US20140004764A1 - Ceramic component - Google Patents
Ceramic component Download PDFInfo
- Publication number
- US20140004764A1 US20140004764A1 US14/018,643 US201314018643A US2014004764A1 US 20140004764 A1 US20140004764 A1 US 20140004764A1 US 201314018643 A US201314018643 A US 201314018643A US 2014004764 A1 US2014004764 A1 US 2014004764A1
- Authority
- US
- United States
- Prior art keywords
- ceramic
- glass
- coating
- fibers
- solid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A ceramic component includes a porous fibrous structure that has fibers that are coated with a protective coating. There is a ceramic coating on the protective coating within pores of the porous fibrous structure. The ceramic coating and porous fibrous structure define a residual interconnected porosity. There is a solid glass or glass/ceramic material is within the residual interconnected porosity.
Description
- This is a divisional application of U.S. patent application Ser. No. 13/251,696, filed on Oct. 3, 2011.
- This disclosure relates to ceramic materials. Ceramic materials are known and used for components such as coatings, ceramic bodies and ceramic matrices. For example, ceramic materials are fabricated using techniques such as polymer impregnation and pyrolysis, melt infiltration, slurry infiltration, slip casting, tape casting, injection molding, dry pressing, isostatic pressing, hot isostatic pressing and others. The selected processing technique controls the chemistry and microstructure of the ceramic material and thus can also limit the chemistry and microstructure.
- Disclosed is a ceramic component that includes a porous fibrous structure that has fibers that are coated with a protective coating. A ceramic coating is located on the protective coating within pores of the porous fibrous structure. The ceramic coating and porous fibrous structure define a residual interconnected porosity. A solid glass or glass/ceramic material is within the residual interconnected porosity.
- In a further non-limiting example, the protective coating is selected from the group consisting of carbon, boron nitride, boron carbide, silicon nitride, silicon carbide, aluminosilicate and combinations thereof, and the ceramic coating is selected from the group consisting of silicon carbide, aluminum nitride, boron nitride, boron phosphide, silicon nitride, beryllium oxide, diamond and combinations thereof.
- A further non-limiting example of any of the forgoing examples includes a final composition, by volume percentage, of: 20-70 of the fibers, up to 5 of the protective coating on the fibers, 5-20 of the coating, and a remainder of the solid glass or glass/ceramic material and residual void volume, wherein the residual void volume is less than 1 volume percent.
- In a further non-limiting example of any of the forgoing examples, the final composition includes: 30-60 of the fibers, 1-2 of the protective coating on the fibers, and 20-40 of the solid glass or glass/ceramic material.
- In a further non-limiting example of any of the forgoing examples, the liquid glass or glass/ceramic material includes a solid ceramic filler.
- In a further non-limiting example of any of the forgoing examples, the solid ceramic filler includes a silicon-containing material.
- In a further non-limiting example of any of the forgoing examples, the porous fibrous structure, ceramic coating and solid glass or glass/ceramic material collectively include less than 1 volume percent of void volume.
- In a further non-limiting example of any of the forgoing examples, the solid glass or glass/ceramic material comprises an element selected from a group consisting of boron, barium, magnesium, lithium, aluminum and combinations thereof.
- In a further non-limiting example of any of the forgoing examples, the solid glass or glass/ceramic material includes a nucleating agent.
- The various features and advantages of the disclosed examples will become apparent to those skilled in the art from the following detailed description. The drawings that accompany the detailed description can be briefly described as follows.
-
FIG. 1 illustrates an example method of fabricating a ceramic component. -
FIG. 2 illustrates various stages through fabrication of a ceramic component. -
FIG. 1 illustrates anexample method 20 of fabricating a ceramic component. As will be appreciated, themethod 20 permits fabrication of ceramic components having unique compositions and/or microstructures that are not heretofore available. Furthermore, themethod 20 can be used to produce compositions and/or microstructures for the enhancement of densification, thermal conductivity or other target property in components such as cooled turbine engine components. - As illustrated in
FIG. 1 , themethod 20 generally includes avapor infiltration step 22, atransfer molding step 24 and asolidification step 26. - As shown, in step 22 a ceramic coating is deposited using vapor infiltration within pores of a porous structure to form a preform body with residual interconnected porosity. As an example, the vapor infiltration includes chemical vapor infiltration (CVI) in which one or more volatile ceramic precursors penetrate into the porous structure and react to deposit the ceramic material within the porous structure. The deposited ceramic material is a result of chemical reaction of the ceramic precursor(s) occurring at the internal surfaces of the porous structure. The infiltration of the precursor(s) is driven by diffusion, an imposed external gas pressure, an imposed vacuum or a combination of these. In one non-limiting example based on silicon carbide, the precursor is methyltrichlorosilane mixed in a hydrogen carrier gas. The methyltrichlorosilane decomposes to silicon carbide. In general, the temperature, time, precursor(s), carrier gas(es), pressure and flow rate(s) are selected to control the composition and amount of the resulting ceramic coating that is deposited.
