US20130273268A1

US20130273268A1 - Artificial grass

Info

Publication number: US20130273268A1
Application number: US13/825,738
Authority: US
Inventors: Romain Luijkx
Original assignee: Total Research and Technology Feluy SA
Current assignee: TotalEnergies One Tech Belgium SA
Priority date: 2010-09-23
Filing date: 2011-09-21
Publication date: 2013-10-17
Also published as: PT2619357T; PL2619357T3; CN103221588A; CA2811159A1; CA2811159C; KR20130051998A; WO2012038471A1; EP2619357B1; CN103221588B; ES2757926T3; KR101401370B1; EP2619357A1

Abstract

Artificial grass tufted from slit film or monofilaments prepared with a polyethylene prepared with a bistetrahydroindenyl or bisindenyl metallocene catalyst complex having (a) a density in the range of 0.910 to 0.937 g/cm³as determined by ISO 1183 at a temperature of 23° C. and (b) a melt index MI2 in the range of 0.5 to 5 g/10 min as determined by ISO 1133/D at a temperature of 190° C. and at a load of 2.16 kg, wherein said polyethylene has a g_{rheo of}less than 0.9 or an LCBI of greater than 0.08, and the polyethylene has a Vicat Softening Temperature T_vaccording to the following equation:

T_v>41234 d²+77500 d−36295

wherein T_vis the Vicat Softening Temperature in ° C. and d is the density of the polyethylene in g/cm³.

Description

FIELD OF THE INVENTION

The present invention relates to polymers and in particular to linear low density polyethylenes (LLDPE) and medium density polyethylenes (MDPE) and to yarn made thereof, in particular to slit film and monofilaments suitable for tufting into artificial grass or also known as artificial turf.

BACKGROUND OF THE INVENTION

Historically, first polypropylene, then HDPE, were used for making monofilaments and slit film in the field of artificial grass. However, more recently, LLDPE and MDPE have become the material of choice due to their superior softness. Conventionally, Ziegler-Natta copolymers of ethylene and 1-octene are used.
In recent years there have been many advances in the production of polyolefins due to the introduction of metallocene catalysts. Because of their single-site nature the polyolefin copolymers produced by metallocene catalysts often are quite uniform in their molecular structure. For example, in comparison to traditional Ziegler-Matta catalysed polyethylenes, they have relatively narrow molecular weight distributions (MWD) and narrow Short Chain Branching Distribution (SCBD).
Certain properties of metallocene catalysed polyethylenes are enhanced by narrow MWD and these materials may be manufactured into useful articles. However for some applications the uniform nature of the SCBD of metallocene produced materials may not readily permit certain structures to be obtained.
Monofilaments have a variety of geometries e.g. circular, flat, elliptical, double diamond shape etc., which may define the final properties such as softness, abrasion and the like. For example when used for artificial grass applications producers optimize this shape in order to provide the required balance of properties. The best are those that do not show area with a very small radius (weakness points creating splitting) and that do not have sharp edges e.g. double diamond, C-shaped, and elliptical.
Generally monofilaments may be manufactured by a melt spinning process with their sizes ranging from 0.1 to 2.5 mm in diameter depending on the intended end use. Polyethylenes have been typically used as raw materials for making monofilaments.
Slit films are prepared from a primary film produced by a blown or a cast film process. The film may be cut into tapes and then oriented typically by stretching the film while passing through an air oven or on a hot plate at a temperature below the melting point.
Synthetic or artificial turf or grass has been used to replace natural grass on playing surfaces, in particular on sports fields e.g. football field. Polymer compositions useful for this application need to exhibit the necessary durability, resistance to fibrillation, resilience, UV and thermal stability and as well as a softness to prevent injury.
WO 07/107307 describes synthetic turf for grass field comprising individual filament yarns consisting essentially of a mixture of a high density polyethylene (HDPE) and a linear low density polyethylene (LLDPE).
JP 2007016367 describes threads for artificial grass mainly comprising 70-95 wt % of a high density polyethylene and 5-30 wt % of an ethylene-alpha-olefin copolymer having a density in the range 0.900-0.925 g/cm³obtained with a metallocene catalyst.
U.S. Pat. No. 4,880,691 describes fibres and multifilaments derived from linear low density copolymers (LLDPE) of ethylene and alpha-olefins having 3-12 carbon atoms produced from Ziegler based catalysts. The copolymers typically have density in the range 0.86 to 0.95 g/cm³and melt index in the range 0.01 to 400 g/10 min.
WO 08/1 13566 and WO 08/1 13567 describe fibres, tapes or filaments comprising polyethylene compositions obtainable by use of single site catalysts wherein the polyethylene compositions have a density of less than 980 kg/m3 and preferably less than 975 kg/m3. The polyethylene compositions are unimodal and preferably exhibit a melt index (2.16 kg) in the range 0.7-4.0 g and a Mw/Mn in the range 2-4 and are suitably prepared by use of bis(cyclopentadienyl) metallocene catalyst systems.
WO2009/101124 describes fibres, tapes and monofilaments based on ethylene copolymers with alpha-olefins, prepared in particular with monocyclopentadienyl catalyst systems, suitable for end-use applications including artificial grass. It does not however disclose any presence of long chain branching within the polyethylene. Not every single-site catalyst induces long chain branching. This can be seen in FIG. 6, wherein a bis(n-butylcyclopentadienyl)zirconium dichloride catalyst does not provide any evidence of long chain branching. It behaves rheologically in the same manner as the Ziegler-Matta catalysed polyethylene, indicating that the polyethylene is linear.
EP 1 469 104 discloses monofilaments or stretched tapes, unwoven or woven into raffia, prepared with a polyethylene catalysed with either a bisindenyl, bistetrahydroindenyl or a biscyclopentadienyl metallocene, substituted or unsubstituted. Artificial grass is not disclosed as a possible application. There is no indication regarding the durability and relative softness of the polyethylene and in particular nothing is indicated regarding friction resulting with objects such as balls.
WO2009/059971 discloses polyethylene resins prepared in a double loop reactor wherein the catalyst system comprises bis-tetrahydroindenyl and bis-indenyl catalyst components deposited on the same support. The polyethylene is only disclosed as being used for blown films. Artificial grass is not disclosed as a possible application.
The aforementioned metallocene derived copolymers are particularly suitable for the production of films and sheets prepared using traditional methods well known in the art.
Examples of such methods are film blowing, film casting and orientation of the partially crystallised product. The films exhibit good processability, improved optical and mechanical properties and good heat sealing properties. However, for applications such as monofilaments and slit film to make artificial turf, suitable polymers require specific molecular structures in order to provide good strain-hardening and the required balances of melt strength and drawability, but also required are higher thermal stability and better ball roll, whilst maintaining or even improving durability.
An object of the invention is to provide a polyethylene that fulfills all of these requirements suitable to make artificial grass (also known as artificial turf). In particular, these requirements include longer durability, higher thermal stability (higher Vicat softening temperatures) and better ball roll.

