US20120160395A1 - Method for manufacturing honeycomb filter - Google Patents
Method for manufacturing honeycomb filter Download PDFInfo
- Publication number
- US20120160395A1 US20120160395A1 US13/412,727 US201213412727A US2012160395A1 US 20120160395 A1 US20120160395 A1 US 20120160395A1 US 201213412727 A US201213412727 A US 201213412727A US 2012160395 A1 US2012160395 A1 US 2012160395A1
- Authority
- US
- United States
- Prior art keywords
- honeycomb
- honeycomb filter
- sealing material
- ceramic block
- peripheral face
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A method for manufacturing a honeycomb filter includes applying a first sealing material paste to a side face of one of honeycomb fired bodies to form a sealing material paste layer thereon. Another of honeycomb fired bodies is laminated on the first sealing material paste layer to manufacture an aggregated body of honeycomb fired bodies. The aggregated body of honeycomb fired bodies is heated so that the first sealing material paste layer is dried and solidified to produce a ceramic block. A second sealing material paste is applied to a peripheral face of the ceramic block in accordance with irregularities formed thereon so that an outer peripheral surface of the honeycomb filter has surface irregularities thereon. The second sealing material paste is dried and solidified to form a sealing material layer on the peripheral face of the ceramic block.
Description
- The present application is a divisional application of the U.S. patent application Ser. No. 12/342,903 filed Dec. 23, 2008, which claims priority under 35 U.S.C. §119 to PCT Application No. PCT/JP2008/055462, filed Mar. 24, 2008. The contents of these applications are incorporated herein by reference in their entirety.
- 1. Field of the Invention
- The present invention relates to a method for manufacturing a honeycomb filter.
- 2. Discussion of the Background
- In recent years, particulate matter (hereinafter, also referred to as “PM”) such as soot discharged from internal combustion engines of vehicles such as buses and trucks, construction machines and the like has raised serious problems as contaminants harmful to the environment and the human body. For this reason, various honeycomb filters, which use a porous ceramic honeycomb structure, have been proposed as filters that capture PM in exhaust gases and purify the exhaust gases.
- As a material for such a honeycomb filter, silicon carbide has been known. In the case where silicon carbide is used as the material for the honeycomb filter, since the silicon carbide has a high coefficient of thermal expansion, a structure of an aggregated honeycomb filter is adopted, in which a plurality of pillar-shaped porous ceramic sintered bodies (honeycomb fired bodies), each having a large number of cells longitudinally placed in parallel with one another, are combined with one another.
- As such an aggregated honeycomb filter, JP-A 2001-162121 has disclosed a honeycomb filter including an aggregated body of honeycomb fired bodies (ceramic block) manufactured by combining a plurality of honeycomb fired bodies with one another, cutting a periphery of the ceramic block so as to have a cross-section in an almost circular shape or the like, and forming a smoothing layer on the peripheral face having irregularities thereon exposed by the cutting process.
- The smoothing layer is formed by filling irregularities corresponding to the shapes of the cell walls exposed by the cutting process so that the honeycomb filter is formed into a round pillar shape or the like.
- The contents of JP-A 2001-162121 are incorporated herein by reference in their entirety.
- According to one aspect of the present invention, a method for manufacturing a honeycomb filter includes preparing a wet mixture including at least one of silicon carbide and silicon-containing silicon carbide. The wet mixture is extrusion-molded to manufacture honeycomb molded bodies each having a longitudinal direction and a plurality of cell walls extending along the longitudinal direction to define a plurality of cells. A plug material paste is provided in the cells to seal either one of both ends of each of the cells.
- The sealed honeycomb molded bodies are fired to manufacture a honeycomb fired bodies. A first sealing material paste is applied to a side face of one of the honeycomb fired bodies to form a sealing material paste layer thereon. Another of the honeycomb fired bodies is laminated on the first sealing material paste layer to manufacture an aggregated body of honeycomb fired bodies. The aggregated body of honeycomb fired bodies is heated so that the first sealing material paste layer is dried and solidified to produce a ceramic block. A second sealing material paste is applied to a peripheral face of the ceramic block in accordance with irregularities formed thereon so that an outer peripheral surface of the honeycomb filter has surface irregularities thereon. The second sealing material paste is dried and solidified to form a sealing material layer on the peripheral face of the ceramic block.
- A more complete appreciation of the invention and many of the attendant advantages thereof will be readily obtained as the same becomes better understood by reference to the following detailed description when considered in connection with the accompanying drawings.
-
FIG. 1 is a perspective view schematically showing one example of a honeycomb filter according to one embodiment of the present invention. -
FIG. 2A is a perspective view schematically showing one example of a honeycomb fired body constituting a honeycomb filter according to one embodiment of the present invention, andFIG. 2B is an A-A line cross-sectional view of the honeycomb fired body shown inFIG. 2A . -
FIG. 3 is a side view of a rectangular pillar-shaped ceramic block constituting a honeycomb filter according to one embodiment of the present invention. -
FIG. 4 is a side view of an almost round pillar-shaped ceramic block obtained by processing the periphery of the rectangular pillar-shaped ceramic block shown inFIG. 3 . -
FIG. 5 is a side view of a honeycomb filter obtained by forming a sealing material layer on a peripheral face of the ceramic block shown inFIG. 4 . -
FIG. 6 is an enlarged cross-sectional view showing an area surrounded by a curved line B inFIG. 5 . -
FIG. 7 is a cross-sectional view of an exhaust gas purifying apparatus provided with the honeycomb filter of a first embodiment. -
FIG. 8 is a D-D line cross-sectional view of the exhaust gas purifying apparatus shown inFIG. 7 . -
FIGS. 9A , 9B and 9C are perspective views each schematically showing one example of the honeycomb fired body constituting the honeycomb filter of a second embodiment. -
FIG. 10 is a perspective view schematically showing another example of a honeycomb filter according to a second embodiment of the present invention. -
FIG. 11 is an enlarged cross-sectional view showing an area surrounded by a curved line E inFIG. 10 . - Embodiments will now be described with reference to the accompanying drawings, wherein like reference numerals designate corresponding or identical elements throughout the various drawings.
