US20120171100A1 - Process for hydrogenation of a silicon tetrahalide and silicon to trihalosilane - Google Patents
Process for hydrogenation of a silicon tetrahalide and silicon to trihalosilane Download PDFInfo
- Publication number
- US20120171100A1 US20120171100A1 US13/385,850 US201213385850A US2012171100A1 US 20120171100 A1 US20120171100 A1 US 20120171100A1 US 201213385850 A US201213385850 A US 201213385850A US 2012171100 A1 US2012171100 A1 US 2012171100A1
- Authority
- US
- United States
- Prior art keywords
- silicon
- bed
- vessel
- particles
- gases
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A process of hydrogenation of a silicon tetrahalide and silicon to a trihalosilane comprising: providing a vessel with at least one inlet and one outlet with a plurality of silicon particles located in a bed inside the vessel and feeding a mixture of gases consisting primarily of a silicon tetrahalide and hydrogen. A calculational procedure is provided where the flow rate of the gases and the incoming size of the silicon particulates are chosen so that at least 90% of the volume of the bed is free of bubbles after allowance for decrease in particle size due to the reaction and attrition resulting in a higher yield of the trihalosilane.
Description
- This is a Divisional of application Ser. No 12/291,115, filed Nov. 05, 2008, now U.S. Pat. No. ______, issued ______, 2012.
- This invention relates generally to the field of high purity silicon production and more specifically to an apparatus and process for hydrogenation of a silicon tetrahalide and silicon to trihalosilane.
- Trihalosilanes such as SiHCl3 and SiHBr3 were first made by the reaction of silicon with the respective hydrogen halide, HCl or HBr, at a temperature of approximately 350° C. and at approximately atmospheric pressure. Yields from this reaction are typically very high, the literature showing yields in excess of 90%, with the remainder being silicon tetrahalide. The trihalosilane most commonly used is trichlorosilane which is purified and decomposed to form very pure silicon. This decomposition reaction also forms the silicon tetrahalide which thus builds up in the process. Various measure have been taken to minimize the production of silicon tetrahalide such as recycling the tetrahalide and using a large excess of hydrogen in the decomposition reactor. The excess tetrahalide has also been oxidized to amorphous silica with the resulting halogen gases being scrubbed. A more recent innovation, based on research by DOE/JPL and described in Breneman U.S. Pat. No. 4,676,967, converts the excess silicon tetrahalide to the trihalosilane by reacting it with hydrogen and silicon at high temperature and pressure in the presence of a copper catalyst.
- The prior hydrogenation technology disclosed in Breneman U.S. Pat. No. 4,676,967 conducts the reaction between silicon, silicon tetrachloride and hydrogen at about 400° C.-600° C. and between 300 and 600 psi in a fluidized bed reactor containing a distribution means above a mixing plenum. In commercial embodiments of the above patent the inlet gas streams of silicon tetrachloride and hydrogen are preferentially heated separately to different temperatures and pressures then mixed in the mixing plenum before passing through the distribution means to form bubbles which contact and fluidize the finely divided silicon. The hydrogen is heated to 500° C. at 325 psig while the silicon tetrachloride is heated to 500° C. at 575 psig, which is above the 530 psig critical pressure of silicon tetrachloride, and then depressurized to 325 psig on mixing with the hydrogen.
- The commercial reactors designed according to Breneman have a lesser yield than smaller scale laboratory tests, such as the ones by Ingle, discussed in “Kinetics of the Hydrogenation of Silicon Tetrachloride, W. Ingle and M. Peffley, J. Electrochem Soc may 1985, pg 1236-1240” and the yield decreases with time with the ultimate need to dump the entire bed of silicon and start over with fresh material. Delaying the mixing to the mixing plenum increases the capital cost and operating cost because it makes heat recovery from the hot effluent gases more difficult and causes operational problems. The silicon tetrahalide frequently contains significant traces of the trihalosilane and dihalosilane which can decompose to silicon inside the tetrahalide heaters causing plugging. Using two separate preheaters increases the capital cost compared to a single train and makes it more difficult to recover heat from the exhaust gas which increases the use of utilities. The provision of a distribution means increases capital cost.