SUMMARY OF THE INVENTION

We have now found that certain polyethylenes in particular those catalysed using bis-tetrahydroindenyl metallocenes polyethylenes exhibit outstanding properties in the solid state when submitted to high deformation or to mechanical stress. The polyethylenes thus obtained are particularly suitable for highly thermal or mechanical demanding applications like the preparation of slit film, monofilaments and the like for end-use applications in artificial grass and synthetic sport surfaces, woven and nonwoven fabrics etc.
The resultant slit film and monofilaments and the like exhibit improved tensile properties expressed as the balance between tenacity and elongation at break. In particular it has been found that the melt index of the polymers may be increased to the benefit of the product processability while maintaining the balance between thermal resistance and mechanical strength. In particular, the polyethylene according to the invention has a high Vicat Softening Temperature i.e. better thermal durability.
Thus according to a first aspect of the present invention there is provided a slit film or monofilament suitable for tufting into artificial grass prepared with a polyethylene prepared with a bistetrahydroindenyl or bisindenyl metallocene catalyst complex having (a) a density in the range of 0.910 to 0.940 g/cm³, preferably 0.910 to 0.937 g/cm³, as determined by ISO 1183 at a temperature of 23° C. and (b) a melt index M12 in the range of 0.5 to 5 g/10 min as determined by ISO 1133/D at a temperature of 190° C. and at a load of 2.16 kg, characterized in that said polyethylene has a g_rheoof less than 0.9 or an LCBI of greater than 0.08. Preferably, the density of the polyethylene is in the range of 0.915 to 0.937 g/cm³. In addition, preferably the polyethylene has a Vicat Softening Temperature T_vmeasured according to ISO 306 conditions A120 (10N and 120° C.) according to the following equation:
T_v>41234 d²+77500 d−36295
wherein T_vis the Vicat Softening Temperature in ° C. and d is the density of the polyethylene in g/cm³.
Thus according to another aspect of the present invention there is provided an artificial grass tufted from a slit film or monofilament of a polyethylene prepared with a bistetrahydroindenyl (bis-THI) or bisindenyl (bis-IND) metallocene catalyst complex wherein the polyethylene has (a) a density in the range of 0.910 to 0.940 g/cm³as determined by ISO 1183 at a temperature of 23° C., preferably of 0.910 to 0.937 g/cm³, and (b) a melt index M12 in the range of 0.5 to 5 g/10 min as determined by ISO 1133/D at a temperature of 190° C. and at a load of 2.16 kg, characterized in that said polyethylene has a g_rheoof less than 0.9 or an LCBI of greater than 0.08. Preferably, the density of the polyethylene is in the range of 0.915 to 0.937 g/cm³. In addition, preferably the polyethylene has a Vicat Softening Temperature T_vmeasured according to ISO 306 conditions Al20 (10N and 120° C.) according to the following equation:
T_v>41234 d²+77500 d−36295
wherein T_vis the Vicat Softening Temperature in ° C. and d is the density of the polyethylene in g/cm³.