- A honeycomb filter according to embodiments of the present invention includes: a ceramic block formed by a plurality of honeycomb fired bodies combined with one another with an adhesive layer interposed therebetween, each of the honeycomb fired bodies having a large number of cells each sealed at either end of the cells and placed longitudinally in parallel with one another with a cell wall therebetween; and a sealing material layer formed on a peripheral face of the ceramic block, the honeycomb fired bodies including silicon carbide or silicon-containing silicon carbide, the ceramic block having the peripheral face with irregularities formed thereon, the irregularities on the peripheral face of the ceramic block including a projected portion formed by a part of the cell wall projecting from the cell wall, the sealing material layer being formed along the irregularities on the peripheral face of the ceramic block, and the honeycomb filter having a peripheral face with irregularities existing thereon.
- In the honeycomb filter according to the embodiments of the present invention, irregularities are formed on a peripheral face of the ceramic block formed by combining a plurality of honeycomb fired bodies with one another, and a sealing material layer is formed along the irregularities.
- The sealing material layer is formed so as not to completely fill the irregularities on the peripheral face of the ceramic block.
- That is, the peripheral face of the honeycomb filter is not smooth, and irregularities exist on the peripheral face of the honeycomb filter.
- In the case where the irregularities exist on the peripheral face of the honeycomb filter, a coefficient of friction between the holding sealing material wound around the honeycomb filter and the peripheral face of the honeycomb filter becomes higher during an installation of the honeycomb filter in a casing. For this reason, even when thermal expansion and thermal shrinkage due to application of heat are repeated in a honeycomb filter manufactured by using a material having a high coefficient of thermal expansion such as silicon carbide or silicon-containing silicon carbide, it may be easier to prevent the displacement of the honeycomb filter from the originally installed position in the casing.
- When the cell is sealed by a plug, “a projected portion formed by a part of the cell wall projecting from the cell wall” means the projecting portion of the cell wall except the plug on the peripheral face of the ceramic block.
- The honeycomb filter according to the embodiments of the present invention will be described in terms of its advantageous effects with respect to conventional honeycomb filters.
- Normally, a honeycomb filter used for purifying exhaust gases is wrapped with a holding sealing material including ceramic fibers and the like on the periphery thereof and installed in a casing that is placed in the middle of an exhaust pipe.
- When the honeycomb filter is installed in the casing, a pressure is applied from the inner wall surface of the casing toward the center of the cross section of the honeycomb filter in the longitudinal direction thereof so that a displacement of the honeycomb filter in the casing is prevented.
- Here, in recent years, with respect to the honeycomb filter, there have been demands for making a thickness of the cell wall thinner to increase the porosity of the cell walls so that a pressure loss is reduced. For this reason, mechanical strength of the honeycomb filter tends to be lower in comparison with that of a conventional honeycomb filter.
- Accordingly, in order to prevent a damage of the honeycomb filter during an installation of the honeycomb filter in the casing, it is necessary to lower the pressure to be applied to the honeycomb filter during the installation of the honeycomb filter in the casing, in comparison with the conventionally applied pressure.
- In the case where the pressure to be applied to the honeycomb filter during the installation of the honeycomb filter in the casing is lowered, however, the application of a honeycomb filter in which the smoothing layer is formed to fill the irregularities on the periphery of the honeycomb filter, such as the conventional honeycomb filter disclosed in JP-A 2001-162121, tends to cause the displacement of the honeycomb filter in the casing during the use of the honeycomb filter.
- In particular, when a regenerating process for burning PM collected in the honeycomb filter is carried out, there may be a case where the honeycomb filter is displaced from the originally installed position in the casing during the process where the honeycomb filter is expanded due to heat generated in the burning and the honeycomb filter is then shrunk along with lowering of the temperature of the honeycomb filter.
- Moreover, the displacement of the honeycomb filter caused by the above reason tends to occur particularly in the honeycomb filter manufactured by using a material having a high coefficient of thermal expansion such as silicon carbide.
- In comparison with such conventional honeycomb filters, the honeycomb filter according to the embodiments of the present invention tends not to be displaced from an originally installed position in the casing when being used, even manufactured by using a material having a high coefficient of thermal expansion such as silicon carbide.
- In the honeycomb filter according to the embodiments of the present invention, the irregularities on the peripheral face of the ceramic block are formed by processing of a periphery of a ceramic block.
- In the honeycomb filter according to the embodiments of the present invention, the sealing material layer is formed along all the surfaces of the irregularities on the peripheral face of the ceramic block.
- In the honeycomb filter according to the embodiments of the present invention, each of the irregularities on the peripheral face of the honeycomb filter has a depth of at least about 0.1 mm and at most about 0.5 mm.
- When the depth of the irregularities is about 0.1 mm or more, the coefficient of friction between the holding sealing material and the peripheral face of the honeycomb filter tends to be made higher.
- Further, when the depth of the irregularities is about 0.5 mm or less, it may be easier to prevent exhaust gases having not passed through the cell wall from flowing into a gap (space) between the honeycomb filter and the holding sealing material.
- In the honeycomb filter according to the embodiments of the present invention, the adhesive layer and the sealing material layer include the same material.
- In the following, an embodiment of the honeycomb filter of the present invention will be described with reference to drawings.
