US20090169742A1 - Coated silicon comprising material for protection against environmental corrosion - Google Patents
Coated silicon comprising material for protection against environmental corrosion Download PDFInfo
- Publication number
- US20090169742A1 US20090169742A1 US11/977,330 US97733007A US2009169742A1 US 20090169742 A1 US20090169742 A1 US 20090169742A1 US 97733007 A US97733007 A US 97733007A US 2009169742 A1 US2009169742 A1 US 2009169742A1
- Authority
- US
- United States
- Prior art keywords
- layer
- substrate
- silicon
- cerium oxide
- gas turbine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
In accordance with an embodiment of the invention, an article is disclosed. The article comprises a gas turbine engine component substrate comprising a silicon material; and an environmental barrier coating overlying the substrate, wherein the environmental barrier coating comprises cerium oxide, and the cerium oxide reduces formation of silicate glass on the substrate upon exposure to corrodant sulfates.
Description
- The invention was made in part under contract number NAS3-01135 awarded by the Government (NASA). Accordingly, the Government has certain rights in this invention.
- This invention relates to protecting materials comprising silicon from environmental corrosion, such as that experienced in the hostile thermal environment of a gas turbine engine. More particularly, the invention relates to an environmental barrier coating (EBC) system for use on silicon comprising substrates for providing protection against environmental corrosion.
- Higher operating temperatures for gas turbine engines are continuously sought in order to increase efficiency. However, as operating temperatures increase, the high temperature durability of the components within the engine must correspondingly increase. In this regard, materials comprising silicon, particularly those with silicon carbide (SiC) as a matrix material or a reinforcing material, are considered useful for high temperature applications, such as for combustor and other hot section components of gas turbine engines.
- However, some silicon substrates may recede and lose mass as a result of formation of volatile Si species, particularly Si(OH)x and SiO when exposed to high temperature, aqueous environments, thus necessitating the use of a protective coating thereon. Accordingly, methods such as described in U.S. Pat. Nos. 5,985,470, 6,444,335, 6,410,148 and 6,759,151, the contents of each of which are incorporated by reference, have addressed shortcomings concerning the use of such silicon substrates by providing an environmental barrier coating (EBC) over the substrate. The EBCs inhibit formation of volatile silicon species, Si(OH)x and SiO, thereby reducing recession and mass loss. A thermal barrier coating (TBC) typically comprising yttria stabilized zirconia may also be employed as an outer layer to the EBC depending upon the operating conditions employed.
- While the current state of the art EBCs, which are typically multi-layer EBCs, may be effective in preventing water vapor recession of the ceramic matrix composite (CMC) substrate, both BSAS, SiC and some rare earth silicates such as some silicates disclosed in U.S. Pat. No. 6,759,151 may be susceptible to silicate glass formation when in contact with sulfate salt deposits as operating conditions continue to increase.
- Accordingly, there is a need to reduce the silicate glass formation rate in materials comprising silicon, particularly in EBC materials. Embodiments of the present invention satisfy this need and others.
- In accordance with an embodiment of the invention, an article is disclosed. The article comprises a gas turbine engine component substrate comprising a silicon material; and an environmental barrier coating overlying the substrate, wherein the environmental barrier coating comprises cerium oxide, and the cerium oxide reduces formation of silicate glass on the substrate upon exposure to corrodant sulfates.
- In accordance with another embodiment of the invention, an article comprises a gas turbine engine component substrate comprising a silicon material. The article further comprises a bond layer comprising a silicon material and overlying the substrate; a first layer comprising mullite and overlying the bond layer; a second layer comprising an barium strontium aluminosilicate and overlying the first layer; and a third layer consisting of cerium oxide and overlying the second layer. The cerium oxide reduces formation of silicate glass on the substrate upon exposure to corrodant sulfates.
- In accordance with another embodiment of the invention, a gas turbine engine component is disclosed. The component comprises a substrate comprising a silicon material; and at least one layer on the substrate selected from the group consisting of: i) an environmental barrier coating comprising cerium oxide, and ii) a dual layer of barium strontium aluminosilicate and a layer consisting of cerium oxide overlying the barium strontium aluminosilicate; wherein the cerium oxide reduces formation of silicate glass on the substrate.
- In accordance with a further embodiment of the invention, a gas turbine engine component comprises a substrate comprising a silicon material. Cerium oxide is deposited directly on the substrate or admixed with the silicon material of the substrate, wherein the cerium oxide reduces formation of silicate glass on the substrate upon exposure to corrodant sulfates.
- In accordance with another embodiment, a method of reducing silicate glass formation on a gas turbine engine component is disclosed. The method comprises providing a substrate of the gas turbine engine component, wherein the substrate comprises a silicon material; and depositing cerium oxide directly on the substrate or admixing cerium oxide with the silicon material of the substrate. The cerium oxide reduces formation of silicon glass on the substrate upon exposure to corrodant sulfates.
