US20080241963A1 - Biochemical labeling materials and manufacturing method thereof - Google Patents
Biochemical labeling materials and manufacturing method thereof Download PDFInfo
- Publication number
- US20080241963A1 US20080241963A1 US11/967,648 US96764807A US2008241963A1 US 20080241963 A1 US20080241963 A1 US 20080241963A1 US 96764807 A US96764807 A US 96764807A US 2008241963 A1 US2008241963 A1 US 2008241963A1
- Authority
- US
- United States
- Prior art keywords
- nanoparticles
- labeling material
- biochemical labeling
- biochemical
- matrix
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A biochemical labeling material and manufacturing method thereof. The manufacturing method provides a plurality of nanoparticles, bonding the nanoparticles to template molecules by molecular imprinting, polymerizing the nanoparticles to form a matrix with uniformly-distributed template molecules, finally removing the template molecules from the matrix to reveal a detection group of the matrix, leaving a cavity with specific area.
Description
- 1. Field of the Invention
- The present invention relates to the field of biochemical labeling materials. More particularly, the invention relates to a biochemical labeling material comprising molecularly imprinted nanoparticles.
- 2. Description of the Related Art
- For an eligible biochemical labeling material, two properties are important; selectivity of analytes, and effectiveness of signals produced after biochemical labeling, with resultant ease of detection.
- Conventional biochemical labeling materials utilize the unique selectivity of antibody to antigen to enhance effectiveness. For example, peptide and other proteins are used as polyclonal antibodies that select the analyte via adsorption. Fluorescent reagents are applied to produce “labeled” signals in terms of variations of wavelength and intensity of fluorescence.
- As nanotechnology develops, semiconductor-nanocrystals are used as fluorescent probes in biochemical labeling materials. Compared to conventional biochemical labeling materials producing weaker, more difficult-to-observe signals, fluorescent probes of semiconductor-nanocrystals, owing to their narrower energy gap, produce stronger signals and more stable fluorescence, adjustable in different situations for different analytes.
- Surface functionalization is performed on most semiconductor-nanocrystals prior to usage as biochemical labeling materials. First, II-IV or III-V group semiconductor-particles (single-semiconductor particles or core-shell particles composed of two semiconductors) are reacted with mercaptoacetic acid to form carboxylic groups attached thereon such that the particles become hydrophilic. Then, proteins are attached to the functionalized particles by covalent bonding. Proteins are polyclonal antibodies able to identify the analyte (i.e. antigen). Once the analyte attaches thereon, the quantum effect of nanocrystal particles generates the signals.
- Bruchez et al, in Semiconductor-Nanocrystals as Fluorescent Biological Labels (Science 281, 2013 (1998)) modify the third Si layer of CdSe-CdS core-shell semiconductor-nanocrystal particles to be hydrophilic, and then re-modify the Si layer by different functional group to become reactive with biochemical substances. Different modification by Si is performed to increase quantum effect and improve properties. Different core-shell semiconductor-nanocrystal particles were studied, with the main purpose thereof being the fluorescent labeling of mouse fibroblast cells.
- Chen et al (Quantum Dot Bioconjugates for Ultrasensitive Nonisotopic Detection, Science 281, 2016 (1998)) study high-fluorescence-semiconductor quantum dot (Zinc Sulfide-capped cadmium selenide) to bond biochemical molecules by covalent bonds and applied to super-high sensitive biochemical labeling materials. Compared to organic dyes, e.g. rhodamine, the intensity of fluorescence increases 20 times, the stability to photobleaching increases 100 times that, but the Spectrum line width is only ⅓ thereof. The manufacturing method thereof uses ZnS-capped CdSe as the quantum dot, modify the surface by mercaptoacetic acid, and bond with proteins by carboxylic groups.
- Tan et al (U.S. Pat. No. 572469) manufacture Ag or Cd semiconductor-nanoparticles by microemulsion and react them with silicate to form a layer of silicate, and a silicate layer is modified to bond with proteins, antibody, or antigen.
- Mirkin et al (WO Patent 2001073123, 2001051665, 9804740) synthesize nanoparticle-oligonucleotide conjugates to detect nucleic acid by the color change owing to combination thereof.
- Ewart et al (WO Patent 9821587) synthesize omit-human IgG-alkaline phosphatase conjugate ZnS:Cu:Aλ capped fluorescent nanoparticles as label materials.
