US20120247841A1 - Coating on pdc/tsp cutter for accelerated leaching - Google Patents

Coating on pdc/tsp cutter for accelerated leaching Download PDF

Info

Publication number
US20120247841A1
US20120247841A1 US13/433,185 US201213433185A US2012247841A1 US 20120247841 A1 US20120247841 A1 US 20120247841A1 US 201213433185 A US201213433185 A US 201213433185A US 2012247841 A1 US2012247841 A1 US 2012247841A1
Authority
US
United States
Prior art keywords
cutting element
mask
substrate
diamond
pcd
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
US13/433,185
Other languages
English (en)
Inventor
Ted Tessitore
Anthony Griffo
Yuelin Shen
Youhe Zhang
Madapusi K. Keshavan
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Smith International Inc
Original Assignee
Smith International Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Smith International Inc filed Critical Smith International Inc
Priority to US13/433,185 priority Critical patent/US20120247841A1/en
Priority to GB1317169.9A priority patent/GB2505573A/en
Priority to PCT/US2012/031208 priority patent/WO2012135497A2/en
Priority to CN201280026392.8A priority patent/CN103582737B/zh
Assigned to SMITH INTERNATIONAL, INC. reassignment SMITH INTERNATIONAL, INC. ASSIGNMENT OF ASSIGNORS INTEREST (SEE DOCUMENT FOR DETAILS). Assignors: GRIFFO, ANTHONY, KESHAVAN, MADAPUSI K., SHEN, YUELIN, TESSITORE, Ted, ZHANG, YOUHE
Publication of US20120247841A1 publication Critical patent/US20120247841A1/en
Priority to US14/802,827 priority patent/US9776917B2/en
Abandoned legal-status Critical Current

Links

Images

Classifications

    • CCHEMISTRY; METALLURGY
    • C03GLASS; MINERAL OR SLAG WOOL
    • C03CCHEMICAL COMPOSITION OF GLASSES, GLAZES OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS MADE FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
    • C03C25/00Surface treatment of fibres or filaments made from glass, minerals or slags
    • C03C25/66Chemical treatment, e.g. leaching, acid or alkali treatment
    • C03C25/68Chemical treatment, e.g. leaching, acid or alkali treatment by etching
    • EFIXED CONSTRUCTIONS
    • E21EARTH OR ROCK DRILLING; MINING
    • E21BEARTH OR ROCK DRILLING; OBTAINING OIL, GAS, WATER, SOLUBLE OR MELTABLE MATERIALS OR A SLURRY OF MINERALS FROM WELLS
    • E21B10/00Drill bits
    • E21B10/46Drill bits characterised by wear resisting parts, e.g. diamond inserts
    • CCHEMISTRY; METALLURGY
    • C22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22CALLOYS
    • C22C1/00Making non-ferrous alloys
    • C22C1/10Alloys containing non-metals
    • C22C1/1094Alloys containing non-metals comprising an after-treatment
    • CCHEMISTRY; METALLURGY
    • C22METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22CALLOYS
    • C22C26/00Alloys containing diamond or cubic or wurtzitic boron nitride, fullerenes or carbon nanotubes
    • EFIXED CONSTRUCTIONS
    • E21EARTH OR ROCK DRILLING; MINING
    • E21BEARTH OR ROCK DRILLING; OBTAINING OIL, GAS, WATER, SOLUBLE OR MELTABLE MATERIALS OR A SLURRY OF MINERALS FROM WELLS
    • E21B10/00Drill bits
    • E21B10/46Drill bits characterised by wear resisting parts, e.g. diamond inserts
    • E21B10/54Drill bits characterised by wear resisting parts, e.g. diamond inserts the bit being of the rotary drag type, e.g. fork-type bits
    • EFIXED CONSTRUCTIONS
    • E21EARTH OR ROCK DRILLING; MINING
    • E21BEARTH OR ROCK DRILLING; OBTAINING OIL, GAS, WATER, SOLUBLE OR MELTABLE MATERIALS OR A SLURRY OF MINERALS FROM WELLS
    • E21B10/00Drill bits
    • E21B10/46Drill bits characterised by wear resisting parts, e.g. diamond inserts
    • E21B10/56Button-type inserts
    • E21B10/567Button-type inserts with preformed cutting elements mounted on a distinct support, e.g. polycrystalline inserts
    • BPERFORMING OPERATIONS; TRANSPORTING
    • B22CASTING; POWDER METALLURGY
    • B22FWORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER; APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
    • B22F3/00Manufacture of workpieces or articles from metallic powder characterised by the manner of compacting or sintering; Apparatus specially adapted therefor ; Presses and furnaces
    • B22F3/24After-treatment of workpieces or articles
    • B22F2003/241Chemical after-treatment on the surface
    • B22F2003/244Leaching