- The lower yield of commercial reactors can be attributed to the design of the distribution means and selection of typical fluidized bed operating conditions which cause bypassing of the silicon by large bubbles of reacting gas which means some of the reacting gas has a very short residence time. From Ingle it can be seen that yield depends on residence time but eventually reaches a plateau; thus a mixture of gas with low and high residence time will have a lower yield than one with the same average residence time where all the gas has the same residence time. The decrease in yield with time is caused by buildup of impurities on the surface of the silicon bed materials, as discussed in Bade, S., “Mechano-chemical reaction of metallurigal grade silicon with gaseous hydrogenchloride in a vibration mill, S. Bade et al, Int. J. Mineral Processing 44-45 (1996) 167-179”. The design of the plenum according to standard fluidized bed practice minimizes the amount of attrition which is thus inadequate to provide sufficient new reactive surface. In order to improve the yield it is important to define the process conditions in a more specific way than the very general definition of a temperature between 400° C.-600° C. and 300 to 600 psi. The key criteria is the ratio of the superficial velocity, U, to the minimum bubbling velocity, Umb, (U/Umb). The superficial velocity is the actual volumetric flow, adjusted for operating temperature and pressure, divided by the cross-sectional area of the vessel. The minimum bubbling velocity, Umb, is the minimum superficial velocity at which bubbles are formed, and is of importance because bubbles move faster than gas in the voids between particles and thus have less residence time. This velocity depends on the gas properties and on the size, shape and density of the granular particles. There are many ways to calculate this property, including computer programs. For large, greater than 200 micron, particles the Umb is essentially the same as the superficial velocity at minimum fluidization, Umf. Providing more comminution is known to be valuable in the similar process of reacting metallurgical grade silicon with hydrogen chloride as is discussed in Bade. The comminution increases reaction rate and yield but the Bade method of using a ball mill makes it difficult and expensive to implement at the high pressure, 500 psig, and high temperature, 500° C., needed for this reaction.
- Thus what is desired is a reactor and a set of operating conditions which provide more even gas-solids contacting, more comminution, better energy recovery and lower capital and operating cost.
- Systems incorporating the invention provide higher yield of the trihalosilane, lower fabrication cost lower cost of operation, high consumption of feed silicon flexible size distribution requirements for the feed metallurgical grade silicon and a flexible operation.
- Other objects and advantages of the present invention will become apparent from the following descriptions, taken in connection with the accompanying drawings, wherein, by way of illustration and example, an embodiment of the present invention is disclosed.
- In accordance with a preferred embodiment of the invention, an apparatus for hydrogenation of a silicon tetrahalide and silicon to trihalosilane comprises: a vessel with no internal flow distribution, one or more gas entries, one or more solids entries, one or more solids drains, one or more gas/solids exits and fresh surface generation by jet grinding. Also further disclosed is a process for choosing a set of operating conditions to take full advantage of the apparatus and an example of improved heat integration. This apparatus has the advantages of higher reaction rates, higher yields of trihalosilane and lower capital and operating costs by better heat integration with the remainder of the process.
- The drawings constitute a part of this specification and include exemplary embodiments to the invention, which may be embodied in various forms. It is to be understood that in some instances various aspects of the invention may be shown exaggerated or enlarged to facilitate an understanding of the invention.
-
FIG. 1 is a schematic diagram illustrating the overall operation of a system incorporating the invention. -
FIG. 2 is a cross sectional view of the reactor portion ofFIG. 1 . -
FIG. 3 is a cross sectional view of the attrition generating gas inlet of the reactor portion ofFIG. 2 . -
FIG. 4 is a modified version ofFIG. 3 showing two inlets - A detailed descriptions of an embodiment incorporating features of the invention is provided herein. It is to be understood, however, that the present invention may be embodied in various forms. Therefore, specific details disclosed herein are not to be interpreted as limiting, but rather as a basis for the claims and as a representative basis for teaching one skilled in the art to employ the present invention in virtually any appropriately detailed system, structure or manner.