- Nanoparticles have thus far been utilized in manufacture of biochemical labeling materials as discussed above, however, the identifying ability of proteins is limited to certain biochemical substrances, and modification of multilayer-nanocrystal particles broadens of Emission Spectrum and instability of photochemical properties.
- Thus, the purpose of the invention is to provide a biochemical labeling material and manufacturing method thereof in which the advantages of using nanoparticles are maintained and selectivity compared to conventional antibody-antigen design is improved, such that the limitation of analytes is relieved and the biochemical labeling material can identify more types of analyte.
- To achieve the purpose, the invention applies molecular imprinting on nanoparticles to endow them with unique selectivity to specific species, and expand the applicability to all kinds of chemical compounds, without limitation to biochemical substances. Moreover, modification of nanoparticles is applied to enhance the effectiveness of signals produced after biochemical labeling.
- The manufacturing method of biochemical labeling material provided comprises providing a plurality of nanoparticles, bonding the nanoparticles to a template molecule by molecular imprinting, polymerizing the nanoparticles to form a matrix with uniformly-distributed template molecule, and removing the template molecule from the matrix to reveal a detection group of the matrix and leave a cavity with specific area.
- The manufacturing method provided can further comprise a surface functionalization treatment of nanoparticles by fluorescent molecule or electron-transfer molecule.
- The following detailed description, given by way of example and not intended to limit the invention solely to the Example described herein, will best be understood in conjunction with the accompanying drawings, in which:
-
FIG. 1 shows a manufacturing diagram of the present invention; -
FIG. 2 illustrates surface functionalization of CdSe(ZnS) nanoparticles in the first Example; -
FIG. 3 illustrates manufacture of biochemical labeling material in one Example by covering CdSe(ZnS) nanoparticles with 4-Vinyl pyridine; -
FIG. 4 a shows a fluorescent spectrum of polymer matrix of functionalized CdSe(ZnS) nanocrystal particles; -
FIG. 4 b shows a fluorescent spectrum of caffeine-bonded polymer matrix of functionalized CdSe(ZnS) nanocrystal particles; -
FIG. 4 c shows a fluorescent spectrum of polymer matrix of functionalized CdSe(ZnS) nanocrystal particles, after reaction with theobromine; -
FIG. 4 d shows a fluorescent spectrum of polymer matrix of functionalized CdSe(ZnS) nanocrystal particles, after reaction with theophyline; and -
FIG. 5 illustrates manufacture of biochemical labeling material in another more Example by covering CdSe(ZnS) nanoparticles with (3-mercaptopropyl) trimethoxy silane. - The manufacturing method of biochemical labeling material provided comprises providing a plurality of nanoparticles, bonding the nanoparticles to a template molecule by molecular imprinting, polymerizing the nanoparticles to form a matrix with uniformly-distributed template molecule, and removing the template molecule from the matrix to reveal a detection group of the matrix and leave a cavity with specific area.
-
FIG. 1 shows a manufacturing diagram of the present invention wherein ◯ represents a nanoparticle, and B the template molecule, e.g., a bio-organo molecule. - During manufacture, first, a plurality of nanoparticles ◯ is provided with an organic-connective molecule x bonded thereon by surface functionalization. Then, molecular imprinting is applied to combine the nanoparticles ◯ with template molecules B. In addition, molecular imprinting can also be applied directly on the nanoparticles ◯ without advance surface functionalization treatment of nanoparticles.
- The nanoparticle ◯ in
FIG. 1 can be semiconductor-nanoparticle, such as II-VI or III-V group semiconductors as follows. - II-VI: CdS, CdSe, CdTe, ZnS, ZnSe, ZnTe, HgS, HgSe, HgTe or other combinations of duad and quadrivalence;and III-V: InP, GaP, GaInP2, GaAs, IrAs, GaN, InN or other combinations of trivalence and pentad.
- Nanoparticles applicable in the present invention can also be metal, for example, Au, Ag, Ni, or Co, or metal oxide, for example, Fe2O3, except semiconductors of II-VI and III-V group and core-shell nanoparticles composed of at least two semiconductors.