-
FIG. 1 is a perspective view schematically showing one example of a honeycomb filter according to one embodiment of the present invention. - In a
honeycomb filter 100 shown inFIG. 1 , aceramic block 103 is formed by combining a plurality of honeycomb firedbodies 110 including porous silicon carbide or silicon-containing silicon carbide with anadhesive layer 101 interposed therebetween, and further, a sealingmaterial layer 102 is formed on aperipheral face 13 of thisceramic block 103. - The
honeycomb filter 100 shown inFIG. 1 has an almost round pillar shape, and irregularities are formed on a peripheral face 10 (side face of the almost round pillar-shaped honeycomb filter) of thehoneycomb filter 100. - The shape of the irregularities on the
peripheral face 10 of thehoneycomb filter 100 corresponds to the shape of the irregularities on theperipheral face 13 of theceramic block 103. - In the following, there will be described the honeycomb fired body constituting the honeycomb filter having irregularities on the peripheral face, the ceramic block including a plurality of the honeycomb fired bodies combined with one another, as well as a honeycomb filter with a sealing material layer formed on the peripheral face of the ceramic block and the sealing material layer.
- First, there is described a honeycomb fired body.
-
FIG. 2A is a perspective view schematically showing one example of a honeycomb fired body constituting a honeycomb filter according to one embodiment of the present invention, andFIG. 2B is an A-A line cross-sectional view of the honeycomb fired body shown inFIG. 2A . - In a honeycomb fired
body 110 shown inFIG. 2A andFIG. 2B , a large number ofcells 111 are disposed in parallel with one another with acell wall 113 therebetween in the longitudinal direction (the direction shown by an arrow “a” inFIG. 2A ), and either one end of each of thecells 111 is sealed by aplug 112. Therefore, exhausted gases G flowing into onecell 111 with an opening on one end face are to be discharged from anothercell 111 with an opening on the other end face after surely passing through acell wall 113 between thecells 111. - Consequently, the
cell wall 113 is allowed to function as a filter to capture PM and the like. - Subsequently, a ceramic block including a plurality of honeycomb fired bodies combined with one another is described.
-
FIG. 3 is a side view of a rectangular pillar-shaped ceramic block including 16 rectangular pillar-shaped honeycomb fired bodies constituting a honeycomb filter according to one embodiment of the present invention combined with one another. - A rectangular pillar-shaped
ceramic block 203 shown inFIG. 3 includes a total of 16 rectangular pillar-shaped honeycomb firedbodies 110, four each in the lengthwise and breadthwise directions, combined with anadhesive layer 101 interposed therebetween. - A
peripheral face 213 of theceramic block 203 is smooth. - A circle shown in
FIG. 3 indicates a face along which the periphery of theceramic block 203 is processed, and by processing the periphery of the rectangular pillar-shapedceramic block 203, a ceramic block having an almost round pillar shape is manufactured. -
FIG. 4 is a side view of an almost round pillar-shaped ceramic block obtained by processing the periphery of the rectangular pillar-shaped ceramic block shown inFIG. 3 . - The
peripheral face 13 of the almost round pillar-shapedceramic block 103 shown inFIG. 4 is not smooth, but irregularities are formed on theperipheral face 13 of theceramic block 103. - The irregularities on the
peripheral face 13 of theceramic block 103 include projectedportions 12, each formed by a part of the cell wall of the honeycomb firedbody 110 projecting from the cell wall. - Here, the shape of the irregularities on the
peripheral face 13 of theceramic block 103 corresponds to the shape of the cell walls of the honeycomb firedbodies 110 and the position where the periphery of the ceramic block is processed. - Subsequently, a honeycomb filter in which a sealing material layer (also referred to as a coat layer) is formed on the peripheral face of the ceramic block and the sealing material layer (coat layer) will be explained.
-
FIG. 5 is a side view of the honeycomb filter obtained by forming a sealing material layer on the peripheral face of the ceramic block shown inFIG. 4 . - Here,
FIG. 5 is also the side view of thehoneycomb filter 100 shown inFIG. 1 . - The sealing
material layer 102 is formed along the irregularities on theperipheral face 13 of theceramic block 103, and particularly formed along all the surfaces of irregularities on theperipheral face 13 of theceramic block 103. - The sealing
material layer 102 is formed by applying a sealing material paste to theperipheral face 13 of theceramic block 103 so as to make the thickness of the sealingmaterial layer 102 thin, for the purpose of not filling all the irregularities on the peripheral face 13 (without smoothing the irregularities) and allowing the irregularities to remain (exist). - Accordingly, on the
peripheral face 10 of thehoneycomb filter 100, there exist the irregularities derived from the irregularities on theperipheral face 13 of theceramic block 103, and the shape of irregularities existing on theperipheral face 10 of thehoneycomb filter 100 corresponds to the shape of the irregularities on theperipheral face 13 of theceramic block 103. -
FIG. 6 is an enlarged cross-sectional view showing an area surrounded by a curved line B inFIG. 5 . - The definition of the depth of the irregularities that exist on peripheral face of the honeycomb filter in the present description is described with reference to
FIG. 6 . - A
circle 14 is drawn so as to be tangent to a projectingportion 16 that most projects outward on theperipheral face 10 of the honeycomb filter. The surface indicated by this circle is defined as “a projecting face”. - Next, a
circle 15 is drawn inside thiscircle 14 so as to be tangent to a recessedportion 17 that is most recessed on the peripheral face of the honeycomb filter. A surface indicated by thecircle 15 is defined as “a recessed face”. - The gap between the
circle 14 indicating the projecting face and thecircle 15 indicating the recessed face (length indicated by an arrow “C” inFIG. 6 ) is defined as the depth of the irregularities on the peripheral face of the honeycomb filter. - The depth of the irregularities on the peripheral face of the honeycomb filter is desirably at least about 0.1 mm and at most about 0.5 mm.
- Moreover, in the case where the shape of a honeycomb filter is not the almost round pillar shape, for example, in the case of a cylindroid shape, an elliptical shape can be used in place of the circle, when the projecting face and the recessed face are determined. That is, a figure similar to the cross-sectional shape of the honeycomb filter may be used.
- Moreover, irrespective of the cross-sectional shape of the honeycomb filter, it is only necessary to use the similar shape for the figure used for determining the projecting face and the figure used for determining the recessed face.