BRIEF DESCRIPTION OF THE FIGURES

FIG. 1 is a graph showing the horizontal activation energy vs shear rate of a resin according to the invention (PE1) and of the market reference's resin (MR).

FIG. 2 is a graph showing the Rheological dynamic analysis (RDA) i.e. complex viscosity vs frequency of a resin according to the invention (PE1) and of the market reference's resin (MR).

FIG. 3 shows a Reimotec® Artificial Turf Monofilament machine schematic.

FIG. 4 shows the C-shape yarn type and its dimensions.

FIG. 5 shows a graph representing strength in N versus elongation in %

FIG. 6 shows a graph of Rheological horizontal activation energy E*h versus reduced frequency w/w_cof various resins prepared with different catalysts (THI=ethylene bis(tetrahydroindenyl)zirconium dichloride, ZN=Ziegler Natta, nBuCp=bis(n-butylcyclopentadienyl)zirconium dichloride, LDPE=high pressure prepared low density polyethylene)catalyst) showing how other catalysts e.g. ZN and other single-site metallocenes do not provide long chain branching.

FIG. 7 shows a graph of Vicat Softening Temperature Tv versus density. The squares represent resins of the prior art. The diamonds represent resins of the present invention.

DETAILED DESCRIPTION OF THE INVENTION

Preferably the polyethylene of the present invention has a unimodal molecular weight distribution, wherein only one peak is observed.
The polyethylene according to all aspects of the present invention preferably has an MWD that is represented by Mw/Mn of typically from 2 to 8, more typically of 3 to 8. The molecular weights are determined by Size Exclusion Chromatography (SEC) at high temperature (145° C.). A 10 mg polyethylene sample is dissolved at 160° C. in 10 ml of trichlorobenzene (technical grade) for 1 hour. Analytical conditions for the GPCV 2000 from WATERS are:

- Injection volume: +/−400 μl
- Automatic sample preparation and injector temperature: 160° C.
- Column temperature: 145° C.
- Detector temperature: 160° C.
- Column set: 2 Shodex AT-806MS and 1 Styragel HT6E
- Flow rate: 1 ml/min
- Detector: Infrared detector (2800-3000 cm⁻¹)
- Calibration: Narrow standards of polystyrene (PS) (commercially available)
- Calculation of molecular weight M_iof each fraction i of eluted polyethylene PE is based on the Mark-Houwink relation:

log10(M_PE)=0.965909 log10(M_PS)−0.28264;

- (cut off on the low molecular weight end at M_PE=1000)

