US20130225401A1

US20130225401A1 - Poly(Ionic Liquid) Sorbents and Membranes for CO2 Separation

Info

Publication number: US20130225401A1
Application number: US13/624,125
Authority: US
Inventors: Youqing Shen; Maciej Radosz
Original assignee: University of Wyoming
Current assignee: University of Wyoming
Priority date: 2004-08-05
Filing date: 2012-09-21
Publication date: 2013-08-29
Also published as: WO2006026064A2; WO2006026064A3; US8449652B2; US20090266230A1

Abstract

Polymerizable ionic liquid monomers and their corresponding polymers (poly(ionic liquid)s) are created and found to exhibit high CO₂sorption. The poly(ionic liquid)s have enhanced and reproducible CO₂sorption capacities and sorption/desorption rates relative to room-temperature ionic liquids. Furthermore, these materials exhibit selectivity relative to other gases such as nitrogen, methane, and oxygen. They are useful as efficient separation agents, such sorbents and membranes. Novel free-radical and condensation polymerization approaches are used in the preparation of the poly(ionic liquids).

Description

This application is a divisional application of U.S. patent application Ser. No. 11/659,484, filed Dec. 11, 2008, which was a National Stage application of PCT/US2005/027833, which claims priority to U.S. Patent Application Ser. No. 60/599,188, filed Aug. 5, 2004.

BACKGROUND OF THE INVENTION

The invention relates generally to novel materials, namely polymers made from ionic liquids, referred to herein as poly(ionic liquid)s, and, more specifically, to poly(ionic liquid)s for absorbing carbon dioxide (CO₂).
Global warming resulting from the increased CO₂concentration in the atmosphere due to emissions of CO₂from fossil fuel combustion is becoming one of most important environmental issues.^1,2Recently, CO₂capture and sequestration are receiving significant attention. For carbon sequestration, because the cost of capture and separation are estimated to make up three-fourths of total costs of ocean or geologic sequestration, it is important to develop new materials and methods to separate and capture CO₂from flue gas^3,4,5and other gas mixtures.
Ionic liquids, which are organic salts that become liquids usually below about 200° C., have attracted attention because of their unique chemical and physical properties and wide application potentials.^6-12Recently, CO₂was found to be remarkably soluble in ionic liquids, and thus ionic liquids have been explored as non-volatile, and reversible absorbents for CO₂separation.^13-21For instance, at 15 bar of CO₂pressure, the CO₂solubility in 1-butyl-3-methylimidazolium hexafluorophosphate ([bmim][PF₆]) is about 23 mol. %.¹⁹The CO₂solubility in the ionic liquids is dependent on their cations and substituents, and especially on their anions.¹⁹For example, fluorine-containing anions (e.g. bis(trifluoromethyl-sulfonyl)imide, Tf₂N),¹⁹or cations,²²or amine groups²³tend to increase the CO₂solubility. Ionic liquids have also been impregnated into porous materials for developing supported liquid membranes. Such membranes have high CO₂selectivity and permeance because of the selective sorption of CO₂in ionic liquids.^24-26
We have found that poly(ionic liquid)s, the polymers prepared from ionic liquid monomers, have higher CO₂sorption capacity than room temperature ionic liquids. Most importantly, the CO₂sorption and desorption of the polymers are much faster than those of ionic liquids and the sorption/desorption is completely reversible. These poly(ionic liquid)s are thus promising as sorbent and membrane materials for CO₂separation.

SUMMARY OF THE INVENTION

The invention consists of a class of new materials consisting of polymers made from ionic liquids. The poly(ionic liquid)s are polymerized ionic liquid monomers and have been found to have a CO₂absorption rate and/or a CO₂absorption capacity higher than that of the ionic liquid monomer. Certain of the poly(ionic liquid)s have a CO₂absorption capacity almost ten times that of the ionic liquid monomer from which they are made. The sorption/desorption rates of the poly(ionic liquid)s are much faster than those of the corresponding ionic liquid monomers, and the poly(ionic liquid)s retain their sorption/desorption properties after going through sorption/desorption cycling. The polymers are made primarily through free radical polymerization, but other methods of polymerization may also be used.
The ionic liquid monomers include: (a) Imidazolium-based ionic liquids, such as (a) 1-[2-(methacryloyloxy)ethyl]-3-butyl-imidazolium tetrafluoroborate ([MABI][BF₄]), 1-(p-vinylbenzyl)-3-butyl-imidazolium tetrafluoroborate ([VBBI][BF₄]), 1-(p-vinylbenzyl)-3-methyl-imidazolium tetrafluoroborate [VBMI][BF₄], 1-(p-vinylbenzyl)-3-butyl-imidazolium hexafluorophosphate [VBBI][PF₆], 1-(p-vinylbenzyl)-3-butyl-imidazolium o-benzoic sulphimide ([VBBI][Sac]), 1-(p-vinylbenzyl)-3-butyl-imidazolium trifluoromethane sulfonamide([VBBI][BF₄]), and (1-butylimidazolium-3)methyl-ethylene oxide ([BIEO][BF₄]); (b) Ammonium-based ionic liquids, such as (p-vinylbenzyl)trimethyl ammonium tetrafluoroborate ([VBTMA][BF₄]), (p-vinylbenzyl)triethyl ammonium tetrafluoroborate ([VBTEA][BF₄]), (p-vinylbenzyl)tributyl ammonium tetrafluoroborate ([VBTBA][BF₄]), 2-(methacryloyloxy)ethyltrimethylamnonium tetrafluoroborate ([MATMA][BF₄]), (p-vinylbenzyl)trimethyl ammonium hexafluorophosphate ([VBTMA][PF₆]), (p-vinylbenzyl)trimethyl ammonium o-benzoic sulphimide ([VBTMA][Sac]), and (p-vinylbenzyl)trimethyl ammonium trifluoromethane sulfonamide ([VBTMA][Tf₂N]); (c) Phosphonium-based ionic liquids, such as (p-vinylbenzyl)triethyl phosphonium tetrafluoroborate ([VBTEP][BF₄]), and (p-vinylbenzyl)triphenyl phosphonium tetrafluoroborate ([VBTPP][BF₄]); (d) Pyridinium-based ionic liquids, such as 1-(p-vinylbenzyl)pyridinium tetrafluoroborate ([VBP][BF₄]); and (e) Condensation polymerization ionic monomers, such as bis(2-hydroxyethyl)dimethyl ammonium tetrafluoroborate ([BHEDMA][BF₄]), 2,2-bis(methylimidazolium methyl)-1,3-propanediol tetrafluoroborate ([BMIMP][BF₄]), and 2,2-bis(butylimidazolium methyl)-1,3-propanediol tetrafluoroborate ([BBIMP][BF₄]).
The invention also consists of a process for the separation and recovery of CO₂, including the steps of contacting a CO₂-containing gas mixture with a solid sorbent that includes at least one poly(ionic liquid) compound under such conditions as to obtain a gas product having a lower concentration of CO₂than the initial gas mixture and a solid sorbent containing absorbed carbon dioxide which has been removed from said gas mixture. Preferably, the solid sorbent is treated under conditions as to substantially desorb the CO₂contained in the solid sorbent so as to obtain a regenerated solid sorbent.

BRIEF DESCRIPTION OF THE FIGURES

FIG. 1 is a graphical representation of the CO₂sorption of the poly(ionic liquids)s (P[VBBI][BF₄](a), P[VBBI][Tf₂N](b), P[MABI][BF₄](c), P[VBBI][Sac](d)), with their corresponding monomers ([VBBI][Tf₂N](e), [MABI][BF₄](g), [VBBI][BF₄](h), [VBBI][Sac](i)), and an ionic liquid [bmim][BF₄](f) as a function of time (592.3 mmHg CO₂, 22° C.).