- Although not particularly limited, examples of the material for forming the sealing material layer include an inorganic binder, an organic binder, inorganic fibers, inorganic particles or a combination thereof.
- The thickness of the sealing material layer is not particularly limited, as long as the thickness is determined depending on the size of the cells of the honeycomb fired bodies constituting the honeycomb filter so that irregularities exist on the peripheral face of the honeycomb filter, and is desirably at least about 0.1 mm and at most about 0.5 mm.
- The following description will discuss a method for manufacturing the honeycomb filter of the present embodiment.
- First, as a ceramic raw material, silicon carbide powders having different average particle diameters, an organic binder, a plasticizer in liquid form, a lubricant and water are mixed to prepare a wet mixture for manufacturing a molded body.
- Successively, this wet mixture is loaded into an extrusion molding machine.
- When the wet mixture is loaded into the extrusion molding machine, the wet mixture is extrusion-molded into a honeycomb molded body having a predetermined shape.
- Next, the honeycomb molded body is cut into a predetermined length, and dried by using a drying apparatus, such as a microwave drying apparatus, a hot-air drying apparatus, a dielectric drying apparatus, a reduced-pressure drying apparatus, a vacuum drying apparatus and a freeze drying apparatus, and a sealing process is carried out by filling predetermined cells with a plug material paste to be a plug for sealing the cells.
- Subsequently, the honeycomb molded body is degreased in a degreasing furnace so as to heat organic substances contained in the honeycomb molded body and firing process is carried out thereon.
- Accordingly, a rectangular pillar-shaped honeycomb fired body as shown in
FIG. 2A andFIG. 2B is manufactured. - Here, as conditions to carry out processes of cutting, drying, sealing, degreasing and firing, conditions used for manufacturing a conventional honeycomb fired body can be used.
- Further, a sealing material paste, which is to be an adhesive layer, is applied to a side face of the resulting honeycomb fired body to form a sealing material paste layer thereon, and another honeycomb fired body is successively laminated with this sealing material paste layer interposed therebetween. By repeating these processes, an aggregated body of honeycomb fired bodies with a predetermined number of honeycomb fired bodies combined with one another is manufactured. Here, with respect to the sealing material paste, a material containing an inorganic binder, an organic binder, and at least one of inorganic fibers and inorganic particles may be used.
- Furthermore, the aggregated body of the honeycomb fired bodies is heated so that the sealing material paste layer is dried and solidified to form an adhesive layer and the rectangular pillar-shaped ceramic block as shown in
FIG. 3 is manufactured. - Subsequently, a cutting process is carried out on the periphery of the ceramic block by using a diamond cutter so that a ceramic block having an almost round pillar shape as shown in
FIG. 4 is manufactured. - On the peripheral face of the ceramic block having the almost round pillar shape formed by the cutting process, irregularities including projected portions, each formed by a part of the cell wall of the honeycomb fired body projecting from the cell wall, are formed.
- Moreover, a sealing material paste is thinly applied to the peripheral face of the ceramic block along the irregularities formed thereon so as to allow the irregularities to exist (remain). As the sealing material paste, the same sealing material paste as that used when the adhesive layer is formed may be used.
- The applying process of the sealing material paste can be carried out by using a squeegee or the like.
- More specifically, a sealing material paste having a low viscosity is prepared by adding water or the like to the sealing material paste used for forming the adhesive layer, and the obtained sealing material paste is applied to the peripheral face of the ceramic block. Then, by making the ceramic block with the sealing material paste coated thereon pass through the squeegee having a cylindrical (pipe) shape, the application of the sealing material paste can be carried out.
- In this case, irregularities are allowed to exist (remain) on the peripheral face by adjusting the gap between the squeegee and the ceramic block and the pressure to be applied to the ceramic block from the squeegee.
- Moreover, the sealing material paste thus applied is dried and solidified, so that a sealing material layer is formed on the peripheral face of the ceramic block.
- By following the above processing, a honeycomb filter having a peripheral face on which the irregularities exist (remain), as shown in
FIG. 5 , can be manufactured. - When manufacturing the honeycomb filter of the present embodiment, the rectangular pillar-shaped ceramic block may be manufactured without sealing the cells which will form the peripheral face of the almost round pillar-shaped ceramic block out of the cells of the honeycomb molded body, and the cutting process may be carried out to this almost round pillar-shaped ceramic block.
- Thereby, the honeycomb filter, in which the irregularities are formed on the peripheral face of a honeycomb filter uninterruptedly from one end face side to another end face side, can be manufactured. This honeycomb filter has the same shape as the honeycomb filter according to a second embodiment described later (see
FIGS. 10 and 11 ). - The honeycomb filter of the present embodiment is installed in an exhaust gas purifying apparatus, and used for purifying exhaust gases.
- An exhaust gas purifying apparatus according to the embodiments of the present invention in which the honeycomb filter of the present embodiment is installed will be described hereinafter.
-
FIG. 7 is a cross-sectional view of the exhaust gas purifying apparatus according to one embodiment of the present invention provided with the honeycomb filter of the present embodiment. - An exhaust
gas purifying apparatus 220 according to the embodiments of the present invention mainly includes thehoneycomb filter 100, acasing 221 that covers the outside of thehoneycomb filter 100, and a holding sealing material 222 (heat insulating material) interposed between thehoneycomb filter 100 and thecasing 221. Further, an introducingpipe 224, which is coupled to an internal combustion engine such as an engine, is connected to one end portion of thecasing 221 on the side from which exhaust gases are introduced, and anexhaust pipe 225 coupled to the outside is connected to the other end portion of thecasing 221. Here, inFIG. 7 , arrows show flows of exhaust gases. -
FIG. 8 is a D-D line cross-sectional view of the exhaust gas purifying apparatus shown inFIG. 7 . - In the exhaust
gas purifying apparatus 220 in which thehoneycomb filter 100 of the present embodiment is installed, theholding sealing material 222 is placed so as to embedding the irregularities formed on theperipheral face 10 of thehoneycomb filter 100 of the present embodiment. Accordingly, the coefficient of friction between the holding sealing material and the peripheral face of the honeycomb filter becomes higher. - For this reason, even when thermal expansion and thermal shrinkage are repeated in the
honeycomb filter 100 because of the application of heat, thehoneycomb filter 100 in thecasing 221 tends not to be displaced. - The effects of the honeycomb filter of the present embodiment will be listed in the following.