Definitions

  • Embodiments disclosed herein relate generally to polycrystalline diamond composites and cutting structures. More particularly, embodiments disclosed herein relate to methods of leaching polycrystalline diamond cutting elements.
  • PCD polycrystalline diamond
  • substrate material typically a sintered metal-carbide
  • PCD comprises a polycrystalline mass of diamonds (typically synthetic) that are bonded together to form an integral, tough, high-strength mass or lattice.
  • the resulting PCD structure produces enhanced properties of wear resistance and hardness, making PCD materials extremely useful in aggressive wear and cutting applications where high levels of wear resistance and hardness are desired.
  • a PDC cutting element may be formed by placing a cemented carbide substrate into the container of a press.
  • a mixture of diamond grains or diamond grains and catalyst binder is placed atop the substrate and treated under high pressure, high temperature conditions.
  • metal binder (often cobalt) migrates from the substrate and passes through the diamond grains to promote intergrowth between the diamond grains.
  • the diamond grains become bonded to each other to form the diamond layer, and the diamond layer is in turn bonded to the substrate.
  • the substrate often comprises a metal-carbide composite material, such as tungsten carbide.
  • the deposited diamond layer is often referred to as the “diamond table” or “abrasive layer.”
  • PCD includes 85-95% by volume diamond and a balance of the binder material, which is present in PCD within the interstices existing between the bonded diamond grains.
  • Binder materials that are typically used in forming PCD include Group VIII elements, with cobalt (Co) being the most common binder material used.
  • FIG. 1 shows a rotary drill bit 10 having a bit body 12 .
  • the lower face of the bit body 12 is formed with a plurality of blades 14 , which extend generally outwardly away from a central longitudinal axis of rotation 16 of the drill bit.
  • a plurality of PDC cutters 18 are disposed side by side along the length of each blade. The number of PDC cutters 18 carried by each blade may vary.
  • the PDC cutters 18 are individually brazed to a stud-like carrier (or substrate), which may be formed from tungsten carbide, and are received and secured within sockets in the respective blade.
  • a significant factor in determining the longevity of PDC cutters is the generation of heat at the cutter contact point, specifically at the exposed part of the PDC layer, caused by friction between the PCD and the work material. This heat causes thermal damage to the PCD in the form of cracks (due to differences in thermal expansion coefficients) which lead to spalling of the polycrystalline diamond layer, delamination between the polycrystalline diamond and substrate, and back conversion of the diamond to graphite causing rapid abrasive wear.
  • the thermal operating range of conventional PDC cutters is typically 700° C. or less.
  • conventional polycrystalline diamond is stable at temperatures of up to 700° C., after which observed increases in temperature may result in permanent damage to and structural failure of polycrystalline diamond.
  • This deterioration in polycrystalline diamond is due to the significant difference in the coefficient of thermal expansion of the binder material, cobalt, as compared to diamond.
  • cobalt the coefficient of thermal expansion of the binder material
  • the cobalt and the diamond lattice will expand at different rates, which may cause cracks to form in the diamond lattice structure and result in deterioration of the polycrystalline diamond.
  • thermal fatigue does not only occur at temperatures above 700° C. Rather, the differential expansion (between cobalt and diamond) even occurs at temperatures as low as 300-400° C., still causing thermal fatigue in the diamond body.
  • damage to polycrystalline diamond can also result from the loss of some diamond-to-diamond bonds (from the initiation of a graphitization process) leading to loss of microstructural integrity and strength loss.
  • strong acids may be used to “leach” the binder from the diamond lattice structure (either a thin volume or entire tablet) to at least reduce the damage experienced from heating diamond-binder composite at different rates upon heating.
  • a strong acid typically nitric acid or combinations of several strong acids (such as nitric and hydrofluoric acid) may be used to treat the diamond table, removing at least a portion of the co-catalyst from the PDC composite.
  • TSP thermally stable polycrystalline
  • TSP includes both of the above (i.e., partially and completely leached) compounds.
  • Interstitial volumes remaining after leaching may be reduced by either furthering consolidation or by filling the volume with a secondary material, such as by processes known in the art and described in U.S. Pat. No. 5,127,923, which is herein incorporated by reference in its entirety.
  • embodiments disclosed herein relate to a cutting element that includes a polycrystalline diamond layer having a cutting face and a diamond layer side surface, a substrate attached to the polycrystalline diamond layer, the substrate having a bottom surface and a substrate side surface, an interface between the diamond layer and the substrate, and a mask covering at least the bottom surface and the substrate side surface of the cutting element.
  • embodiments disclosed herein relate to a method for leaching a cutting element that includes providing a cutting element, the cutting element having a substrate and polycrystalline diamond layer attached to the substrate, masking at least the substrate portion of the cutting element with a mask, leaving an unmasked portion of the diamond layer of the cutting element, placing the masked cutting element in a leaching agent, wherein at least the unmasked portion of the cutting element contacts the leaching agent, and removing the masked cutting element from the leaching agent.
  • embodiments disclosed herein relate to a method of leaching a cutting element that includes providing a cutting element, the cutting element having a substrate and polycrystalline diamond layer attached to the substrate, fitting at least the substrate portion of the cutting element in a pre-formed mask, leaving an unmasked portion of the diamond layer of the cutting element, placing the cutting element in a leaching agent, wherein at least the unmasked portion of the cutting element contacts the leaching agent, and removing the cutting element from the leaching agent.
  • FIG. 1 is an illustration of a PCD drill bit.
  • FIG. 2 shows a PCD cutting element
  • FIG. 3 is a cross-sectional view of a masked PCD cutting element according to embodiments of the present disclosure.
  • FIGS. 4A-B show side views of masked PCD cutting elements according to embodiments of the present disclosure.
  • FIGS. 5A-B is an illustration of steps for forming a masked PCD cutting element according to embodiments of the present disclosure.
  • FIG. 6 is a cross-sectional view of a masked cutting element according to embodiments of the present disclosure.
  • Embodiments described herein relate to polycrystalline diamond cutting elements and to methods of leaching the same.
  • Polycrystalline diamond cutting elements of the present disclosure include a carbide substrate and a polycrystalline diamond layer attached thereon.
  • the methods of leaching described below include protecting the carbide substrate from the leaching process.
  • PCD refers to polycrystalline diamond that has been formed, at high pressure/high temperature (HPHT) conditions, through the use of a solvent metal catalyst, such as those included in Group VIII of the Periodic Table.
  • thermally stable polycrystalline diamond refers to intercrystalline bonded diamond that includes a volume or region that has been rendered substantially free of the solvent metal catalyst used to form PCD, or the solvent metal catalyst used to form PCD remains in the region of the diamond body but is otherwise reacted or rendered ineffective in its ability to adversely impact the bonded diamond at elevated temperatures as discussed above.
  • a PCD cutting element 20 has a polycrystalline diamond (PCD) layer 22 attached to a substrate 24 .
  • the substrate 24 has a bottom surface 25 and a substrate side surface 26 .