FIG. 2 is a graphical representation of the CO₂sorption of poly(ionic liquid)s with different polymer backbones (592.3 mmHg of CO₂and 22° C.).

FIG. 3 is a graphical representation of the CO₂sorption of poly(ionic liquid)s with different substituents (592.3 mmHg of CO₂and 22° C.).

FIG. 4 is a graphical representation of the CO₂sorption of poly(ionic liquid)s with different anions (592.3 mmHg of CO₂and 22° C.).

FIG. 5 is a graphical representation of the gas (CO₂, O₂, N₂) sorption of P[VBBI][BF₄] as a function of time at 592.3 mmHg, 22° C.

FIG. 6 is a graphical representation of the weight change of P[VBBI][BF₄] (1 g) (without buoyancy correction) after introducing CO₂into the system, and then replacing CO₂with N₂(total pressure 592.3 mmHg, 22° C.).

FIG. 7 is a graphical representation of the isothermal sorption of P[VBBI][BF₄] and P[MABI][BF₄] at different CO₂pressures (22° C.).

FIG. 8 is a graphical representation of the cycles of CO₂sorption (592.3 mmHg CO₂, 22° C.) and desorption of P[VBBI][BF₄] and P[MABI][BF₄] under vacuum;

FIG. 9 is a graphical representation of CO₂sorption (592.3 mmHg CO₂, 22° C.) and desorption of a typical ionic liquid [bmim] [BF₄] under vacuum.

FIG. 10 is a graphical representation of the CO₂sorption of P[VBBI][BF₄] with different particle sizes (592.3 mmHg, 22° C.).

FIG. 11 is a graphical representation of the CO₂sorption of poly(ionic liquid)s with different types of cation.

FIG. 12 is a graphical representation of the CO₂sorption of poly(ionic liquid)s with different types of anion.

FIG. 13 is a graphical representation of the CO₂sorption in poly(ionic liquid)s with different backbones

FIG. 14 is a graphical representation of the CO₂sorption in poly(ionic liquid)s with different substituents.

FIG. 15 is a graphical representation of the effect of crosslinking on CO₂sorption in poly(ionic liquid)s.

FIG. 16 is a graphical representation of the CO₂/CH₄selectivity for P[VBTMA][BF₄]-g-PEG and P[MATMA][BF₄]-g-PEG

FIG. 17 is a graphical representation of the CO₂/CH₄selectivity for representative polymers and grafted poly(ionic liquids) (♦: representative polymers; : P[MATMA][BF₄]-g-PEG at 35° C., 50° C. and 70° C.; ▴: P[VBTMA][BF₄]-g-PEG at 35° C., 50° C. and 70° C.)

FIG. 18 is a graphical representation of the CO₂/N₂selectivity for P[VBTMA][BF₄]-g-PEG and P[MATMA][BF₄]-g-PEG

FIG. 19 is a graphical representation of the CO₂/N₂selectivity for representative polymers and grafted poly(ionic liquids) (♦: representative polymers; : P[MATMA][BF₄]-g-PEG at 35° C., 50° C. and 70° C.; ▴: P[VBTMA][BF₄]-g-PEG at 35° C., 50° C. and 70° C.)

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

In this description, each material is introduced by its full chemical name followed by a shortened name in parenthesis, for example, 1-[2-(methacryloyloxy)ethyl]-3-butyl-imidazolium tetrafluoroborate ([MABI][BF₄]). Following the initial introduction, only the shortened name is used.
Ionic liquids are organic salts with melting points usually below 200° C., often below room temperature. They can be substitutes for the traditional organic solvents in chemical reactions. The most common examples are imidazolium and pyridinium derivatives, but phosphonium or tetralkylammonium compounds have also been explored. Specific examples of ionic liquid monomers used for polymer synthesis and other applications include but are not limited to:
(1) Ionic liquid monomers based on imidazolium, such as 1-[2-(methacryloyloxy)ethyl]-3-butyl-imidazolium tetrafluoroborate ([MABI][BF₄]), 1-(p-vinylbenzyl)-3-butyl-imidazolium tetrafluoroborate ([VBBI][BF₄]), 1-(p-vinylbenzyl)-3-methyl-imidazolium tetrafluoroborate ([VBMI][BF₄]),1-(p-vinylbenzyl)-3-butyl-imidazolium hexafluorophosphate ([VBBI][PF₆]), 1-(p-vinylbenzyl)-3-butyl-imidazolium o-benzoic sulphimide ([VBBI][Sac]), 1-(p-vinylbenzyl)-3-butyl-imidazolium trifluoromethane sulfonamide ([VBBI][BF₄]), (1-butylimidazolium-3)methyl-ethylene oxide ([BIEO][BF₄]);
(2) Ionic liquid monomers based on ammonium, such as (p-vinylbenzyltrimethyl)ammonium tetrafluoroborate ([VBTMA][BF₄]), (p-vinylbenzyl)triethyl ammonium tetrafluoroborate ([VBTEA][BF₄]), (p-vinylbenzyl)tributyl ammonium tetrafluoroborate ([VBTBA][BF₄]), [2-(methacryloyloxy)ethyl]trimethylamnonium tetrafluoroborate ([MATMA][BF₄]), (p-vinylbenzyl)trimethyl ammonium hexafluorophosphate ([VBTMA][PF₆]), (p-vinylbenzyl)trimethyl ammonium o-benzoic sulphimide ([VBTMA][Sac]), (p-vinylbenzyltrimethyl)ammonium trifluoromethane sulfonamide ([VBTMA][Tf₂N]);
(3) Ionic liquid monomers based on phosphonium, such as (p-vinylbenzyl)triethyl phosphonium tetrafluoroborate ([VBTEP][BF₄]), (p-vinylbenzyl)triphenyl phosphonium tetrafluoroborate ([VBTPP][BF₄]);
(4) Ionic liquid monomers based on pyridinium, such as 1-(p-vinylbenzyl)pyridinium tetrafluoroborate ([VBP][BF₄]);
(5) Ionic liquid monomers for condensation polymerization, such as bis(2-hydroxyethyl)dimethyl ammonium tetrafluoroborate ([BHEDMA][BF₄]), 2,2-bis(methylimidazolium methyl)-1,3-propanediol tetrafluoroborate ([BMIMP][BF₄]), and 2,2-bis(butylimidazolium methyl)-1,3-propanediol tetrafluoroborate ([BBIMP][BF₄]).
Poly(ionic liquid)s as used in this specification means polymers formed using ionic liquids as monomers via free radical polymerization or other kind of polymerization.
Free radical polymerization is a common and useful reaction for making polymers from vinyl monomers, that is, from small molecules containing carbon-carbon double bonds. Polymers made by free radical polymerization include polystyrene, poly(methyl methacrylate), poly(vinyl acetate) and branched polyethylene. Free radical polymerization begins with a molecule called an initiator; common initiators are benzoyl peroxide or 2,2′-azo-bis-isobutyrylnitrile (AIBN).