- (1) Since the irregularities exist on the peripheral face of the honeycomb filter of the present embodiment, when the honeycomb filter is installed in the casing, the coefficient of friction between the holding sealing material wound around the honeycomb filter and the peripheral face of the honeycomb filter tends to be higher. For this reason, even when thermal expansion and thermal shrinkage are repeated in the honeycomb filter because of the application of heat, the honeycomb filter from the originally installed position in the casing tends not to be displaced.
- (2) Moreover, the depth of the irregularities that exist on the peripheral face of the honeycomb filter is at least about 0.1 mm and at most about 0.5 mm.
- For this reason, the coefficient of friction between the holding sealing material and the peripheral face of the honeycomb filter tends to be higher, and further, it may be easier to prevent exhaust gases that having not passed through the cell wall from flowing into the gap (space) between the honeycomb filter and the holding sealing material.
- Here, in the honeycomb filter in which the irregularities are formed on the peripheral face of the honeycomb filter uninterruptedly from one end face side to another end face side, the shape of the peripheral face of the honeycomb filter tends to be more complicated. Accordingly, when the honeycomb filter is installed in the casing, the coefficient of friction between the holding sealing material wound around the honeycomb filter and the peripheral face of the honeycomb filter tends to be much higher. For this reason, even when thermal expansion and thermal shrinkage are repeated in the honeycomb filter because of the application of heat, the displacement of the honeycomb filter from the originally installed position in the casing tends to be effectively prevented.
- The following description will discuss Examples that specifically disclose the first embodiment of the present invention. Here, the present invention is not intended to be limited only to these Examples.
- An amount of 52.8% by weight of a silicon carbide coarse powder having an average particle diameter of 22 μm and 22.6% by weight of a silicon carbide fine powder having an average particle diameter of 0.5 μm were mixed. To the resulting mixture, 2.1% by weight of an acrylic resin, 4.6% by weight of an organic binder (methylcellulose), 2.8% by weight of a lubricant (UNILUB, manufactured by NOF Corporation), 1.3% by weight of glycerin, and 13.8% by weight of water were added, and then kneaded to prepare a wet mixture. The obtained wet mixture was extrusion-molded, so that a raw honeycomb molded body having almost the same shape as the shape shown in
FIG. 2A and having cells not sealed was manufactured. - Next, the raw honeycomb molded body was dried by using a microwave drying apparatus to obtain a dried honeycomb molded body. Then, using a plug material paste having the same composition as that of the raw molded body, predetermined cells were filled, and the dried honeycomb molded body filled with the plug material paste was again dried by using a drying apparatus.
- The dried honeycomb molded body was degreased at 400° C., and then fired at 2200° C. under normal pressure and argon atmosphere for three hours, so that a honeycomb fired body including a silicon carbide sintered body, with a porosity of 45%, an average pore diameter of 15 μm, a size of 34.3 mm×34.3 mm×150 mm, the number of cells (cell density) of 300 pcs/inch2 and a thickness of the cell wall of 0.25 mm (10 mil), was manufactured.
- By using a heat resistant sealing material paste containing 30% by weight of alumina fibers having an average fiber length of 20 μm, 21% by weight of silicon carbide particles having an average particle diameter of 0.6 μm, 15% by weight of silica sol, 5.6% by weight of carboxymethylcellulose and 28.4% by weight of water, a plurality of honeycomb fired bodies were bonded to one another, and the sealing material paste was dried and solidified at 120° C. so as to form sealing material layers; thus, a rectangular pillar-shaped ceramic block was manufactured.
- Subsequently, the periphery of the rectangular pillar-shaped ceramic block was cut by using a diamond cutter so that a ceramic block having an almost round pillar shape was manufactured.
- On the peripheral face of this ceramic block, irregularities including projected portions, each formed by a part of the cell wall of the honeycomb fired body projecting from the cell wall, were formed.
- Subsequently, a sealing material paste, prepared by adding 30% by weight of water to 70% by weight of the sealing material paste used for forming the adhesive layer and further kneading, was applied to the peripheral face of the ceramic block along the irregularities thereon so that the irregularities existed (remained) on the peripheral face by using a squeegee having a cylindrical (pipe) shape.
- Then, the sealing material paste applied to the peripheral face of the ceramic block was dried and solidified at 120° C. so as to form sealing material layers; thus, a round pillar-shaped honeycomb filter having a sealing material layer on the peripheral face and irregularities existing on the peripheral face, was manufactured.
- With respect to the honeycomb filter manufactured in Example 1, the depth of the irregularities on the peripheral face was measured and found to be 0.3 mm.
- Honeycomb filters were respectively manufactured by following the same procedure as in Example 1 except that the depth of the irregularities existing (remaining) on the peripheral face of the honeycomb filter was changed as shown in Table 1, by changing the amount (thickness) of the sealing material paste to be applied and the pressure to be applied to the ceramic block from the squeegee and the gap between the squeegee and the ceramic block.
- A honeycomb filter was manufactured by following the same procedure as in Example 1 except that the amount of the sealing material paste to be applied to the peripheral face of the ceramic block was increased and the gap between the squeegee and the ceramic block was changed so as to fill all the irregularities on the periphery of the ceramic block and make the peripheral face of the honeycomb filter smooth.