- Semiconductor-nanoparticles normally illuminate under extra energy due to the band gap thereof usually falling between the spectrum of visible light and infrared, for example, photoluminescence(PL) or electroluminescence(EL). Luminescent properties of the above nanoparticle ◯, e.g., intensity or wavelength of luminescence, are related to the reciprocal effect between energy of the organic molecule x and semiconductor-nanoparticle ◯, such that when the bio-organo molecule B approaches the nanoparticle ◯, the molecular structure of organic molecule x changes, as does the electronic orbit, and thus the reciprocal effect between nanoparticle ◯ alters the luminescent intensity and wavelength.
- In
FIG. 1 , organic molecule x performs both energy and electron transfers. - For energy transfer, if x is fluorescent with higher luminant energy than the band gap of semiconductor-nanoparticle ◯, x transfers energy to the nanoparticle ◯ after excitation to enhance the fluorescent intensity of nanoparticle ◯. After connection of x and B results in the yield rate change of fluorescent quantum dots, the fluorescent intensity of semiconductor particle ◯ is thereby changed. X can be a fluorescent molecule such as a molecule with resonant structure, electron acceptor, or electron donor, or organic molecule with transition metals or inner-transition metals, such as, dansyl chloride, anthracene, pyrene, coumarine, n-vinylcarbazole, or combination thereof.
- If x is an electron-transfer molecule, e.g., an electron donor, x transfers electrons to semiconductor-nanoparticle ◯ after excitation to change the fluorescent wavelength of semiconductor-nanoparticle ◯. Contrarily, when x is an electron acceptor, electrons are transferred from the semiconductor-nanoparticle ◯ to organic molecule x after excitation of x, and the fluorescent wavelength of hanoparticle ◯ is changed as well. The electron-transfer ability of x changes if B connects thereon, and the fluorescent wavelength of semiconductor particle ◯ changes accordingly. X can be an electron donor, such as amine, porphine molecule with metal for example, Fe or Mn, organic phosphorous molecule. X can also be an electron acceptor, such as fullerene, aromatic, organophosphine, quinone, carotene, or derivatives thereof.
- Except for two kinds of x, 3-mercaptopropyl) trimethoxy silane or 3-aminopropyltrimethoxysilane is also applicable to functionalize the surface of nanoparticle to form a functional group capable of forming hydrogen bonding with template molecule. 4-vinyl pyridine and allyl twmercaptothiol are applicable as well to form unsaturated double bonds on the surface nanoparticle. Furthermore, (3-mercaptopropyl) trimethoxy silane and vinyltrimethoxysilane are also applicable to form unsaturated double bonds on the surface nanoparticle.
- Molecular imprinting process firstly forms a complex of a template molecule, i.e. bio-organo molecule B in this case, and a monomer by non-covalent or covalent bonds formed therebetween. Polymerization of complexes is then performed under a crosslinking agent, and a biochemical labeling material is finally obtained after removal of template molecule. The interaction between polymer and template molecule is the basis of the high selectivity polymer. The obtained material, as ion exchange resin, has substantially larger apertures and superior hardness. The size of aperture allows permeation of solvents or reagents into the reactive sites to remove the template molecules and bond thereon (if the template molecule is completely surrounded by polymer, the removal is not possible, such that the “reactive site” remains unreactive). The imprinted polymer carries a reactive area having affinity for the target-bio-organo molecule B and acts as the selective absorbent in solid-phase extraction (SPE) and affinity chromatography.
- The provided manufacturing method of biochemical labeling material firstly forms a polymer matrix via reaction of surface modified semiconductor-nanoparticles, specific template molecules, functional monomers, initiators, and crosslinking agent. The template molecules are then removed to reveal a detection group of the matrix and leave a cavity with specific area. Nanoparticles as well as molecule-detection groups are thus well distributed in the polymer matrix. The polymer matrix is applicable for a biochemical labeling material due to the quantum effect resulting from the adsorption and desorption of template molecule on nanoparticles.
