US20140231816A1 - High electron mobility transistor and method of forming the same - Google Patents
High electron mobility transistor and method of forming the same Download PDFInfo
- Publication number
- US20140231816A1 US20140231816A1 US13/769,785 US201313769785A US2014231816A1 US 20140231816 A1 US20140231816 A1 US 20140231816A1 US 201313769785 A US201313769785 A US 201313769785A US 2014231816 A1 US2014231816 A1 US 2014231816A1
- Authority
- US
- United States
- Prior art keywords
- layer
- iii
- compound layer
- over
- compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
- In semiconductor technology, due to the high mobility values, Group III-Group V (or III-V) semiconductor compounds are used to form various integrated circuit devices, such as high power field-effect transistors, high frequency transistors, and High Electron Mobility Transistors (HEMTs). A HEMT is a field effect transistor incorporating a 2-Dimensional Electron Gas (2DEG) layer close to the junction between two materials with different band gaps (i.e., a heterojunction). The 2DEG layer, instead of a doped region as is generally the case for Metal Oxide Semiconductor Field Effect Transistors (MOSFETs), acts as the channel. In contrast with the MOSFETs, the HEMTs have a number of attractive properties including high electron mobility, the ability to transmit signals at high frequencies, etc.
- For a more complete understanding of the embodiments, and the advantages thereof, reference is now made to the following descriptions taken in conjunction with the accompanying drawings, in which:
-
FIGS. 1 through 9 are cross-sectional views of intermediate stages in the manufacturing of a High Electron Mobility Transistor (HEMT) in accordance with some exemplary embodiments; -
FIG. 10 illustrates a schematic process flow for forming the HEMT in accordance with exemplary embodiments; and -
FIGS. 11 through 17 are cross-sectional views of intermediate stages in the manufacturing of HEMTs in accordance with alternative embodiments. - The making and using of the embodiments of the disclosure are discussed in detail below. It should be appreciated, however, that the embodiments provide many applicable concepts that can be embodied in a wide variety of specific contexts. The specific embodiments discussed are illustrative, and do not limit the scope of the disclosure.
- A High Electron Mobility Transistor (HEMT) and the method of forming the same are provided in accordance with various exemplary embodiments. The intermediate stages of forming the HEMT are illustrated. The variations of the embodiments are discussed. Throughout the various views and illustrative embodiments, like reference numbers are used to designate like elements. The process for forming the HEMT may be found referring to the
exemplary process flow 100 shown inFIG. 10 . Additional process steps may be provided before, during, or afterprocess 100 inFIG. 10 . Various figures have been simplified for a better understanding of the concepts of the present disclosure. -
FIGS. 1 through 9 illustrate the cross-sectional views of intermediate stages in the formation of an HEMT in accordance with exemplary embodiments. The HEMT is formed using a gate first approach, in which a gate electrode is formed before the formation of source and drain regions. Referring toFIG. 1 , which is a cross-sectional view of a portion ofsubstrate 20,substrate 20 may be a part ofwafer 10. In some embodiments,substrate 20 includes a silicon carbide (SiC) substrate, a sapphire substrate, a silicon substrate, or the like.Substrate 20 may be a bulk substrate formed of a bulk material, or may be a composite substrate including a plurality of layers that are formed of different materials. - In accordance with some embodiments,
buffer layer 22 is first formed oversubstrate 20, which acts as the buffer and/or the transition layer for the subsequently formed overlying layers. The respective step is shown asstep 101 inFIG. 10 .Buffer layer 22 may be epitaxially grown using Metal Organic Vapor Phase Epitaxy (MOVPE).Buffer layer 22 may function as an interface to reduce lattice mismatch betweensubstrate 20 and the subsequently formed III-V compound layers 26 (FIG. 3) and 28 (FIG. 4 ). In some embodiments,buffer layer 22 includes an aluminum nitride (AlN) layer having a thickness in a range between about 10 nanometers (nm) and about 300 nm.Buffer layer 22 may include a single layer or a plurality of layers. For example,buffer layer 22 may include low-temperature AlN layer 22A formed at a temperature between about 800° C. and about 1,200° C., and high-temperature AlN layer 22B formed at a temperature between about 1,000° C. and about 1,400° C. In some embodiments,buffer layer 22A has a thickness in a range between about 10 nanometers (nm) and about 100 nm, andbuffer layer 22B has a thickness in a range between about 100 nanometers (nm) and about 200 nm. - Referring to