- A honeycomb filter including a round pillar-shaped ceramic block was manufactured by following the same procedure as in Example 1 except that a sealing material layer was not formed on the peripheral face of the ceramic block.
- With respect to the honeycomb filters manufactured in these Examples and Comparative Examples, performances when installed in an exhaust gas purifying apparatus were evaluated.
- As shown in
FIG. 7 , a holding sealing material is wound around the honeycomb filter and the honeycomb filter was installed in the exhaust gas purifying apparatus. Further, one end of the exhaust gas purifying apparatus was connected to a 2L (litter) common-rail-type diesel engine. - Then, the engine was driven at the number of revolutions of 2000 min−1 and a torque of 47 Nm so that exhaust gases from the engine were allowed to pass through the honeycomb filter. The apparatus was driven until 6.0 g of PM per liter of the honeycomb filter was captured, and regenerating process of the honeycomb filter was carried out through burning the PM by post injection. This was defined as one cycle.
- After repeating this cycle 50 times, a degree of the displacement of the honeycomb filter compared to the position before the test was visually observed.
- With respect to the honeycomb filter manufactured in each Example and the like, a shift length (mm) was collectively shown in Table 1.
- In the same manner as in the evaluation test for displacement, the honeycomb filter was installed in an exhaust gas purifying apparatus, and exhaust gases from the engine were allowed to pass through the honeycomb filter.
- After having the exhaust gases pass through the honeycomb filter for one hour, the exhaust gas purifying apparatus was disassembled. Then, the surface of the holding sealing material wound around the peripheral face of the honeycomb filter was visually observed to confirm whether or not any leakage of PM through the peripheral face of the honeycomb filter had occurred. With respect to the honeycomb filters manufactured in each Example and each Comparative Example, the presence or absence of the leakage of PM from the peripheral face of the honeycomb filter was checked, and the result was collectively shown in Table 1.
-
TABLE 1 Honeycomb filter Presence or Presence absence Depth Evaluation result or absence of of Dis- of sealing irregularities irregu- place- Presence or material on peripheral larities ment absence of layer face (mm) (mm) PM leakage Example 1 Present Present 0.3 <1 Absent Example 2 Present Present 0.1 <1 Absent Example 3 Present Present 0.5 <1 Absent Comparative Present Absent — 15 Absent Example 1 Comparative Absent Present 1.1 <1 Present Example 2 - In the case where the honeycomb filter manufactured in each Example was used, even after repeating the regeneration process, namely, even after thermal expansion and thermal shrinkage had been repeated in the honeycomb filter, the displacement of the honeycomb filter in the casing was less than 1 mm.
- In contrast, in a case where the regeneration process was carried out repeatedly on the honeycomb filter manufactured in Comparative Example 1, the displacement of the honeycomb filter in the casing became greater.
- As a result, it is presumed that in the honeycomb filters of each Example, since the irregularities existed on the peripheral face of the honeycomb filter, the coefficient of friction between the holding sealing material wound around the honeycomb filter and the peripheral face of the honeycomb filter became higher.
- Moreover, in the honeycomb filter of each Example having the sealing material layer formed thereon, no PM leakage was observed from the peripheral face of the honeycomb filter.
- In contrast, in the honeycomb filter manufactured in Comparative Example 2, since no sealing material layer was formed on the peripheral face, PM leakage from the peripheral face of the honeycomb filter was observed.
- That is, it is considered that, by forming the sealing material layer on the peripheral face of the honeycomb filter, the PM leakage from the peripheral face of the honeycomb filter can be prevented.
- The following description will discuss a second embodiment that is another embodiment of the present invention.
- In the present embodiment, a plurality of kinds of honeycomb fired bodies (honeycomb molded bodies) having respectively different cross-sectional shapes were manufactured, and by combining the plurality of kinds of honeycomb fired bodies, a ceramic block having an almost round pillar shape was manufactured without cutting the periphery thereof, so that the honeycomb filter according to the embodiments of the present invention was manufactured.
-
FIGS. 9A , 9B and 9C are perspective views each schematically showing one example of the honeycomb fired body constituting a honeycomb filter of the second embodiment. - A honeycomb fired
body 320, shown inFIG. 9A , has one side face having irregularities thereon and two smooth side faces. - A honeycomb fired
body 330, shown inFIG. 9B , has one side face having irregularities thereon and three smooth side faces. - A honeycomb fired
body 340, shown inFIG. 9C , has no side face having irregularities thereon, but four smooth side faces to provide a rectangular pillar shape. - In the present embodiment, four rectangular pillar-shaped honeycomb fired
bodies 340 were disposed in the center and eight honeycomb firedbodies 330 were disposed around the center honeycomb firedbodies 340 so as to be adjacent thereto. Further, four honeycomb firedbodies 320 were disposed adjacent to the honeycomb firedbodies 330. Then, respective honeycomb fired bodies were combined with one another with adhesive layers interposed between the side faces thereof, so that a ceramic block was manufactured. - The cross-sectional shape perpendicular to the longitudinal direction of the ceramic block thus manufactured is almost the same as the cross-sectional shape of the ceramic block having an almost round pillar shape shown in
FIG. 4 . - On the peripheral face of this ceramic block, irregularities are formed, which are derived from the shapes of the side faces having irregularities thereon of the honeycomb fired
bodies 320 and the honeycomb firedbodies 330. - Moreover, by thinly applying a sealing material paste to the peripheral face of the ceramic block along the irregularities formed thereon, a sealing material layer is formed in a manner so as to allow the irregularities to exist (remain) thereon; thus a honeycomb filter having a peripheral face with irregularities formed thereon can be manufactured.