  • the PCD layer has a cutting face 27 and a diamond layer side surface 28 .
  • An interface 23 is formed between the PCD layer 22 and the substrate 24 .
  • the diamond layer side surface 28 and the substrate side surface 26 together form the outer surface of the PCD cutting element.
  • the outer surface of PCD cutting elements of the present disclosure may be referred herein to as the “outer side surface,” the “side surface,” the “outer circumferential surface,” or the like.
  • a PCD layer may be formed in a conventional manner, such as by HPHT sintering of “green” particles to create intercrystalline bonding between the particles.
  • HPHT processes can be found, for example, in U.S. Pat. Nos. 4,694,918; 5,370,195; and 4,525,178.
  • a metal catalyst such as cobalt or other Group VIII metals, may be included with the unsintered mass of crystalline particles to promote intercrystalline diamond-to-diamond bonding.
  • the catalyst material may be provided in the form of powder and mixed with the diamond grains, or may be infiltrated into the diamond grains during HPHT sintering.
  • An exemplary minimum temperature is about 1200° C. and an exemplary minimum pressure is about 35 kbars. Typical processing is at a pressure of about 45 kbar and 1300° C.
  • temperatures and pressures may be used, and the scope of the present invention is not limited to specifically referenced temperatures and pressures.
  • Diamond grains useful for forming PCD may include any type of diamond particle, including natural or synthetic diamond powders having a wide range of grain sizes.
  • such diamond powders may have an average grains size in the range from submicrometer in size to 100 micrometers, and from 1 to 80 micrometers in other embodiments.
  • the diamond powder may include grains having a mono- or multi-modal distribution.
  • Synthetic diamond powder is known to include small amounts of solvent metal catalyst material and other materials entrained within the diamond crystals themselves. Unlike synthetic diamond powder, natural diamond powder does not include such solvent metal catalyst material and other materials entrained within the diamond crystals. It is theorized that the inclusion of materials other than the solvent catalyst in the synthetic diamond powder can operate to impair or limit the extent to which the resulting PCD body can be rendered thermally stable, as these materials along with the solvent catalyst must also be removed or otherwise neutralized.
  • the diamond grain powder may be combined with or already includes a desired amount of catalyst material to facilitate desired intercrystalline diamond bonding during HPHT processing.
  • Suitable catalyst materials useful for forming the PCD body include those solvent metals selected from Group VIII of the Periodic Table, with cobalt (Co) being the most common, and mixtures or alloys of two or more of these materials.
  • the diamond grain powder and catalyst material mixture may comprise 85-95% by volume diamond grain powder and the remaining amount catalyst material.
  • the diamond grain powder can be used without adding a solvent metal catalyst in applications where the solvent metal catalyst can be provided by infiltration during HPHT processing from the adjacent substrate or adjacent other body to be bonded to the PCD body.
  • the diamond powder may be combined with the desired catalyst material in a reaction cell, and the reaction cell is then placed under processing conditions sufficient to cause the intercrystalline bonding between the diamond particles.
  • a selected substrate is loaded into the container adjacent the diamond powder mixture prior to HPHT processing.
  • the metal solvent catalyst needed for catalyzing intercrystalline bonding of the diamond may be provided by infiltration, in which case it may not be necessary to mix the diamond powder with a metal solvent catalyst prior to HPHT processing.
  • the catalyst material in the mixture melts and infiltrates the diamond grain powder to facilitate intercrystalline diamond bonding.
  • the catalyst material may migrate into the interstitial regions within the microstructure of the so-formed PCD body that exists between the diamond bonded grains. It should be noted that if too much additional non-diamond material is present in the powdered mass of crystalline particles, appreciable intercrystalline bonding is prevented during the sintering process. Such a sintered material where appreciable intercrystalline bonding has not occurred is not within the definition of PCD.
  • a PCD body may be formed that has, in one embodiment, at least about 80 percent by volume diamond, with the remaining balance of the interstitial regions between the diamond grains occupied by the catalyst material.
  • such diamond content may comprise at least 85 percent by volume of the formed PCD body, and at least 90 percent by volume in yet another embodiment.
  • other diamond densities or gradients of diamond densities
  • the PCD bodies being leached in accordance with the present disclosure include what is frequently referred to in the art as “high density” PCD, which refers to a diamond body having a diamond content of at least 90 percent by volume.
  • the high density PCD used in the method of the present disclosure may have a density of at least 92 percent by volume up to 97 percent by volume.
  • the leaching time and potential inability to effectively leach similarly increases.
  • the PCD layer may be attached to a substrate during the formation of the PCD layer or subsequent to forming the PCD layer.
  • Embodiments disclosed herein may have carbide substrate such as, for example, a cemented tungsten carbide substrate formed from tungsten carbide particles dispersed in a binder metal matrix, such as iron, nickel, or cobalt.
  • a mask may then be applied to the cutting element such that the mask covers at least the entire outer surface of the substrate.
  • the mask may also cover a portion of the outer side surface of the diamond layer.
  • a “mask” refers to a masking coating, a pre-formed mask or an institute mask that coats the outer surface of a portion of a cutting element to protect the masked portion from a leaching environment.
  • the term “mask” may be interchangeable with the term “masking coating” or “coating.”
  • the term “mask” may be interchangeable with the term “pre-formed mask” or “institute mask.”
  • a PCD cutter 30 has a PCD layer 32 attached to a substrate 34 .
  • the substrate 34 has a bottom surface 35 and a substrate side surface 36 .
  • the PCD layer has a cutting face 37 and a diamond layer side surface 38 .
  • An interface 33 is formed between the PCD layer 32 and the substrate 34 .
  • the substrate side surface 36 and the diamond layer side surface 38 form the outer circumferential surface of the PCD cutter 30 .
  • the intersection of the diamond layer side surface 38 and the cutting face 37 forms a cutting edge 39 , which in this case is a bevel.
  • a mask 31 is applied to the outer surface of the PCD cutter 30 such that it covers the entire bottom surface 35 of the substrate and extends a distance D from the bottom surface 35 up the outer circumferential surface of the PCD cutter 30 toward the cutting face 37 to cover the entire substrate side surface 36 and a portion of the diamond layer side surface 38 .
  • a mask may extend a uniform distance around the outer side surface of a cutting element from the bottom surface.
  • a mask may be applied to the outer surface of a cutting element such that the mask extends a non-uniform distance around the outer circumferential surface of the cutting element from the bottom surface toward the cutting face of the cutting element.
  • masked cutting elements are shown as having a mask extending up the side surface of the cutting elements.
  • the mask 41 extends the same distance D around the outer side surface of a cutting element 40 such that the mask has a planar top end 41 a that is parallel with the cutting face 47 .
  • FIG. 4A the mask 41 extends the same distance D around the outer side surface of a cutting element 40 such that the mask has a planar top end 41 a that is parallel with the cutting face 47 .