FIG. 2 , III-Vcompound layer 24 is formed overbuffer layer 22. The respective step is also shown asstep 101 inFIG. 10 . III-Vcompound layer 24 may also act as a buffer layer, and hence is referred to asbuffer layer 24 hereinafter.Buffer layer 24 can be epitaxially grown using MOVPE, for example.Buffer layer 24 may include an aluminum gallium nitride (AlGaN) layer, which may have a thickness in a range from about 500 nm to about 1,000 nm.Buffer layer 24 may be a graded buffer layer, which means that the relative amounts of the respective aluminum and/or gallium content change with depth in the layer throughout a part or the total thickness ofbuffer layer 24. The relative amounts may change gradually to reduce the lattice parameter with the distance fromsubstrate 20. For example,FIG. 2 schematically illustrated threesub layers sub layers sub layer 24A has an aluminum percentage between about 65 percent and about 85 percent,sub layer 24B has an aluminum percentage between about 35 percent and about 60 percent, andsub layer 24C has an aluminum percentage between about 10 percent and about 30 percent. - Referring to
FIG. 3 , first III-Vcompound layer 26 is grown over buffer layer 24 (step 102 inFIG. 10 ). In some embodiments, III-Vcompound layer 26 is a gallium nitride (GaN) layer. GaNlayer 26 may be epitaxially grown by using, for example, MOVPE, during which a gallium-containing precursor and a nitrogen-containing precursor are used. The gallium-containing precursor may include trimethylgallium (TMG), triethylgallium (TEG), or other suitable gallium-containing chemicals. The nitrogen-containing precursor may include ammonia (NH3), tertiarybutylamine (TBAm), phenyl hydrazine, or other suitable chemicals. In some exemplary embodiments, III-Vcompound layer 26 has a thickness ranging from about 0.5 micron to about 10 microns. III-Vcompound layer 26 may be undoped. Alternatively, III-Vcompound layer 26 is unintentionally doped, such as lightly doped with n-type dopants due to a precursor used for forming III-V compound layer 26, with no dopant that may cause III-V compound layer 26 to be n-type or p-type intentionally added. - Referring to
FIG. 4 , a second III-V compound layer 28 is grown on, and may contact, III-V compound layer 26. The respective step is shown asstep 104 inFIG. 10 . III-Vcompound layer 28 has a band gap greater than the band gap of III-V compound layer 26. Aninterface 31 is formed between III-V compound layer 26 and III-V compound layer 28. When the respective HEMT is operated,carrier channel 30, which is known as a Two-Dimensional Electron Gas (2DEG), is formed and located in III-Vcompound layer 26 nearinterface 31. In some embodiments, III-Vcompound layer 28 is an AlGaN layer. - III-V
compound layer 28 may be epitaxially grown over III-V compound layer 26 through MOVPE, for example. When formed of AlGaN, III-V compound layer 28 may be grown using an aluminum-containing precursor, a gallium-containing precursor, and a nitrogen-containing precursor. The aluminum-containing precursor may include trimethylaluminum (TMA), triethylaluminium (TEA), or other suitable chemicals. The gallium-containing precursor and the nitrogen-containing precursor may be selected from the same candidate precursors used for formingGaN layer 26. In some exemplary embodiments, AlGaNlayer 28 has a thickness ranging from about 3 nm to about 50 nm. -
FIG. 5 illustrates the formation of crystallineinterfacial layer 32. The respective step is shown asstep 106 inFIG. 10 . Crystallineinterfacial layer 32 may have a single crystalline structure, or may have a polycrystalline structure. In some embodiments, crystallineinterfacial layer 32 comprises a dielectric material, or comprises a semiconductor material with a relatively high resistivity and a relatively high band gap. In some exemplary embodiments, the band gap of crystallineinterfacial layer 32 is higher than the band gap of III-V compound layer 26 (such as GaN). Furthermore, in some embodiments, the band gap of crystallineinterfacial layer 32 is higher than the band gaps of III-V compound layers 28 (such as AlGaN) and 26, although other materials with lower band gaps may also be used. In the embodiments that crystallineinterfacial layer 32 comprises a semiconductor material, the respective semiconductor material may be selected from AlN, InxAlyGazN (with x+y+z=1, and 0≦x, y, and z≦1), or the like. In the embodiments that crystallineinterfacial layer 32 comprises a dielectric material, the respective dielectric material may be selected from SiNx, SiOx, Al2O3, MgO, Ga2O3, La2O3, HfO2, ZrO2, Y2O3, Gd2O3, Ce2O3, Ta2O3, Ta2O5, combinations thereof, and multi-layers thereof. - Crystalline