- The
vapor infiltration step 22 is controlled such that the resulting residual porosity of the preform body is within a predefined range. In one example, the predefined range is 40-80 volume percent of the preform body. If the ceramic coating reduces the residual porosity to less than about 40 volume percent, the interconnectivity of residual porosity is reduced such that the liquid glass material is unable to later substantially fully infiltrate the porosity to form a near fully dense component. - In the
transfer molding step 24, a heated, liquid glass or glass/ceramic material is deposited within the residual porosity of the preform body using transfer molding. The liquid glass or glass/ceramic material is then cooled atstep 26 to increase viscosity and thereby immobilize the glass or glass/ceramic material as a solid to form a ceramic material that includes the solid glass or glass/ceramic material, the ceramic coating and the porous structure. As an example, the preform body is subjected to a ceramic glass-transfer molding process in which the body is located in a suitable molding tool. Molten glass or glass/ceramic of the selected composition is injected into the tool cavity to infiltrate the residual porosity of the preform body. The body is cooled to solidify the glass or glass/ceramic into a solid glass or glass/ceramic material. Optionally, a thermal heat treatment is conducted after solidification to induce selective crystallization of ceramic phase(s) within the glass or glass/ceramic. An example temperature range for the heat treatment is from about 1000° C. to about 1500° C. for times ranging from about 10 minutes to about 4 hours. - As used herein, the term “ceramic” refers to inorganic, non-metallic materials that may be crystalline, partially crystalline or substantially or fully amorphous, and including allotropes of carbon, such as graphite and diamond. Further, the term “glass” as used herein, refers to an amorphous or partially amorphous ceramic material. In one embodiment, the ceramic coating is different from the glass or glass/ceramic material in at least one of composition, microstructure and physical property. In a further embodiment, the ceramic coating is a crystalline ceramic material and the glass or glass/ceramic material is partially or fully amorphous.
- The chemical composition of the ceramic coating, porous structure and glass or glass/ceramic material can be tailored to control the desired properties of the final ceramic component that is formed by
method 20. In one example, themethod 20 is used to enhance thermal conductivity of the composite material. For instance, the ceramic coating that is deposited into the pores of the porous structure has a first thermal conductivity and the glass or glass/ceramic material has a second thermal conductivity that is lower than the first coefficient of thermal conductivity. Thus, the ceramic coating acts as a thermal transfer network in the ceramic component while the glass or glass/ceramic material enhances other properties, such as thermal resistance, dimensional stability and corrosion resistance. - In a further embodiment, the ceramic coating is a non-oxide ceramic material. In a further example, the ceramic coating is selected from silicon carbide, aluminum nitride, boron nitride, boron phosphide, silicon nitride, beryllium oxide, diamond or other solid with high thermal conductivity or combinations thereof.
- In a further embodiment, the porous structure is a porous fibrous structure. For example, the porous fibrous structure is a fabric, weave, tape, braid, two-dimensional, or three-dimensional structure that is coated or uncoated with a protective coating. In one example, the porous fibrous structure includes ceramic fibers and/or carbon fibers. The ceramic fibers include oxide or non-oxide ceramic fibers. In a further example, the ceramic fibers are silicon carbide fibers. In other examples, the fibers are silicon oxycarbide, silicon oxycarbide with refractory metal dopants such as Ti, B, Zr, or Hf and/or glass or glass/ceramic fibers. It is to be understood that the porous structure may alternatively be another kind of porous structure that may or may not include fibers.
- In a further embodiment, the porous fibrous structure includes a protective coating on the fibers. The protective coating includes an oxide layer, a non-oxide layer or both and can be a monolayer coating or a multilayer coating. For instance, the protective coating includes one or more layers of carbon, boron nitride, boron carbide, silicon nitride, silicon carbide and aluminosilicate including combinations of these, including alternating layers of different compositions.
- In a further embodiment, the ceramic glass is a silicate-based glass or glass/ceramic. For example, the silicate-based glass or glass/ceramic includes boron, barium, magnesium, lithium, aluminum or combinations thereof. In a further example, the silicate-based glass or glass/ceramic additionally includes a nucleating agent that serves to precipitate crystalline phases from the amorphous phase with the application of thermal treatment. In one non-limiting example, the nucleating agent includes zirconium.
- In a further embodiment, the selected glass or glass/ceramic material additionally includes a solid filler to modify the properties of the ceramic component. In one example, the solid filler is a solid ceramic filler, such as silicon carbide. In other examples, the solid filler is a silicon-containing filler, such as oxides, nitrides, borides, carbides and combinations thereof that include silicon.