-
FIG. 10 is a perspective view schematically showing one example of a honeycomb filter of the present embodiment. -
FIG. 11 is an enlarged cross-sectional view showing an area surrounded by a curved line E inFIG. 10 . - As shown in
FIGS. 10 and 11 , a sealingmaterial layer 302 is formed along the irregularities on aperipheral face 313 of aceramic block 303, and particularly formed along all the surfaces of irregularities on theperipheral face 313 of theceramic block 303 in ahoneycomb filter 300 according to the present embodiment. - Accordingly, on the
peripheral face 310 of thehoneycomb filter 300, there exist the irregularities (a projectingportion 316 and a recessed portion 317) derived from the irregularities on theperipheral face 313 of theceramic block 303, and the shape of irregularities existing on theperipheral face 310 of thehoneycomb filter 300 corresponds to the shape of the irregularities on theperipheral face 313 of theceramic block 303. - Here, each honeycomb fired body to be used in the present embodiment can be manufactured by following the same procedure as in the first embodiment except that the shape of a die to be used when a honeycomb molded body is formed through extrusion molding process is different.
- The honeycomb filter of the present embodiment can also exert effects (1) and (2) described in the first embodiment.
- Here, as shown in
FIGS. 10 and 11 , in the honeycomb filter of the present embodiment, the cells which form the peripheral face of the almost round pillar-shaped ceramic block are not sealed. Therefore, the irregularities are formed on the peripheral face of the honeycomb filter uninterruptedly from one end face side to another end face side. Thus, in the honeycomb filter according to the present embodiment, the shape of the peripheral face of the honeycomb filter becomes more complicated. - Accordingly, when the honeycomb filter according to the present embodiment is installed in the casing, the coefficient of friction between the holding sealing material wound around the honeycomb filter and the peripheral face of the honeycomb filter tends to be much higher. For this reason, even when thermal expansion and thermal shrinkage are repeated in the honeycomb filter because of the application of heat, the displacement of the honeycomb filter from the originally installed position in the casing tends to be effectively prevented.
- The shape of the honeycomb filter according to the embodiments of the present invention is not particularly limited to an almost round pillar shape, and may be a desired pillar shape such as an almost cylindroid shape, an almost pillar shape with a racetrack end face and an almost polygonal pillar shape.
- Although not particularly limited, the shape of the honeycomb fired bodies is preferably designed to easily combine the honeycomb fired bodies with one another when forming a ceramic block. For example, a square, rectangular, hexagonal or sector shape may be used as its cross-sectional shape.
- The porosity of the honeycomb fired body is not particularly limited, and desirably at least about 35% and at most about 60%.
- When the honeycomb fired body is used as a filter, the porosity of about 35% or more tends not to cause clogging in the honeycomb filter according to the embodiments of the present invention. In contrast, the porosity of about 60% or less tends not to cause a reduction in the strength of the honeycomb fired body, resulting in less possible breakage.
- The average pore diameter of the honeycomb fired body constituting the honeycomb filter according to the embodiments of the present invention is desirably at least about 5 μm and at most about 30 μm.
- When the honeycomb fired body is used as a filter, the average pore diameter of about 5 μm or more tends not to cause clogging due to PM. In contrast, the average pore diameter of about 30 μm or less tends not cause PM to pass through the pores. As a result, the honeycomb fired body is more likely to capture the PM, which enables functioning as a filter.
- Here, the porosity and the average pore diameter can be measured through conventionally known methods such as a mercury porosimetry, Archimedes method, and a measuring method using a scanning electronic microscope (SEM).
- The thickness of the cell wall of the honeycomb fired body constituting the honeycomb filter according to the embodiments of the present invention is not particularly limited, however, desirably at least about 0.2 and at most about 0.4 mm.
- The thickness of the cell wall of about 0.2 mm or more tends not to cause the thickness of the cell walls supporting the honeycomb structure to become too thin, which is more likely to maintain the strength of the honeycomb filter; in contrast, the thickness of about 0.4 mm or less tends not to cause an increase in the pressure loss.
- Further, the cell density in the cross-section perpendicular to the longitudinal direction of the honeycomb filter according to the embodiments of the present invention is not particularly limited. However, a desirable lower limit thereof is about 31.0 pcs/cm2 (about 200 pcs/inch) and a desirable upper limit is about 93.0 pcs/cm2 (about 600 pcs/inch2). Amore desirable lower limit is about 38.8 pcs/cm2 (about 250 pcs/inch2) and a more desirable upper limit is about 77.5 pcs/cm2 (about 500 pcs/inch2).
- The main component of the material of the honeycomb filter according to the embodiments of the present invention is not limited to silicon carbide, and may be ceramics (silicon-containing silicon carbide) in which metallic silicon is blended with silicon carbide.
- Especially, a silicon-containing silicon carbide ceramic containing about 60 wt % or more of silicon carbide is desirable.
- In addition, the silicon carbide may specifically include a recrystallized SiC or a reaction-sintered SiC.
- The particle diameter of the ceramic powder is not particularly limited, and the ceramic powder that tends not to cause the case where the size of the honeycomb fired body manufactured by the following firing treatment becomes smaller than that of the honeycomb molded body after degreased is preferable.
- The organic binder in the wet mixture is not particularly limited, and examples thereof include methylcellulose, carboxymethylcellulose, hydroxyethylcellulose, polyethylene glycol, and the like. Methylcellulose is desirable out of these. A blending amount of the organic binder is desirably at least about 1 part by weight and at most about 10 parts by weight with respect to 100 parts by weight of ceramic powder.
- The plasticizer in the wet mixture is not particularly limited, and examples thereof include glycerin and the like. The lubricant is not particularly limited, and examples thereof include polyoxyalkylene-based compounds such as polyoxyethylene alkyl ether and polyoxypropylene alkyl ether, and the like.
- Specific examples of the lubricant include polyoxyethylene monobutyl ether, polyoxypropylene monobutyl ether, and the like.
- Moreover, the plasticizer and the lubricant are not required to be contained in the wet mixture in some cases.
- In addition, a dispersant solution may be used upon preparing a wet mixture, and examples of the dispersant solution include water, an organic solvent such as benzene, alcohol such as methanol, and the like.