EXAMPLE 1

Materials

4-Vinylbenzyl chloride, methacryloyl chloride, 1-butylimidazole, 2-bromoethanol, lithium trifluoromethane sulfonimide, potassium hexafluorophosphate, sodium tetrafluoroborate, 2,6-di-tert-butyl-4-methyl phenol (DBMP), 2,2′-azobisisobutyronitrile (AIBN), aluminum isopropoxide, epichlorohydrin, N,N-dimethylformamide (DMF), acetonitrile, and acetone were purchased from Aldrich. 1-Methylimidazole, and o-benzoic sulphimide sodium salt hydrate were purchased from Lancaster Synthesis Inc. These chemicals were used without further purification.

Synthesis and Characterization

1-[2-(Methylacryloyloxy)ethyl]-3-butyl-imidazolium tetrafluoroborate ([MABI][BF₄]) and 1-(p-vinylbenzyl)-3-butyl-imidazolium tetrafluoroborate ([VBBI][BF₄]) were synthesized according to our published reports,^27,28as shown in Schemes 1 and 2. 1-(p-Vinylbenzyl)-3-butyl-imidazolium hexafluorophosphate ([VBBI][PF₆]), 1-(p-vinylbenzyl)-3-butyl-imidazolium o-benzoic sulphimide ([VBBI][Sac]), 1-(p-vinylbenzyl)-3-butyl-imidazolium trifluoromethane sulfonamide ([VBBI][Tf₂N]) were synthesized by a similar procedure except using NaPF₆, o-benzoic sulphimide sodium salt hydrate (NaSac) or lithium trifluoromethane sulfonamide (LiTf₂N) for anion exchange reactions. The yields were 93.0%, 49.6%, 39.9%, respectively.
1-(p-Vinylbenzyl)-3-methyl-imidazolium tetrafluoroborate ([VBMI][BF₄]) was synthesized as follows: To a 50 ml flask, p-vinylbenzyl chloride (10 ml, 0.064 mole), a small amount of DBMP, and 1-methylimdazole (5.14 ml, 0.064 mole) were added and heated at 45° C. overnight. The solution became gradually viscous. NaBF₄(5.2 g, 0.47 mole) and dry acetone (30 ml) were added. The mixture was stirred at room temperature. The viscous liquid dissolved gradually while a white solid precipitated. After 12 h reaction, the precipitate was removed by filtration. The solvent was removed under vacuum. The solid was washed with water and ether, and dried by vacuuming at room temperature, producing 14 g of white crystals (yield 76.5%).
[VBBI][BF₄]: ¹H NMR (400 MHz, DMSO-d₆, ppm): δ 9.24 (1H, s), 7.80 (2H, s), 7.51 (2H, d) 7.35 (2H, d), 6.73 (1H, m), 5.89 (1H, d) 5.27 (1H, d), 5.40 (2H, s), 4.14 (2H, t), 1.78 (2H, m), 1.24 (2H, m), 0.88 (3H, t). mp: 67-68° C.
[VBBI][PF₆] ¹H NMR (400 MHz, DMSO-d₆, ppm): δ 9.22 (1H, s), 7.80 (2H, s), 7.48 (2H, d) 7.35 (2H, d), 6.73 (1H, m), 5.89(1H, d), 5.30 (1H, d), 5.46 (2H, s), 4.14 (2H, t), 1.79 (2H, m), 1.22 (2H, m), 0.87 (3H, t). mp: 87-88.5° C.
[VBBI][Sac] ¹H NMR (400 MHz, DMSO-d₆, ppm) δ 9.38 (1H, s), 7.80 (2H, s) 7.66 (1H, d), 7.61(1H, d), 7.59 (2H, d), 7.49 (2H, d), 7.40 (2H,d), 6.72 (1H, m) 5.84 (1H, d), 5.42 (2H, s), 5.26 (2H, d) 4.16 (2H, m) 1.73 (2H, m), 1.21 (2H, m), 0.84 (3H, m). mp: −36-−38° C.
[VBBI][Tf₂N] ¹H NMR (400 MHz, DMSO-d₆, ppm): δ 8.83 (1H, s), 7.44 (2H, s), 7.34 (2H, d) 7.27 (2H, d), 6.70 (1H, m), 5.79(1H,d) 5.33 (1H, d), 5.31 (2H, s), 4.17 (2H, t), 1.84 (2H, m), 1.35 (2H, m), 0.94 (3H, t). mp: −61-−62° C.
[VBMI][BF₄]: ¹H NMR (400 MHz, DMSO-d₆, ppm): 9.13 (1H, s), 7.71 (1H, s), 7.63 (1H, s), 7.52 (1H, d), 7.42 (2H, d), 6.75 (1H, m), 5.88 (1H, d), 5.41(2H, s), 5.26 (1H, d), 3.86 (3H, s). mp: 42-44° C.
Poly(ionic liquid)s were prepared from above ionic liquid monomers by free radical polymerization. A typical example is as the following: [VBBI][BF₄] (3 g), AIBN (30 mg) and DMF (3 ml) were charged into a reaction tube. The tube was tightly sealed, and degassed. It was immersed in an oil bath at 60° C. for 6 h. The solution was poured into methanol to precipitate out the polymer. The polymer was dried under vacuum at 100° C. The yield was 2.3 g (75%).
Poly[1-(p-Vinylbenzyl)-3-butyl-imidazolium tetrafluoroborate] (P[VBBI][BF₄]): ¹H NMR (DMSO-d₆, 400 MHz, ppm): δ 9.12 (s, 1H), 7.8 (br, 1H), 7.4 (br, 1H),7.1 (br, 2 H), 6.4 (br, 2H), 5.6-4.9 (br, 2H), 4.1 (br, 2H) , 2.1-1.0 (m, 7H), 0.8 (s, 3 H). Anal. Calcd for (C₁₆H₂₁BF₄N₂)n: C, 58.56%; H, 6.45%; N, 8.54%. Found: C, 58.35%; H, 6.43%; N, 8.50%.
Poly[1-(p-Vinylbenzyl)-3-butyl-imidazolium hexafluorophosphate] (P[VBBI][PF₆]): ¹H NMR (DMSO-d₆, 400 MHz, ppm): δ 9.16 (s, 1H), 7.72 (br, 1H), 7.47 (br, 1H), 7.04 (br, 2H), 6.42 (br, 2H), 5.23 (br, 2H), 4.15 (br, 2H) , 2.1-0.8 (m,10H) Anal. Calcd for (C₁₆H₂₁F₆N₂P)_n: C, 49.75%; H, 5.48%; N, 7.25%; Found: C, 49.70%; H, 5.37%; N, 7.12%.
Poly[1-(p-Vinylbenzyl)-3-butyl-imidazolium o-benzoic sulphimide] (P[VBBI][Sac]): ¹H NMR (DMSO-d₆, 400 MHz, ppm): δ 9.44 (s, 1H), 7.5-7.9 (br, 6H), 7.19 (br, 2H), 6.35 (br, 2H), 5.35 (br, 2H), 4.15 (br, 2H) , 1.9-0.5 (m,10H) Anal. Calcd for (C₂₃H₂₅N₃O₃S)_n: C, 65.25; H, 5.91; N, 9.93. Found: C, 64.11; H, 6.05; N, 9.68.