The most common molecular weight averages used in establishing molecular weight/property relationships are the number average (Mn), weight average (Mw), and z average (Mz) molecular weights. These averages are defined by the following expressions and are determined from the calculated M_i:
$M_{n} = \frac{\sum_{i} N_{i} M_{i}}{\sum_{i} N_{i}} = \frac{\sum_{i} W_{i}}{\sum_{i} W_{i} / M_{i}} = \frac{\sum_{i} h_{i}}{\sum_{i} h_{i} / M_{i}}$ $M_{w} = \frac{\sum_{i} N_{i} M_{i}^{2}}{\sum_{i} N_{i} M_{i}} = \frac{\sum_{i} W_{i} M_{i}}{\sum_{i} M_{i}} = \frac{\sum_{i} h_{i} M_{i}}{\sum_{i} M_{i}}$ $M_{z} = \frac{\sum_{i} N_{i} M_{i}^{3}}{\sum_{i} N_{i} M_{i}^{2}} = \frac{\sum_{i} W_{i} M_{i}^{2}}{\sum_{i} W_{i} M_{i}} = \frac{\sum_{i} h_{i} M_{i}^{2}}{\sum_{i} h_{i} M_{i}}$
Here N_iand W_iare the number and weight, respectively, of molecules having molecular weight M_i. The third representation in each case (farthest right) defines how one obtains these averages from SEC chromatograms. h_iis the height (from baseline) of the SEC curve at the i_thelution fraction and M_iis the molecular weight of species eluting at this increment.
Preferably, the polyethylene of the present invention has a g_rheo, indicative of long chain branching, of less than 0.85. g_rheois equal to one for linear PE and decreases with increasing amount of LCB. It is observed that significant improvement prediction as function of molecular weight can be obtained by including effects of short chain branching (SCB) and molecular weight distribution (MWD). Therefore Mz, Mn and density corrections are included.
g_rheois therefore determined according to the disclosure in WO 2008/113680:
$g_{rheo} (PE) = \frac{M_{w} (SEC)}{M_{w} (η_{0}, MWD, SCB)}$
wherein M_w(SEC) is the weight average molecular weight obtained from size exclusion chromatography expressed in kDa, as described above,
and wherein M_w(η₀, MWD, SCB) is determined according to the following:
M _w(η₀ , MWD, SCB)=exp(1.7789+0.199769 LnM_n+0.209026(Lnη ₀)+0.955(1nρ)−0.007561(LnM _z)(Lnη ₀)+0.02355(1nM _z)²)
Number- and z-average molecular weights, Mn and Mz expressed in kDa, are obtained from size exclusion chromatography as described above.
Density ρ is measured in g/cm³and measured according to ISO 1183 at a temperature of 23° C.
Zero shear viscosity η₀in Pa.s is obtained from a frequency sweep experiment combined with a creep experiment, in order to extend the frequency range to values down to 10⁻⁴s⁻¹or lower, and taking the usual assumption of equivalence of angular frequency (rad/s) and shear rate. Zero shear viscosity η_ois estimated by fitting with Carreau-Yasuda flow curve (η-W) at a temperature of 190° C., obtained by oscillatory shear rheology on ARES equipment (manufactured by TA Instruments) in the linear viscoelasticity domain. Circular frequency (W in rad/s) varies from 0.05-0.1 rad/s to 250-500 rad/s, typically 0.1 to 250 rad/s, and the shear strain is typically 10%. In practice, the creep experiment is carried out at a temperature of 190° C. under nitrogen atmosphere with a stress level such that after 1200 s the total strain is less than 20%. The apparatus used is an ARG2 manufactured by TA instruments.
The intrinsic viscosity inferred from rheology can thus be expressed using the Carreau-Yasuda equation:
η=η₀/(1+(W*τ)^b)^((1−n)/b)
wherein parameters τ, b and n are fitting parameters called respectively ‘relaxation time’, ‘breadth parameter’ and ‘power-law parameter’, which are obtained using non-linear regression with standard software such as SigmaPlot® version 10 or the Excel® Solver function. From this η₀in Pa.s can thus be obtained and used in the equation for Mw (η₀, MWD, SCB) provided above.