- Turning first to
FIG. 1 there is shown an overall flow diagram illustrating an embodiment of the invention used to save energy costs when integrated into the overall process for production of the trihalosilane. A high pressure recycle liquidsilicon tetrahalide stream 112, comes from adownstream process 120, and is preheated in afirst heat exchanger 121, by heat exchange with aneffluent gas stream 106, to form a heatedstream 113, which is then is mixed with a recycledcompressed hydrogen stream 111, also from thedownstream process 120, to reduce the evaporation temperature of the liquidsilicon tetrahalide stream 112. The mixture is then evaporated in anevaporator 122. The heat can be provided by any utility, bait is particularly advantageous to usesteam 108 and recover acondensate 109. A resultingmixed vapor stream 114 is then heated by asecond heat exchanger 123 which simultaneusly cools acyclone effluent stream 105 from areactor cyclone 127. A very hot, 450° C.-550° C.,stream 115 exiting thesecond heat exchanger 123 is further heated with anelectric heater 124 to bring the temperature up to 500° C-600° C. in aninlet gas stream 116, prior to entering ahydrogenation reactor 126 with its ownelectrical heater 104. This heater can be external as shown or can be internal with penetrations through the reactor wall. Granulated metallurgical grade silicon, MGS, typically from about 440 to about 700 microns in diameter, is intermittently added from alock hopper 125 via anMGS stream 100 and reacts with the 500-600° C.inlet gas stream 116 to form the desiredtrichlorosilane product stream 101. Thisproduct stream 101 then enters thecyclone 127 where a primarysolid waste stream 102 of spent metallurgical grade silicon is removed. Thecyclone effluent 105 is then cooled in thesecond heat exchanger 123 to form the cooledeffluent gas stream 106 which is then further cooled by thefirst heat exchanger 121 to form a cooledstream 107 which then continues on to thedownstream process 120. In the prior art the yield decreased with time so aprimary waste stream 102 was also removed from the process on a periodic basis, typically one year, by emptying the entire reactor. This is not desired because of the loss of yield during operation and the time and consequent loss of production involved in the shutdown. In the present process grinding (attrition) is provided to remove the unreactive surface layer that builds up in thereator 102 over time and to thus remove it as dust in thecyclone waste stream 103. The specific design of the attrition mechanisms are discussed below in regard toFIGS. 2 and 3 . -
FIG. 2 is a cross sectional view of areactor 200 portion, corresponding to thehydrogenation reactor 126 ofFIG. 1 . Agas flow 201, which corresponds to the 500-600° C.inlet gas stream 116 ofFIG. 1 , enters through aceramic insert 206 in aninlet nozzle 204 located at the bottom of thereactor 126, entraining somesolid silicon particles 202 as it forms aninternal jet 203. The gas in thejet 203 then accelerates the entrainedparticles 202 until they hit a bed ofparticles 211 positioned within the reactor at which time grinding occurs due to the impact of the fast moving entrainedparticles 202 with the relativelystationary particles 211 in the bulk of the bed. The reactor does not contain any internal flow distributors to direct the flow path of the inlet gas streams.Gas 205 diffuses from thejet 203, and flows upwards through the bed ofstationary particles 211. A fraction of the gas may form bubbles 212, as shown but this is not required for operation. In fact, it is preferred that at least 90% of the volume of the bed is free of bubbles. Aneffluent gas 208 leaves the top 213 of the bed ofparticles 211 and carries with it somesmall dust particles 209 some of which drop out 210 in a disengagingspace 214 above the bed and some are carried out with theeffluent gas 208 through anexit 215. Theeffluent gas 208 which is a gas anddust mixture stream 216 then goes into thecyclone 217, which corresponds to thecyclone 127 ofFIG. 