interfacial layer 32 may be formed using MOCVD, Atomic Layer Deposition (ALD), Physical Vapor Deposition (PVD), or the like. The process conditions for forming crystallineinterfacial layer 32 is controlled, so that crystallineinterfacial layer 32 has a good crystalline structure, for example, with a single-crystalline structure or at least poly-crystalline structure. With crystallineinterfacial layer 32 having a good crystalline structure, the bonding between the atoms of crystallineinterfacial layer 32 is strong. As a result, the Interfacial Density of States (Dit) at the interface between crystallineinterfacial layer 32 and III-V compound layer 28 is low. The resulting HEMT 42 (FIG. 9 ) thus has a small threshold voltage (Vt) shift, and the reliability ofHEMT 42 is improved. The appropriate process conditions for forming the crystalline structure may include, for example, increasing the deposition temperature to 500° C. or higher. - In some exemplary embodiments, crystalline
interfacial layer 32 may be formed in-situ with the formation of III-V compound layer 28 in a same process chamber, with no vacuum break occurring between the formation of III-V compound layer 28 and the formation of crystallineinterfacial layer 32. In alternative embodiments, crystallineinterfacial layer 32 is formed ex-situ with the formation of III-V compound layer 28, for example, in different process chambers. - Crystalline
interfacial layer 32 may be formed as a crystalline layer as deposited, or may be formed as a poly-crystalline layer or near-amorphous layer, and I subsequently re-crystallized through a high-temperature annealing. The high-temperature annealing may be performed with an annealing temperature greater than the re-crystallization temperature of the deposited layer (re-crystallization temperature depends on the deposited layer species, and may be higher than 550° C., for example, for HfO2). Crystallineinterfacial layer 32 may have a thickness between about 2 Å and about 100 Å, although different thicknesses may be used. - Next, as shown in
FIG. 6 ,dielectric passivation layer 34 is deposited (step 108 inFIG. 10 ) over, and may contact, a top surface of crystallineinterfacial layer 32. In some exemplary embodiments,dielectric passivation layer 34 has a thickness in a range from about 100 Å to about 5,000 Å. An exemplarydielectric passivation layer 34 includes silicon oxide and/or silicon nitride. When comprising silicon nitride,dielectric passivation layer 34 may be formed by performing a Low-Pressure Chemical Vapor Deposition (LPCVD) method (without plasma) using SiH4 and NH3 gases.Dielectric passivation layer 34 protects the underlying crystallineinterfacial layer 32 and III-V compound layer 28 from the damage caused by plasma, which plasma is generated in the following processes. - Next, referring to
FIG. 7 , opening 35 is formed indielectric passivation layer 34, for example, through etching. A portion of the top surface of crystallineinterfacial layer 32 is thus exposed. In some examples,dielectric passivation layer 34 comprises silicon nitride, andopening 35 is formed in a dry etching environment including BCl3, for example, as the etchant gas. - Further referring to 7, in some embodiments,
gate dielectric layer 36 is deposited over dielectric passivation layer 34 (step 110 inFIG. 10 ).Gate dielectric layer 36 also extends intoopening 35, and hence includes a portion overlapping and contacting crystallineinterfacial layer 32. Furthermore,gate dielectric layer 36 includes portions on the sidewalls ofdielectric passivation layer 34, and portions overlappingdielectric passivation layer 34.Gate dielectric layer 36 may reduce a leakage current from the respective gate electrode 38 (FIG. 9 ) to III-V compound layer 28. As a result, the resulting HEMT 42 (FIG. 9 ) could be operated under high operation voltages for various applications. - In some embodiments,