- In accordance with another embodiment, a method of reducing silicate glass formation on a gas turbine engine component comprises providing a substrate of the gas turbine engine component, wherein the substrate comprises a silicon material. The method further comprises depositing a bond layer comprising a silicon material and overlying the substrate; depositing a first layer comprising mullite and overlying the bond layer; depositing a second layer comprising an environmental barrier coating overlying the first layer; and depositing a layer consisting of cerium oxide overlying second layer or admixing cerium oxide with barium strontium aluminosilicate. The cerium oxide reduces formation of silicon glass on the substrate upon exposure to corrodant sulfates.
- Other features and advantages will be apparent from the following more detailed description, taken in conjunction with the accompanying drawing, which illustrate by way of example the principles of the invention.
-
FIG. 1 is a cross-sectional view of a gas turbine engine component formed of a material comprising Si and having an environmental barrier coating thereon, in accordance with an embodiment of the invention. - Applicant has determined through testing that silicon comprising materials may adversely react with deposited sulfates. For example, this material may react with Na2SO4 at temperatures such as about 1700° F. (927° C.) and higher, and MgSO4/CaSO4 may react at temperatures such as about 2200° F. (1204° C.) and higher. This reaction causes corrosion and forms a silicate glass from the silicon comprising material. Deep pitting and CO evolution can degrade the performance of the silicon comprising material. Additionally, this may prevent EBCs from acting as optimal water recession barriers for silicon comprising substrates as silicate glass has a high recession rate.
- Embodiments of the present invention improve upon prior coated silicon comprising materials, particularly EBC systems used upon silicon comprising material substrates. These embodiments are generally applicable to components that operate within environments of relatively high temperatures, and are thus subjected to thermal cycling, stresses, oxidation, and corrosion. Examples of such components include, but are not limited to, combustor components, blades, shrouds, flaps, seals, vanes, and other components of gas turbine engines.
- Referring to
FIG. 1 , an EBCsystem 10 of a first embodiment is shown. The EBCsystem 10 includes an EBC 12, and asurface region 16 or substrate of acomponent 18. Thecomponent 18, or at least the surface region (substrate) 16 of thecomponent 18, is formed of a silicon comprising material (particularly those for articles exposed to high temperatures), such as SiC/SiC ceramic matrix composites (CMC). However, embodiments of the invention are generally applicable to other materials comprising silicon. Examples of silicon comprising materials include, but are not limited to, those with a dispersion of silicon carbide, silicon carbide and/or silicon particles as a reinforcement material in a metallic or nonmetallic matrix. Also included are those having a silicon carbide, silicon aluminum oxynitride, silicon nitride and/or silicon comprising matrix, and particularly composite materials that employ silicon carbide, silicon nitride and/or silicon as both the reinforcement and matrix materials (e.g., SiC/SiC ceramic matrix composites (CMC)). Silicon comprising materials further include metal silicides including, but not limited to, molybdenum and niobium silicides. Thus, according to embodiments of the invention, thesilicon comprising substrate 16 may be a silicon comprising ceramic material as, for example, silicon carbide, silicon nitride, silicon carbon nitride, silicon oxynitride and silicon aluminum oxynitride. In accordance with one embodiment, thesilicon comprising substrate 16 comprises a silicon comprising matrix with reinforcing fibers, particles and the like and, more particularly, a fiber reinforced silicon based matrix. Particularly suitable ceramic substrates are a silicon carbide coated silicon carbide fiber-reinforced silicon carbide particle and silicon matrix, a carbon fiber-reinforced silicon carbide matrix and a silicon carbide fiber-reinforced silicon nitride matrix. Particularly useful silicon-metal alloys for use assubstrates 16 for the article of embodiments of the invention include molybdenum-silicon alloys, niobium-silicon alloys, and other Si comprising alloys having a coefficient of thermal expansion compatible with the other layer(s) described herein. - In accordance with one embodiment, the surface region or
substrate 16 of thecomponent 18 is protected by the multilayer EBCsystem 10 that includes the EBC 12 for providing environmental protection to thecomponent 18. Optionally, a top coat or conventional thermal barrier coating (not shown), as well as optional conventional intermediate layer(s) (not shown) may be provided on top of the EBC 12 for providing further thermal insulation to the underlying layers depending upon desired operational temperatures. - The
multi-layered EBC 12 of the embodiment shown inFIG. 1 , preferably has four layers, as shown therein. These four layers may include abond layer 22, afirst layer 24, asecond layer 26 and athird layer 28. Thebond layer 22 overlays thesubstrate 16 of thecomponent 18 and preferably comprises silicon, such as at least one of silicon metal and silicon dioxide. Thisbond layer 22 is useful to improve oxidation resistance of thesurface region 16 and enhance bonding between thefirst layer 24 and thesurface region 16, particularly if thesurface region 16 comprises silicon carbide or silicon nitride. A suitable thickness for thebond layer 22 is about 12.5 to about 250 micrometers. Suitable materials forbond layer 22 also include those described in the afore-referenced U.S. Pat. No. 6,410,148. For example,bond layer 22 can include a silicon metal or a SiO2 layer. - The