Poly[1-(p-Vinylbenzyl)-3-butyl-imidazolium trifluoromethane sulfonamide] (P[VBBI][Tf₂N]): ¹H NMR (DMSO-d₆, 400 MHz, ppm): δ 9.20 (s, 1H), 7.73 (br, 1H), 7.44 (br, 1H), 6.94 (br, 2 H), 6.33 (br, 2H), 5.19 (br, 2H), 4.13 (br, 2H), 2.0-1.0 (m,7H), 0.81 (s, 3H). Anal. Calcd for (C₁₈H₂₁N₃F₆O₄S₂)_n: C, 41.46; H, 4.03; N, 8.06. Found: C, 41.46; H, 4.13; N, 7.94.
Poly{1-[2-(Methylacryloyloxy)ethyl]-3-butyl-imidazolium tetrafluoroborate} (P[MABI][BF₄]): ¹H NMR (DMSO-d₆, 400 MHz, ppm): δ 9.1 (br, 1H), 7.9-7.6 (d, 2H), 4.8-3.8 (m 6H), 2.0-0.2 (m, 12H). Anal. Calcd for (C₉H₁₈BF₄NO₂)_n: C, 48.17 H, 6.49; N, 8.65. Found: C, 47.68; H, 6.48; N, 6.48.
Poly[1-(p-vinylbenzyl)-3-methyl-imidazolium tetrafluoroborate] (P[VBMI][BF₄]): ¹H NMR (DMSO-d₆, 400 MHz, ppm): δ 9.10 (1H, br), 7.60-7.30 (2H, br), 7.10 (2H, br), 6.40 (2H, br), 5.30(2H, br), 3.70 (2H, br) 2.1˜0.5 (3H, br). Anal. Calcd for (C₁₃H₁₅BF₄N₂)_n: C, 54.58; H, 5.25; N, 9.80. Found: C, 52.74; H, 5.33, ; N, 9.38.
The poly(ionic liquid) with poly(ethylene oxide) backbone was synthesized from poly(epichlorohydrin) (Scheme 3). Aluminum isopropoxide (0.18 g, 0.88 mmol) was added into a 100 mL flask. The flask was degassed by repeated vacuum/nitrogen purging (5 cycles). Degassed THF (25 mL) and epichlorohydrin (5.0 mL, 66 mmol) was added by degassed syringes. After the reaction flask was immersed into a 40° C. oil bath for 12 hours, the poly(epichlorohydrin) was precipitated out by adding a large amount of hexane. 3.3 g of poly(epichlorohydrin) was dissolved in 50 mL of DMF. N-butylimidazole (5.0 g, 40 mmol) was added to the DMF solution. This solution was stirred at 80° C. for 5 days, and then NaBF₄(4.4 g, 40 mmol) was added. After the mixture was stirred at room temperature for 2 days, sodium chloride precipitate was removed by filtration. Anhydrous ethyl ether was added to the filtrate to precipitate the poly(ionic liquid). The obtained P[BIEO][BF₄] was washed with ethyl ether and dried in vacuum oven at 50° C. for one day. ¹H-NMR (acetone-d₆): δ 8.86 (1H, s), 7.69 (2H, br), 4.44-4.31 (4H, br), 3.97 (1H, br), 3.67 (2H, br), 1.88 (2H, br), 1.34 (2H, br), 0.93 (3H, br). Anal. Calcd for (C₁₀H₁₇BF₄N₂O)_n: C, 44.80; H, 6.34; N, 10.46. Found: C, 44.66; H, 6.26; N, 10.11.
The syntheses of ionic liquid monomers are shown in Schemes 1-3. Two steps were generally involved in the preparations: the quaternization reaction of 1-butylimidazole or 1-methylimidazole with 4-vinylbenzyl chloride or 2-bromoethyl methacrylate, and the anion exchange reaction of the halide ions with tetrafluoroborate, hexafluorophosphate, Sac or Tf₂N anions.
The quaternization with 4-vinylbenzyl chloride was fast with a high yield. The anion exchange of the resulting chloride [VBBI][Cl] and [VBMI][Cl] with BF₄ ⁻ produced the monomers, [VBBI][BF₄] and [VBMI][BF₄], as crystalline solids, which are soluble in acetone, acetonitrile, dichloromethane, DMF, and DMSO, but insoluble in diethyl ether. [VBBI][PF₆] is also a solid with similar solubility. [VBBI][Sac] and [VBBI][Tf₂N] are liquid at room temperature and soluble in acetone, acetonitrile, DMF, and DMSO. [VBBI][Tf₂N] is also soluble in ethyl ether.
The quaternization of N-butylimidazole with 2-bromoethyl methacrylate was slow and difficult to get high yield of [MABI][Br]. After the anion exchange, [MABI][BF₄] is also a liquid at room temperature and soluble in above polar solvents but insoluble in ethyl ether and other nonpolar solvents.
All above ionic liquid monomers, unlike their corresponding chloride salts, are insoluble in water. So unreacted chloride salts could be easily removed by washing with water. Silver nitrate tests indicated that no chloride was present in all the ionic liquid monomers.
The poly(ionic liquid)s, except for P[BIEO][BF₄] which was synthesized by the polymer reaction shown in Scheme 3, were prepared by free radical polymerization of the ionic liquid monomers using AIBN as initiators. DMF was used as solvent because all poly(ionic liquid)s are soluble in it. All these ionic liquid monomers are easily polymerized with high conversions. Poly(ionic liquid)s were precipitated in methanol to remove unreacted monomers. DMF residue in polymers was removed by drying at 100° C. under vacuum. All poly(ionic liquid)s can dissolve in DMF, DMSO, acetonitrile, but are insoluble in water, dichloromethane and toluene. H¹NMR and element analysis indicated the poly(ionic liquid)s were pure.