gate dielectric layer 36 has a thickness range from about 3 nm to about 50 nm. The exemplary materials ofgate dielectric layer 36 may be selected from silicon oxide, silicon nitride, gallium oxide, aluminum oxide, scandium oxide, zirconium oxide, lanthanum oxide, hafnium oxide, and combinations thereof.Gate dielectric layer 36 may have an amorphous structure in order to reduce the leakage current flowing throughgate dielectric layer 36, wherein the amorphous structure is formed through adjusting process conditions. In some embodiments,gate dielectric layer 36 is formed using Atomic Layer Deposition (ALD). In other embodiments,gate dielectric layer 36 is formed using Plasma Enhanced Chemical Vapor Deposition (PECVD) or LPCVD. Thegate dielectric layer 36 is formed in an amorphous or non-crystallization structure which may be formed in a lower temperature than crystallineinterfacial layer 32. -
FIG. 8 illustrates a cross-sectional view thewafer 10 after the formation ofgate electrode 38 over gate dielectric layer 36 (step 112 inFIG. 10 ).Gate electrode 38 comprises a portion extending into opening 35 (FIG. 7 ), and may further include portions overlappingdielectric passivation layer 34 andgate dielectric 36.Gate dielectric layer 36 thus separatesgate electrode 38 fromdielectric passivation layer 34 and crystallineinterfacial layer 32. In some embodiments, the formation ofgate electrode 38 includes depositing a blanket gate electrode layer overgate dielectric layer 36 and fillingopening 35 shown inFIG. 7 , and performing lithography and etching processes on the gate electrode layer to definegate electrode 38. In some embodiments,gate electrode 38 includes a conductive material layer that includes a refractory metal or the respective compounds including, e.g., titanium (Ti), titanium nitride (TiN), titanium tungsten (TiW), Tantalum (Ta), Tantalum nitride (TaN), and tungsten (W). In other examples,gate electrode 38 includes nickel (Ni), gold (Au), copper (Cu), or the alloys thereof. -
FIG. 9 illustrates a cross-sectional view ofwafer 10 after metal features 40 are formed (step 114 inFIG. 10 ). Two openings (occupied by metal features 40) are formed on the opposite sides ofgate electrode 38, for example, by lithography and etching processes performed ongate dielectric layer 36,dielectric passivation layer 34, and crystallineinterfacial layer 32. The portions of III-V compound layer 28 on opposite sides ofgate electrode 38 are thus exposed. In some exemplary formation process of metal features 40, a metal layer (not shown) is deposited over gate dielectric layer 36 (and dielectric passivation layer 34), which metal layer fills the openings indielectric layer 36,dielectric passivation layer 34, and crystallineinterfacial layer 32. The metal layer further contacts III-V compound layer 28 and possibly an underlying layer(s). A photoresist layer (not shown) is formed over the metal layer and then patterned. The patterned photoresist layer is then used as an etching mask to pattern the metal layer down to the underlyinggate dielectric layer 36 ordielectric passivation layer 34. The remaining portions of the metal layer are metal features 40. The photoresist layer is removed after the formation of the metal features 40. Metal features 40 are configured as at least parts of the source and drain regions of the resultingHEMT 42. In the above described embodiments,gate dielectric 36,gate electrode 38, metal features 40, andcarrier channel 30form HEMT 42. When a voltage is applied togate electrode 38, a device current may be modulated. - In some embodiments, metal features 40 include one or more conductive materials. For example, metal features 40 may comprise Ti, Co, Ni, W, Pt, Ta, Pd, Mo, TiN, an AlCu alloy, and alloys thereof. In other examples, each of metal features 40 includes a bottom Ti/TiN layer, an AlCu layer overlying the bottom Ti/TiN layer, and a top Ti layer overlying the AlCu layer. The formation methods of the metal layer include ALD or PVD processes. In some embodiments, a thermal annealing process is applied to metal features 40 such that metal features 40 react with III-
V compound layer 28 and III-V compound layer 26 to forminter-metallic compound 41. Inter-metallic compound 41 (which also forms parts of the source and drain regions of HEMT 42) thus connects to the opposite ends ofchannel 30, and provides for more effective electrical connection tocarrier channel 30. - A band gap discontinuity exists between III-