1 , where most of thedust 218 is removed in acyclone waste stream 103, and the cleaned gas leaves from the top of the cyclone in astream 219, which corresponds to thecyclone effluent stream 105 ofFIG. 1 . Additionalmetallurgical grade silicon 220 is added through asilicon inlet port 207 which is shown as entering through the side near the top of thereactor 200. While the reactor is described as having aceramic insert 206 in aninlet nozzle 204 one or more of other inlets and outlets can also be lined with an abrasion resistant ceramic composition. Suitable materials include, but are not limited to silicon nitride, silicon oxide, silicon oxynitride, alumina, mullite or silicon carbide -
FIG. 3 is a further expanded cross-sectional view of areactor inlet 300 filled with a bed of MGS particles 310 (corresponding to the bed ofparticles 211 ofFIG. 2 ). Asingle inlet 305 is designed to produce high attrition of themetallurgical silicon particles 310 by using an inlet gas stream 304 (corresponding to the 500-600° C.inlet gas stream 116 ofFIG. 1 ) to entrain theparticles 310 and accelerate them in a jet 301 (corresponding to theinternal jet 203 ofFIG. 2 ) until they collide with slow moving particles in the bulk of thebed 211.Particle flow paths particles 202 as they come down the cone walls into thejet 301. Theinlet 305 is lined with a removable ceramic insert 306 (corresponding toceramic insert 206 ofFIG. 2 ) to reduce the wear caused by attrition which is also shaped to increase the velocity of theinlet gas 304. The shape of theceramic insert 306 and opening into thebed 211 can be changed to modify the pressure drop and attrition as necessary to tune thereactor 200. The insert is retained by aretention ring 308 fastened to the inside of the reactor and cushioned with a flexiblehigh temperature gasket 307 at the top and bottom. The bottom of the insert is supported by a smallerdiameter reducing flange 309 which is preferably the same internal diameter as theceramic insert 306. -
FIG. 4 shows a variation ofFIG. 3 .Dual inlets FIG. 3 with eachinlet ceramic insert 406 to reduce the wear caused by the attrition. Inlet gas streams 404, 405, enter through theinlets vertical jet 401. The lateral vector of the velocity of each jet is converted to attrition at a higher rate than the vertical vector because the lateral vectors oppose each other whereas the vertical vector impacts into a bed of particles which are free to move. Thus the two interacting jets produce more attrition than would be expected from the same conditions for two non-interacting jets. The increase in attrition is related to anangle 409 between the intersecting gas streams 404, 405 and reaches a maximum when the angle equals 180 degrees. The attrition provided serves to remove the already reacted surface of theparticles 211 and exposes a fresh silicon surface to attack which increases the reaction rate and hence the throughput and yield of trihalosilane. The solid residue which would otherwise stay in the reactor is transported out as small surface dust particles. Acenter drain 407 for removing the bed is shown also. - Table 1 presents the flows and temperatures of an example of the process. Based on the conditions shown in Table 1 operating conditions can be selected to minimize bubbling and maximize yield and throughput and as a result maximize the production of the desired trihalosilane for a given reactor. The maximum velocity that can occur without bubbling is, by definition, the minimum bubbling velocity,
U mb. Operating at U/U mb of 1 gives the maximum flow without bubbling. -