  • the mask 41 extends up the side surface of a cutting element 40 to varying but continuous distances D 1 , D 2 , etc. along the outer circumferential surface of the cutting element 40 such that the mask 41 has a slanted top end 41 a (i.e., not parallel to the cutting face). It is within the scope of this disclosure that the top of the mask may form other non-planar, or non-continuous shapes.
  • the unmasked portion of the cutting element may be designed to have a particular shape or depth (from the cutting face) such that upon leaching the unmasked portion, residual stresses in the PCD cutting element are minimized.
  • a mask may be applied to a cutting element by applying a masking coating to the outer surface of a cutting element.
  • a masking coating may include diamond-like carbon (“DLC”) material.
  • DLC diamond-like carbon
  • the term “DLC” or diamond-like carbon” refers to an amorphous carbonaceous coating that possesses a significant amount of (if not all) sp 3 hybridization, with a balance of sp 2 hybridization. While diamond is traditionally formed in a cubic crystal structure, DLC is amorphous due to the mixture of cubic and hexagonal lattice structure (mixed layer by layer) formed as a result of a high energy process (i.e., PE-CVD, among others).
  • DLC can contain pure sp 3 carbon and/or a mixture of sp 3 and sp 2 carbon, it has no long range crystalline order and is referred to as “amorphous.”
  • DLC masking coatings may be applied to the outer surface of a cutting element by chemical vapor deposition (CVD) methods, including plasma enhanced chemical vapor deposition (PE-CVD), and hallow cathode PE-CVD, for example.
  • CVD chemical vapor deposition
  • PE-CVD plasma enhanced chemical vapor deposition
  • hallow cathode PE-CVD hallow cathode PE-CVD
  • a carbon precursor such as methane, acetylene, butane, toluene, etc
  • properties of the coating may be tailored by adjusting the sp 3 (diamond), sp 2 (graphite) and sp 1 (linear) bonding hybridization ratios in the coating, by varying the source gas and hydrogen content. For example, the highest sp 3 ratio (most diamond-like) is obtained by methane, but this also may produce a lower deposition rate compared to higher carbon molecules and also a higher compressive stress, limiting film thickness to approximately 5000 Angstroms.
  • dopants e.g., silicon or silicon oxide
  • An organic-based precursor such as hexemethyldisiloxane can be mixed with the hydrocarbon precursor(s) to introduce these dopants.
  • multiple layers of coatings may be deposited.
  • the deposition process can be modified by deposition of a thin methane-based layer, followed by the use of a higher deposition rate, lower stress precursors such as toluene, or by higher energy ion bombardment to increase adhesion and reduce stress.
  • several layers, including DLC and non-DLC layers, may be deposited on the cutting element. For example, multiple layers may be applied to the cutting element under a DLC top layer to promote adhesion.
  • masking coatings according to embodiments of the present disclosure may include a wide range of inert materials that are able to sustain strong acid attack under elevated temperature and pressure.
  • masking coatings of the present disclosure may include chemical resistant air dry inks, chemical resistant UV cured inks, Teflon, and microwave cured materials.
  • Masking coatings made of such materials may be applied by sputter coating, physical vapor deposition, CVD, or other spray coating methods, for example.
  • a first layer may coat the majority of the cutting element and a second layer may coat only the interface area, or potential gaps, between the cutting element and the first layer.
  • a mask coating 61 may have potential gaps, or crevices, at the mask top end 61 a , between the mask 61 and the cutting element 60 .
  • a second layer 68 of coating or masking material may be applied to the top end 61 a of the mask in order to seal any potential gaps.
  • the first layer may offer processing protection, while the second layer may further prevent processing materials from invading the protected area.
  • the second layer may be made of the same material or a different type of material as required to provide an adequate seal at the interface area.
  • a first layer may be applied to coat only the protected area of the cutting element and the second layer may be applied to seal any potential voids or holes in the first layer, i.e., the second layer may be applied over the first layer.
  • the masking coating deposited may depend on the number of layers, but may generally be less than 200 microns.
  • the masking coating may be applied so that the mask has a thickness ranging from about 1 micron to about 200 microns.
  • the masking coating may have a thickness ranging from about 0.5 microns to about 20 microns. While thinner coatings may reduce cost and the likelihood of spalling, defects inside the coating may cause leaching acid to leak in. Thicker coatings may improve continuity of the coating and prevent such acid leakage.
  • the thickness of the masking coating may depend on, for example, the type of coating and the surface roughness of the surface to be coated.
  • a protective seal is formed around the masked portion of the cutting element, thereby shielding it from a leaching environment.
  • the leaching environment while beneficial in forming TSP in a cutting element, may be detrimental to the substrate portion of the cutting element.
  • the leaching agent may remove or react with the binder material that holds the substrate together.
  • a pre-formed mask may be fitted around a PCD cutting element to protect at least the substrate of a PCD cutting element during a leaching process.
  • a “pre-formed mask” refers to a material that has been extruded into the shape of a cup, into which a cutting element snugly fits.
  • a pre-formed mask may also be referred to as a pod, shell, casing, or other like terminology.
  • a pre-formed mask differs from the masking coating described above in that the pre-formed mask holds its shape (i.e., holds the shape of a cup).
  • a pre-formed mask may have special properties that allow the pre-formed mask to reduce in size or shrink in the form of an encapsulating device around a cutting element by use of heat, ultra violet radiation, microwave, etc.
  • a pre-formed mask covers, or coats, the outer surface of at least the substrate of a cutting element to protect it from a leaching environment.
  • a pre-formed mask may be formed by extruding polyvinyl chloride or other suitable materials, such as any acid-proof material, a high temperature material, and/or plastics such as polyvinylidene fluoride, into the shape of a cup.
  • Methods of extruding a pre-formed mask include any that are known to those skilled in the art, including, for example, thermoforming, tubing extruding, or blown film extrusion methods.
  • a PCD cutting element masked with a pre-formed mask is shown.
  • a pre-formed mask 51 is extruded into a cup shape having a bottom 51 c and a cylindrically-shaped wall 51 b extending perpendicular from the bottom 51 c .
  • the wall 51 b has a thickness t and a height H.
  • a pre-formed mask may have a wall thickness t. The thickness t may be determined based on the ability of the pre-formed mask material to resist process chemical attack over time and on the temperature of the process and temperature limitations of the pre-formed mask material.
  • a PCD cutter 50 having a polycrystalline diamond layer 52 attached to a substrate 54 may then be fitted into the pre-formed mask 51 by inserting the cutter 50 , substrate 54 end first, through the top end 51 a of the pre-formed mask 51 .
  • the pre-formed mask 51 may be made so that the inner diameter is only slightly larger than the diameter of the cutter 50 , thereby providing a snug fit between the pre-formed mask 51 and the cutter 50 .
  • the pre-formed mask 51 covers at least the substrate and extends over a portion of the diamond layer 52 .
  • a pre-formed mask may have a wall height H that covers only the substrate. In other embodiments, the wall height may extend over the substrate outer surface to about 1 to 1.5 mm from the cutting surface of the diamond layer.