V compound layer 28 and III-V compound layer 26, creating the verythin layer 30 of highly mobile conducting electrons in III-V compound layer 26. Thisthin layer 30 is referred to as a Two-Dimensional Electron Gas (2DEG), which is schematically illustrated.2DEG 30 forms the carrier channel, which is the channel ofHEMT 42. The carrier channel of 2DEG is located in III-V compound layer 26 and nearinterface 31 between III-V compound layer 28 and III-V compound layer 26. The carrier channel has high electron mobility partly because III-V compound layer 26 is undoped or unintentionally doped, and the electrons can move freely without collision or with substantially reduced collisions with impurities. -
FIGS. 11 through 17 illustrate cross-sectional views of intermediate stages in the formation of HEMTs in accordance with alternative embodiments. Unless specified otherwise, the materials and formation methods of the components in these embodiments are essentially the same as the like components, which are denoted by like reference numerals in the embodiments shown inFIGS. 1 through 9 . The details regarding the formation process and the materials of the components shown inFIGS. 11 through 17 may thus be found in the discussion of the embodiment shown inFIGS. 1 through 9 . -
FIGS. 11 through 13 illustrate cross-sectional views of intermediate stages in the formation of an HEMT using another gate first approach. The initial steps of these embodiments are essentially the same as shown inFIGS. 1 through 5 , and hence the details of the formation processes are not repeated herein. Next, as shown inFIG. 11 ,gate dielectric layer 36 andgate electrode layer 38 are formed.Gate dielectric layer 36 is over, and may be in contact with, crystallineinterfacial layer 32. -
FIG. 12 illustrates the patterning ofgate electrode layer 38,gate dielectric layer 36, and crystallineinterfacial layer 32, whose remaining portions are also referred to asgate electrode 38,gate dielectric 36, and crystallineinterfacial layer 32, respectively.Gate electrode 38,gate dielectric 36, and crystallineinterfacial layer 32 are co-terminus, which means that the respective edges ofgate electrode 38,gate dielectric 36, and crystallineinterfacial layer 32 are aligned with each other. -
FIG. 13 illustrates the formation ofdielectric passivation layer 34 and metal features 40.Dielectric passivation layer 34 comprises a top portion overlappinggate electrode 38, sidewall portions on the edges ofgate electrode 38,gate dielectric 36, and crystallineinterfacial layer 32, and horizontal portions on the top surface of III-V compound layer 28. Metal features 40 penetrate throughdielectric passivation layer 34 to electrically connect to III-V compound layer 28 and2DEG 30, for example, throughinter-metallic compound 41. -
FIGS. 14 through 17 illustrate cross-sectional views of intermediate stages in the formation of an HEMT using a gate last approach. The initial steps of these embodiments are essentially the same as shown inFIGS. 1 through 5 , and hence the details of the formation processes are not repeated herein. Next, as shown inFIG. 14 ,dielectric passivation layer 34 is formed over, and may be in contact with, crystallineinterfacial layer 32. InFIG. 15 , metal features 40 are formed. Metal features 40 penetrate throughdielectric passivation layer 34 and crystallineinterfacial layer 32 to electrically connect to III-V compound layer 28 and2DEG 30, for example, throughinter-metallic compound 41. AlthoughFIG. 15 illustratesinter-metallic compound 41,inter-metallic compound 41 may not be formed at this stage, and may be formed as a result of the subsequent thermal processes. - Next, referring to
FIG. 16 ,dielectric capping layer 37 is formed. In some embodiments,dielectric capping layer 37 comprises an oxide, a nitride, or multi-layers thereof.Dielectric capping layer 37 comprises portions overlapping metal features 40, and portions overdielectric passivation layer 34. Next, a patterning step is performed ondielectric capping layer 37 anddielectric passivation layer 34 andopening 35 is formed as a result of the patterning. The top surface of crystallineinterfacial layer 32 is exposed throughopening 35. - Next, as shown in
FIG. 17 ,gate dielectric layer 36 andgate electrode layer 38 are formed.Gate dielectric layer 36 extends into opening 35 (FIG. 16 ). Furthermore,gate dielectric layer 36 comprises a first portion inopening 35 and in contact with crystallineinterfacial layer 32, second portions on the edges ofdielectric capping layer 37 anddielectric passivation layer 34, and third portions overlappingdielectric capping layer 37,dielectric passivation layer 34, and metal features 40.Gate electrode 38 also extends into opening 35 (FIG. 16 ). In subsequent steps (not shown), Inter-Layer Dielectric (not shown) may be formed to cover the structure inFIG. 17 , and contact plugs (not shown) may be formed to electrically couple togate electrode 38 and meta features 40. The formation ofHEMT 42 is thus finished. -