Alternative from the literature: LCBI

The long chain branching can also be represented by LCBI, although it does not take into account the effects of molecular weight distribution and also short chain branching (comonomer content). A g_rheoof less than 0.9 is the same as an LCBI of greater than 0.08. A preferred g_rheoof less than 0.85 is the same as an LCBI of greater than 0.13.
LCBI can be determined as introduced by Shroff and Mavridis (R. N. Shroff and H. Mavridis, Macromolecules, 32, 8454 (1999)). It is defined as the ratio of intrinsic viscosities of PE resins estimated by rheology to that determined via solution techniques.
$LCBI = \frac{{[η]}_{rheo}}{{[η]}_{sol}} - 1$
wherein [η]_rheoand [η]_solare the intrinsic viscosities obtained respectively from rheology or via solution.
Thus, LCBI is zero for linear samples and is above zero for polyethylene containing long chain branching. Instead of determining intrinsic viscosity from the relative viscosity at 0.2 dg/min as explained in the publication of Shroff and Mavridis, intrinsic viscosity value is calculated here via solution (expressed in dl/g) in terms of weight average molecular weight M_w(expressed in Da) obtained by size exclusion chromatography (SEC) (obtained as described above) with equation:
[η]_sol=5.25*10⁻⁴(M _w)^0.76
For the intrinsic viscosity obtained from rheology:
Zero shear viscosity η₀, expressed in Pa.s, is also related to the weight average molecular weight M_w,expressed in Da, by equation
η₀=4.4927*10⁻¹⁶(M _w)^3.8412
This equation was derived with 50 linear PE samples, both metallocene and Ziegler-Natta catalysed polyethylene, with M_wranging from 30 to 700 kDa, MWD values from 2 to 25 and density from 0.87 to 0.965 g/cm³. When this equation is solved for M_was a function of η₀, the definition for M_wcan be used in the Shroff and Mavridis equation above to obtain the intrinsic viscosity obtained from rheology:
[η]_rheo=0.572*(η₀)^0.1979
Note that the Zero shear viscosity η₀is estimated by fitting with a Carreau-Yasuda flow curve (η-W) exactly as described above for g_rheo.
The LCBI is thus determined as:
$LCBI = \frac{0.572 * {(η_{0})}^{0.1979}}{5.25 * 10^{- 4} {(M_{w})}^{0.76}} - 1$
wherein η₀is the zero shear viscosity in Pa.s, obtained as described above and M_wis the weight average molecular weight in Da, obtained as described above.
LCBI and g_rheoare also linked mathematically (for g_rheofrom 0.7 to 1):
LCBI=exp(−0.76 ln (g_rheo))−1
The polyethylene of the present invention preferably has a density from 0.910 to 0.937 g/cm³, more preferably 0.915 to 0.937 g/cm³, more preferably from 0.915 to 0.935 g/cm³, even more preferably from 0.918 to 0.935 g/cm³, even more preferably from 0.920 to 0.935 g/cm³, most preferably between 0.923 to 0.934 g/cm³.
Preferably, the polyethylene of the present invention has a MI2 of from 0.7 to 4 g/10 min, more preferably from 0.8 to 3.5 g/10 min, most preferably from 0.9 to 3.4 g/10 min.
The polyethylene according to the invention has particular rheological properties due to its long chain branching. Preferably, the polyethylene has a rheological horizontal activation energy of more than 40 kJ/mol at a frequency of 1 s⁻¹and a rheological horizontal activation energy of less than 40 kJ/mol at a frequency of 100 s⁻¹. More preferably, the polyethylene has a rheological horizontal activation energy of more than 45 kJ/mol at a frequency of 1 s⁻¹and a rheological horizontal activation energy of less than 40 kJ/mol at a frequency of 100 s⁻¹. This can be seen in FIG. 1. Rheological horizontal activation energy is measured on a Rheometrics® ARES rheometer at 170, 190 and 210° C. by inducing shear deformation within the linear viscoelastic regime (at 10% deformation) and recording complex viscosity at different shear rates.
Preferably, the polyethylene of the invention is an ethylene alpha-olefin copolymer, wherein the alpha-olefin has from 4 to 12 carbon atoms. Most preferred alpha-olefins are 1-butene, 1-hexene, 4-methyl-1-pentene and 1-octene, most preferably 1-hexene. Preferably, the polyethylene has a comonomer content, preferably 1-hexene, of less than 30 wt %, more preferably of less than 20 wt %, even more preferably of less than 15 wt %, and most preferably of less than 10 wt %.
The metallocene is selected from at least one of the following formula bis-IND (I) or bis-THI (II):
wherein each R is the same or different and is selected from hydrogen or XR′_vin which X is chosen from carbon, silicon, germanium, oxygen or nitrogen, and each R′ is the same or different and is chosen from hydrogen or a hydrocarbyl of from 1 to 20 carbon atoms and v+1 is the valence of X, R being preferably selected from hydrogen, methyl, ethyl, n-propyl, isopropyl, n-butyl and tert-butyl; R″ is a structural bridge between the two indenyl or tetrahydroindenyls to impart stereo rigidity that comprises a C₁-C₄alkylene radical, a dialkyl germanium, silicon or siloxane, or an alkyl phosphine or amine radical; Q is a hydrocarbyl radical having from 1 to 20 carbon atoms or a halogen, preferably chlorine or fluorine; and M is a transition metal Group 4 of the Periodic Table or vanadium.
Most preferred complexes are those wherein M is zirconium, titanium or hafnium, preferably zirconium.