first layer 24 is located on thebond layer 22 and comprises mullite. This mullite comprisingfirst layer 24 serves to adhere thesecond layer 26 to thesurface region 16, while also preventing interactions between thesecond layer 26 and the silicon comprisingsurface region 16 at elevated temperatures. Thefirst layer 24 may also comprise BSAS for less demanding applications, e.g. temperatures below about 1300° C. The addition of BSAS to thelayer 24 is also relatively compatible with the silicon comprisingsurface region 16 in terms of having a CTE of about 5.27 ppm/° C., as compared to a CTE of about 4.9 ppm/° C. for SiC/SiC CMC. Preferably,first layer 24 comprises mullite-barrium strontium aluminosilicate (BSAS) in an amount of between about 40 to 80 wt. % mullite and between about 20 to 60 wt. % BSAS. A suitable thickness range for the mullite comprisingfirst layer 24 is about 25 to about 250 micrometers. - The
second layer 26 overlies the firstmullite comprising layer 24 and typically comprises BSAS and may consist essentially of BSAS. This layer provides excellent environmental protection and thermal barrier properties due to its low thermal conductivity. Particularly, BSAS can serve as an environmental barrier to the underlyingmullite comprising layer 24, which would exhibit significant silica activity and volatilization if exposed to water vapor at high temperatures. Additionally, BSAS is physically compliant with a SiC comprising substrate, such as that suitable forsurface region 16, and is relatively compatible with themullite comprising layer 24 and the silicon comprisingsurface region 16 in terms of CTE. A suitable thickness range forlayer 26 is about 25 to about 500 micrometers, depending upon the particular application. - The
second layer 26 may alternatively or additionally comprise a rare earth silicate such as described in U.S. Pat. No. 6,759,151. For example, rare earth silicates, such as those described in U.S. Pat. No. 6,759,151 may be employed as in place of the BSAS described herein or admixed therewith. As a further example, rare earth silicates include, but are not limited to, RE2O3, SiO2, 2RE2O3.3SiO2, RE2O3.2SiO2, and combinations thereof, where RE is a rare earth element selected from the group consisting of Sc, Dy, Ho, Er, Tm, Yb, Lu, Eu, Gd, Tb and combinations thereof. - In the embodiment shown in
FIG. 1 , theEBC 12 also comprises a cerium oxide (CeO2) layer 28 (third layer 28) located on top of thesecond layer 26. A suitable thickness range for this layer is between about 5 to about 75 micrometers, also depending upon the particular application. Alternatively, the cerium oxide may be admixed with thesecond layer 26. For example, cerium oxide may be admixed in any suitable amounts such as in a 50:50-weight percentage with the constituents of thesecond layer 26. - In alternate embodiments of the invention, the
EBC 12 may comprise thesecond layer 26 deposited directly on the substrate comprising silicon and thethird layer 28 deposited on thesecond layer 26. Alternatively, an admixed layer of the second layer and thethird layer 28 may be deposited on the substrate comprising silicon. It should be noted that in these embodiments,bond layer 22 may also be employed and deposited directly on the substrate comprising silicon with the additional layers deposited on thebond layer 22. -
- Thus, in accordance with embodiments of the invention, a single layer, EBC of BSAS and CeO2 admixed therewith, as described above, may be used to provide environmental protection to the underlying silicon comprising material. This embodiment is particularly useful for operating temperatures below about 3000° F. (1371° C.), Alternatively, a CeO2 layer, as described above, may be deposited on top of the BSAS layer.
- The
layers - Accordingly, Applicant has advantageously determined that deposition of this high melting point acidic compound, CeO2, will result in dissolution into the basic corrosion melt and increase the eutectic temperature and/or decrease the basicity of the solution. This will advantageously slow and/or stop the silicate glass formation on the surface of the silicon comprising material by raising the melting point or decreasing the basicity of the silicate glass of the corrodant mix.
- While various embodiments are described herein, it will be appreciated from the specification that various combinations of elements, variations and improvements therein may be made by those skilled in the art, and are within the scope of the invention.
Claims (4)
1-14. (canceled)
15. A method of reducing silicate glass formation on a gas turbine engine component comprising:
providing a substrate of the gas turbine engine component, wherein the substrate comprises a silicon material; and
depositing cerium oxide directly on the substrate or admixing cerium oxide with the silicon material of the substrate; wherein the cerium oxide reduces formation of silicon glass on the substrate upon exposure to corrodant sulfates.
16. A method of reducing silicate glass formation on a gas turbine engine component comprising:
providing a substrate of the gas turbine engine component, wherein the substrate comprises a silicon material;
depositing a bond layer comprising a silicon material and overlying the substrate;
depositing a first layer comprising mullite and overlying the bond layer;
depositing a second layer comprising barium strontium aluminosilicate overlying the first layer; and
depositing a layer consisting of cerium oxide overlying second layer or admixing cerium oxide with the barium strontium aluminosilicate; wherein the cerium oxide reduces formation of silicon glass on the substrate upon exposure to corrodant sulfates.
17. The method of claim 16 , wherein each layer is deposited by a method selected from the group consisting of: air plasma spray, vacuum plasma spray, chemical vapor deposition and high velocity oxy fuel.