CO₂Sorption and Desorption

The CO₂sorption of the poly(ionic liquid)s was measured using a Cahn 1000 Electrobalance. The sample pan and the counterweight of the balance were configured symmetrically to minimize buoyancy effects. The microbalance has 100 g capacity and 1.0 μg sensitivity and is suitable for study of sorption and diffusion of gases on/in solid or liquid materials. CO₂gas (99.995%) was dried by passing two drying columns (length×diameter: 15 in×2 in) packed with P₂O₅. The fine powder of the ionic liquid polymer was dried and degassed at 70° C. under vacuum for 12 h to remove moisture or other volatile contaminants. It was further dried in the balance by evacuating the chamber at high vacuum until its weight reached constant for at least 30 min. CO₂was introduced into the chamber and the sample weight increase was recorded until the weight did not change significantly in 30 min. The buoyancy effects in these measurements were corrected according to the literature.²⁹The system was validated by measuring the CO₂sorption of an ionic liquid, 1-n-butyl-3-methyl imidazolium tetrafluoroborate ([bmim][BF₄]). The measured CO₂sorption capacity of [bmim][BF₄] was identical to the reported.¹⁹
CO₂has remarkable solubility in imidazolium-based ionic liquids because of its interactions with the anions and cations of ionic liquids.¹⁹The CO₂sorption of (P[VBBI][BF₄] (a), P[VBBI][Tf₂N](b), P[MABI][BF₄] (c), P[VBBI] [Sac](d)), with their corresponding monomers ([VBBI][Tf₂N](e), [MABI][BF₄](g), [VBBI][BF₄](h), [VBBI][Sac](i)), and an ionic liquid [bmim][BE](f) as a function of time (592.3 mmHg CO₂, 22° C.) is shown in FIG. 1. The CO₂solubility of [bmim][BF₄] was tested first and found consistent with that reported in the literature,¹⁹which validated the setup of the apparatus.
At the equilibrium, P[VBBI][BF₄], P[VBBI][Tf₂N], P[MABI][BF₄] and P[VBBI][Sac], respectively, took up 2.27 mol %, 2.23 mol % , 1.78 mol % and 1.55 mol % of CO₂in terms of their monomer units. In comparison, room temperature ionic liquid [bmim][BF₄] absorbed 1.34 mol % of CO₂under the same conditions. [VBBI][BF₄] monomer had no measurable sorption of CO₂because of its crystalline structure. [MABI][BF₄], [VBBI][Sac] and [VBBI][Tf₂N] monomers are liquid at room temperature. [MABI][BF₄] had the same CO₂sorption capacity as [bmim][BF₄]. [VBBI][Tf₂N] had a CO₂sorption capacity of 1.96 mol %, higher than that of [bmim][BF₄], which is consistent with the report that the ionic liquid with Tf₂N anions had higher capacity than ionic liquids with BF₄anions.¹⁴[VBBI][Sac] did not take up any CO₂when it was exposed to CO₂(FIG. 1). This comparison shows that polymerizing ionic liquids can increase the CO₂sorption capacity.
Meanwhile, the CO₂sorption of the ploy(ionic liquid)s was much faster than that of ionic liquids. It takes only several minutes for the poly(ionic liquid)s to reach their 90% capacity and less than 30 minutes to reach their equilibrium capacity. In contrast, room temperature ionic liquids [MABI][BF₄] and [bmim][BF₄] needed more than 400 min to reach their equilibrium capacity (FIG. 1).
The CO₂sorption of poly(ionic liquid)s with different backbones, cations, and anions was compared to understand the factors affecting the CO₂sorption. The CO₂sorption kinetics of poly(ionic liquid)s with different backbones are shown in FIG. 2. At the equilibrium, the polymers sorbed 2.27 mol % (P[VBBI][BF₄]), 1.78 mol % (P[MABI][BF₄]) and 1.06 mol % (P[BIEO][BF₄]), respectively, in terms of their monomer units at 592.3 mmHg of CO₂and 22° C. With the same butylimidazolium cation and BF₄ ⁻ anion, the polymer with polystyrene backbone had a higher CO₂sorption capacity than those with polymethylmethacrylate and polyethylene glycol backbones. The polymer with polyethylene glycol backbone had the lowest capacity.
The effect of substituent of the imidazolium cation on the CO₂sorption is shown in FIG. 3. P[VBMI][BF₄], which has a methyl substituent on its imidazolium cation, had a higher capacity (3.05 mol. %) than P[VBBI][BF₄] (2.27 mol. %) with butyl group. This indicates that a large substituent on the imidazolium cation may block the CO₂sorption.
The effect of the anions on the CO₂sorption capacity of the poly(ionic liquid)s is shown in FIG. 4. The CO₂sorption capacity the P[VBBI]-based polymers depends on the type of the anions: it was 2.80 mol. % for P[VBBI][PF₄], 2.27 mol % for P[VBBI][BF₄], 2.23 mol. % for P[VBBI][Tf₂N] and 1.55 mol. % for P[VBBI][Sac], respectively, in terms of their monomer units at 592.3 mmHg of CO₂and 22° C. This trend is different from that of ionic liquids. The CO₂solubility in ionic liquids with Tf₂N⁻ anions is much higher than those with PF₆ ⁻ or BF₄ ⁻ anions.¹⁹By contrast, the poly(ionic liquid) with PF₆ ⁻ anions ([PVBBI][PF₆]) had the highest sorption capacity, and those with BF₄ ⁻ and Tf₂N⁻ anions had a similar capacity. The poly(ionic liquid) with Sac⁻ anions could take up 1.55mol % of CO₂even though the anion contains no fluorine atoms. These results indicate that for poly(ionic liquid)s, fluorine-atoms are not a decisive factor for CO₂sorption but fluorine-atoms in the anions indeed enhance the CO₂sorption.
The CO₂sorption of the polymers is very selective, as shown in FIG. 5. There was no weight increase when the polymers were exposed to N₂or 0₂under the same conditions, which means that poly(ionic liquid)s can selectively absorb CO₂.
The selective CO₂sorption of the poly(ionic liquid)s was also confirmed by a gas-replacement experiment. The CO₂sorption of P[VBBI][BF₄] (1 gram) and desorption by replacing CO₂with N₂are shown in FIG. 6. After introducing CO₂into the balance, the sample weight increased rapidly until it became constant after 12 min. The weight increase was 2.1 mg, and the actual weight increase was 3.10 mg after a buoyancy correction. When N₂was introduced into the chambers while maintaining the total pressure in the chambers at ambient pressure (592.3 mmHg), the sample weight decreased gradually, and finally reached −0.56 mg, which was equal to the buoyancy of the sample under N₂. This experiment indicates that the poly(ionic liquid) does not take up N₂. Similar experiments conformed that there was no O₂sorption.
The sorption isotherms of P[VBIM][BF₄] and P[BIMT][BF₄] at different CO₂partial pressures and 22° C. are shown in FIG. 7. The different CO₂partial pressures were obtained by adjusting the N₂/CO₂ratio of the mixed gas charged to the balance chambers because P[VBIM][BF₄] and P[MABI][BF₄] had no N₂sorption. As shown in FIG. 7, the CO₂mole fraction in the polymers increased with the increase of CO₂partial pressure.
Henry's constant is defined as
$H = \lim_{x \to 0} \frac{p}{x}$
where H is Henry's constant, x is the mole fraction of gas sorbed in the polymer in term of monomeric unit, and P is the CO₂partial pressure. Since the x vs. P plots were not linear in the entire pressure range, Henry's constants were calculated by fitting the data and extrapolating the slope to the zero CO₂partial pressure.¹⁶Henry's constant was 26.0 bar for P[VBBI][BF₄] and 37.7 bar for P[MABI][BF₄], which is lower than that of room temperature ionic liquid [bmim][PF₆] (38.7 bar at 10° C. and 53.4 bar at 25° C.).¹⁶
Stable sorption capacity after repeated sorption/desorption is important for materials used for CO₂separation. Four cycles of CO₂sorption and desorption of P[VBBI][BF₄] and P[MABI][BF₄] were tested by filling the chambers with CO₂and then vacuuming (FIG. 8 a). The sorption and desorption of P[VBBI][BF₄] and P[MABI][BF₄] were all very fast. It took only about 30 min to take up CO₂and to have a complete desorption of CO₂. The desorption was complete, suggesting that the sorption/desorption was reversible. No change in sorption/desorption kinetics and sorption capacity was observed after the four cycles. By contrast, the desorption of CO₂from room temperature ionic liquids [bmim][BF₄] was very slow (FIG. 8 b)
The enhanced sorption capacity and fast sorption/desorption rates of the poly(ionic liquid)s were unexpected because all polymers are solid at room temperature. An immediate question is whether the sorption occurred on the surface (adsorption) or in the bulk (absorption) or both. The BET surface area of P[VBBI][BF₄] was measured by nitrogen sorption and its morphology was examined by SEM. The measured BET surface area of P[VBBI][BF₄] sample was 0.295 m²/g, The calculated CO₂-adsorption assuming a monolayer of CO₂on this surface was only 0.0128 wt %, much less than the measured CO₂sorption capacities. The SEM indicated that the particles had a nonporous structure, and the average diameter of the particles was about 100 μm.
The CO₂sorption of P[VBBI][BF₄] samples with different particle sizes was tested (FIG. 10). The particle size did not significantly affect the capacity of CO₂sorption and the sample with a big size even had a slightly higher sorption capacity. However, the particle size affected the rate of CO₂sorption. The CO₂sorption of the sample with big particle sizes (>250 μm in diameter) was slow, and needed about 120 minutes to reach its full sorption capacity, while those with the particle diameters less than 125 μm in diameter only needed less than 30 mins.
Without being bound to any particular theory, it appears that the CO₂sorption of the polymer particles involves more absorption (the bulk) but less adsorption (the surface). Their CO₂sorption capacity mainly depends on the chemical structure of poly(ionic liquid)s, while the rate of CO₂sorption depends on the particle size due to the CO₂diffusion in the polymers.