- In a further embodiment, the chemical compositions of the ceramic coating, porous structure and glass or glass/ceramic material are selected to enhance the
transfer molding step 24. For example, the compositions of the ceramic coating and the glass or glass/ceramic material disclosed herein are compatible such that the glass or glass/ceramic material in the liquid state wets the ceramic coating to aid in substantially fully filling the residual interconnected porosity during thetransfer molding step 24. The compatibility between the ceramic coating and the glass or glass/ceramic material reduces the molding pressure needed in thetransfer molding step 24 and thus enhances filling of the pores and process efficiency and repeatability. Furthermore, the composition, temperature and/or pressure can be adjusted to change the viscosity of the glass or glass/ceramic material to enhance the filling of the pores. In one example, the residual porosity in the preform body is 40-80 volume percent and the liquid ceramic glass material is molded at a viscosity of about 5-15 Pa·s and a molding pressure of about 0.5-1.5 ksi (3.4-10.3 megapascals) to produce a residual void volume of less than one volume percent in the final ceramic component. In a further example of the compatibility, the chemical composition of the ceramic coating includes, as a constituent element, at least one element in common with the chemical composition of the glass or glass/ceramic material. -
FIG. 2 illustrates three different stages (A), (B) and (C) in a fabrication of a finalceramic component 40 according to themethod 20. It is to be understood that themethod 20 is not limited to fabrication of the exemplaryceramic component 40. As shown in initial stage (A), a porousfibrous structure 42 includes a plurality offibers 44 that defineopen pores 46 there between. In this example, each of thefibers 44 includes aprotective coating 44 a of composition described herein disposed on the outer surfaces of thefibers 44. - The
fibers 44 in this example are transversely oriented to each other such that there is a first layer of parallel fibers and an adjacent second layer of parallel fibers that are orientated at approximately 90 degrees to the fibers of the first layer. Given this description, one of ordinary skill in the art will recognize other fiber orientations and arrangements to meet their particular needs. - Referring to stage (B), a
ceramic coating 48 is deposited into thepores 46 of the porousfibrous structure 42 to form apreform body 50 with residualinterconnected porosity 52. - At stage (C), the liquid glass or glass/ceramic material is transfer-molded into the residual
interconnected porosity 52 of thepreform body 50. Upon solidification, solid glass or glass/ceramic material 54 substantially fills the residualinterconnected porosity 52. Theceramic component 40 is thus formed of the solid glass or glass/ceramic material 54, theceramic coating 48 and the porousfibrous structure 42. - In the illustrated example, the
ceramic component 40 fabricated according tomethod 20 includes a final composition, by volume percentage, of: - 20-70 of the
fibers 44, - up to 5 of the
protective coating 44 a on thefibers 44, - 5-20 of the
ceramic coating 48, and - a remainder of the solid glass or glass/
ceramic material 54 and residual void volume, wherein the residual void volume is less than 1 volume percent. It is to be understood that the volume percentages of the constituents in the final composition must total 100%. - In a further example, the final composition from above includes:
- 30-60 of the
fibers 44, - 1-2 of the
protective coating 44 a on thefibers 44, and - 20-40 of the solid glass or glass/
ceramic material 54. - Although a combination of features is shown in the illustrated examples, not all of them need to be combined to realize the benefits of various embodiments of this disclosure. In other words, a system designed according to an embodiment of this disclosure will not necessarily include all of the features shown in any one of the Figures or all of the portions schematically shown in the Figures. Moreover, selected features of one example embodiment may be combined with selected features of other example embodiments.
- The preceding description is exemplary rather than limiting in nature. Variations and modifications to the disclosed examples may become apparent to those skilled in the art that do not necessarily depart from the essence of this disclosure. The scope of legal protection given to this disclosure can only be determined by studying the following claims.
Claims (9)
1. A ceramic component comprising:
a porous fibrous structure including fibers that are coated with a protective coating;
a ceramic coating on the protective coating within pores of the porous fibrous structure, the ceramic coating and porous fibrous structure defining a residual interconnected porosity; and
a solid glass or glass/ceramic material within the residual interconnected porosity.
2. The ceramic component as recited in claim 1 , wherein the protective coating is selected from the group consisting of carbon, boron nitride, boron carbide, silicon nitride, silicon carbide, aluminosilicate and combinations thereof, and the ceramic coating is selected from the group consisting of silicon carbide, aluminum nitride, boron nitride, boron phosphide, silicon nitride, beryllium oxide, diamond and combinations thereof.
3. The ceramic component as recited in claim 1 , including a final composition, by volume percentage, of:
20-70 of the fibers,
up to 5 of the protective coating on the fibers,
5-20 of the coating, and
a remainder of the solid glass or glass/ceramic material and residual void volume, wherein the residual void volume is less than 1 volume percent.
4. The ceramic component as recited in claim 3 , wherein the final composition includes:
30-60 of the fibers,
1-2 of the protective coating on the fibers, and
20-40 of the solid glass or glass/ceramic material.
5. The ceramic component as recited in claim 1 , wherein the liquid glass or glass/ceramic material includes a solid ceramic filler.
6. The method as recited in claim 5 , wherein the solid ceramic filler includes a silicon-containing material.
7. The ceramic component as recited in claim 1 , wherein the porous fibrous structure, ceramic coating and solid glass or glass/ceramic material collectively include less than 1 volume percent of void volume.
8. The ceramic component as recited in claim 1 , wherein the solid glass or glass/ceramic material comprises an element selected from a group consisting of boron, barium, magnesium, lithium, aluminum and combinations thereof.
9. The ceramic component as recited in claim 7 , wherein the solid glass or glass/ceramic material includes a nucleating agent.