steps to form subsequent layers of the textured surface until the desired textured surface of the bond coat material is achieved.
12. The method of claim 11 , further comprising indexing the energy beam pattern between layers such that not all layers have the same geometry.
13. The method of claim 11 , further comprising indexing the energy beam pattern between layers to form a geometric feature comprising a protruding undercut.
14. A gas turbine engine component comprising a thermal barrier coating system comprising the geometric feature formed by the method of claim 13 .
15. The method of claim 11 , further comprising:
depositing particles of the bond coat material and particles of a flux material onto the surface;
selectively melting portions of the bond coat and flux material particles to form a first layer of the bond coat material covered by a layer of slag on the surface; and
removing the slag prior to any subsequent depositing and selectively melting step.
16. The method of claim 11 , further comprising selectively melting the portions of the bond coat material particles with a laser beam patterned by beam shaping optics comprising a filter cartridge.
17. The method of claim 16 , wherein a first filter cartridge is used to form a first laser beam pattern for a first layer, and a second filter cartridge is used to form a second laser beam pattern different than the first laser beam pattern for a subsequent layer.