EXAMPLE 2

Materials

4-vinylbenzyl chloride (90%), 1-methylimidazole (98%), lithium trifluoromethane sulfonimide 99.95%, potassium hexafluorophosphate 98%, sodium tetrafluoroborate (98%), 2, 6-Di-tert-butyl-4-methyl phenol (98%) (DBMP), N,N-Dimethylformamide (99.8%) (DMF), acetonitrile (99.5+%), acetone (99.5+%), aqueous [2-(methacryloyloxy)ethyl]rimethyl ammonium chloride solution (75 wt. %), (p-vinylbenzyl)trimethylammonium chloride (98%), triethylamine (99.5%), tributylamine (99.5%) triphenylphosphine 99%, α,α′-azobis(isobutyrobitrile)(AIBN) (98%) were purchased from Aldrich.1-methyl imidazole 99%, o-Benzoic sulphimide sodium salt hydrate (97%) were purchased from Lancaster Synthesis Inc. Pyridine was purchased from Fisher scientific. All chemicals were used as received.

Synthesis and Characterization

(p-vinylbenzyl)trimethyl ammonium tetrafluoroborate ([VBTMA][BF₄]) and 2-(methacryloyloxy)ethyltrimethylamnonium tetrafluoroborate ([MATMA][BF₄]) were synthesized as described previously³⁰using (p-vinylbenzyl)triethyl phosphonium tetrafluoroborate ([VBTEP][BF₄]), (p-vinylbenzyl)triphenyl phosphonium tetrafluoroborate ([VBTPP][BF₄]).
The synthesis of (p-vinylbenzyl)triphenyl phosphonium tetrafluoroborate ([VBTPP][BF₄]), 1-(p-vinylbenzyl)pyridinium tetrafluoroborate ([VBP][BF₄]) and 1-(p-vinylbenzyl)-3-methyl-imidazolium tetrafluoroborate ([VBMI][BF₄]) is similar to 1-(p-vinylbenzyl)-3-butyl-imidazolium tetrafluoroborate ([VBBI][BF₄]) [VBBI][BF₄] (VBIT), as reported previously,²⁸using triphenylphosphine, pyridine and 1-methyl imidazole instead of 1-butylimidazole, respectively.
The synthesis of (p-vinylbenzyl)triethylammonium tetrafluoroborate [VBTEA][BF₄] and (p-vinyl benzyl)tributylammonium tetrafluoroborate [VBTBA][BF₄] was follows: In a 50 ml flask, 4-vinylbenzyl chloride (6.1 g, 0.04 mol) and triethylamine (4.2 g, 0.042 mol) mol were mixed and heated at 50° C. under N₂atmosphere for 2 days. The formed solid was washed with diethyl ether. The resultant white solid (8.5 g, 0.033 mol) was mixed with NaBF₄(3.8 g, 0.035) in 50 acetonitrile and stirred at room temperature for 2 days. The salt precipitate was removed by filtration. The filtrate was concentrated and poured into 200 ml diethyl ether to precipitate out product. White crystal precipitate was formed, collected by filtration, and dried under vacuum. The total yield was 9.2 g (75%). [VBTBA][BF₄] was synthesized according to a similar procedure with yield of 64%.
In the synthesis of bis[(p-vinylbenzyl)dimethylammonium]ethane, [BVDEA][BF₄], which is an ionic liquid crosslinker, tetramethylethylenediamine (5.8 g, 0.05 mol), 4-vinylbenzyl chloride (16.0 g, 0.105 mol) and 0.1 g DBMP were mixed in 50 ml DMF. The resulting solution was heated at 50° C. for 2 days. The solution was poured into 400 ml diethyl ether to precipitate out the product. After filtration and drying under vacuum, 15.8 g white crystal product was obtained. The product was reacted with NaBF₄(4.3 g, 0.04 mol) in 50 ml dried acetonitrile for 2 days. After the reaction, the insoluble chloride salt was removed by filtration. The product was collected by filtration and dried under vacuum. The overall yield was 16.7 g (63.7%).
Poly(ionic liquid)s were synthesized by free radical polymerization using AIBN as initiator in DMF as described previously.³⁰The crosslinked P[VBTMA][BF₄] was synthesized in the same way except for adding 5 wt % of the crosslinker.
The polymers were characterized by ¹H NMR on a Bruker Advance DRX-400 spectrometer using d⁶-dimethylsulfoxide (DMSO-d⁶) as solvent. The elemental analyses of polymers were tested by Midwest Microlab LLC (US). The CO₂sorption of the poly(ionic liquid)s was measured using a Cahn 1000 Electrobalance.
The structures of poly(ionic liquid)s are shown in Schemes 4 and 5. Two steps were generally involved in the preparation of ionic liquid monomers: the quaternization reaction and the anion exchange reaction of the halide ions with tetrafluoroborate, hexafluorophosphate, Sac or Tf₂N anions. The resulting monomers are soluble in polar solvents, such as DMF, acetone, or acetonitrile. All monomers based on ammonium except for P[VBTMA][Tf₂N] are soluble in H₂O. The ionic liquid monomers based on phosphonium, pyridium, imidazolium are insoluble in H₂O. The poly(ionic liquid)s are soluble in DMF.
The ¹H NMR and elemental analyses indicated that the ionic liquid monomers and poly(ionic liquid)s obtained were pure.

CO₂Sorption and Desorption

FIG. 11 shows the effect of cation types on CO₂sorption of poly(ionic liquid)s. The CO₂sorption capacity of poly(ionic liquid)s with different cations is as follows: P[VBTMA][BF₄] (10.2 mol. %) <P[VBTP][BF₄] (7.8 mol. %) <P[VBP][BF₄] (3.6%) <P[VBMI][BF₄] (3.0%). The solubility increases with increasing cation polarity. The polymer based on ammonium has the highest solubility because of its highest cation polarity. The polymer based on imidazolium, with the lowest cation polarity, has the lowest solubility.
FIG. 12 shows the effect of anion types on the CO₂solubility of poly(ionic liquid)s. The four polymers have the same cation structure, but different anions. P[VBTMA][PF₆] and P[VBTMA][BF₄] have a similar CO₂solubility of 10.7 mol. % and 10.2 mol. %, respectively. P[VBTMA][[Sac] and P[VBTMA][Tf₂N] have a solubility of 2.8 mol. % and 2.7%, respectively. The two poly(ionic liquid)s with inorganic anion have much higher solubility than the two with an organic anion, which can be explained in terms of the anion polarity effect on the interaction between the poly(ionic liquid)s with CO₂; the higher the anion polarity, the higher the affinity to CO₂. As a result the poly(ionic liquid) with high anion polarity exhibit a higher CO₂solubility.
The CO₂sorption kinetics of poly(ionic liquid)s with different backbones are shown in FIG. 13. At the equilibrium, the polymers took up 10.22 mol % (P[VBTMA][BF₄]), 7.99 mol % (P[MATMA][BF₄]), respectively, in terms of their monomer units at 592.3 mmHg of CO₂and 22° C. With the same ammonium cation and BF₄ ⁻ anion, the polymer with polystyrene backbone had a higher CO₂sorption capacity than that with polymethylmethacrylate backbone.
The effect of substituent of the ammonium cation on the CO₂sorption is shown in FIG. 14. Their CO₂sorption capacities are as follows: P[VBTMA][BF₄] (10.2 mol. %) >P[VBTEA][BF₄] (4.85 mol. %) >P[VBTBA][BF₄] (3.1 mol. %). Obviously, the CO₂sorption capacity decreases with increasing length of the substituent, which indicates that a large substituent on the ammonium cation blocks CO₂sorption.
FIG. 15 shows the effect of crosslinking on CO₂sorption of poly(ionic liquid). Compared with P[VBTMA][BF₄] without crosslinking, the CO₂sorption capacity of 5%-crosslinked P[VBTMA][BF₄] decreased by 17.3%.