  • a pre-formed mask may be fitted around a cutting element by inserting the cutting element into a pre-formed mask, placing the assembly in a vacuum, and applying heat to the pre-formed mask to tighten the pre-formed mask around the cutting element. It should be appreciated that depending on the type of material used to make the pre-formed mask, different vacuum pressures and temperatures may be used to shrink-fit the pre-formed mask to the cutting element. A sealing process, as described above, may then be used to seal the top part of the pre-formed mask to the outer surface of the cutting element.
  • an institute mask may be formed around a PCD cutting element to protect at least the substrate of a PCD cutting element during a leaching process.
  • an “institute mask” refers to a material that encases one or more cutting elements by injection molding or similar practices known in the art.
  • An institute mask may be made of the protective mask materials described above, such as plastics, acid-proof materials, and/or high temperature materials. Methods of encasing one or more cutting elements with an institute mask may include, for example, enclosing one or more cutting elements into a single block or fixture.
  • a protective material used to form the institute mask may then be injected into the block or fixture around the one or more cutting elements to encase the cutting elements, thereby forming the institute mask.
  • one or more cutting elements may be coated with a protective material during a single process, thereby reducing processing time.
  • the masked cutting element may be subjected to a leaching process.
  • the seal formed between the mask and the PCD cutting element prevent leaching agents from contacting, and thus removing material from the part of the cutting element protected by the mask.
  • the catalyst material is removed only from the unmasked portion of the PCD cutting element, which includes at least a portion of the PCD layer.
  • the term “removed” refers to the reduced presence of catalyst material in the PCD layer, and is understood to mean that a substantial portion of the catalyst material no longer resides in the leached PCD. However, one skilled in the art would appreciate that trace amounts of catalyst material may still remain in the microstructure of the leached PCD layer within the interstitial regions and/or adhered to the surface of the diamond grains. Alternatively, rather than actually removing the catalyst material from the leached portion of the PCD layer, the selected region of the PCD layer can be rendered thermally stable by treating the catalyst material in a manner that reduces or eliminates the potential for the catalyst material to adversely impact the intercrystalline bonded diamond at elevated temperatures.
  • the catalyst material may be combined chemically with another material to cause it to no longer act as a catalyst material (or to have less thermal mismatch with diamond), or can be transformed into another material that again causes it to no longer act as a catalyst material (or to have less thermal mismatch with diamond).
  • the terms “removing substantially all” or “substantially free” is intended to cover the different methods in which the catalyst material can be treated to no longer adversely impact the intercrystalline diamond in the leached portion of the PCD layer with increasing temperature.
  • the quantity of the catalyst material remaining in the PCD microstructure after the PCD layer has been subjected to a leaching treatment may vary, for example, on factors such as the treatment conditions, including treatment time. Further, one skilled in the art would appreciate that it may be acceptable or desired in certain applications to allow a small amount of catalyst material to stay in the leached area of the PCD layer.
  • the leached area of the PCD layer may include up to 1-2 percent by weight of the catalyst material.
  • the amount of residual catalyst present in the leached area of a PCD layer may depend on the diamond density of the material and the thickness of the area leached.
  • a conventional leaching process involves the exposure of an object to be leached with a leaching agent, such as described in U.S. Pat. No. 4,224,380, which is herein incorporated by reference in its entirety.
  • the leaching agent may be a weak, strong, or mixtures of acids.
  • the leaching agent may be a caustic material such as NaOH or KOH.
  • Suitable acids may include, for example, nitric acid, hydrofluoric acid, hydrochloric acid, sulfuric acid, phosphoric acid, or perchloric acid, or combinations of these acids.
  • other acidic and basic leaching agents may be used as desired. Those having ordinary skill in the art will appreciate that the molarity of the leaching agent may be adjusted depending on the time desired to leach, concerns about hazards, etc.
  • PCD cutting elements that have been masked according to embodiments of the present disclosure may be leached by conventional means.
  • a masked PCD cutting element may be placed in a leaching agent bath, wherein the masked PCD cutting element is placed in the bath container with the PCD layer facing the bottom of the container so that the PCD layer may be fully immersed in the leaching agent.
  • Other exemplary leaching methods may also include subjecting the PCD cutting element to increased pressures and/or increased temperatures in addition to immersing the PCD layer in a leaching agent.
  • a masked PCD cutting element may be held in place during the leaching process to ensure more controlled exposure of the PCD layer to the leaching bath.
  • a masked PCD cutting element may be held in place above a leaching agent bath such that a specific amount of the PCD layer (e.g., a uniform distance from the cutting face of the PCD layer) is immersed in the leaching agent.
  • Means of holding a masked PCD cutting element in place during the leaching process may include using a magnetic capturing device.
  • a masked PCD cutting element according to embodiments of the present disclosure may be held by a magnetic capturing device so that the area immersed in a leaching agent bath includes the distance of the desired leaching depth.
  • the desired leaching depth may range from about 1,000 microns to about 2 ⁇ 3 of the diamond table thickness from the cutting face of the PCD layer. In other embodiments, the desired leaching depth may range from about 600 microns to about 800 microns.
  • a magnetic capturing device may be a fixture, form, frame or other shape that has strong magnets imbedded within it that may be used to attract and hold cutting elements, once coated or masked, in place during the chemical process.
  • the protected cutting elements may be held in such a manner as to suspend them in a liquid chemical or otherwise held and exposed to a vapor or mist chemical for processing.
  • the use of a strong magnet may also be used to fabricate a fixture or device for holding the cutting element during application, curing, etc. of a mask and then again during the mask removal process.
  • the magnets may be protected by the device casing or by other means from the processing environments, including during applying a mask, leaching, and removing a mask.
  • masks upon leaching an unmasked portion of a cutting element, may be removed by thermal, mechanical, or other processes. Processes that will cause the mask materials to breakdown or weaken may be used to remove the mask, which may be chosen based on the time, cost, and susceptibility of the mask material to break down. For example, according to some embodiments of the present disclosure, masks may be removed by grit blasting or grinding in order to break the bond between the surface of the cutting element and the mask.
  • leaching a masked PCD cutting element by leaching a masked PCD cutting element according to embodiments of the present disclosure, greater control may be exercised over the size and shape of the PCD cutting element that is leached.
  • partially leached prior art PCD cutting elements are typically limited to having a planar interface between the portion of PCD that is exposed to a leaching agent and the remaining portion of the PCD cutting element.
  • embodiments of the present disclosure may have curved or other non-planar unmasked sections of the PCD cutting element to be leached.
  • higher stress regions of a PCD cutting element may be targeted and selectively leached according to embodiments disclosed herein.
  • the DLC mask provides resistance to leaching acids and to increased processing temperatures and pressures, while also being able to form a strong bond with the cutting element.