TABLE 1 Stream Number 114 115 116 100 102 101 Temperature (° C.) 151.30 524.90 600.00 25.00 50.00 600.00 Pressure (atm) 29.94 29.67 29.19 1.00 1.00 25.19 Total molar flow (kmol/h) 115.63 115.63 115.63 3.92 0.00 111.84 Formula MW g/mol kmol/h kmol/h kmol/h kmol/h kmol/h kmol/h Gases/Liquids H2(g) 2.016 7.44E+01 7.44E+01 7.44E+01 0.00E+00 0.00E+00 6.72E+01 SiCl4 (g + l) 169.898 3.92E+01 3.92E+01 3.92E+01 0.00E+00 0.00E+00 2.83E+01 SiHCl3 (g + l) 135.452 1.16E+00 1.16E+00 1.16E+00 0.00E+00 0.00E+00 1.59E+01 SiH2Cl2 (g + l) 101.007 8.50E−02 8.50E−02 8.50E−02 0.00E+00 0.00E+00 1.79E−01 HCl(g) 36.461 6.74E−01 6.74E−01 6.74E−01 0.00E+00 0.00E+00 1.95E−01 AlCl3(g) 133.341 7.12E−04 7.12E−04 7.12E−04 0.00E+00 0.00E+00 1.22E−02 CH4(g) 16.043 4.91E−02 4.91E−02 4.91E−02 0.00E+00 0.00E+00 5.84E−02 Si(CH3)Cl3 (g + l) 149.479 5.01E−04 5.01E−04 5.01E−04 0.00E+00 0.00E+00 5.48E−04 SiH(CH3)Cl2 (g + l) 115.034 1.55E−04 1.55E−04 1.55E−04 0.00E+00 0.00E+00 1.55E−04 TiCl4(g) 189.712 1.14E−04 1.14E−04 1.14E−04 0.00E+00 0.00E+00 6.11E−04 TiCl4(l) 189.712 0.00E+00 0.00E+00 0.00E+00 0.00E+00 0.00E+00 0.00E+00 PH3(g) 33.997 3.66E−04 3.66E−04 3.66E−04 0.00E+00 0.00E+00 4.33E−04 BCl3 (g + l) 117.169 7.68E−05 7.68E−05 7.68E−05 0.00E+00 0.00E+00 2.00E−04 Solids Cu 63.546 8.23E−06 8.23E−06 8.23E−06 1.31E−03 3.85E−05 1.25E−03 Si 28.086 2.48E−04 2.48E−04 2.48E−04 3.89E+00 1.16E−03 3.75E−02 FeSi 83.933 3.00E−05 3.00E−05 3.00E−05 0.00E+00 1.40E−04 4.54E−03 CaCl2 110.986 5.15E−06 5.15E−06 5.15E−06 0.00E+00 2.41E−05 7.79E−04 Cu3As 265.560 7.95E−08 7.95E−08 7.95E−08 0.00E+00 3.72E−07 1.20E−05 As 74.922 1.05E−07 1.05E−07 1.05E−07 2.94E−05 4.92E−07 1.59E−05 CrCl2 122.902 1.34E−07 1.34E−07 1.34E−07 0.00E+00 6.24E−07 2.02E−05 AlCl3(s) 133.341 0.00E+00 0.00E+00 0.00E+00 0.00E+00 0.00E+00 0.00E+00 Stream Number 103 105 106 107 112 113 Temperature (° C.) 50.00 550.00 176.30 130.00 100.00 162.70 Pressure (atm) 1.00 24.39 24.25 24.12 29.90 29.80 Total molar flow (kmol/h) 0.04 111.80 111.80 111.80 40.13 40.13 Formula MW g/mol kmol/h kmol/h kmol/h kmol/h kmol/h kmol/h Gases/Liquids H2(g) 2.016 0.00E+00 6.72E+01 6.72E+01 6.72E+01 0.00E+00 0.00E+00 SiCl4 (g + l) 169.898 0.00E+00 2.83E+01 2.83E+01 2.83E+01 3.92E+01 3.92E+01 SiHCl3 (g + l) 135.452 0.00E+00 1.59E+01 1.59E+01 1.59E+01 9.03E−01 9.03E−01 SiH2Cl2 (g + l) 101.007 0.00E+00 1.79E−01 1.79E−01 1.79E−01 2.03E−06 2.03E−06 HCl(g) 36.461 0.00E+00 1.95E−01 1.95E−01 1.95E−01 0.00E+00 0.00E+00 AlCl3(g) 133.341 0.00E+00 1.22E−02 0.00E+00 1.98E−03 7.12E−04 7.12E−04 CH4(g) 16.043 0.00E+00 5.84E−02 5.84E−02 5.84E−02 0.00E+00 0.00E+00 Si(CH3)Cl3 (g + l) 149.479 0.00E+00 5.48E−04 5.48E−04 5.48E−04 5.01E−04 5.01E−04 SiH(CH3)Cl2 (g + l) 115.034 0.00E+00 1.55E−04 1.55E−04 1.55E−04 1.55E−04 1.55E−04 TiCl4(g) 189.712 0.00E+00 6.11E−04 0.00E+00 0.00E+00 0.00E+00 0.00E+00 TiCl4(l) 189.712 0.00E+00 0.00E+00 6.11E−04 6.11E−04 1.14E−04 1.14E−04 PH3(g) 33.997 0.00E+00 4.33E−04 4.33E−04 4.33E−04 0.00E+00 0.00E+00 BCl3 (g + l) 117.169 0.00E+00 2.00E−04 2.00E−04 2.00E−04 1.79E−10 1.79E−10 Solids Cu 63.546 1.20E−03 4.98E−05 4.98E−05 4.98E−05 8.23E−06 8.23E−06 Si 28.086 3.60E−02 1.50E−03 1.50E−03 1.50E−03 2.48E−04 2.48E−04 FeSi 83.933 4.36E−03 1.82E−04 1.82E−04 1.82E−04 3.00E−05 3.00E−05 CaCl2 110.986 7.48E−04 3.11E−05 3.11E−05 3.11E−05 5.15E−06 5.15E−06 Cu3As 265.560 1.15E−05 4.81E−07 4.81E−07 4.81E−07 7.95E−08 7.95E−08 As 74.922 1.53E−05 6.36E−07 6.36E−07 6.36E−07 1.05E−07 1.05E−07 CrCl2 122.902 1.94E−05 8.08E−07 8.08E−07 8.08E−07 1.34E−07 1.34E−07 AlCl3(s) 133.341 0.00E+00 0.00E+00 1.24E−02 1.05E−02 0.00E+00 0.00E+00 - As noted above this can be calculated in many ways but one particularly useful equation is the David and Harrison equation:
-
U mb =U mf=0.0055*ε3/(1-ε)g D p 2(ρp−ρf)/μf -
- Where: ε is the voidage at Umb
- g is the acceleration of gravity
- Dp is the diameter of the particle
- ρp is the particle density
- ρf is the fluid density.