- The core-shell semiconductor-nanoparticles were prepared as follows. 5 g TOPO was first heated in a flask under vacuum and 190° C. for a few hours, 0.5 ml TOP was then added and the temperature is lowered to 60° C. Then, n-Hexane with about 0.1-0.4 mmol CdSe nanocrystal particles dispersed therein was poured into the reacting flask, and drawn out. The reacting flask with CdSe nanocrystal particles dispersed in TOPO and TOP was further heated and precursors of Zn and S, for example, ZnEt2 and hexamethyl disilathiane respectively, of equivalent molar weight in 2-4 ml TOP were added under nitrogen. The temperature was then lowered to 90° C. after adequate mixing, after continuing mixing for a few hours, CdSe(ZnS) was precipitated by addition of n-butyl alcohol and methyl alcohol.
- In
FIG. 2 , the surface functionalization of CdSe(ZnS) nanoparticles in the first Example is illustrated. - As in
FIG. 2 , the surface functionalizaiton of CdSe(ZnS) nanoparticles first dissolves the CdSe(ZnS) nanoparticles in methyl alcohol solvent containing 0.17% (v/v) (3-mercaptopropyl) trimethoxy silane and 25% dimethyl sulfoxide(DMSO) with PH value between 10˜11. After overnight mixing, the solution was then diluted with tetramethyl ammonium hydroxide and reflowed at 69° C. for 30 minutes. Then, methyl alcohol solvent containing trimethoxysilylpropyl urea and 3-aminopropyltrimethoxysilane was added after the temperature was lowered, and mixing continued for 2 hours. The solution was reflowed again for 5 minutes and cooled. Basic chlorotrimethylsilane solution was then added and finally 50% acetone, isopropyl alcohol solution was added to precipitate the greasy solid. - TOP/TOPO capped CdSe nanocrystal particles were first prepared as follows. TOPO was put in a flask to dry under vacuum at 180° C. for 1 hour, and the flask was then filled with nitrogen and heated to 350° C. 1 M TOPSe solution (4 mmole) with CdSe2(2.78 mmole) and TOP (16 ml) were then poured into the stirred TOPO. The particles became mossy after addition of extra methyl alcohol. The mossy precipitate, soluble in organic solvent, was then separated by a centrifuge.
- As in
FIG. 3 , nanocrystal particles were first modified as follows. - CdSe(ZnS) was first treated by 4-Vinyl pyridine to perform surface functionalization. The template molecules, such as caffeine, and various functional monomers, such as ethylene glycol dimethacrylate (EGDMA), were then added to form complexes in toluene at 60° C. The initiator, benzoyl peroxide (BPO) was then added to initiate the crosslinking reaction. The polymer matrix with uniformly distributed funtionalized semiconductor-nanocrystal particles was obtained after removal of template molecules. The molar ratio of CdSe(ZnS) nanoparticles: caffeine: EGDMA: BPO was 0.8:0.8:140:0.3.
- The polymer matrix then underwent the labeling test of the template molecule, caffeine.
-
FIG. 4 a shows a fluorescent spectrum of polymer matrix of functionalized CdSe(ZnS) nanocrystal particles, wherein the maximum intensity is about 520 a.u., indicating the polymer matrix with caffeine molecules bonded thereon brought distinct quantum effect as shown inFIG. 4 b in which the fluorescent spectrum of caffeine-bonded polymer matrix of functionalized CdSe(ZnS) nanocrystal particles was displayed, lowering the maximum intensity to about 120 a.u. - Molecules with similar molecular structure to caffeine, for example, theobromine and theophyline were then identified by the polymer matrix to test the selectivity thereof.
FIG. 4 c andFIG. 4 d show fluorescent spectrums of polymer matrix of functionalized CdSe(ZnS) nanocrystal particles, after reaction with theobromine and theophyline, respectively. ComparingFIG. 4 c and 4 d with 4 a, there is no distinct difference, indicating that the polymer matrix did not integrate with theobromine or theophyline, and exhibited detection ability as well as highly specific selectivity to the template molecules of caffeine. - First, the TOP-TOPO capped CdSe nanocrystal particles were prepared as described in Example 2.
- As in
FIG. 5 , the surface functionalization of nanocrystal particles was first performed to bond (3-mercaptopropyl) trimethoxy silane via Na2SiO2 to CdSe(ZnS), then add vinyltrimethoxysilane and perform hydrolysis concentration reaction with slight acidic catalyst. The reactant obtained forms a polymer matrix with uniformly distributed semiconductor-nanocrystal particles with functional monomers, e.g. EGDMA, a crosslinking agent and template molecules, e.g. caffeine. The molar ratio of CdSe(ZnS): caffeine: EGDMA: catalyst was 0.8:0.8:140:0.3. - While the invention has been described by way of example and in terms of the preferred embodiments, it is to be understood that the invention is not limited to the disclosed embodiments. To the contrary, it is intended to cover various modifications and similar arrangements (as would be apparent to those skilled in the art). Therefore, the scope of the appended claims should be accorded the broadest interpretation so as to encompass all such modifications and similar arrangements.