- Furthermore, a molding auxiliary may be added to the wet mixture.
- The molding auxiliary is not particularly limited, and examples thereof include ethylene glycol, dextrin, fatty acid, fatty acid soap, polyalcohol and the like.
- Furthermore, a pore-forming agent such as balloons that are fine hollow spheres including oxide-based ceramics, spherical acrylic particles, graphite and the like may be added to the wet mixture, if necessary.
- The balloon is not particularly limited, and examples thereof include alumina balloon, glass micro balloon, shirasu balloon, fly ash balloon (FA balloon), mullite balloon and the like. Alumina balloon is desirably used among these.
- Though the plug material paste for sealing the cells is not particularly limited, a plug to be manufactured through the subsequent processes desirably has a porosity of 30 to 75%, and for example, it is possible to use a plug material paste having the same composition as that of the wet mixture of the raw material.
- In the honeycomb filter according to the embodiments of the present invention, the sealing material paste used for forming the adhesive layer and the sealing material paste used for forming the sealing material layer (coat layer) may have either the same compositions or the different compositions.
- Examples of the inorganic binder in the sealing material paste include silica sol, alumina sol, and the like. Each of these materials may be used alone, or two or more kinds of these may be used in combination. Silica sol is desirable among the inorganic binders.
- Examples of the organic binder in the sealing material paste include polyvinyl alcohol, methyl cellulose, ethyl cellulose, carboxymethylcellulose, and the like. Each of these may be used alone or two or more kinds of these may be used in combination. Carboxymethylcellulose is desirable among the organic binders.
- Examples of the inorganic fibers in the sealing material paste include ceramic fibers and the like such as silica-alumina, mullite, alumina, and silica. Each of these may be used alone or two or more kinds of these may be used in combination. Alumina fibers are desirable among the inorganic fibers.
- Examples of the inorganic particles in the sealing material paste include carbides, nitrides, and the like, and specific examples thereof include inorganic powder or the like made from silicon carbide, silicon nitride, boron nitride and the like. Each of these may be used alone, or two or more kinds of these may be used in combination. Out of the inorganic particles, silicon carbide is desirably used due to its superior thermal conductivity.
- Moreover, a pore-forming agent such as balloons that are fine hollow spheres including oxide-based ceramics, spherical acrylic particles, graphite and the like may be added to the adhesive paste and the sealing material paste, if necessary. The balloons are not particularly limited, and examples thereof include alumina balloons, glass micro-balloons, shirasu balloons, fly ash balloons (FA balloons), mullite balloons, and the like. Alumina balloons are more desirably used among these.
- The method for forming the adhesive layer is not limited to the method described in the first embodiment and may be a method in which each of the honeycomb fired bodies is temporarily fixed in a molding frame having almost the same shape as the shape of the ceramic block to be manufactured and a sealing material paste is injected into the each gap between the honeycomb fired bodies, and the like.
- The catalyst to convert or purify exhaust gases may be supported on the honeycomb filter according to the embodiments of the present invention, and desirable examples of the catalyst to be supported include noble metals such as platinum, palladium and rhodium. Out of these, platinum is more desirable. Moreover, an alkali metal such as potassium and sodium, and an alkali earth metal such as barium may be used as other catalysts. These catalysts may be used alone, or two or more kinds of these may be used in combination.
- Obviously, numerous modifications and variations of the present invention are possible in light of the above teachings. It is therefore to be understood that within the scope of the appended claims, the invention may be practiced otherwise than as specifically described herein.
Claims (7)
1. A method for manufacturing a honeycomb filter, said method comprising:
preparing a wet mixture comprising at least one of silicon carbide and silicon-containing silicon carbide;
extrusion-molding said wet mixture to manufacture honeycomb molded bodies each having a longitudinal direction and a plurality of cell walls extending along the longitudinal direction to define a plurality of cells;
providing a plug material paste in the cells to seal either one of both ends of each of said cells;
firing said sealed honeycomb molded bodies to manufacture a honeycomb fired bodies;
applying a first sealing material paste to a side face of one of said honeycomb fired bodies to form a sealing material paste layer thereon;
laminating another of said honeycomb fired bodies on said first sealing material paste layer to manufacture an aggregated body of honeycomb fired bodies;
heating said aggregated body of honeycomb fired bodies so that said first sealing material paste layer is dried and solidified to produce a ceramic block;
applying a second sealing material paste to a peripheral face of said ceramic block in accordance with irregularities formed thereon so that an outer peripheral surface of the honeycomb filter has surface irregularities thereon; and
drying and solidifying said second sealing material paste to form a sealing material layer on the peripheral face of said ceramic block.
2. The method for manufacturing a honeycomb filter according to claim 1 , further comprising:
cutting the peripheral face of said ceramic block.
3. The method for manufacturing a honeycomb filter according to claim 1 , wherein said second sealing material paste has a viscosity lower than a viscosity of said first sealing material paste.
4. The method for manufacturing a honeycomb filter according to claim 1 , further comprising:
passing said ceramic block on which said second sealing material paste is coated through a squeegee having a cylindrical shape so that a coated surface of the ceramic block keeps the irregularities formed on the peripheral face of said ceramic block.
5. The method for manufacturing a honeycomb filter according to claim 1 , wherein the cells have exposed cells which are exposed on the peripheral face of said ceramic block, and wherein the exposed cells are not sealed in the filling step.
6. The method for manufacturing a honeycomb filter according to claim 1 , wherein a plurality of honeycomb molded bodies having different cross-sectional shapes are manufactured in said extrusion-molding step.
7. The method for manufacturing a honeycomb filter according to claim 6 , wherein said plurality of honeycomb molded bodies have a rectangular pillar shape with four side faces and comprises,
a first honeycomb molded body having one side face with irregularities thereon and two smooth side faces;
a second honeycomb molded body having one side face with irregularities thereon and three smooth side faces; and
a third honeycomb molded body having four smooth side faces.