- μf is the viscosity of the fluid
- The value of the voidage depends on the shape of the particle and can be measured for any given sample of metallurgical grade silicon. The diameter of the particle is the average projected diameter and can be measured by standard sieving techniques and adjusted as necessary for the sphericity. The viscosity of the gas increases with temperature and is dependent on the composition. There are several standard ways to accurately predict it. The easiest way to increase the Umb is to increase the average particle diameter, Dp.
- The gas inlet composition is as in Table 1
- ε is the voidage at Umb=0.4
- g is the acceleration of gravity=980 m/s2
- Dp is the diameter of the particle=To be calculated
- ρp is the particle density=2.33 g/cc
- ρf is the fluid density.=0.0218 g/cc
- μf is the viscosity of the fluid=0.00024 poise
- U is the max. superficial velocity=0.11 m/sec=Umb
- Therefore the desired minimum average particle size=444 microns. Since MGS is quite angular this particle size should be adjusted by dividing by the sphericity which is typically about 0.86. This gives the average particle size, 516 microns as measured by sieve analysis. Further standard population balance calculations can be made to allow for the shrinkage of the particle due to reaction and the decrease in size due to attrition to arrive at the required minimum average particle size for the feed to the reactor. Once a reasonable estimate has been obtained for the correct particle size for the feed, a test may be performed.
- A reactor 10 meters long was charged with a 7 m high bed using MGS of a nominal 750 micron size. The reactor was run for 120 hours under the conditions of Table 1 and batches of metallurgical grade silicon were added once per hour to maintain level. At the end of the run a sample of the MGS in the bed was taken from the bed and analyzed and the results are shown below.
-
TABLE 2 Weight % of Particles in a sieve size range Sieve size Particle Microns Wt % 0-50 0.03% 50-100 0.24% 100-150 0.61% 150-200 0.96% 200-250 0.94% 250-300 2.44% 300-350 5.16% 350-400 3.85% 400-450 5.49% 450-500 7.53% 500-550 10.02% 600-600 13.01% 650-650 14.88% 650-700 16.52% 700-750 15.24% 750-800 3.08%
The average particle size was calculated at 538 microns - While the invention has been described in connection with a preferred embodiment, it is not intended to limit the scope of the invention to the particular form set forth, but on the contrary, it is intended to cover such alternatives, modifications, and equivalents as may be included within the spirit and scope of the invention as defined by the appended claims.
Claims (5)
1. A process for hydrogenation of a silicon tetrahalide and silicon to trihalosilane comprising:
providing a vessel with at least one inlet and at least one outlet and a bed comprising a plurality of silicon particles located inside the vessel, and
feeding a mixture of gases comprising a silicon tetrahalide and hydrogen into the vessel and through the bed, wherein the flow rate of the mixture of gases and the average size of the silicon particles are chosen so that at least 90% of the volume of the bed is free of bubbles.
2. The process of claim 1 where the velocity of the mixture of gases is equal to or less than a minimum bubbling velocity calculated based on the properties of the gases and silicon particles in the bed so as to maintain at least 90% of the volume of the bed free of bubbles.
3. The process of claim 1 where an average size of the silicon particles is determined by selecting the velocity of the gases through the vessel to provide at least 90% of the volume of the bed free of bubbles, said velocity being equal to or less than a calculated minimum bubbling velocity.
4. The process of claim 1 where additional silicon particles larger than an average size in the vessel are added intermittently to maintain the average size of particles in the vessel at or above a chosen size.
5. The process of claim 4 wherein standard population balance calculations, making allowance for reaction and attrition of the silicon particles in the vessel, are used to calculate a minimum size for the feed particles.