Landscapes

  • Engineering & Computer Science (AREA)
  • Chemical & Material Sciences (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Life Sciences & Earth Sciences (AREA)
  • Organic Chemistry (AREA)
  • Geology (AREA)
  • Mining & Mineral Resources (AREA)
  • Metallurgy (AREA)
  • General Life Sciences & Earth Sciences (AREA)
  • Geochemistry & Mineralogy (AREA)
  • Fluid Mechanics (AREA)
  • Environmental & Geological Engineering (AREA)
  • Physics & Mathematics (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • General Chemical & Material Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Earth Drilling (AREA)
  • Light Receiving Elements (AREA)
  • Carbon And Carbon Compounds (AREA)
US13/433,185 2011-03-29 2012-03-28 Coating on pdc/tsp cutter for accelerated leaching Abandoned US20120247841A1 (en)

Priority Applications (5)

Application Number Priority Date Filing Date Title
US13/433,185 US20120247841A1 (en) 2011-03-29 2012-03-28 Coating on pdc/tsp cutter for accelerated leaching
GB1317169.9A GB2505573A (en) 2011-03-29 2012-03-29 Coating on PDC/TSP cutter for accelerated leaching
PCT/US2012/031208 WO2012135497A2 (en) 2011-03-29 2012-03-29 Coating on pdc/tsp cutter for accelerated leaching
CN201280026392.8A CN103582737B (zh) 2011-03-29 2012-03-29 切割元件以及用于浸滤切割元件的方法
US14/802,827 US9776917B2 (en) 2011-03-29 2015-07-17 Coating on PDC/TSP cutter for accelerated leaching

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US201161468849P 2011-03-29 2011-03-29
US13/433,185 US20120247841A1 (en) 2011-03-29 2012-03-28 Coating on pdc/tsp cutter for accelerated leaching

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US14/802,827 Division US9776917B2 (en) 2011-03-29 2015-07-17 Coating on PDC/TSP cutter for accelerated leaching

Publications (1)

Publication Number Publication Date
US20120247841A1 true US20120247841A1 (en) 2012-10-04

Family

ID=46925768

Family Applications (2)