Each indenyl or tetrahydroindenyl component may be substituted with R in the same way or differently from one another at one or more positions on the cyclopentadienyl ring or on the cyclohexenyl ring. Each substituent is independently chosen.
If the cyclopentadienyl ring is substituted, its substituent groups must not be so bulky as to affect coordination of the olefin monomer to the metal M. Any substituents XR′v on the cyclopentadienyl ring are preferably methyl. More preferably, at least one and most preferably both cyclopentadienyl rings are unsubstituted.
In a particularly preferred embodiment, the metallocene comprises a bridged unsubstituted bis-indenyl or bis-tetrahydroindenyl i.e. all R are hydrogens. More preferably, the metallocene comprises a bridged unsubstituted bis-tetrahydroindenyl.
Most preferably, the metallocene is ethylene-bis(tetrahydroindenyl)zirconium dichloride or ethylene-bis(tetrahydroindenyl) zirconium difluoride.
Suitable activating agents for use in the preparation of the polyethylene of the present invention are those having an ionising action typically used with the aforementioned metallocene complexes. These include aluminoxanes such as methyl aluminoxane (MAO) and fluorinated MAO, boranes such as tris(pentafluorophenyl) borane and borates. Other suitable activating agents are well known in the art include aluminium alkyls, in particular one or more of TIBAL, TEAL or TNOAL.
Aluminoxanes are well known in the art and preferably comprise oligomeric linear and/or cyclic alkyl aluminoxanes. Aluminoxanes may be prepared in a number of ways and preferably are prepare by contacting water and a trialkylaluminium compound, for example trimethylalurninium, in a suitable organic medium such as benzene or an aliphatic hydrocarbon.
The catalysts used to prepare the copolymers of the present invention may suitably be supported.
Suitable support materials include inorganic metal oxides or alternatively polymeric supports may be used for example polyethylene, polypropylene, clays, zeolites, etc.
The most preferred support material for use with the supported catalysts of the present invention is silica. Preferably the support is silica, a modified silica alumina or a modified silica, for example MAO-modified silica or a fluorinated silica support.
Polymerisable monomers suitable for use in this aspect of the present invention include ethylene, propylene, 1-butene, 1-hexene, 1-octene, 1-decene, styrene, butadiene, and polar monomers for example vinyl acetate, methyl methacrylate, etc. Preferred monomers are those having 2 to 10 carbon atoms in particular ethylene, propylene, 1-butene or 1-hexene. Most preferably, the invention covers ethylene polymerisation with 1-hexene as the comonomer.
The polymerisation of the polyethylene can be carried out in the slurry phase. Slurry polymerisation is preferably used to prepare the high density polyethylene. The polymerisation temperature ranges from 20 to 125° C., preferably from 55 to 105° C., more preferably from 60 to 100° C. and most preferably from 65 to 98° C. and the pressure ranges from 0.1 to 10 MPa, preferably from 1 to 6 MPa, more preferably from 2 to 4.5 MPa, for a time ranging from 10 minutes to 6 hours, preferably from 1 to 3 hours, most preferably from 1 to 2.5 hours. Preferably, the polymerisation is carried out in a liquid full loop reactor or even two liquid full loop reactors connected in series.
The polyethylene for the slit film and monofilaments for the artificial grass of the present invention may additionally contain usual additives well known to those skilled in the art such as antioxidants, stabilizers, processing aids, fillers, flame retardants, coloured pigments or similar. These additives may be present in quantities generally between 0.01 and 15 weight % based on the weight of the polyethylene.
The present invention is particularly directed to the yarn (slit film and monofilaments) suitable for use in artificial turfs or grasses including synthetic sporting surfaces.
The slit film or monofilament or similar according to all aspects of the present invention may typically be in stretched form.
The slit film or monofilament or similar according to all aspects of the present invention may have a draw ratio in the range 1: 3 to 1:8, preferably 1:3 to 1:6, more preferably 1:3 to 1:4.
According to another aspect of the present invention the artificial grass tufted with the monofilaments or slit film according to the invention, have similar processing behaviour to Ziegler-Natta copolymers of ethylene and 1-octene, which are conventionally used. In addition the ball roll is almost similar to natural grass, with a much softer feel and a higher durability.
The yarn (monofilaments and slit films) obtainable from the polyethylene prepared using metallocene catalyst system according to the invention, exhibit similar compromise between tenacity and elongation at break as those prepared from traditional Ziegler Natta catalysts and 1-octene comonomer, but at lower density, thereby enabling the final yarn to be softer and therefore advantageous for artificial grass applications.
Alternatively the melt index of the copolymers produced with the bis-THI or bis-IND metallocenes can be increased to the benefit of the product processability while maintaining a similar balance between tenacity and elongation at break.