Claims (23)
1. (canceled)
2. A method for manufacturing a biochemical labeling material comprising:
providing a plurality of nanoparticles;
bonding the nanoparticles to a template molecule by molecular imprinting;
polymerizing the nanoparticles to form a matrix with uniformly-distributed template molecule; and
removing the template molecule from the matrix to reveal a detection group of the matrix and leave a cavity with specific area,
wherein the nanoparticles are metal.
3. The method for manufacturing a biochemical labeling material as claimed in claim 2 , wherein the nanoparticles are Au, Ag, Ni, or Co.
4. A method for manufacturing a biochemical labeling material comprising:
providing a plurality of nanoparticles;
bonding the nanoparticles to a template molecule by molecular imprinting;
polymerizing the nanoparticles to form a matrix with uniformly-distributed template molecule; and
removing the template molecule from the matrix to reveal a detection group of the matrix and leave a cavity with specific area,
wherein the nanoparticles are metal oxide.
5. The method for manufacturing a biochemical labeling material as claimed in claim 4 , wherein the nanoparticles are iron oxide.
6-17. (canceled)
18. A biochemical labeling material manufactured by a method comprising:
providing a plurality of nanoparticles;
bonding the nanoparticles to a template molecule by molecular imprinting;
polymerizing the nanoparticles to form a matrix with uniformly-distributed template molecule; and
removing the template molecule from the matrix to reveal a detection group of the matrix and leave a cavity with specific area.
19. A biochemical labeling material as claimed in claim 18 , wherein the nanoparticles are metal.
20. A biochemical labeling material as claimed in claim 19 , wherein the nanoparticles are Au, Ag, Ni, or Co.
21. A biochemical labeling material as claimed in claim 18 , wherein the nanoparticles are metal oxide.
22. A biochemical labeling material as claimed in claim 21 , wherein the nanoparticles are iron oxide.
23. A biochemical labeling material as claimed in claim 18 , wherein the nanoparticles are semiconductors.
24. A biochemical labeling material as claimed in claim 23 , wherein the nanoparticles are II-VI or III-V group semiconductors.
25. A biochemical labeling material as claimed in claim 23 , wherein the nanoparticles have core-shell structure of at least two semiconductors.
26. A biochemical labeling material as claimed in claim 18 , wherein the surface of nanoparticles is further functionalized prior to the bonding with template molecule.
27. A biochemical labeling material as claimed in claim 26 , wherein the surface of nanoparticles is functionalized by fluorescent molecule.
28. A biochemical labeling material as claimed in claim 27 , wherein the fluorescent molecule is dansyl-chloride, anthracene, pyrene, coumarine, n-vinylcarbazole or derivatives thereof
29. A biochemical labeling material as claimed in claim 26 , wherein the surface of nanoparticles is functionalized by electron-transfer molecule.
30. A biochemical labeling material as claimed in claim 29 , wherein the electron-transfer molecule is amine, porphine, fullerene, organophosphine, carotene, or derivatives thereof
31. A biochemical labeling material as claimed in claim 26 , wherein the surface of nanoparticles is functionalized by (3-mercaptopropyl) trimethoxy silane or (3-aminopropyl) trimethoxy silane to form a functional group thereon, able to bond to the template molecule by hydrogen bond.
32. A biochemical labeling material as claimed in claim 26 , wherein the surface of nanoparticles is functionalized by (4-vinyl pyridine) or allyl mercaptothiol to form an unsaturated double-bond thereon.
33. A biochemical labeling material as claimed in claim 26 , wherein the surface of nanoparticles was functionalized by (3-mercaptopropyl) trimethoxy silane) or vinyl trimethoxy silane to form an unsaturated double-bond thereon.
34. A biochemical labeling material as claimed in claim 18 , wherein a functional monomer, a crosslinking agent, and an initiator are further added during polymerization of nanoparticles.