Application Number Title Priority Date Filing Date
US13/433,185 Abandoned US20120247841A1 (en) 2011-03-29 2012-03-28 Coating on pdc/tsp cutter for accelerated leaching
US14/802,827 Active 2032-08-21 US9776917B2 (en) 2011-03-29 2015-07-17 Coating on PDC/TSP cutter for accelerated leaching

Family Applications After (1)

Application Number Title Priority Date Filing Date
US14/802,827 Active 2032-08-21 US9776917B2 (en) 2011-03-29 2015-07-17 Coating on PDC/TSP cutter for accelerated leaching

Country Status (4)

Country Link
US (2) US20120247841A1 (zh)
CN (1) CN103582737B (zh)
GB (1) GB2505573A (zh)
WO (1) WO2012135497A2 (zh)

Cited By (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2015006696A1 (en) * 2013-07-12 2015-01-15 Smith International, Inc. Cutter protection during leaching process
GB2519669A (en) * 2013-10-22 2015-04-29 Element Six Ltd A seal for a support structure for a body of polycrystalline diamond material during processing and support structure comprising same
US20150298292A1 (en) * 2012-11-05 2015-10-22 Element Six Abrasives S.A. A polycrystalline super hard construction and a method for making same
US9227302B1 (en) 2013-01-28 2016-01-05 Us Synthetic Corporation Overmolded protective leaching mask assemblies and methods of use
US9598908B2 (en) 2013-12-16 2017-03-21 Diamond Innovations, Inc Multilayer coating process protecting the substrate of thermally stable polycrystalline diamond cutter
US9789587B1 (en) * 2013-12-16 2017-10-17 Us Synthetic Corporation Leaching assemblies, systems, and methods for processing superabrasive elements
US10655398B2 (en) 2015-06-26 2020-05-19 Halliburton Energy Services, Inc. Attachment of TSP diamond ring using brazing and mechanical locking
US11014157B2 (en) 2014-12-17 2021-05-25 Schlumberger Technology Corporation Solid PCD with transition layers to accelerate full leaching of catalyst
US11192218B1 (en) * 2012-11-21 2021-12-07 Us Synthetic Corporation Methods of processing a polycrystalline diamond element

Families Citing this family (16)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2016085449A1 (en) 2014-11-24 2016-06-02 Halliburton Energy Services, Inc. Determining the leaching profile of a cutter on a drilling tool
CN104594813A (zh) * 2015-01-15 2015-05-06 河南晶锐超硬材料有限公司 一种聚晶金刚石复合片及处理方法
CN107236935B (zh) * 2017-04-28 2019-05-14 同济大学 一种在聚晶金刚石复合片上沉积cvd金刚石涂层的方法
US10465775B1 (en) 2018-07-30 2019-11-05 XR Downhole, LLC Cam follower with polycrystalline diamond engagement element
US10738821B2 (en) 2018-07-30 2020-08-11 XR Downhole, LLC Polycrystalline diamond radial bearing
US11054000B2 (en) 2018-07-30 2021-07-06 Pi Tech Innovations Llc Polycrystalline diamond power transmission surfaces
US11035407B2 (en) 2018-07-30 2021-06-15 XR Downhole, LLC Material treatments for diamond-on-diamond reactive material bearing engagements
US11371556B2 (en) 2018-07-30 2022-06-28 Xr Reserve Llc Polycrystalline diamond linear bearings
US11014759B2 (en) 2018-07-30 2021-05-25 XR Downhole, LLC Roller ball assembly with superhard elements
US11286985B2 (en) 2018-07-30 2022-03-29 Xr Downhole Llc Polycrystalline diamond bearings for rotating machinery with compliance
US11187040B2 (en) 2018-07-30 2021-11-30 XR Downhole, LLC Downhole drilling tool with a polycrystalline diamond bearing
US11603715B2 (en) 2018-08-02 2023-03-14 Xr Reserve Llc Sucker rod couplings and tool joints with polycrystalline diamond elements
CA3107538A1 (en) 2018-08-02 2020-02-06 XR Downhole, LLC Polycrystalline diamond tubular protection
US11614126B2 (en) 2020-05-29 2023-03-28 Pi Tech Innovations Llc Joints with diamond bearing surfaces
US11655850B2 (en) 2020-11-09 2023-05-23 Pi Tech Innovations Llc Continuous diamond surface bearings for sliding engagement with metal surfaces
US11794290B2 (en) * 2021-01-24 2023-10-24 Cnpc Usa Corporation Method for forming cutters

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4976324A (en) * 1989-09-22 1990-12-11 Baker Hughes Incorporated Drill bit having diamond film cutting surface
US5188900A (en) * 1989-10-18 1993-02-23 Dow Corning Corporation Substrates having an abrasion-resistant coating formed thereon