EXAMPLES

Ethylene with 1-hexene as comonomer (at 3 wt %) were polymerized according to the invention using ethylene-bis(tetrahydroindenyl)zirconium dichloride as the metallocene catalyst in a slurry polymerisation process in a liquid full loop reactor to provide a polyethylene PE1 having the following properties:

- a density of 0.934 g/cm³as measured according to ISO 1183 at 23° C.
- an M12 of 3.1 as measured according to ISO 1133/D at 190° C. under a load of 2.16 kg
- an Mn of 24 kDa, Mw of 62 kDa and an Mz of 112 kDa
- g_rheoof 0.81 (which is the same as an LCB1 of 0.17)
- At a shear rate of 1 s⁻¹, the horizontal activation energy is at 46.6 kJ/mol (See FIG. 1)
- At a shear rate of 100 s⁻¹, the horizontal activation energy is at 36.1 kJ/mol (See FIG. 1)
- Vicat Softening Temperature 121.3° C. measured according to ISO 306 with conditions A120 (10N, 120° C./h)
- Vicat Softening Temperature of 121.3° C. measured according to ISO 306 with conditions A120 (10N, 120° C./h)
- The formula T_v>41234 d²+77500 d−36295 wherein T_vis the Vicat Softening Temperature (in ° C.) and d is the density (in g/cm³) is thus fulfilled
- Antioxidants package: Irgafos 168, Irganox 1010
- Antiacid: NONE REQUIRED

This polyethylene PE1 was tested against a Ziegler-Natta catalysed LLDPE- 1-octene (4.9 wt %) copolymer MR, the Market Reference, having the following properties

- a density of 0.935 g/cm³
- an M12 of 2.5 g/10 min
- an Mn of 23 kDa, Mw of 80 kDa and an Mz of 228 kDa
- g_rheoof 0.96 (which is the same as an LCBI of 0.03)
- At a shear rate of 1 s⁻¹, the horizontal activation energy is at 31.7 kJ/mol (See FIG. 1)
- At a shear rate of 100 s⁻¹, the horizontal activation energy is at 29.1 kJ/mol (See FIG. 1)
- Vicat Softening Temperature of 117.1° C. measured according to ISO 306 with conditions A120 (10N, 120° C./h)
- The formula T_v>41234 d²+77500 d−36295 wherein T_vis the Vicat Softening Temperature (in ° C.) and d is the density (in g/cm³) is NOT fulfilled
- Antioxidants package: Irgafos 168, Irganox 1010, Irganox 1076,
- Antiacid: Calcium stearate

The g_rheoand shear rate responses are indicative of sparse long chain branching, preferably distributed over the highest molecular weight chains.
FIG. 7 shows a graph of Vicat Softening Temperature Tv versus density. The squares represent resins of the prior art. The diamonds represent resins of the present invention. It can be seen the resins of the present invention have a higher Vicat Softening Temperature Tv at the same density of resins of the prior art.
The following line setup was used to prepare the monofilaments of PE1 and comparative MR on a Reimotec Artificial Turf Monofilament machine (see FIG. 3):

- 30 strands emerging from 1 die
- Yarn type: C shape (See FIG. 4)
- Output 50 kg/h fixed by gear pump
- Versatile 60 mm screw with enhanced feeding zone
- Line speed 155 m/min
- Water cooling bath
- 3 stretching ovens: first 2 were using hot water, last one was left open
- Total draw ratio between 3 and 4
- Titre 1900 dtex
- 2 yarns per bobbin
- Colour & anti-UV masterbatch 491 from BASF (6% added)
- PPA from Schulman (AMF 705-1% added)

It was observed that the extruder back pressure dropped by 15% from 65 to 55 bar from the MR comparative to the PE1 polyethylene. Thus processability of the polyethylene according to the invention is easier than the comparative resin. This allows for longer production runs and lower maintenance frequency of the machines. Or in the alternative, the extrusion temperature can be reduced, thereby saving energy.
Without being bound by theory, the ease of processing is probably attributable to the shear thinning induced by the long chain branching. This is also demonstrated in the Rheological dynamic analysis (RDA). Despite the narrower MWD of PE1, it still has a lower complex viscosity behavior due to the presence of long chain branching.
Both samples appear to have similar shrinkage (˜9% in hot water and ˜2% in hot air), however, PE1 yarn has slightly higher tenacity and elongation at break (FIG. 5 which shows strength in N versus elongation in %)
The monofilaments thus obtained were twisted (6 monofilaments wrapped around each other), then tufted into artificial grass using 15 kg/m2 of granulated SBR 0.5-2 mm (from Monkton Rubber Ltd) and 15 kg/m2 of rounded sand 0.2-0.8 mm (from Garside Sands Ltd) and finally tested according to FIFA 2* testing requirements, including mechanical wear tests of 20,200 cycles on a Lisport® machine. The following results were observed as tested according to the Handbook for Test Methods for Football Turf (2009 edition):