EXAMPLE 3

Materials

Bis(2-hydroxyethyl)dimethyl ammonium chloride (Acros, 99%), 2,2-Bis(bromomethyl)-1,3-propanediol (Aldrich, 98%), 1-Methylimidazole (Lancaster, 99%), 1-Butylimidazole (Aldrich, 98%), 1,1-Carbonyldiimidazole (Aldrich, reagent grade), terephthaloyl chloride (Aldrich, 99+%), sodium tetrafluoroborate (Aldrich, 98%, NaBF₄), dimethyl sulfoxide (Aldrich, 99.9+%, DMSO) and methanol (A.C.S. reagent) were used as received. Acetonitrile (Aldrich, 99.5+%), N,N-Dimethylformamide (Aldrich, 99.8%, DMF) and triethylamine (EMD, 99.5%, Et₃N) were used after removing water by molecular sieves.

Synthesis and Characterization

The synthesis of the monomers, Bis(2-hydroxyethyl)dimethyl ammonium tetrafluoroborate ([BHEDMA][BF₄]) 1, 2,2-Bis(methylimidazolium methyl)-1,3-propanediol tetrafluoroborate ([BMIMP][BF₄]) 2 and 2,2-Bis(butylimidazolium methyl)-1,3-propanediol tetrafluoroborate ([BBIMP][BF₄]) 3 is shown in Scheme 6. The reagents and conditions were: a) NaBF₄, acetonitrile, room temperature, 48 h, 96%; b) 1-Methylimidazole, N₂, 60° C., 24 h, 98%; c) NaBF₄, acetonitrile, room temperature, 48 h, 96%; d) 1-Butylimidazole, N₂, 80° C., 24 h, 97%; d) NaBF₄, acetonitrile, room temperature, 48 h, 96%. Monomer 1 is an ammonium-based ionic liquid, while 2 and 3 are imidazolium-based ionic liquids.
The synthesis of polycarbonate (PC) and polyethylene terephthalate (PET) types of ionic liquid polymers by condensation polymerization is as follows. The PC type of ionic liquid polymers can be synthesized using the monomers 1 (2 or 3) reacted with 1,1-carbonyldiimidazole. The PET type of ionic liquid polymers can be synthesized using the monomers 1 (2 or 3) reacted with terephthaloyl chloride, respectively. Both kinds of condensation polymerizations required a strict 1:1 ratio of the reagents with different difunctional groups. All the reactions were carried out in DMF at 60° C. for 24 h. All the polymers were precipiatated by methanol after polymerization and dried under vacuum at 50° C.
The ionic liquid monomer 1 is colorless, while 2 and 3 have a light yellow color. Synthesis of 2 and 3 in a N₂atmosphere is necessary because the imidazole group is liable to be oxidized by the O₂in the air, which will make the product have a brown color. For the 1-methylimidazole is more active than 1-butylimidazole, it will react with 2,2-Bis(bromomethyl)-1,3-propanediol at a lower temperature (60° C.) than that of the 1-Butylimidazole (80° C.). All the monomers (1, 2 and 3) are viscous liquids, and they all absorb moisture quickly when contacting air, so all of them need to be dried in a rotating evaporator before the polymerization.
The polycondensation synthesis of the PC type polymers, poly(bis(2-hydroxyethyl)dimethyl ammonium tetrafluoroborate) carbonate (P[BHEDMA][BF4]C) 4, poly(2,2-Bis(methylimidazolium methyl)-1,3-propanediol tetrafluoroborate) carbonate (P[BMIMP][BF₄]C) 5, and poly(2,2-Bis(butylimidazolium methyl)-1,3-propanediol tetrafluoroborate) carbonate (P[BBIMP][BF₄]C) 6 is shown in Scheme 7. Polymer 4 is white, while 5 and 6 have a light yellow color. At room temperature, all polymers are easily crashed into fine powders. Polymer 4 is soluble in acetonitrile, and polymer 5 and 6 are soluble in chloroform. They all can be cast into membranes for CO₂separation using a solvent evaporation method.
The synthesis of the PET type polymers, poly(Bis(2-hydroxyethyl)dimethyl ammonium tetrafluoroborate) terephthalate (P[BHEDMA][BF4]T) 7, poly(2,2-Bis(methylimidazolium methyl)-1,3-propanediol tetrafluoroborate) terephthalate (P[BMIMP][BF₄]T) 8 and poly(2,2-Bis(butylimidazolium methyl)-1,3-propanediol tetrafluoroborate) terephthalate (P[BBIMP][BF₄]T) 9, is shown in Scheme 8. Triethylamine was added to the reaction system slowly to remove the hydrogen chloride. The obtained three polymers (7, 8 and 9) are all white powders. But the solubilities of them are not as good as those for the corresponding PC types because their phenyl groups increase the rigidity of the polymer chains greatly. Because they are only soluble in solvents with strong polarity and high boiling points, such as DMSO and DMF, it is difficult to fabricate them into membranes using the solvent evaporation method.

EXAMPLE 4

Poly(Ionic Liquid) Membranes for CO₂/CH₄and CO₂/N₂Separations

Poly(ionic liquid) grafted with polyethylene (PEG), for example P[VBTMA][BF₄]-g-PEG and P[MATMA][BF₄]-g-PEG [How were these “grafts” made?] were used to prepare membranes for CO₂/CH₄and CO₂/N₂separations at 35° C., 50° C. and 70° C., all at 40 psig. These materials were tested for permeability and selectivity. FIG. 16 shows the CO₂/CH₄selectivity. FIG. 17 shows that our graft copolymers have better properties than the previously studied representative polymers for CO₂/CH₄separation. FIG. 18 shows the selectivity of CO₂/N₂for both P[VBTMA][BF₄]-g-PEG and P[MATMA][BF₄]-g-PEG at 35° C., 50° C. and 70° C. FIG. 19 illustrates that both P[VBTMA][BF₄]-g-PEG and P[MATMA][BF₄]-g-PEG membranes exhibit better ideal separation performance than the representative polymers because the data lie well above the upper limit bound curve, particularly for P[MATMA][BF₄]-g-PEG 2000.
The foregoing description and drawings comprise illustrative embodiments of the present inventions. The foregoing embodiments and the methods described herein may vary based on the ability, experience, and preference of those skilled in the art. Merely listing the steps of the method in a certain order does not constitute any limitation on the order of the steps of the method. The foregoing description and drawings merely explain and illustrate the invention, and the invention is not limited thereto, except insofar as the claims are so limited. Those skilled in the art who have the disclosure before them will be able to make modifications and variations therein without departing from the scope of the invention.