HEMTs 42 formed in accordance with the embodiments of the present disclosure include crystalline interfacial layer 32 (FIGS. 9 , 13, and 17), and gate dielectric 36 over and contacting crystallineinterfacial layer 32. In conventional HEMT formation processes, although gate dielectrics may be used to separate gate electrodes and the underlying semiconductor materials to reduce leakage currents, the Dit at the interfaces between the gate dielectrics and the respective underlying semiconductors is very high. The high Dit results in a very high threshold voltage (Vt) shift, which may be as high as 4 volts or higher. Therefore, the formation of gate dielectrics was not advantageous. By inserting the crystalline interfacial layer 32 (FIGS. 9 , 13, and 17), which has a good crystalline structure and good bonding between atoms, the semiconductor material (such aslayer 28 inFIGS. 9 , 13, and 17) is in contact with the crystallineinterfacial layer 32 that has the good crystalline structure, and hence the Dit at the interface betweenlayer 28 andlayer 32 is low. As a comparison, if crystallineinterfacial layer 32 is not formed,gate dielectric 36 would have been in contact with theunderlying layer 28, and the respective interface has a much higher Dit, and in turn causes a much higher Vt shift. - In accordance with some embodiments, an HEMT includes a first III-V compound layer having a first band gap, and a second III-V compound layer having a second band gap over the first III-V compound layer. The second band gap is greater than the first band gap. A crystalline interfacial layer is overlying and in contact with the second III-V compound layer. A gate dielectric is over the crystalline interfacial layer. A gate electrode is over the gate dielectric. A source region and a drain region are over the second III-V compound layer, and are on opposite sides of the gate electrode.
- In accordance with other embodiments, an HEMT includes a first III-V compound layer, a second III-V compound layer over the first III-V compound layer, and a crystalline interfacial layer over and in contact with the second III-V compound layer. A dielectric passivation layer is over the crystalline interfacial layer. A gate dielectric includes a portion penetrating through the dielectric passivation layer to contact a top surface of a portion of the crystalline interfacial layer. A gate electrode is over the gate dielectric. A source region and a drain region are over the second III-V compound layer and on opposite sides of the gate electrode.
- In accordance with yet other embodiments, a method of forming an HEMT includes epitaxially growing a first III-V compound layer, epitaxially growing a second III-V compound layer over the first III-V compound layer, and growing a crystalline interfacial layer over and in contact with the second III-V compound layer. The method further includes forming a gate electrode over the III-V compound layer, and forming a source region and a drain region over the second III-V compound layer and on opposite sides of the gate electrode.
- Although the embodiments and their advantages have been described in detail, it should be understood that various changes, substitutions and alterations can be made herein without departing from the spirit and scope of the embodiments as defined by the appended claims. Moreover, the scope of the present application is not intended to be limited to the particular embodiments of the process, machine, manufacture, and composition of matter, means, methods and steps described in the specification. As one of ordinary skill in the art will readily appreciate from the disclosure, processes, machines, manufacture, compositions of matter, means, methods, or steps, presently existing or later to be developed, that perform substantially the same function or achieve substantially the same result as the corresponding embodiments described herein may be utilized according to the disclosure. Accordingly, the appended claims are intended to include within their scope such processes, machines, manufacture, compositions of matter, means, methods, or steps. In addition, each claim constitutes a separate embodiment, and the combination of various claims and embodiments are within the scope of the disclosure.
Claims (20)