PRODUCT IDENTIFICATION
Monofilament material			MR	PE1
Mass per unit area		[g/m²]	2702	2554
Tufts per unit area		[m⁻²]	16.7	16.7
Pile length		[mm]	59	56
Pile weight		[g/m²]	1403	1451
CARPET PROPERTIES
Tuft withdrawal force		[N]	18	20
Water permeability of carpet		[mm/h]	4155	5176
Water permeability of system		[mm/h]	2162	2149
Vertical ball rebound	Dry	[m]	0.80	0.91
EN 12335	Wet	[m]	0.93	0.98
	After wear	[m]	0.99	0.96
Angle ball rebound	Dry		52%	55%
	Wet		76%	76%
PRODUCT IDENTIFICATION
Monofilament material			MR	PE1
Ball roll	Dry	[m]	6.8	6.5
	Wet	[m]	7.1	7.0
Shock absorption	Dry		65%	65%
EN 14808	Wet		63%	62%
	After wear		56%	53%
	−5° C.		66%	60%
	40° C.		65%	66%
Vertical Deformation	Dry	[mm]	8.0	7.5
EN 15301-1 using studded test foot	Wet	[mm]	8.0	7.5
	After wear	[mm]	6.0	5.0
Rotational resistance	Dry	[N.m]	37	39
EN 14809	Wet	[N.m]	37	36
	After wear	[N.m]	34	40
Linear stud deceleration value	Dry	[g]	4.0	3.4
	Wet	[g]	4.1	3.9
Linear stud slide value	Dry		175	160
	Wet		195	182
Skin/surface friction	Dry	[μ]	0.67	0.58
Skin abrasion	Dry		24%	15%
Carpet tuft withdrawal		[N]	18	20
	After	[N]	14	16
	ageing
UV resistance			pass	pass
Visual deterioration after	Cycles		30,000	60,000

The effects of simulated wear (“After wear” as given in the table) were measured after 20,200 cycles on a Lisport® machine.
The PE1 polyethylene tufted monofilaments as artificial grass shows:

- Lower dry ball roll replicates more accurately the behaviour of natural grass
- Lower values for skin/surface friction and skin abrasion indicate a softer feel—despite being at a higher density than MR
- Extended Lisport testing revealed no degradation before 60,000 cycles, which is twice that of MR
- Less low molecular weight species and absence of calcium stearate eliminate the risk of water carry-over and lead to less die deposit, allowing for longer production runs (longer intervals between maintenance, i.e. when the die and filters have to be cleaned).
- Longer thermal durability due to the higher Vicat softening temperature

Claims

1. Artificial grass tufted from slit film or monofilaments prepared with a polyethylene prepared with a bistetrahydroindenyl or bisindenyl metallocene catalyst complex having (a) a density in the range of 0.910 to 0.937 g/cm3 as determined by ISO 1183 at a temperature of 23° C. and (b) a melt index MI2 in the range of 0.5 to 5 g/10 min as determined by ISO 1133/D at a temperature of 190° C. and at a load of 2.16 kg,

wherein said polyethylene has a grheo of less than 0.9 or an LCBI of greater than 0.08,

and wherein the polyethylene has a Vicat Softening Temperature Tv, measured according to ISO 306 conditions A120, according to the following equation:

Tv>41234 d ²+77500 d−36295

wherein Tv is the Vicat Softening Temperature in ° C. and d is the density of the polyethylene in g/cm3.

2. Artificial grass according to claim 1 wherein the polyethylene has a g_rheoof less than 0.85 or an LCBI of greater than 0.13.

3. Artificial grass according to claim 1 wherein the polyethylene has a MI2 of 0.7 to 3.5 g/10 min.

4. Artificial grass according to claim 1 wherein the polyethylene has a density of 0.910 to 0.935 g/cm³.

5. Artificial grass according to claim 1 wherein the rheological horizontal activation energy of the polyethylene at a frequency of 1 s⁻¹is greater than 40 kJ/mol and at a frequency of 100 s⁻¹is less than 40 kJ/mol.

6. Artificial grass according to claim 1 wherein the rheological horizontal activation energy of the polyethylene at a frequency of 1 s ⁻¹is greater than 45 kJ/mol.

7. Artificial grass according to claim 1 wherein the polyethylene is a copolymer of ethylene and 1-hexene comonomer.

8. Artificial grass according to claim 1 wherein the polyethylene has a 1-hexene content of less than 10 wt %.

9. Artificial grass according to claim 1 being in a stretched form.

10. Artificial grass according to claim 1 having a draw ratio in the range 1:3 to 1:10 and preferably 1:4 to 1:10.

11. The artificial grass according to claim 1 wherein the grass has a durability of at least 60,000 cycles as measured on a Lisport® machine.