Family Cites Families (16)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4104344A (en) 1975-09-12 1978-08-01 Brigham Young University High thermal conductivity substrate
US4288248A (en) 1978-03-28 1981-09-08 General Electric Company Temperature resistant abrasive compact and method for making same
US4224380A (en) 1978-03-28 1980-09-23 General Electric Company Temperature resistant abrasive compact and method for making same
US4525178A (en) 1984-04-16 1985-06-25 Megadiamond Industries, Inc. Composite polycrystalline diamond
US5127923A (en) 1985-01-10 1992-07-07 U.S. Synthetic Corporation Composite abrasive compact having high thermal stability
US4694918A (en) 1985-04-29 1987-09-22 Smith International, Inc. Rock bit with diamond tip inserts
US5370195A (en) 1993-09-20 1994-12-06 Smith International, Inc. Drill bit inserts enhanced with polycrystalline diamond
US20070169419A1 (en) * 2006-01-26 2007-07-26 Ulterra Drilling Technologies, Inc. Sonochemical leaching of polycrystalline diamond
US7998573B2 (en) * 2006-12-21 2011-08-16 Us Synthetic Corporation Superabrasive compact including diamond-silicon carbide composite, methods of fabrication thereof, and applications therefor
US7757792B2 (en) * 2008-07-18 2010-07-20 Omni Ip Ltd Method and apparatus for selectively leaching portions of PDC cutters already mounted in drill bits
US8261841B2 (en) * 2009-02-17 2012-09-11 Exxonmobil Research And Engineering Company Coated oil and gas well production devices
CA2683260A1 (en) * 2008-10-20 2010-04-20 Smith International, Inc. Techniques and materials for the accelerated removal of catalyst material from diamond bodies
US8662209B2 (en) * 2009-03-27 2014-03-04 Varel International, Ind., L.P. Backfilled polycrystalline diamond cutter with high thermal conductivity
US9352447B2 (en) * 2009-09-08 2016-05-31 Us Synthetic Corporation Superabrasive elements and methods for processing and manufacturing the same using protective layers
CN101787530B (zh) * 2010-03-01 2011-06-29 南京航空航天大学 SiC先驱体法制备金刚石涂层的方法
EP2407629B1 (de) * 2010-07-16 2012-12-19 BAUER Maschinen GmbH Bohrvorrichtung und Bohrverfahren

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4976324A (en) * 1989-09-22 1990-12-11 Baker Hughes Incorporated Drill bit having diamond film cutting surface
US5188900A (en) * 1989-10-18 1993-02-23 Dow Corning Corporation Substrates having an abrasion-resistant coating formed thereon

Cited By (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20150298292A1 (en) * 2012-11-05 2015-10-22 Element Six Abrasives S.A. A polycrystalline super hard construction and a method for making same
US11192218B1 (en) * 2012-11-21 2021-12-07 Us Synthetic Corporation Methods of processing a polycrystalline diamond element
US9227302B1 (en) 2013-01-28 2016-01-05 Us Synthetic Corporation Overmolded protective leaching mask assemblies and methods of use
US10391613B1 (en) 2013-01-28 2019-08-27 Us Synthetic Corporation Protective leaching mask assemblies and methods of use
US11541509B1 (en) 2013-01-28 2023-01-03 Us Synthetic Corporation Protective leaching mask assemblies and methods of use
WO2015006696A1 (en) * 2013-07-12 2015-01-15 Smith International, Inc. Cutter protection during leaching process
GB2519669A (en) * 2013-10-22 2015-04-29 Element Six Ltd A seal for a support structure for a body of polycrystalline diamond material during processing and support structure comprising same
US9598908B2 (en) 2013-12-16 2017-03-21 Diamond Innovations, Inc Multilayer coating process protecting the substrate of thermally stable polycrystalline diamond cutter
US9789587B1 (en) * 2013-12-16 2017-10-17 Us Synthetic Corporation Leaching assemblies, systems, and methods for processing superabrasive elements
US11014157B2 (en) 2014-12-17 2021-05-25 Schlumberger Technology Corporation Solid PCD with transition layers to accelerate full leaching of catalyst
US10655398B2 (en) 2015-06-26 2020-05-19 Halliburton Energy Services, Inc. Attachment of TSP diamond ring using brazing and mechanical locking

Also Published As

Publication number Publication date
CN103582737A (zh) 2014-02-12
WO2012135497A2 (en) 2012-10-04
US20150321952A1 (en) 2015-11-12
US9776917B2 (en) 2017-10-03
CN103582737B (zh) 2016-10-05
GB201317169D0 (en) 2013-11-06
GB2505573A (en) 2014-03-05
WO2012135497A3 (en) 2013-02-28

Similar Documents

Publication Publication Date Title
US9776917B2 (en) Coating on PDC/TSP cutter for accelerated leaching
US8932377B2 (en) Deep leach pressure vessel for shear cutters
US20100108403A1 (en) Surface coatings on cutting elements
US8328891B2 (en) Methods of forming thermally stable polycrystalline diamond cutters
US8702825B2 (en) Composite cutter substrate to mitigate residual stress
US20170246730A1 (en) Interface Modification of Polycrystalline Diamond Compact
US20110232200A1 (en) Manufacture of thermally stable cutting elements
US20100012389A1 (en) Methods of forming polycrystalline diamond cutters
US20130168159A1 (en) Solid pcd cutter
EP3399136B1 (en) Methods of forming polycrystalline diamond compacts
US11370664B1 (en) Leaching assemblies, systems, and methods for processing superabrasive elements
US20140352228A1 (en) Method of processing polycrystalline diamond material
US20150014067A1 (en) Cutter protection during leaching process
US9138865B2 (en) Method to improve efficiency of PCD leaching
US9789587B1 (en) Leaching assemblies, systems, and methods for processing superabrasive elements
US20140144712A1 (en) Eruption control in thermally stable pcd products by the addition of transition metal carbide
US10166523B2 (en) Support structure for a body of polycrystalline diamond material during leaching
WO2017075626A1 (en) Eruption minimization in thermally stable pcd products
WO2015059196A1 (en) A seal for a support structure for a body of polycrystalline diamond material during processing and support structure comprising same
GB2512776A (en) Composite cutter substrate to mitigate residual stress

Legal Events

Date Code Title Description
AS Assignment

Owner name: SMITH INTERNATIONAL, INC., TEXAS

Free format text: ASSIGNMENT OF ASSIGNORS INTEREST;ASSIGNORS:TESSITORE, TED;GRIFFO, ANTHONY;SHEN, YUELIN;AND OTHERS;SIGNING DATES FROM 20120509 TO 20120510;REEL/FRAME:028385/0116

STCB Information on status: application discontinuation

Free format text: ABANDONED -- FAILURE TO RESPOND TO AN OFFICE ACTION