REFERENCES

1. Azar, C.; Rodhe, H. Science 1997, 276, 1818-1819.
2. Ruether, J. A. FETC Programs for Reducing Greenhouse Gas Emissions. Report No. DOE/EFTC-98/1058, U.S. Department of Energy: Pittsburgh, Pa., 1999.
3. DOE/OS-FE. Carbon sequestration. State of the Science; Office of Science and Office of Fossil Energy; U.S. Department of Energy: Washington, D.C., 1999.
4. U.S. Department of Energy. Carbon Sequestration-Research and Development; 1999. http://www.fe.doe.gov/coal_power/sequestration/reports/rd/index.html.
5. White, C. M.; Strazisar, B. R.; Granite, E. J. Hoffman; Pennline, H. W. J. Air & Waste Manage. Assoc. 2003, 53: 645-715
6. Huddleston, J. G.; Willauer, H. D.; Swatloski, R. P.; Rogers, R. D. Chem Commun 1998, 16, 1765-1766.
7. Wasserscheid, P.; Keim, W. Angew Chem Int Ed 2000, 39, 3772-3789.
8. Welton, T. Chem Rev 1999, 99, 2071-2084.
9. Rogers, R. D. and Seddon, K. R. (ed), Ionic Liquids as Green Solvents: Progress and Prospects, American Chemical Society: Washington, D.C., 2003.
10. Ding, J.; Zhou, D.; Spinks, G.; Wallace, G; Forsyth, S.; Forsyth, M.; MacFarlane, D. Chem. Mater 2003; 15, 2392-2398.
11. Liang, C.; Yuan, C-Y.; Warmack, R. J.; Barnes, C. E. and Dai, S. Anal Chem 2002, 74, 2172-2176.
12. Pernak, J.; Czepukowicz, A.; Poz'niak, R. Ind Eng Chem Res 2001, 40, 2379-2383.
13. Blanchard, L. A.; Hancu, D.; Beckman, E. J.; Brennecke, J. F. Nature 1999, 399, 28-29.
14. Blanchard, L. A.; Gu, Z. Y.; Brennecke, J. F. J Phys Chem B 2001, 105, 2437-2444.
15. Blanchard, L.A.; Brennecke, J. F. Ind Eng Chem Res 2001, 40, 287-292.
16. Anthony, J. L.; Maginn, E. J.; Brennecke, J. F. J Phys Chem B 2002, 106, 7315-7320.
17. Kamps, A. P.-S.; Tuma, D.; Xia, J.; Maurer, G. J Chem Eng Data 2003, 48, 746-749.
18. Husson-Borg, P.; Majer, V.; Costa Gomes, M. F. J Chem Eng Data 2003, 48, 480-485.
19. Cadena, C.; Anthony, J. L.; Shah, J. K.; Morrow, T. I.; Brennecke, J. F. and Maginn, E. J. J Am Chem Soc 2004, 126, 5300-5308.
20. Scovazzo, P.; Camper, D.; Kieft, J.; Poshusta, J.; Koval, C.; Noble, R. D. Ind Eng Chem Res 2004, 43, 6855-6860.
21. Camper, D.; Scovazzo, P.; Koval, C.; Noble, R. D. Ind Eng Chem Res 2004, 43, 3049-3054.
22. Baltus, R. E.; Culbertson, B. H.; Dai, S.; Luo, H.; DePaoli, D. W. J Phys Chem B 2004, 108, 721-727
23. Bates, E. D.; Mayton, R. D.; Ntai, I.; Davis Jr., J. H. J Am Chem Soc 2002, 124, 926.
24. Scovazzo, P.; Kieft, J.; Finan, D. A.; Koval, C.; DuBois, D. L.; Noble, R. D. J Memb Sci 2004, 238, 57-63;
25. Scovazzo, P.; Visser, A. E.; Davis, J. H., Jr.; Rogers, R. D.; Koval, C. A.; DuBois, D. L.; Noble, R. D. ACS Symp Ser 2002, 818, 69-87;
26. Fortunato, R.; Afonso, C. A. M.; Reis, M. A. M.; Crespo, J. G. J Memb Sci 2004, 242, 197-209.
27. Ding, S.; Tang, H. Radosz, M.; Shen, Y. J Polym Sci Part A: Poly Chem 2004, 42, 5794-5801.
28. Tang, H.; Tang, J.;Radosz, M.; Shen, Y. J Polym Sci Part A: Poly Chem 2005, 43, 1432-1443.
29. Macedonia, M. D.; Moore, D. D. and Maginn, E. J. Langmuir 2000, 16, 3823-3834
30. Tang, J. B.; Sun, W. L.; Tang, H. D. Radosz, M.; Shen, Y. Chem. Commun. 2005, 3325-3327.

Claims

We claim:

1. A solid sorbent for separation of carbon dioxide from a stream of mixed gases containing carbon dioxide, comprising a polymer of a polymerized ionic liquid monomer wherein the ionic liquid is selected from the group consisting of:

(a) imidazolium-based ionic liquids, consisting of 1-[2-(methacryloyloxy)ethyl]-3-butyl-imidazolium tetrafluoroborate ([MABI][BF₄]), 1-(p-vinylbenzyl)-3-butyl-imidazolium tetrafluoroborate ([VBBI][BF_4l]), 1-(p-vinylbenzyl)-3-methyl-imidazolium tetrafluoroborate [VBMI][BF₄], 1-(p-vinylbenzyl)-3-butyl-imidazolium hexafluorophosphate [VBBI][PF₆], 1-(p-vinylbenzyl)-3-butyl-imidazolium o-benzoic sulphimide ([VBBI][Sac]), 1-(p-vinylbenzyl)-3-butyl-imidazolium trifluoromethane sulfonamide([VBBI][BF₄]), and (1-butylimidazolium-3)methyl-ethylene oxide ([BIEO][BF₄]);

(b) ammonium-based ionic liquids, consisting of (p-vinylbenzyl)trimethyl ammonium tetrafluoroborate ([VBTMA][BF₄]), (p-vinylbenzyl)triethyl ammonium tetrafluoroborate ([VBTEA][BF₄]), (p-vinylbenzyl)tributyl ammonium tetrafluoroborate ([VBTBA][BF₄]), 2-(methacryloyloxy)ethyltrimethylamnonium tetrafluoroborate ([MATMA][BF₄]), (p-vinylbenzyl)trimethyl ammonium hexafluorophosphate ([VBTMA][PF₆]), (p-vinylbenzyl)trimethyl ammonium o-benzoic sulphimide ([VBTMA][Sac]), and (p-vinylbenzyl)trimethyl ammonium trifluoromethane sulfonamide ([VBTMA][Tf₂N]);

(c) phosphonium-based ionic liquids, consisting of (p-vinylbenzyl)triethyl phosphonium tetrafluoroborate ([VBTEP][BF₄]), and (p-vinylbenzyl)triphenyl phosphonium tetrafluoroborate ([VBTPP][BF₄]);

(d) pyridinium-based ionic liquids, consisting of 1-(p-vinylbenzyl)pyridinium tetrafluoroborate ([VBP][BF₄]) and

(e) condensation polymerization ionic monomers, consisting of bis(2-hydroxyethyl)dimethyl ammonium tetrafluoroborate ([BHEDMA][BF₄]), 2,2-bis(methylimidazolium methyl)-1,3-propanediol tetrafluoroborate ([BMIMP][BF₄]), and 2,2-bis(butylimidazolium methyl)-1,3-propanediol tetrafluoroborate ([BBIMP][BF₄]).

2. A solid sorbent as defined in claim 1, further comprising an inorganic moiety.

3. A solid sorbent as defined in claim 1, further comprising a co-polymer.

4. A solid sorbent as defined in claim 1, wherein the polymerization is a polymerization method selected from the group consisting of radical polymerization and condensation polymerization.